The PPG PITT-CHAR XP flame retardant system has been used by COOEC to preventing the thermal softening of steel in the high temperature,whose degradation temperature is 80 ℃.To prevent damage to PPG PITT-CHAR XP fire...The PPG PITT-CHAR XP flame retardant system has been used by COOEC to preventing the thermal softening of steel in the high temperature,whose degradation temperature is 80 ℃.To prevent damage to PPG PITT-CHAR XP fire retardant paint from excessive heat during welding,it is necessary to get accurately reserved area near the welding joints prior to welding. For the foregoing reasons,the 80 ℃ temperature field distribution of thick plate multi-pass welding was analyzed with SYSWELD.The influence of welding groove form and time interval on welding temperature field was also analyzed. Results showed that the range of 80 ℃ welding temperature field increased with the increasing of weld layers at first and then it inclined to stable value. Interpass time setting was crucial to control the range of 80 ℃ welding temperature field. It was also found that double V groove had better thermal diffusivity than double-bevel groove.And double-bevel groove was better than single V groove.展开更多
The present study reported the effect of filler metals on the microstructure and mechanical properties of pulsed current gas tungsten arc-welded Inconel 718 plates. Two different filler metals such as ERNiCr-3 and ERN...The present study reported the effect of filler metals on the microstructure and mechanical properties of pulsed current gas tungsten arc-welded Inconel 718 plates. Two different filler metals such as ERNiCr-3 and ERNiCrMo-4 were employed for welding Inconel 718. The primary objective of this study is to suppress or eradicate the deleterious phase such as Laves or δ （delta） which is considered to be detrimental to the weld properties. Microstructure examination corroborated the presence of unmixed zone at the HAZ for both the weldments. Tensile test trials envisaged that ERNiCrMo-4 weldments offered better tensile properties compared to ERNiCr-3 weldments, whereas the impact toughness was found to be better for ERNiCr-3 weldments. Line mapping analysis was carried out to study the elemental migration across the weldments. The structure-property relationships of the weldments were arrived at using the combined tech- niques of optical and scanning electron microscopy. Optical and SEM/EDAX analysis showed that there is no prominent occurrence of deleterious phases at the weld zone on employing these filler metals.展开更多
The welding of medium and thick plates has a wide range of applications in the engineering field.Industrial welding robots are gradually replacing traditional welding operations due to their significant advantages,suc...The welding of medium and thick plates has a wide range of applications in the engineering field.Industrial welding robots are gradually replacing traditional welding operations due to their significant advantages,such as high welding quality,high work efficiency,and effective reduction of labor intensity.Ensuring the accuracy of the welding trajectory for the welding robot is crucial for guaranteeing welding quality.In this paper,the author uses the chaos sparrow search algorithm to optimize the trajectory of a multi-layer and multi-pass welding robot for medium and thick plates.Firstly,the Sparrow Search Algorithm(SSA)is improved by introducing tent chaotic mapping and Gaussian mutation of the inertia weight factor.Secondly,in order to prevent the welding robot arm from colliding with obstacles in the welding environment during the welding process,maintain the stability of the welding robot,and ensure the continuous stability of the changes in each joint angle,joint angular velocity,and angular velocity of the joint angle,a welding robot model is established by improving the Denavit-Hartenberg parameter method.A multi-objective optimization fitness function is used to optimize the trajectory of the welding robot,minimizing time and energy consumption.Thirdly,the optimization and convergence performance of SSA and Chaos Sparrow Search Algorithm(CSSA)are compared through 10 benchmark test functions.Based on the six sets of test functions,the CSSA algorithm consistently maintains superior optimization performance and has excellent stability,with a faster decline in the convergence curve compared to the SSA algorithm.Finally,the accuracy of welding is tested through V-shaped multi-layer and multi-pass welding experiments.The experimental results show that the CSSA algorithm has a strong superiority in trajectory optimization of multi-layer and multi-pass welding for medium and thick plates,with an accuracy rate of 99.5%.It is an effective optimization method that can meet the actual needs of production.展开更多
Dissimilar AZ31B magnesium alloy and DC56D steel were welded via AA1060 aluminum alloy by magnetic pulse welding.The effects of primary and secondary welding processes on the welded interface were comparatively invest...Dissimilar AZ31B magnesium alloy and DC56D steel were welded via AA1060 aluminum alloy by magnetic pulse welding.The effects of primary and secondary welding processes on the welded interface were comparatively investigated.Macroscopic morphology,microstructure,and interfacial structure of the joints were analyzed using scanning electron microscope,energy dispersive spectrometer,and X-ray diffractometer(XRD).The results show that magnetic pulse welding of dissimilar Mg/Fe metals is achieved using an Al interlayer,which acts as a bridge for deformation and diffusion.Specifically,the AZ31B/AA1060 interface exhibits a typical wavy morphology,and a transition zone exists at the joint interface,which may result in an extremely complex microstructure.The microstructure of this transition zone differs from that of AZ31B magnesium and 1060 Al alloys,and it is identified as brittle intermetallic compounds(IMCs)Al_(3)Mg_(2) and Al_(12)Mg_(17).The transition zone is mainly distributed on the Al side,with the maximum thickness of Al-side transition layer reaching approximately 13.53μm.Incomplete melting layers with varying thicknesses are observed at the primary weld interface,while micron-sized hole defects appear in the transition zone of the secondary weld interface.The AA1060/DC56D interface is mainly straight,with only a small number of discontinuous transition zones distributed intermittently along the interface.These transition zones are characterized by the presence of the brittle IMC FeAl_(3),with a maximum thickness of about 4μm.展开更多
Magnesium-rare earth(Mg-RE)alloys are pivotal for lightweight applications in aerospace and advanced engineering due to their high specific strength.However,manufacturing large-scale complex components via monolithic ...Magnesium-rare earth(Mg-RE)alloys are pivotal for lightweight applications in aerospace and advanced engineering due to their high specific strength.However,manufacturing large-scale complex components via monolithic casting is challenging owing to defects such as RE oxides and shrinkage porosity,making fusion welding essential for both defect repair and structural joining.This review comprehensively examines recent advances in fusion welding of Mg-RE alloys,with emphasis on the interplay between their unique physicochemical properties and welding metallurgy.Various fusion welding methods suitable for Mg-RE alloys are compared and analyzed.Detailed characterization of joint regions reveals how thermal gradients and cooling rates govern phase evolution,grain morphology,and defect formation.Moreover,welding parameters and heat treatment strategies are systematically discussed for the microstructural configuration,especially for the inherent conflicts between grain coarsening in fusion zone and eutectic dissolution in heat-affected zone.Future research directions are also outlined.By correlating Mg-RE alloy properties with fusion welding processes,this review provides practical insights for designing reliable welded structures in critical applications.展开更多
Joining dissimilar materials encounters significant engineering challenges due to the contrast in material properties that makes conventional welding not feasible.Magnetic Pulse Welding(MPW)offers a solidstate joining...Joining dissimilar materials encounters significant engineering challenges due to the contrast in material properties that makes conventional welding not feasible.Magnetic Pulse Welding(MPW)offers a solidstate joining technique that overcomes these issues by using impact to create strong bonds without melting the substrate materials.This study investigates the weldability of aluminum alloy Al-5754 with Al-7075 and MARS 380 steel,used in armouring solutions of defense systems,by the use of MPW.In this work,weldability windows are investigated by varying standoff distances between the coating material and its substrate(0.25-4.5 mm)and discharge energies(5-13 kJ)with both O-shape and U-shape inductors.Mechanical strength of the welded joints were assessed through single lap shear tests,identifying optimal welding parameters.Then,the velocity profiles of the flyer plates were measured using heterodyne velocimetry to understand the dynamics of the impact.Then,substructures assembled with the optimal welding conditions were subjected to ballistic testing using 7.62 mm×51 mm NATO and 9 mm×19 mm Parabellum munitions to evaluate the resilience of the welds under ballistic impact.The outcomes demonstrate that MPW effectively joins Al-5754 with both Al-7075 and MARS 380,producing robust welds capable of withstanding ballistic impacts under certain conditions.This research advances the application of MPW in lightweight ballistic protection of defense systems,contributing to the development of more resilient and lighter protective structures.展开更多
This work examines the microstructure and corrosion properties of fine-grained Al 7075 across different regions under varying cooling conditions during friction stir welding.The findings demonstrate that forced coolin...This work examines the microstructure and corrosion properties of fine-grained Al 7075 across different regions under varying cooling conditions during friction stir welding.The findings demonstrate that forced cooling significantly improves the corrosion resistance of the welded joints.Specifically,the corrosion resistance was the highest in the stir zone,followed by the thermo-mechanical affected zone,and then the heat affected zone.Forced cooling mitigates grain growth by controlling the welding thermal effects,thereby increasing the proportion ofΣ3 grain boundaries.The modification of these microstructural characteristics promotes the formation of a dense oxide layer,thereby enhancing the corrosion resistance.Furthermore,forced cooling mitigates the precipitation and coarsening of the anodic phase in the stir zone,which in turn reduces the susceptibility of the joint to pitting corrosion.Additionally,the lower recrystallization texture content in the joint,resulting from forced cooling,contributes to a reduction in the number of corrosion-active sites,thereby further improving the corrosion performance of the welded joint.展开更多
Marine thin plates are susceptible to welding deformation owing to their low structural stiffness.Therefore,the efficient and accurate prediction of welding deformation is essential for improving welding quality.The t...Marine thin plates are susceptible to welding deformation owing to their low structural stiffness.Therefore,the efficient and accurate prediction of welding deformation is essential for improving welding quality.The traditional thermal elastic-plastic finite element method(TEP-FEM)can accurately predict welding deformation.However,its efficiency is low because of the complex nonlinear transient computation,making it difficult to meet the needs of rapid engineering evaluation.To address this challenge,this study proposes an efficient prediction method for welding deformation in marine thin plate butt welds.This method is based on the coupled temperature gradient-thermal strain method(TG-TSM)that integrates inherent strain theory with a shell element finite element model.The proposed method first extracts the distribution pattern and characteristic value of welding-induced inherent strain through TEP-FEM analysis.This strain is then converted into the equivalent thermal load applied to the shell element model for rapid computation.The proposed method-particularly,the gradual temperature gradient-thermal strain method(GTG-TSM)-achieved improved computational efficiency and consistent precision.Furthermore,the proposed method required much less computation time than the traditional TEP-FEM.Thus,this study lays the foundation for future prediction of welding deformation in more complex marine thin plates.展开更多
The dissimilar 2B06 and 7B04 Al alloy joints were prepared by refill friction stir spot welding(RFSSW),and the microstructural evolution and corrosion behavior of the joints were investigated.Based on microstructural ...The dissimilar 2B06 and 7B04 Al alloy joints were prepared by refill friction stir spot welding(RFSSW),and the microstructural evolution and corrosion behavior of the joints were investigated.Based on microstructural analysis,the welded joints exhibit distinct microstructural zones,including the stir zone(SZ),thermomechanically affected zone(TMAZ),and heat-affected zone(HAZ).The grain size of each zone is in the order of HAZ>TMAZ>SZ.Notably,the TMAZ and HAZ contain significantly larger secondary-phase particles compared to the SZ,with particle size in the HAZ increasing at higher rotational speeds.Electrochemical tests indicate that corrosion susceptibility follows the sequence of HAZ>TMAZ>SZ>BM,with greater sensitivity observed at increased rotational speeds.Post-corrosion mechanical performance degradation primarily arises from crevice corrosion at joint overlaps,but not from the changes in the microstructure.展开更多
Welding deformation adversely affects the quality and precision of structural components,and traditional methods require significant material resources and time.Machine learning has demonstrated exceptional ac-curacy ...Welding deformation adversely affects the quality and precision of structural components,and traditional methods require significant material resources and time.Machine learning has demonstrated exceptional ac-curacy and efficiency in solving complex problems.Thus,the use of machine learning to predict welding de-formations is a novel approach.In this study,laser welding experiments were conducted on a TC4 titanium alloy to establish a welding deformation dataset.The deep neural network(DNN)and convolutional neural network(CNN)models were designed and constructed,with average prediction errors of 0.85 mm and 0.94 mm on the validation set,respectively.To further optimize the network parameters,a differential evolution algorithm was employed through mutation,crossover,and selection.The results indicated that after optimization,the pre-diction errors of the DNN and CNN models reduced to 0.75 mm and 0.85 mm,respectively.These represent accuracy improvements of 14.8%and 9.6%,respectively.The optimized models exhibited superior predictive performances for the validation set.展开更多
Multi-pass tandem gas metal arc welding(TGMAW) for Al 5083 alloy plates with 30 mm thickness is carried out to study its high efficiency and high quality. The welding process is evaluated by high-speed photographs and...Multi-pass tandem gas metal arc welding(TGMAW) for Al 5083 alloy plates with 30 mm thickness is carried out to study its high efficiency and high quality. The welding process is evaluated by high-speed photographs and electrical signals. The deposition rate and welding time are calculated to characterize the welding efficiency. The bead formation, porosity, microstructure and mechanical properties are tested and analyzed. The results indicate that though arc deflection occurs due to the electromagnetic interference between two arcs during TGMAW process, it does not affect the welding process stability significantly. The deposition rate and welding time of TGMAW process are about 15 g/min larger and about 16.7% less than those of gas metal arc welding(GMAW)process respectively, accompanied by the reduction of heat input. The TGMAW welded joint has less porosity and more refined microstructure to contribute to the improvement of mechanical properties(micro-hardness, tensile strength and ductility). It can be concluded that TGMAW process yields excellent performance of welded joint with improved welding efficiency, which makes it extremely practical during welding of thick plates.展开更多
Titanium alloy has the advantages of high strength,strong corrosion resistance,excellent high and low temperature mechanical properties,etc.,and is widely used in aerospace,shipbuilding,weapons and equipment,and other...Titanium alloy has the advantages of high strength,strong corrosion resistance,excellent high and low temperature mechanical properties,etc.,and is widely used in aerospace,shipbuilding,weapons and equipment,and other fields.In recent years,with the continuous increase in demand for medium-thick plate titanium alloys,corresponding welding technologies have also continued to develop.Therefore,this article reviews the research progress of deep penetration welding technology for medium-thick plate titanium alloys,mainly covering traditional arc welding,high-energy beam welding,and other welding technologies.Among many methods,narrow gap welding,hybrid welding,and external energy field assistance welding all contribute to improving the welding efficiency and quality of medium-thick plate titanium alloys.Finally,the development trend of deep penetration welding technology for mediumthick plate titanium alloys is prospected.展开更多
Friction stir lap welding of AA2195 Al-Li alloy and Ti alloy was conducted to investigate the formation,microstructure,and mechanical properties of the joints.Results show that under different welding parameters,with ...Friction stir lap welding of AA2195 Al-Li alloy and Ti alloy was conducted to investigate the formation,microstructure,and mechanical properties of the joints.Results show that under different welding parameters,with the decrease in welding heat input,the weld surface is smoother.The Ti/Al joint interface is flat without obvious Ti and Al mixed structure,and the hook structure is not formed under optimal parameters.Due to the enhanced breaking effect of the stirring head,the hook structural defects and intermetallic compounds are more likely to form at the Ti/Al interface at high rotational speed of 1000 r/min,thereby deteriorating the mechanical properties of joints.Decreasing the heat input is beneficial to hardness enhancement of the aluminum alloy in the weld nugget zone.Under the optimal parameters of rotation speed of 800 r/min and welding speed of 120 mm/min,the maximum tensile shear strength of joint is 289 N/mm.展开更多
Friction stir welding(FSW)is a relatively new welding technique that has significant advantages compared to the fusion welding techniques in joining non weld able alloys by fusion,such as aluminum alloys.Three FSW sea...Friction stir welding(FSW)is a relatively new welding technique that has significant advantages compared to the fusion welding techniques in joining non weld able alloys by fusion,such as aluminum alloys.Three FSW seams of AA6061-T6 plates were made us-ing different FSW parameters.The structure of the FSW seams was investigated using X-ray diffraction(XRD),scanning electron mi-croscope(SEM)and non destructive testing(NDT)techniques and their hardness was also measured.The dominated phase in the AA6061-T6 alloy and the FSW seams was theα-Al.The FSW seam had lower content of the secondary phases than the AA6061-T6 al-loy.The hardness of the FSW seams was decreased by about 30%compared to the AA6061-T6 alloy.The temperature distributions in the weld seams were also studied experimentally and numerically modeled and the results were in a good agreement.展开更多
Laser twin-arc GTAW(LTA-GTAW)process has been developed by using the synergic interaction effects of laser and a coupled arc in a weld pool to achieve higher energy efficiency.In this study,bead-on-plate welding was c...Laser twin-arc GTAW(LTA-GTAW)process has been developed by using the synergic interaction effects of laser and a coupled arc in a weld pool to achieve higher energy efficiency.In this study,bead-on-plate welding was conducted on 8-mm-thick Q235B work-pieces to investigate the variation of hybrid arc profile,the influence of hybrid arc profile on weld forming,microstructure and mech-anical properties of the joint during the LTA-GTAW process.The influence of Laser-GTAW and LTA-GTAW methods on weld surface appearance,heat input per unit length,and weld metal microstructure were also demonstrated systematically.The LTA-GTAW can make the distribution of arc energy more reasonable in welding depth and width.When defocus is 0,I_(f)is 330 A,I_(b)is 240 A,laser power is 2.4 kW,and spacing between heat sources of tungsten electrode is 10 mm,the weld shape is better.Compared with Laser-GTAW,LTA-GTAW can achieve lower heat input at the same penetration depth,and the microstructure of the weld is refined.The tensile strength of the welded joint is 121.8%of the base material,and the fracture mode of the welded joint is ductile fracture,the comprehensive mechanical properties are better.展开更多
The composite structures/components made by friction stir lap welding(FSLW)of Mg alloy sheet and Al alloy sheet are of wide application potentials in the manufacturing sector of transportation vehicles.To further impr...The composite structures/components made by friction stir lap welding(FSLW)of Mg alloy sheet and Al alloy sheet are of wide application potentials in the manufacturing sector of transportation vehicles.To further improve the joint quality,the ultrasonic vibration(UV)is exerted in FSLW,and the UV enhanced FSLW(UVeFSLW)was developed for making Mg-to-Al dissimilar joints.The numerical analysis and experimental investigation were combined to study the process mechanism in Mg/Al UVeFSLW.An equation related to the temperature and strain rate was derived to calculate the grain size at different locations of the weld nugget zone,and the effect of grain size distribution on the threshold thermal stress was included,so that the prediction accuracy of flow stress was further improved.With such modified constitutive equation,the numerical simulation was conducted to compare the heat generation,temperature profiles and material flow behaviors in Mg/Al UVeFSLW/FSLW processes.It was found that the exerted UV decreased the temperature at two checking points on the tool/workpiece interface from 707/671 K in FSLW to 689/660 K in UVeFSLW,which suppressed the IMCs thickness at Mg-Al interface from 1.7μm in FSLW to 1.1μm in UVeFSLW.The exerted UV increased the horizontal materials flow ability,and decreased the upward flow ability,which resulted in the increase of effective sheet thickness/effective lap width from 2.01/3.70 mm in FSLW to 2.04/4.84 mm in UVeFSLW.Therefore,the ultrasonic vibration improved the tensile shear strength of Mg-to-Al lap joints by 18%.展开更多
基金Project(No.2016ZDJS05B03)supported by Shandong Key ResearchDevelopment Plan,Project(No.17CX06005&No.18CX06054A)supported by Department of Science&Technology of Shandong Province the Fundamental Research Funds for the Central Universities
文摘The PPG PITT-CHAR XP flame retardant system has been used by COOEC to preventing the thermal softening of steel in the high temperature,whose degradation temperature is 80 ℃.To prevent damage to PPG PITT-CHAR XP fire retardant paint from excessive heat during welding,it is necessary to get accurately reserved area near the welding joints prior to welding. For the foregoing reasons,the 80 ℃ temperature field distribution of thick plate multi-pass welding was analyzed with SYSWELD.The influence of welding groove form and time interval on welding temperature field was also analyzed. Results showed that the range of 80 ℃ welding temperature field increased with the increasing of weld layers at first and then it inclined to stable value. Interpass time setting was crucial to control the range of 80 ℃ welding temperature field. It was also found that double V groove had better thermal diffusivity than double-bevel groove.And double-bevel groove was better than single V groove.
基金sincerely acknowledge Aeronautical Research & Development Board (AR & DB), Govt. of India for funding this project
文摘The present study reported the effect of filler metals on the microstructure and mechanical properties of pulsed current gas tungsten arc-welded Inconel 718 plates. Two different filler metals such as ERNiCr-3 and ERNiCrMo-4 were employed for welding Inconel 718. The primary objective of this study is to suppress or eradicate the deleterious phase such as Laves or δ （delta） which is considered to be detrimental to the weld properties. Microstructure examination corroborated the presence of unmixed zone at the HAZ for both the weldments. Tensile test trials envisaged that ERNiCrMo-4 weldments offered better tensile properties compared to ERNiCr-3 weldments, whereas the impact toughness was found to be better for ERNiCr-3 weldments. Line mapping analysis was carried out to study the elemental migration across the weldments. The structure-property relationships of the weldments were arrived at using the combined tech- niques of optical and scanning electron microscopy. Optical and SEM/EDAX analysis showed that there is no prominent occurrence of deleterious phases at the weld zone on employing these filler metals.
基金support by Ningxia Key R&D projects“Integration and demonstration application of intelligent finishing system for large casting riser robot”(No.2021BEE03002)Ningxia Natural Science Foundation Project“Research on detection and location of large casting welding seam based on depth learning”(No.2020AAC03201).
文摘The welding of medium and thick plates has a wide range of applications in the engineering field.Industrial welding robots are gradually replacing traditional welding operations due to their significant advantages,such as high welding quality,high work efficiency,and effective reduction of labor intensity.Ensuring the accuracy of the welding trajectory for the welding robot is crucial for guaranteeing welding quality.In this paper,the author uses the chaos sparrow search algorithm to optimize the trajectory of a multi-layer and multi-pass welding robot for medium and thick plates.Firstly,the Sparrow Search Algorithm(SSA)is improved by introducing tent chaotic mapping and Gaussian mutation of the inertia weight factor.Secondly,in order to prevent the welding robot arm from colliding with obstacles in the welding environment during the welding process,maintain the stability of the welding robot,and ensure the continuous stability of the changes in each joint angle,joint angular velocity,and angular velocity of the joint angle,a welding robot model is established by improving the Denavit-Hartenberg parameter method.A multi-objective optimization fitness function is used to optimize the trajectory of the welding robot,minimizing time and energy consumption.Thirdly,the optimization and convergence performance of SSA and Chaos Sparrow Search Algorithm(CSSA)are compared through 10 benchmark test functions.Based on the six sets of test functions,the CSSA algorithm consistently maintains superior optimization performance and has excellent stability,with a faster decline in the convergence curve compared to the SSA algorithm.Finally,the accuracy of welding is tested through V-shaped multi-layer and multi-pass welding experiments.The experimental results show that the CSSA algorithm has a strong superiority in trajectory optimization of multi-layer and multi-pass welding for medium and thick plates,with an accuracy rate of 99.5%.It is an effective optimization method that can meet the actual needs of production.
文摘Dissimilar AZ31B magnesium alloy and DC56D steel were welded via AA1060 aluminum alloy by magnetic pulse welding.The effects of primary and secondary welding processes on the welded interface were comparatively investigated.Macroscopic morphology,microstructure,and interfacial structure of the joints were analyzed using scanning electron microscope,energy dispersive spectrometer,and X-ray diffractometer(XRD).The results show that magnetic pulse welding of dissimilar Mg/Fe metals is achieved using an Al interlayer,which acts as a bridge for deformation and diffusion.Specifically,the AZ31B/AA1060 interface exhibits a typical wavy morphology,and a transition zone exists at the joint interface,which may result in an extremely complex microstructure.The microstructure of this transition zone differs from that of AZ31B magnesium and 1060 Al alloys,and it is identified as brittle intermetallic compounds(IMCs)Al_(3)Mg_(2) and Al_(12)Mg_(17).The transition zone is mainly distributed on the Al side,with the maximum thickness of Al-side transition layer reaching approximately 13.53μm.Incomplete melting layers with varying thicknesses are observed at the primary weld interface,while micron-sized hole defects appear in the transition zone of the secondary weld interface.The AA1060/DC56D interface is mainly straight,with only a small number of discontinuous transition zones distributed intermittently along the interface.These transition zones are characterized by the presence of the brittle IMC FeAl_(3),with a maximum thickness of about 4μm.
基金supported by the National Natural Science Foundation of China(No.52405394)the Natural Science Foundation of Shanghai(No.24ZR1436500)+2 种基金the Natural Science Foundation of Chongqing(No.CSTB2024NSCQMSX0677)the Science Innovation Foundation of Shanghai Academy of Spaceflight Technology(No.SAST2024-039)the Startup Fund for Young Faculty at SJTU(No.24X010502880).
文摘Magnesium-rare earth(Mg-RE)alloys are pivotal for lightweight applications in aerospace and advanced engineering due to their high specific strength.However,manufacturing large-scale complex components via monolithic casting is challenging owing to defects such as RE oxides and shrinkage porosity,making fusion welding essential for both defect repair and structural joining.This review comprehensively examines recent advances in fusion welding of Mg-RE alloys,with emphasis on the interplay between their unique physicochemical properties and welding metallurgy.Various fusion welding methods suitable for Mg-RE alloys are compared and analyzed.Detailed characterization of joint regions reveals how thermal gradients and cooling rates govern phase evolution,grain morphology,and defect formation.Moreover,welding parameters and heat treatment strategies are systematically discussed for the microstructural configuration,especially for the inherent conflicts between grain coarsening in fusion zone and eutectic dissolution in heat-affected zone.Future research directions are also outlined.By correlating Mg-RE alloy properties with fusion welding processes,this review provides practical insights for designing reliable welded structures in critical applications.
基金funded on the one hand by Agence de l'Innovation de Défense(AID)grant reference number 2021650044on the other hand by Ecole Centrale de Nantes。
文摘Joining dissimilar materials encounters significant engineering challenges due to the contrast in material properties that makes conventional welding not feasible.Magnetic Pulse Welding(MPW)offers a solidstate joining technique that overcomes these issues by using impact to create strong bonds without melting the substrate materials.This study investigates the weldability of aluminum alloy Al-5754 with Al-7075 and MARS 380 steel,used in armouring solutions of defense systems,by the use of MPW.In this work,weldability windows are investigated by varying standoff distances between the coating material and its substrate(0.25-4.5 mm)and discharge energies(5-13 kJ)with both O-shape and U-shape inductors.Mechanical strength of the welded joints were assessed through single lap shear tests,identifying optimal welding parameters.Then,the velocity profiles of the flyer plates were measured using heterodyne velocimetry to understand the dynamics of the impact.Then,substructures assembled with the optimal welding conditions were subjected to ballistic testing using 7.62 mm×51 mm NATO and 9 mm×19 mm Parabellum munitions to evaluate the resilience of the welds under ballistic impact.The outcomes demonstrate that MPW effectively joins Al-5754 with both Al-7075 and MARS 380,producing robust welds capable of withstanding ballistic impacts under certain conditions.This research advances the application of MPW in lightweight ballistic protection of defense systems,contributing to the development of more resilient and lighter protective structures.
基金Project(ASM-20240)supported by the Key Laboratory of Advanced Structural Materials(Changchun University of Technology),Ministry of Education,ChinaProject(2022TD-30)supported by the Scientific and Technological Innovation Team Project of Shaanxi Innovation Capability Support Plan,China。
文摘This work examines the microstructure and corrosion properties of fine-grained Al 7075 across different regions under varying cooling conditions during friction stir welding.The findings demonstrate that forced cooling significantly improves the corrosion resistance of the welded joints.Specifically,the corrosion resistance was the highest in the stir zone,followed by the thermo-mechanical affected zone,and then the heat affected zone.Forced cooling mitigates grain growth by controlling the welding thermal effects,thereby increasing the proportion ofΣ3 grain boundaries.The modification of these microstructural characteristics promotes the formation of a dense oxide layer,thereby enhancing the corrosion resistance.Furthermore,forced cooling mitigates the precipitation and coarsening of the anodic phase in the stir zone,which in turn reduces the susceptibility of the joint to pitting corrosion.Additionally,the lower recrystallization texture content in the joint,resulting from forced cooling,contributes to a reduction in the number of corrosion-active sites,thereby further improving the corrosion performance of the welded joint.
基金Supported by the National Natural Science Foundation of China under Grant No.51975138the High-Tech Ship Scientific Research Project from the Ministry of Industry and Information Technology under Grant No.CJ05N20the National Defense Basic Research Project under Grant No.JCKY2023604C006.
文摘Marine thin plates are susceptible to welding deformation owing to their low structural stiffness.Therefore,the efficient and accurate prediction of welding deformation is essential for improving welding quality.The traditional thermal elastic-plastic finite element method(TEP-FEM)can accurately predict welding deformation.However,its efficiency is low because of the complex nonlinear transient computation,making it difficult to meet the needs of rapid engineering evaluation.To address this challenge,this study proposes an efficient prediction method for welding deformation in marine thin plate butt welds.This method is based on the coupled temperature gradient-thermal strain method(TG-TSM)that integrates inherent strain theory with a shell element finite element model.The proposed method first extracts the distribution pattern and characteristic value of welding-induced inherent strain through TEP-FEM analysis.This strain is then converted into the equivalent thermal load applied to the shell element model for rapid computation.The proposed method-particularly,the gradual temperature gradient-thermal strain method(GTG-TSM)-achieved improved computational efficiency and consistent precision.Furthermore,the proposed method required much less computation time than the traditional TEP-FEM.Thus,this study lays the foundation for future prediction of welding deformation in more complex marine thin plates.
基金supported by the National Natural Science Foundation of China (Nos. 52075449, 51975480)。
文摘The dissimilar 2B06 and 7B04 Al alloy joints were prepared by refill friction stir spot welding(RFSSW),and the microstructural evolution and corrosion behavior of the joints were investigated.Based on microstructural analysis,the welded joints exhibit distinct microstructural zones,including the stir zone(SZ),thermomechanically affected zone(TMAZ),and heat-affected zone(HAZ).The grain size of each zone is in the order of HAZ>TMAZ>SZ.Notably,the TMAZ and HAZ contain significantly larger secondary-phase particles compared to the SZ,with particle size in the HAZ increasing at higher rotational speeds.Electrochemical tests indicate that corrosion susceptibility follows the sequence of HAZ>TMAZ>SZ>BM,with greater sensitivity observed at increased rotational speeds.Post-corrosion mechanical performance degradation primarily arises from crevice corrosion at joint overlaps,but not from the changes in the microstructure.
基金Supported by Defense Industrial Technology Development Program of China(Grant No.JCKY2021605B015).
文摘Welding deformation adversely affects the quality and precision of structural components,and traditional methods require significant material resources and time.Machine learning has demonstrated exceptional ac-curacy and efficiency in solving complex problems.Thus,the use of machine learning to predict welding de-formations is a novel approach.In this study,laser welding experiments were conducted on a TC4 titanium alloy to establish a welding deformation dataset.The deep neural network(DNN)and convolutional neural network(CNN)models were designed and constructed,with average prediction errors of 0.85 mm and 0.94 mm on the validation set,respectively.To further optimize the network parameters,a differential evolution algorithm was employed through mutation,crossover,and selection.The results indicated that after optimization,the pre-diction errors of the DNN and CNN models reduced to 0.75 mm and 0.85 mm,respectively.These represent accuracy improvements of 14.8%and 9.6%,respectively.The optimized models exhibited superior predictive performances for the validation set.
基金the National Natural Science Foundation of China(No.51475297)the Fund of the Ministry of Industry and Information Technology of China Under the Project of LNG Shipbuilding
文摘Multi-pass tandem gas metal arc welding(TGMAW) for Al 5083 alloy plates with 30 mm thickness is carried out to study its high efficiency and high quality. The welding process is evaluated by high-speed photographs and electrical signals. The deposition rate and welding time are calculated to characterize the welding efficiency. The bead formation, porosity, microstructure and mechanical properties are tested and analyzed. The results indicate that though arc deflection occurs due to the electromagnetic interference between two arcs during TGMAW process, it does not affect the welding process stability significantly. The deposition rate and welding time of TGMAW process are about 15 g/min larger and about 16.7% less than those of gas metal arc welding(GMAW)process respectively, accompanied by the reduction of heat input. The TGMAW welded joint has less porosity and more refined microstructure to contribute to the improvement of mechanical properties(micro-hardness, tensile strength and ductility). It can be concluded that TGMAW process yields excellent performance of welded joint with improved welding efficiency, which makes it extremely practical during welding of thick plates.
基金financially supported by the Key Research and Development Program of Ningbo(Grant No.2023Z098)Natural Science Foundation of Inner Mongolia(Grant No.2023MS05040)+1 种基金Shenyang Collaborative Innovation Center Project for Multiple Energy Fields Composite Processing of Special Materials(Grant No.JG210027)Shenyang Key Technology Special Project of The Open Competition Mechanism to Select the Best Solution(Grant Nos.2022210101000827,2022-0-43-048).
文摘Titanium alloy has the advantages of high strength,strong corrosion resistance,excellent high and low temperature mechanical properties,etc.,and is widely used in aerospace,shipbuilding,weapons and equipment,and other fields.In recent years,with the continuous increase in demand for medium-thick plate titanium alloys,corresponding welding technologies have also continued to develop.Therefore,this article reviews the research progress of deep penetration welding technology for medium-thick plate titanium alloys,mainly covering traditional arc welding,high-energy beam welding,and other welding technologies.Among many methods,narrow gap welding,hybrid welding,and external energy field assistance welding all contribute to improving the welding efficiency and quality of medium-thick plate titanium alloys.Finally,the development trend of deep penetration welding technology for mediumthick plate titanium alloys is prospected.
基金National Natural Science Foundation of China(52275349)Key Research and Development Program of Shandong Province(2021ZLGX01)。
文摘Friction stir lap welding of AA2195 Al-Li alloy and Ti alloy was conducted to investigate the formation,microstructure,and mechanical properties of the joints.Results show that under different welding parameters,with the decrease in welding heat input,the weld surface is smoother.The Ti/Al joint interface is flat without obvious Ti and Al mixed structure,and the hook structure is not formed under optimal parameters.Due to the enhanced breaking effect of the stirring head,the hook structural defects and intermetallic compounds are more likely to form at the Ti/Al interface at high rotational speed of 1000 r/min,thereby deteriorating the mechanical properties of joints.Decreasing the heat input is beneficial to hardness enhancement of the aluminum alloy in the weld nugget zone.Under the optimal parameters of rotation speed of 800 r/min and welding speed of 120 mm/min,the maximum tensile shear strength of joint is 289 N/mm.
文摘Friction stir welding(FSW)is a relatively new welding technique that has significant advantages compared to the fusion welding techniques in joining non weld able alloys by fusion,such as aluminum alloys.Three FSW seams of AA6061-T6 plates were made us-ing different FSW parameters.The structure of the FSW seams was investigated using X-ray diffraction(XRD),scanning electron mi-croscope(SEM)and non destructive testing(NDT)techniques and their hardness was also measured.The dominated phase in the AA6061-T6 alloy and the FSW seams was theα-Al.The FSW seam had lower content of the secondary phases than the AA6061-T6 al-loy.The hardness of the FSW seams was decreased by about 30%compared to the AA6061-T6 alloy.The temperature distributions in the weld seams were also studied experimentally and numerically modeled and the results were in a good agreement.
基金supported by the Industrial Innovation Major Technology Global Unveiling Project of Jining City(2022JBZP004)Taishan Scholars Project.
文摘Laser twin-arc GTAW(LTA-GTAW)process has been developed by using the synergic interaction effects of laser and a coupled arc in a weld pool to achieve higher energy efficiency.In this study,bead-on-plate welding was conducted on 8-mm-thick Q235B work-pieces to investigate the variation of hybrid arc profile,the influence of hybrid arc profile on weld forming,microstructure and mech-anical properties of the joint during the LTA-GTAW process.The influence of Laser-GTAW and LTA-GTAW methods on weld surface appearance,heat input per unit length,and weld metal microstructure were also demonstrated systematically.The LTA-GTAW can make the distribution of arc energy more reasonable in welding depth and width.When defocus is 0,I_(f)is 330 A,I_(b)is 240 A,laser power is 2.4 kW,and spacing between heat sources of tungsten electrode is 10 mm,the weld shape is better.Compared with Laser-GTAW,LTA-GTAW can achieve lower heat input at the same penetration depth,and the microstructure of the weld is refined.The tensile strength of the welded joint is 121.8%of the base material,and the fracture mode of the welded joint is ductile fracture,the comprehensive mechanical properties are better.
基金supported by the National Natural Science Foundation of China(Grant No.52035005)the Key R&D Program of Shandong Province in China(Grant No.2021ZLGX01).
文摘The composite structures/components made by friction stir lap welding(FSLW)of Mg alloy sheet and Al alloy sheet are of wide application potentials in the manufacturing sector of transportation vehicles.To further improve the joint quality,the ultrasonic vibration(UV)is exerted in FSLW,and the UV enhanced FSLW(UVeFSLW)was developed for making Mg-to-Al dissimilar joints.The numerical analysis and experimental investigation were combined to study the process mechanism in Mg/Al UVeFSLW.An equation related to the temperature and strain rate was derived to calculate the grain size at different locations of the weld nugget zone,and the effect of grain size distribution on the threshold thermal stress was included,so that the prediction accuracy of flow stress was further improved.With such modified constitutive equation,the numerical simulation was conducted to compare the heat generation,temperature profiles and material flow behaviors in Mg/Al UVeFSLW/FSLW processes.It was found that the exerted UV decreased the temperature at two checking points on the tool/workpiece interface from 707/671 K in FSLW to 689/660 K in UVeFSLW,which suppressed the IMCs thickness at Mg-Al interface from 1.7μm in FSLW to 1.1μm in UVeFSLW.The exerted UV increased the horizontal materials flow ability,and decreased the upward flow ability,which resulted in the increase of effective sheet thickness/effective lap width from 2.01/3.70 mm in FSLW to 2.04/4.84 mm in UVeFSLW.Therefore,the ultrasonic vibration improved the tensile shear strength of Mg-to-Al lap joints by 18%.