The structural parameters of the aggregated state of polyamide (PA)-1010 annealed at various temperatures were computed by means of the desmearing intensity from Smalt Angle X-ray Scattering (SAXS) measurements and by...The structural parameters of the aggregated state of polyamide (PA)-1010 annealed at various temperatures were computed by means of the desmearing intensity from Smalt Angle X-ray Scattering (SAXS) measurements and by using the concept of the distance distribution function. The results indicated that the structural parameters of the aggregated state were strongly dependent upon heat treatment conditions and the maximum values of the structural parameters were obtained for the samples annealed at T = 175 degrees C. The particle size Z annealed at different temperature was ranged between 8.1-12.8nm, and the values of the distance distribution function P-max(Z) were obtained when Z = 4.0-6.8 nm. Using one dimension electron density correlation function (1D EDCF) method long period (L) and thickness of the lamellar (d(0)) were estimated and were found to increase with the increase of the degree of crystallinity.展开更多
In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ fo...In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ for Polyamide-1010 samples with various annealing treatment.Through extrapolating method,the Tg obtained was approximately 58℃.Based on the one-dimensional electron density correlation function of partially crystalline polymers,some structural parameters of Polyamide-1010 were determined by SAXS.展开更多
基金The Project was supported by the National Key Projects for Fundamental Research"Macromolecular Condensed State",The State Science and Technology Commission of China
文摘The structural parameters of the aggregated state of polyamide (PA)-1010 annealed at various temperatures were computed by means of the desmearing intensity from Smalt Angle X-ray Scattering (SAXS) measurements and by using the concept of the distance distribution function. The results indicated that the structural parameters of the aggregated state were strongly dependent upon heat treatment conditions and the maximum values of the structural parameters were obtained for the samples annealed at T = 175 degrees C. The particle size Z annealed at different temperature was ranged between 8.1-12.8nm, and the values of the distance distribution function P-max(Z) were obtained when Z = 4.0-6.8 nm. Using one dimension electron density correlation function (1D EDCF) method long period (L) and thickness of the lamellar (d(0)) were estimated and were found to increase with the increase of the degree of crystallinity.
文摘In this work,the influence of heat treatment on Polyamide-1010 structure of aggregation state was studied by using WAXD and SAXS techniques.The results showed that the best crystallinity was obtained nearby T=175℃ for Polyamide-1010 samples with various annealing treatment.Through extrapolating method,the Tg obtained was approximately 58℃.Based on the one-dimensional electron density correlation function of partially crystalline polymers,some structural parameters of Polyamide-1010 were determined by SAXS.