Toddy palm fruit have an apparent density below 0.8 g/cm³and offer an interesting lightweight construction potential in polylactide(PLA)composites reinforced with 37 mass-%fibres.Single fibre bundles show similar...Toddy palm fruit have an apparent density below 0.8 g/cm³and offer an interesting lightweight construction potential in polylactide(PLA)composites reinforced with 37 mass-%fibres.Single fibre bundles show similar mechanical properties compared with coir:tensile strength of 240 MPa,Young´s modulus of 3.8 GPa and an elongation at break of 31%.However,density and diameter(~50μm)of fruit fibre bundles are significantly lower.The compression moulded composites have a density of 0.9 g/cm³and achieved an unnotched Charpy impact strength of 12 kJ/m^(2),a tensile strength of 25 MPa,Young’s modulus of 1.9 GPa and an elongation at break of 9%.Due to the high porosity of the composites and the different stress-strain behaviour of fibre and matrix the fibre-reinforcement potential could not be fully used.Maximum stress of the composite was reached at the elongation at break of the PLA-matrix(~2%)while the fibre achieved its maximum stress at an elongation of~31%.After reaching the maximum stress of the composite,the fibres were pulled out from the matrix with low energy absorption,resulting in a decrease in stress and a limited reinforcement potential.Additionally,the study investigates whether an insect attack by the Asian fruit fly on the mesocarp has a significant influence on the mechanical fibre characteristics.The results have shown that only the rough surface of the fibre bundles is smoothed by insect infestation.The mechanical properties were not significantly affected.For this reason insect-infested fruits of the toddy palm,which are no longer suitable for food production,can be used for the production of sustainable composite materials.展开更多
Polyl(lactide),PLA,suffers from bitleness and low heat deflection temperature(HDT),which limits its application as an engineering plastic.In this work,poly(L-lactide)/poly(D-lactide)/ethylene-vinyl acetate glycidyl me...Polyl(lactide),PLA,suffers from bitleness and low heat deflection temperature(HDT),which limits its application as an engineering plastic.In this work,poly(L-lactide)/poly(D-lactide)/ethylene-vinyl acetate glycidyl methacrylate random copolymer(PLLA/PDL A/EVM-GMA=1/1/x)composites were prepared by melt blending,and the in situ formed EVM-g PLA copolymers improved the compatibility between PLA and EVM-GMA.Subsequently,the blends were subjected to a two-step annealing process during compression molding,i.e.first annealing at 120℃ to rapidly form a certain amount of stereocomplex(sc)crystallites as nucleation sites,and then annealing at 200℃ to guide the formation of new sccrystallites.Both differential scanning calorimetry(DSC)and wide angle X-ray dffrction(WAXD)measurements confirmed the formation of highly stereocomplexed PLA products.Mechanical results showed that the PLLA/PDLA blend with 20 wt%of EVM-GMA had a notched impact strength up to 65 kJ/m2 and an elongation at break of 48%,while maintaining a tensile strength of 40 MPa.Meanwhile,dynamic mechanical analysis(DMA)and heat deflection tests showed that the PLA composite had an HDT up to 142℃ which is 90℃ higher than that of normal PLA products.Scanning electron microscopy(SEM)confirmed the fine dispersion of EVM-GMA particles,which facilitated to understand the toughening mechanism.Furthermore,the highly stereocomplexed PLA composites simultaneously exhibited excellent chemical and hydrolysis resistance.Therefore,these fascinating properties may extend the application range of sc PLA material as an engineering bioplastic.展开更多
PLA composites containing biomass fillers from the three herbaceous plants such as reed,wheat stalk,and coco-nut fiber with length and diameter at the scale of several millimeters were prepared without using additives...PLA composites containing biomass fillers from the three herbaceous plants such as reed,wheat stalk,and coco-nut fiber with length and diameter at the scale of several millimeters were prepared without using additives.The reinforcement effect on the properties of PLA/biomass filler composites is investigated.The research results show that the PLA/biomass filler composites exhibit good stiffness,flexural strength,and impact toughness.Among the three kinds of biomass fillers,reed reinforced PLA composites show optimal mechanical properties.When filled with 40%–50%reed,the flexural moduli of the composites are over 7000 MPa.Flexural strength retains at the same level of pure PLA.The notch impact strength reaches to 4.50±0.73 kJ/m^(2),which is 2.06 times higher than that of pure PLA.Furthermore,the introduction of biomass fillers increases the crystallization ability of PLA and does not increase the water absorption of the composites.This research demonstrated that PLA composites prepared with biomass fillers from the herbaceous plants(namely herb plastic composites,HPCs)is a material with good comprehensive mechanical properties while retaining the intrinsic particularity of biological sources.展开更多
To clarify the effects of lignin as a biodegradable filler added into the PLA matrix,PLA/lignin composites with or without silane coupling agent ofγ-(2,3-epoxypropoxy)propy trimethoxysilane(KH560)were prepared by a o...To clarify the effects of lignin as a biodegradable filler added into the PLA matrix,PLA/lignin composites with or without silane coupling agent ofγ-(2,3-epoxypropoxy)propy trimethoxysilane(KH560)were prepared by a one-step solvent-free modification method.The effects of KH560 as a compatibilizer on the morphology,chemical structure,crystallization behavior,thermal degradative behavior as well as mechanical strength of the PLA/lignin composites were analyzed in detail.It was found that,after modification by KH560,the fractured surfaces of composites became smooth,suggested sufficient bonding between the lignin and PLA in the composites with KH560 coupling agent molecules.This result further proved by 1H NMR and ATR spectra of the composites that lignin and PLA formed stable chemical bonds with KH560.Due to the toughening effect of KH560,mainly affect the molecular chain mobility,the thermodynamic properties of LG-KH560/PLA composites were all reduced.When compared to the conventional solution modification method of adding silane coupling agents into PLA/lignin,the composites were synthesized via a single-step reactive extrusion modification procedure in this work showed relatively low tensile strength,which mainly because the existence of the free radicals due to coupling agents result in the composite’s deterioration and subsequent weakening of the tensile properties.展开更多
Nonporous and porous C/PLA/nano-HA composites were fabricated by the process of solvent blending and freeze-drying technique, and the effect of porous structure on the mechanical properties of C/PLA/nano-HA composites...Nonporous and porous C/PLA/nano-HA composites were fabricated by the process of solvent blending and freeze-drying technique, and the effect of porous structure on the mechanical properties of C/PLA/nano-HA composites scaffold was investigated and analyzed. The results show that the effects of porous structure on the bending strength, modulus and curves of stress and strain were obvious. Compared with nonporous sample, the curves of stress and strain of porous sample show more rough, and alternative phenomenon of stress increase and stress relaxation appears. It is strongly suggested that the fracture model of C/PLA/nano-HA composites scaffold transforms from the local to global load due to the porous structure.展开更多
This paper describes the flexural properties of biodegradable composites made using natural fiber and biodegradable plastics. Biodegradable composites were fabricated from bamboo fiber bundles and PLA (polylactic acid...This paper describes the flexural properties of biodegradable composites made using natural fiber and biodegradable plastics. Biodegradable composites were fabricated from bamboo fiber bundles and PLA (polylactic acid) resin. In this research, effect of molding temperature and fiber content on flexural properties of bamboo fiber reinforced composites was investigated. The flexural strength of this composite increased with increasing fiber content up to 70%. The flexural strength of composites decreased at molding temperature of 180°C. Biodegradable composites possessed extremely high flexural strength of 273 MPa, in the case of molding temperature of 160°C and fiber content of 70%.展开更多
In order to improve the thermal properties of polylactic acid（PLA） filament,nano-SiO_2 was applied to mix with PLA,then they were spun as composite filament by melt-spinning.The dispersion of nano SiO_2 and the frac...In order to improve the thermal properties of polylactic acid（PLA） filament,nano-SiO_2 was applied to mix with PLA,then they were spun as composite filament by melt-spinning.The dispersion of nano SiO_2 and the fracture surfaces of filaments were studied by scanning electron microscopy（SEM）.The properties of composite filament,such as orientation degree,mechanical properties,and surface friction properties,were analyzed.The thermal performances of composite filament were analyzed by differential scanning calorimetry（DSC） and thermo gravimetric analysis（TGA）.The results showed that the nano-SiO_2 modified by 5% KH-550 could disperse evenly and loosely in nano-scale,and 1 wt% and 3 wt% nano-SiO_2 dispersed throughout PLA evenly.As the quantity of nano-SiO_2 increased,the properties of composite filament,such as orientation degree,friction coefficient,thermal decomposition temperature,and glass transition temperature,increased more or less.The breaking tenacity increased when 1 wt% SiO_2 was added in PLA,but declined when 3 wt% SiO_2 was added.展开更多
The hydroxyapatite/polylactide biocomposites were prepared by absorption process in liquid phase. The method avoided many disadvantages, such as inaterfusion of chemical impurity substances, nonuniformity dispersal o...The hydroxyapatite/polylactide biocomposites were prepared by absorption process in liquid phase. The method avoided many disadvantages, such as inaterfusion of chemical impurity substances, nonuniformity dispersal of HA in PLA, low molecular weight of PLA . HA particles were uniformly dispersed in PLA matrix, and showed well ndhesion with PLA matrix. The biocomposites have the higher mechanical properties and suitable decomposable capability.展开更多
In order to improve the thermal properties of polylactic acid( PLA) master batch,the nano-SiO2 was applied to mixing with PLA. The structure and thermal properties of the composite master batches were studied. The res...In order to improve the thermal properties of polylactic acid( PLA) master batch,the nano-SiO2 was applied to mixing with PLA. The structure and thermal properties of the composite master batches were studied. The results showed that the nano-SiO2 modified by 3% coupling agent KH-570 could be dispersed evenly in PLA in small scale. The thermal decomposition temperature of composite master batches increased by 6. 20-10. 80 ℃, the glass transition temperature increased by 0. 22-5. 16 ℃,and the heat enthalpy at the glass transition temperature increased by 0. 574-2. 437 J /g,compared with pure PLA. The composite master batch possessed superior thermal stability and heat resistance.展开更多
A new entire biodegradable scaffold has been developed which does not require precellularization before transplantation.This new kind of vascular scaffold prototype made from porous poly-ε-caprolactone( PCL) membrane...A new entire biodegradable scaffold has been developed which does not require precellularization before transplantation.This new kind of vascular scaffold prototype made from porous poly-ε-caprolactone( PCL) membrane to provide three-dimensional environment for cell growth, and embedded with weft-knitted polylactic acid( PLA) fabric to support mechanics.The aim of this paper is to study the variation tendency of mechanical properties with the fabric spacing changing.The basic geometrical parameters were measured to characterize properties of the samples.The tensile and compressive elastic recovery of the samples were tested by the universal mechanical tester and radial compression apparatus,respectively.Both tensile and compressive properties enhanced when reducing the fabric spacing of the composite vascular scaffold.展开更多
Hydroxyapatite/polylactide (HA/PLA) composites have been intensively investigated for their potential as biodegradable fixation devices to heal bone fractures. However, most of these composites failed to achieve a bon...Hydroxyapatite/polylactide (HA/PLA) composites have been intensively investigated for their potential as biodegradable fixation devices to heal bone fractures. However, most of these composites failed to achieve a bone-mimicking level of mechanical properties, which is an essential demand of the targeted application. In this study, the nano-hydroxyapatite/polylactide composites were used as the matrix and continuous phosphate glass fibres (PGF) served as the major reinforcement to obtain the nano-HA/PGF/PLA hybrid composites. While the PGF volume fraction remained constant (25%), the nano-HA content (in weight) varied from 0% to 20%. As nano-HA loading increased, the flexural modulus of the composites increased from 8.70 ± 0.35 GPa to 14.97 ± 1.30 GPa, and the flexural strengths were enhanced from 236.31 ± 10.83 MPa to 310.55 ± 22.88 MPa. However, it is found that the degradation rates are higher with more nano-HA loaded. Enhanced water absorption ability, as well as increased voids in the composites is possible reasons for the accelerated degradation of composites with higher nano-HA loading. The hybrid composites possess mechanical properties that are superior to most of the HA/PLA composites in previous research while maintaining the biodegradability. With a proper loading of nano-HA in composites of 10 weight percent, the composites are also found with improved mechanical properties without catastrophic degradation. The composites developed in this study have great potential as biodegradable bone fixation device with enhanced load-bearing ability as confirmed and superior bioactivity as anticipated.展开更多
The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by b...The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by braiding PLA filaments with 4 to 24 spindles on flax yarns.After curing at different temperatures(180℃and 190℃),the core/sheath structural flax/PLA composite yarns were manufactured.According to the results of the tensile test,the flax/PLA composite yarn with 4-spindle PLA yarns as a sheath layer and at a curing temperature of 180℃reached the maximum elastic modulus of about(5.79±0.65)GPa and the maximum tensile strength of about(162.17±18.18)MPa.This flax/PLA composite yarn with good mechanical properties would be suitable for green composites in the automobile manufacturing industry and building materials.展开更多
In order to prepare cellulose nanocrystals( CNCs)-coated polylactide( PLA) microspheres for the use of drug delivery and tissue engineering,a Pickering emulsion route was applied. The stable Pickering emulsions were p...In order to prepare cellulose nanocrystals( CNCs)-coated polylactide( PLA) microspheres for the use of drug delivery and tissue engineering,a Pickering emulsion route was applied. The stable Pickering emulsions were prepared using CNCs as efficient stabilizers without any additional surfactant. The microspheres were successfully fabricated after volatilization of the solvent. What's more,the size of microspheres could be controlled by fabrication parameters.展开更多
Spherical carbon particles were prepared by using waste Guilin rice noodles as raw materials.By blending the rice noodles based carbon(RC)powders with polylactic acid(PLA),A series of black RC/PLA 3D printing composit...Spherical carbon particles were prepared by using waste Guilin rice noodles as raw materials.By blending the rice noodles based carbon(RC)powders with polylactic acid(PLA),A series of black RC/PLA 3D printing composites were synthesized and characterized.The mechanical testing result shows that the RC/PLA 3D printing composites display better mechanical properties than that of pure PLA.Moreover,the composite with carbon treated with high temperature carbonization has better impact strength.展开更多
基金funded within the framework of the BMBF exchange project“Thai-German Agro-based Fibre Exchange Programme-Sustainable Development:From Plant to Product(Acronym:AgroFibre)”under the registration number 01DP15016.
文摘Toddy palm fruit have an apparent density below 0.8 g/cm³and offer an interesting lightweight construction potential in polylactide(PLA)composites reinforced with 37 mass-%fibres.Single fibre bundles show similar mechanical properties compared with coir:tensile strength of 240 MPa,Young´s modulus of 3.8 GPa and an elongation at break of 31%.However,density and diameter(~50μm)of fruit fibre bundles are significantly lower.The compression moulded composites have a density of 0.9 g/cm³and achieved an unnotched Charpy impact strength of 12 kJ/m^(2),a tensile strength of 25 MPa,Young’s modulus of 1.9 GPa and an elongation at break of 9%.Due to the high porosity of the composites and the different stress-strain behaviour of fibre and matrix the fibre-reinforcement potential could not be fully used.Maximum stress of the composite was reached at the elongation at break of the PLA-matrix(~2%)while the fibre achieved its maximum stress at an elongation of~31%.After reaching the maximum stress of the composite,the fibres were pulled out from the matrix with low energy absorption,resulting in a decrease in stress and a limited reinforcement potential.Additionally,the study investigates whether an insect attack by the Asian fruit fly on the mesocarp has a significant influence on the mechanical fibre characteristics.The results have shown that only the rough surface of the fibre bundles is smoothed by insect infestation.The mechanical properties were not significantly affected.For this reason insect-infested fruits of the toddy palm,which are no longer suitable for food production,can be used for the production of sustainable composite materials.
基金This work was financially supported by the National Natural Science Foundation of China(Nos.51873082 and 51903106)Fundamental Research Funds for the Central Universities(No.JUSRP11928).
文摘Polyl(lactide),PLA,suffers from bitleness and low heat deflection temperature(HDT),which limits its application as an engineering plastic.In this work,poly(L-lactide)/poly(D-lactide)/ethylene-vinyl acetate glycidyl methacrylate random copolymer(PLLA/PDL A/EVM-GMA=1/1/x)composites were prepared by melt blending,and the in situ formed EVM-g PLA copolymers improved the compatibility between PLA and EVM-GMA.Subsequently,the blends were subjected to a two-step annealing process during compression molding,i.e.first annealing at 120℃ to rapidly form a certain amount of stereocomplex(sc)crystallites as nucleation sites,and then annealing at 200℃ to guide the formation of new sccrystallites.Both differential scanning calorimetry(DSC)and wide angle X-ray dffrction(WAXD)measurements confirmed the formation of highly stereocomplexed PLA products.Mechanical results showed that the PLLA/PDLA blend with 20 wt%of EVM-GMA had a notched impact strength up to 65 kJ/m2 and an elongation at break of 48%,while maintaining a tensile strength of 40 MPa.Meanwhile,dynamic mechanical analysis(DMA)and heat deflection tests showed that the PLA composite had an HDT up to 142℃ which is 90℃ higher than that of normal PLA products.Scanning electron microscopy(SEM)confirmed the fine dispersion of EVM-GMA particles,which facilitated to understand the toughening mechanism.Furthermore,the highly stereocomplexed PLA composites simultaneously exhibited excellent chemical and hydrolysis resistance.Therefore,these fascinating properties may extend the application range of sc PLA material as an engineering bioplastic.
基金supported by“One Belt,One Road”Projects of China Academy of Sciences(174433KYSB20190082)Science and Technology Service Network Plan of China Academy of Sciences(KFJ-STS-QYZD-2021-16-002)+2 种基金Key Projects of Ningbo Public Welfare Science and Technology Plan(2021S020)Ningbo Natural Science Foundation(2021J196)Youth Innovation Promotion Association CAS(2017339).
文摘PLA composites containing biomass fillers from the three herbaceous plants such as reed,wheat stalk,and coco-nut fiber with length and diameter at the scale of several millimeters were prepared without using additives.The reinforcement effect on the properties of PLA/biomass filler composites is investigated.The research results show that the PLA/biomass filler composites exhibit good stiffness,flexural strength,and impact toughness.Among the three kinds of biomass fillers,reed reinforced PLA composites show optimal mechanical properties.When filled with 40%–50%reed,the flexural moduli of the composites are over 7000 MPa.Flexural strength retains at the same level of pure PLA.The notch impact strength reaches to 4.50±0.73 kJ/m^(2),which is 2.06 times higher than that of pure PLA.Furthermore,the introduction of biomass fillers increases the crystallization ability of PLA and does not increase the water absorption of the composites.This research demonstrated that PLA composites prepared with biomass fillers from the herbaceous plants(namely herb plastic composites,HPCs)is a material with good comprehensive mechanical properties while retaining the intrinsic particularity of biological sources.
基金funded by the National Key Research and Development Program of China(grant number:2019YFD1101201)the National Natural Science Foundation of China(grant numbers:51773005 and 21905008)the Beijing Natural Science Foundation(grant number:2194071).
文摘To clarify the effects of lignin as a biodegradable filler added into the PLA matrix,PLA/lignin composites with or without silane coupling agent ofγ-(2,3-epoxypropoxy)propy trimethoxysilane(KH560)were prepared by a one-step solvent-free modification method.The effects of KH560 as a compatibilizer on the morphology,chemical structure,crystallization behavior,thermal degradative behavior as well as mechanical strength of the PLA/lignin composites were analyzed in detail.It was found that,after modification by KH560,the fractured surfaces of composites became smooth,suggested sufficient bonding between the lignin and PLA in the composites with KH560 coupling agent molecules.This result further proved by 1H NMR and ATR spectra of the composites that lignin and PLA formed stable chemical bonds with KH560.Due to the toughening effect of KH560,mainly affect the molecular chain mobility,the thermodynamic properties of LG-KH560/PLA composites were all reduced.When compared to the conventional solution modification method of adding silane coupling agents into PLA/lignin,the composites were synthesized via a single-step reactive extrusion modification procedure in this work showed relatively low tensile strength,which mainly because the existence of the free radicals due to coupling agents result in the composite’s deterioration and subsequent weakening of the tensile properties.
基金Project(30870609) supported by the National Natural Science Foundation of ChinaProjects(KJ081205 KJ091213) supported by the Natural Science Foundation of Chongqing Education Committee, China
文摘Nonporous and porous C/PLA/nano-HA composites were fabricated by the process of solvent blending and freeze-drying technique, and the effect of porous structure on the mechanical properties of C/PLA/nano-HA composites scaffold was investigated and analyzed. The results show that the effects of porous structure on the bending strength, modulus and curves of stress and strain were obvious. Compared with nonporous sample, the curves of stress and strain of porous sample show more rough, and alternative phenomenon of stress increase and stress relaxation appears. It is strongly suggested that the fracture model of C/PLA/nano-HA composites scaffold transforms from the local to global load due to the porous structure.
文摘This paper describes the flexural properties of biodegradable composites made using natural fiber and biodegradable plastics. Biodegradable composites were fabricated from bamboo fiber bundles and PLA (polylactic acid) resin. In this research, effect of molding temperature and fiber content on flexural properties of bamboo fiber reinforced composites was investigated. The flexural strength of this composite increased with increasing fiber content up to 70%. The flexural strength of composites decreased at molding temperature of 180°C. Biodegradable composites possessed extremely high flexural strength of 273 MPa, in the case of molding temperature of 160°C and fiber content of 70%.
基金Funded by the Shanxi Province Science Foundation for Youths of China[Nos.2014021020-2 and 2015021076]the Shanxi Province Higher School Science and Technology Innovation Project[No.2015125]+2 种基金the Project of Taiyuan University of Technology[Nos.2013T0202013T0212013T022]
文摘In order to improve the thermal properties of polylactic acid（PLA） filament,nano-SiO_2 was applied to mix with PLA,then they were spun as composite filament by melt-spinning.The dispersion of nano SiO_2 and the fracture surfaces of filaments were studied by scanning electron microscopy（SEM）.The properties of composite filament,such as orientation degree,mechanical properties,and surface friction properties,were analyzed.The thermal performances of composite filament were analyzed by differential scanning calorimetry（DSC） and thermo gravimetric analysis（TGA）.The results showed that the nano-SiO_2 modified by 5% KH-550 could disperse evenly and loosely in nano-scale,and 1 wt% and 3 wt% nano-SiO_2 dispersed throughout PLA evenly.As the quantity of nano-SiO_2 increased,the properties of composite filament,such as orientation degree,friction coefficient,thermal decomposition temperature,and glass transition temperature,increased more or less.The breaking tenacity increased when 1 wt% SiO_2 was added in PLA,but declined when 3 wt% SiO_2 was added.
文摘The hydroxyapatite/polylactide biocomposites were prepared by absorption process in liquid phase. The method avoided many disadvantages, such as inaterfusion of chemical impurity substances, nonuniformity dispersal of HA in PLA, low molecular weight of PLA . HA particles were uniformly dispersed in PLA matrix, and showed well ndhesion with PLA matrix. The biocomposites have the higher mechanical properties and suitable decomposable capability.
基金Shanxi Province Science Foundation for Youths,China(No.2014021020-2)the Projects of Taiyuan University of Technology,China(Nos.2012L074,2013T020,2013T021,and 2013T022)Shanxi Province College Students Training Program,China(No.2013067)
文摘In order to improve the thermal properties of polylactic acid( PLA) master batch,the nano-SiO2 was applied to mixing with PLA. The structure and thermal properties of the composite master batches were studied. The results showed that the nano-SiO2 modified by 3% coupling agent KH-570 could be dispersed evenly in PLA in small scale. The thermal decomposition temperature of composite master batches increased by 6. 20-10. 80 ℃, the glass transition temperature increased by 0. 22-5. 16 ℃,and the heat enthalpy at the glass transition temperature increased by 0. 574-2. 437 J /g,compared with pure PLA. The composite master batch possessed superior thermal stability and heat resistance.
基金the Fundamental Research Funds for the Central Universities,China，National Natural Science Foundation of China，"111 Project" Biomedical Textile Materials Science and Technology,China，the Donghua University Innovation Fund of Graduate Project,China
文摘A new entire biodegradable scaffold has been developed which does not require precellularization before transplantation.This new kind of vascular scaffold prototype made from porous poly-ε-caprolactone( PCL) membrane to provide three-dimensional environment for cell growth, and embedded with weft-knitted polylactic acid( PLA) fabric to support mechanics.The aim of this paper is to study the variation tendency of mechanical properties with the fabric spacing changing.The basic geometrical parameters were measured to characterize properties of the samples.The tensile and compressive elastic recovery of the samples were tested by the universal mechanical tester and radial compression apparatus,respectively.Both tensile and compressive properties enhanced when reducing the fabric spacing of the composite vascular scaffold.
文摘Hydroxyapatite/polylactide (HA/PLA) composites have been intensively investigated for their potential as biodegradable fixation devices to heal bone fractures. However, most of these composites failed to achieve a bone-mimicking level of mechanical properties, which is an essential demand of the targeted application. In this study, the nano-hydroxyapatite/polylactide composites were used as the matrix and continuous phosphate glass fibres (PGF) served as the major reinforcement to obtain the nano-HA/PGF/PLA hybrid composites. While the PGF volume fraction remained constant (25%), the nano-HA content (in weight) varied from 0% to 20%. As nano-HA loading increased, the flexural modulus of the composites increased from 8.70 ± 0.35 GPa to 14.97 ± 1.30 GPa, and the flexural strengths were enhanced from 236.31 ± 10.83 MPa to 310.55 ± 22.88 MPa. However, it is found that the degradation rates are higher with more nano-HA loaded. Enhanced water absorption ability, as well as increased voids in the composites is possible reasons for the accelerated degradation of composites with higher nano-HA loading. The hybrid composites possess mechanical properties that are superior to most of the HA/PLA composites in previous research while maintaining the biodegradability. With a proper loading of nano-HA in composites of 10 weight percent, the composites are also found with improved mechanical properties without catastrophic degradation. The composites developed in this study have great potential as biodegradable bone fixation device with enhanced load-bearing ability as confirmed and superior bioactivity as anticipated.
基金National Natural Science Foundation of China(No.52273054)Shanghai Natural Science Foundation,China(No.20ZR1402200)。
文摘The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by braiding PLA filaments with 4 to 24 spindles on flax yarns.After curing at different temperatures(180℃and 190℃),the core/sheath structural flax/PLA composite yarns were manufactured.According to the results of the tensile test,the flax/PLA composite yarn with 4-spindle PLA yarns as a sheath layer and at a curing temperature of 180℃reached the maximum elastic modulus of about(5.79±0.65)GPa and the maximum tensile strength of about(162.17±18.18)MPa.This flax/PLA composite yarn with good mechanical properties would be suitable for green composites in the automobile manufacturing industry and building materials.
基金National Key Technology R&D Program of China(No.2014BAC13B02)National Natural Science Foundation of China(No.51403035)+1 种基金Programme of Introducing Talents of Discipline to Universities,China(No.105-07-005735)the Fundamental Research Funds for the Central Universities,China(No.15D110510)
文摘In order to prepare cellulose nanocrystals( CNCs)-coated polylactide( PLA) microspheres for the use of drug delivery and tissue engineering,a Pickering emulsion route was applied. The stable Pickering emulsions were prepared using CNCs as efficient stabilizers without any additional surfactant. The microspheres were successfully fabricated after volatilization of the solvent. What's more,the size of microspheres could be controlled by fabrication parameters.
基金supported by grants of the National Nature Science Foundation of China(No.51763007)National Undergraduate Innovation and Entrepreneurship Training Program(No.201910596205).
文摘Spherical carbon particles were prepared by using waste Guilin rice noodles as raw materials.By blending the rice noodles based carbon(RC)powders with polylactic acid(PLA),A series of black RC/PLA 3D printing composites were synthesized and characterized.The mechanical testing result shows that the RC/PLA 3D printing composites display better mechanical properties than that of pure PLA.Moreover,the composite with carbon treated with high temperature carbonization has better impact strength.