We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner ...We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner than 75μm and was then heated to temperatures up to 900 ℃. New cementitious material was prepared by proportioning fly ash and DAAC, named as AF. X-ray diffraction（XRD） was employed to identify the crystalline phases of DAAC before and after rehydration. The hydration process of AF was analyzed by the heat of hydration and non-evaporable water content（Wn）. The experimental results show that the highest reactivity of DAAC can be obtained by calcining the powder at 700 ℃ and the dehydrated products are mainly β-C2 S and CaO. The cumulative heat of hydration and Wn was found to be strongly dependent on the replacement level of fl y ash, increasing the replacement level of fl y ash lowered them in AF. The strength contribution rates on pozzolanic effect of fl y ash in AF are always negative, showing a contrary tendency of that of cement-fl y ash system.展开更多
TiZrV film is mainly applied in the ultra-high vacuum pipes of storage rings. Thin fihn coatings of palladium, which are added onto the TiZrV film to increase the service life of nonevaporable getters and enhance H2 p...TiZrV film is mainly applied in the ultra-high vacuum pipes of storage rings. Thin fihn coatings of palladium, which are added onto the TiZrV film to increase the service life of nonevaporable getters and enhance H2 pumping speed, were deposited on the inner face of stainless steel pipes by dc magnetron sputtering using argon gas as the sputtering gas. The TiZrV-Pd film properties were investigated by atomic force microscope （AFM）, scanning electron microscope （SEM）, X-ray photoelectron spectroscopy （XPS） and X-Ray Diffraction （XRD）. The grain size of TiZrV and Pd films were about 0.42 1.3 nm and 8.5-18.25 nm respectively. It was found that the roughness of TiZrV films is small, about 2 4 nm, but for Pd film it is large, about 17 19 nm. The PP At. % of Pd in TiZrV/Pd films varied from 86.84 to 87.56 according to the XPS test results.展开更多
基金Funded by the"863"National High-tech Research and Development Program of China(No.2012AA06A112)
文摘We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner than 75μm and was then heated to temperatures up to 900 ℃. New cementitious material was prepared by proportioning fly ash and DAAC, named as AF. X-ray diffraction（XRD） was employed to identify the crystalline phases of DAAC before and after rehydration. The hydration process of AF was analyzed by the heat of hydration and non-evaporable water content（Wn）. The experimental results show that the highest reactivity of DAAC can be obtained by calcining the powder at 700 ℃ and the dehydrated products are mainly β-C2 S and CaO. The cumulative heat of hydration and Wn was found to be strongly dependent on the replacement level of fl y ash, increasing the replacement level of fl y ash lowered them in AF. The strength contribution rates on pozzolanic effect of fl y ash in AF are always negative, showing a contrary tendency of that of cement-fl y ash system.
基金Supported by National Natural Science Funds of China(11205155)Fundamental Research Funds for the Central Universities(WK2310000041)
文摘TiZrV film is mainly applied in the ultra-high vacuum pipes of storage rings. Thin fihn coatings of palladium, which are added onto the TiZrV film to increase the service life of nonevaporable getters and enhance H2 pumping speed, were deposited on the inner face of stainless steel pipes by dc magnetron sputtering using argon gas as the sputtering gas. The TiZrV-Pd film properties were investigated by atomic force microscope （AFM）, scanning electron microscope （SEM）, X-ray photoelectron spectroscopy （XPS） and X-Ray Diffraction （XRD）. The grain size of TiZrV and Pd films were about 0.42 1.3 nm and 8.5-18.25 nm respectively. It was found that the roughness of TiZrV films is small, about 2 4 nm, but for Pd film it is large, about 17 19 nm. The PP At. % of Pd in TiZrV/Pd films varied from 86.84 to 87.56 according to the XPS test results.