In this work, the accelerated weathering test of immersion-wet-dry combined cycles was carried ont. The artificial acid rain of NaHSO3-(NH4)2SO4-H2SO4 solution system was selected as immersion solution. Acidity of art...In this work, the accelerated weathering test of immersion-wet-dry combined cycles was carried ont. The artificial acid rain of NaHSO3-(NH4)2SO4-H2SO4 solution system was selected as immersion solution. Acidity of artificial acid rain affected corrossion weight loss of carbon steel, and pH 4.1 was found to be a critical point. Anodic reaction resistance of the samples during accelerated weathering test increased with exposed time by electrochemical measurement.展开更多
Heavy rain is a kind of severe weather, often causing floods and serious soil erosion, leading to engineering losses, embankment rupture and crop flooding and other significant economic losses. Especially for some low...Heavy rain is a kind of severe weather, often causing floods and serious soil erosion, leading to engineering losses, embankment rupture and crop flooding and other significant economic losses. Especially for some low-lying terrain areas, rainwater cannot quickly vent caused by farm water and soil moisture being too saturated, so it will cause more geological disasters. This article combines live and forecast data, aiming at the results of the mid-rainstorm forecast in North China during the period of 7.19-2016, and compares with the actual situation of rainstorm. We carry out the mid-term forecast of the rainstorm. The atmosphere is a kind of medium with various fluctuation phenomena, and its physical properties and changes are studied by the analysis of volatility which is an important research method. It is important to improve the accuracy of such severe weather forecasting rainstorms and to take precautionary measures in a timely manner to minimize the losses caused by rainstorms.展开更多
An 800 kV electric power substation can have more than one hundred of porcelain multicone type insulators supporting busbar structures.Two or more sections in series,having middle and end fittings,compose these insula...An 800 kV electric power substation can have more than one hundred of porcelain multicone type insulators supporting busbar structures.Two or more sections in series,having middle and end fittings,compose these insulators.Ageing process can cause degradation of the cement used in this type of insulator and this fact can affect its dielectric performance under heavy rain.This paper presents results of an investigation based on power frequency high voltage tests performed on 800 kV porcelain multicone type insulators,removed from service after having operated for more than 20 years,as well a non-used one that had been stored on site for long time.The insulators were tested in different arrangements:each section at a time and the two sections assembled in series,as actually used insulator columns.The tests were carried out under artificial rain ranging from 1 mm/min to 5 mm/min.The results have confirmed a reduction of up to 30% in the insulator power frequency flashover voltage under 5 mm/min rain conditions and gave important information to the utility about radial cracks that were observed in many insulators and about the discharge mechanisms along the insulators under rain.展开更多
Stay cables with various surface profiles were tested in wind tunnel. Dimples and helical fillets were applied to mitigate the rain- wind induced vibration. The rain-wind excited responses of the cable with smooth sur...Stay cables with various surface profiles were tested in wind tunnel. Dimples and helical fillets were applied to mitigate the rain- wind induced vibration. The rain-wind excited responses of the cable with smooth surface were larger than those of the cables with dimples and helical fillets. At high Reynolds number, the drag coefficients of cables with dimples and helical fillets are much larger than those of smooth surface cable.展开更多
文摘In this work, the accelerated weathering test of immersion-wet-dry combined cycles was carried ont. The artificial acid rain of NaHSO3-(NH4)2SO4-H2SO4 solution system was selected as immersion solution. Acidity of artificial acid rain affected corrossion weight loss of carbon steel, and pH 4.1 was found to be a critical point. Anodic reaction resistance of the samples during accelerated weathering test increased with exposed time by electrochemical measurement.
文摘Heavy rain is a kind of severe weather, often causing floods and serious soil erosion, leading to engineering losses, embankment rupture and crop flooding and other significant economic losses. Especially for some low-lying terrain areas, rainwater cannot quickly vent caused by farm water and soil moisture being too saturated, so it will cause more geological disasters. This article combines live and forecast data, aiming at the results of the mid-rainstorm forecast in North China during the period of 7.19-2016, and compares with the actual situation of rainstorm. We carry out the mid-term forecast of the rainstorm. The atmosphere is a kind of medium with various fluctuation phenomena, and its physical properties and changes are studied by the analysis of volatility which is an important research method. It is important to improve the accuracy of such severe weather forecasting rainstorms and to take precautionary measures in a timely manner to minimize the losses caused by rainstorms.
文摘An 800 kV electric power substation can have more than one hundred of porcelain multicone type insulators supporting busbar structures.Two or more sections in series,having middle and end fittings,compose these insulators.Ageing process can cause degradation of the cement used in this type of insulator and this fact can affect its dielectric performance under heavy rain.This paper presents results of an investigation based on power frequency high voltage tests performed on 800 kV porcelain multicone type insulators,removed from service after having operated for more than 20 years,as well a non-used one that had been stored on site for long time.The insulators were tested in different arrangements:each section at a time and the two sections assembled in series,as actually used insulator columns.The tests were carried out under artificial rain ranging from 1 mm/min to 5 mm/min.The results have confirmed a reduction of up to 30% in the insulator power frequency flashover voltage under 5 mm/min rain conditions and gave important information to the utility about radial cracks that were observed in many insulators and about the discharge mechanisms along the insulators under rain.
文摘Stay cables with various surface profiles were tested in wind tunnel. Dimples and helical fillets were applied to mitigate the rain- wind induced vibration. The rain-wind excited responses of the cable with smooth surface were larger than those of the cables with dimples and helical fillets. At high Reynolds number, the drag coefficients of cables with dimples and helical fillets are much larger than those of smooth surface cable.