In this study,composite films consisting of polylactic acid(PLA),ethyl cellulose(EC),and zein were prepared by solution casting method,and their performance and application in chilled fresh meat preservation were inve...In this study,composite films consisting of polylactic acid(PLA),ethyl cellulose(EC),and zein were prepared by solution casting method,and their performance and application in chilled fresh meat preservation were investigated.The results showed that the three materials had satisfactory compatibility in the composite film.Addition of EC and zein effectively improved the mechanical properties,thermodynamic properties,surface hydrophilicity,oxygen permeability,and degradation properties of PLA films.When the ratio of PLA to EC was 3:7,the tensile strength and elongation at break reached maximum values of 16.6 MPa and 30.5%,respectively.Moreover,under different conditions,the composite film exhibited better degradability than the PLA film.The composite film with a 3:7 ratio of PLA to EC had the best performance,with a degradation rate of 21.75%after 84 days.Chilled fresh meat wrapped with the composite film showed significantly improved antioxidant,antibacterial,and water-holding properties.展开更多
Alcoholysis is one of the most effective methods for recycling polyester plastics.While many researchers claim that both alcohol and polymer reactants are activated simultaneously in the alcoholysis reaction,more reli...Alcoholysis is one of the most effective methods for recycling polyester plastics.While many researchers claim that both alcohol and polymer reactants are activated simultaneously in the alcoholysis reaction,more reliable experimental evidence is needed to fully understand the process,and the catalytic mechanism remains elusive.To address this issue,we proposed a reactant-modulated catalytic depolymerization strategy involving a pre-mixing of alcohol or polylactic acid(PLA)with an organic base catalyst.Through systematic experimental and theoretical investigations,we have confirmed that different intermediates are formed during pre-mixing the catalyst with PLA or methanol,which can either slow down or accelerate the subsequent alcoholysis reaction.By employing the methanol-modulated depolymerization technique,we successfully achieved PLA alcoholysis at temperatures as low as–40℃.We further investigated the solubility and reactivity of different polyesters,including PET,PC,PBS,PBAT,PCL,and PLA,revealing an efficient recycling method for PLA.By optimizing reaction conditions in a continuous flow reactor,we recovered 127.3 g of methyl lactate from 100 g of plastic cups in just 4 h at room temperature.These findings greatly improve our grasp of polyester solvolysis processes and create new opportunities within the plastics sector recycling.展开更多
Polylactic acid(PLA),a biodegradable polymer,exhibits superior mechanical strength and processability.However,its broader adoption is hindered by inherent brittleness,low hydrophilicity,and sluggish crystallization ki...Polylactic acid(PLA),a biodegradable polymer,exhibits superior mechanical strength and processability.However,its broader adoption is hindered by inherent brittleness,low hydrophilicity,and sluggish crystallization kinetics.Chitosan(CS),a natural polysaccharide renowned for its biocompatibility and biodegradability,offers potential to address these limitations.While both materials have garnered significant attention in materials science,research on their integration via melt blending and the resulting performance enhancements for food-contact plastics remains understudied.This research comprehensively explores how different levels of CS content,from 0% to 10%,impact the characteristics of chitosan/polylactic acid(CS/PLA)composites.It specifically analyzes the influence of various CS concentrations on the mechanical attributes,crystallization behavior,thermomechanical properties,and rheological performance of these composites.The study concludes that a CS content of 4% in the CS/PLA composite results in the best overall properties.At this point,its elongation at break and impact strength reached theirmaximum values(16.16% and 20.63 kJ/m^(2)),representing increases of 23.9% and 15.7% compared to pure PLA.At this particular concentration,CS is evenly distributed throughout the PLA matrix,acting as a heterogeneous nucleating agent.It facilitates the crystallization of the composite material and offers effective reinforcement.This study presents a promising approach for developing environmentally friendly and sustainable alternatives to fossil-based plastics,highlighting significant research value and practical application potential.展开更多
An innovative microcrystalline cellulose(MCC)natural fibre powder-reinforced PLA biocomposite was investigated using the hand lay-up technique.The polymer matrix composite(PMC)samples were prepared by varying the weig...An innovative microcrystalline cellulose(MCC)natural fibre powder-reinforced PLA biocomposite was investigated using the hand lay-up technique.The polymer matrix composite(PMC)samples were prepared by varying the weight percentages(wt.%)of both PLA matrix and MCC reinforcement:pure PLA/100:0,90:10,80:20,70:30,60:40 and 50:50 wt.%,respectively.From the results obtained,MCC powder,with its impressive aspect ratio,proved to be an ideal reinforcement for the PLA,exhibiting exceptional mechanical properties.It was evident that the 80:20 wt.%biocomposite sample exhibited the maximum improvement in the tensile,flexural,notched impact,compressive strength and hardness by 28.85%,20.00%,91.66%,21.53%and 35.82%,respectively compared to the pure PLA sample.Similarly,during the thermogravimetric analysis(TGA),the same 80:20 wt.%biocomposite sample showed a minimum weight loss of 20%at 400℃,among others.The morphological study using Field Emission Scanning Electron Microscopy(FE-SEM)revealed that the uniform distribution of cellulose reinforcement in the PLA matrix actively improved the mechanical properties of the biocomposites,especially the optimal 80:20 wt.%sample.Importantly,it was evident that the optimal PLA/cellulose biocomposite sample could be a suitable and alternative sustainable,environmentally friendly and biodegradable material for semi/structural applications,replacing synthetic and traditional components.展开更多
Polylactic acid(PLA)is a potential polymer material used as a substitute for traditional plastics,and the accurate molecular weight distribution range of PLA is strictly required in practical applications.Therefore,ex...Polylactic acid(PLA)is a potential polymer material used as a substitute for traditional plastics,and the accurate molecular weight distribution range of PLA is strictly required in practical applications.Therefore,exploring the relationship between synthetic conditions and PLA molecular weight is crucially important.In this work,direct polycondensation combined with overlay sampling uniform design(OSUD)was applied to synthesize the low molecular weight PLA.Then a multiple regression model and two artificial neural network models on PLA molecular weight versus reaction temperature,reaction time,and catalyst dosage were developed for PLA molecular weight prediction.The characterization results indicated that the low molecular weight PLA was efficiently synthesized under this method.Meanwhile,the experimental dataset acquired from OSUD successfully established three predictive models for PLA molecular weight.Among them,both artificial neural network models had significantly better predictive performance than the regression model.Notably,the radial basis function neural network model had the best predictive accuracy with only 11.9%of mean relative error on the validation dataset,which improved by 67.7%compared with the traditional multiple regression model.This work successfully predicted PLA molecular weight in a direct polycondensation process using artificial neural network models combined with OSUD,which provided guidance for the future implementation of molecular weight-controlled polymer's synthesis.展开更多
The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by b...The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by braiding PLA filaments with 4 to 24 spindles on flax yarns.After curing at different temperatures(180℃and 190℃),the core/sheath structural flax/PLA composite yarns were manufactured.According to the results of the tensile test,the flax/PLA composite yarn with 4-spindle PLA yarns as a sheath layer and at a curing temperature of 180℃reached the maximum elastic modulus of about(5.79±0.65)GPa and the maximum tensile strength of about(162.17±18.18)MPa.This flax/PLA composite yarn with good mechanical properties would be suitable for green composites in the automobile manufacturing industry and building materials.展开更多
Flexible supercapacitors with high mechanical strength,excellent flexibility,and high performance are highly desired to meet the increasing demands of flexible electronics.However,the trade-offbetween mechanical and e...Flexible supercapacitors with high mechanical strength,excellent flexibility,and high performance are highly desired to meet the increasing demands of flexible electronics.However,the trade-offbetween mechanical and electrochemical properties remains challenging.In this context,an interface-engineered strategy approach was proposed to construct polylactic acid(PLA)/polyaniline(PANI)/MXene(PPM)film electrodes for flexible supercapacitor applications.In the PPM electrode,the porous PLA prepared from the nonsolvent-induced-phase-separation method served as an ideal flexible substrate,providing excel-lent flexibility and high mechanical strength,whereas PANI as the coupling agent,enhanced the interfa-cial strength between PLA and the electroactive MXene that was firmly anchored and deposited on PLA through a facile layer-by-layer dip coating method.The tensile strength at break,elongation at break,and toughness of PPM are 53.09 MPa,11.09%,and 4.12 MJ/m^(3),respectively,much higher than those of pure MXene(29.36 MPa,4.62%,and 0.75 MJ/m^(3)).At an optimum mass loading density of 3 mg cm−2 for MXene,the fabricated PPM3 film electrode achieved a high specific capacitance of 290.8 F g^(−1)at a cur-rent density of 1 A g^(−1)in the three-electrode setup,approximately 1.5 times that of 190.8 F g^(−1)for pure MXene.Meanwhile,the symmetric all-solid-state supercapacitor based on PPM3 film electrodes delivers a high specific capacitance of 193.7 F g^(−1)at a current density of 0.25 A g^(−1),with a corresponding high energy density of 9.3 Wh kg^(−1)at a power density of 291.3 W kg^(−1).The SC retains 86%of its original ca-pacitance even bent at 120°and also possesses an excellent fire-retardant ability,demonstrating its great potential for flexible and safe wearable electronics.展开更多
Aim Ciprofloxacin polylactic acid microspheres (CFX-PLA-MS) were preparedusing solvent evaporation method from a solid-in-oil-in-water emulsion system. Methods Orthogonalexperiment was used to optimize the method of C...Aim Ciprofloxacin polylactic acid microspheres (CFX-PLA-MS) were preparedusing solvent evaporation method from a solid-in-oil-in-water emulsion system. Methods Orthogonalexperiment was used to optimize the method of CFX-PLA-MS preparation. Microspheres werecharacterized in terms of morphology, size, encapsulation efficiency, drug loading and in vitro drugrelease. Results The physical state of CFX-PLA-MS was determined by scanning electron microscopy(SEM) and differential scanning calorimetry (DSC) . Microspheres formed were spherical with smoothsurfaces. Drug was enveloped in microspheres without mixing physically with PLA. The averageparticle size was 280.80 ± 0.15 μm, with over 90% of microspheres falling in the range of 250 -390 μm. The encapsulation efficiency was 65.8% ± 0.58% and the drug loading was 34.1% ± 0.51% .In vitro release study revealed a profile of sustained release of Ciprofloxacin from CFX-PLA-MS. Theaccumulated release percentage and half-life (T_(1/2) of Ciprofloxacin microspheres were 84.0% in53.2 h, and 31.9 h, respectively. Higuchi equation was Q= -0.0043 + 0.003 9 t^(1/2), r = 0.9941.Conclusion Ciprofloxacin microspheres have been successfully prepared and sustained release of CFXfrom microspheres is achieved.展开更多
Thermal decomposition of polylactic acid （PLA） was studied in the presence of pine wood sawdust （PS）, walnut shell （WS）, corncob （CC） in order to understand the pyrolytic behavior of these components occurring...Thermal decomposition of polylactic acid （PLA） was studied in the presence of pine wood sawdust （PS）, walnut shell （WS）, corncob （CC） in order to understand the pyrolytic behavior of these components occurring in waste. A thermogravimetric analyzer （TGA） was applied for monitoring the mass loss profiles under heating rate of 10℃·min^-1. Results obtained from this comprehensive investigation indicated that PLA was decomposed in the temperature range 300 -372℃, whereas the thermal degradation temperature of biomass is 183-462℃. The difference of mass loss （AW） between experimental and theoretical ones, calculated as algebraic sums of those from each separated component, is about 17%-46% at 300-400℃. These experimental results indicated a significant synergistic effect during PLA and biomass copyrolysis. Moreover, a kinetic analysis was performed to fit thermogravimetric data, the global processes being considered as one to two consecutive reactions. A reasonable fit to the experimental data was obtained for all materials and their blends.展开更多
The effects of adding poly （ethylene glycol） （PEG） into polylactic acid/thermoplastic starch blends （PLA/TPS） on the properties were investigated by DSC, SEM and mechanical property-testing. The blends of PLA/TP...The effects of adding poly （ethylene glycol） （PEG） into polylactic acid/thermoplastic starch blends （PLA/TPS） on the properties were investigated by DSC, SEM and mechanical property-testing. The blends of PLA/TPS blended with increasing content PEG exhibited lower temperature of glass transition （T） and lower temperature of melting （T） as well as higher melt flow index （MFI）, which indicates the plasticization and proeessability of the composites were dramatically improved. The tensile strength, flexural strength and izod impact strength of PLA/TPS （80/20） increased at first and then decreased with increasing content of PEG due to stronger interfacial adhesion. The optimized mechanical property can be obtained for the blend with 3 wt % PEG. The samples containing PEG after soil burial for 5 months showed quicker degradation being accompanied with large weight loss and mechanical properties loss.展开更多
Biodegradable polymers are highly attractive as potential alternatives to petroleum-based polymers in an attempt to achieve carbon neutrality whilst maintaining the mechanical properties of the structures.Among these ...Biodegradable polymers are highly attractive as potential alternatives to petroleum-based polymers in an attempt to achieve carbon neutrality whilst maintaining the mechanical properties of the structures.Among these polymers,polylactic acid(PLA)is particularly promising due to its good mechanical properties,biocompatibility and thermoplasticity.In this work,we aim to enhance the mechanical properties of PLA using mechanically-defibrated cellulose nanofibers(CNFs)that exhibit remarkable mechanical properties and biodegradability.We also employ fused deposition modeling(FDM),one of the three-dimensional printing methods for thermoplastic polymers,for the low-cost fabrication of the products.Mechanically-defibrated CNF-reinforced PLA matrix composites are fabricated by FDM.Their tensile properties are investigated in two printing directions(0°/90°and+45°/-45°).The discussion about the relationship between printing direction and tensile behavoir of mechanically-defibrated CNF-reinforced PLA matrix composite is the unique point of this study.We further discuss the microstructure and fracture surface of mechanically-defibrated CNF-reinforced PLA matrix composite by scanning electron microscope.展开更多
Starch/polylactic acid(PLA) composites were prepared by melt extrusion, with corn starch and PLA as raw materials, glycerol as the plasticizer. Effects of starch/PLA ratio on the interdependence of two-phase and other...Starch/polylactic acid(PLA) composites were prepared by melt extrusion, with corn starch and PLA as raw materials, glycerol as the plasticizer. Effects of starch/PLA ratio on the interdependence of two-phase and other properties of the composites were studied. The combination of results of TGA with SEM indicated that the interdependence between starch and PLA was increased gradually as the starch/PLA ratio reduced. DSC results showed that the glass transition temperature(Tg), melting temperature(Tm) and degree of crystallinity of PLA in composites were increased gradually, whereas the cold crystallization temperature(Tc) was gradually decreased as the starch/PLA ratio reduced. The rheological properties of composites were closely related with the interdependence of two-phase, with reducing starch/PLA proportion, the interdependence was increased, and then the strain for storage modulus was firstl reduced and then gradually increased. Frequency scanning showed that the storage modulus and complex viscosity were decreased with reducing starch content. As the starch/PLA ratio reduced, the matrix phase PLA was increased, so that the strength of composites was increased gradually, whereas water absorption rate was decreased gradually.展开更多
High-performance liquid chromatography （HPLC） was employed to determine drug release rates based on emamectin benzoate concentrations in the medium. Release kinetics equations were used to fit the drug release behav...High-performance liquid chromatography （HPLC） was employed to determine drug release rates based on emamectin benzoate concentrations in the medium. Release kinetics equations were used to fit the drug release behavior. The effects of particle size and release medium pH on the release rate were also investigated. The indoor toxicity of emamectin benzoate-loaded polylactic acid microspheres on the diamondback moth larva （Plutella xylostella） was studied to explore drug sustained-release performance. In acidic and neutral media, the drug release behavior of the microspheres was in accord with the first-order kinetics equation. Increasing the spray dosage of emamectin benzoate-loaded polylactic acid microspheres initially resulted in an equivalent insecticidal efficacy with the conventional emamectin benzoate microemulsion. However, the drug persistence period was four-fold longer than that observed using the conventional formulation. The developed emamectin benzoate-loaded polylactic acid microspheres showed dramatic sustained-release performance. A treatment threshold of greater than 35 mg mL-1 was established for an efficient accumulated release concentration of emamectin benzoate-loaded microspheres.展开更多
At present,the clinical reconstruction of the auricle usually adopts the strategy of taking autologous costal cartilage.This method has great trauma to patients,poor plasticity and inaccurate shaping.Three-dimensional...At present,the clinical reconstruction of the auricle usually adopts the strategy of taking autologous costal cartilage.This method has great trauma to patients,poor plasticity and inaccurate shaping.Three-dimensional(3D)printing technology has made a great breakthrough in the clinical application of orthopedic implants.This study explored the combination of 3D printing and tissue engineering to precisely reconstruct the auricle.First,a polylactic acid(PLA)polymer scaffold with a precisely customized patient appearance was fabricated,and then auricle cartilage fragments were loaded into the 3D-printed porous PLA scaffold to promote auricle reconstruction.In vitro,gelatin methacrylamide(GelMA)hydrogels loaded with different sizes of rabbit ear cartilage fragments were studied to assess the regenerative activity of various autologous cartilage fragments.In vivo,rat ear cartilage fragments were placed in an accurately designed porous PLA polymer ear scaffold to promote auricle reconstruction.The results indicated that the chondrocytes in the cartilage fragments could maintain the morphological phenotype in vitro.After three months of implantation observation,it was conducive to promoting the subsequent regeneration of cartilage in vivo.The autologous cartilage fragments combined with 3D printing technology show promising potential in auricle reconstruction.展开更多
Polylactic acid(PLA)possesses good mechanical and biodegradability properties which make it a suitable material for polymer composites whereas brittleness and high costs limit its utilization in various applications.T...Polylactic acid(PLA)possesses good mechanical and biodegradability properties which make it a suitable material for polymer composites whereas brittleness and high costs limit its utilization in various applications.The reinforcement of natural fibres with biopolymers has been formed to be an efficient technique to develop composites having the ability to be fully biodegradable.This study concerns with the incorporation of various percentages of untreated and alkali-treated Coir Fibres(CF)and pineapple leaf fibres(PALF)in PLA biocomposites and characterizations of flexural,morphological and dynamic mechanical properties.Flexural properties showed that the treated C1P1 hybrid composites(C1P1A)displayed highest flexural strength(35.81 MPa)and modulus(5.28 GPa)among all hybrid biocomposites.Scanning Electron Microscopy(SEM)revealed a behaviour of fibre-matrix adhesion in untreated treated biocomposites.SEM observation revealed good dispersion of the fillers in PLA.Dynamic mechanical analysis revealed that C1P1A showed highest glass transition temperature(Tg)and storage modulus(E')while untreated C3P7 displayed the least Tg and E'.Overall findings showed that alkali-treated hybrid biocomposites(CF/PALF/PLA)especially C1P1A have improved flexural properties,dynamic and morphological properties over untreated biocomposites.Success of these findings will provide attracting consideration of these hybrid biocomposites for various lightweight uses in a broad selection of industrial applications such as biomedical sectors,automobile,construction,electronics equipment,and hardware tools.展开更多
Lanthanum(La)has tremendous potential in the treatment and prevention of bone diseases especially osteoporosis and metabolic disorders.However,controlling its distribution and keeping the release of La^(3+)ions sustai...Lanthanum(La)has tremendous potential in the treatment and prevention of bone diseases especially osteoporosis and metabolic disorders.However,controlling its distribution and keeping the release of La^(3+)ions sustained and steady in the body is still a big challenge.In this study,we prepared La-OCP powders via co-precipitation method,and further prepared La-OCP/PLA porous scaffolds by 3 D printing.La^(3+)was successfully introduced into the OCP crystal structure and substituted Ca^(2+)at the Ca-5 and Ca-8 sites.In particular,some La^(3+)ions were deposited on the crystal surface in the form of nanoparticles.Both octacalcium phosphate(OCP,Ca_(8)H_(2)(PO_(4))_6·5 H_(2)O)crystals and nanoparticles played as the carriers for La^(3+)ions.The La-OCP/PLA scaffolds displayed obvious mineralization effects and sustained release of La^(3+).The scaffolds contained a uniform structure with rough micro surface topography which acted as a suitable pathway for BMSCs cells to adhere,grow and proliferation.At a certain La^(3+)concentration,the extracts from La-OCP/PLA scaffolds increased the expression of osteogenesis-related genes,thus promoting the osteogenic differentiation of BMSCs.Moreover,the extracts regulated the immune responses.The experiment in vivo proved that La-OCP/PLA porous scaffolds were safe and could enhance bone defect regeneration in vivo.These findings suggest that 3 D printed La-OCP/PLA porous scaffolds have promising potentials in bone tissue engineering.展开更多
With the increasing awareness of environmental protection and rational utilization of resources,natural fiber reinforced composites have shown broad development prospects.Apocynum fiber,known as the“king of wild fibe...With the increasing awareness of environmental protection and rational utilization of resources,natural fiber reinforced composites have shown broad development prospects.Apocynum fiber,known as the“king of wild fiber”,not only has moisture absorption,air permeability,and good mechanical properties but also has many health-related advantages such as antibacterial properties.In this study,four types of needle-punched Apocynum fiber and ramie fiber mat reinforced polylactic acid(PLA)composites were fabricated.Mechanical and thermal properties of the composites were tested and analyzed.The results showed that compared with those of the ramie fiber finish needle-punched mat reinforced composites,the tensile strength and the tensile modulus of Apocynum fiber finish needle-punched mat reinforced composites had increased by 15.3%and 60.1%,respectively.In comparison,the bending strength and the bending modulus were decreased by 21.8%and 7.6%,respectively.Moreover,compared with the Apocynum fiber finish needled-punched mat reinforced composites and the ramie fiber finish needle-punched mat reinforced composites,the Apocynum 50/ramie 50 finish needle-punched mat reinforced composites had the best tensile and bending properties.The after-fracture morphology was detected by a scanning electron microscope(SEM).The thermal properties of the composites were also characterized.It was found that the thermal properties of the four types of composites showed very similar behaviors.展开更多
Microfibrillated cellulose(MFC)is often added to polylactic acid(PLA)matrixes as a reinforcing filler to obtain fully-biodegradable composites with improved mechanical properties.However,the incompatibility between MF...Microfibrillated cellulose(MFC)is often added to polylactic acid(PLA)matrixes as a reinforcing filler to obtain fully-biodegradable composites with improved mechanical properties.However,the incompatibility between MFC and the PLA matrix limits the mechanical performance of MFC-reinforced PLA composites.In this paper,DL-lactic acid-grafted-MFC(MFC-g-DL)was used to improve the compatibility with PLA.Reinforced composites were prepared by melt extrusion and hot-cold pressing.The tensile strength of the PLA/MFC-g-DL composite increased by 22.1%compared with that of PLA after adding 1%MFC-g-DL.Scanning electron microscopy(SEM),differential scanning calorimetry(DSC),and dynamic thermomechanical analysis(DMA)were used to explore the enhancement mechanism.The energy dissipation in the MFC network and the improved compatibility between PLA and MFC-g-DL played important roles in the reinforcement.The SEM results showed that there was a closer combination between PLA and MFC-g-DL.The DSC results showed that the addition of cellulose changed the glass transition temperature,melting temperature,and crystallization temperature of PLA.The TG results showed that the initial and maximum decomposition temperature were lower than those of PLA.The ultraviolet spectra showed that the composite had good transparency at a low concentration of MFC-g-DL.展开更多
Polylactic acid(PLA)bioplastic is a common material used in Fused Deposition Modeling(FDM)3D printing.It is biodegradable and environmentally friendly biopolymer which made out of corn.However,it exhibits weak mechani...Polylactic acid(PLA)bioplastic is a common material used in Fused Deposition Modeling(FDM)3D printing.It is biodegradable and environmentally friendly biopolymer which made out of corn.However,it exhibits weak mechanical properties which reduced its usability as a functional prototype in a real-world application.In the present study,two PLA composites are created through coextruded with 3K carbon fibres and twisted Kevlar string(as core fibre)to form a fibre reinforced parts(FRP).The mechanical strength of printed parts was examined using ASTM D638 standard with a strain rate of 1 mm/min.It has been demonstrated that the FRPs coextruded with 3K carbon fibres had achieved significant improvement in Young’s modulus(+180.6%,9.205 GPa),ultimate tensile strength(+175.3%,103 MPa)and maximum tensile strain(+21.6%,1.833%).Although the Young’s modulus of Kevlar FRP was found to be similar to as compared to unreinforced PLA(~3.29 GPa),it has gained significant increment in terms of maximum tensile strain(+179.7%,104.64 MPa),and maximum tensile strain(+257%,5.384%).Thus,this study revealed two unique composite materials,in which the 3K carbon FRP can offer stiff and high strength structure while Kevlar FRP offers similar strength but at a higher elasticity.展开更多
The main objective of this work was to study and develop composite materials by experiments with mixtures of synthetic(glass fiber, carbon fiber) and natural fiber(durian skin fiber) reinforcements on a polylactic aci...The main objective of this work was to study and develop composite materials by experiments with mixtures of synthetic(glass fiber, carbon fiber) and natural fiber(durian skin fiber) reinforcements on a polylactic acid(PLA) matrix composite, because of its excellent mechanical properties. Durian skin fiber(DSF) is a natural waste throughout Thailand, and an alternative to recycling is to realize its potential as a new reinforcement through mixing and the injection molding processes. The flexural strength(σ_(F)) and flexural modulus(E_(F)) of the composites from specimens showed a maximum value by content of durian skin fiber at 10 wt%, for good performance relative to particle dispersion between the matrix and the fiber, and showed a minimum value by content of durian skin fiber at 20 wt%, because the reinforcement material affects the mechanical properties in the experiments.展开更多
文摘In this study,composite films consisting of polylactic acid(PLA),ethyl cellulose(EC),and zein were prepared by solution casting method,and their performance and application in chilled fresh meat preservation were investigated.The results showed that the three materials had satisfactory compatibility in the composite film.Addition of EC and zein effectively improved the mechanical properties,thermodynamic properties,surface hydrophilicity,oxygen permeability,and degradation properties of PLA films.When the ratio of PLA to EC was 3:7,the tensile strength and elongation at break reached maximum values of 16.6 MPa and 30.5%,respectively.Moreover,under different conditions,the composite film exhibited better degradability than the PLA film.The composite film with a 3:7 ratio of PLA to EC had the best performance,with a degradation rate of 21.75%after 84 days.Chilled fresh meat wrapped with the composite film showed significantly improved antioxidant,antibacterial,and water-holding properties.
文摘Alcoholysis is one of the most effective methods for recycling polyester plastics.While many researchers claim that both alcohol and polymer reactants are activated simultaneously in the alcoholysis reaction,more reliable experimental evidence is needed to fully understand the process,and the catalytic mechanism remains elusive.To address this issue,we proposed a reactant-modulated catalytic depolymerization strategy involving a pre-mixing of alcohol or polylactic acid(PLA)with an organic base catalyst.Through systematic experimental and theoretical investigations,we have confirmed that different intermediates are formed during pre-mixing the catalyst with PLA or methanol,which can either slow down or accelerate the subsequent alcoholysis reaction.By employing the methanol-modulated depolymerization technique,we successfully achieved PLA alcoholysis at temperatures as low as–40℃.We further investigated the solubility and reactivity of different polyesters,including PET,PC,PBS,PBAT,PCL,and PLA,revealing an efficient recycling method for PLA.By optimizing reaction conditions in a continuous flow reactor,we recovered 127.3 g of methyl lactate from 100 g of plastic cups in just 4 h at room temperature.These findings greatly improve our grasp of polyester solvolysis processes and create new opportunities within the plastics sector recycling.
基金funded by National Natural Science Foundation of China(NSFC),grant number(No.U2341237).
文摘Polylactic acid(PLA),a biodegradable polymer,exhibits superior mechanical strength and processability.However,its broader adoption is hindered by inherent brittleness,low hydrophilicity,and sluggish crystallization kinetics.Chitosan(CS),a natural polysaccharide renowned for its biocompatibility and biodegradability,offers potential to address these limitations.While both materials have garnered significant attention in materials science,research on their integration via melt blending and the resulting performance enhancements for food-contact plastics remains understudied.This research comprehensively explores how different levels of CS content,from 0% to 10%,impact the characteristics of chitosan/polylactic acid(CS/PLA)composites.It specifically analyzes the influence of various CS concentrations on the mechanical attributes,crystallization behavior,thermomechanical properties,and rheological performance of these composites.The study concludes that a CS content of 4% in the CS/PLA composite results in the best overall properties.At this point,its elongation at break and impact strength reached theirmaximum values(16.16% and 20.63 kJ/m^(2)),representing increases of 23.9% and 15.7% compared to pure PLA.At this particular concentration,CS is evenly distributed throughout the PLA matrix,acting as a heterogeneous nucleating agent.It facilitates the crystallization of the composite material and offers effective reinforcement.This study presents a promising approach for developing environmentally friendly and sustainable alternatives to fossil-based plastics,highlighting significant research value and practical application potential.
基金funding from Researchers Supporting Project Number(RSP2024R355),King Saud University,Riyadh,Saudi Arabia.
文摘An innovative microcrystalline cellulose(MCC)natural fibre powder-reinforced PLA biocomposite was investigated using the hand lay-up technique.The polymer matrix composite(PMC)samples were prepared by varying the weight percentages(wt.%)of both PLA matrix and MCC reinforcement:pure PLA/100:0,90:10,80:20,70:30,60:40 and 50:50 wt.%,respectively.From the results obtained,MCC powder,with its impressive aspect ratio,proved to be an ideal reinforcement for the PLA,exhibiting exceptional mechanical properties.It was evident that the 80:20 wt.%biocomposite sample exhibited the maximum improvement in the tensile,flexural,notched impact,compressive strength and hardness by 28.85%,20.00%,91.66%,21.53%and 35.82%,respectively compared to the pure PLA sample.Similarly,during the thermogravimetric analysis(TGA),the same 80:20 wt.%biocomposite sample showed a minimum weight loss of 20%at 400℃,among others.The morphological study using Field Emission Scanning Electron Microscopy(FE-SEM)revealed that the uniform distribution of cellulose reinforcement in the PLA matrix actively improved the mechanical properties of the biocomposites,especially the optimal 80:20 wt.%sample.Importantly,it was evident that the optimal PLA/cellulose biocomposite sample could be a suitable and alternative sustainable,environmentally friendly and biodegradable material for semi/structural applications,replacing synthetic and traditional components.
基金funded by the Zhejiang Provincial Natural Science Foundation of China(LD21B060001)the National Natural Science Foundation of China(22078296,21576240).
文摘Polylactic acid(PLA)is a potential polymer material used as a substitute for traditional plastics,and the accurate molecular weight distribution range of PLA is strictly required in practical applications.Therefore,exploring the relationship between synthetic conditions and PLA molecular weight is crucially important.In this work,direct polycondensation combined with overlay sampling uniform design(OSUD)was applied to synthesize the low molecular weight PLA.Then a multiple regression model and two artificial neural network models on PLA molecular weight versus reaction temperature,reaction time,and catalyst dosage were developed for PLA molecular weight prediction.The characterization results indicated that the low molecular weight PLA was efficiently synthesized under this method.Meanwhile,the experimental dataset acquired from OSUD successfully established three predictive models for PLA molecular weight.Among them,both artificial neural network models had significantly better predictive performance than the regression model.Notably,the radial basis function neural network model had the best predictive accuracy with only 11.9%of mean relative error on the validation dataset,which improved by 67.7%compared with the traditional multiple regression model.This work successfully predicted PLA molecular weight in a direct polycondensation process using artificial neural network models combined with OSUD,which provided guidance for the future implementation of molecular weight-controlled polymer's synthesis.
基金National Natural Science Foundation of China(No.52273054)Shanghai Natural Science Foundation,China(No.20ZR1402200)。
文摘The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by braiding PLA filaments with 4 to 24 spindles on flax yarns.After curing at different temperatures(180℃and 190℃),the core/sheath structural flax/PLA composite yarns were manufactured.According to the results of the tensile test,the flax/PLA composite yarn with 4-spindle PLA yarns as a sheath layer and at a curing temperature of 180℃reached the maximum elastic modulus of about(5.79±0.65)GPa and the maximum tensile strength of about(162.17±18.18)MPa.This flax/PLA composite yarn with good mechanical properties would be suitable for green composites in the automobile manufacturing industry and building materials.
基金supported by the Young Elite Scien-tists Sponsorship Program by Tianjin(No.TJSQNTJ-2018-03)the Deanship of Scientific Re-search at Northern Border University,Arar,KSA for funding this re-search work through the project number NBU-FPEJ-2024-2605-01.
文摘Flexible supercapacitors with high mechanical strength,excellent flexibility,and high performance are highly desired to meet the increasing demands of flexible electronics.However,the trade-offbetween mechanical and electrochemical properties remains challenging.In this context,an interface-engineered strategy approach was proposed to construct polylactic acid(PLA)/polyaniline(PANI)/MXene(PPM)film electrodes for flexible supercapacitor applications.In the PPM electrode,the porous PLA prepared from the nonsolvent-induced-phase-separation method served as an ideal flexible substrate,providing excel-lent flexibility and high mechanical strength,whereas PANI as the coupling agent,enhanced the interfa-cial strength between PLA and the electroactive MXene that was firmly anchored and deposited on PLA through a facile layer-by-layer dip coating method.The tensile strength at break,elongation at break,and toughness of PPM are 53.09 MPa,11.09%,and 4.12 MJ/m^(3),respectively,much higher than those of pure MXene(29.36 MPa,4.62%,and 0.75 MJ/m^(3)).At an optimum mass loading density of 3 mg cm−2 for MXene,the fabricated PPM3 film electrode achieved a high specific capacitance of 290.8 F g^(−1)at a cur-rent density of 1 A g^(−1)in the three-electrode setup,approximately 1.5 times that of 190.8 F g^(−1)for pure MXene.Meanwhile,the symmetric all-solid-state supercapacitor based on PPM3 film electrodes delivers a high specific capacitance of 193.7 F g^(−1)at a current density of 0.25 A g^(−1),with a corresponding high energy density of 9.3 Wh kg^(−1)at a power density of 291.3 W kg^(−1).The SC retains 86%of its original ca-pacitance even bent at 120°and also possesses an excellent fire-retardant ability,demonstrating its great potential for flexible and safe wearable electronics.
基金National Natural Science Foundation of Guangdong Province (020885,980504).
文摘Aim Ciprofloxacin polylactic acid microspheres (CFX-PLA-MS) were preparedusing solvent evaporation method from a solid-in-oil-in-water emulsion system. Methods Orthogonalexperiment was used to optimize the method of CFX-PLA-MS preparation. Microspheres werecharacterized in terms of morphology, size, encapsulation efficiency, drug loading and in vitro drugrelease. Results The physical state of CFX-PLA-MS was determined by scanning electron microscopy(SEM) and differential scanning calorimetry (DSC) . Microspheres formed were spherical with smoothsurfaces. Drug was enveloped in microspheres without mixing physically with PLA. The averageparticle size was 280.80 ± 0.15 μm, with over 90% of microspheres falling in the range of 250 -390 μm. The encapsulation efficiency was 65.8% ± 0.58% and the drug loading was 34.1% ± 0.51% .In vitro release study revealed a profile of sustained release of Ciprofloxacin from CFX-PLA-MS. Theaccumulated release percentage and half-life (T_(1/2) of Ciprofloxacin microspheres were 84.0% in53.2 h, and 31.9 h, respectively. Higuchi equation was Q= -0.0043 + 0.003 9 t^(1/2), r = 0.9941.Conclusion Ciprofloxacin microspheres have been successfully prepared and sustained release of CFXfrom microspheres is achieved.
文摘Thermal decomposition of polylactic acid （PLA） was studied in the presence of pine wood sawdust （PS）, walnut shell （WS）, corncob （CC） in order to understand the pyrolytic behavior of these components occurring in waste. A thermogravimetric analyzer （TGA） was applied for monitoring the mass loss profiles under heating rate of 10℃·min^-1. Results obtained from this comprehensive investigation indicated that PLA was decomposed in the temperature range 300 -372℃, whereas the thermal degradation temperature of biomass is 183-462℃. The difference of mass loss （AW） between experimental and theoretical ones, calculated as algebraic sums of those from each separated component, is about 17%-46% at 300-400℃. These experimental results indicated a significant synergistic effect during PLA and biomass copyrolysis. Moreover, a kinetic analysis was performed to fit thermogravimetric data, the global processes being considered as one to two consecutive reactions. A reasonable fit to the experimental data was obtained for all materials and their blends.
文摘The effects of adding poly （ethylene glycol） （PEG） into polylactic acid/thermoplastic starch blends （PLA/TPS） on the properties were investigated by DSC, SEM and mechanical property-testing. The blends of PLA/TPS blended with increasing content PEG exhibited lower temperature of glass transition （T） and lower temperature of melting （T） as well as higher melt flow index （MFI）, which indicates the plasticization and proeessability of the composites were dramatically improved. The tensile strength, flexural strength and izod impact strength of PLA/TPS （80/20） increased at first and then decreased with increasing content of PEG due to stronger interfacial adhesion. The optimized mechanical property can be obtained for the blend with 3 wt % PEG. The samples containing PEG after soil burial for 5 months showed quicker degradation being accompanied with large weight loss and mechanical properties loss.
基金supported by the Program for Creation of Interdisciplinary Research and Ensemble Program of Frontier Research Institute for Interdisciplinary Sciences,Tohoku University。
文摘Biodegradable polymers are highly attractive as potential alternatives to petroleum-based polymers in an attempt to achieve carbon neutrality whilst maintaining the mechanical properties of the structures.Among these polymers,polylactic acid(PLA)is particularly promising due to its good mechanical properties,biocompatibility and thermoplasticity.In this work,we aim to enhance the mechanical properties of PLA using mechanically-defibrated cellulose nanofibers(CNFs)that exhibit remarkable mechanical properties and biodegradability.We also employ fused deposition modeling(FDM),one of the three-dimensional printing methods for thermoplastic polymers,for the low-cost fabrication of the products.Mechanically-defibrated CNF-reinforced PLA matrix composites are fabricated by FDM.Their tensile properties are investigated in two printing directions(0°/90°and+45°/-45°).The discussion about the relationship between printing direction and tensile behavoir of mechanically-defibrated CNF-reinforced PLA matrix composite is the unique point of this study.We further discuss the microstructure and fracture surface of mechanically-defibrated CNF-reinforced PLA matrix composite by scanning electron microscope.
基金Funded by the National Forestry Public Welfare Industry Major Projects of Scientific Research(No.201504502)National Natural Science Foundation of China(No.31200442)Supported by the Post Doctorate Research from the Ministry of Science and Technology of China(No.2014M550178)
文摘Starch/polylactic acid(PLA) composites were prepared by melt extrusion, with corn starch and PLA as raw materials, glycerol as the plasticizer. Effects of starch/PLA ratio on the interdependence of two-phase and other properties of the composites were studied. The combination of results of TGA with SEM indicated that the interdependence between starch and PLA was increased gradually as the starch/PLA ratio reduced. DSC results showed that the glass transition temperature(Tg), melting temperature(Tm) and degree of crystallinity of PLA in composites were increased gradually, whereas the cold crystallization temperature(Tc) was gradually decreased as the starch/PLA ratio reduced. The rheological properties of composites were closely related with the interdependence of two-phase, with reducing starch/PLA proportion, the interdependence was increased, and then the strain for storage modulus was firstl reduced and then gradually increased. Frequency scanning showed that the storage modulus and complex viscosity were decreased with reducing starch content. As the starch/PLA ratio reduced, the matrix phase PLA was increased, so that the strength of composites was increased gradually, whereas water absorption rate was decreased gradually.
基金supported by the National Key Research and Development Program of China (2016YFD0200502, 2017YFD0200301)
文摘High-performance liquid chromatography （HPLC） was employed to determine drug release rates based on emamectin benzoate concentrations in the medium. Release kinetics equations were used to fit the drug release behavior. The effects of particle size and release medium pH on the release rate were also investigated. The indoor toxicity of emamectin benzoate-loaded polylactic acid microspheres on the diamondback moth larva （Plutella xylostella） was studied to explore drug sustained-release performance. In acidic and neutral media, the drug release behavior of the microspheres was in accord with the first-order kinetics equation. Increasing the spray dosage of emamectin benzoate-loaded polylactic acid microspheres initially resulted in an equivalent insecticidal efficacy with the conventional emamectin benzoate microemulsion. However, the drug persistence period was four-fold longer than that observed using the conventional formulation. The developed emamectin benzoate-loaded polylactic acid microspheres showed dramatic sustained-release performance. A treatment threshold of greater than 35 mg mL-1 was established for an efficient accumulated release concentration of emamectin benzoate-loaded microspheres.
基金supported by the National Natural Science Foundation of China(No.81171731)the Project of Chengdu Science and Technology Bureau(Nos.2021-YF05-01619-SN and 2021-RC05-00022-CG)+2 种基金the Science and Technology Project of Tibet Autonomous Region(Nos.XZ202202YD0013C and XZ201901-GB-08)the Sichuan Science and Technology Program(No.2022YFG0066)the 1·3·5 Project for Disciplines of Excellence,West China Hospital,Sichuan University(Nos.ZYJC21026,ZYGD21001 and ZYJC21077).
文摘At present,the clinical reconstruction of the auricle usually adopts the strategy of taking autologous costal cartilage.This method has great trauma to patients,poor plasticity and inaccurate shaping.Three-dimensional(3D)printing technology has made a great breakthrough in the clinical application of orthopedic implants.This study explored the combination of 3D printing and tissue engineering to precisely reconstruct the auricle.First,a polylactic acid(PLA)polymer scaffold with a precisely customized patient appearance was fabricated,and then auricle cartilage fragments were loaded into the 3D-printed porous PLA scaffold to promote auricle reconstruction.In vitro,gelatin methacrylamide(GelMA)hydrogels loaded with different sizes of rabbit ear cartilage fragments were studied to assess the regenerative activity of various autologous cartilage fragments.In vivo,rat ear cartilage fragments were placed in an accurately designed porous PLA polymer ear scaffold to promote auricle reconstruction.The results indicated that the chondrocytes in the cartilage fragments could maintain the morphological phenotype in vitro.After three months of implantation observation,it was conducive to promoting the subsequent regeneration of cartilage in vivo.The autologous cartilage fragments combined with 3D printing technology show promising potential in auricle reconstruction.
基金gratitude to Institute of Tropical Forestry and Forest Products(INTROP),Universiti Putra Malaysia for supporting the funding of research through Grant No:6369108funded by Researchers Supporting Project number(RSP-2021/117),King Saud University,Riyadh,Saudi Arabia.
文摘Polylactic acid(PLA)possesses good mechanical and biodegradability properties which make it a suitable material for polymer composites whereas brittleness and high costs limit its utilization in various applications.The reinforcement of natural fibres with biopolymers has been formed to be an efficient technique to develop composites having the ability to be fully biodegradable.This study concerns with the incorporation of various percentages of untreated and alkali-treated Coir Fibres(CF)and pineapple leaf fibres(PALF)in PLA biocomposites and characterizations of flexural,morphological and dynamic mechanical properties.Flexural properties showed that the treated C1P1 hybrid composites(C1P1A)displayed highest flexural strength(35.81 MPa)and modulus(5.28 GPa)among all hybrid biocomposites.Scanning Electron Microscopy(SEM)revealed a behaviour of fibre-matrix adhesion in untreated treated biocomposites.SEM observation revealed good dispersion of the fillers in PLA.Dynamic mechanical analysis revealed that C1P1A showed highest glass transition temperature(Tg)and storage modulus(E')while untreated C3P7 displayed the least Tg and E'.Overall findings showed that alkali-treated hybrid biocomposites(CF/PALF/PLA)especially C1P1A have improved flexural properties,dynamic and morphological properties over untreated biocomposites.Success of these findings will provide attracting consideration of these hybrid biocomposites for various lightweight uses in a broad selection of industrial applications such as biomedical sectors,automobile,construction,electronics equipment,and hardware tools.
基金financially supported by the National Natural Science Foundation of China(No.82072074)the National Natural Science Foundation of China(No.51801198)+2 种基金funds of Scientific and Technological Plan of Fujian Province(No.2020Y0083)the Natural and Science Foundation of Fujian Province(No.2019I0027)the Funds of Scientific and Technological Plan of Fujian Province(No.2020L3026)。
文摘Lanthanum(La)has tremendous potential in the treatment and prevention of bone diseases especially osteoporosis and metabolic disorders.However,controlling its distribution and keeping the release of La^(3+)ions sustained and steady in the body is still a big challenge.In this study,we prepared La-OCP powders via co-precipitation method,and further prepared La-OCP/PLA porous scaffolds by 3 D printing.La^(3+)was successfully introduced into the OCP crystal structure and substituted Ca^(2+)at the Ca-5 and Ca-8 sites.In particular,some La^(3+)ions were deposited on the crystal surface in the form of nanoparticles.Both octacalcium phosphate(OCP,Ca_(8)H_(2)(PO_(4))_6·5 H_(2)O)crystals and nanoparticles played as the carriers for La^(3+)ions.The La-OCP/PLA scaffolds displayed obvious mineralization effects and sustained release of La^(3+).The scaffolds contained a uniform structure with rough micro surface topography which acted as a suitable pathway for BMSCs cells to adhere,grow and proliferation.At a certain La^(3+)concentration,the extracts from La-OCP/PLA scaffolds increased the expression of osteogenesis-related genes,thus promoting the osteogenic differentiation of BMSCs.Moreover,the extracts regulated the immune responses.The experiment in vivo proved that La-OCP/PLA porous scaffolds were safe and could enhance bone defect regeneration in vivo.These findings suggest that 3 D printed La-OCP/PLA porous scaffolds have promising potentials in bone tissue engineering.
基金National Natural Science Foundation of China(No.50803010)Natural Science Foundation of Shanghai,China(No.14ZR1400100)。
文摘With the increasing awareness of environmental protection and rational utilization of resources,natural fiber reinforced composites have shown broad development prospects.Apocynum fiber,known as the“king of wild fiber”,not only has moisture absorption,air permeability,and good mechanical properties but also has many health-related advantages such as antibacterial properties.In this study,four types of needle-punched Apocynum fiber and ramie fiber mat reinforced polylactic acid(PLA)composites were fabricated.Mechanical and thermal properties of the composites were tested and analyzed.The results showed that compared with those of the ramie fiber finish needle-punched mat reinforced composites,the tensile strength and the tensile modulus of Apocynum fiber finish needle-punched mat reinforced composites had increased by 15.3%and 60.1%,respectively.In comparison,the bending strength and the bending modulus were decreased by 21.8%and 7.6%,respectively.Moreover,compared with the Apocynum fiber finish needled-punched mat reinforced composites and the ramie fiber finish needle-punched mat reinforced composites,the Apocynum 50/ramie 50 finish needle-punched mat reinforced composites had the best tensile and bending properties.The after-fracture morphology was detected by a scanning electron microscope(SEM).The thermal properties of the composites were also characterized.It was found that the thermal properties of the four types of composites showed very similar behaviors.
基金the Natural Science Foundation of China(No.32071704).
文摘Microfibrillated cellulose(MFC)is often added to polylactic acid(PLA)matrixes as a reinforcing filler to obtain fully-biodegradable composites with improved mechanical properties.However,the incompatibility between MFC and the PLA matrix limits the mechanical performance of MFC-reinforced PLA composites.In this paper,DL-lactic acid-grafted-MFC(MFC-g-DL)was used to improve the compatibility with PLA.Reinforced composites were prepared by melt extrusion and hot-cold pressing.The tensile strength of the PLA/MFC-g-DL composite increased by 22.1%compared with that of PLA after adding 1%MFC-g-DL.Scanning electron microscopy(SEM),differential scanning calorimetry(DSC),and dynamic thermomechanical analysis(DMA)were used to explore the enhancement mechanism.The energy dissipation in the MFC network and the improved compatibility between PLA and MFC-g-DL played important roles in the reinforcement.The SEM results showed that there was a closer combination between PLA and MFC-g-DL.The DSC results showed that the addition of cellulose changed the glass transition temperature,melting temperature,and crystallization temperature of PLA.The TG results showed that the initial and maximum decomposition temperature were lower than those of PLA.The ultraviolet spectra showed that the composite had good transparency at a low concentration of MFC-g-DL.
基金This project is funded by Universiti Tunku Abdul Rahman through the grant number IPSR/RMC/UTARRF/2018-C2/T02.
文摘Polylactic acid(PLA)bioplastic is a common material used in Fused Deposition Modeling(FDM)3D printing.It is biodegradable and environmentally friendly biopolymer which made out of corn.However,it exhibits weak mechanical properties which reduced its usability as a functional prototype in a real-world application.In the present study,two PLA composites are created through coextruded with 3K carbon fibres and twisted Kevlar string(as core fibre)to form a fibre reinforced parts(FRP).The mechanical strength of printed parts was examined using ASTM D638 standard with a strain rate of 1 mm/min.It has been demonstrated that the FRPs coextruded with 3K carbon fibres had achieved significant improvement in Young’s modulus(+180.6%,9.205 GPa),ultimate tensile strength(+175.3%,103 MPa)and maximum tensile strain(+21.6%,1.833%).Although the Young’s modulus of Kevlar FRP was found to be similar to as compared to unreinforced PLA(~3.29 GPa),it has gained significant increment in terms of maximum tensile strain(+179.7%,104.64 MPa),and maximum tensile strain(+257%,5.384%).Thus,this study revealed two unique composite materials,in which the 3K carbon FRP can offer stiff and high strength structure while Kevlar FRP offers similar strength but at a higher elasticity.
文摘The main objective of this work was to study and develop composite materials by experiments with mixtures of synthetic(glass fiber, carbon fiber) and natural fiber(durian skin fiber) reinforcements on a polylactic acid(PLA) matrix composite, because of its excellent mechanical properties. Durian skin fiber(DSF) is a natural waste throughout Thailand, and an alternative to recycling is to realize its potential as a new reinforcement through mixing and the injection molding processes. The flexural strength(σ_(F)) and flexural modulus(E_(F)) of the composites from specimens showed a maximum value by content of durian skin fiber at 10 wt%, for good performance relative to particle dispersion between the matrix and the fiber, and showed a minimum value by content of durian skin fiber at 20 wt%, because the reinforcement material affects the mechanical properties in the experiments.