The aim of this study was to fabricate multi-layered recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL composites for microwave absorbing applications in the 1 - 4 GHz frequency range. Th...The aim of this study was to fabricate multi-layered recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL composites for microwave absorbing applications in the 1 - 4 GHz frequency range. The multi-layered composites were 6 mm thick and each consisted of a 2 mm thick layer of recycled α-Fe<sub>2</sub>O<sub>3</sub>/PCL composites at various loadings (5 wt% - 25 wt%) of 16.2 nm recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller, placed between two layers of 2 mm thick OPEFB fiber/PCL composites blended at a fixed ratio of 7:3. The real (ε') and imaginary (ε") components of the relative complex permittivity were measured using the open-ended coaxial probe technique and the values obtained were applied as inputs for the Finite Element Method to calculate the reflection coefficient magnitudes from which the reflection loss (RL) properties were determined. Both ε' and ε" increased linearly with recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller content and the values of ε' varied between 3.0 and 3.9 while the ε" values ranged between 0.26 and 0.64 within 1 - 4 GHz. The RL (dB) showed the most prominent values within the 1.38 - 1.46 GHz band with a minimum of -38 dB attained by the 25 wt% composite. Another batch of minimum values occurred in the 2.39 - 3.49 GHz range with the lowest of -25 dB at 2.8 GHz. The recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL multi-layered composites are promising materials that can be engineered for solving noise problems in the 1 - 4 GHz range.展开更多
A multi-layered composite scaffolds consisting of poly （ L- ne） （ P （LLA-CL） ）, collagen （COL） and chitosan （CS） were fabricated by a bi-directional electrospinnlng method. Synthetic P （LLA-CL） was used as...A multi-layered composite scaffolds consisting of poly （ L- ne） （ P （LLA-CL） ）, collagen （COL） and chitosan （CS） were fabricated by a bi-directional electrospinnlng method. Synthetic P （LLA-CL） was used as the middle layer to enhance the strength, while natural COL/CS blending （9： 1, v/v） was used as the bioactive surfaces （inner and outer layers ） to improve the biocompatibility. Each three transitional layers were set between inner/outer layer and middle layer for delamination resistance. Scanning electron microscopy （SEM） was used to observe the fiber morphology. The Fourier transform infrared attenuated total reflectance spectroscopy （FTIR-ATR） spectra, X- ray diffraction （XRD） and thermogravimetry （TG） tests were used to analyze the physical properties of the scaffolds. The results showed that the modified clectrospinning method bad no negative effect on the components, crystal structure and thermostability of the scaffolds, but could effectively combine the mechanical property of synthetic material and biocompatibility of natural materials. Such method could be applied to the fabrication of composite scaffolds for vascular, skin. and nerve tissue engineering.展开更多
A philosophy for the design of novel,lightweight,multi-layered armor,referred to as Composite Armor Philosophy(CAP),which can adapt to the passive protection of light-,medium-,and heavy-armored vehicles,is presented i...A philosophy for the design of novel,lightweight,multi-layered armor,referred to as Composite Armor Philosophy(CAP),which can adapt to the passive protection of light-,medium-,and heavy-armored vehicles,is presented in this study.CAP can serve as a guiding principle to assist designers in comprehending the distinct roles fulfilled by each component.The CAP proposal comprises four functional layers,organized in a suggested hierarchy of materials.Particularly notable is the inclusion of a ceramic-composite principle,representing an advanced and innovative solution in the field of armor design.This paper showcases real-world defense industry applications,offering case studies that demonstrate the effectiveness of this advanced approach.CAP represents a significant milestone in the history of passive protection,marking an evolutionary leap in the field.This philosophical approach provides designers with a powerful toolset with which to enhance the protection capabilities of military vehicles,making them more resilient and better equipped to meet the challenges of modern warfare.展开更多
Metallic glass composites hold significant potential as structural materials.However,few methods are available to enhance their mechanical properties postcasting.In this study,simple pre-tensile training was applied t...Metallic glass composites hold significant potential as structural materials.However,few methods are available to enhance their mechanical properties postcasting.In this study,simple pre-tensile training was applied to a TRIP-reinforced metallic glass composite,resulting in a more than one-third increase in plasticity,while the reliability of plasticity was also enhanced.The deformation mechanism was further elucidated,revealing that pre-tension induced the formation of multilayered nanostructures at the dendrite-glass interface.This microstructural evolution facilitates the formation of finer martensite laths within the dendrites and multiple shear bands in the glass matrix during compression,thereby enabling more uniform plastic deformation.These findings suggest that simple preloading treatments may offer a viable approach to regulating the microstructure of as-cast metallic glass composites and optimizing their mechanical properties.展开更多
This work aims to evaluate the feasibility of the fabrication of nanostructured Cu/Al/Ag multi-layered composites by accumulative roll bonding(ARB),and to analyze the tensile properties and electrical conductivity of ...This work aims to evaluate the feasibility of the fabrication of nanostructured Cu/Al/Ag multi-layered composites by accumulative roll bonding(ARB),and to analyze the tensile properties and electrical conductivity of the produced composites.A theoretical model using strengthening mechanisms and some structural parameters extracted from X-ray diffraction is also developed to predict the tensile strength of the composites.It was found that by progression of ARB,the experimental and calculated tensile strengths are enhanced,reach a maximum of about 450 and 510 MPa at the fifth cycle of ARB,respectively and then are reduced.The electrical conductivity decreased slightly by increasing the number of ARB cycles at initial ARB cycles,but the decrease was intensified at the final ARB cycles.In conclusion,the merit of ARB to fabricate this type of multi-layered nanocomposites and the accuracy of the developed model to predict tensile strength were realized.展开更多
Carbon fiber reinforced high density polyethylene multi-layered laminated composite panels（HDPE/CF MLCP） with excellent in-plane properties along transverse direction have been formulated. Composite architectures wi...Carbon fiber reinforced high density polyethylene multi-layered laminated composite panels（HDPE/CF MLCP） with excellent in-plane properties along transverse direction have been formulated. Composite architectures with carbon fiber（CF） designed in 2D layout in conventional composites can alleviate their properties in thickness direction, but all attempts so far developed have achieved restrained success. Here,we have exposed an approach to the high strength composite challenge, without altering the 2D stack design on the basis of concept of fiber reinforced laminated composites that would provide enhanced mechanical and thermal properties along transverse direction. CF sheets allowed the buckling of adjoining plies in 2D MLCP. We fabricated 2D MLCP by stacking the alternative CF and HDPE layers under different loading conditions, which resulted in high strength composites. These plies of CF and HDPE served as unit cells for MLCP, with CF offering much-needed fracture toughness and hardness to these materials.For 2D HDPE/CF MLCP, we demonstrated noteworthy improvement in physical and chemical interaction between CF and HDPE, in-plane fracture strain, flexural strength（30.684 MPa）, bending modulus（7436.254 MPa）, thermal stability（40.94%）, and surface morphology, upon increasing the CF layers up to twenty, enabling these composites truly for high temperature and high strength applications.展开更多
Among various architectures of polymers,end-group-free rings have attracted growing interests due to their distinct physicochemical performances over the linear counterparts which are exemplified by reduced hydrodynam...Among various architectures of polymers,end-group-free rings have attracted growing interests due to their distinct physicochemical performances over the linear counterparts which are exemplified by reduced hydrodynamic size and slower degradation.It is key to develop facile methods to large-scale synthesis of polymer rings with tunable compositions and microstructures.Recent progresses in large-scale synthesis of polymer rings against single-chain dynamic nanoparticles,and the example applications in synchronous enhancing toughness and strength of polymer nanocomposites are summarized.Once there is the breakthrough in rational design and effective large-scale synthesis of polymer rings and their functional derivatives,a family of cyclic functional hybrids would be available,thus providing a new paradigm in developing polymer science and engineering.展开更多
Ultrasonic-Assisted Grinding(UAG)is a novel manufacturing technology that shows promising promise for use in processing Ceramic Matrix Composites(CMCs).Nevertheless,analyzing the material removal process of CMCs with ...Ultrasonic-Assisted Grinding(UAG)is a novel manufacturing technology that shows promising promise for use in processing Ceramic Matrix Composites(CMCs).Nevertheless,analyzing the material removal process of CMCs with multidirectional structure during UAG is challenging,impeding the progress and improvement of the UAG process.This work examined the impact of ultrasonic vibration on the dynamic mechanical characteristics during processing.Additionally,we experimentally elucidated the material removal mechanism of CMCs during the scratching process under the influence of vertical vibration.The results indicate that the introduction of ultrasonic vibration causes a strain rate effect,resulting in a modification of the material removal mechanism,subsequently impacting the processing quality.Ultrasonic vibration increases the dynamic strength and brittleness of the fibers in CMCs,leading to more cracks at fracture,which changes from the original bending fracture to shear fracture.In addition,ultrasonic vibration can effectively inhibit the impact of scratching depth and anisotropy on the removal mechanism of CMCs,resulting in a more uniform surface of CMCs after processing.展开更多
A composite electrocatalyst,CoMoNiO-S/NF-110(NF is nickel foam),was synthesized through electrodeposition,followed by pyrolysis and then the vulcanization process.CoMoNiO-S/NF-110 exhibited a structure where Ni3S2 and...A composite electrocatalyst,CoMoNiO-S/NF-110(NF is nickel foam),was synthesized through electrodeposition,followed by pyrolysis and then the vulcanization process.CoMoNiO-S/NF-110 exhibited a structure where Ni3S2 and Mo2S3 nanoparticles were integrated at the edges of Co3O4 nanosheets,creating a rich,heterogeneous interface that enhances the synergistic effects of each component.In an alkaline electrolyte,the synthesized CoMoNiO-S/NF-110 exhibited superior electrocatalytic performance for oxygen evolution reaction(OER),achieving current densities of 100 and 200 mA·cm^(-2) with low overpotentials of 199.4 and 224.4 mV,respectively,outperforming RuO2 and several high-performance Mo and Ni-based catalysts.This excellent performance is attributed to the rich interface formed between the components and active sites exposed by the defect structure.展开更多
KIT-5/Beta composite supports were synthesized using an in situ self-assembly hydrothermal method,and NiW/KIT-5/Beta catalysts were prepared by impregnation.A series of characterization techniques were utilized to eva...KIT-5/Beta composite supports were synthesized using an in situ self-assembly hydrothermal method,and NiW/KIT-5/Beta catalysts were prepared by impregnation.A series of characterization techniques were utilized to evaluate the influence of varying hydrothermal synthesis temperatures on the physicochemical properties of both the KIT-5/Beta supports and the resulting catalysts.The catalytic performances of catalysts were evaluated under reaction conditions of 320℃,4 MPa H_(2)pressure,and a weight hourly space velocity(WHSV)of 4.8 h^(-1)for hydrodenitrogenation(HDN)of quinoline.The results indicated that the specific surface area and pore structure of the materials could be effectively regulated by adjusting the hydrothermal synthesis temperature,which in turn influenced the number of active sites on the catalyst.The NiW/KB-125 catalyst,synthesized at 125℃,presented the highest quinoline HDN efficiency(96.8%),which can be attributed to its favorable pore channel structure,greater Brønsted acid number,higher degree of metal sulfidation(80.12%)and appropriate metal-support interaction(MSI).展开更多
Carbon fiber-reinforced carbon aerogel(C/CA)composites are one of the most promising candidates for applications requiring both thermal insulation and load bearing capabilities.The preparation of anti-oxidation coatin...Carbon fiber-reinforced carbon aerogel(C/CA)composites are one of the most promising candidates for applications requiring both thermal insulation and load bearing capabilities.The preparation of anti-oxidation coatings on C/CA to address its susceptibility to oxidation is a feasible approach to promote its application in oxidative environments.However,the currently reported coatings on C/CA mainly focus on improving the ablation performance and coating preparation process typically necessitating high-temperature heat treatment.This procedure can increase its thermal conductivity and reduce its thermal insulation ability.In this study,a series of ceramic-resin coatings were fabricated on C/CA through a simple slurry brushing-drying approach at room temperature.The effects of phenolic resin content on the coating structure,residual stress,thermal shock,and oxidation behaviors were investigated.Due to the adhesive properties and curing-induced shrinkage,the PR-7.5 coating(containing 7.5%(in mass)phenolic resin in the slurry)exhibits bonding strength close to fracture strength of the substrate and residual compressive stress of 0.853 GPa,which is beneficial for resisting thermal shock cracking.However,excessive resin content(PR-10.0 containing 10.0%(in mass)phenolic resin in the slurry)induces tensile stress due to uneven curing shrinkage,thereby leading to thermal shock cracking.Meanwhile,oxidation tests reveal significantly reduced weight losses for PR-7.5(17.46%at 800℃/100 min,8.15%at 1000℃/120 min,3.15%at 1200℃/120 min)versus uncoated C/CA’s 44.60%loss at 800℃/20 min.This work provides a brand-new and simple approach to improving the anti-oxidation performance of C/CA and expands its application in mild oxidative environments.展开更多
The poor electrical conductivity of metal-organic frameworks(MOFs)limits their electrocatalytic performance in the oxygen evolution reaction(OER).In this study,a Py@Co-MOF composite material based on pyrene(Py)molecul...The poor electrical conductivity of metal-organic frameworks(MOFs)limits their electrocatalytic performance in the oxygen evolution reaction(OER).In this study,a Py@Co-MOF composite material based on pyrene(Py)molecules and{[Co2(BINDI)(DMA)_(2)]·DMA}_(n)(Co-MOF,H4BINDI=N,N'-bis(5-isophthalic acid)naphthalenediimide,DMA=N,N-dimethylacetamide)was synthesized via a one-pot method,leveragingπ-πinteractions between pyrene and Co-MOF to modulate electrical conductivity.Results demonstrate that the Py@Co-MOF catalyst exhibited significantly enhanced OER performance compared to pure Co-MOF or pyrene-based electrodes,achieving an overpotential of 246 mV at a current density of 10 mA·cm^(-2) along with excellent stability.Density functional theory(DFT)calculations reveal that the formation of O*in the second step is the rate-determining step(RDS)during the OER process on Co-MOF,with an energy barrier of 0.85 eV due to the weak adsorption affinity of the OH*intermediate for Co sites.CCDC:2419276.展开更多
Graphene/copper-based composite heat sinks demonstrate extensive application potential in military equipment thermal management,high-power electronic packaging,new energy vehicles,and 5G communication systems,due to t...Graphene/copper-based composite heat sinks demonstrate extensive application potential in military equipment thermal management,high-power electronic packaging,new energy vehicles,and 5G communication systems,due to their outstanding properties,including high thermal conductivity,tunable thermal expansion coefficients,excellent mechanical strength,and low density.However,the industrial-scale application of these composites faces critical challenges during the fabrication of components with complex structures,such as inhomogeneous dispersion of graphene within the copper matrix and poor interfacial bonding between the two phases,which substantially undermine the overall performance of graphene/copper-based composites.To address these issues,the preparation methods for graphene/copper-based composite heat sinks were reviewed.For each method,a rigorous analysis was presented to clarify its inherent advantages and unavoidable restrictions.Furthermore,the latest research progress in addressing three core scientific challenges was synthesized,including uniform dispersion of graphene,interfacial optimization mechanisms,and molecular dynamics simulations for elucidating the structure-property relationships.Finally,the future development directions of graphene/copper-based composite heat sinks in engineering applications were prospected.展开更多
We mixed Bacillus subtilis and brewing yeast to prepare composite microbial self-healing materials,and studied the self-healing effect of composite microorganisms in mortar cracks of different widths and cracking ages...We mixed Bacillus subtilis and brewing yeast to prepare composite microbial self-healing materials,and studied the self-healing effect of composite microorganisms in mortar cracks of different widths and cracking ages.The experimental results show that the performance and self-healing effect of composite micro-organisms are significantly better than those of single microorganisms.For cracks with widths of 0.2-0.4 mm,the repair effect of the composite microorganisms at 28 days is 42.7%and 71.2%higher than that of pure Bacillus and pure yeast,respectively.The repairing rate of the area with the widths of the cracks of 0.2-0.4,0.4-0.6,and 0.6-0.8 mm are 100%,77.3%,and 53.4%,respectively.The area repair rates corresponding to cracking ages of 56,90,and 180 days are 73.3%,55.4%,and 30.8%,respectively.展开更多
Traditional dynamic analysis of mechanical structures,often limited to individual beams or plates,fails to fully capture their dynamic behaviors.In systems where space and mass are constrained,such as the battery supp...Traditional dynamic analysis of mechanical structures,often limited to individual beams or plates,fails to fully capture their dynamic behaviors.In systems where space and mass are constrained,such as the battery support structures in electric aircraft,conventional absorbers and isolators are insufficient for effective vibration control.This study simplifies the battery support structure of electric aircraft as an integrated composite beam consisting of three interconnected beams,and investigated its structural dynamics properties and nonlinear vibration control under thermal conditions caused by battery heat.The nonlinear vibration control is performed using the Nitinol steel wire ropes(Ni Ti-ST),with nonlinear damping properties.The natural frequencies of system are determined using the Rayleigh-Ritz technique.Theoretical results are validated through both Finite Element Method(FEM)and hammer tests.Moreover,the dynamic equations are derived using the Lagrange method and discretized via the Galerkin Truncation Method(GTM).The Harmonic Balance Method(HBM)is used to evaluate the vibration responses of the integrated model,with further verification through the Runge-Kutta Method(RKM).The experiments are conducted to corroborate the theoretical analysis.The results show that the system frequency changes in stages with the increase of the stiffness of the integrated composite beam connection.Especially in the case of varying environments,as the temperature increases,the frequency of system will first increase to a certain maximum value and then gradually decrease.Furthermore,the NiTi-ST effectively reduces vibration in the integrated composite beam,particularly under varying temperatures and external excitations.展开更多
Transportation structures such as composite pavements and railway foundations typically consist of multi-layered media designed to withstand high bearing capacity.A theoretical understanding of load transfer mechanism...Transportation structures such as composite pavements and railway foundations typically consist of multi-layered media designed to withstand high bearing capacity.A theoretical understanding of load transfer mechanisms in these multi-layer composites is essential,as it offers intuitive insights into parametric influences and facilitates enhanced structural performance.This paper employs an improved transfer matrix method to address the limitations of existing theoretical approaches for analyzing multi-layer composite structures.By establishing a twodimensional composite pavement model,it investigates load transfer characteristics and validates the accuracy through finite element simulation.The proposed method offers a straightforward analytical approach for examining internal interactions between structural layers.Case studies indicate that the concrete surface layer is the main load-bearing layer for most vertical normal and shear stresses.The soil base layer reduces the overall mechanical response of the substructure,while horizontal actions increase the risk of interfacial slip and cracking.Structural optimization analysis demonstrates that increasing the thickness of the concrete surface layer,enhancing the thickness and stiffness of the soil base layer,or incorporating gradient layers can significantly mitigate these risks of interfacial slip and cracking.The findings of this study can guide the optimization design,parameter analysis,and damage prevention of multi-layer composite structures.展开更多
The TiB+TiC dual-reinforced B_(4)C/TC4 composite was in-situ fabricated via incorporating 0.5wt%B_(4)C reinforcement during the laser melting deposition process.Different heat treatments of annealing and solid solutio...The TiB+TiC dual-reinforced B_(4)C/TC4 composite was in-situ fabricated via incorporating 0.5wt%B_(4)C reinforcement during the laser melting deposition process.Different heat treatments of annealing and solid solution were used to regulate the microstructure,mechanical properties,and corrosion properties of B_(4)C/TC4 composite.Results show that with the increase in temperature from 500℃to 800°C,partial lamellarα-Ti in the as-deposited sample is gradually transformed into equiaxedα-Ti,accompanied by the disappearance of basketweave microstructure.At 1100°C,a small portion of TiC phase suffers fusion.This composite exhibits the optimal combination of strength and plasticity after annealing at 500℃for 4 h followed by furnace cooling,which is attributed to the stress release effect and the refined basketweave microstructure.However,this composite shows a decline in corrosion resistance after various heat treatments due to grain coarsening and micro-galvanic corrosion.展开更多
This work addresses optimality aspects related to composite laminates having layers with different orientations.RegressionNeuralNetworks can model the mechanical behavior of these laminates,specifically the stressstra...This work addresses optimality aspects related to composite laminates having layers with different orientations.RegressionNeuralNetworks can model the mechanical behavior of these laminates,specifically the stressstrain relationship.If this model has strong generalization ability,it can be coupled with a metaheuristic algorithm–the PSO algorithm used in this article–to address an optimization problem(OP)related to the orientations of composite laminates.To solve OPs,this paper proposes an optimization framework(OFW)that connects the two components,the optimal solution search mechanism and the RNN model.The OFW has two modules:the search mechanism(Adaptive Hybrid Topology PSO)and the Prediction and Computation Module(PCM).The PCM undertakes all the activities concerning the OP at hand:the stress-strain model,constraints checking,and computation of the objective function.Two case studies about the layers’orientations of laminated specimens are conducted to validate the proposed framework.The specimens belong to“Off-axis oriented specimens”and are subjects of two OPs.The algorithms for AHTPSO and for the two PCMs(one for each problem)are proposed and implemented by MATLAB scripts and functions.Simulations are carried out for different initial conditions.The solutions demonstrated that the OFW is effective and has a highly acceptable computational complexity.The limitation of using the OFWis the generalization ability of the RNN model or any other regression models.To harness the RNN model efficiently,it must have a very good generalization power.If this condition ismet,the OFWcan be integrated into any design process to make optimal choices of the layers’orientations.展开更多
In this study,using 3,5‑di(3′,5′‑dicarboxylphenyl)‑1H‑1,2,4‑triazole(H4L)as ligands,a gadolinia‑based organic framework complex{[GdNa(L)(H_(2)O)3]·2H_(2)O}_(n)(Gd‑Na‑MOF)was successfully designed and synthesize...In this study,using 3,5‑di(3′,5′‑dicarboxylphenyl)‑1H‑1,2,4‑triazole(H4L)as ligands,a gadolinia‑based organic framework complex{[GdNa(L)(H_(2)O)3]·2H_(2)O}_(n)(Gd‑Na‑MOF)was successfully designed and synthesized by hydrothermal method.The structure and properties were systematically characterized and tested by techniques such as single‑crystal X‑ray diffraction,powder X‑ray diffraction,thermogravimetric analysis,infrared spectroscopy,and fluorescence spectroscopy.The results indicate that this complex has a unique 3D structure,excellent thermal stability,and outstanding luminescent performance.Based on its luminescent properties,a polymer‑embedding method was employed to fabricate the Gd‑Na‑MOF into a flexible,washable composite fluorescent film,Gd‑Na‑MOF@PMMA/BMA(PMMA=polymethyl methacrylate,BMA=butyl methacrylate).This fluorescent film exhibited highly sensitive recognition capability for tyramine,with a low detection limit of 1.66μmol·L^(-1).It was used for the detection of tyramine in bananas,with a recovery rate of 96.92%‑100.26%.CCDC:2466949.展开更多
Biochar and biochar composites are versatile materials that can be used in many applications.In this study,biochar was prepared from sawdust and combined with the yttrium iron garnet(YIG)nanocrystal to investigate the...Biochar and biochar composites are versatile materials that can be used in many applications.In this study,biochar was prepared from sawdust and combined with the yttrium iron garnet(YIG)nanocrystal to investigate the shielding effectiveness of the composite structure.Firstly,the effect of the pyrolysis temperature on the shielding effectiveness of biochar was investigated.Secondly,biochars combined with YIG nanocrystals with different contents and shielding effectiveness of the composites were investigated.The electromagnetic effectiveness of the samples was investigated within the X band(8-12 GHz).The findings indicate that biochar demonstrates enhanced absorption properties with elevated pyrolysis temperatures.Biochars demonstrated an approximate 40 d B shielding effectiveness,while YIG exhibited approximately 7 d B,corresponding to absorption at 8 GHz.However,the combination of biochar and YIG exhibited exceptional absorption,reaching 67.12 d B at 8 GHz.展开更多
文摘The aim of this study was to fabricate multi-layered recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL composites for microwave absorbing applications in the 1 - 4 GHz frequency range. The multi-layered composites were 6 mm thick and each consisted of a 2 mm thick layer of recycled α-Fe<sub>2</sub>O<sub>3</sub>/PCL composites at various loadings (5 wt% - 25 wt%) of 16.2 nm recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller, placed between two layers of 2 mm thick OPEFB fiber/PCL composites blended at a fixed ratio of 7:3. The real (ε') and imaginary (ε") components of the relative complex permittivity were measured using the open-ended coaxial probe technique and the values obtained were applied as inputs for the Finite Element Method to calculate the reflection coefficient magnitudes from which the reflection loss (RL) properties were determined. Both ε' and ε" increased linearly with recycled α-Fe<sub>2</sub>O<sub>3</sub> nanofiller content and the values of ε' varied between 3.0 and 3.9 while the ε" values ranged between 0.26 and 0.64 within 1 - 4 GHz. The RL (dB) showed the most prominent values within the 1.38 - 1.46 GHz band with a minimum of -38 dB attained by the 25 wt% composite. Another batch of minimum values occurred in the 2.39 - 3.49 GHz range with the lowest of -25 dB at 2.8 GHz. The recycled α-Fe<sub>2</sub>O<sub>3</sub>/OPEFB fiber/PCL multi-layered composites are promising materials that can be engineered for solving noise problems in the 1 - 4 GHz range.
基金"111 Project" Biomedical Textile Materials Science and Technology,China，National Natural Science Foundations of China，Science and Technology Commission of Shanghai Municipality,China，Ph.D.Programs Foundation of Ministry of Education of China
文摘A multi-layered composite scaffolds consisting of poly （ L- ne） （ P （LLA-CL） ）, collagen （COL） and chitosan （CS） were fabricated by a bi-directional electrospinnlng method. Synthetic P （LLA-CL） was used as the middle layer to enhance the strength, while natural COL/CS blending （9： 1, v/v） was used as the bioactive surfaces （inner and outer layers ） to improve the biocompatibility. Each three transitional layers were set between inner/outer layer and middle layer for delamination resistance. Scanning electron microscopy （SEM） was used to observe the fiber morphology. The Fourier transform infrared attenuated total reflectance spectroscopy （FTIR-ATR） spectra, X- ray diffraction （XRD） and thermogravimetry （TG） tests were used to analyze the physical properties of the scaffolds. The results showed that the modified clectrospinning method bad no negative effect on the components, crystal structure and thermostability of the scaffolds, but could effectively combine the mechanical property of synthetic material and biocompatibility of natural materials. Such method could be applied to the fabrication of composite scaffolds for vascular, skin. and nerve tissue engineering.
基金co-financed by the European Regional Development Fund of the European UnionGreek national funds through the Operational Program Competitiveness,Entrepreneurship and Innovation,under the call RESEARCH-CREATE-INNOVATE(project code:T1EDK-04429)。
文摘A philosophy for the design of novel,lightweight,multi-layered armor,referred to as Composite Armor Philosophy(CAP),which can adapt to the passive protection of light-,medium-,and heavy-armored vehicles,is presented in this study.CAP can serve as a guiding principle to assist designers in comprehending the distinct roles fulfilled by each component.The CAP proposal comprises four functional layers,organized in a suggested hierarchy of materials.Particularly notable is the inclusion of a ceramic-composite principle,representing an advanced and innovative solution in the field of armor design.This paper showcases real-world defense industry applications,offering case studies that demonstrate the effectiveness of this advanced approach.CAP represents a significant milestone in the history of passive protection,marking an evolutionary leap in the field.This philosophical approach provides designers with a powerful toolset with which to enhance the protection capabilities of military vehicles,making them more resilient and better equipped to meet the challenges of modern warfare.
基金financially supported by the National Key Research and Development Plan(No.2021YFA1600600)the National Natural Science Foundation of China(Nos.52271093 and 52074257)+3 种基金the Rare Earth Advanced Materials Technology Innovation Center(No.CXZX-B-2023110011)the Space Application System of China Manned Space Program(No.YYMT1201-EXP08)the special fund for Science and Technology Innovation Teams of Shanxi Province(No.202304051001036)the Fundamental Research Funds for the Central Universities(No.N2325008)
文摘Metallic glass composites hold significant potential as structural materials.However,few methods are available to enhance their mechanical properties postcasting.In this study,simple pre-tensile training was applied to a TRIP-reinforced metallic glass composite,resulting in a more than one-third increase in plasticity,while the reliability of plasticity was also enhanced.The deformation mechanism was further elucidated,revealing that pre-tension induced the formation of multilayered nanostructures at the dendrite-glass interface.This microstructural evolution facilitates the formation of finer martensite laths within the dendrites and multiple shear bands in the glass matrix during compression,thereby enabling more uniform plastic deformation.These findings suggest that simple preloading treatments may offer a viable approach to regulating the microstructure of as-cast metallic glass composites and optimizing their mechanical properties.
文摘This work aims to evaluate the feasibility of the fabrication of nanostructured Cu/Al/Ag multi-layered composites by accumulative roll bonding(ARB),and to analyze the tensile properties and electrical conductivity of the produced composites.A theoretical model using strengthening mechanisms and some structural parameters extracted from X-ray diffraction is also developed to predict the tensile strength of the composites.It was found that by progression of ARB,the experimental and calculated tensile strengths are enhanced,reach a maximum of about 450 and 510 MPa at the fifth cycle of ARB,respectively and then are reduced.The electrical conductivity decreased slightly by increasing the number of ARB cycles at initial ARB cycles,but the decrease was intensified at the final ARB cycles.In conclusion,the merit of ARB to fabricate this type of multi-layered nanocomposites and the accuracy of the developed model to predict tensile strength were realized.
文摘Carbon fiber reinforced high density polyethylene multi-layered laminated composite panels（HDPE/CF MLCP） with excellent in-plane properties along transverse direction have been formulated. Composite architectures with carbon fiber（CF） designed in 2D layout in conventional composites can alleviate their properties in thickness direction, but all attempts so far developed have achieved restrained success. Here,we have exposed an approach to the high strength composite challenge, without altering the 2D stack design on the basis of concept of fiber reinforced laminated composites that would provide enhanced mechanical and thermal properties along transverse direction. CF sheets allowed the buckling of adjoining plies in 2D MLCP. We fabricated 2D MLCP by stacking the alternative CF and HDPE layers under different loading conditions, which resulted in high strength composites. These plies of CF and HDPE served as unit cells for MLCP, with CF offering much-needed fracture toughness and hardness to these materials.For 2D HDPE/CF MLCP, we demonstrated noteworthy improvement in physical and chemical interaction between CF and HDPE, in-plane fracture strain, flexural strength（30.684 MPa）, bending modulus（7436.254 MPa）, thermal stability（40.94%）, and surface morphology, upon increasing the CF layers up to twenty, enabling these composites truly for high temperature and high strength applications.
基金Supported by the National Natural Science Foundation of China(Nos.52293472,22473096 and 22471164)。
文摘Among various architectures of polymers,end-group-free rings have attracted growing interests due to their distinct physicochemical performances over the linear counterparts which are exemplified by reduced hydrodynamic size and slower degradation.It is key to develop facile methods to large-scale synthesis of polymer rings with tunable compositions and microstructures.Recent progresses in large-scale synthesis of polymer rings against single-chain dynamic nanoparticles,and the example applications in synchronous enhancing toughness and strength of polymer nanocomposites are summarized.Once there is the breakthrough in rational design and effective large-scale synthesis of polymer rings and their functional derivatives,a family of cyclic functional hybrids would be available,thus providing a new paradigm in developing polymer science and engineering.
基金supported by the National Science Foundation for Distinguished Young Scholars of China(No.52325506)the Fundamental Research Funds for the Central Universities(No.DUT22LAB501)。
文摘Ultrasonic-Assisted Grinding(UAG)is a novel manufacturing technology that shows promising promise for use in processing Ceramic Matrix Composites(CMCs).Nevertheless,analyzing the material removal process of CMCs with multidirectional structure during UAG is challenging,impeding the progress and improvement of the UAG process.This work examined the impact of ultrasonic vibration on the dynamic mechanical characteristics during processing.Additionally,we experimentally elucidated the material removal mechanism of CMCs during the scratching process under the influence of vertical vibration.The results indicate that the introduction of ultrasonic vibration causes a strain rate effect,resulting in a modification of the material removal mechanism,subsequently impacting the processing quality.Ultrasonic vibration increases the dynamic strength and brittleness of the fibers in CMCs,leading to more cracks at fracture,which changes from the original bending fracture to shear fracture.In addition,ultrasonic vibration can effectively inhibit the impact of scratching depth and anisotropy on the removal mechanism of CMCs,resulting in a more uniform surface of CMCs after processing.
文摘A composite electrocatalyst,CoMoNiO-S/NF-110(NF is nickel foam),was synthesized through electrodeposition,followed by pyrolysis and then the vulcanization process.CoMoNiO-S/NF-110 exhibited a structure where Ni3S2 and Mo2S3 nanoparticles were integrated at the edges of Co3O4 nanosheets,creating a rich,heterogeneous interface that enhances the synergistic effects of each component.In an alkaline electrolyte,the synthesized CoMoNiO-S/NF-110 exhibited superior electrocatalytic performance for oxygen evolution reaction(OER),achieving current densities of 100 and 200 mA·cm^(-2) with low overpotentials of 199.4 and 224.4 mV,respectively,outperforming RuO2 and several high-performance Mo and Ni-based catalysts.This excellent performance is attributed to the rich interface formed between the components and active sites exposed by the defect structure.
基金Supported by the Autonomous Research Project of SKLCC(2024BWZ003)Strategic Priority Research Program of the Chinese Academy of Sciences(XDA0390401)the Doctoral Research Start-up Funding of Shanxi Institute of Technology(026012).
文摘KIT-5/Beta composite supports were synthesized using an in situ self-assembly hydrothermal method,and NiW/KIT-5/Beta catalysts were prepared by impregnation.A series of characterization techniques were utilized to evaluate the influence of varying hydrothermal synthesis temperatures on the physicochemical properties of both the KIT-5/Beta supports and the resulting catalysts.The catalytic performances of catalysts were evaluated under reaction conditions of 320℃,4 MPa H_(2)pressure,and a weight hourly space velocity(WHSV)of 4.8 h^(-1)for hydrodenitrogenation(HDN)of quinoline.The results indicated that the specific surface area and pore structure of the materials could be effectively regulated by adjusting the hydrothermal synthesis temperature,which in turn influenced the number of active sites on the catalyst.The NiW/KB-125 catalyst,synthesized at 125℃,presented the highest quinoline HDN efficiency(96.8%),which can be attributed to its favorable pore channel structure,greater Brønsted acid number,higher degree of metal sulfidation(80.12%)and appropriate metal-support interaction(MSI).
基金National Natural Science Foundation of China(52272075,52472053)Research Fund of Youth Innovation Promotion Association of CAS,China(2021190)Defense Industrial Technology Development Program(JCKY2021130B007)。
文摘Carbon fiber-reinforced carbon aerogel(C/CA)composites are one of the most promising candidates for applications requiring both thermal insulation and load bearing capabilities.The preparation of anti-oxidation coatings on C/CA to address its susceptibility to oxidation is a feasible approach to promote its application in oxidative environments.However,the currently reported coatings on C/CA mainly focus on improving the ablation performance and coating preparation process typically necessitating high-temperature heat treatment.This procedure can increase its thermal conductivity and reduce its thermal insulation ability.In this study,a series of ceramic-resin coatings were fabricated on C/CA through a simple slurry brushing-drying approach at room temperature.The effects of phenolic resin content on the coating structure,residual stress,thermal shock,and oxidation behaviors were investigated.Due to the adhesive properties and curing-induced shrinkage,the PR-7.5 coating(containing 7.5%(in mass)phenolic resin in the slurry)exhibits bonding strength close to fracture strength of the substrate and residual compressive stress of 0.853 GPa,which is beneficial for resisting thermal shock cracking.However,excessive resin content(PR-10.0 containing 10.0%(in mass)phenolic resin in the slurry)induces tensile stress due to uneven curing shrinkage,thereby leading to thermal shock cracking.Meanwhile,oxidation tests reveal significantly reduced weight losses for PR-7.5(17.46%at 800℃/100 min,8.15%at 1000℃/120 min,3.15%at 1200℃/120 min)versus uncoated C/CA’s 44.60%loss at 800℃/20 min.This work provides a brand-new and simple approach to improving the anti-oxidation performance of C/CA and expands its application in mild oxidative environments.
文摘The poor electrical conductivity of metal-organic frameworks(MOFs)limits their electrocatalytic performance in the oxygen evolution reaction(OER).In this study,a Py@Co-MOF composite material based on pyrene(Py)molecules and{[Co2(BINDI)(DMA)_(2)]·DMA}_(n)(Co-MOF,H4BINDI=N,N'-bis(5-isophthalic acid)naphthalenediimide,DMA=N,N-dimethylacetamide)was synthesized via a one-pot method,leveragingπ-πinteractions between pyrene and Co-MOF to modulate electrical conductivity.Results demonstrate that the Py@Co-MOF catalyst exhibited significantly enhanced OER performance compared to pure Co-MOF or pyrene-based electrodes,achieving an overpotential of 246 mV at a current density of 10 mA·cm^(-2) along with excellent stability.Density functional theory(DFT)calculations reveal that the formation of O*in the second step is the rate-determining step(RDS)during the OER process on Co-MOF,with an energy barrier of 0.85 eV due to the weak adsorption affinity of the OH*intermediate for Co sites.CCDC:2419276.
基金Research Start-Up Fund Project of Anhui Polytechnic University(S022023017)University Research Project of Anhui Province(2023AH050937)+1 种基金Anhui Polytechnic University Research Foundation for Introducing Talents(2022YQQ003)Anhui Province Key Laboratory of Intelligent Vehicle Chassis by Wire。
文摘Graphene/copper-based composite heat sinks demonstrate extensive application potential in military equipment thermal management,high-power electronic packaging,new energy vehicles,and 5G communication systems,due to their outstanding properties,including high thermal conductivity,tunable thermal expansion coefficients,excellent mechanical strength,and low density.However,the industrial-scale application of these composites faces critical challenges during the fabrication of components with complex structures,such as inhomogeneous dispersion of graphene within the copper matrix and poor interfacial bonding between the two phases,which substantially undermine the overall performance of graphene/copper-based composites.To address these issues,the preparation methods for graphene/copper-based composite heat sinks were reviewed.For each method,a rigorous analysis was presented to clarify its inherent advantages and unavoidable restrictions.Furthermore,the latest research progress in addressing three core scientific challenges was synthesized,including uniform dispersion of graphene,interfacial optimization mechanisms,and molecular dynamics simulations for elucidating the structure-property relationships.Finally,the future development directions of graphene/copper-based composite heat sinks in engineering applications were prospected.
基金Funded by the National Key R&D Program of China(No.2023YFC3806100)the National Nature Science Foundation of China(No.52278269,52278268)+2 种基金the Tianjin Outstanding Young Scholars Science Fund Project(No.22JCJQJC00020)the Key Project of Tianjin Natural Science Foundation(No.23JCZDJC00430)the Joint Research Center of China and Foreign Countries Special Fund of Tianjin Innovation Platform(No.24PTLYHZ00240)。
文摘We mixed Bacillus subtilis and brewing yeast to prepare composite microbial self-healing materials,and studied the self-healing effect of composite microorganisms in mortar cracks of different widths and cracking ages.The experimental results show that the performance and self-healing effect of composite micro-organisms are significantly better than those of single microorganisms.For cracks with widths of 0.2-0.4 mm,the repair effect of the composite microorganisms at 28 days is 42.7%and 71.2%higher than that of pure Bacillus and pure yeast,respectively.The repairing rate of the area with the widths of the cracks of 0.2-0.4,0.4-0.6,and 0.6-0.8 mm are 100%,77.3%,and 53.4%,respectively.The area repair rates corresponding to cracking ages of 56,90,and 180 days are 73.3%,55.4%,and 30.8%,respectively.
基金supported by the National Natural Science Foundation of China(No.12272240)the Liaoning Revitalization Talents Program,China(No.XLYC2203197)。
文摘Traditional dynamic analysis of mechanical structures,often limited to individual beams or plates,fails to fully capture their dynamic behaviors.In systems where space and mass are constrained,such as the battery support structures in electric aircraft,conventional absorbers and isolators are insufficient for effective vibration control.This study simplifies the battery support structure of electric aircraft as an integrated composite beam consisting of three interconnected beams,and investigated its structural dynamics properties and nonlinear vibration control under thermal conditions caused by battery heat.The nonlinear vibration control is performed using the Nitinol steel wire ropes(Ni Ti-ST),with nonlinear damping properties.The natural frequencies of system are determined using the Rayleigh-Ritz technique.Theoretical results are validated through both Finite Element Method(FEM)and hammer tests.Moreover,the dynamic equations are derived using the Lagrange method and discretized via the Galerkin Truncation Method(GTM).The Harmonic Balance Method(HBM)is used to evaluate the vibration responses of the integrated model,with further verification through the Runge-Kutta Method(RKM).The experiments are conducted to corroborate the theoretical analysis.The results show that the system frequency changes in stages with the increase of the stiffness of the integrated composite beam connection.Especially in the case of varying environments,as the temperature increases,the frequency of system will first increase to a certain maximum value and then gradually decrease.Furthermore,the NiTi-ST effectively reduces vibration in the integrated composite beam,particularly under varying temperatures and external excitations.
基金supported by Fundamental Research Funds for the Central Universities(No.lzujbky-2024-05)Innovation Foundation of Provincial Education Department of Gansu(2024B-005)+2 种基金Scientific Department of Gansu(24CXGA083,24CXGA024,JK2024-28,JK2024-32 and 23CXJA0007)Industrial Support Plan Project of Provincial Education Department of Gansu(2025CYZC-003 and CYZC-2024-10)the Hunan Natural Science Foundation Science and Education Joint Fund Project(2022JJ60109).
文摘Transportation structures such as composite pavements and railway foundations typically consist of multi-layered media designed to withstand high bearing capacity.A theoretical understanding of load transfer mechanisms in these multi-layer composites is essential,as it offers intuitive insights into parametric influences and facilitates enhanced structural performance.This paper employs an improved transfer matrix method to address the limitations of existing theoretical approaches for analyzing multi-layer composite structures.By establishing a twodimensional composite pavement model,it investigates load transfer characteristics and validates the accuracy through finite element simulation.The proposed method offers a straightforward analytical approach for examining internal interactions between structural layers.Case studies indicate that the concrete surface layer is the main load-bearing layer for most vertical normal and shear stresses.The soil base layer reduces the overall mechanical response of the substructure,while horizontal actions increase the risk of interfacial slip and cracking.Structural optimization analysis demonstrates that increasing the thickness of the concrete surface layer,enhancing the thickness and stiffness of the soil base layer,or incorporating gradient layers can significantly mitigate these risks of interfacial slip and cracking.The findings of this study can guide the optimization design,parameter analysis,and damage prevention of multi-layer composite structures.
基金Tianjin Municipal Natural Science Foundation(23JCYBJC00040)National Natural Science Foundation of China(52175369)。
文摘The TiB+TiC dual-reinforced B_(4)C/TC4 composite was in-situ fabricated via incorporating 0.5wt%B_(4)C reinforcement during the laser melting deposition process.Different heat treatments of annealing and solid solution were used to regulate the microstructure,mechanical properties,and corrosion properties of B_(4)C/TC4 composite.Results show that with the increase in temperature from 500℃to 800°C,partial lamellarα-Ti in the as-deposited sample is gradually transformed into equiaxedα-Ti,accompanied by the disappearance of basketweave microstructure.At 1100°C,a small portion of TiC phase suffers fusion.This composite exhibits the optimal combination of strength and plasticity after annealing at 500℃for 4 h followed by furnace cooling,which is attributed to the stress release effect and the refined basketweave microstructure.However,this composite shows a decline in corrosion resistance after various heat treatments due to grain coarsening and micro-galvanic corrosion.
基金supported by the Ministry of Research,Innovation and Digitization,CNCS/CCCDI–UEFISCDI(Romania),Nr.11/2024,within PNCDI IV.The APC received no external funding.
文摘This work addresses optimality aspects related to composite laminates having layers with different orientations.RegressionNeuralNetworks can model the mechanical behavior of these laminates,specifically the stressstrain relationship.If this model has strong generalization ability,it can be coupled with a metaheuristic algorithm–the PSO algorithm used in this article–to address an optimization problem(OP)related to the orientations of composite laminates.To solve OPs,this paper proposes an optimization framework(OFW)that connects the two components,the optimal solution search mechanism and the RNN model.The OFW has two modules:the search mechanism(Adaptive Hybrid Topology PSO)and the Prediction and Computation Module(PCM).The PCM undertakes all the activities concerning the OP at hand:the stress-strain model,constraints checking,and computation of the objective function.Two case studies about the layers’orientations of laminated specimens are conducted to validate the proposed framework.The specimens belong to“Off-axis oriented specimens”and are subjects of two OPs.The algorithms for AHTPSO and for the two PCMs(one for each problem)are proposed and implemented by MATLAB scripts and functions.Simulations are carried out for different initial conditions.The solutions demonstrated that the OFW is effective and has a highly acceptable computational complexity.The limitation of using the OFWis the generalization ability of the RNN model or any other regression models.To harness the RNN model efficiently,it must have a very good generalization power.If this condition ismet,the OFWcan be integrated into any design process to make optimal choices of the layers’orientations.
文摘In this study,using 3,5‑di(3′,5′‑dicarboxylphenyl)‑1H‑1,2,4‑triazole(H4L)as ligands,a gadolinia‑based organic framework complex{[GdNa(L)(H_(2)O)3]·2H_(2)O}_(n)(Gd‑Na‑MOF)was successfully designed and synthesized by hydrothermal method.The structure and properties were systematically characterized and tested by techniques such as single‑crystal X‑ray diffraction,powder X‑ray diffraction,thermogravimetric analysis,infrared spectroscopy,and fluorescence spectroscopy.The results indicate that this complex has a unique 3D structure,excellent thermal stability,and outstanding luminescent performance.Based on its luminescent properties,a polymer‑embedding method was employed to fabricate the Gd‑Na‑MOF into a flexible,washable composite fluorescent film,Gd‑Na‑MOF@PMMA/BMA(PMMA=polymethyl methacrylate,BMA=butyl methacrylate).This fluorescent film exhibited highly sensitive recognition capability for tyramine,with a low detection limit of 1.66μmol·L^(-1).It was used for the detection of tyramine in bananas,with a recovery rate of 96.92%‑100.26%.CCDC:2466949.
基金support provided by the Center for Fabrication and Application of Electronic Materials at Dokuz Eylül University,Türkiye。
文摘Biochar and biochar composites are versatile materials that can be used in many applications.In this study,biochar was prepared from sawdust and combined with the yttrium iron garnet(YIG)nanocrystal to investigate the shielding effectiveness of the composite structure.Firstly,the effect of the pyrolysis temperature on the shielding effectiveness of biochar was investigated.Secondly,biochars combined with YIG nanocrystals with different contents and shielding effectiveness of the composites were investigated.The electromagnetic effectiveness of the samples was investigated within the X band(8-12 GHz).The findings indicate that biochar demonstrates enhanced absorption properties with elevated pyrolysis temperatures.Biochars demonstrated an approximate 40 d B shielding effectiveness,while YIG exhibited approximately 7 d B,corresponding to absorption at 8 GHz.However,the combination of biochar and YIG exhibited exceptional absorption,reaching 67.12 d B at 8 GHz.