A new type of magnesium oxychloride cement(MOC)was prepared based on calcined MgO powder from hydromagnesite in Tibet,China,with the addition of MgCl_(2),a by-product of potassium extraction from the salt lake.The eff...A new type of magnesium oxychloride cement(MOC)was prepared based on calcined MgO powder from hydromagnesite in Tibet,China,with the addition of MgCl_(2),a by-product of potassium extraction from the salt lake.The effect of MgO on the microstructure and properties of magnesium oxychloride cement was investigated under different calcination temperatures and time of hydromagnesite,and the hydration process,pore structure and hydration products of the materials were investigated by isothermal calorimeter,MIP,XRD,and SEM,and the mechanical properties of the materials were examined by compressive strength test.The compressive strength test shows that under the optimal conditions(800℃-2 h),the compressive strength of MOC is 75.65 MPa for 7 d and 87.98 MPa for 28 d in the indoor environment.The main exothermic period of MOC is delayed by about 10 h compared with that of 500℃-2 h and extended by about 30 h in the process of MOC preparation,which led to the alleviation of the exothermic concentration phenomenon,and the initial solidification time of the MOC specimens is 5.25 h,and the final solidification time is 11.82 h.The MOC phase maintained in indoor air for 28 d mainly consist of P5 and unreacted MgO,and the P5 in the matrix shows the slat-like shape and fills the gaps in the form of needles and rods,and the total porosity is 18.55%.展开更多
基金Funded by the Xining Key R&D and Transformation Program(No.2024-Y-11)the Qinghai Province“Kunlun Talents-Highend Innovation and Entrepreneurship Talents”Top Talents。
文摘A new type of magnesium oxychloride cement(MOC)was prepared based on calcined MgO powder from hydromagnesite in Tibet,China,with the addition of MgCl_(2),a by-product of potassium extraction from the salt lake.The effect of MgO on the microstructure and properties of magnesium oxychloride cement was investigated under different calcination temperatures and time of hydromagnesite,and the hydration process,pore structure and hydration products of the materials were investigated by isothermal calorimeter,MIP,XRD,and SEM,and the mechanical properties of the materials were examined by compressive strength test.The compressive strength test shows that under the optimal conditions(800℃-2 h),the compressive strength of MOC is 75.65 MPa for 7 d and 87.98 MPa for 28 d in the indoor environment.The main exothermic period of MOC is delayed by about 10 h compared with that of 500℃-2 h and extended by about 30 h in the process of MOC preparation,which led to the alleviation of the exothermic concentration phenomenon,and the initial solidification time of the MOC specimens is 5.25 h,and the final solidification time is 11.82 h.The MOC phase maintained in indoor air for 28 d mainly consist of P5 and unreacted MgO,and the P5 in the matrix shows the slat-like shape and fills the gaps in the form of needles and rods,and the total porosity is 18.55%.