Fabrication of flame retardants from renewable biomass has aroused extensive interest over the past decade.This work reported a synthesis of isosorbide-derived polyphosphonate(PICPP)as an anti-flammable agent for poly...Fabrication of flame retardants from renewable biomass has aroused extensive interest over the past decade.This work reported a synthesis of isosorbide-derived polyphosphonate(PICPP)as an anti-flammable agent for poly(lactic acid)(PLA).The presence of PICPP notably declined the storage modulus of PLA/PICPP owing to the declined molecular weight of PLA catalyzed by the presence of PICPP.PLA and PLA/PICPP thermally degraded in one stage under either air or nitrogen atmosphere.With increasing the amount of PICPP,the onset thermal decomposition temperature of PLA/PICPP was decreased gradually,owing to the earlier decomposition of PICPP.With only 10 wt%of PICPP,PLA/PICPP-10 achieved a high limiting oxygen index of 30.0%and UL-94 V-0 classification,manifesting that PICPP was an efficient anti-flammable agent for PLA.The inclusion of 15 wt%PICPP also caused 33%and 16%decline in PHRR and THR of PLA,respectively.TG-IR results clarified that PLA/PICPP produced the less typical pyrolysis products especially flammable carbonyls than PLA,which may account for the suppressed PHRR and THR values of PLA/PICPP.展开更多
基金The work was financially supported by the Hong Kong Scholars Program(Grant No.XJ2020003)the Basic Research Program of Jiangnan University(JUSRP121029).
文摘Fabrication of flame retardants from renewable biomass has aroused extensive interest over the past decade.This work reported a synthesis of isosorbide-derived polyphosphonate(PICPP)as an anti-flammable agent for poly(lactic acid)(PLA).The presence of PICPP notably declined the storage modulus of PLA/PICPP owing to the declined molecular weight of PLA catalyzed by the presence of PICPP.PLA and PLA/PICPP thermally degraded in one stage under either air or nitrogen atmosphere.With increasing the amount of PICPP,the onset thermal decomposition temperature of PLA/PICPP was decreased gradually,owing to the earlier decomposition of PICPP.With only 10 wt%of PICPP,PLA/PICPP-10 achieved a high limiting oxygen index of 30.0%and UL-94 V-0 classification,manifesting that PICPP was an efficient anti-flammable agent for PLA.The inclusion of 15 wt%PICPP also caused 33%and 16%decline in PHRR and THR of PLA,respectively.TG-IR results clarified that PLA/PICPP produced the less typical pyrolysis products especially flammable carbonyls than PLA,which may account for the suppressed PHRR and THR values of PLA/PICPP.