Compared with Y_(3)Al_(5)O_(12):Ce^(3+),Y3MgAl3SiO12:Ce^(3+)(YMASG:Ce^(3+))reveals great potential for highpower white lighting with red-shift spectrum.Herein,YMASG:Ce^(3+)transparent ceramics were explored to be synt...Compared with Y_(3)Al_(5)O_(12):Ce^(3+),Y3MgAl3SiO12:Ce^(3+)(YMASG:Ce^(3+))reveals great potential for highpower white lighting with red-shift spectrum.Herein,YMASG:Ce^(3+)transparent ceramics were explored to be synthesized in the air following hot isostatic pressure(HIP)treatment to obtain tunable and optimized optical properties.Then phase purity,microstructure,transmittance,and photoluminescence of YMASG:Ce^(3+)ceramics were investigated.The emission peak of YMASG:Ce^(3+)transparent ceramic can be tuned from 573 to 592 nm with the variation of Ce^(3+)doping concentration.It should be noted that this YMASG:0.2 at%Ce^(3+)transparent ceramic with emission peak at 579 nm under 450 nm excitation exhibits the highest internal/external quantum efficiency(72%/65%).The white LED device using YMASG:0.2 at%Ce^(3+)transparent ceramic with a 0.4 mm thickness demonstrates a luminous efficiency(LE)of 106 lm/W,correlated color temperature of 3158 K,and color coordinate(0.3933,0.3265).Thermal stability can be significantly imporoved by the incorporation of Lu^(3+)in YMASG transparent ceramic,and the Y3-yLuyMgAl3SiO12:0.2 at/Ce^(3+)(y=0-2.5)transparent ceramics were fabricated.The highest thermal stability(88%@150℃of the integrated emission intensity at 25℃)can be achieved wheny=2.5.The maximum LE of 154 Im/W can be obtained from Y_(0.5)Lu_(2.5)MgAl_(3)SiO_(12):0.2 at%Ce^(3+)transparent ceramic.These results indicate that YMASG:Ce^(3+)transparent ceramics with optimized properties can be regarded as an encouraging candidate for highpower white lighting.展开更多
基金supported by the National Natural Science Foundation of China(51972304,51971208)Beijing Municipal Science and Technology Project(Z191100004819002)The Project of Scientific Experiment on Chinese Manned Space Station,China。
文摘Compared with Y_(3)Al_(5)O_(12):Ce^(3+),Y3MgAl3SiO12:Ce^(3+)(YMASG:Ce^(3+))reveals great potential for highpower white lighting with red-shift spectrum.Herein,YMASG:Ce^(3+)transparent ceramics were explored to be synthesized in the air following hot isostatic pressure(HIP)treatment to obtain tunable and optimized optical properties.Then phase purity,microstructure,transmittance,and photoluminescence of YMASG:Ce^(3+)ceramics were investigated.The emission peak of YMASG:Ce^(3+)transparent ceramic can be tuned from 573 to 592 nm with the variation of Ce^(3+)doping concentration.It should be noted that this YMASG:0.2 at%Ce^(3+)transparent ceramic with emission peak at 579 nm under 450 nm excitation exhibits the highest internal/external quantum efficiency(72%/65%).The white LED device using YMASG:0.2 at%Ce^(3+)transparent ceramic with a 0.4 mm thickness demonstrates a luminous efficiency(LE)of 106 lm/W,correlated color temperature of 3158 K,and color coordinate(0.3933,0.3265).Thermal stability can be significantly imporoved by the incorporation of Lu^(3+)in YMASG transparent ceramic,and the Y3-yLuyMgAl3SiO12:0.2 at/Ce^(3+)(y=0-2.5)transparent ceramics were fabricated.The highest thermal stability(88%@150℃of the integrated emission intensity at 25℃)can be achieved wheny=2.5.The maximum LE of 154 Im/W can be obtained from Y_(0.5)Lu_(2.5)MgAl_(3)SiO_(12):0.2 at%Ce^(3+)transparent ceramic.These results indicate that YMASG:Ce^(3+)transparent ceramics with optimized properties can be regarded as an encouraging candidate for highpower white lighting.
