Silicon-carbide-fiber-reinforced silicon-carbide-ceramic-based matrix(SiC/SiC)composites possess excellent properties such as low density,high strength and high temperature resistance,showing a potential application f...Silicon-carbide-fiber-reinforced silicon-carbide-ceramic-based matrix(SiC/SiC)composites possess excellent properties such as low density,high strength and high temperature resistance,showing a potential application for structural components in the aerospace field,but their oxidation behavior remains largely unknown.In this study,Yb_(2)Si_(2)O_(7)modified SiC/SiC(SiC/SiC-Yb_(2)Si_(2)O_(7))mini-composites were prepared by introducing Yb_(2)Si_(2)O_(7)as anti-oxidation phase into SiC fiber bundles via Sol-Gel and depositing SiC matrix by chemical vapor deposition(CVD).Influence of Yb_(2)Si_(2)O_(7)on microstructure,mechanical property and oxidation behavior of SiC/SiC mini-composites was investigated.The results showed that after oxidation in air at 1200 and 1400℃for 50 h,the tensile strength retentions of SiC/SiC mini-composites were 77%and 69%,respectively,and the fracture morphology exhibited flat.The Yb_(2)Si_(2)O_(7)introduced by Sol-Gel partially distributed in layers,contributing to the toughening of the material.On the fracture surface,there was interlayer debonding,which extended energy dissipation mechanism of SiC/SiC mini-composites.Tensile strength of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites at room temperature was 484 MPa.After oxidation in air at 1200 and 1400℃for 50 h,the tensile strengths decreased to 425 and 374 MPa,resulting in retention rates of 88%and 77%,respectively.It displayed typical non-brittle fracture characteristics.The interface oxygen content of SiC/SiC mini-composites at the fracture surface was higher than that of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites,indicating that introduction of Yb_(2)Si_(2)O_(7)could alleviate oxygen diffusion towards the interface,and therefore improve the oxidation resistance of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites.展开更多
The effect of the pyrolytic carbon(PyC)interface thickness on the heat-stability of CansasⅡSiC_(f)/SiC composites under Ar up to 1500℃was studied in detail.After the heat treatment at 1500℃for 50 h,the interface bo...The effect of the pyrolytic carbon(PyC)interface thickness on the heat-stability of CansasⅡSiC_(f)/SiC composites under Ar up to 1500℃was studied in detail.After the heat treatment at 1500℃for 50 h,the interface bonding strength of the thin interface(about 200 nm)decreases from 74.4 to 20.1 MPa(73.0%),while that of the thick interface(about 2μm)declines from 7.3 to 3.2 MPa(52.7%).At the same time,the decline fraction of strength of the composites with the thin interface is 12.1%,less than that with the thick interface(42.0%).The fiber strength also decreases after heat treatment,which may be due to the significant growth ofβ-SiC grains and critical defects.The different heat-stability of the interface with the thin and thick thickness might be related to the inconsistency of the degree of the graphitization of PyC.Compared with the composites with the thick interface,the composites with the thin interface remained higher tensile strength after heat treatment due to the better interface bonding strength.The interface with strong bonding strength could protect the fiber by postponing the decomposition of amorphous phases SiC_(x)O_(y) and hindering the generation of fiber defects.展开更多
基金National Natural Science Foundation of China(52222202)National Key R&D Program of China(2022YFB3707700)+2 种基金Project of Shanghai Science and Technology Innovation Action Plan(21511104800)Shanghai Pilot Program for Basic Research-Chinese Academy of Science,Shanghai Branch(JCYJ-SHFY-2021-001)Science Center for Gas Turbine Project(P2022-B-Ⅳ-001-001)。
文摘Silicon-carbide-fiber-reinforced silicon-carbide-ceramic-based matrix(SiC/SiC)composites possess excellent properties such as low density,high strength and high temperature resistance,showing a potential application for structural components in the aerospace field,but their oxidation behavior remains largely unknown.In this study,Yb_(2)Si_(2)O_(7)modified SiC/SiC(SiC/SiC-Yb_(2)Si_(2)O_(7))mini-composites were prepared by introducing Yb_(2)Si_(2)O_(7)as anti-oxidation phase into SiC fiber bundles via Sol-Gel and depositing SiC matrix by chemical vapor deposition(CVD).Influence of Yb_(2)Si_(2)O_(7)on microstructure,mechanical property and oxidation behavior of SiC/SiC mini-composites was investigated.The results showed that after oxidation in air at 1200 and 1400℃for 50 h,the tensile strength retentions of SiC/SiC mini-composites were 77%and 69%,respectively,and the fracture morphology exhibited flat.The Yb_(2)Si_(2)O_(7)introduced by Sol-Gel partially distributed in layers,contributing to the toughening of the material.On the fracture surface,there was interlayer debonding,which extended energy dissipation mechanism of SiC/SiC mini-composites.Tensile strength of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites at room temperature was 484 MPa.After oxidation in air at 1200 and 1400℃for 50 h,the tensile strengths decreased to 425 and 374 MPa,resulting in retention rates of 88%and 77%,respectively.It displayed typical non-brittle fracture characteristics.The interface oxygen content of SiC/SiC mini-composites at the fracture surface was higher than that of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites,indicating that introduction of Yb_(2)Si_(2)O_(7)could alleviate oxygen diffusion towards the interface,and therefore improve the oxidation resistance of SiC/SiC-Yb_(2)Si_(2)O_(7)mini-composites.
基金Funded by the National Science and Technology Major Project(No.2017-IV-0005-0042)the China Postdoctoral Science Foundation(No.2021M691566)。
文摘The effect of the pyrolytic carbon(PyC)interface thickness on the heat-stability of CansasⅡSiC_(f)/SiC composites under Ar up to 1500℃was studied in detail.After the heat treatment at 1500℃for 50 h,the interface bonding strength of the thin interface(about 200 nm)decreases from 74.4 to 20.1 MPa(73.0%),while that of the thick interface(about 2μm)declines from 7.3 to 3.2 MPa(52.7%).At the same time,the decline fraction of strength of the composites with the thin interface is 12.1%,less than that with the thick interface(42.0%).The fiber strength also decreases after heat treatment,which may be due to the significant growth ofβ-SiC grains and critical defects.The different heat-stability of the interface with the thin and thick thickness might be related to the inconsistency of the degree of the graphitization of PyC.Compared with the composites with the thick interface,the composites with the thin interface remained higher tensile strength after heat treatment due to the better interface bonding strength.The interface with strong bonding strength could protect the fiber by postponing the decomposition of amorphous phases SiC_(x)O_(y) and hindering the generation of fiber defects.