A nickel alloy matrix high-temperature self-lubricating coating(77.5 wt%(Ni-Cr-Mo-Al)-12.5 wt%Ag-10 wt%BaF2/CaF2)was prepared by plasma spraying technique.Results show that the Vickers microhardness of coating is(2.9&...A nickel alloy matrix high-temperature self-lubricating coating(77.5 wt%(Ni-Cr-Mo-Al)-12.5 wt%Ag-10 wt%BaF2/CaF2)was prepared by plasma spraying technique.Results show that the Vickers microhardness of coating is(2.9±0.5)GPa,and the average bonding strength is about(35.6±0.5)MPa.The coating rubbing against Inconel 718 superalloy pin exhibits superior tribological performance with coefficient of friction(COF)of below 0.25 and wear rate of 8.2×10^(-5)-15.2×10^(-5)mm^(3)·N^(-1)·m^(-1)at a wide temperature range from 25 to 800℃,and the COF and the wear rate are slightly reduced with temperature increasing.The low COF and wear rate were attributed to the synergistic effects of Ag,BaF_(2)/CaF_(2),Ag2MoO_(4)and BaMoO_(4).展开更多
The effect of cerium dioxide(CeO_2)as an additive on the structure and properties of a melting type coating has been studied by means of microhardness measurement,scanning electron microscopy and thermal analysis. The...The effect of cerium dioxide(CeO_2)as an additive on the structure and properties of a melting type coating has been studied by means of microhardness measurement,scanning electron microscopy and thermal analysis. The results show that cerium dioxide can modify the microstructure and tribological properties of the coating. Model LIC-23 composite coating which contains CeO_2 performs well as a self-lubricating coating in hydrochloric acid solution.展开更多
The objective of this research was to develop a novel self-lubricating coating on an AA6061 aluminum alloy.Three coatings were prepared by the plasma electrolytic oxidation（PEO） process using 50-, 500-, and 1000-Hz ...The objective of this research was to develop a novel self-lubricating coating on an AA6061 aluminum alloy.Three coatings were prepared by the plasma electrolytic oxidation（PEO） process using 50-, 500-, and 1000-Hz pulsed direct current, respectively. The as-deposited coatings were then post-treated using two different methods, viz., ultrasonic vibration-aided vacuum oil impregnation（UVOI） and oil impregnation under ambient pressure（OIAP）. After posttreatment, an oil-containing, self-lubricating top layer was formed on the coatings. The effects of the coatings＇ surface morphologies and structures on their oil-holding capabilities were discussed. The results revealed that coatings prepared with higher frequency had a greater oil-holding capacity using OIAP post-treatment, while those prepared with lower frequency had a greater oil-containing capability using UVOI post-treatment. These phenomena are related to the morphologies of the coatings produced with various current modes. The tribological properties of the coatings before and after post-treatments were investigated by pin-on-disc sliding wear tests. Due to the formation of a lubricant-containing top layer, the post-treatment coatings had a lower friction coefficient and improved wear resistance compared with the asdeposited coatings. In addition, the coatings after UVOI treatment had better wear performance than those post-treated using the OIAP process. Among all coatings, the coating produced with a 50-Hz pulsed current followed by UVOI posttreatment achieved the lowest friction coefficient（0.03） and best wear resistance when sliding against a Si3N4 ceramic counterface. This study indicates that a novel self-lubricating coating can be prepared by a PEO process combined with vacuum oil impregnation post-treatment.展开更多
Black nickel coatings have emerged as a research hotspot in materials science due to their excellent performance and broad application prospects.In this study,nickel-based black coatings were fabricated on low-carbon ...Black nickel coatings have emerged as a research hotspot in materials science due to their excellent performance and broad application prospects.In this study,nickel-based black coatings were fabricated on low-carbon steel substrates via photo-assisted electrodeposition.A systematic investigation was conducted on the effects of cerium ion concentration and nano-ceria(CeO_(2))particle content in the electrolyte on the coating properties,along with an analysis of the temporal evolution of coating’s corrosion resistance.When the cerium ion concentration in the electrolyte was 0.05 mol/L,the coating exhibited a uniform black appearance with a light absorption rate of 95%,an emissivity of 0.87,maximum impedance,and the lowest corrosion tendency,demonstrating optimal comprehensive performance.The coating prepared with a nano-ceria concentration of 6 g/L in the electrolyte exhibited an emissivity of 0.9,achieved a 5B adhesion grade(ASTM D3359-09),and demonstrated a one-order-of-magnitude reduction in corrosion current density compared to coatings fabricated without nano-ceria in the electrolyte.With prolonged storage time,the coating's impedance slightly increased,leading to improved corrosion resistance.展开更多
Carbon fiber-reinforced carbon aerogel(C/CA)composites are one of the most promising candidates for applications requiring both thermal insulation and load bearing capabilities.The preparation of anti-oxidation coatin...Carbon fiber-reinforced carbon aerogel(C/CA)composites are one of the most promising candidates for applications requiring both thermal insulation and load bearing capabilities.The preparation of anti-oxidation coatings on C/CA to address its susceptibility to oxidation is a feasible approach to promote its application in oxidative environments.However,the currently reported coatings on C/CA mainly focus on improving the ablation performance and coating preparation process typically necessitating high-temperature heat treatment.This procedure can increase its thermal conductivity and reduce its thermal insulation ability.In this study,a series of ceramic-resin coatings were fabricated on C/CA through a simple slurry brushing-drying approach at room temperature.The effects of phenolic resin content on the coating structure,residual stress,thermal shock,and oxidation behaviors were investigated.Due to the adhesive properties and curing-induced shrinkage,the PR-7.5 coating(containing 7.5%(in mass)phenolic resin in the slurry)exhibits bonding strength close to fracture strength of the substrate and residual compressive stress of 0.853 GPa,which is beneficial for resisting thermal shock cracking.However,excessive resin content(PR-10.0 containing 10.0%(in mass)phenolic resin in the slurry)induces tensile stress due to uneven curing shrinkage,thereby leading to thermal shock cracking.Meanwhile,oxidation tests reveal significantly reduced weight losses for PR-7.5(17.46%at 800℃/100 min,8.15%at 1000℃/120 min,3.15%at 1200℃/120 min)versus uncoated C/CA’s 44.60%loss at 800℃/20 min.This work provides a brand-new and simple approach to improving the anti-oxidation performance of C/CA and expands its application in mild oxidative environments.展开更多
To mitigate the impact of interdiffusion reactions between the silicide slurry and Ta12W alloy substrate during vacuum sintering process on the oxidation resistance of the silicide coating,a micro-arc oxidation pretre...To mitigate the impact of interdiffusion reactions between the silicide slurry and Ta12W alloy substrate during vacuum sintering process on the oxidation resistance of the silicide coating,a micro-arc oxidation pretreatment was employed to construct a Ta_(2)O_(5)ceramic layer on the Ta12W alloy surface.Subsequently,a slurry spraying-vacuum sintering method was used to prepare a Si-Cr-Ti-Zr coating on the pretreated substrate.Comparative studies were conducted on the microstructure,phase composition,and isothermal oxidation resistance(at 1600℃)of the as-prepared coatings with and without the micro-arc oxidation ceramic layer.The results show that the Ta_(2)O_(5)layer prepared at 400 V is more continuous and has smaller pores than that prepared at 350 V.After microarc oxidation pretreatment,the Si-Cr-Ti-Zr coating on Ta12W alloy consists of three distinct layers:an upper layer dominated by Ti_(5)Si_(3),Ta_(5)Si_(3),and ZrSi;a middle layer dominated by TaSi_(2);a coating/substrate interfacial reaction layer dominated by Ta_(5)Si_(3).Both the Si-Cr-Ti-Zr coatings with and without the Ta_(2)O_(5)ceramic layer do not fail after isothermal oxidation at 1600℃for 5 h.Notably,the addition of the Ta2O5 ceramic layer reduces the high-temperature oxidation rate of the coating.展开更多
Platinum group metals have high melting points,strong corrosion resistance,stable chemical properties,and low oxygen permeability in high-temperature oxygen-containing environments.As thermal protective coating materi...Platinum group metals have high melting points,strong corrosion resistance,stable chemical properties,and low oxygen permeability in high-temperature oxygen-containing environments.As thermal protective coating materials,they have gained essential applications in the aerospace field and have excellent prospects for application in frontier military fields,such as protecting hot-end components of hypersonic aircraft.This research reviewed the latest research progress of platinum group metal coatings with hightemperature oxidation resistance,including coating preparation techniques,oxidation failure,and alloying modification.The leading preparation techniques of current platinum group metal coatings were discussed,as well as the advantages and disadvantages of various existing preparation techniques.Besides,the intrinsic properties,failure forms,and failure mechanisms of coatings of single platinum group metal in high-temperature oxygen-containing environments were analyzed.On this basis,the necessity,main methods,and main achievements of alloying modification of platinum group metals were summarized.Finally,the future development of platinum group coatings with high-temperature oxidation resistance was discussed and prospected.展开更多
Nanoporous polymers are extensively coated on various substrates to deliver optical,permselective,or other functions.However,it remains desired to fast produce uniform nanoporous polymer coatings on substrates with co...Nanoporous polymers are extensively coated on various substrates to deliver optical,permselective,or other functions.However,it remains desired to fast produce uniform nanoporous polymer coatings on substrates with complex surfaces.Herein,by manipulating the interactions between block copolymers and selective solvents,we prepare repairable nanoporous polymers on arbitrary substrates.This is realized by an extremely simple sequential coating process:sequential coating of block copolymers and their swelling agents on substrate surfaces.The swelling agents are comprised of two solvents that swell the constituent blocks of the copolymers to different degrees,rapidly producing polymer coatings with uniform,interconnected,sub-50 nm pores.This sequential coating process is able to conformally build nanoporous polymers on nonplanar substrates with large lateral sizes and complex surface features,and also to in situ repair defects arising during usages.We further demonstrate that the nanoporous coatings show excellent antireflective and membrane separation performances.This sequential coating process is dictated by polymer–solvent interactions,and is expected to find applications in diverse fields for its simplicity,adaptability,and the capability to produce well-defined nanoporosities.展开更多
An advanced AlCrSiN/AlCrN/CrN/Cr multilayer coating was developed via hybrid multiarc ion plating and high-power impulse magnetron sputtering.The multilayer design enhanced the substrate-coating compatibility,achievin...An advanced AlCrSiN/AlCrN/CrN/Cr multilayer coating was developed via hybrid multiarc ion plating and high-power impulse magnetron sputtering.The multilayer design enhanced the substrate-coating compatibility,achieving a critical load of 87.8 N.Silicon doping induced nanocrystallization and amorphization,increasing the hardness to 26 GPa.At high temperatures,a nanoscale Cr-rich(Cr,Al)_(2)O_(3) layer was formed,effectively inhibiting oxygen diffusion.The coating underwent unique phase transformations,during which Cr_(2)N and amorphous Si3N4 were converted into dispersed SiCr_(3) nanoparticles,which stabilized Cr atoms and suppressed their outward diffusion.Ab initio molecular dynamics simulations revealed that Cr atoms exhibited higher chemical activity and oxygen-capture capability than Al atoms and Si atoms served as diffusion barriers by pinning onto the oxidized surface,considerably improving the oxidation resistance of the coating.展开更多
The high-temperature interaction of nanostructured Lu_(2)Si_(2)O_(7) environmental barrier coatings(EBCs)with calcium-magnesium-aluminosilicate(CMAS)was investigated at 1400℃ for 1,10,25,and 50 h to evaluate the coat...The high-temperature interaction of nanostructured Lu_(2)Si_(2)O_(7) environmental barrier coatings(EBCs)with calcium-magnesium-aluminosilicate(CMAS)was investigated at 1400℃ for 1,10,25,and 50 h to evaluate the coating’s resistance to CMAS corrosion.The results indicate a phase transformation over time,transitioning from Ca_(2)Lu_(8)(SiO_(4))6O_(2) apatite and Lu_(2)Si_(2)O_(7) to solely Lu_(2)Si_(2)O_(7).The interaction of the Lu_(2)Si_(2)O_(7) coating with the CMAS melts was divided into three stages based on the corrosion reaction behavior.The delamination cracks were distributed throughout the interface between the Si bond layer and Lu_(2)Si_(2)O_(7) layer after corroded at 1400℃ for 50 h,signifying coating failure.In addition,the influence of monosilicates,disilicates,and corrosion duration on the recession layer thickness was analyzed by comparing previous reports on RE_(2)SiO_(5)/RE_(2)Si_(2)O_(7) coatings(RE=Gd,Yb,Lu,Er).Furthermore,the variation in the thermally grown oxide layer thickness in CMAS-corroded Lu_(2)Si_(2)O_(7) coatings was systematically investigated.展开更多
Dual-layer thermal barrier coatings(TBCs)with ultrahigh temperature resistance were prepared on the surface of molybdenum-rhenium alloy hot-end components.The preparation of the MoSi_(2)-Gd_(2)Zr_(2)O_(7)dual-layer TB...Dual-layer thermal barrier coatings(TBCs)with ultrahigh temperature resistance were prepared on the surface of molybdenum-rhenium alloy hot-end components.The preparation of the MoSi_(2)-Gd_(2)Zr_(2)O_(7)dual-layer TBCs was designed based on the coefficient of thermal expansion and the coating functionality,and it was completed using atmospheric plasma spraying technique.The microstructure,mechanical properties,and thermal properties were analyzed.Results indicate that the adhesion of the prepared dual-layer composite TBCs is excellent,and no noticeable cracks appear at the interface.Compared with the MoSi_(2)coating with a low fracture toughness(0.88 MPa·m^(1/2)),the Gd_(2)Zr_(2)O_(7)coating exhibits higher fracture toughness(1.74 MPa·m^(1/2))and stronger resistance to crack propagation.The prepared MoSi_(2)-Gd_(2)Zr_(2)O_(7)composite coatings have a high porosity(39%),low thermal conductivity(1.020 W·(m·K)^(−1),1200℃),and low thermal diffusivity(0.249 mm^(2)/s,1200℃).Additionally,they possess a high oxygen-vacancy concentration,which ensures excellent insulation performance.展开更多
TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing Ti...TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing TiB_(2)coatings have disadvantages such as high equipment costs,complicated processes,and highly toxic gas emissions.This paper proposes an environmentally friendly method,which requires inexpensive equipment and simple processing,for preparing TiB_(2)coating on molybdenum via electrophoretic deposition within Na3AlF6-based molten salts.The produced TiB_(2)layer had an approximate thickness of 60μm and exhibited high density,outstanding hardness(38.2 GPa)and robust adhesion strength(51 N).Additionally,high-temperature oxidation experiments revealed that,at900℃,the TiB_(2)coating provided effective protection to the molybdenum substrate against oxidation for 3 h.This result indicates that the TiB_(2)coating prepared on molybdenum using molten salt electrophoretic deposition possesses good high-temperature oxidation resistance.展开更多
When micro/nano-scale gradient coatings are subject to large thermal gradients or high heat fluxes,the spatial size effect cannot be ignored.It is important to understand how the size effect influences the thermal fra...When micro/nano-scale gradient coatings are subject to large thermal gradients or high heat fluxes,the spatial size effect cannot be ignored.It is important to understand how the size effect influences the thermal fracture behavior of functionally graded coating/substrate structures.This study aims at analyzing the transient thermal fracture behavior of collinear interface cracks in functionally graded coating/substrate structures based on the nonlocal dual-phase-lag heat conduction model.By means of integral transform techniques,the mixed boundary problem is transformed into a set of singular integral equations,which are solved by the Chebyshev polynomials.The effects of the nonlocal parameter,coating thickness,crack spacing,and non-homogeneous parameters on the temperature and stress intensity factors(SIFs)are examined.The numerical results show that these parameters play an essential role in controlling the thermal fracture behavior of the structures,especially at micro/nano-scales.展开更多
Waterborne acrylic coatings are widely utilized due to their cost-effectiveness,high transparency,strong resistance to weather and chemicals,impressive mechanical properties,and excellent adhesion to various substrate...Waterborne acrylic coatings are widely utilized due to their cost-effectiveness,high transparency,strong resistance to weather and chemicals,impressive mechanical properties,and excellent adhesion to various substrates.In these coatings,a reactive emulsifier containing phosphate groups can be integrated into the molecular chain during polymerization,which enhances the coating's compactness and corrosion resistance.This work focuses on the synthesis of styrene-butyl acrylate(St-BA)latex and methyl methacrylate-butyl acrylate(MMA-BA)latex using the reactive phosphate emulsifier ANPEO_(10)-P_(1) through seed emulsion polymerization,achieving a conversion rate of approximately 99%and a solid content close to 50%.The resulting coatings from St-BA and MMA-BA latexes demonstrated long-term corrosion protection for carbon steel and aluminum alloy due to in-situ phosphatization,effectively preventing flash rust.Notably,the MMA-BA coating exhibited remarkable durability,enduring immersion for up to 1224 h(51 d)on Q 235 carbon steel before reaching the failure threshold(|Z|0.01 Hz£106Ω·cm^(2))on Q 235 carbon steel.On 5052 aluminum alloy,the St-BA coating maintained|Z|0.01 Hz>10^(8)Ω·cm^(2) for 480 h(20 d).Furthermore,the corrosion resistance of St-BA and MMA BA coatings on Q 235 steel sheet and 5052 aluminum alloy surpassed that of commercially available MMA-BA and St BA coatings after immersion in a 3.5 wt%NaCl aqueous solution.This work also delves into the anticorrosion mechanism of MMA-BA and St-BA coatings.展开更多
The Sn−2Al filler metal was utilized to bond W90 tungsten heavy alloys by the ultrasonic-assisted coating technology in atmospheric environment at 250℃.The effects of ultrasonic power and ultrasonic time on microstru...The Sn−2Al filler metal was utilized to bond W90 tungsten heavy alloys by the ultrasonic-assisted coating technology in atmospheric environment at 250℃.The effects of ultrasonic power and ultrasonic time on microstructure and interfacial strength of Sn−2Al/W90 interface were investigated.The ultrasound improved the wettability of Sn−2Al filler metal on W90 surface.As the ultrasonic power increased and ultrasonic time increased,the size of Al phase in seam decreased.The maximum value of Sn−2Al/W90 interfacial strength reached 30.1 MPa.Based on the acoustic pressure simulation and bubble dynamics,the intensity of cavitation effect was proportional to ultrasonic power.The generated high temperature and high pressure by cavitation effect reached 83799.6 K and 1.26×10^(14) Pa,respectively.展开更多
Polymer nanocomposite coatings(PNCCs)are unprecedented generation of coatings engineered for displaying inexpensive and brilliant functional surface coatings with eminent corrosion guard,mechanical resistance,antimicr...Polymer nanocomposite coatings(PNCCs)are unprecedented generation of coatings engineered for displaying inexpensive and brilliant functional surface coatings with eminent corrosion guard,mechanical resistance,antimicrobial,chemical durability,electrical insulation,and UV aging features.Due to their widely anticipation in petroleum,applications in building,conveyance,aerospace,electronics,automobiles and energy,these multi-functional coatings have a tremendous leverage in human life,all technological and scientific subjects.Numerous applications have been made for multilateral polymers like polyurethane(PU),epoxy(EP),polyaniline(PANI)conductive polymer,polypyrrole(PPy),and etc,on various metallic surfaces especially,carbon steel substrate owing to their excellent resistance properties.Practically,nanomaterials can possess potential in the all-interdisciplinary domains of materials science and engineering,chemical and physical sciences,biological and health sciences.As known,the designed polymer nanocomposite coating paradigm is fundamentally constituted from polymer or resin as a vehicle and inorganic nanofillers(nanoparticles and nanocomposites).Some commercialized and excessively employed nanocontainers in polymer nanocomposite coating formulations,like ZnO,TiO_(2),carbon nanotubes(CNTs),clay,SiO_(2),Al_(2)O_(3),graphene,GO,CeO_(2),ZrO_(2),FeTiO_(3),etc were discussed.The current review covered the chemistry and potential applications of the largest utilized multifunctional polymer nanocomposite coatings such as EP,PU and other considerable PNCCs.Lately,a titanic attention was made for epoxy nanocomposites because of their distinct physicochemical characteristics,which result from the combined qualities of the nanoparticles and polymer material unity.In addition,the author incorporated some of his scientific contributions in this area represented in construction of innovative functional polymer nanocomposites for a variety of uses with high economic,industrial impacts and future orientation.Furthermore,some newly published applications of polymer nanocomposite coatings were incorporated and discussed.展开更多
Aluminum-based composite abradable seal coatings are pivotal to improving the efficiency of aero engines or gas turbines.However,the adhesive transfer frequently occurs between metallic blade tips and aluminum-based c...Aluminum-based composite abradable seal coatings are pivotal to improving the efficiency of aero engines or gas turbines.However,the adhesive transfer frequently occurs between metallic blade tips and aluminum-based composite coatings,resulting in engine vibration and even jam.Many past studies had tried to solve this problem by reducing coating hardness,improving lubrication,or strengthening blade tips,but all had failed.In this paper,we proposed a novel epoxy-based composite abradable seal coating,eliminating adhesive transfer by changing metal-to-metal scraping pair to metal-to-polymer scraping pair.The coating was developed via a hierarchical structure design.Large spherical pores were uniformly distributed in the continuous epoxy matrix with fine graphite dispersion.By adding 20 vol.%graphite and 50 vol.%hollow microspheres,a self-lubricating epoxy-based coating of 0.26 friction coefficient with thermal conductivity of 0.28 W/(m·K),coating HR15 Y hardness at 54.8,and bonding strength at 18.7 MPa can be reached.When the metallic blades scrape the epoxy-based composite coating,no adhesive transfer occurs.Besides,a smooth scraped surface is formed by pseudoplastic deformation.This epoxy-based composite abradable seal coating opens a new way to improve the efficiency and reliable operations of air engine compressors.展开更多
The combined micro arc oxidation （MAO） and a hybrid beam deposition process was used to deposit duplex （Si：N）-DLC/MAO coatings on AZ80 magnesium alloy. The microstructure and composition of the duplex coatings we...The combined micro arc oxidation （MAO） and a hybrid beam deposition process was used to deposit duplex （Si：N）-DLC/MAO coatings on AZ80 magnesium alloy. The microstructure and composition of the duplex coatings were analyzed by Raman spectroscopy, X-ray photoelectron spectroscope （XPS）, scanning electron microscope （SEM） and atomic force microscopy （AFM）. Tribological behaviors of the coatings were studied by ball-on-disk friction test. It was found that the ID/IG ratio of the （Si：N）-DLC （diamond-like carbon） top films increases with decreasing C2H2/N2 ratio. The （Si：N）-DLC top film with SigN4 was formed on the MAO coated sample as the C2H2/N2 ratio was 10sccm：5sccm, which showed an increasing critical load compared with the pure DLC directly deposited on the Mg alloy substrate. As a result, the （Si：N）-DLC/MAO coating exhibited an advanced wear protection for the substrate.展开更多
To improve the mechanical properties of self-lubricating chromium vanadium nitride （CrVN） coatings, va- nadium nitride （VN） is combined with CrVN to form multilayered CrVN/VN coatings through an in-line magnetron ...To improve the mechanical properties of self-lubricating chromium vanadium nitride （CrVN） coatings, va- nadium nitride （VN） is combined with CrVN to form multilayered CrVN/VN coatings through an in-line magnetron sputtering system. The strengthening effect of the period thickness on the mechanical and tribological properties is studied. X-ray diffractometer, low-angle X-ray reflectivity, scanning electron microscopy, atomic force microscopy, electron probe micro-analyzer and X-ray photoelectron spectroscopy are employed to characterize the microstructures and chemical composition. Nanoindentation and ball-on-disc tribo-tester are used in characterization of the mechanical and tribological properties. The CrVN/VN multilayer coatings demonstrate good lubrication property with coefficient of friction down to 0.23. Multilayering with VN, the hardness of CrVN jumps to 27.6 GPa with period thickness of 6 nm, which has an improvement of 5.1 GPa compared with that of 22.5 GPa from rule-of-mixture.展开更多
Ni-based submicron WS2/CaF2 self-lubricating composite coatings were produced on carbon steel substrate by high velocity oxygen fuel(HVOF) spray processing, and the microstructure and mechanical properties of the coat...Ni-based submicron WS2/CaF2 self-lubricating composite coatings were produced on carbon steel substrate by high velocity oxygen fuel(HVOF) spray processing, and the microstructure and mechanical properties of the coatings were investigated. Non-uniform microstructure characterized by some pores and microcracks is observed in the produced composite coatings, which leads to low microhardness value, low adhesive strength and low frictional coefficient. For Ni45-5%CaF2-10%WS2 (mass fraction) and Ni45-10%CaF2-5%WS2 (mass fraction) coatings, under the test condition of load 40 N and speed 2 m/s, the friction coefficients obtained at room temperature are in the range of 0.35-0.48 and 0.31-0.41, respectively. The friction coefficients of two kinds of coatings increase to 0.4-0.63 and 0.35-0.46, respectively, at the test speed of 1 m/s. And the Ni45-10%CaF2-5%WS2 coating presents the minimum friction coefficient of 0.32-0.38 and good anti-wear properties at 400 ℃.展开更多
基金the International Science and Technology Cooperation Program of China(No.2015DFR51090)the National Program on Key Research Project of China(No.2016YFE0111400)。
文摘A nickel alloy matrix high-temperature self-lubricating coating(77.5 wt%(Ni-Cr-Mo-Al)-12.5 wt%Ag-10 wt%BaF2/CaF2)was prepared by plasma spraying technique.Results show that the Vickers microhardness of coating is(2.9±0.5)GPa,and the average bonding strength is about(35.6±0.5)MPa.The coating rubbing against Inconel 718 superalloy pin exhibits superior tribological performance with coefficient of friction(COF)of below 0.25 and wear rate of 8.2×10^(-5)-15.2×10^(-5)mm^(3)·N^(-1)·m^(-1)at a wide temperature range from 25 to 800℃,and the COF and the wear rate are slightly reduced with temperature increasing.The low COF and wear rate were attributed to the synergistic effects of Ag,BaF_(2)/CaF_(2),Ag2MoO_(4)and BaMoO_(4).
基金This is supported by the Youth Research Fund of Chinese Academy of Sciences
文摘The effect of cerium dioxide(CeO_2)as an additive on the structure and properties of a melting type coating has been studied by means of microhardness measurement,scanning electron microscopy and thermal analysis. The results show that cerium dioxide can modify the microstructure and tribological properties of the coating. Model LIC-23 composite coating which contains CeO_2 performs well as a self-lubricating coating in hydrochloric acid solution.
基金financially supported by the National Natural Science Foundation of China (No. 51301153)the National Undergraduate Training Programs for Innovation and Entrepreneurship of China (201410345022)
文摘The objective of this research was to develop a novel self-lubricating coating on an AA6061 aluminum alloy.Three coatings were prepared by the plasma electrolytic oxidation（PEO） process using 50-, 500-, and 1000-Hz pulsed direct current, respectively. The as-deposited coatings were then post-treated using two different methods, viz., ultrasonic vibration-aided vacuum oil impregnation（UVOI） and oil impregnation under ambient pressure（OIAP）. After posttreatment, an oil-containing, self-lubricating top layer was formed on the coatings. The effects of the coatings＇ surface morphologies and structures on their oil-holding capabilities were discussed. The results revealed that coatings prepared with higher frequency had a greater oil-holding capacity using OIAP post-treatment, while those prepared with lower frequency had a greater oil-containing capability using UVOI post-treatment. These phenomena are related to the morphologies of the coatings produced with various current modes. The tribological properties of the coatings before and after post-treatments were investigated by pin-on-disc sliding wear tests. Due to the formation of a lubricant-containing top layer, the post-treatment coatings had a lower friction coefficient and improved wear resistance compared with the asdeposited coatings. In addition, the coatings after UVOI treatment had better wear performance than those post-treated using the OIAP process. Among all coatings, the coating produced with a 50-Hz pulsed current followed by UVOI posttreatment achieved the lowest friction coefficient（0.03） and best wear resistance when sliding against a Si3N4 ceramic counterface. This study indicates that a novel self-lubricating coating can be prepared by a PEO process combined with vacuum oil impregnation post-treatment.
文摘Black nickel coatings have emerged as a research hotspot in materials science due to their excellent performance and broad application prospects.In this study,nickel-based black coatings were fabricated on low-carbon steel substrates via photo-assisted electrodeposition.A systematic investigation was conducted on the effects of cerium ion concentration and nano-ceria(CeO_(2))particle content in the electrolyte on the coating properties,along with an analysis of the temporal evolution of coating’s corrosion resistance.When the cerium ion concentration in the electrolyte was 0.05 mol/L,the coating exhibited a uniform black appearance with a light absorption rate of 95%,an emissivity of 0.87,maximum impedance,and the lowest corrosion tendency,demonstrating optimal comprehensive performance.The coating prepared with a nano-ceria concentration of 6 g/L in the electrolyte exhibited an emissivity of 0.9,achieved a 5B adhesion grade(ASTM D3359-09),and demonstrated a one-order-of-magnitude reduction in corrosion current density compared to coatings fabricated without nano-ceria in the electrolyte.With prolonged storage time,the coating's impedance slightly increased,leading to improved corrosion resistance.
基金National Natural Science Foundation of China(52272075,52472053)Research Fund of Youth Innovation Promotion Association of CAS,China(2021190)Defense Industrial Technology Development Program(JCKY2021130B007)。
文摘Carbon fiber-reinforced carbon aerogel(C/CA)composites are one of the most promising candidates for applications requiring both thermal insulation and load bearing capabilities.The preparation of anti-oxidation coatings on C/CA to address its susceptibility to oxidation is a feasible approach to promote its application in oxidative environments.However,the currently reported coatings on C/CA mainly focus on improving the ablation performance and coating preparation process typically necessitating high-temperature heat treatment.This procedure can increase its thermal conductivity and reduce its thermal insulation ability.In this study,a series of ceramic-resin coatings were fabricated on C/CA through a simple slurry brushing-drying approach at room temperature.The effects of phenolic resin content on the coating structure,residual stress,thermal shock,and oxidation behaviors were investigated.Due to the adhesive properties and curing-induced shrinkage,the PR-7.5 coating(containing 7.5%(in mass)phenolic resin in the slurry)exhibits bonding strength close to fracture strength of the substrate and residual compressive stress of 0.853 GPa,which is beneficial for resisting thermal shock cracking.However,excessive resin content(PR-10.0 containing 10.0%(in mass)phenolic resin in the slurry)induces tensile stress due to uneven curing shrinkage,thereby leading to thermal shock cracking.Meanwhile,oxidation tests reveal significantly reduced weight losses for PR-7.5(17.46%at 800℃/100 min,8.15%at 1000℃/120 min,3.15%at 1200℃/120 min)versus uncoated C/CA’s 44.60%loss at 800℃/20 min.This work provides a brand-new and simple approach to improving the anti-oxidation performance of C/CA and expands its application in mild oxidative environments.
基金National Natural Science Foundation of China(52071274)Key Research and Development Projects of Shaanxi Province(2023-YBGY-442)Science and Technology Nova Project-Innovative Talent Promotion Program of Shaanxi Province(2020KJXX-062)。
文摘To mitigate the impact of interdiffusion reactions between the silicide slurry and Ta12W alloy substrate during vacuum sintering process on the oxidation resistance of the silicide coating,a micro-arc oxidation pretreatment was employed to construct a Ta_(2)O_(5)ceramic layer on the Ta12W alloy surface.Subsequently,a slurry spraying-vacuum sintering method was used to prepare a Si-Cr-Ti-Zr coating on the pretreated substrate.Comparative studies were conducted on the microstructure,phase composition,and isothermal oxidation resistance(at 1600℃)of the as-prepared coatings with and without the micro-arc oxidation ceramic layer.The results show that the Ta_(2)O_(5)layer prepared at 400 V is more continuous and has smaller pores than that prepared at 350 V.After microarc oxidation pretreatment,the Si-Cr-Ti-Zr coating on Ta12W alloy consists of three distinct layers:an upper layer dominated by Ti_(5)Si_(3),Ta_(5)Si_(3),and ZrSi;a middle layer dominated by TaSi_(2);a coating/substrate interfacial reaction layer dominated by Ta_(5)Si_(3).Both the Si-Cr-Ti-Zr coatings with and without the Ta_(2)O_(5)ceramic layer do not fail after isothermal oxidation at 1600℃for 5 h.Notably,the addition of the Ta2O5 ceramic layer reduces the high-temperature oxidation rate of the coating.
文摘Platinum group metals have high melting points,strong corrosion resistance,stable chemical properties,and low oxygen permeability in high-temperature oxygen-containing environments.As thermal protective coating materials,they have gained essential applications in the aerospace field and have excellent prospects for application in frontier military fields,such as protecting hot-end components of hypersonic aircraft.This research reviewed the latest research progress of platinum group metal coatings with hightemperature oxidation resistance,including coating preparation techniques,oxidation failure,and alloying modification.The leading preparation techniques of current platinum group metal coatings were discussed,as well as the advantages and disadvantages of various existing preparation techniques.Besides,the intrinsic properties,failure forms,and failure mechanisms of coatings of single platinum group metal in high-temperature oxygen-containing environments were analyzed.On this basis,the necessity,main methods,and main achievements of alloying modification of platinum group metals were summarized.Finally,the future development of platinum group coatings with high-temperature oxidation resistance was discussed and prospected.
基金support from National Science Foundation of China(22438005)the Natural Science Foundation of Jiangsu Province(BE2022056-3)is gratefully acknowledged.
文摘Nanoporous polymers are extensively coated on various substrates to deliver optical,permselective,or other functions.However,it remains desired to fast produce uniform nanoporous polymer coatings on substrates with complex surfaces.Herein,by manipulating the interactions between block copolymers and selective solvents,we prepare repairable nanoporous polymers on arbitrary substrates.This is realized by an extremely simple sequential coating process:sequential coating of block copolymers and their swelling agents on substrate surfaces.The swelling agents are comprised of two solvents that swell the constituent blocks of the copolymers to different degrees,rapidly producing polymer coatings with uniform,interconnected,sub-50 nm pores.This sequential coating process is able to conformally build nanoporous polymers on nonplanar substrates with large lateral sizes and complex surface features,and also to in situ repair defects arising during usages.We further demonstrate that the nanoporous coatings show excellent antireflective and membrane separation performances.This sequential coating process is dictated by polymer–solvent interactions,and is expected to find applications in diverse fields for its simplicity,adaptability,and the capability to produce well-defined nanoporosities.
基金financially supported by the National Science and Technology Major Project(No.2024ZD1404705)。
文摘An advanced AlCrSiN/AlCrN/CrN/Cr multilayer coating was developed via hybrid multiarc ion plating and high-power impulse magnetron sputtering.The multilayer design enhanced the substrate-coating compatibility,achieving a critical load of 87.8 N.Silicon doping induced nanocrystallization and amorphization,increasing the hardness to 26 GPa.At high temperatures,a nanoscale Cr-rich(Cr,Al)_(2)O_(3) layer was formed,effectively inhibiting oxygen diffusion.The coating underwent unique phase transformations,during which Cr_(2)N and amorphous Si3N4 were converted into dispersed SiCr_(3) nanoparticles,which stabilized Cr atoms and suppressed their outward diffusion.Ab initio molecular dynamics simulations revealed that Cr atoms exhibited higher chemical activity and oxygen-capture capability than Al atoms and Si atoms served as diffusion barriers by pinning onto the oxidized surface,considerably improving the oxidation resistance of the coating.
基金supported by the National Science and Technology Major Project of China(No.2017-VI-0020-0093).
文摘The high-temperature interaction of nanostructured Lu_(2)Si_(2)O_(7) environmental barrier coatings(EBCs)with calcium-magnesium-aluminosilicate(CMAS)was investigated at 1400℃ for 1,10,25,and 50 h to evaluate the coating’s resistance to CMAS corrosion.The results indicate a phase transformation over time,transitioning from Ca_(2)Lu_(8)(SiO_(4))6O_(2) apatite and Lu_(2)Si_(2)O_(7) to solely Lu_(2)Si_(2)O_(7).The interaction of the Lu_(2)Si_(2)O_(7) coating with the CMAS melts was divided into three stages based on the corrosion reaction behavior.The delamination cracks were distributed throughout the interface between the Si bond layer and Lu_(2)Si_(2)O_(7) layer after corroded at 1400℃ for 50 h,signifying coating failure.In addition,the influence of monosilicates,disilicates,and corrosion duration on the recession layer thickness was analyzed by comparing previous reports on RE_(2)SiO_(5)/RE_(2)Si_(2)O_(7) coatings(RE=Gd,Yb,Lu,Er).Furthermore,the variation in the thermally grown oxide layer thickness in CMAS-corroded Lu_(2)Si_(2)O_(7) coatings was systematically investigated.
基金Supported by Scientific and Technological Innovation of Shaanxi Provincial State-Owned Capital Operation Budget(2022-056)Institute's Self-Developed Technology Program(0801YK2317)+4 种基金Qin Chuangyuan Cites High-Level Innovation and Entrepreneurship Talent Program(QCYRCXM-2023-120)Qin Chuangyuan Industry Cluster Zone“Four Chains”Integration Program(2024CY-JJQ-46)National Natural Science Foundation of China(52071274)Key Research and Development Projects of Shaanxi Province(2023-YBGY-442)Science and Technology Nova Project-Innovative Talent Promotion Program of Shaanxi Province(2020KJXX-062)。
文摘Dual-layer thermal barrier coatings(TBCs)with ultrahigh temperature resistance were prepared on the surface of molybdenum-rhenium alloy hot-end components.The preparation of the MoSi_(2)-Gd_(2)Zr_(2)O_(7)dual-layer TBCs was designed based on the coefficient of thermal expansion and the coating functionality,and it was completed using atmospheric plasma spraying technique.The microstructure,mechanical properties,and thermal properties were analyzed.Results indicate that the adhesion of the prepared dual-layer composite TBCs is excellent,and no noticeable cracks appear at the interface.Compared with the MoSi_(2)coating with a low fracture toughness(0.88 MPa·m^(1/2)),the Gd_(2)Zr_(2)O_(7)coating exhibits higher fracture toughness(1.74 MPa·m^(1/2))and stronger resistance to crack propagation.The prepared MoSi_(2)-Gd_(2)Zr_(2)O_(7)composite coatings have a high porosity(39%),low thermal conductivity(1.020 W·(m·K)^(−1),1200℃),and low thermal diffusivity(0.249 mm^(2)/s,1200℃).Additionally,they possess a high oxygen-vacancy concentration,which ensures excellent insulation performance.
基金supported by the Original Exploratory Program of the National Natural Science Foundation of China(No.52450012)。
文摘TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing TiB_(2)coatings have disadvantages such as high equipment costs,complicated processes,and highly toxic gas emissions.This paper proposes an environmentally friendly method,which requires inexpensive equipment and simple processing,for preparing TiB_(2)coating on molybdenum via electrophoretic deposition within Na3AlF6-based molten salts.The produced TiB_(2)layer had an approximate thickness of 60μm and exhibited high density,outstanding hardness(38.2 GPa)and robust adhesion strength(51 N).Additionally,high-temperature oxidation experiments revealed that,at900℃,the TiB_(2)coating provided effective protection to the molybdenum substrate against oxidation for 3 h.This result indicates that the TiB_(2)coating prepared on molybdenum using molten salt electrophoretic deposition possesses good high-temperature oxidation resistance.
基金Project supported by the Natural Science Foundation of Shandong Province of China(No.ZR2024MA085)the Fundamental Research Funds for Central Universities of China(No.27RA2515008)。
文摘When micro/nano-scale gradient coatings are subject to large thermal gradients or high heat fluxes,the spatial size effect cannot be ignored.It is important to understand how the size effect influences the thermal fracture behavior of functionally graded coating/substrate structures.This study aims at analyzing the transient thermal fracture behavior of collinear interface cracks in functionally graded coating/substrate structures based on the nonlocal dual-phase-lag heat conduction model.By means of integral transform techniques,the mixed boundary problem is transformed into a set of singular integral equations,which are solved by the Chebyshev polynomials.The effects of the nonlocal parameter,coating thickness,crack spacing,and non-homogeneous parameters on the temperature and stress intensity factors(SIFs)are examined.The numerical results show that these parameters play an essential role in controlling the thermal fracture behavior of the structures,especially at micro/nano-scales.
基金Project(52373065)supported by the National Natural Science Foundation of ChinaProject(2220004002898)supported by the Zhuhai Industry University Research Cooperation and Basic and Applied Research Projects,China。
文摘Waterborne acrylic coatings are widely utilized due to their cost-effectiveness,high transparency,strong resistance to weather and chemicals,impressive mechanical properties,and excellent adhesion to various substrates.In these coatings,a reactive emulsifier containing phosphate groups can be integrated into the molecular chain during polymerization,which enhances the coating's compactness and corrosion resistance.This work focuses on the synthesis of styrene-butyl acrylate(St-BA)latex and methyl methacrylate-butyl acrylate(MMA-BA)latex using the reactive phosphate emulsifier ANPEO_(10)-P_(1) through seed emulsion polymerization,achieving a conversion rate of approximately 99%and a solid content close to 50%.The resulting coatings from St-BA and MMA-BA latexes demonstrated long-term corrosion protection for carbon steel and aluminum alloy due to in-situ phosphatization,effectively preventing flash rust.Notably,the MMA-BA coating exhibited remarkable durability,enduring immersion for up to 1224 h(51 d)on Q 235 carbon steel before reaching the failure threshold(|Z|0.01 Hz£106Ω·cm^(2))on Q 235 carbon steel.On 5052 aluminum alloy,the St-BA coating maintained|Z|0.01 Hz>10^(8)Ω·cm^(2) for 480 h(20 d).Furthermore,the corrosion resistance of St-BA and MMA BA coatings on Q 235 steel sheet and 5052 aluminum alloy surpassed that of commercially available MMA-BA and St BA coatings after immersion in a 3.5 wt%NaCl aqueous solution.This work also delves into the anticorrosion mechanism of MMA-BA and St-BA coatings.
基金supported by the National Natural Science Foundation of China(Nos.52105330,52175307)the Natural Science Foundation of Shandong Province,China(No.ZR2023JQ021)。
文摘The Sn−2Al filler metal was utilized to bond W90 tungsten heavy alloys by the ultrasonic-assisted coating technology in atmospheric environment at 250℃.The effects of ultrasonic power and ultrasonic time on microstructure and interfacial strength of Sn−2Al/W90 interface were investigated.The ultrasound improved the wettability of Sn−2Al filler metal on W90 surface.As the ultrasonic power increased and ultrasonic time increased,the size of Al phase in seam decreased.The maximum value of Sn−2Al/W90 interfacial strength reached 30.1 MPa.Based on the acoustic pressure simulation and bubble dynamics,the intensity of cavitation effect was proportional to ultrasonic power.The generated high temperature and high pressure by cavitation effect reached 83799.6 K and 1.26×10^(14) Pa,respectively.
文摘Polymer nanocomposite coatings(PNCCs)are unprecedented generation of coatings engineered for displaying inexpensive and brilliant functional surface coatings with eminent corrosion guard,mechanical resistance,antimicrobial,chemical durability,electrical insulation,and UV aging features.Due to their widely anticipation in petroleum,applications in building,conveyance,aerospace,electronics,automobiles and energy,these multi-functional coatings have a tremendous leverage in human life,all technological and scientific subjects.Numerous applications have been made for multilateral polymers like polyurethane(PU),epoxy(EP),polyaniline(PANI)conductive polymer,polypyrrole(PPy),and etc,on various metallic surfaces especially,carbon steel substrate owing to their excellent resistance properties.Practically,nanomaterials can possess potential in the all-interdisciplinary domains of materials science and engineering,chemical and physical sciences,biological and health sciences.As known,the designed polymer nanocomposite coating paradigm is fundamentally constituted from polymer or resin as a vehicle and inorganic nanofillers(nanoparticles and nanocomposites).Some commercialized and excessively employed nanocontainers in polymer nanocomposite coating formulations,like ZnO,TiO_(2),carbon nanotubes(CNTs),clay,SiO_(2),Al_(2)O_(3),graphene,GO,CeO_(2),ZrO_(2),FeTiO_(3),etc were discussed.The current review covered the chemistry and potential applications of the largest utilized multifunctional polymer nanocomposite coatings such as EP,PU and other considerable PNCCs.Lately,a titanic attention was made for epoxy nanocomposites because of their distinct physicochemical characteristics,which result from the combined qualities of the nanoparticles and polymer material unity.In addition,the author incorporated some of his scientific contributions in this area represented in construction of innovative functional polymer nanocomposites for a variety of uses with high economic,industrial impacts and future orientation.Furthermore,some newly published applications of polymer nanocomposite coatings were incorporated and discussed.
基金financially supported by the National Science and Technology Major Project(No.2017-VII-0012-0107)the National Program for Support of Top-notch Young Professionals。
文摘Aluminum-based composite abradable seal coatings are pivotal to improving the efficiency of aero engines or gas turbines.However,the adhesive transfer frequently occurs between metallic blade tips and aluminum-based composite coatings,resulting in engine vibration and even jam.Many past studies had tried to solve this problem by reducing coating hardness,improving lubrication,or strengthening blade tips,but all had failed.In this paper,we proposed a novel epoxy-based composite abradable seal coating,eliminating adhesive transfer by changing metal-to-metal scraping pair to metal-to-polymer scraping pair.The coating was developed via a hierarchical structure design.Large spherical pores were uniformly distributed in the continuous epoxy matrix with fine graphite dispersion.By adding 20 vol.%graphite and 50 vol.%hollow microspheres,a self-lubricating epoxy-based coating of 0.26 friction coefficient with thermal conductivity of 0.28 W/(m·K),coating HR15 Y hardness at 54.8,and bonding strength at 18.7 MPa can be reached.When the metallic blades scrape the epoxy-based composite coating,no adhesive transfer occurs.Besides,a smooth scraped surface is formed by pseudoplastic deformation.This epoxy-based composite abradable seal coating opens a new way to improve the efficiency and reliable operations of air engine compressors.
基金the financial support of the National Natural Science Foundation of China(Grant No.51201176)Industrialization Project of Education Department of Shaanxi Province(GrantNo.2012JC13)Zhejiang Provincial Natural Science Foundation of China(Grant No.Y2110401)
文摘The combined micro arc oxidation （MAO） and a hybrid beam deposition process was used to deposit duplex （Si：N）-DLC/MAO coatings on AZ80 magnesium alloy. The microstructure and composition of the duplex coatings were analyzed by Raman spectroscopy, X-ray photoelectron spectroscope （XPS）, scanning electron microscope （SEM） and atomic force microscopy （AFM）. Tribological behaviors of the coatings were studied by ball-on-disk friction test. It was found that the ID/IG ratio of the （Si：N）-DLC （diamond-like carbon） top films increases with decreasing C2H2/N2 ratio. The （Si：N）-DLC top film with SigN4 was formed on the MAO coated sample as the C2H2/N2 ratio was 10sccm：5sccm, which showed an increasing critical load compared with the pure DLC directly deposited on the Mg alloy substrate. As a result, the （Si：N）-DLC/MAO coating exhibited an advanced wear protection for the substrate.
基金Item Sponsored by National Natural Science Foundation of China(51202035)
文摘To improve the mechanical properties of self-lubricating chromium vanadium nitride （CrVN） coatings, va- nadium nitride （VN） is combined with CrVN to form multilayered CrVN/VN coatings through an in-line magnetron sputtering system. The strengthening effect of the period thickness on the mechanical and tribological properties is studied. X-ray diffractometer, low-angle X-ray reflectivity, scanning electron microscopy, atomic force microscopy, electron probe micro-analyzer and X-ray photoelectron spectroscopy are employed to characterize the microstructures and chemical composition. Nanoindentation and ball-on-disc tribo-tester are used in characterization of the mechanical and tribological properties. The CrVN/VN multilayer coatings demonstrate good lubrication property with coefficient of friction down to 0.23. Multilayering with VN, the hardness of CrVN jumps to 27.6 GPa with period thickness of 6 nm, which has an improvement of 5.1 GPa compared with that of 22.5 GPa from rule-of-mixture.
基金Project(50575081) supported by the National Natural Science Foundation of China
文摘Ni-based submicron WS2/CaF2 self-lubricating composite coatings were produced on carbon steel substrate by high velocity oxygen fuel(HVOF) spray processing, and the microstructure and mechanical properties of the coatings were investigated. Non-uniform microstructure characterized by some pores and microcracks is observed in the produced composite coatings, which leads to low microhardness value, low adhesive strength and low frictional coefficient. For Ni45-5%CaF2-10%WS2 (mass fraction) and Ni45-10%CaF2-5%WS2 (mass fraction) coatings, under the test condition of load 40 N and speed 2 m/s, the friction coefficients obtained at room temperature are in the range of 0.35-0.48 and 0.31-0.41, respectively. The friction coefficients of two kinds of coatings increase to 0.4-0.63 and 0.35-0.46, respectively, at the test speed of 1 m/s. And the Ni45-10%CaF2-5%WS2 coating presents the minimum friction coefficient of 0.32-0.38 and good anti-wear properties at 400 ℃.