β-Sialon/ZrN bonded corundum composites were synthesized using fused white corundum,alumina micro powder,zircon and carbon black by nitridation reaction sintering process. Phase composition and microstructure of the ...β-Sialon/ZrN bonded corundum composites were synthesized using fused white corundum,alumina micro powder,zircon and carbon black by nitridation reaction sintering process. Phase composition and microstructure of the synthesized composites were investigated by X-ray powder diffraction and scanning electronic microscope,and the formation process of the composites was discussed. The results show that the composites with different compositions can be obtained by controlling the heating temperature and contents of zircon and carbon black. The proper temperature to synthesize the composites is 1773 K.展开更多
Sialon ceramics were prepared by the nitridation of Si,Al and Al2O3 powders with the transition metals(Fe Co,Ni)catalysts.The phase composition,microstructure and mechanical properties of specimens were studied Compar...Sialon ceramics were prepared by the nitridation of Si,Al and Al2O3 powders with the transition metals(Fe Co,Ni)catalysts.The phase composition,microstructure and mechanical properties of specimens were studied Compared with the catalyst-free specimen,the addition of Fe,Co and Ni greatly promoted the nitridation process of Sialon ceramics and improved the weight gain rate and mechanical properties of specimens.With the increased content of catalysts,the apparent porosity of the products decreased first and then increased,contrary to flexural strength and compressive strength.The specimen with 2.5 wt%Fe had the highest flexural strength 145.8 MPa and it exhibited the highest compressive strength of 594.6 MPa when Co content was 2.5 wt%,whereas they were 71.9 and 78.7 MPa,respectively,when without catalyst.展开更多
Hexagonal boron nitride ceramic（h-BN） based on the nitridation of B powders was obtained by reaction sintering method. The effects of sintering temperature on the mechanical properties and microstructure of the resu...Hexagonal boron nitride ceramic（h-BN） based on the nitridation of B powders was obtained by reaction sintering method. The effects of sintering temperature on the mechanical properties and microstructure of the resultant products were investigated and the reaction mechanism was discussed. Results showed that the reaction between B and N2 occurred vigorously at temperatures ranging from 1 000 ℃ to 1 300 ℃, which resulted in the generation of t-BN. When the temperature exceeded 1 450 ℃, transformation from t-BN to h-BN began to occur. As the sintering temperature increased, the spherical particles of t-BN gradually transformed into fine sheet particles of h-BN. These particles subsequently displayed a compact arrangement to achieve a more uniform microstructure, thereby increasing the strength.展开更多
High purity vanadium nitride(VN)powders were prepared via a two-step process using vanadium trioxide(V2 O3)as the raw material.The V2 O3 was firstly reduced at 873 K in Ar atmosphere via magnesiothermic reduction reac...High purity vanadium nitride(VN)powders were prepared via a two-step process using vanadium trioxide(V2 O3)as the raw material.The V2 O3 was firstly reduced at 873 K in Ar atmosphere via magnesiothermic reduction reaction to get the mixture of V and MgO,and then the products were further nitrided at 1473 K in N2 atmosphere.Finally,the as-prepared samples were acid-leached to obtain pure VN powders.X-ray diffractometry and field-emission scanning electron microscopy were used to analyze the phase transition and morphological evolution of the samples.The results reveal that the overall morphology of the obtained VN powder retains the morphology of the initial V2 O3 powders.After removing MgO by acidic leaching,the porous VN particles can be obtained,with the oxygen content of 0.178 wt.%.Compared with the traditional methods,high purity VN powders with a small amount of oxygen and no carbon can be obtained.展开更多
Si3N4 powder was synthesized by carbothermal re- duction nitridation reaction using sawdust as carbon source and introducing SiO2 by silica sol immersion. Effects of SiO2 content of silica sol, molding pressure, react...Si3N4 powder was synthesized by carbothermal re- duction nitridation reaction using sawdust as carbon source and introducing SiO2 by silica sol immersion. Effects of SiO2 content of silica sol, molding pressure, reaction temperature, reaction duration, and N2 flow rate on phase compositions and microstructure of result- ants were studied. The results show that using 7. 5 mass% SiO2 containing silica sol immersed sawdust as raw materials, the prepared Si3N4 powder is featured with high α-Si3N4 content, few impurities, etc. in the conditions of 1 450 ℃ of reaction temperature, 9 h of reaction duration, 400 mL ·min- 1 of N2 flow rate and 10 MPa of molding pressure.展开更多
Nanoparticles of refractory compounds represent a class of stable materials showing a great promise to support localized surface plasmon resonances(LSPRs)in both visible and near infrared(NIR)spectral regions.It is st...Nanoparticles of refractory compounds represent a class of stable materials showing a great promise to support localized surface plasmon resonances(LSPRs)in both visible and near infrared(NIR)spectral regions.It is still challenging to rationally tune the LSPR band because of the difficulty to control the density of charge carriers in individual refractory nanoparticles and maintain the dispersity of nanoparticles in the processes of synthesis and applications.In this work,controlled chemical transformation of titanium dioxide(TiO_(2))nanoparticles encapsulated with mesoporous silica(SiO_(2))shells to titanium nitride(TiN)via nitridation reaction at elevated temperatures is developed to tune the density of free electrons in the resulting titanium-oxide-nitride(TiO_(x)N_(y))nanoparticles.Such tunability enables a flexibility to support LSPR-based optical absorption in the synthesized TiO_(x)N_(y)@SiO_(2) core-shell nanoparticles across both the visible and NIR regions.The silica shells play a crucial role in preventing the sintering of TiO_(x)N_(y) nanoparticles in the nitridation reaction and maintaining the stability of TiOxNy nanoparticles in applications.The LSPR-based broadband absorption of light in the TiO_(x)N_(y)@SiO_(2) nanoparticles exhibits strong photothermal effect with photo-to-thermal conversion efficiency as high as〜76%.展开更多
基金Project(50274021) supported by the National Natural Science Foundation of China and Baoshan Iron and Steel Co., Ltd.
文摘β-Sialon/ZrN bonded corundum composites were synthesized using fused white corundum,alumina micro powder,zircon and carbon black by nitridation reaction sintering process. Phase composition and microstructure of the synthesized composites were investigated by X-ray powder diffraction and scanning electronic microscope,and the formation process of the composites was discussed. The results show that the composites with different compositions can be obtained by controlling the heating temperature and contents of zircon and carbon black. The proper temperature to synthesize the composites is 1773 K.
基金financially supported by the National Natural Science Foundation of China(Nos.51772140 and 51862024)the Natural Science Foundation of Jiangxi Province(No.20171ACB21033)+1 种基金the Science and Technology Project of the Education Department of Jiangxi Province(No.GJJ170573)the Graduate Innovation Special Fund of Nanchang Hangkong University(No.YC2018-S358)。
文摘Sialon ceramics were prepared by the nitridation of Si,Al and Al2O3 powders with the transition metals(Fe Co,Ni)catalysts.The phase composition,microstructure and mechanical properties of specimens were studied Compared with the catalyst-free specimen,the addition of Fe,Co and Ni greatly promoted the nitridation process of Sialon ceramics and improved the weight gain rate and mechanical properties of specimens.With the increased content of catalysts,the apparent porosity of the products decreased first and then increased,contrary to flexural strength and compressive strength.The specimen with 2.5 wt%Fe had the highest flexural strength 145.8 MPa and it exhibited the highest compressive strength of 594.6 MPa when Co content was 2.5 wt%,whereas they were 71.9 and 78.7 MPa,respectively,when without catalyst.
基金Funded by the Scientific and Technological Development Project of Yantai(2013JH020)
文摘Hexagonal boron nitride ceramic（h-BN） based on the nitridation of B powders was obtained by reaction sintering method. The effects of sintering temperature on the mechanical properties and microstructure of the resultant products were investigated and the reaction mechanism was discussed. Results showed that the reaction between B and N2 occurred vigorously at temperatures ranging from 1 000 ℃ to 1 300 ℃, which resulted in the generation of t-BN. When the temperature exceeded 1 450 ℃, transformation from t-BN to h-BN began to occur. As the sintering temperature increased, the spherical particles of t-BN gradually transformed into fine sheet particles of h-BN. These particles subsequently displayed a compact arrangement to achieve a more uniform microstructure, thereby increasing the strength.
基金Project(51725401) supported by the National Natural Science Foundation of China
文摘High purity vanadium nitride(VN)powders were prepared via a two-step process using vanadium trioxide(V2 O3)as the raw material.The V2 O3 was firstly reduced at 873 K in Ar atmosphere via magnesiothermic reduction reaction to get the mixture of V and MgO,and then the products were further nitrided at 1473 K in N2 atmosphere.Finally,the as-prepared samples were acid-leached to obtain pure VN powders.X-ray diffractometry and field-emission scanning electron microscopy were used to analyze the phase transition and morphological evolution of the samples.The results reveal that the overall morphology of the obtained VN powder retains the morphology of the initial V2 O3 powders.After removing MgO by acidic leaching,the porous VN particles can be obtained,with the oxygen content of 0.178 wt.%.Compared with the traditional methods,high purity VN powders with a small amount of oxygen and no carbon can be obtained.
文摘Si3N4 powder was synthesized by carbothermal re- duction nitridation reaction using sawdust as carbon source and introducing SiO2 by silica sol immersion. Effects of SiO2 content of silica sol, molding pressure, reaction temperature, reaction duration, and N2 flow rate on phase compositions and microstructure of result- ants were studied. The results show that using 7. 5 mass% SiO2 containing silica sol immersed sawdust as raw materials, the prepared Si3N4 powder is featured with high α-Si3N4 content, few impurities, etc. in the conditions of 1 450 ℃ of reaction temperature, 9 h of reaction duration, 400 mL ·min- 1 of N2 flow rate and 10 MPa of molding pressure.
基金funded by the department of the Army Basic Research Program through the Edgewood Chemical and Biological Center,U.S.Army Research Office(No.W911NF-15-2-0052).
文摘Nanoparticles of refractory compounds represent a class of stable materials showing a great promise to support localized surface plasmon resonances(LSPRs)in both visible and near infrared(NIR)spectral regions.It is still challenging to rationally tune the LSPR band because of the difficulty to control the density of charge carriers in individual refractory nanoparticles and maintain the dispersity of nanoparticles in the processes of synthesis and applications.In this work,controlled chemical transformation of titanium dioxide(TiO_(2))nanoparticles encapsulated with mesoporous silica(SiO_(2))shells to titanium nitride(TiN)via nitridation reaction at elevated temperatures is developed to tune the density of free electrons in the resulting titanium-oxide-nitride(TiO_(x)N_(y))nanoparticles.Such tunability enables a flexibility to support LSPR-based optical absorption in the synthesized TiO_(x)N_(y)@SiO_(2) core-shell nanoparticles across both the visible and NIR regions.The silica shells play a crucial role in preventing the sintering of TiO_(x)N_(y) nanoparticles in the nitridation reaction and maintaining the stability of TiOxNy nanoparticles in applications.The LSPR-based broadband absorption of light in the TiO_(x)N_(y)@SiO_(2) nanoparticles exhibits strong photothermal effect with photo-to-thermal conversion efficiency as high as〜76%.