Novel ceramics from waste material made of(x) paper ash–(80-x) cullet–20 kaolin clay(10 wt% ≤ x ≤ 30 wt%) were successfully synthesized using a conventional solid-state reaction technique. Energy-dispersive X-ray ...Novel ceramics from waste material made of(x) paper ash–(80-x) cullet–20 kaolin clay(10 wt% ≤ x ≤ 30 wt%) were successfully synthesized using a conventional solid-state reaction technique. Energy-dispersive X-ray analysis confirmed the presence of Si, Ca, Al, and Fe in the waste material for preparing these ceramics. The influence of the cullet content on the phase structures and the dielectric properties of these ceramics were systematically investigated. The impedance spectra were verified in the range from 1 Hz to 10 MHz at room temperature. The phase of the ceramics was found to primarily consist of wollastonite(CaSiO_3), along with minor phases of γ-dicalcium silicate(Ca_2SiO_4) and quartz(SiO_2). The sample with a cullet content of 55 wt% possessed the optimum wollastonite structure and exhibited good dielectric properties. An increase of the cullet content beyond 55 wt% resulted in a structural change from wollastonite to dicalcium silicate, a decrease in dielectric constant, and an increase in dielectric loss. All experimental results suggested that these novel ceramics from waste are applicable for electronic devices.展开更多
Material conversion from paper sludge ash （PSA） in NaOH solution was attempted to synthesize the adsorbent for removal of inorganic pollutants, such as Pb^2＋, NH^4＋ and PO4^3- from aqueous solution. PSA of 0.5 g w...Material conversion from paper sludge ash （PSA） in NaOH solution was attempted to synthesize the adsorbent for removal of inorganic pollutants, such as Pb^2＋, NH^4＋ and PO4^3- from aqueous solution. PSA of 0.5 g was added into 10 mL of 3 mol/L NaOH solution, and then heated at 80, 120, and 160℃ for 6-48 hr to obtain the product. PSA mainly composed of two crystalline phases, gehlenite （Ca2Al2SiO7） and anorthite （CaAl2Si2O8）, and amorphous phase. Hydroxysodalite （Na6Al6Si6O24-8H2O） was formed at 80℃, and anorthite dissolved, whereas gehlenite remained unaffected. Katoite （Ca3Al2SiO4（OH）8） was formed over 120℃, and hydroxycancrinite （Nas（OH）2Al6Si6O24·2H2O） was formed at 160℃, due to the dissolution of both gehlenite and anorthite. Specific surface areas of the products were almost same and were higher than that of raw ash. Cation exchange capacities （CECs） of the products were also higher than that of raw ash, and CEC obtained at lower temperature was higher. Removal abilities of products for Pb^2＋, NH4＋, and PO4^3- were higher than that of raw ash. With increasing reaction temperature, the removal efficiencies of Pb^2＋ and NH4＋ decreased due to the decrease of CEC of the product, while removal efficiency for PO4^3- was almost same. The concentrations of Si and AI in the solution and the crystalline phases in the solid during the reaction explain the formation of the product phases at each temperature.展开更多
基金the financial support from the Ministry of Higher Education, Universiti Teknologi Malaysia via Grants of Vote: 08H42 and 4F752
文摘Novel ceramics from waste material made of(x) paper ash–(80-x) cullet–20 kaolin clay(10 wt% ≤ x ≤ 30 wt%) were successfully synthesized using a conventional solid-state reaction technique. Energy-dispersive X-ray analysis confirmed the presence of Si, Ca, Al, and Fe in the waste material for preparing these ceramics. The influence of the cullet content on the phase structures and the dielectric properties of these ceramics were systematically investigated. The impedance spectra were verified in the range from 1 Hz to 10 MHz at room temperature. The phase of the ceramics was found to primarily consist of wollastonite(CaSiO_3), along with minor phases of γ-dicalcium silicate(Ca_2SiO_4) and quartz(SiO_2). The sample with a cullet content of 55 wt% possessed the optimum wollastonite structure and exhibited good dielectric properties. An increase of the cullet content beyond 55 wt% resulted in a structural change from wollastonite to dicalcium silicate, a decrease in dielectric constant, and an increase in dielectric loss. All experimental results suggested that these novel ceramics from waste are applicable for electronic devices.
基金supported by the Mukai Science and Technology Foundation and the Intelligent Cosmos Academic Foundation
文摘Material conversion from paper sludge ash （PSA） in NaOH solution was attempted to synthesize the adsorbent for removal of inorganic pollutants, such as Pb^2＋, NH^4＋ and PO4^3- from aqueous solution. PSA of 0.5 g was added into 10 mL of 3 mol/L NaOH solution, and then heated at 80, 120, and 160℃ for 6-48 hr to obtain the product. PSA mainly composed of two crystalline phases, gehlenite （Ca2Al2SiO7） and anorthite （CaAl2Si2O8）, and amorphous phase. Hydroxysodalite （Na6Al6Si6O24-8H2O） was formed at 80℃, and anorthite dissolved, whereas gehlenite remained unaffected. Katoite （Ca3Al2SiO4（OH）8） was formed over 120℃, and hydroxycancrinite （Nas（OH）2Al6Si6O24·2H2O） was formed at 160℃, due to the dissolution of both gehlenite and anorthite. Specific surface areas of the products were almost same and were higher than that of raw ash. Cation exchange capacities （CECs） of the products were also higher than that of raw ash, and CEC obtained at lower temperature was higher. Removal abilities of products for Pb^2＋, NH4＋, and PO4^3- were higher than that of raw ash. With increasing reaction temperature, the removal efficiencies of Pb^2＋ and NH4＋ decreased due to the decrease of CEC of the product, while removal efficiency for PO4^3- was almost same. The concentrations of Si and AI in the solution and the crystalline phases in the solid during the reaction explain the formation of the product phases at each temperature.