r GO/Ti O_2复合材料优异的光催化性能为其在有机染料降解,雨水消毒和催化析氢等方面的应用提供可能,通过与金属、金属化合物或高聚物复合可提升光催化效率和化学稳定性。分析反应机理,阐述现阶段研究的重点和不足,同时对未来发展和应...r GO/Ti O_2复合材料优异的光催化性能为其在有机染料降解,雨水消毒和催化析氢等方面的应用提供可能,通过与金属、金属化合物或高聚物复合可提升光催化效率和化学稳定性。分析反应机理,阐述现阶段研究的重点和不足,同时对未来发展和应用进行展望。展开更多
Due to the low concentration of indoor air contaminants, photocatalytic technology shows low efficiency for indoor air purification. The application of TiO2 for photocatalytic removal of formaldehyde is limited, becau...Due to the low concentration of indoor air contaminants, photocatalytic technology shows low efficiency for indoor air purification. The application of TiO2 for photocatalytic removal of formaldehyde is limited, because TiO2 can only absorb ultraviolet （UV） light. Immobilization of TiO2 nanoparticles on the surface of graphene can improve the visible light photocatalytic activity and the adsorption capacity. In this study, rGO （reduced graphene oxide）/TiO2 was synthesized through a hydrotherrnal method using titanium tetrabutoxide and graphene oxide as precursors, and was used for the degradation of low concentration formaldehyde in indoor air under visible light illumination. Characterization of the crystalline structure and morphology of rGO/TiO2 revealed that most GO was reduced to rGO during the hydrothermal treatment, and anatase TiO2 nanoparticles （with particle size of 15-30 nm） were dispersed well on the surface of the rGO sheets, rGO/TiO2 exhibited excellent photocatalyfic activity for degradation of formaldehyde in indoor air and this can be attributed to the role ofrGO, which can act as the electron sink and transporter for separating photo-generated electron-hole pairs through interfacial charge transfer. Furthermore, rGO could adsorb formaldehyde molecules from air to produce a high concentration of formaldehyde on the surface of rGO/ TiO2. Under visible light irradiation for 240 min, the concentration of formaldehyde could be reduced to 58.5 ppbV. rGO/TiO2 showed excellent moisture-resistance behavior, and after five cycles, rGO/TiO2 maintained high photocatalytic activity for the removal of formaldehyde （84.6%）. This work suggests that the synthesized rGO/TiO2 is a promising photocatalyst for indoor formaldehyde removal.展开更多
BiOI-sensitized titanium dioxide (TiO2) photocatalysts were prepared by a deposition method at room temperature and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller su...BiOI-sensitized titanium dioxide (TiO2) photocatalysts were prepared by a deposition method at room temperature and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller surface area measurements. The photocatalytic activities of the catalysts were evaluated for the degradation of methyl orange (MO) solution under UV and visible light irradiation. The effects of catalyst amount, initial pH value, initial concentration of MO, as well as KI amount were investigated. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst was also tested. It is shown that BiOI sensitization enhances the photocatalytic activities of TiO2. With BiOI content increasing, the photocatalytic activities of BiOI/TiO2 under UV and visible light irradiation first increase, reaching a maximum around BiOI content of 1.7%, and then decrease with further increasing BiOI content. The 1.7% BiOI/TiO2 catalyst obviously exhibits much higher visible light photocatalytic activity than P25, and its UV light photocatalytic activity is slightly higher than that of P25. Under the conditions of a catalytic dose of 1.5 g.L-1, initial pH of 3.0, initial MO concentration of 20 mg.L-1, UV power of 300 W, and air flow rate of 0.8 L.min-1, complete degradatio is achieved within 60 min. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst is highly reliable.展开更多
A series of Z-scheme TiO2/g-C3N4/RGO ternary heterojunction photocatalysts are successfully constructed via a direct electrospinning technique coupled with an annealing process for the first time. They are investigate...A series of Z-scheme TiO2/g-C3N4/RGO ternary heterojunction photocatalysts are successfully constructed via a direct electrospinning technique coupled with an annealing process for the first time. They are investigated comprehensively in terms of crystal structure, morphology, composition, specific surface area, photoelectrochemical properties, photodegradation performance, etc. Compared with binary TiO2/g-C3N4 and single-component photocatalysts, ternary heterojunction photocatalysts show the best photodegradation performance for RhB under stimulated sunlight. This can be attributed to the enlarged specific surface area (111.41 m2/g), the formation of Z-scheme heterojunction, and the high separation migration efficiency of photoexcited charge carriers. A potential Z-scheme mechanism for ternary heterojunction photocatalysts is proposed to elucidate the remarkably ameliorated photocatalytic performance based on active species trapping experiments, PL detection test of hydroxyl radicals, and photoelectrochemical properties.展开更多
Zn0.4Cd0.6S/TiO2/Reduced graphene oxide(Zn0.4Cd0.6S/TiO2/RGO)nano-photocatalyst was synthe-sized by a facile solvothermal method.During the reaction,TiO2 and Zn0.8Cd0.2S nanoparticles were evenly dispersed across the ...Zn0.4Cd0.6S/TiO2/Reduced graphene oxide(Zn0.4Cd0.6S/TiO2/RGO)nano-photocatalyst was synthe-sized by a facile solvothermal method.During the reaction,TiO2 and Zn0.8Cd0.2S nanoparticles were evenly dispersed across the surface of RGO,which enhanced response to visible light.The photocatalytic activity of as-synthesized Zn0.4Cd0.6S/TiO2/RGO nanocomposite was studied by means of degrading methylene blue(MB)through the irradiation of visible light.Compared with other nanocomposites,the Zn0.4Cd0.6S/TiO2/RGO nanocomposite showed the highest photocatalytic degradation efficiency(96%)and high stability,which was 5.4 times of photodegradation efficiency of pure TiO2.展开更多
基金financially supported by China Postdoctoral Science Foundation(No.2016M592496)Natural Science Foundation of Guangdong Province,China(Nos.2017A030310279,2014A030310431)+1 种基金National Natural Science Foundation of China(Nos.41501319,91645119,21207039,U1201231,51378218,51108187 and 50978103)Guangzhou science and technology plan(No.201607010095)
文摘Due to the low concentration of indoor air contaminants, photocatalytic technology shows low efficiency for indoor air purification. The application of TiO2 for photocatalytic removal of formaldehyde is limited, because TiO2 can only absorb ultraviolet （UV） light. Immobilization of TiO2 nanoparticles on the surface of graphene can improve the visible light photocatalytic activity and the adsorption capacity. In this study, rGO （reduced graphene oxide）/TiO2 was synthesized through a hydrotherrnal method using titanium tetrabutoxide and graphene oxide as precursors, and was used for the degradation of low concentration formaldehyde in indoor air under visible light illumination. Characterization of the crystalline structure and morphology of rGO/TiO2 revealed that most GO was reduced to rGO during the hydrothermal treatment, and anatase TiO2 nanoparticles （with particle size of 15-30 nm） were dispersed well on the surface of the rGO sheets, rGO/TiO2 exhibited excellent photocatalyfic activity for degradation of formaldehyde in indoor air and this can be attributed to the role ofrGO, which can act as the electron sink and transporter for separating photo-generated electron-hole pairs through interfacial charge transfer. Furthermore, rGO could adsorb formaldehyde molecules from air to produce a high concentration of formaldehyde on the surface of rGO/ TiO2. Under visible light irradiation for 240 min, the concentration of formaldehyde could be reduced to 58.5 ppbV. rGO/TiO2 showed excellent moisture-resistance behavior, and after five cycles, rGO/TiO2 maintained high photocatalytic activity for the removal of formaldehyde （84.6%）. This work suggests that the synthesized rGO/TiO2 is a promising photocatalyst for indoor formaldehyde removal.
基金financially supported by the National Natural Science Foundation of China(No.21171091)the Natural Science Foundation of Higher Education Institutions in Anhui Province(Nos.KJ2012A217,KJ2012B135,and KJ2012B136)
文摘BiOI-sensitized titanium dioxide (TiO2) photocatalysts were prepared by a deposition method at room temperature and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller surface area measurements. The photocatalytic activities of the catalysts were evaluated for the degradation of methyl orange (MO) solution under UV and visible light irradiation. The effects of catalyst amount, initial pH value, initial concentration of MO, as well as KI amount were investigated. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst was also tested. It is shown that BiOI sensitization enhances the photocatalytic activities of TiO2. With BiOI content increasing, the photocatalytic activities of BiOI/TiO2 under UV and visible light irradiation first increase, reaching a maximum around BiOI content of 1.7%, and then decrease with further increasing BiOI content. The 1.7% BiOI/TiO2 catalyst obviously exhibits much higher visible light photocatalytic activity than P25, and its UV light photocatalytic activity is slightly higher than that of P25. Under the conditions of a catalytic dose of 1.5 g.L-1, initial pH of 3.0, initial MO concentration of 20 mg.L-1, UV power of 300 W, and air flow rate of 0.8 L.min-1, complete degradatio is achieved within 60 min. The repeatability of photocatalytic activity of the 1.7% BiOI/TiO2 catalyst is highly reliable.
基金supported by the Scientific Research Project from Hubei Provincial Department of Education(Q20181808)the Research and Innovation Initiatives of Wuhan Polytechnic University(2018J04,2018Y07)~~
文摘A series of Z-scheme TiO2/g-C3N4/RGO ternary heterojunction photocatalysts are successfully constructed via a direct electrospinning technique coupled with an annealing process for the first time. They are investigated comprehensively in terms of crystal structure, morphology, composition, specific surface area, photoelectrochemical properties, photodegradation performance, etc. Compared with binary TiO2/g-C3N4 and single-component photocatalysts, ternary heterojunction photocatalysts show the best photodegradation performance for RhB under stimulated sunlight. This can be attributed to the enlarged specific surface area (111.41 m2/g), the formation of Z-scheme heterojunction, and the high separation migration efficiency of photoexcited charge carriers. A potential Z-scheme mechanism for ternary heterojunction photocatalysts is proposed to elucidate the remarkably ameliorated photocatalytic performance based on active species trapping experiments, PL detection test of hydroxyl radicals, and photoelectrochemical properties.
文摘Zn0.4Cd0.6S/TiO2/Reduced graphene oxide(Zn0.4Cd0.6S/TiO2/RGO)nano-photocatalyst was synthe-sized by a facile solvothermal method.During the reaction,TiO2 and Zn0.8Cd0.2S nanoparticles were evenly dispersed across the surface of RGO,which enhanced response to visible light.The photocatalytic activity of as-synthesized Zn0.4Cd0.6S/TiO2/RGO nanocomposite was studied by means of degrading methylene blue(MB)through the irradiation of visible light.Compared with other nanocomposites,the Zn0.4Cd0.6S/TiO2/RGO nanocomposite showed the highest photocatalytic degradation efficiency(96%)and high stability,which was 5.4 times of photodegradation efficiency of pure TiO2.