The effect of different intermediate annealing heat treatments on the surface microstructures and anodic oxide film structures of rolled Al-5.6Mg sheets was studied.The results show that when the continuous annealing ...The effect of different intermediate annealing heat treatments on the surface microstructures and anodic oxide film structures of rolled Al-5.6Mg sheets was studied.The results show that when the continuous annealing is used to control microstructures of the sheets instead of the static state annealing in the intermediate annealing process,the surface grain size of the sheets can be reduced by about 65.7%,and the size of the Mg precipitation phase(Mg_(2)Al_(3))can be reduced by about 67%.Under the combined influence of grain size,precipitation phase,and texture,the highest glossiness can be obtained,which is attributed to continuous intermediate annealing and stabilization annealing at low temperature.The uniform grain and precipitation structures is beneficial to reducing the inhomogeneous dissolution of the oxide film and to obtain the anodic oxide film with uniform thickness and high glossiness.展开更多
Super-fine electrohydrodynamic inkjet(SIJ)printing of perovskite nanocrystal(PNC)colloid ink exhibits significant potential in the fabrication of high-resolution color conversion microstructures arrays for fullcolor m...Super-fine electrohydrodynamic inkjet(SIJ)printing of perovskite nanocrystal(PNC)colloid ink exhibits significant potential in the fabrication of high-resolution color conversion microstructures arrays for fullcolor micro-LED displays.However,the impact of solvent on both the printing process and the morphology of SIJ-printed PNC color conversion microstructures remains underexplored.In this study,we prepared samples of CsPbBr3PNC colloid inks in various solvents and investigated the solvent's impact on SIJ printed PNC microstructures.Our findings reveal that the boiling point of the solvent is crucial to the SIJ printing process of PNC colloid inks.Only does the boiling point of the solvent fall in the optimal range,the regular positioned,micron-scaled,conical PNC microstructures can be successfully printed.Below this optimal range,the ink is unable to be ejected from the nozzle;while above this range,irregular positioned microstructures with nanoscale height and coffee-ring-like morphology are produced.Based on these observations,high-resolution color conversion PNC microstructures were effectively prepared using SIJ printing of PNC colloid ink dispersed in dimethylbenzene solvent.展开更多
The combination of dual-main-phase(DMP)(Nd,Ce)-Fe-B magnets and grain boundary diffusion process(GBDP)is currently a research topic for obtaining high-cost performance materials in rare earth permanent magnet fields.T...The combination of dual-main-phase(DMP)(Nd,Ce)-Fe-B magnets and grain boundary diffusion process(GBDP)is currently a research topic for obtaining high-cost performance materials in rare earth permanent magnet fields.The novel structural features of GBDP(Nd,Ce)-Fe-B magnets give a version of different domain reversal processes from those of non-diffused magnets.In this work,the in-situ magnetic domain evolution of the DMP magnets was observed at elevated temperatures,and the temperature demagnetization and coercivity mechanism of the GBDP dual-main-phase(Nd,Ce)-Fe-B magnets are discussed.The results show that the shell composition of different types of grains in DMP magnets is similar,while the magnetic microstructure results indicate the Ce-rich grains tend to demagnetize first.Dy-rich shell with a high anisotropic field caused by GBDP leads to an increase in the nucleation field,which enhances the coercivity.It is found that much more grains exhibit single domain characteristics in the remanent state for GBDP dual-main-phase(Nd,Ce)-Fe-B magnets.In addition,the grains that undergo demagnetization first are Ce-rich or Nd-rich grains,which is different from that of non-diffused magnets.These results were not found in previous studies but can be intuitively characterized from the perspective of magnetic domains in this work,providing a new perspective and understanding of the performance improvement of magnetic materials.展开更多
Refractory high/medium-entropy alloys(RH/MEAs)are known for their outstanding performance at el-evated temperatures;however,they usually exhibit poor room-temperature plasticity,which can be at-tributed to the non-uni...Refractory high/medium-entropy alloys(RH/MEAs)are known for their outstanding performance at el-evated temperatures;however,they usually exhibit poor room-temperature plasticity,which can be at-tributed to the non-uniform deformation that occurs at room temperature.Once cracks nucleate,they will rapidly propagate into vertical splitting cracks.Here,we introduce multiple phases including FCC and HCP phases into the NbMoTa RMEA via appropriate addition of carbon.The results show that multiple-phase synergy effectively suppresses non-uniform deformation,thereby delaying the onset of vertical splitting cracks.An optimal combination of compressive strength-plasticity is achieved by the(NbMoTa)_(92.5)C_(7.5) alloy.The significant improvement in room-temperature mechanical properties can be attributed to its hierarchical microstructure:in the mesoscale,the BCC matrix is divided by eutectic structures;while at the microscale,the BCC matrix is further refined by abundant lath-like FCC precipitates.The FCC precip-itates contain high-density stacking faults,acting as a dislocation source under compressive loading.The HCP phase in the eutectic microstructures,in turn,acts as a strong barrier to dislocation movement and simultaneously increases the dislocation storage capacity.These findings open a new route to tailor the microstructure and mechanical properties of RH/MEAs.展开更多
Ferroelastic rare earth tantalates(RETaO_(4))are widely researched as the next-generation thermal barrier coatings(TBCs),and RETaO_(4)powders are hugely significant for synthesizing their coatings.The current research...Ferroelastic rare earth tantalates(RETaO_(4))are widely researched as the next-generation thermal barrier coatings(TBCs),and RETaO_(4)powders are hugely significant for synthesizing their coatings.The current research used chemical co-precipitation within an automated experimental device to synthesize RETaO_(4)(RE=Nd,Sm,Gd,Ho,Er)powders.The device automatically monitored and controlled the solutions'pH,improving the chemical co-precipitation efficiency.The crystal structure and microstructure of the RETaO_(4)powders can be controlled by changing the annealing temperature,and the materials undergo an m'-m phase transition.The m'-RETaO_(4)powders exhibit nano-size grains,while m-RETaO_(4)powders evince micron-size grains,altered by the annealing temperatures.A simultaneous thermal analysis es-timates the reversive ferroelastic tetragonal-monoclinic phase transition temperatures.Overall,this research focuses on the synthesis,crystal structures,microstructures,and phase transition of the fabricated RETaO_(4)powders.展开更多
Microscale metallic structures enhanced by additive manufacturing technology have attracted extensive attention especially in microelectronics and electromechanical devices.Meniscus-confined electrodeposition(MCED)adv...Microscale metallic structures enhanced by additive manufacturing technology have attracted extensive attention especially in microelectronics and electromechanical devices.Meniscus-confined electrodeposition(MCED)advances microscale 3D metal printing,enabling simpler fabrication of superior metallic microstructures in air without complex equipment or post-processing.However,accurately predicting growth rates with current MCED techniques remain challenging,which is essential for precise structure fabrication and preventing nozzle clogging.In this work,we present a novel approach to electrochemical 3D printing that utilizes a self-adjusting,voxelated method for fabricating metallic microstructures.Diverging from conventional voxelated printing which focuses on monitoring voxel thickness for structure control,this technique adopts a holistic strategy.It ensures each voxel’s position is in alignment with the final structure by synchronizing the micropipette’s trajectory during deposition with the intended design,thus facilitating self-regulation of voxel position and reducing errors associated with environmental fluctuations in deposition parameters.The method’s ability to print micropillars with various tilt angles,high density,and helical arrays demonstrates its refined control over the deposition process.Transmission electron microscopy analysis reveals that the deposited structures,which are fabricated through layer-by-layer(voxel)printing,contain nanotwins that are widely known to enhance the material’s mechanical and electrical properties.Correspondingly,in situ scanning electron microscopy(SEM)microcompression tests confirm this enhancement,showing these structures exhibit a compressive yield strength exceeding 1 GPa.The indentation tests provided an average hardness of 3.71 GPa,which is the highest value reported in previous work using MCED.The resistivity measured by the four-point probe method was(1.95±0.01)×10^(−7)Ω·m,nearly 11 times that of bulk copper.These findings demonstrate the considerable advantage of this technique in fabricating complex metallic microstructures with enhanced mechanical properties,making it suitable for advanced applications in microsensors,microelectronics,and micro-electromechanical systems.展开更多
The Irtysh tectonic belt lies on the southern margin of the Chinese Altai Orogen. Several secondary shear zones with NW-SE strikes have developed in this tectonic belt, and the deformation processes are of great signi...The Irtysh tectonic belt lies on the southern margin of the Chinese Altai Orogen. Several secondary shear zones with NW-SE strikes have developed in this tectonic belt, and the deformation processes are of great significance to understanding the tectonic regime of the Altai Orogen in the Late Paleozoic. The Tuerhongshate ductile shear zone is located in the eastern Irtysh tectonic belt with obvious deformed structures. The felsic rocks are strongly mylonitized, exhibiting S-C fabrics, asymmetric rotational porphyroclasts, and bookshelf structures of the plagioclases, indicating a sinistral shear sense. The deformation mechanisms, lattice preferred orientations (LPOs) of quartz, and opening angles of quartz c-axis suggest that the deformation temperatures range from 400 to 500 ℃, consistent with higher-greenschist to lower-amphibolite facies conditions. The calculated kinematic vorticity values (W_(k)) of the studied samples range from 0.53 to 0.89 and indicate general shear to simple shear, based on rotational rigid porphyroclast method and oblique grain-shaped/quartz c-axis fabric method. The U-Pb ages of magmatic zircons in felsic mylonites indicate that the sinistral shear occurred after 296.7 ± 3.0 Ma (Early Permian) in the Tuerhongshate shear zone and persisted for approximately 13 Ma. Combined with the tectonic setting and the observed sinistral strike-slip shear indicators in the mylonite zone, these features demonstrate that the Irtysh tectonic belt was in a post-orogenic and strike-slip environment following the closure of the Irtysh Ocean.展开更多
The microstructures,mechanical properties,and fracture behaviors of an Al-5.9Zn-1.9Mg alloy subjected to thermomechanical treatment across different pre-rolling temperatures have been exhaustively investigated in pres...The microstructures,mechanical properties,and fracture behaviors of an Al-5.9Zn-1.9Mg alloy subjected to thermomechanical treatment across different pre-rolling temperatures have been exhaustively investigated in present work.The pre-deformation temperature exerts a modest influence on grain morphology,while it profoundly impacts the dislocation configurations and precipitation behaviors.Elevating the rolling temperature from ambient to 170℃results in a reduction in dislocation density within grains accompanied by a notable enhancement in their distributional uniformity.While advancing the temperature to 320℃prompts the premature formation of precipitates during deformation,which diminishes the precipitation during the subsequent ageing.Tensile results reveal that the thermomechanical treatment incorporating pre-rolling at 170℃confers a substantial strengthening effect on the alloy on the basis of both grain boundary strengthening and dislocation strengthening stemmed from pre-deformation along with the precipitation strengthening generated by ageing.Furthermore,the microstructure exhibits a relatively scarce presence of inhomogeneous features such as dislocation pile-ups and micro shear bands,contributing favorably to enhance the ductility of the alloy that presents the mixture of cleavage fracture and dimple-induced failure.展开更多
Optical singularities are topological defects of electromagnetic fields;they include phase singularity in scalar fields,polarization singularity in vector fields,and three-dimensional(3D)singularities such as optical ...Optical singularities are topological defects of electromagnetic fields;they include phase singularity in scalar fields,polarization singularity in vector fields,and three-dimensional(3D)singularities such as optical skyrmions.The exploitation of photonic microstructures to generate and manipulate optical singularities has attracted wide research interest in recent years,with many photonic microstructures having been devised to this end.Accompanying these designs,scattered phenomenological theories have been proposed to expound the working mechanisms behind individual designs.In this work,instead of focusing on a specific type of microstructure,we concentrate on the most common geometric features of these microstructures—namely,symmetries—and revisit the process of generating optical singularities in microstructures from a symmetry viewpoint.By systematically employing the projection operator technique in group theory,we develop a widely applicable theoretical scheme to explore optical singularities in microstructures with rosette(i.e.,rotational and reflection)symmetries.Our scheme agrees well with previously reported works and further reveals that the eigenmodes of a symmetric microstructure can support multiplexed phase singularities in different components,such as out-of-plane,radial,azimuthal,and left-and right-handed circular components.Based on these phase singularities,more complicated optical singularities may be synthesized,including C points,V points,L lines,Néel-and bubble-type optical skyrmions,and optical lattices,to name a few.We demonstrate that the topological invariants associated with optical singularities are protected by the symmetries of the microstructure.Lastly,based on symmetry arguments,we formulate a so-called symmetry matching condition to clarify the excitation of a specific type of optical singularity.Our work establishes a unified theoretical framework to explore optical singularities in photonic microstructures with symmetries,shedding light on the symmetry origin of multidimensional and multiplexed optical singularities and providing a symmetry perspective for exploring many singularity-related effects in optics and photonics.展开更多
It is one of the big bottleneck problems for graphene to be uniformly distributed in ceramic matrix composites. A two-step approach was applied to prepare Graphene Nanoplatelets/Yt tria-Stabilized Zirconia(GNPs/YSZ) c...It is one of the big bottleneck problems for graphene to be uniformly distributed in ceramic matrix composites. A two-step approach was applied to prepare Graphene Nanoplatelets/Yt tria-Stabilized Zirconia(GNPs/YSZ) composites. Initially, GNPs were combined with YSZ through nanoparticle regranulation technology to obtain uniformly dispersed powders. Subsequently, the prepared powders were sintered by Spark Plasma Sintering(SPS). Systematic investigation was carried out to examine how GNPs regulate the phase, microstructures, and nanomechanical properties of GNPs/YSZ composite ceramics with different sintering temperatures.Results show that the GNPs can inhibit the coalescence of adjacent grains in YSZ ceramics. Herein,we propose that the intensity ratio of 2D peak to G peak of GNPs in Raman spectrum serves as a key indicator to assess the nanomechanical properties of GNPs/YSZ composites. When the intensity ratio of 2D peak to G peak is 0.5–0.6, the GNPs/YSZ composites obtained in the sintering temperature range of 1 200–1 250.C exhibit excellent nanomechanical properties such as hardness,elastic modulus, wear and creep resistance.展开更多
F-actin microstructures dominate cellular viscoelasticity and have been used to identify the migration and malignance of living cancer cells.Diabetic cancer patients suffer from increased metastasis and tumor recurren...F-actin microstructures dominate cellular viscoelasticity and have been used to identify the migration and malignance of living cancer cells.Diabetic cancer patients suffer from increased metastasis and tumor recurrence.However,the long-term evolution and correlation of F-actin microstructures and viscoelasticity distribution are still poorly understood in living cancer cells under varying glucose environment.Herein,by using atomic force microscopy with amplitude modulation-frequency modulation and nanoindentation mode,we characterized the hierarchical F-actin microstructures and the multi-passage viscoelasticity evolution in living Huh-7 cancer cells transferred from high to low glucose level.The highly oriented stress fibers connected by thinner fiber networks were observed in high glucose environment.The circumferential actin networks composed by straight segment-like fibers and the randomly distributed actin fragments connected by ultrathin crosslinking fibers were observed in low glucose environment.The viscoelasticity within the nucleus and the cytoplasm of living Huh-7 cancer cells showed longterm fluctuations over tens of passages after switching glucose environments.The viscoelasticity of cytoplasm was more responsive to the change of glucose environments than nucleus,which was due to the reorganization of F-actin microstructures.Our work provides the microstructural and nanomechanical understanding on the migration and proliferation of living cancer cells under varying glucose environment.展开更多
Notable advancements have been made in the additive manufacturing(AM)of aerospace materials,driven by the needs for integrated components with intricate geometries and small-lot production of high-value components.Nic...Notable advancements have been made in the additive manufacturing(AM)of aerospace materials,driven by the needs for integrated components with intricate geometries and small-lot production of high-value components.Nickel-based superalloys,pivotal materials for high-temperature bearing components in aeroengines,present significant challenges in the fabrication of complex parts due to their great hardness.Huge attention and rapid progress have been garnered in AM processing of nicklebased superalloys,largely owing to its distinct benefits in the freedom of fabrication and reduced manufacturing lifecycle.Despite extensive research into AM in nickel-based superalloys,the corresponding results and conclusions are scattered attributed to the variety of nickel-based superalloys and complex AM processing parameters.Therefore,there is still a pressing need for a comprehensive and deep understanding of the relationship between the AM processing and microstructures and mechanical performance of nickel-based superalloys.This review introduces the processing characteristics of four primary AM technologies utilized for superalloys and summarizes the microstructures and mechanical properties prior to and post-heat treatments.Additionally,this review presents innovative superalloys specifically accommodated to AM processing and offers insights into the material development and performance improvement,aiming to provide a valuable assessment on AM processing of nickel-based superalloys and an effective guidance for the future research.展开更多
The fracture behavior at high temperatures of the Ti−22Al−26Nb alloy,which features duplex lamellar,bimodal,and Widmanstätten structures,was studied.Samples of the alloy were prepared through compression deformat...The fracture behavior at high temperatures of the Ti−22Al−26Nb alloy,which features duplex lamellar,bimodal,and Widmanstätten structures,was studied.Samples of the alloy were prepared through compression deformation in the trans-phase region followed by subsequent heat treatment.The results indicate that at 650℃,the fracture toughness of the Ti−22Al−26Nb alloy is increased by 41.7%compared to that with original microstructures.The content of the B2 phase significantly influences the inherent fracture toughness of the material,while the morphology and distribution of the precipitated phases primarily affect the tortuosity of the crack propagation path.Among the microstructural features,the morphology and geometric orientation of the lamellae most significantly impact the crack path;consequently,the Widmanstätten structure exhibits the most tortuous fracture path.Additionally,a predictive model for fracture toughness is developed,which effectively predicts the fracture toughness of Ti−22Al−26Nb alloys with various microstructures at 650℃.展开更多
The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal ho...The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal hot extrusion parameters are determined as ingot initial temperature of 380°C and extrusion speed of 3 mm/s.The hot-extruded aluminum alloy after T6 heat treatment presents superior mechanical properties with yield strength of 519.6 MPa,ultimate tensile strength of 582.1 MPa,and elongation of 11.0%.Compared with the properties of gravity-cast and liquid-forged alloys,the yield strength of hot-extruded alloy increases by 30.8%and 4.9%,and the ultimate tensile strength improves by 43.5%and 10.2%,respectively.The significant improvement in tensile strength of the hot-extruded alloys is attributed to the elimination of casting defects and the refinement of matrix grain and eutectic phases.In addition,the hot-extruded alloy demonstrates superior plasticity compared with the liquid-forged alloy.This is because severe plastic deformation occurs during hot extrusion,which effectively breaks and disperses the eutectic phases,facilitating the dissolution and precipitation of the second phases and inhibiting the microcrack initiation.展开更多
A356-based metal matrix composites with 10% SiC particles of 10 rtm were fabricated by stir casting and direct squeeze casting process under applied pressures of 0.1 （gravity）, 25, 50 and 75 MPa. The microstructures...A356-based metal matrix composites with 10% SiC particles of 10 rtm were fabricated by stir casting and direct squeeze casting process under applied pressures of 0.1 （gravity）, 25, 50 and 75 MPa. The microstructures and mechanical properties of the as-cast and T6 heat-treated castings were investigated. The results show that as the applied pressures increase, the casting defects as particle-porosity clusters reduce and the incorporation between the particles and matrix can be improved. The tensile strength, hardness, and coefficients of thermal expansion （CTE） increase with the increase of the pressures. Compared with the as-cast composite castings, the tensile strength and hardness of the heat-treated casting are improved whereas CTEs tend to decrease in T6-treated condition. For the gravity cast composites, there are some particle-porosity clusters on the fracture surface, and the clusters are hardly detected on the fracture surface of the samples solidified at the external pressures. Different fracture behaviors are found between the composites solidified at the gravity and imposed pressures.展开更多
The hot compression curves and deformed microstructures were investigated under various hot deformation conditions in three states:hot isostatic pressing(HIP,A1),HIP+hot extrusion at 1100℃(A2),and HIP+hot extrusion a...The hot compression curves and deformed microstructures were investigated under various hot deformation conditions in three states:hot isostatic pressing(HIP,A1),HIP+hot extrusion at 1100℃(A2),and HIP+hot extrusion at 1150℃(A3).The results show that A2 sample,extruded at 1100℃ with uniform γ+γ′duplex microstructures,demonstrates excellent hot deformation behavior at both 1050 and 1100℃.The true stress-true strain curves of A2 sample maintain a hardening-softening equilibrium over a larger strain range,with post-deformation average grain size of 5μm.The as-HIPed A1 sample and 1150℃ extruded A3 sample exhibit a softening region in deformation curves at 1050℃,and the grain microstructures reflect an incomplete recrystallized state,i.e.combination of fine recrystallized grains and initial larger grains,characterized by a necklace-like microstructure.The predominant recrystallization mechanism for these samples is strain-induced boundary migration.At 1150℃ with a strain rate of 0.001 s^(-1),the influence of the initial microstructure on hot deformation behavior and resultant microstructure is relatively less pronounced,and postdeformation microstructures are fully recrystallized grains.Fine-grained microstructures are conducive to maximizing the hot deformation potential of alloy.By judiciously adjusting deformation regimes,a fine and uniform deformed microstructure can be obtained.展开更多
Microstructures and element distributions of the as-cast, hot-rolled and cold-rolled Cu-Mg-Te-Y alloys were studied. Effects of rolling process and annealing temperature on the properties of the Cu-Mg-Te-Y alloys were...Microstructures and element distributions of the as-cast, hot-rolled and cold-rolled Cu-Mg-Te-Y alloys were studied. Effects of rolling process and annealing temperature on the properties of the Cu-Mg-Te-Y alloys were correspondingly investigated. The results indicate that the Mg element is homogeneously distributed in the matrix and the fragmentized Cu2Te phase is dispersed in the matrix after hot rolling. Then, the Cu2Te phase is further stretched to strip shape after the cold rolling process. The microstructures of the cold-rolled alloy keep unchanged for the sample annealed below 390 ℃ for 1 h. However, after annealing at 550 ℃ for 1 h, the copper alloy with fibrous microstructures formed during the cold rolling process recrystallizes, leading to an obvious drop of hardening effect and an increase of electrical conductivity. The Cu-Mg-Te-Y alloy with better comprehensive properties is obtained by annealing at 360-390 ℃.展开更多
The microstructures and mechanical properties of Mg-6Zn-1Mn-4Sn-1.5Nd alloy subjected to extrusion and T5 treatment were investigated using optical microscopy（OM）, X-ray diffractometer（XRD）, scanning electron micr...The microstructures and mechanical properties of Mg-6Zn-1Mn-4Sn-1.5Nd alloy subjected to extrusion and T5 treatment were investigated using optical microscopy（OM）, X-ray diffractometer（XRD）, scanning electron microscopy（SEM）, electron back scattered diffraction（EBSD）, transmission electron microscopy（TEM）, hardness tests and uniaxial tensile tests. The results showed that the as-cast alloy consisted of α（Mg）, Mn, Mg7Zn3, Mg2 Sn and Mg Sn Nd phases. Dynamic recrystallization has completed during the extrusion process and the average grain size was 7.2 μm. After T5 treatment, the strength increased obviously, the yield strength and ultimate tensile strength of as-extruded alloy were increased by 94 and 34 MPa, respectively. Microstructure characterization revealed that the improvement of strength was determined by the high number density of β′1 rods.展开更多
In order to reveal the differences caused by forging and rolling process for titanium ingots, hot compression behavior, mechanical properties and the microstructures of forged billets and rolled ones were investigated...In order to reveal the differences caused by forging and rolling process for titanium ingots, hot compression behavior, mechanical properties and the microstructures of forged billets and rolled ones were investigated in detail using Gleeble-1500 thermal mechanical simulator, universal testing machine and optical microscope （OM）. The compression deformation experimental data of commercially pure titanium （CP-Ti） were mapped to be a T vs lg diagram in which data fall into three distinct regions, i.e., three-stage work hardening, two-stage work hardening and flow softening, which can be separated by border lines at 17.5 and 15.4 for lg Z, where Z represents the Zener-Hollomon parameter. The deformation twin is found to have higher Z-value corresponding to the work hardening region. The differences in microstructures and mechanical properties for two kinds of billets indicate that forged billet consists of deformation twins and some twin intersections, and many twins cross the grain boundaries. However, nearly no twins can be seen in the microstructure of billet formed by rolling under optical microscope （OM）, but there are equiaxed and platelike grains. Tensile tests and Vickers hardness test indicate that yield strength, tensile strength and microhardness of the samples after forging are higher than those after rolling.展开更多
Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners a...Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.展开更多
文摘The effect of different intermediate annealing heat treatments on the surface microstructures and anodic oxide film structures of rolled Al-5.6Mg sheets was studied.The results show that when the continuous annealing is used to control microstructures of the sheets instead of the static state annealing in the intermediate annealing process,the surface grain size of the sheets can be reduced by about 65.7%,and the size of the Mg precipitation phase(Mg_(2)Al_(3))can be reduced by about 67%.Under the combined influence of grain size,precipitation phase,and texture,the highest glossiness can be obtained,which is attributed to continuous intermediate annealing and stabilization annealing at low temperature.The uniform grain and precipitation structures is beneficial to reducing the inhomogeneous dissolution of the oxide film and to obtain the anodic oxide film with uniform thickness and high glossiness.
基金supported by the National Natural Science Foundation of China(No.62374142)Fundamental Research Funds for the Central Universities(Nos.20720220085 and 20720240064)+2 种基金External Cooperation Program of Fujian(No.2022I0004)Major Science and Technology Project of Xiamen in China(No.3502Z20191015)Xiamen Natural Science Foundation Youth Project(No.3502Z202471002)。
文摘Super-fine electrohydrodynamic inkjet(SIJ)printing of perovskite nanocrystal(PNC)colloid ink exhibits significant potential in the fabrication of high-resolution color conversion microstructures arrays for fullcolor micro-LED displays.However,the impact of solvent on both the printing process and the morphology of SIJ-printed PNC color conversion microstructures remains underexplored.In this study,we prepared samples of CsPbBr3PNC colloid inks in various solvents and investigated the solvent's impact on SIJ printed PNC microstructures.Our findings reveal that the boiling point of the solvent is crucial to the SIJ printing process of PNC colloid inks.Only does the boiling point of the solvent fall in the optimal range,the regular positioned,micron-scaled,conical PNC microstructures can be successfully printed.Below this optimal range,the ink is unable to be ejected from the nozzle;while above this range,irregular positioned microstructures with nanoscale height and coffee-ring-like morphology are produced.Based on these observations,high-resolution color conversion PNC microstructures were effectively prepared using SIJ printing of PNC colloid ink dispersed in dimethylbenzene solvent.
基金supported by the National Key Research and Development Program of China(Nos.2021YFB3503003,2021YFB3503100,and 2022YFB3505401).
文摘The combination of dual-main-phase(DMP)(Nd,Ce)-Fe-B magnets and grain boundary diffusion process(GBDP)is currently a research topic for obtaining high-cost performance materials in rare earth permanent magnet fields.The novel structural features of GBDP(Nd,Ce)-Fe-B magnets give a version of different domain reversal processes from those of non-diffused magnets.In this work,the in-situ magnetic domain evolution of the DMP magnets was observed at elevated temperatures,and the temperature demagnetization and coercivity mechanism of the GBDP dual-main-phase(Nd,Ce)-Fe-B magnets are discussed.The results show that the shell composition of different types of grains in DMP magnets is similar,while the magnetic microstructure results indicate the Ce-rich grains tend to demagnetize first.Dy-rich shell with a high anisotropic field caused by GBDP leads to an increase in the nucleation field,which enhances the coercivity.It is found that much more grains exhibit single domain characteristics in the remanent state for GBDP dual-main-phase(Nd,Ce)-Fe-B magnets.In addition,the grains that undergo demagnetization first are Ce-rich or Nd-rich grains,which is different from that of non-diffused magnets.These results were not found in previous studies but can be intuitively characterized from the perspective of magnetic domains in this work,providing a new perspective and understanding of the performance improvement of magnetic materials.
基金financial support from the Na-tional Natural Science Foundation of China(No.52231006)National Key Research and Development Program of China(No.2017YFB0702003)the National Natural Science Foundation of China(No.51871217).
文摘Refractory high/medium-entropy alloys(RH/MEAs)are known for their outstanding performance at el-evated temperatures;however,they usually exhibit poor room-temperature plasticity,which can be at-tributed to the non-uniform deformation that occurs at room temperature.Once cracks nucleate,they will rapidly propagate into vertical splitting cracks.Here,we introduce multiple phases including FCC and HCP phases into the NbMoTa RMEA via appropriate addition of carbon.The results show that multiple-phase synergy effectively suppresses non-uniform deformation,thereby delaying the onset of vertical splitting cracks.An optimal combination of compressive strength-plasticity is achieved by the(NbMoTa)_(92.5)C_(7.5) alloy.The significant improvement in room-temperature mechanical properties can be attributed to its hierarchical microstructure:in the mesoscale,the BCC matrix is divided by eutectic structures;while at the microscale,the BCC matrix is further refined by abundant lath-like FCC precipitates.The FCC precip-itates contain high-density stacking faults,acting as a dislocation source under compressive loading.The HCP phase in the eutectic microstructures,in turn,acts as a strong barrier to dislocation movement and simultaneously increases the dislocation storage capacity.These findings open a new route to tailor the microstructure and mechanical properties of RH/MEAs.
基金the Rare and Precious Metals Material Genetic Engineering Project of Yunnan Province(202102AB080019-1)National Key Research and Development Program of China(2022YFB3708600)the National Natural Science Foundation of China(91960103).
文摘Ferroelastic rare earth tantalates(RETaO_(4))are widely researched as the next-generation thermal barrier coatings(TBCs),and RETaO_(4)powders are hugely significant for synthesizing their coatings.The current research used chemical co-precipitation within an automated experimental device to synthesize RETaO_(4)(RE=Nd,Sm,Gd,Ho,Er)powders.The device automatically monitored and controlled the solutions'pH,improving the chemical co-precipitation efficiency.The crystal structure and microstructure of the RETaO_(4)powders can be controlled by changing the annealing temperature,and the materials undergo an m'-m phase transition.The m'-RETaO_(4)powders exhibit nano-size grains,while m-RETaO_(4)powders evince micron-size grains,altered by the annealing temperatures.A simultaneous thermal analysis es-timates the reversive ferroelastic tetragonal-monoclinic phase transition temperatures.Overall,this research focuses on the synthesis,crystal structures,microstructures,and phase transition of the fabricated RETaO_(4)powders.
基金supported in part by National Key R&D Program of China under Grant 2023YFB4705600in part by the National Natural Science Foundation of China under Grants 61925304,62127810 and 62203138+1 种基金in part by the National Postdoctoral Program for Innovative Talents under Grant BX20200107in part by the Self-Planned Task(No.SKLRS202205C)of State Key Laboratory of Robotics and System(HIT).
文摘Microscale metallic structures enhanced by additive manufacturing technology have attracted extensive attention especially in microelectronics and electromechanical devices.Meniscus-confined electrodeposition(MCED)advances microscale 3D metal printing,enabling simpler fabrication of superior metallic microstructures in air without complex equipment or post-processing.However,accurately predicting growth rates with current MCED techniques remain challenging,which is essential for precise structure fabrication and preventing nozzle clogging.In this work,we present a novel approach to electrochemical 3D printing that utilizes a self-adjusting,voxelated method for fabricating metallic microstructures.Diverging from conventional voxelated printing which focuses on monitoring voxel thickness for structure control,this technique adopts a holistic strategy.It ensures each voxel’s position is in alignment with the final structure by synchronizing the micropipette’s trajectory during deposition with the intended design,thus facilitating self-regulation of voxel position and reducing errors associated with environmental fluctuations in deposition parameters.The method’s ability to print micropillars with various tilt angles,high density,and helical arrays demonstrates its refined control over the deposition process.Transmission electron microscopy analysis reveals that the deposited structures,which are fabricated through layer-by-layer(voxel)printing,contain nanotwins that are widely known to enhance the material’s mechanical and electrical properties.Correspondingly,in situ scanning electron microscopy(SEM)microcompression tests confirm this enhancement,showing these structures exhibit a compressive yield strength exceeding 1 GPa.The indentation tests provided an average hardness of 3.71 GPa,which is the highest value reported in previous work using MCED.The resistivity measured by the four-point probe method was(1.95±0.01)×10^(−7)Ω·m,nearly 11 times that of bulk copper.These findings demonstrate the considerable advantage of this technique in fabricating complex metallic microstructures with enhanced mechanical properties,making it suitable for advanced applications in microsensors,microelectronics,and micro-electromechanical systems.
基金support for this study was provided by the Strategic Priority Research Program(B)of the Chinese Academy of Sciences(No.XDB18030601)the One Hundred Talents Project of Shaanxi Province to Laixi Tongthe Natural Science Foundation of Shaanxi Province(No.2023-JC-QN-0283)granted to Chao Li.
文摘The Irtysh tectonic belt lies on the southern margin of the Chinese Altai Orogen. Several secondary shear zones with NW-SE strikes have developed in this tectonic belt, and the deformation processes are of great significance to understanding the tectonic regime of the Altai Orogen in the Late Paleozoic. The Tuerhongshate ductile shear zone is located in the eastern Irtysh tectonic belt with obvious deformed structures. The felsic rocks are strongly mylonitized, exhibiting S-C fabrics, asymmetric rotational porphyroclasts, and bookshelf structures of the plagioclases, indicating a sinistral shear sense. The deformation mechanisms, lattice preferred orientations (LPOs) of quartz, and opening angles of quartz c-axis suggest that the deformation temperatures range from 400 to 500 ℃, consistent with higher-greenschist to lower-amphibolite facies conditions. The calculated kinematic vorticity values (W_(k)) of the studied samples range from 0.53 to 0.89 and indicate general shear to simple shear, based on rotational rigid porphyroclast method and oblique grain-shaped/quartz c-axis fabric method. The U-Pb ages of magmatic zircons in felsic mylonites indicate that the sinistral shear occurred after 296.7 ± 3.0 Ma (Early Permian) in the Tuerhongshate shear zone and persisted for approximately 13 Ma. Combined with the tectonic setting and the observed sinistral strike-slip shear indicators in the mylonite zone, these features demonstrate that the Irtysh tectonic belt was in a post-orogenic and strike-slip environment following the closure of the Irtysh Ocean.
基金Project(ZZYJKT2025-03) supported by the Project of State Key Laboratory of Precision Manufacturing for Extreme Service Performance,Central South University,ChinaProject(2024YFB3411200) supported by the National Key Research and Development Program of China。
文摘The microstructures,mechanical properties,and fracture behaviors of an Al-5.9Zn-1.9Mg alloy subjected to thermomechanical treatment across different pre-rolling temperatures have been exhaustively investigated in present work.The pre-deformation temperature exerts a modest influence on grain morphology,while it profoundly impacts the dislocation configurations and precipitation behaviors.Elevating the rolling temperature from ambient to 170℃results in a reduction in dislocation density within grains accompanied by a notable enhancement in their distributional uniformity.While advancing the temperature to 320℃prompts the premature formation of precipitates during deformation,which diminishes the precipitation during the subsequent ageing.Tensile results reveal that the thermomechanical treatment incorporating pre-rolling at 170℃confers a substantial strengthening effect on the alloy on the basis of both grain boundary strengthening and dislocation strengthening stemmed from pre-deformation along with the precipitation strengthening generated by ageing.Furthermore,the microstructure exhibits a relatively scarce presence of inhomogeneous features such as dislocation pile-ups and micro shear bands,contributing favorably to enhance the ductility of the alloy that presents the mixture of cleavage fracture and dimple-induced failure.
基金supported by the National Natural Science Foun-dation of China(62301596 and 62288101)Shaanxi Provincial Science and Technology Innovation Team(23-CX-TD-48)+4 种基金the KU Leuven internal funds:the C1 Project(C14/19/083)the Interdisciplinary Network Project(IDN/20/014)the Small Infrastructure Grant(KA/20/019)the Research Foundation of Flanders(FWO)Project(G090017N,G088822N,and V408823N)the Danish National Research Foundation(DNRF165).
文摘Optical singularities are topological defects of electromagnetic fields;they include phase singularity in scalar fields,polarization singularity in vector fields,and three-dimensional(3D)singularities such as optical skyrmions.The exploitation of photonic microstructures to generate and manipulate optical singularities has attracted wide research interest in recent years,with many photonic microstructures having been devised to this end.Accompanying these designs,scattered phenomenological theories have been proposed to expound the working mechanisms behind individual designs.In this work,instead of focusing on a specific type of microstructure,we concentrate on the most common geometric features of these microstructures—namely,symmetries—and revisit the process of generating optical singularities in microstructures from a symmetry viewpoint.By systematically employing the projection operator technique in group theory,we develop a widely applicable theoretical scheme to explore optical singularities in microstructures with rosette(i.e.,rotational and reflection)symmetries.Our scheme agrees well with previously reported works and further reveals that the eigenmodes of a symmetric microstructure can support multiplexed phase singularities in different components,such as out-of-plane,radial,azimuthal,and left-and right-handed circular components.Based on these phase singularities,more complicated optical singularities may be synthesized,including C points,V points,L lines,Néel-and bubble-type optical skyrmions,and optical lattices,to name a few.We demonstrate that the topological invariants associated with optical singularities are protected by the symmetries of the microstructure.Lastly,based on symmetry arguments,we formulate a so-called symmetry matching condition to clarify the excitation of a specific type of optical singularity.Our work establishes a unified theoretical framework to explore optical singularities in photonic microstructures with symmetries,shedding light on the symmetry origin of multidimensional and multiplexed optical singularities and providing a symmetry perspective for exploring many singularity-related effects in optics and photonics.
基金supported from the National Natural Science Foundation of China(No.52371062)the Open Foundation from National Key Laboratory of Materials Behavior and Evaluation Technology in Space Environments,China,the National Key Research and Development Program of China(No.2020YFB2007900)the National Major Science and Technology Projects of China(No.2017-VI-0020-0093).
文摘It is one of the big bottleneck problems for graphene to be uniformly distributed in ceramic matrix composites. A two-step approach was applied to prepare Graphene Nanoplatelets/Yt tria-Stabilized Zirconia(GNPs/YSZ) composites. Initially, GNPs were combined with YSZ through nanoparticle regranulation technology to obtain uniformly dispersed powders. Subsequently, the prepared powders were sintered by Spark Plasma Sintering(SPS). Systematic investigation was carried out to examine how GNPs regulate the phase, microstructures, and nanomechanical properties of GNPs/YSZ composite ceramics with different sintering temperatures.Results show that the GNPs can inhibit the coalescence of adjacent grains in YSZ ceramics. Herein,we propose that the intensity ratio of 2D peak to G peak of GNPs in Raman spectrum serves as a key indicator to assess the nanomechanical properties of GNPs/YSZ composites. When the intensity ratio of 2D peak to G peak is 0.5–0.6, the GNPs/YSZ composites obtained in the sintering temperature range of 1 200–1 250.C exhibit excellent nanomechanical properties such as hardness,elastic modulus, wear and creep resistance.
基金supported by the National Natural Science Foundation of China(Grant No.11972383)to Wenpeng Zhuby the National Natural Science Foundation of China(Grant No.12132020)to Yue Zhengby the Guangdong Provincial Key Laboratory of Magnetoelectric Physics and Devices(Grant No.2022B1212010008).
文摘F-actin microstructures dominate cellular viscoelasticity and have been used to identify the migration and malignance of living cancer cells.Diabetic cancer patients suffer from increased metastasis and tumor recurrence.However,the long-term evolution and correlation of F-actin microstructures and viscoelasticity distribution are still poorly understood in living cancer cells under varying glucose environment.Herein,by using atomic force microscopy with amplitude modulation-frequency modulation and nanoindentation mode,we characterized the hierarchical F-actin microstructures and the multi-passage viscoelasticity evolution in living Huh-7 cancer cells transferred from high to low glucose level.The highly oriented stress fibers connected by thinner fiber networks were observed in high glucose environment.The circumferential actin networks composed by straight segment-like fibers and the randomly distributed actin fragments connected by ultrathin crosslinking fibers were observed in low glucose environment.The viscoelasticity within the nucleus and the cytoplasm of living Huh-7 cancer cells showed longterm fluctuations over tens of passages after switching glucose environments.The viscoelasticity of cytoplasm was more responsive to the change of glucose environments than nucleus,which was due to the reorganization of F-actin microstructures.Our work provides the microstructural and nanomechanical understanding on the migration and proliferation of living cancer cells under varying glucose environment.
基金financially supported by the National Key R&D Program of China(No.2021YFB3702301)the National Natural Science Foundation of China(No.52101068]+2 种基金the China Postdoctoral Science Foundation[No.2022T150342]the Postdoctoral International Exchange Program[No.YJ20210129]the Shuimu Tsinghua Scholar Program(No.2020SM100)
文摘Notable advancements have been made in the additive manufacturing(AM)of aerospace materials,driven by the needs for integrated components with intricate geometries and small-lot production of high-value components.Nickel-based superalloys,pivotal materials for high-temperature bearing components in aeroengines,present significant challenges in the fabrication of complex parts due to their great hardness.Huge attention and rapid progress have been garnered in AM processing of nicklebased superalloys,largely owing to its distinct benefits in the freedom of fabrication and reduced manufacturing lifecycle.Despite extensive research into AM in nickel-based superalloys,the corresponding results and conclusions are scattered attributed to the variety of nickel-based superalloys and complex AM processing parameters.Therefore,there is still a pressing need for a comprehensive and deep understanding of the relationship between the AM processing and microstructures and mechanical performance of nickel-based superalloys.This review introduces the processing characteristics of four primary AM technologies utilized for superalloys and summarizes the microstructures and mechanical properties prior to and post-heat treatments.Additionally,this review presents innovative superalloys specifically accommodated to AM processing and offers insights into the material development and performance improvement,aiming to provide a valuable assessment on AM processing of nickel-based superalloys and an effective guidance for the future research.
基金financially supported by the National Natural Science Foundation of China(Nos.51975175,51875158)。
文摘The fracture behavior at high temperatures of the Ti−22Al−26Nb alloy,which features duplex lamellar,bimodal,and Widmanstätten structures,was studied.Samples of the alloy were prepared through compression deformation in the trans-phase region followed by subsequent heat treatment.The results indicate that at 650℃,the fracture toughness of the Ti−22Al−26Nb alloy is increased by 41.7%compared to that with original microstructures.The content of the B2 phase significantly influences the inherent fracture toughness of the material,while the morphology and distribution of the precipitated phases primarily affect the tortuosity of the crack propagation path.Among the microstructural features,the morphology and geometric orientation of the lamellae most significantly impact the crack path;consequently,the Widmanstätten structure exhibits the most tortuous fracture path.Additionally,a predictive model for fracture toughness is developed,which effectively predicts the fracture toughness of Ti−22Al−26Nb alloys with various microstructures at 650℃.
基金Natural Science Foundation of Shandong Province of China(ZR2023QE193)。
文摘The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal hot extrusion parameters are determined as ingot initial temperature of 380°C and extrusion speed of 3 mm/s.The hot-extruded aluminum alloy after T6 heat treatment presents superior mechanical properties with yield strength of 519.6 MPa,ultimate tensile strength of 582.1 MPa,and elongation of 11.0%.Compared with the properties of gravity-cast and liquid-forged alloys,the yield strength of hot-extruded alloy increases by 30.8%and 4.9%,and the ultimate tensile strength improves by 43.5%and 10.2%,respectively.The significant improvement in tensile strength of the hot-extruded alloys is attributed to the elimination of casting defects and the refinement of matrix grain and eutectic phases.In addition,the hot-extruded alloy demonstrates superior plasticity compared with the liquid-forged alloy.This is because severe plastic deformation occurs during hot extrusion,which effectively breaks and disperses the eutectic phases,facilitating the dissolution and precipitation of the second phases and inhibiting the microcrack initiation.
基金Project (50975093) supported by the National Natural Science Foundation of ChinaProject (2012ZP0006) supported by the Fundamental Research Funds for the Central Universities,China
文摘A356-based metal matrix composites with 10% SiC particles of 10 rtm were fabricated by stir casting and direct squeeze casting process under applied pressures of 0.1 （gravity）, 25, 50 and 75 MPa. The microstructures and mechanical properties of the as-cast and T6 heat-treated castings were investigated. The results show that as the applied pressures increase, the casting defects as particle-porosity clusters reduce and the incorporation between the particles and matrix can be improved. The tensile strength, hardness, and coefficients of thermal expansion （CTE） increase with the increase of the pressures. Compared with the as-cast composite castings, the tensile strength and hardness of the heat-treated casting are improved whereas CTEs tend to decrease in T6-treated condition. For the gravity cast composites, there are some particle-porosity clusters on the fracture surface, and the clusters are hardly detected on the fracture surface of the samples solidified at the external pressures. Different fracture behaviors are found between the composites solidified at the gravity and imposed pressures.
基金Shenzhen Science and Technology Program(KJZD20230923113900001)Project of Industry and Information Technology Bureau of Shenzhen Municipality(201806071403422960)。
文摘The hot compression curves and deformed microstructures were investigated under various hot deformation conditions in three states:hot isostatic pressing(HIP,A1),HIP+hot extrusion at 1100℃(A2),and HIP+hot extrusion at 1150℃(A3).The results show that A2 sample,extruded at 1100℃ with uniform γ+γ′duplex microstructures,demonstrates excellent hot deformation behavior at both 1050 and 1100℃.The true stress-true strain curves of A2 sample maintain a hardening-softening equilibrium over a larger strain range,with post-deformation average grain size of 5μm.The as-HIPed A1 sample and 1150℃ extruded A3 sample exhibit a softening region in deformation curves at 1050℃,and the grain microstructures reflect an incomplete recrystallized state,i.e.combination of fine recrystallized grains and initial larger grains,characterized by a necklace-like microstructure.The predominant recrystallization mechanism for these samples is strain-induced boundary migration.At 1150℃ with a strain rate of 0.001 s^(-1),the influence of the initial microstructure on hot deformation behavior and resultant microstructure is relatively less pronounced,and postdeformation microstructures are fully recrystallized grains.Fine-grained microstructures are conducive to maximizing the hot deformation potential of alloy.By judiciously adjusting deformation regimes,a fine and uniform deformed microstructure can be obtained.
基金Project (50875031) supported by the National Natural Science Foundation of ChinaProject (DUT122D205) supported by the Fundamental Research Funds for the Central Universities,China
文摘Microstructures and element distributions of the as-cast, hot-rolled and cold-rolled Cu-Mg-Te-Y alloys were studied. Effects of rolling process and annealing temperature on the properties of the Cu-Mg-Te-Y alloys were correspondingly investigated. The results indicate that the Mg element is homogeneously distributed in the matrix and the fragmentized Cu2Te phase is dispersed in the matrix after hot rolling. Then, the Cu2Te phase is further stretched to strip shape after the cold rolling process. The microstructures of the cold-rolled alloy keep unchanged for the sample annealed below 390 ℃ for 1 h. However, after annealing at 550 ℃ for 1 h, the copper alloy with fibrous microstructures formed during the cold rolling process recrystallizes, leading to an obvious drop of hardening effect and an increase of electrical conductivity. The Cu-Mg-Te-Y alloy with better comprehensive properties is obtained by annealing at 360-390 ℃.
基金Project(2013CB632200)supported by the National Great Theoretic Research,ChinaProject(2011BAE22B01-3)supported by the National Sci&Tech Support Program,ChinaProject(2010DFR50010)supported by the International Cooperation,Sharing Fund of Chongqing University’s Large-scale Equipment,China
文摘The microstructures and mechanical properties of Mg-6Zn-1Mn-4Sn-1.5Nd alloy subjected to extrusion and T5 treatment were investigated using optical microscopy（OM）, X-ray diffractometer（XRD）, scanning electron microscopy（SEM）, electron back scattered diffraction（EBSD）, transmission electron microscopy（TEM）, hardness tests and uniaxial tensile tests. The results showed that the as-cast alloy consisted of α（Mg）, Mn, Mg7Zn3, Mg2 Sn and Mg Sn Nd phases. Dynamic recrystallization has completed during the extrusion process and the average grain size was 7.2 μm. After T5 treatment, the strength increased obviously, the yield strength and ultimate tensile strength of as-extruded alloy were increased by 94 and 34 MPa, respectively. Microstructure characterization revealed that the improvement of strength was determined by the high number density of β′1 rods.
文摘In order to reveal the differences caused by forging and rolling process for titanium ingots, hot compression behavior, mechanical properties and the microstructures of forged billets and rolled ones were investigated in detail using Gleeble-1500 thermal mechanical simulator, universal testing machine and optical microscope （OM）. The compression deformation experimental data of commercially pure titanium （CP-Ti） were mapped to be a T vs lg diagram in which data fall into three distinct regions, i.e., three-stage work hardening, two-stage work hardening and flow softening, which can be separated by border lines at 17.5 and 15.4 for lg Z, where Z represents the Zener-Hollomon parameter. The deformation twin is found to have higher Z-value corresponding to the work hardening region. The differences in microstructures and mechanical properties for two kinds of billets indicate that forged billet consists of deformation twins and some twin intersections, and many twins cross the grain boundaries. However, nearly no twins can be seen in the microstructure of billet formed by rolling under optical microscope （OM）, but there are equiaxed and platelike grains. Tensile tests and Vickers hardness test indicate that yield strength, tensile strength and microhardness of the samples after forging are higher than those after rolling.
基金Project (09C26279200863) supported by Technology Innovation Fund Project of High-tech Small and Medium Enterprises,Ministry of Science and Technology of ChinaProject (BA2011084) supported by Special Fund Project on Science and Technology Achievement Transformation of Jiangsu Province,China
文摘Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.