The use of CO_(2) as monomer to synthesize polymer materials is an important and potential applications topic from the viewpoint of green and sustainable chemistry.A new kind of CO_(2)-based polyurea(PUa)was synthesiz...The use of CO_(2) as monomer to synthesize polymer materials is an important and potential applications topic from the viewpoint of green and sustainable chemistry.A new kind of CO_(2)-based polyurea(PUa)was synthesized by polycondensation of CO_(2) with 4,7,10-trioxa-1,13-tridecanediamine and tris(2-aminoethyl)amine(TAEA).TAEA was used as cross-link reagent.The mechanical properties of PUa were significantly improved by inserted the crosslink agent of TAEA.The formed slight cross-linked PUa exhibited excellent mechanical properties with tensile strength of 26.8 MPa,elongation at break of 34%and Young’s modulus of 351 MPa.Moreover,it could be remolded for 3 times without obvious change in the mechanical properties,which are ascribed to the hydrogen bonding interaction among the main chains and the slight cross-linked structure.In addition,the synthesized CO_(2)-based PUa is of outstanding thermal performance with an initial decomposition temperature above 300℃,besides it is tolerance for a variety of organic solvents.展开更多
文摘The use of CO_(2) as monomer to synthesize polymer materials is an important and potential applications topic from the viewpoint of green and sustainable chemistry.A new kind of CO_(2)-based polyurea(PUa)was synthesized by polycondensation of CO_(2) with 4,7,10-trioxa-1,13-tridecanediamine and tris(2-aminoethyl)amine(TAEA).TAEA was used as cross-link reagent.The mechanical properties of PUa were significantly improved by inserted the crosslink agent of TAEA.The formed slight cross-linked PUa exhibited excellent mechanical properties with tensile strength of 26.8 MPa,elongation at break of 34%and Young’s modulus of 351 MPa.Moreover,it could be remolded for 3 times without obvious change in the mechanical properties,which are ascribed to the hydrogen bonding interaction among the main chains and the slight cross-linked structure.In addition,the synthesized CO_(2)-based PUa is of outstanding thermal performance with an initial decomposition temperature above 300℃,besides it is tolerance for a variety of organic solvents.