In this paper,magnetic composite Fe3 O4/CeO2（MC Fe/Ce） was synthesized via CeO2 covered onto the surface of Fe3O4 by sol-precipitation method.The as-synthesized samples were characterized by FE-SEM,XRD,SEM-EDS and F...In this paper,magnetic composite Fe3 O4/CeO2（MC Fe/Ce） was synthesized via CeO2 covered onto the surface of Fe3O4 by sol-precipitation method.The as-synthesized samples were characterized by FE-SEM,XRD,SEM-EDS and FT-IR spectrum.The pseudo-second-order（PSO） kinetic can describe well the adsorption of Acid black 210（AB210） onto the as-obtained MC Fe/Ce of which the adsorption isotherm fits the Langmuir adsorption model better than Freundlich adsorption model.Furthermore,the maximum monolayer adsorption capacity of MC Fe/Ce is about 93 mg/g,which is 6 times more than that of commercial CeO2 for AB210.Moreover,the removal rate of the adsorbates for AB210 is 82.3% after first adsorption and still about 70% the fourth forth adsorption experiments within 120 min,which demonstrates that the obtained MC Fe/Ce has outstanding adsorption capacity and good stability.Additionally,the composite can be easily separated from aqueous solution in a few seconds with an external magnetic field due to its magnetic property,which is vital and has potential for its practical applications.展开更多
This work studied CuO/CeO2-Co3O4 with wt% Ce:Co ratio 95:5 for selective CO oxidation with effect of? wt% Cu loading. The catalysts were prepared by co-precipitation. Characterizations of catalysts were carried out by...This work studied CuO/CeO2-Co3O4 with wt% Ce:Co ratio 95:5 for selective CO oxidation with effect of? wt% Cu loading. The catalysts were prepared by co-precipitation. Characterizations of catalysts were carried out by XRD and BET techniques. The results showed a good dispersion of CuO for 5 wt% Cu loading catalysts and showed high specific surface area of catalyst. For selective CO oxidation, both 5CuO and 30CuO catalysts could remove completely CO in the presence of excess hydrogen at 423 K and 20CuO could eliminate CO completely at 443 K. Moreover, considering the selectivity to CO oxidation, the 5CuO catalyst has shown the highest selectivity of 85% while the 30CuO catalyst obtains the selectivity of 65% at the reaction temperature of 423 K.展开更多
基金Project supported by the Capacity Building Program of Shanghai Local Universities(12160503600)
文摘In this paper,magnetic composite Fe3 O4/CeO2（MC Fe/Ce） was synthesized via CeO2 covered onto the surface of Fe3O4 by sol-precipitation method.The as-synthesized samples were characterized by FE-SEM,XRD,SEM-EDS and FT-IR spectrum.The pseudo-second-order（PSO） kinetic can describe well the adsorption of Acid black 210（AB210） onto the as-obtained MC Fe/Ce of which the adsorption isotherm fits the Langmuir adsorption model better than Freundlich adsorption model.Furthermore,the maximum monolayer adsorption capacity of MC Fe/Ce is about 93 mg/g,which is 6 times more than that of commercial CeO2 for AB210.Moreover,the removal rate of the adsorbates for AB210 is 82.3% after first adsorption and still about 70% the fourth forth adsorption experiments within 120 min,which demonstrates that the obtained MC Fe/Ce has outstanding adsorption capacity and good stability.Additionally,the composite can be easily separated from aqueous solution in a few seconds with an external magnetic field due to its magnetic property,which is vital and has potential for its practical applications.
文摘This work studied CuO/CeO2-Co3O4 with wt% Ce:Co ratio 95:5 for selective CO oxidation with effect of? wt% Cu loading. The catalysts were prepared by co-precipitation. Characterizations of catalysts were carried out by XRD and BET techniques. The results showed a good dispersion of CuO for 5 wt% Cu loading catalysts and showed high specific surface area of catalyst. For selective CO oxidation, both 5CuO and 30CuO catalysts could remove completely CO in the presence of excess hydrogen at 423 K and 20CuO could eliminate CO completely at 443 K. Moreover, considering the selectivity to CO oxidation, the 5CuO catalyst has shown the highest selectivity of 85% while the 30CuO catalyst obtains the selectivity of 65% at the reaction temperature of 423 K.