The morphology and structure of melt spinning Ni-33.6at% Al doped with B and RE were investigated.The results show that the alloy consists of L10 martensitic grains and L12 Ni3Al at the grain boundaries when it contai...The morphology and structure of melt spinning Ni-33.6at% Al doped with B and RE were investigated.The results show that the alloy consists of L10 martensitic grains and L12 Ni3Al at the grain boundaries when it contains no B and RE.The addition of 0.11-0.31wt% B can suppress the martensitic transformation and Ni3Al separation at the boundaries,and a supersaturated B2 single phase NiAl is obtained.The addition of 0.05wt% RE can eliminate Ni3Al precipitated at the boundaries and get complete martensite,but 0.2-0.8wt% RE addition can suppress the martensitic transformation, and supersaturated B2 single phase NiAl is obtained.The formation mechanism of supersaturated B2 single phase NiAl has been analyzed.展开更多
文摘The morphology and structure of melt spinning Ni-33.6at% Al doped with B and RE were investigated.The results show that the alloy consists of L10 martensitic grains and L12 Ni3Al at the grain boundaries when it contains no B and RE.The addition of 0.11-0.31wt% B can suppress the martensitic transformation and Ni3Al separation at the boundaries,and a supersaturated B2 single phase NiAl is obtained.The addition of 0.05wt% RE can eliminate Ni3Al precipitated at the boundaries and get complete martensite,but 0.2-0.8wt% RE addition can suppress the martensitic transformation, and supersaturated B2 single phase NiAl is obtained.The formation mechanism of supersaturated B2 single phase NiAl has been analyzed.