Oolitic iron ore is one of the most important iron resources. This paper reports the recovery of iron from high phosphorus oolitic iron ore using coal-based reduction and magnetic separation. The influences of reducti...Oolitic iron ore is one of the most important iron resources. This paper reports the recovery of iron from high phosphorus oolitic iron ore using coal-based reduction and magnetic separation. The influences of reduction temperature, reduction time, C/O mole ratio, and CaO content on the metallization degree and iron recovery were investigated in detail. Experimental results show that reduced products with the metallization degree of 95.82% could be produced under the optimal conditions （i.e., reduction temperature, 1250℃; reduction time, 50 min; C/O mole ratio, 2.0; and CaO content, 10wt%）. The magnetic concentrate containing 89.63wt% Fe with the iron recovery of 96.21% was obtained. According to the mineralogical and morphologic analysis, the iron minerals had been reduced and iron was mainly enriched into the metallic iron phase embedded in the slag matrix in the form of spherical particles. Apatite was also reduced to phosphorus, which partially migrated into the metallic iron phase.展开更多
The technology of direct reduction by adding sodium carbonate （Na2CO3） and magnetic separation was developed to treat Western Australian high phosphorus iron ore. The iron ore and reduced product were investigated b...The technology of direct reduction by adding sodium carbonate （Na2CO3） and magnetic separation was developed to treat Western Australian high phosphorus iron ore. The iron ore and reduced product were investigated by optical microscopy and scanning electron microscopy. It is found that phosphorus exists within limonite in the form of solid solution, which cannot be removed through traditional ways. During reduction roasting, Na2CO3 reacts with gangue minerals （SiO2 and A1203）, forming aluminum silicate-containing phosphorus and damaging the ore structure, which promotes the separation between iron and phosphorus during magnetic separation. Meanwhile, Na2CO3 also improves the growth of iron grains, increasing the iron grade and iron recovery. The iron concentrate, assaying 94.12wt% Fe and 0.07wt% P at the iron recovery of 96.83% and the dephosphorization rate of 74.08%, is obtained under the optimum conditions. The final product （metal iron powder） after briquetting can be used as the burden for steelmaking by an alactrie a.re furnace to rer）la,ce scrar） steel.展开更多
To reveal the formation and characteristics of metallic iron grains in coal-based reduction, oolitic iron ore was isothermally re- duced in various reduction times at various reduction temperatures. The microstructure...To reveal the formation and characteristics of metallic iron grains in coal-based reduction, oolitic iron ore was isothermally re- duced in various reduction times at various reduction temperatures. The microstructure and size of the metallic iron phase were investigated by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and a Bgrimm process mineralogy analyzer. In the results, the re- duced Fe separates from the ore and forms metallic iron protuberances, and then the subsequent reduced Fe diffuses to the protuberances and grows into metallic iron grains. Most of the metallic iron grains exist in the quasi-spherical shape and inlaid in the slag matrix. The cumula- tive frequency of metallic iron grain size is markedly influenced by both reduction time and temperature. With increasing reduction temperature and time, the grain size of metallic iron obviously increases. According to the classical grain growth equation, the growth kinetic parameters, i.e., time exponent, growth activation energy, and pre-exponential constant, are estimated to be 1.3759 ± 0.0374, 103.18 kJ·mol^-1, and 922.05, respec- tively. Using these calculated parameters, a growth model is established to describe the growth behavior of metallic iron grains.展开更多
This study focuses on the reduction of phosphorus from high-phosphorus-content oolitic iron ore via coal-based reduction. The distribution behavior of phosphorus （i.e., the phosphorus content and the phosphorus distr...This study focuses on the reduction of phosphorus from high-phosphorus-content oolitic iron ore via coal-based reduction. The distribution behavior of phosphorus （i.e., the phosphorus content and the phosphorus distribution ratio in the metal, slag, and gas phases） during reduction was investigated in detail. Experimental results showed that the distribution behavior of phosphorus was strongly influenced by the reduction temperature, the reduction time, and the C/O molar ratio. A higher temperature and a longer reaction time were more favor-able for phosphorus reduction and enrichment in the metal phase. An increase in the C/O ratio improved phosphorus reduction but also hin-dered the mass transfer of the reduced phosphorus when the C/O ratio exceeded 2.0. According to scanning electron microscopy analysis, the iron ore was transformed from an integral structure to metal and slag fractions during the reduction process. Apatite in the ore was reduced to P, and the reduced P was mainly enriched in the metal phase. These results suggest that the proposed method may enable utilization of high-phosphorus-content oolitic iron ore resources.展开更多
Iron ore reduction is a primary unit operation in current metallurgy processes and dominates the energy consumption and greenhouse gas(GHG)emissions of the iron-making process,Therefore,even a slight improvement of th...Iron ore reduction is a primary unit operation in current metallurgy processes and dominates the energy consumption and greenhouse gas(GHG)emissions of the iron-making process,Therefore,even a slight improvement of the energy efficiency or GHG emissions of iron ore reduction would yield considerable benefits to the cost of pig iron and,more importantly,to mitigation of the associated carbon footprint.The current study presents a discrete model that describes the iron ore reduction process for a single pellet.The transient reaction progress can be predicted and is validated against experimental measurements under various operating conditions,including different reducing gases and temperatures.The effects of pressure,isothermality,gas composition,and flow rate on reduction are investigated.The reduction rate increases significantly with increasing pressure until 5 atm,and the entire reduction process occurs more slowly under non-isothermal conditions than under isothermal conditions.This work provides a solid foundation for the development of a comprehensive particulate system model that considers both heat and mass transfer.展开更多
A water cooling treatment was applied in the coal-based reduction of high-chromium vanadium and titanium （V-Ti-Cr） iron ore from the Hongge region of Panzhihua, China. Its effects on the metallization ratio （η）, ...A water cooling treatment was applied in the coal-based reduction of high-chromium vanadium and titanium （V-Ti-Cr） iron ore from the Hongge region of Panzhihua, China. Its effects on the metallization ratio （η）, S removal ratio （Rs）, and P removal ratio （Rp） were studied and analyzed on the basis of chemical composition determined via inductively coupled plasma optical emission spectroscopy. The metallic iron particle size and the element distribution of Fe, V, Cr, and Ti in a reduced briquette after water cooling treatment at 1350℃ were determined and observed via scanning electron microscopy. The results show that the water cooling treatment improved the η, Rs, and Rp in the coal-based reduction of V-Ti-Cr iron ore compared to those obtained with a furnace cooling treatment. Meanwhile, the particle size of metallic iron obtained via the water cooling treatment was smaller than that of metallic iron obtained via the furnace cooling treatment; however, the particle size reached 70 μm at 1350℃, which is substantially larger than the minimum particle size required （20 μm） for magnetic separation. Therefore, the water cooling treatment described in this work is a good method for improving the quality of metallic iron in coal-based reduction and it could be applied in the coal-based reduction of V-Ti-Cr iron ore followed by magnetic separation.展开更多
Beneficiation of Malaysian iron ore is becoming necessary as iron resources are depleting. However, the upgrading process is challenging because of the weak magnetic properties of Malaysian iron ore. In this study, bi...Beneficiation of Malaysian iron ore is becoming necessary as iron resources are depleting. However, the upgrading process is challenging because of the weak magnetic properties of Malaysian iron ore. In this study, bio-char derived from oil palm empty fruit bunch （EFB） was utilized as an energy source for reduction roasting. Mixtures of Malaysian iron ore and the bio-char were pressed into briquettes and subjected to reduction roasting processes at 873-1173 K. The extent of reduction was estimated on the basis of mass loss, and the mag-netization of samples was measured using a vibrating sample magnetometer （VSM）. When reduced at 873 K, the original goethite-rich ore was converted into hematite. An increase in temperature to 1073 K caused a significant conversion of hematite into magnetite and enhanced the magnetic susceptibility and saturation magnetization of samples. The magnetic properties diminished at 1173 K as the iron ore was par-tially reduced to wustite. This reduction roasting by using the bio-char can assist in upgrading the iron ore by improving its magnetic proper-ties展开更多
Reduction roasting-acid leaching process was utilized to process high-iron-content manganese oxide ore using black charcoal as reductant. The results indicate that, compared with the traditional reductant of anthracit...Reduction roasting-acid leaching process was utilized to process high-iron-content manganese oxide ore using black charcoal as reductant. The results indicate that, compared with the traditional reductant of anthracite, higher manganese extraction efficiency is achieved at lower roasting temperature and shorter residence time. The effects of roasting parameters on the leaching efficiency of Mn and Fe were studied, and the optimal parameters are determined as follows: roasting temperature is 650 °C, residence time is 40 min, and black charcoal dosage is 10%(mass fraction). Under these conditions, the leaching efficiency of Mn reaches 82.37% while that of Fe is controlled below 7%. XRD results show that a majority of MnO2 and Fe2O3 in the raw ore are reduced to MnO and Fe3O4, respectively.展开更多
Ferronickel enrichment and extraction from nickel laterite ore were studied through reduction and magnetic separation. Reduction experiments were performed using hydrogen and carbon monoxide as reductants at different...Ferronickel enrichment and extraction from nickel laterite ore were studied through reduction and magnetic separation. Reduction experiments were performed using hydrogen and carbon monoxide as reductants at different temperatures （700-1000℃）. Magnetic separa- tion of the reduced products was conducted using a SLon-100 cycle pulsating magnetic separator （1.2 T）. Composition analysis indicates that the nickel laterite ore contains a total iron content of 22.50wt% and a total nickel content of 1.91wt%. Its mineral composition mainly con- sists of serpentine, hortonolite, and goethite. During the reduction process, the grade of nickel and iron in the products increases with in- creasing reduction temperature. Although a higher temperature is more favorable for reduction, the temperature exceeding 1000℃ results in sintering of the products, preventing magnetic separation. After magnetic separation, the maximum total nickel and iron concentrations are 5.43wt% and 56.86wt%, and the corresponding recovery rates are 84.38% and 53.76%, respectively.展开更多
An isothermal kinetic study of a novel technique for reducing agglomerated iron ore by volatiles released by pyrolysis of lean-grade non-coking coal was carried out at temperature from 1050 to 1200℃ for 10-120 min. T...An isothermal kinetic study of a novel technique for reducing agglomerated iron ore by volatiles released by pyrolysis of lean-grade non-coking coal was carried out at temperature from 1050 to 1200℃ for 10-120 min. The reduced samples were characterized by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and chemical analysis. A good degree of metallization and reduction was achieved. Gas diffusion through the solid was identified as the reaction-rate-controlling resistance; however, during the initial period, particularly at lower temperatures, resistance to interfacial chemical reaction was also significant, though not dominant. The apparent rate constant was observed to increase marginally with decreasing size of the particles constituting the nuggets. The apparent activation energy of reduction was estimated to be in the range from 49.640 to 51.220 kJ/mol and was not observed to be affected by the particle size. The sulfur and carbon contents in the reduced samples were also determined.展开更多
The increasing consumption of plastics inevitably results in increasing amounts of waste plastics. Because of their long degradation periods, these wastes negatively affect the natural environment. Numerous studies ha...The increasing consumption of plastics inevitably results in increasing amounts of waste plastics. Because of their long degradation periods, these wastes negatively affect the natural environment. Numerous studies have been conducted to recycle and eliminate waste plastics. The potential for recycling waste plastics in the iron and steel industry has been underestimated; the high C and H contents of plastics may make them suitable as alternative reductants in the reduction process of iron ore. This study aims to substitute plastic wastes for coal in reduction melting process and to investigate their performance during reduction at high temperature. We used a common type of waste plastic, polyethylene terephthalate （PET）, because of its high carbon and hydrogen contents. Composite pellets containing PET wastes, coke, and magnetite iron ore were reduced at selected temperatures of 1400 and 1450℃ for reduction time from 2 to 10 min to investigate the reduction melting behavior of these pellets. The results showed that an increased temperature and reduction time increased the reduction ratio of the pellets. The optimum experimental conditions for obtaining metallic iron （iron nuggets） were reduction at 1450℃ for 10 min using composite pellets containing 60% PET and 40% coke.展开更多
A thermodynamic analysis of the carbothermic reduction of high-phosphorus oolitic iron ore（HPOIO） was conducted by the Fact Sage thermochemical software. The effects of temperature, C/O ratio, additive types, and do...A thermodynamic analysis of the carbothermic reduction of high-phosphorus oolitic iron ore（HPOIO） was conducted by the Fact Sage thermochemical software. The effects of temperature, C/O ratio, additive types, and dosages both on the reduction of fluorapatite and the formation of liquid slag were studied. The results show that the minimum thermodynamic reduction temperature of fluorapatite by carbon decreases to about 850°C, which is mainly ascribed to the presence of SiO_2, Al_2O_3, and Fe. The reduction rate of fluorapatite increases and the amount of liquid slag decreases with the rise of C/O ratio. The reduction of fluorapatite is hindered by the addition of CaO and Na_2CO_3, thereby allowing the selective reduction of iron oxides upon controlled C/O ratio. The thermodynamic results obtain in the present work are in good agreement with the experimental results available in the literatures.展开更多
As the emission control regulations get stricter,the NO;reduction in the sintering process becomes an important environmental concern owing to its role in the formation of photochemical smog and acid rain.The NOxemiss...As the emission control regulations get stricter,the NO;reduction in the sintering process becomes an important environmental concern owing to its role in the formation of photochemical smog and acid rain.The NOxemissions from the sintering machine account for 48% of total amount from the iron and steel industry.Thus,it is essential to reduce NO;emissions from the sintering machine,for the achievement of clean production of sinter.Ca-Fe oxides,serving as the main binding phase in the sinter,are therefore used as additives into the sintering mixture to reduce NOxemissions.The results show that the NO;reduction ratio achieves 27.76% with 8% Ca-Fe oxides additives since the Ca-Fe oxides can advance the ignition and inhibit the nitrogen oxidation compared with the conventional condition.Meanwhile,the existence of Ca-Fe oxides was beneficial to the sinter quality since they were typical low melting point compounds.The optimal mass fraction of Ca-Fe oxides additives should be less than 8%since the permeability of sintering bed was significantly decreased with a further increase of the Ca-Fe oxides fines,inhibiting the mineralization reaction of sintering mixture.Additionally,the appropriate particle size can be obtained when mixing an equal amount of Ca-Fe oxides additives of-0.5 mm and 0.5-3.0 mm in size.展开更多
Aiming at recovering iron from high-iron-content copper slag, this article introduced a combination technol- ogy of deep reduction and magnetic beneficiation, investigated the iron recovery efficiency and optimized th...Aiming at recovering iron from high-iron-content copper slag, this article introduced a combination technol- ogy of deep reduction and magnetic beneficiation, investigated the iron recovery efficiency and optimized the technical conditions. When coke powder with 86wt% fixed carbon was used as a reductant, iron was successfully extracted from the copper slag. Under the optimized condition of the coke powder content of 14wt%, the calcium-to-silicon mass ratio （Ca/Si） of 0.2, the roasting temperature of 1300℃, the roasting time of 3 h, the grinding time of 20 min, and the magnetic field intensity of 61 kA-m-1, the iron recovery rate of the copper slag can reach 91.82%, and the extracted iron powder has an iron grade of 96.21%. With the characteristics of high iron grade and low impurity content, the extracted iron powder can be used as high-quality raw materials of weathering steel.展开更多
Iron nugget and boron-rich slag can be obtained in a short time through high-temperature reduction of boron- bearing iron concentrate by carbonaceous material, both of which are agglomerated together as a carbon compo...Iron nugget and boron-rich slag can be obtained in a short time through high-temperature reduction of boron- bearing iron concentrate by carbonaceous material, both of which are agglomerated together as a carbon composite pellet. This is a novel flow sheet for the comprehensive utilization of boron-bearing iron concentrate to produce a new kind of man-made boron ore. The effect of reducing agent species （i.e., carbon species） on the reduction and melting process of the composite pellet was investigated at a laboratory scale in the present work. The results show that, the reduction rate of the composite pellet increases from bituminite, anthracite, to coke at temperatures ranging from 950 to 1300~C. Reduction temperature has an important effect on the microstructure of reduced pellets. Carbon species also affects the behavior of reduced metallic iron particles. The anthracite-bearing composite pellet melts faster than the bituminite- bearing composite pellet, and the coke-bearing composite pellet cannot melt due to the high fusion point of coke ash. With anthracite as the reducing agent, the recovery rates of iron and boron are 96.5% and 95.7%, respectively. This work can help us get a further understanding of the new process mechanism.展开更多
Based on the fluidized roasting reduction technology of low-grade pyrolusite coupling with pretreatment of stone coal, the manganese reduction efficiency was investigated and technical conditions were optimized. It is...Based on the fluidized roasting reduction technology of low-grade pyrolusite coupling with pretreatment of stone coal, the manganese reduction efficiency was investigated and technical conditions were optimized. It is found that the optimum manganese reduction efficiency can be up to 98.97% under the conditions that the mass ratio of stone coal to pyrolusite is 3：1, the roasting temperature of stone coal is 1000℃, the roasting temperature of pyrolusite is 800℃, and the roasting time is 2 h. Other low-grade pyrolusite ores in China from Guangxi, Hunan, and Guizhou Provinces were tested and all these minerals responded well, giving -99% manganese reduction efficiency. Meanwhile, the reduction kinetic model has been established. It is confirmed that the reduction process is controlled by the interface chemical reaction. The apparent activation energy is 36.397 kJ/mol.展开更多
To achieve high efficiency utilization of Panzhihua vanadium titano-magnetite, a new process of metalizing reduction and magnetic separation based on hot briquetting is proposed, and factors that affect the cold stren...To achieve high efficiency utilization of Panzhihua vanadium titano-magnetite, a new process of metalizing reduction and magnetic separation based on hot briquetting is proposed, and factors that affect the cold strength of the hot-briquetting products and the efficiency of reduction and magnetic separation are successively investigated through laboratory experiments. The relevant mechanisms are elucidated on the basis of microstructural observations. Experimental results show that the optimal process parameters for hot briquetting include a hot briquetting temperature of 475°C, a carbon ratio of 1.2, ore and coal particle sizes of less than 74 μm. Additionally, with respect to metalizing reduction and magnetic separation, the rational parameters include a magnetic field intensity of 50 mT, a reduction temperature of 1350°C, a reduction time of 60 min, and a carbon ratio of 1.2. Under these above conditions, the crushing strength of the hot-briquetting agglomerates is 1480 N, and the recovery ratios of iron, vanadium, and titanium are as high as 91.19%, 61.82%, and 85.31%, respectively. The new process of metalizing reduction and magnetic separation based on hot briquetting demonstrates the evident technological advantages of high efficiency separation of iron from other valuable elements in the vanadium titano-magnetite.展开更多
The reduction of vanadium titano-magnetite pellets by H_2-CO at temperatures from 850 to 1050°C was investigated in this paper. The influences of pre-oxidation treatment, reduction temperature, and V_（H_2）/（V_...The reduction of vanadium titano-magnetite pellets by H_2-CO at temperatures from 850 to 1050°C was investigated in this paper. The influences of pre-oxidation treatment, reduction temperature, and V_（H_2）/（V_（H_2） ＋ VCO） on the metallization degree were studied. The results showed that pre-oxidation played a substantial role in the reduction of vanadium titano-magnetite pellets. During the reduction process, the metallization degree increased with increasing temperature and increasing V_（H_2） /（V_（H_2） ＋ VCO）. The phase transformation of pre-oxidized vanadium titano-magnetite pellets during the reduction process under an H_2 atmosphere and a CO atmosphere was discussed, and the reduced samples were analyzed by scanning electron microscopy（SEM） in conjunction with back scatter electron（BSE） imaging. The results show that the difference in thermodynamic reducing ability between H_2 and CO is not the only factor that leads to differences in the reduction results obtained using different atmospheres. Some of Fe_（3-x）Ti_xO_4 cannot be reduced under a CO atmosphere because of the densification of particles＇ structure and because of the enrichment of Mg in unreacted cores. By contrast, a loose structure of particles was obtained when the pellets were reduced under an H_2 atmosphere and this structure decreased the resistance to gas diffusion. Moreover, the phenomenon of Mg enrichment in unreacted cores disappeared during H_2 reduction. Both the lower resistance to gas diffusion and the lack of Mg enrichment facilitated the reduction of vanadium titano-magnetite.展开更多
To process optimization and improve the degree of reduction, a two-step experiment was designed. The experiment was carried out in the micro-fluidized bed. The reactor in the micro-fluidized bed is operated as a diffe...To process optimization and improve the degree of reduction, a two-step experiment was designed. The experiment was carried out in the micro-fluidized bed. The reactor in the micro-fluidized bed is operated as a differential reactor to ensure an equal temperature and residence time with the reactor volume. The experiment used Brazilian iron ore and reducing gas of CO. The operating temperature was 400 to 800 ℃ and the residence time was between 10 and 60 min. In correspondence with experiment, microscopic technique was applied too. The test shows that temperature and residence time of the pre-reduction stage have an important effect on the degree of reduction. By using two-step experiment, the maximum value of reduction degree increases by 44.1% compared with the maximum value of traditional reduction experiment. Microscopic analysis shows that the specific surface area, surface morphology and texture of reduced iron ore after pre-reduction stage have an important effect on the degree of final reduction too.展开更多
Micro-fluidized bed reactor is a new research method for the reduction of iron ore fines. The reactor is op- erated as a differential reactor to ensure a constant gas concentration and temperature within the reactor v...Micro-fluidized bed reactor is a new research method for the reduction of iron ore fines. The reactor is op- erated as a differential reactor to ensure a constant gas concentration and temperature within the reactor volume. In order to understand the dynamic process of the reduction reaction in micro-fluidized bed, a series of kinetic experi- ments were designed. In the micro fluidized bed, the use of shrinking core model describes the dynamic behavior of reduction of iron ore. And the apparent activation energy is calculated in the range of 700--850 ~C while the initial atmosphere is 100% content of CO.展开更多
基金supported by the National Natural Science Foundation of China(Nos.51134002 and 51074036)
文摘Oolitic iron ore is one of the most important iron resources. This paper reports the recovery of iron from high phosphorus oolitic iron ore using coal-based reduction and magnetic separation. The influences of reduction temperature, reduction time, C/O mole ratio, and CaO content on the metallization degree and iron recovery were investigated in detail. Experimental results show that reduced products with the metallization degree of 95.82% could be produced under the optimal conditions （i.e., reduction temperature, 1250℃; reduction time, 50 min; C/O mole ratio, 2.0; and CaO content, 10wt%）. The magnetic concentrate containing 89.63wt% Fe with the iron recovery of 96.21% was obtained. According to the mineralogical and morphologic analysis, the iron minerals had been reduced and iron was mainly enriched into the metallic iron phase embedded in the slag matrix in the form of spherical particles. Apatite was also reduced to phosphorus, which partially migrated into the metallic iron phase.
基金support by China Scholarship Council(No.201206370127)support from CSIRO,Australia
文摘The technology of direct reduction by adding sodium carbonate （Na2CO3） and magnetic separation was developed to treat Western Australian high phosphorus iron ore. The iron ore and reduced product were investigated by optical microscopy and scanning electron microscopy. It is found that phosphorus exists within limonite in the form of solid solution, which cannot be removed through traditional ways. During reduction roasting, Na2CO3 reacts with gangue minerals （SiO2 and A1203）, forming aluminum silicate-containing phosphorus and damaging the ore structure, which promotes the separation between iron and phosphorus during magnetic separation. Meanwhile, Na2CO3 also improves the growth of iron grains, increasing the iron grade and iron recovery. The iron concentrate, assaying 94.12wt% Fe and 0.07wt% P at the iron recovery of 96.83% and the dephosphorization rate of 74.08%, is obtained under the optimum conditions. The final product （metal iron powder） after briquetting can be used as the burden for steelmaking by an alactrie a.re furnace to rer）la,ce scrar） steel.
基金financially supported by the National Natural Science Foundation of China(Nos.51134002 and 51604063)the Fundamental Research Funds for the Central Universities(No.N140108001)
文摘To reveal the formation and characteristics of metallic iron grains in coal-based reduction, oolitic iron ore was isothermally re- duced in various reduction times at various reduction temperatures. The microstructure and size of the metallic iron phase were investigated by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and a Bgrimm process mineralogy analyzer. In the results, the re- duced Fe separates from the ore and forms metallic iron protuberances, and then the subsequent reduced Fe diffuses to the protuberances and grows into metallic iron grains. Most of the metallic iron grains exist in the quasi-spherical shape and inlaid in the slag matrix. The cumula- tive frequency of metallic iron grain size is markedly influenced by both reduction time and temperature. With increasing reduction temperature and time, the grain size of metallic iron obviously increases. According to the classical grain growth equation, the growth kinetic parameters, i.e., time exponent, growth activation energy, and pre-exponential constant, are estimated to be 1.3759 ± 0.0374, 103.18 kJ·mol^-1, and 922.05, respec- tively. Using these calculated parameters, a growth model is established to describe the growth behavior of metallic iron grains.
基金financially supported by the National Natural Science Foundation of China(No.51134002)the Fundamental Research Funds for the Central Universi-ties of China(No.N120601004)
文摘This study focuses on the reduction of phosphorus from high-phosphorus-content oolitic iron ore via coal-based reduction. The distribution behavior of phosphorus （i.e., the phosphorus content and the phosphorus distribution ratio in the metal, slag, and gas phases） during reduction was investigated in detail. Experimental results showed that the distribution behavior of phosphorus was strongly influenced by the reduction temperature, the reduction time, and the C/O molar ratio. A higher temperature and a longer reaction time were more favor-able for phosphorus reduction and enrichment in the metal phase. An increase in the C/O ratio improved phosphorus reduction but also hin-dered the mass transfer of the reduced phosphorus when the C/O ratio exceeded 2.0. According to scanning electron microscopy analysis, the iron ore was transformed from an integral structure to metal and slag fractions during the reduction process. Apatite in the ore was reduced to P, and the reduced P was mainly enriched in the metal phase. These results suggest that the proposed method may enable utilization of high-phosphorus-content oolitic iron ore resources.
基金The author is grateful to the National Natural Science Foun-dation of China project(51904122)the Key Project of jiangxi Provincial Research and Development(20192BBHL80016)the Opening Research Project of State Key Laboratory of Multiphase Flow in Power Engineering for financial support of this work.
文摘Iron ore reduction is a primary unit operation in current metallurgy processes and dominates the energy consumption and greenhouse gas(GHG)emissions of the iron-making process,Therefore,even a slight improvement of the energy efficiency or GHG emissions of iron ore reduction would yield considerable benefits to the cost of pig iron and,more importantly,to mitigation of the associated carbon footprint.The current study presents a discrete model that describes the iron ore reduction process for a single pellet.The transient reaction progress can be predicted and is validated against experimental measurements under various operating conditions,including different reducing gases and temperatures.The effects of pressure,isothermality,gas composition,and flow rate on reduction are investigated.The reduction rate increases significantly with increasing pressure until 5 atm,and the entire reduction process occurs more slowly under non-isothermal conditions than under isothermal conditions.This work provides a solid foundation for the development of a comprehensive particulate system model that considers both heat and mass transfer.
基金financially supported by the Programs of the National Natural Science Foundation of China(Nos.51604065,51090384,51674084,51174051,and 51574082)the National Basic Research Program of China(No.2013CB632603)+1 种基金the Fundamental Funds for the Central Universities(Nos.150203003 and 150202001)the National Key Technology Research and development Program(No.2015BAB19B02)
文摘A water cooling treatment was applied in the coal-based reduction of high-chromium vanadium and titanium （V-Ti-Cr） iron ore from the Hongge region of Panzhihua, China. Its effects on the metallization ratio （η）, S removal ratio （Rs）, and P removal ratio （Rp） were studied and analyzed on the basis of chemical composition determined via inductively coupled plasma optical emission spectroscopy. The metallic iron particle size and the element distribution of Fe, V, Cr, and Ti in a reduced briquette after water cooling treatment at 1350℃ were determined and observed via scanning electron microscopy. The results show that the water cooling treatment improved the η, Rs, and Rp in the coal-based reduction of V-Ti-Cr iron ore compared to those obtained with a furnace cooling treatment. Meanwhile, the particle size of metallic iron obtained via the water cooling treatment was smaller than that of metallic iron obtained via the furnace cooling treatment; however, the particle size reached 70 μm at 1350℃, which is substantially larger than the minimum particle size required （20 μm） for magnetic separation. Therefore, the water cooling treatment described in this work is a good method for improving the quality of metallic iron in coal-based reduction and it could be applied in the coal-based reduction of V-Ti-Cr iron ore followed by magnetic separation.
基金financial support from the Interna-tional Islamic University Malaysia through a Research Matching Grant Scheme(RMGS11-004-0017)from the Ministry of Science Technology and Innovation,Malaysia through a Technofund Project(TF1011D220)
文摘Beneficiation of Malaysian iron ore is becoming necessary as iron resources are depleting. However, the upgrading process is challenging because of the weak magnetic properties of Malaysian iron ore. In this study, bio-char derived from oil palm empty fruit bunch （EFB） was utilized as an energy source for reduction roasting. Mixtures of Malaysian iron ore and the bio-char were pressed into briquettes and subjected to reduction roasting processes at 873-1173 K. The extent of reduction was estimated on the basis of mass loss, and the mag-netization of samples was measured using a vibrating sample magnetometer （VSM）. When reduced at 873 K, the original goethite-rich ore was converted into hematite. An increase in temperature to 1073 K caused a significant conversion of hematite into magnetite and enhanced the magnetic susceptibility and saturation magnetization of samples. The magnetic properties diminished at 1173 K as the iron ore was par-tially reduced to wustite. This reduction roasting by using the bio-char can assist in upgrading the iron ore by improving its magnetic proper-ties
基金Project(2013JSJJ028)supported by the Teachers’Research Fund of Central South University,ChinaProject supported by Co-Innovation Center for Clean and Efficient Utilization of Strategic Mineral Resources,China
文摘Reduction roasting-acid leaching process was utilized to process high-iron-content manganese oxide ore using black charcoal as reductant. The results indicate that, compared with the traditional reductant of anthracite, higher manganese extraction efficiency is achieved at lower roasting temperature and shorter residence time. The effects of roasting parameters on the leaching efficiency of Mn and Fe were studied, and the optimal parameters are determined as follows: roasting temperature is 650 °C, residence time is 40 min, and black charcoal dosage is 10%(mass fraction). Under these conditions, the leaching efficiency of Mn reaches 82.37% while that of Fe is controlled below 7%. XRD results show that a majority of MnO2 and Fe2O3 in the raw ore are reduced to MnO and Fe3O4, respectively.
文摘Ferronickel enrichment and extraction from nickel laterite ore were studied through reduction and magnetic separation. Reduction experiments were performed using hydrogen and carbon monoxide as reductants at different temperatures （700-1000℃）. Magnetic separa- tion of the reduced products was conducted using a SLon-100 cycle pulsating magnetic separator （1.2 T）. Composition analysis indicates that the nickel laterite ore contains a total iron content of 22.50wt% and a total nickel content of 1.91wt%. Its mineral composition mainly con- sists of serpentine, hortonolite, and goethite. During the reduction process, the grade of nickel and iron in the products increases with in- creasing reduction temperature. Although a higher temperature is more favorable for reduction, the temperature exceeding 1000℃ results in sintering of the products, preventing magnetic separation. After magnetic separation, the maximum total nickel and iron concentrations are 5.43wt% and 56.86wt%, and the corresponding recovery rates are 84.38% and 53.76%, respectively.
基金financial support from Technical Quality Improvement Programme (TEQIP) phase-IIJadavpur University towards fellowship is also acknowledged
文摘An isothermal kinetic study of a novel technique for reducing agglomerated iron ore by volatiles released by pyrolysis of lean-grade non-coking coal was carried out at temperature from 1050 to 1200℃ for 10-120 min. The reduced samples were characterized by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and chemical analysis. A good degree of metallization and reduction was achieved. Gas diffusion through the solid was identified as the reaction-rate-controlling resistance; however, during the initial period, particularly at lower temperatures, resistance to interfacial chemical reaction was also significant, though not dominant. The apparent rate constant was observed to increase marginally with decreasing size of the particles constituting the nuggets. The apparent activation energy of reduction was estimated to be in the range from 49.640 to 51.220 kJ/mol and was not observed to be affected by the particle size. The sulfur and carbon contents in the reduced samples were also determined.
基金financially supported by Yildiz Technical University Scientific Research Projects Coordination Department (No. 2011-07-02-KAP02)
文摘The increasing consumption of plastics inevitably results in increasing amounts of waste plastics. Because of their long degradation periods, these wastes negatively affect the natural environment. Numerous studies have been conducted to recycle and eliminate waste plastics. The potential for recycling waste plastics in the iron and steel industry has been underestimated; the high C and H contents of plastics may make them suitable as alternative reductants in the reduction process of iron ore. This study aims to substitute plastic wastes for coal in reduction melting process and to investigate their performance during reduction at high temperature. We used a common type of waste plastic, polyethylene terephthalate （PET）, because of its high carbon and hydrogen contents. Composite pellets containing PET wastes, coke, and magnetite iron ore were reduced at selected temperatures of 1400 and 1450℃ for reduction time from 2 to 10 min to investigate the reduction melting behavior of these pellets. The results showed that an increased temperature and reduction time increased the reduction ratio of the pellets. The optimum experimental conditions for obtaining metallic iron （iron nuggets） were reduction at 1450℃ for 10 min using composite pellets containing 60% PET and 40% coke.
基金financially supported by the National Science Fund of China(No.51134002)the Foundation of Jiangxi Educational Committee,China(No.GJJ150624)the Doctoral Scientific Research Foundation of Jiangxi University of Science and Technology,China(No.JXXJBS16004)
文摘A thermodynamic analysis of the carbothermic reduction of high-phosphorus oolitic iron ore（HPOIO） was conducted by the Fact Sage thermochemical software. The effects of temperature, C/O ratio, additive types, and dosages both on the reduction of fluorapatite and the formation of liquid slag were studied. The results show that the minimum thermodynamic reduction temperature of fluorapatite by carbon decreases to about 850°C, which is mainly ascribed to the presence of SiO_2, Al_2O_3, and Fe. The reduction rate of fluorapatite increases and the amount of liquid slag decreases with the rise of C/O ratio. The reduction of fluorapatite is hindered by the addition of CaO and Na_2CO_3, thereby allowing the selective reduction of iron oxides upon controlled C/O ratio. The thermodynamic results obtain in the present work are in good agreement with the experimental results available in the literatures.
文摘As the emission control regulations get stricter,the NO;reduction in the sintering process becomes an important environmental concern owing to its role in the formation of photochemical smog and acid rain.The NOxemissions from the sintering machine account for 48% of total amount from the iron and steel industry.Thus,it is essential to reduce NO;emissions from the sintering machine,for the achievement of clean production of sinter.Ca-Fe oxides,serving as the main binding phase in the sinter,are therefore used as additives into the sintering mixture to reduce NOxemissions.The results show that the NO;reduction ratio achieves 27.76% with 8% Ca-Fe oxides additives since the Ca-Fe oxides can advance the ignition and inhibit the nitrogen oxidation compared with the conventional condition.Meanwhile,the existence of Ca-Fe oxides was beneficial to the sinter quality since they were typical low melting point compounds.The optimal mass fraction of Ca-Fe oxides additives should be less than 8%since the permeability of sintering bed was significantly decreased with a further increase of the Ca-Fe oxides fines,inhibiting the mineralization reaction of sintering mixture.Additionally,the appropriate particle size can be obtained when mixing an equal amount of Ca-Fe oxides additives of-0.5 mm and 0.5-3.0 mm in size.
基金the National High Technology Research and Development Program of China(No.2012AA062406)
文摘Aiming at recovering iron from high-iron-content copper slag, this article introduced a combination technol- ogy of deep reduction and magnetic beneficiation, investigated the iron recovery efficiency and optimized the technical conditions. When coke powder with 86wt% fixed carbon was used as a reductant, iron was successfully extracted from the copper slag. Under the optimized condition of the coke powder content of 14wt%, the calcium-to-silicon mass ratio （Ca/Si） of 0.2, the roasting temperature of 1300℃, the roasting time of 3 h, the grinding time of 20 min, and the magnetic field intensity of 61 kA-m-1, the iron recovery rate of the copper slag can reach 91.82%, and the extracted iron powder has an iron grade of 96.21%. With the characteristics of high iron grade and low impurity content, the extracted iron powder can be used as high-quality raw materials of weathering steel.
基金support by the National Natural Science Foundation of China(No.51274033)
文摘Iron nugget and boron-rich slag can be obtained in a short time through high-temperature reduction of boron- bearing iron concentrate by carbonaceous material, both of which are agglomerated together as a carbon composite pellet. This is a novel flow sheet for the comprehensive utilization of boron-bearing iron concentrate to produce a new kind of man-made boron ore. The effect of reducing agent species （i.e., carbon species） on the reduction and melting process of the composite pellet was investigated at a laboratory scale in the present work. The results show that, the reduction rate of the composite pellet increases from bituminite, anthracite, to coke at temperatures ranging from 950 to 1300~C. Reduction temperature has an important effect on the microstructure of reduced pellets. Carbon species also affects the behavior of reduced metallic iron particles. The anthracite-bearing composite pellet melts faster than the bituminite- bearing composite pellet, and the coke-bearing composite pellet cannot melt due to the high fusion point of coke ash. With anthracite as the reducing agent, the recovery rates of iron and boron are 96.5% and 95.7%, respectively. This work can help us get a further understanding of the new process mechanism.
基金financially supported by the National Natural Science Foundation of China (Nos. 21176026 and 21176242)the National High Technology Research and Development Program of China (No. 2012AA062401)+2 种基金the National Key Technology R&D Program of China (Nos.2012BAB07B05 and 2012BAB14B05)China Ocean Mineral resources R&D Association (No. DY125-15-T-08)the Fundamental Reserarch Funds for the Central Universities of China (No. FRT-TP-09-002B)
文摘Based on the fluidized roasting reduction technology of low-grade pyrolusite coupling with pretreatment of stone coal, the manganese reduction efficiency was investigated and technical conditions were optimized. It is found that the optimum manganese reduction efficiency can be up to 98.97% under the conditions that the mass ratio of stone coal to pyrolusite is 3：1, the roasting temperature of stone coal is 1000℃, the roasting temperature of pyrolusite is 800℃, and the roasting time is 2 h. Other low-grade pyrolusite ores in China from Guangxi, Hunan, and Guizhou Provinces were tested and all these minerals responded well, giving -99% manganese reduction efficiency. Meanwhile, the reduction kinetic model has been established. It is confirmed that the reduction process is controlled by the interface chemical reaction. The apparent activation energy is 36.397 kJ/mol.
基金financially supported by the National High-Tech Research and Development Program of China (No. 2012AA062302)the Major Program of the National Natural Science Foundation of China (No. 51090384)the Fundamental Research Funds of the Central Universities of China (No. N110202001)
文摘To achieve high efficiency utilization of Panzhihua vanadium titano-magnetite, a new process of metalizing reduction and magnetic separation based on hot briquetting is proposed, and factors that affect the cold strength of the hot-briquetting products and the efficiency of reduction and magnetic separation are successively investigated through laboratory experiments. The relevant mechanisms are elucidated on the basis of microstructural observations. Experimental results show that the optimal process parameters for hot briquetting include a hot briquetting temperature of 475°C, a carbon ratio of 1.2, ore and coal particle sizes of less than 74 μm. Additionally, with respect to metalizing reduction and magnetic separation, the rational parameters include a magnetic field intensity of 50 mT, a reduction temperature of 1350°C, a reduction time of 60 min, and a carbon ratio of 1.2. Under these above conditions, the crushing strength of the hot-briquetting agglomerates is 1480 N, and the recovery ratios of iron, vanadium, and titanium are as high as 91.19%, 61.82%, and 85.31%, respectively. The new process of metalizing reduction and magnetic separation based on hot briquetting demonstrates the evident technological advantages of high efficiency separation of iron from other valuable elements in the vanadium titano-magnetite.
基金financially supported by the Fundamental Research Funds for the Central Universities(2014zzts273)
文摘The reduction of vanadium titano-magnetite pellets by H_2-CO at temperatures from 850 to 1050°C was investigated in this paper. The influences of pre-oxidation treatment, reduction temperature, and V_（H_2）/（V_（H_2） ＋ VCO） on the metallization degree were studied. The results showed that pre-oxidation played a substantial role in the reduction of vanadium titano-magnetite pellets. During the reduction process, the metallization degree increased with increasing temperature and increasing V_（H_2） /（V_（H_2） ＋ VCO）. The phase transformation of pre-oxidized vanadium titano-magnetite pellets during the reduction process under an H_2 atmosphere and a CO atmosphere was discussed, and the reduced samples were analyzed by scanning electron microscopy（SEM） in conjunction with back scatter electron（BSE） imaging. The results show that the difference in thermodynamic reducing ability between H_2 and CO is not the only factor that leads to differences in the reduction results obtained using different atmospheres. Some of Fe_（3-x）Ti_xO_4 cannot be reduced under a CO atmosphere because of the densification of particles＇ structure and because of the enrichment of Mg in unreacted cores. By contrast, a loose structure of particles was obtained when the pellets were reduced under an H_2 atmosphere and this structure decreased the resistance to gas diffusion. Moreover, the phenomenon of Mg enrichment in unreacted cores disappeared during H_2 reduction. Both the lower resistance to gas diffusion and the lack of Mg enrichment facilitated the reduction of vanadium titano-magnetite.
基金Item Sponsored by National Natural Science Foundation of China(50834007)
文摘To process optimization and improve the degree of reduction, a two-step experiment was designed. The experiment was carried out in the micro-fluidized bed. The reactor in the micro-fluidized bed is operated as a differential reactor to ensure an equal temperature and residence time with the reactor volume. The experiment used Brazilian iron ore and reducing gas of CO. The operating temperature was 400 to 800 ℃ and the residence time was between 10 and 60 min. In correspondence with experiment, microscopic technique was applied too. The test shows that temperature and residence time of the pre-reduction stage have an important effect on the degree of reduction. By using two-step experiment, the maximum value of reduction degree increases by 44.1% compared with the maximum value of traditional reduction experiment. Microscopic analysis shows that the specific surface area, surface morphology and texture of reduced iron ore after pre-reduction stage have an important effect on the degree of final reduction too.
基金Sponsored by National Natural Science Foundation of China (50834007)
文摘Micro-fluidized bed reactor is a new research method for the reduction of iron ore fines. The reactor is op- erated as a differential reactor to ensure a constant gas concentration and temperature within the reactor volume. In order to understand the dynamic process of the reduction reaction in micro-fluidized bed, a series of kinetic experi- ments were designed. In the micro fluidized bed, the use of shrinking core model describes the dynamic behavior of reduction of iron ore. And the apparent activation energy is calculated in the range of 700--850 ~C while the initial atmosphere is 100% content of CO.