Strontium aluminate long persistence phos phors are synthesized by combustion method. By control- ling the raw material ratio （Sr/Al）, the effects of phase composition on subsequent spectroscopic properties of phosp...Strontium aluminate long persistence phos phors are synthesized by combustion method. By control- ling the raw material ratio （Sr/Al）, the effects of phase composition on subsequent spectroscopic properties of phosphors are studied. Results show that the phase com-position changes from strontium-rich phase to aluminum- rich phase with the decrease of Sr/AI： when the rate of Al/Sr changes from 3：1 to 1：1, the main crystal phase of samples is Sr3Al206, and it exhibits the characteristic fluorescence of Eu^3＋ in the lattice of Sr3Al206; when the rate of Al/Sr is between 1：2 and 2：7, phase composition is the mixture of SrAl204 and SrAl4OT, and it emits the characteristic fluorescence of Eu^2＋ in SrAl204 but not in SrAl4OT; when Al/Sr decreases to 1：4 or even 1：12, the main crystal phase of samples transform into SrAl12019, and the characteristic emission peak is about 470 nm, which corresponds to the characteristic emission of Eu2＋ in SrAl12019. At the end of the article, the influence laws of two different synthesis methods on phase composition of samples between high-temperature solid method and combustion method are compared. Compared with the high-temperature solid method, the rule of influence is similar, but the mole ratio of Al/Sr in products is always higher than the initial ratio of the raw material, and com-pounds like Sr4Al14025 are not obtained by combustion method.展开更多
基金financially supported by the National Natural Science Foundation of China(No.NSFC50962001)the Scientific Research Foundation of Beifang Ethnic University for Nationalities(No.2010Y042)
文摘Strontium aluminate long persistence phos phors are synthesized by combustion method. By control- ling the raw material ratio （Sr/Al）, the effects of phase composition on subsequent spectroscopic properties of phosphors are studied. Results show that the phase com-position changes from strontium-rich phase to aluminum- rich phase with the decrease of Sr/AI： when the rate of Al/Sr changes from 3：1 to 1：1, the main crystal phase of samples is Sr3Al206, and it exhibits the characteristic fluorescence of Eu^3＋ in the lattice of Sr3Al206; when the rate of Al/Sr is between 1：2 and 2：7, phase composition is the mixture of SrAl204 and SrAl4OT, and it emits the characteristic fluorescence of Eu^2＋ in SrAl204 but not in SrAl4OT; when Al/Sr decreases to 1：4 or even 1：12, the main crystal phase of samples transform into SrAl12019, and the characteristic emission peak is about 470 nm, which corresponds to the characteristic emission of Eu2＋ in SrAl12019. At the end of the article, the influence laws of two different synthesis methods on phase composition of samples between high-temperature solid method and combustion method are compared. Compared with the high-temperature solid method, the rule of influence is similar, but the mole ratio of Al/Sr in products is always higher than the initial ratio of the raw material, and com-pounds like Sr4Al14025 are not obtained by combustion method.