Hollow mesoporous silica spheres with magnetite cores(HMSMC) have been fabricated by Vacuum Nano-casting Route. The amount of magnetite cores and saturation magnetization value can be easily adjusted by changing the c...Hollow mesoporous silica spheres with magnetite cores(HMSMC) have been fabricated by Vacuum Nano-casting Route. The amount of magnetite cores and saturation magnetization value can be easily adjusted by changing the concentration of iron nitrate solution used in the synthesis procedure. Furthermore, the as-prepared HMSMCs still maintain narrow mesopore distribution, high surface area and large pore volume after the hollow cores of hollow mesoporous silica spheres were filled with magnetite particles. Specially, when the saturation magnetization value of as-prepared HMSMCs reaches 22.0 emu/g, the surface area and pore volume of corresponding HMSMCs are 149 m^2/g and 0.19 cm^3/g, respectively, and the pore size is 2.30 nm. The corresponding samples are characterized by X-ray diffraction, N_2 sorption isotherms, transmission electron microscopy and vibrating-sample magnetometer.展开更多
基金support of this research by the National Science Foundation of China(Grant No.50702072)Chinese Academy of Science(Grant No.KJCX2.YW.M02)+1 种基金National 863 Projects(Grant No.2007AA03Z317)Shanghai Nano-Science Program(Grant No.0852nm03900)
文摘Hollow mesoporous silica spheres with magnetite cores(HMSMC) have been fabricated by Vacuum Nano-casting Route. The amount of magnetite cores and saturation magnetization value can be easily adjusted by changing the concentration of iron nitrate solution used in the synthesis procedure. Furthermore, the as-prepared HMSMCs still maintain narrow mesopore distribution, high surface area and large pore volume after the hollow cores of hollow mesoporous silica spheres were filled with magnetite particles. Specially, when the saturation magnetization value of as-prepared HMSMCs reaches 22.0 emu/g, the surface area and pore volume of corresponding HMSMCs are 149 m^2/g and 0.19 cm^3/g, respectively, and the pore size is 2.30 nm. The corresponding samples are characterized by X-ray diffraction, N_2 sorption isotherms, transmission electron microscopy and vibrating-sample magnetometer.