This scientific paper gives consideration to the information on the structure of the triple component system,in particular MgO-Al_(2)O_(3)-TiO_(2) that serves as a basis for the production of thermal resistance materi...This scientific paper gives consideration to the information on the structure of the triple component system,in particular MgO-Al_(2)O_(3)-TiO_(2) that serves as a basis for the production of thermal resistance materials.The structure of such binary systems as MgO-Al_(2)O_(3),Al_(2)O_(3)-TiO_(2),MgO-TiO_(2) was described and the data available for the MgO-Al_(2)O_(3)-TiO_(2) system were given.Thermodynamic data on all the system compounds were also presented and used for the computation of a change in the free Gibbs energy in the temperature range form 800 K to 1900 K for the basic exchange reactions.It was established that the triangulation of the MgO-Al_(2)O_(3)-TiO_(2) system was changed in the three temperature intervals:in the temperature range lower than 1537 K TiO_(2) existed as the polymorphous modification,i.e.anatase;in the temperature range from 1537 K to 2076 K TiO_(2) existed as a polymorphous modification in form of rutile and tialite was stable;and at the temperatures above 2076 K the availability of stochiometric compound of Al4TiO_(8) was possible.In the temperature range lower than 1537 K the two-phase equilibra of Al_(2)O_(3)-MgTi2O_(5),Mg-MgALCU MgTiO_(3)-MgAl_(2)O_(4),and Mg_(2)TiO_(4)-MgAl_(2)O_(4) were stable;in the temperature range from 1537 K to 2076 K the two-phase equilibria of MgTigO_(5)-AlgTiO_(5),MgTiO_(3)-Al_(2)TiO_(5),MgTiO_(3)-Al_(2)O_(3),MgTiO_(3)-MgAl_(2)O_(4),and Mg_(2)TiO_(4)-MgAl_(2)O_(4) were stable,and above 2076 K the MgTi_(2)O_(5)-Al_(2)TiO_(5),MgTi_(2)O_(5)-Al_(4)TiO_(8),Al_(4)TiO_(8)-MgTiO_(3),Al_(4)TiO_(8)-Mg_(2)TiO_(4),Al_(4)TiO_(8)-Mg0,and Al_(4)TiO_(8)-MgAl_(2)O_(4) systems were stable.展开更多
文摘This scientific paper gives consideration to the information on the structure of the triple component system,in particular MgO-Al_(2)O_(3)-TiO_(2) that serves as a basis for the production of thermal resistance materials.The structure of such binary systems as MgO-Al_(2)O_(3),Al_(2)O_(3)-TiO_(2),MgO-TiO_(2) was described and the data available for the MgO-Al_(2)O_(3)-TiO_(2) system were given.Thermodynamic data on all the system compounds were also presented and used for the computation of a change in the free Gibbs energy in the temperature range form 800 K to 1900 K for the basic exchange reactions.It was established that the triangulation of the MgO-Al_(2)O_(3)-TiO_(2) system was changed in the three temperature intervals:in the temperature range lower than 1537 K TiO_(2) existed as the polymorphous modification,i.e.anatase;in the temperature range from 1537 K to 2076 K TiO_(2) existed as a polymorphous modification in form of rutile and tialite was stable;and at the temperatures above 2076 K the availability of stochiometric compound of Al4TiO_(8) was possible.In the temperature range lower than 1537 K the two-phase equilibra of Al_(2)O_(3)-MgTi2O_(5),Mg-MgALCU MgTiO_(3)-MgAl_(2)O_(4),and Mg_(2)TiO_(4)-MgAl_(2)O_(4) were stable;in the temperature range from 1537 K to 2076 K the two-phase equilibria of MgTigO_(5)-AlgTiO_(5),MgTiO_(3)-Al_(2)TiO_(5),MgTiO_(3)-Al_(2)O_(3),MgTiO_(3)-MgAl_(2)O_(4),and Mg_(2)TiO_(4)-MgAl_(2)O_(4) were stable,and above 2076 K the MgTi_(2)O_(5)-Al_(2)TiO_(5),MgTi_(2)O_(5)-Al_(4)TiO_(8),Al_(4)TiO_(8)-MgTiO_(3),Al_(4)TiO_(8)-Mg_(2)TiO_(4),Al_(4)TiO_(8)-Mg0,and Al_(4)TiO_(8)-MgAl_(2)O_(4) systems were stable.