Inconel 718 superalloy coating was prepared on a martensitic steel substrate by cold gas dynamic spraying （ CGDS ）. Microstructure and micro-hardness of the coating were characterized by means of scanning electronic...Inconel 718 superalloy coating was prepared on a martensitic steel substrate by cold gas dynamic spraying （ CGDS ）. Microstructure and micro-hardness of the coating were characterized by means of scanning electronic microscope （SEM） ,energy dispersive spectrometer （EDS）, and micro-hardness and nano-indentation tests. The results have indicated that the coating＇ s thickness can reach more than 300 um, and there exists a good interfacial cohesion between the coating and the substrate. The quantity and size of the defects at the bottom, middle and top areas increase gradually. There is no significant change to the original microstructure of the Inconel 718 superalloy particle after the process of CGDS ;and an obvious torsional deformation on the particle＇ s profile is produced while little deformation at the center part occurs. The micro-hardness of the coating at the bottom, middle and top areas decreases in turn. Compared with the bottom area, the micro-hardness of the middle and top areas decreases by about 10% and 21%, respectively. The nano-hardness of the coating is much lower than the original particle,which decreases by about 13.5% at the bottom area and 28% at the top area,respectively. The distribution of micro-defects is an important factor to the micro-hardness of the coating.展开更多
For many years, intermetallic materials promise applications in a wide variety of technology areas. NiAl intermetallic compound is material that exhibits important characteristics such as high corrosion resistance and...For many years, intermetallic materials promise applications in a wide variety of technology areas. NiAl intermetallic compound is material that exhibits important characteristics such as high corrosion resistance and low density besides its ability to retain strength and stiffness at elevated temperatures. However NiAl intermetallic is too hard, brittle and exhibits very low ductility at room temperature being the reason because this material is not yet available for structural applications. In order to increase the ductility of the NiAl intermetallic compound, the addition of a third alloying element has been proved, nevertheless it is important to determine if such additions decrease or increase the hardness and the corrosion resistance of the alloy. So, the present investigation reports the corrosion performance of the NiAl intermetallic compound modified with Cu, emphasizing the EIS analysis and the relation between physical parameters and the modelling equations used in the Equivalent Electric Circuit. It was found that the addition of Cu promotes the formation of the γ’-Ni<sub>3</sub>Al phase in Cu contents greater than 15 at. %, in addition to a decrease in micro hardness and an increment in the I<sub>corr</sub> values. In this way, the electrochemical characterization evidenced a high corrosion resistance of these intermetallic alloys.展开更多
Dissimilar AZ31B magnesium alloy and DC56D steel were welded via AA1060 aluminum alloy by magnetic pulse welding.The effects of primary and secondary welding processes on the welded interface were comparatively invest...Dissimilar AZ31B magnesium alloy and DC56D steel were welded via AA1060 aluminum alloy by magnetic pulse welding.The effects of primary and secondary welding processes on the welded interface were comparatively investigated.Macroscopic morphology,microstructure,and interfacial structure of the joints were analyzed using scanning electron microscope,energy dispersive spectrometer,and X-ray diffractometer(XRD).The results show that magnetic pulse welding of dissimilar Mg/Fe metals is achieved using an Al interlayer,which acts as a bridge for deformation and diffusion.Specifically,the AZ31B/AA1060 interface exhibits a typical wavy morphology,and a transition zone exists at the joint interface,which may result in an extremely complex microstructure.The microstructure of this transition zone differs from that of AZ31B magnesium and 1060 Al alloys,and it is identified as brittle intermetallic compounds(IMCs)Al_(3)Mg_(2) and Al_(12)Mg_(17).The transition zone is mainly distributed on the Al side,with the maximum thickness of Al-side transition layer reaching approximately 13.53μm.Incomplete melting layers with varying thicknesses are observed at the primary weld interface,while micron-sized hole defects appear in the transition zone of the secondary weld interface.The AA1060/DC56D interface is mainly straight,with only a small number of discontinuous transition zones distributed intermittently along the interface.These transition zones are characterized by the presence of the brittle IMC FeAl_(3),with a maximum thickness of about 4μm.展开更多
In current research,Li_(2)O-Al_(2)O_(3)-SiO_(2)glass-ceramics were prepared by conventional meltquenching and subsequent heat treatment method.The effect of Al_(2)O_(3)content on microstructures,thermal properties,cry...In current research,Li_(2)O-Al_(2)O_(3)-SiO_(2)glass-ceramics were prepared by conventional meltquenching and subsequent heat treatment method.The effect of Al_(2)O_(3)content on microstructures,thermal properties,crystallization behaviours and mechanical properties were investigated.FTIR,Raman spectroscopy and nuclear magnetic resonance spectroscopy microstructure analysis showed that the silico-oxygen network was damaged,while the increase of[AlO_(4)]content repaired the glass network,and finally made the glass network have better connectivity,with the decrease of SiO_(2).The thermal analysis confirmed the increasing glass transition and crystallization temperatures from growing Al_(2)O_(3)content.In addition,different crystal phases can be precipitated in the glass matrix,such as LiAlSi_(4)O_(10),Li_(2)Si_(2)O_(5) in glass with low Al_(2)O_(3)content,the combination of Li_xAl_xSi_(1-x)O_(2),LiAlSi_(3)O_(8),Li_(2)SiO_(3)in glass with intermediate Al_(2)O_(3)content,and the combination of LiAlSi_(2)O_(6),SiO_(2)in glass with high Al_(2)O_(3)content.The hardness of as-prepared glass gradually increases with the increase of the Al_(2)O_(3)content.The Vickers hardness of the glass-ceramics is highly dependent on the Al_(2)O_(3)content in the glass and the heat treatment temperatures,reaching a maximum of 10.11 GPa.Scanning electron microscope images show that the crystals change from spherical to massive and finally to sheet.The change of glass structure,crystal phase and morphology is the main reason for the different mechanical properties.展开更多
The microstructure of high Nb-TiAl alloys was optimized by the addition of a small amount of Ta elements to further improve their properties.A series of Ti46Al1.5Cr8Nb-xTa(x=0.2,0.4,0.6,0.8,1.0,at.%)alloys were prepar...The microstructure of high Nb-TiAl alloys was optimized by the addition of a small amount of Ta elements to further improve their properties.A series of Ti46Al1.5Cr8Nb-xTa(x=0.2,0.4,0.6,0.8,1.0,at.%)alloys were prepared by vacuum arc melting.The microstructure,mechanical properties,and related influencing mechanisms were systematically investigated.The results indicate that the solidification microstructure of the Ti46Al1.5Cr8Nb-xTa alloys comprises theγ-TiAl phase,α_(2)-Ti_(3)Al phase,and B2 phase.As the Ta content increases from 0.2 at.%to 1.0 at.%,the content ofα_(2)phase and B2 phase increases,while theγphase content decreases.Among them,the B2 phase shows the most pronounced change,being significantly refined,with its content increasing from 12.49%to 21.91%.In addition,the average size of the lamellar colony decreases from 160.65 to 94.44μm.The addition of the Ta element shifts the solidification path toward lower aluminum concentrations,leading to changes in phase content.The tantalum-induced increase in the B2 phase and enhanced supercooling at the solidification front provide the basis for lamellar colony refinement.Compressive testing at room temperature reveals that the Ti46 Al1.5 Cr8 Nb0.4 Ta alloy exhibits optimal compressive properties,achieving a compressive strength of 2,434 MPa and a compressive strain of 33.1%.The improvement of its properties is attributed to a combination of lamellar colony refinement,solid solution strengthening resulting from the incorporation of Ta element,and a reduction in the c/a of theγphase.展开更多
The rapid advancements in computer vision(CV)technology have transformed the traditional approaches to material microstructure analysis.This review outlines the history of CV and explores the applications of deep-lear...The rapid advancements in computer vision(CV)technology have transformed the traditional approaches to material microstructure analysis.This review outlines the history of CV and explores the applications of deep-learning(DL)-driven CV in four key areas of materials science:microstructure-based performance prediction,microstructure information generation,microstructure defect detection,and crystal structure-based property prediction.The CV has significantly reduced the cost of traditional experimental methods used in material performance prediction.Moreover,recent progress made in generating microstructure images and detecting microstructural defects using CV has led to increased efficiency and reliability in material performance assessments.The DL-driven CV models can accelerate the design of new materials with optimized performance by integrating predictions based on both crystal and microstructural data,thereby allowing for the discovery and innovation of next-generation materials.Finally,the review provides insights into the rapid interdisciplinary developments in the field of materials science and future prospects.展开更多
The age-hardening response,mechanical,and corrosion-resistant properties of AA7085 alloys with and without the addition of 0.3 wt.%scandium(Sc)were compared.Using advanced techniques such as aberration-corrected trans...The age-hardening response,mechanical,and corrosion-resistant properties of AA7085 alloys with and without the addition of 0.3 wt.%scandium(Sc)were compared.Using advanced techniques such as aberration-corrected transmission electron microscopy and first-principles calculations,the underlying micromechanisms of Sc microalloying were revealed.Results show that the increase in strength of the AA7085-Sc alloy is mainly attributed to the decreased Al grain size and increased number density of both Al_(3)Sc@Al_(3)(Sc,Zr)core−shell nanoparticles and Sc-containingη_(p) and GP−η_(p) nanoprecipitates.Strong strain fields and evident electron transfer from Zr to the neighboring matrix Al atoms exist at the Al_(3)Sc@Al_(3)(Sc,Zr)/Al interface.The Sc doping in GP−η_(p) andη_(p) suppresses the GP−η_(p)→η_(p) transformation.Modified corrosion resistance of the AA7085-Sc alloy compared with AA7085 alloy is associated with the fine grain boundary precipitates ofη_(p)hases and narrow precipitation free zone.The reasons of property changes of AA7085 alloy after Sc microalloying are explored based on the multiscale microstructural characterization.展开更多
The unique crystallographic lamellar microstructure(CLM) Ni-based superalloys fabricated by laser powder bed fusion(LPBF) exhibits excellent tensile properties.This study aims to investigate CLM's high-temperature...The unique crystallographic lamellar microstructure(CLM) Ni-based superalloys fabricated by laser powder bed fusion(LPBF) exhibits excellent tensile properties.This study aims to investigate CLM's high-temperature stress rupture behavior and use these findings to improve the additive manufacturing process.The result shows that the high temperature-induced intergranular fracture in <110> grain region is responsible for stress rupture failure under both conditions of 760 ℃/780 MPa and 980 ℃/260 MPa.Among them,the sub-grain boundary fracture occurs only under high temperature and low stress,980 ℃/260 MPa.Due to the severe intergranular fracture induced by stray grains,the stress rupture life is very low under both conditions.According to the finite element simulation,the formation of stray grains stems from the unstable heat flow within the melt pool during the process.In addition,the shorter stress rupture lifetime does not excite a more pronounced dislocation network around the γ′ phase.However,the deformation twins can still be activated inside the <110> grains,so it has excellent plasticity under both test conditions.Finally,this work indicates that the future optimization of CLM by LPBF should focus on eliminating of high-angle grain boundaries in <110> grains.展开更多
A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The resu...A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.展开更多
Crushing waste coral concrete into recycled aggregates to create recycled coral aggregate concrete(RCAC)contributes to sustainable construction development on offshore islands and reefs.To investigate the impact of re...Crushing waste coral concrete into recycled aggregates to create recycled coral aggregate concrete(RCAC)contributes to sustainable construction development on offshore islands and reefs.To investigate the impact of recycled coral aggregate on concrete properties,this study performed a comprehensive analysis of the physical properties of recycled coral aggregate and the basic mechanical properties and microstructure of RCAC.The test results indicate that,compared to coral debris,the crushing index of recycled coral aggregate was reduced by 9.4%,while porosity decreased by 33.5%.Furthermore,RCAC retained the early strength characteristics of coral concrete,with compressive strength and flexural strength exhibiting a notable increase as the water-cement ratio decreased.Under identical conditions,the compressive strength and flexural strength of RCAC were 12.7% and 2.5% higher than coral concrete's,respectively,with porosity correspondingly reduced from 3.13% to 5.11%.This enhancement could be attributed to the new mortar filling the recycled coral aggregate.Scanning electron microscopy(SEM)analysis revealed three distinct interface transition zones within RCAC,with the‘new mortar-old mortar’interface identified as the weakest.The above findings provided a reference for the sustainable use of coral concrete in constructing offshore islands.展开更多
The Cu-12Fe alloy has attracted significant attention due to its excellent electrical conductivity and electromagnetic shielding capability,high strength,cost-effectiveness,and recyclability.In the present work,the Cu...The Cu-12Fe alloy has attracted significant attention due to its excellent electrical conductivity and electromagnetic shielding capability,high strength,cost-effectiveness,and recyclability.In the present work,the Cu-12Fe alloy strip with the thickness of 2.4 mm was successfully produced by twin-roll strip casting.The microstructure and properties of the Cu-12Fe alloy were tailored by cold rolling and aging treatment.The tensile strength of the as-cast strip is approximately 328 MPa and its elongation is 25%.The Fe phase randomly dispersed in the matrix,and the average size of Fe-rich phase is 2μm.Besides,enrichment of Fe phase is observed in the central layer of the strip,results in the formation of the“sandwich structure”.Moreover,the as-cast strip of Cu-12Fe was directly cold-rolled from 2.4 to 0.12 mm.The directly cold-rolled sample after aging at 450℃for 16 h(ProcessⅠ)shows excellent electrical conductivity of 69.5%IACS,the tensile strength and elongation are 513 MPa and 3.8%,the saturation magnetic flux density is 20.1 emu·g^(-1),and the coercive force is 25.2 Oe.In ProcessⅡ,the as-cast strip firstly cold-rolled to 1.2 mm,then aged at 500℃for 1.5 h,followed by cold rolling to 0.12 mm,finally aged at 450℃for 16 h.The sample after ProcessⅡshows the electrical conductivity of 66.3%IACS,the tensile strength of 533 MPa,an elongation of 3.5%,saturation magnetic flux density of 21.4 emu·g^(-1),and the coercive force of 22.3 Oe.展开更多
High entropy alloys(HEAs)have recently attracted significant attention due to their exceptional mechanical properties and potential applications across various fields.Friction stir welding and processing(FSW/P),as not...High entropy alloys(HEAs)have recently attracted significant attention due to their exceptional mechanical properties and potential applications across various fields.Friction stir welding and processing(FSW/P),as notable solid-state welding and processing techniques,have been proved effectiveness in enhancing microstructures and mechanical properties of HEAs.This review article summarizes the current status of FSW/P of HEAs.The welding materials and conditions used for FSW/P in HEAs are reviewed and discussed.The effects of FSW/P on the evolutions of grain structure,texture,dislocation,and secondary phase for different HEAs are highlighted.Furthermore,the influences of FSW/P on the mechanical properties of various HEAs are analyzed.Finally,potential applications,challenges,and future directions of FSW/P in HEAs are forecasted.Overall,FSW/P enable to refine grains of HEAs through dynamic recrystallization and to activate diverse deformation mechanisms of HEAs through tailoring phase structures,thereby significantly improving the strength,hardness,and ductility of both single-and dual-phase HEAs.Future progress in this field will rely on comprehensive optimization of processing parameters and alloy composition,integration of multi-scale modeling with advanced characterization for in-depth exploration of microstructural mechanisms,systematic evaluation of functional properties,and effective bridging of the gap between laboratory research and industrial application.The review aims to provide an overview of recent advancements in the FSW/P of HEAs and encourage further research in this area.展开更多
The dependence of shrinkage porosities on microstructure characteristics of Mg−12Al alloy was investigated.The distribution,morphology,size,and number density of shrinkage porosities were analyzed under different cool...The dependence of shrinkage porosities on microstructure characteristics of Mg−12Al alloy was investigated.The distribution,morphology,size,and number density of shrinkage porosities were analyzed under different cooling rates.The relationship between shrinkage porosities and microstructure characteristics was discussed in terms of temperature conditions,feeding channel characteristics,and feeding capacity.Further,the feeding behavior of the residual liquid phase in the solid skeleton was quantified by introducing permeability.Results show a strong correlation between the solid microstructure skeleton and shrinkage porosity characteristics.An increase in permeability corresponds to a declining number density of shrinkage porosities.This study aims to provide a more complete understanding how to reduce shrinkage porosities by controlling microstructure characteristics.展开更多
This study investigated enhancing the wear resistance of Ti6Al4V alloys for medical applications by incorporating Ti C nanoreinforcements using advanced spark plasma sintering(SPS). The addition of up to 2.5wt% Ti C s...This study investigated enhancing the wear resistance of Ti6Al4V alloys for medical applications by incorporating Ti C nanoreinforcements using advanced spark plasma sintering(SPS). The addition of up to 2.5wt% Ti C significantly improved the mechanical properties, including a notable 18.2% increase in hardness(HV 332). Fretting wear tests against 316L stainless steel(SS316L) balls demonstrated a 20wt%–22wt% reduction in wear volume in the Ti6Al4V/Ti C composites compared with the monolithic alloy. Microstructural analysis revealed that Ti C reinforcement controlled the grain orientation and reduced the β-phase content, which contributed to enhanced mechanical properties. The monolithic alloy exhibited a Widmanstätten lamellar microstructure, while increasing the Ti C content modified the wear mechanisms from ploughing and adhesion(0–0.5wt%) to pitting and abrasion(1wt%–2.5wt%). At higher reinforcement levels, the formation of a robust oxide layer through tribo-oxide treatment effectively reduced the wear volume by minimizing the abrasive effects and plastic deformation. This study highlights the potential of SPS-mediated Ti C reinforcement as a transformative approach for improving the performance of Ti6Al4V alloys, paving the way for advanced medical applications.展开更多
The dissimilar 2B06 and 7B04 Al alloy joints were prepared by refill friction stir spot welding(RFSSW),and the microstructural evolution and corrosion behavior of the joints were investigated.Based on microstructural ...The dissimilar 2B06 and 7B04 Al alloy joints were prepared by refill friction stir spot welding(RFSSW),and the microstructural evolution and corrosion behavior of the joints were investigated.Based on microstructural analysis,the welded joints exhibit distinct microstructural zones,including the stir zone(SZ),thermomechanically affected zone(TMAZ),and heat-affected zone(HAZ).The grain size of each zone is in the order of HAZ>TMAZ>SZ.Notably,the TMAZ and HAZ contain significantly larger secondary-phase particles compared to the SZ,with particle size in the HAZ increasing at higher rotational speeds.Electrochemical tests indicate that corrosion susceptibility follows the sequence of HAZ>TMAZ>SZ>BM,with greater sensitivity observed at increased rotational speeds.Post-corrosion mechanical performance degradation primarily arises from crevice corrosion at joint overlaps,but not from the changes in the microstructure.展开更多
A novel Ti-6.38Al-3.87V-2.43Mo alloy was designed with a cluster formula of 12[Al-Ti12](V0.75Mo0.25Ti2)+4[Al-Ti12](Al3)by replacing Ti with Mo/V on the basis of the Ti-Al congruent alloy.The effects of laser power and...A novel Ti-6.38Al-3.87V-2.43Mo alloy was designed with a cluster formula of 12[Al-Ti12](V0.75Mo0.25Ti2)+4[Al-Ti12](Al3)by replacing Ti with Mo/V on the basis of the Ti-Al congruent alloy.The effects of laser power and scanning speed on the molten pool size,surface roughness,relative density,microstructure,and micro-hardness of single-track and bulk Ti-6.38Al-3.87V-2.43Mo samples prepared via laser additive manufacturing(LAM)were investigated.The results show that processing parameters significantly affect the formability,microstructure,and micro-hardness of the alloy.With decreasing laser power from 1,900 W to 1,000 W,the relative density is decreased from 99.86%to 90.91%due to the increase of lack-of-fusion;however,with increasing scanning speed,the relative density does not change significantly,but exceeds 99%.In particular,Ti-6.38Al-3.87V-2.43Mo samples of single-track and bulk exhibit a good formability under an input laser power of 1,900 W and a scanning speed of 8 mm·s_(-1),and display the lowest surface roughness(Ra=13.33μm)and the highest relative density(99.86%).Besides,the microstructure of LAM Ti-6.38Al-3.87V-2.43Mo alloy coarsens with increasing laser power or decreasing scanning speed due to the greater input energy reducing the cooling rate.The coarsening of the microstructure decreases the microhardness of the alloy.展开更多
The n-SiO2/Ni composite electro-brush plating coating was prepared on the 1045 steel substrate. SEM and TEM were utilized to analyze the surface and cross-section morphologies or the microstructures of the composite c...The n-SiO2/Ni composite electro-brush plating coating was prepared on the 1045 steel substrate. SEM and TEM were utilized to analyze the surface and cross-section morphologies or the microstructures of the composite coating before and after heat treatment, as well as a micro-hardness tester was used to measure the micro-hardness before and after heat treatment. The results show that the entrance of nano SiO2 particles into composite coating makes the micro-hardness higher. After heat treatment, due to the obstruction to growth of Ni crystals from nano particles, the composite coating still possesses a higher micro-hardness than that of common Ni-base coating.展开更多
We have described in detail the effects of nano-SiO_(2),nano-CaCO_(3),carbon nanotubes,and nano-Al_(2)O_(3) on geopolymer concrete from the perspectives of macro mechanics and microstructure.The existing research resu...We have described in detail the effects of nano-SiO_(2),nano-CaCO_(3),carbon nanotubes,and nano-Al_(2)O_(3) on geopolymer concrete from the perspectives of macro mechanics and microstructure.The existing research results show that the mechanism of nano-materials on geopolymer concrete mainly includes the filling effect,nucleation effect,and bridging effect,the appropriate amount of nano-materials can be used as fillers to reduce the porosity of geopolymer concrete,and can also react with Ca(OH)2 to produce C-S-H gel,thereby improving the mechanical properties of geopolymer concrete.The optimum content of nano-SiO_(2) is between 1.0%and 2.0%.The optimum content of nano-CaCO_(3) is between 2.0%and 3.0%.The optimum content of carbon nanotubes is between 0.1%and 0.2%.The optimum content of nano-Al_(2)O_(3) is between 1.0%and 2.0%.The main problems existing in the research and application of nanomaterial-modified geopolymer concrete are summarized,which lays a foundation for the further application of nanomaterial in geopolymer concrete.展开更多
The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal ho...The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal hot extrusion parameters are determined as ingot initial temperature of 380°C and extrusion speed of 3 mm/s.The hot-extruded aluminum alloy after T6 heat treatment presents superior mechanical properties with yield strength of 519.6 MPa,ultimate tensile strength of 582.1 MPa,and elongation of 11.0%.Compared with the properties of gravity-cast and liquid-forged alloys,the yield strength of hot-extruded alloy increases by 30.8%and 4.9%,and the ultimate tensile strength improves by 43.5%and 10.2%,respectively.The significant improvement in tensile strength of the hot-extruded alloys is attributed to the elimination of casting defects and the refinement of matrix grain and eutectic phases.In addition,the hot-extruded alloy demonstrates superior plasticity compared with the liquid-forged alloy.This is because severe plastic deformation occurs during hot extrusion,which effectively breaks and disperses the eutectic phases,facilitating the dissolution and precipitation of the second phases and inhibiting the microcrack initiation.展开更多
In-situ formed high Mn steel coating reinforced by carbides was formed by laser surface alloying(LSA).Laser alloyed layers on 1Cr18Ni9Ti steel with Mn+W_(2)C(specimen A),Mn+NiWC(specimen B)and Mn+SiC(specimen C)powder...In-situ formed high Mn steel coating reinforced by carbides was formed by laser surface alloying(LSA).Laser alloyed layers on 1Cr18Ni9Ti steel with Mn+W_(2)C(specimen A),Mn+NiWC(specimen B)and Mn+SiC(specimen C)powders were fabricated to improve the wear and corrosion behavior of 1Cr18Ni9Ti steel blades in high speed mixers.Microstructure evolution,phases,element distribution,microhardness,wear and corrosion behavior of the laser alloyed layers were investigated.Results indicated that high Mn steel matrix composites with undissolved W_(2)C,WC and other in-situ formed carbides were formed by LSA with Mn+W_(2)C and Mn+NiWC while SiC totally dissolved into the high Mn matrix when adding Mn+SiC.Ni as the binding phase in Ni-WC powder decreased the crack sensitivity of the alloyed layer as compared with the addition of W_(2)C powder.An improvement in average microhardness was achieved in the matrix in specimen A,B and C,with the value of 615,602 and 277 HV_(0.5),while that of the substrate was 212 HV_(0.5).The increase of microhardness,wear and corrosion resistance is highly corelated to microstructure,formed phases,type and content of carbides,micro-hardness and toughness of the alloyed layers.展开更多
文摘Inconel 718 superalloy coating was prepared on a martensitic steel substrate by cold gas dynamic spraying （ CGDS ）. Microstructure and micro-hardness of the coating were characterized by means of scanning electronic microscope （SEM） ,energy dispersive spectrometer （EDS）, and micro-hardness and nano-indentation tests. The results have indicated that the coating＇ s thickness can reach more than 300 um, and there exists a good interfacial cohesion between the coating and the substrate. The quantity and size of the defects at the bottom, middle and top areas increase gradually. There is no significant change to the original microstructure of the Inconel 718 superalloy particle after the process of CGDS ;and an obvious torsional deformation on the particle＇ s profile is produced while little deformation at the center part occurs. The micro-hardness of the coating at the bottom, middle and top areas decreases in turn. Compared with the bottom area, the micro-hardness of the middle and top areas decreases by about 10% and 21%, respectively. The nano-hardness of the coating is much lower than the original particle,which decreases by about 13.5% at the bottom area and 28% at the top area,respectively. The distribution of micro-defects is an important factor to the micro-hardness of the coating.
文摘For many years, intermetallic materials promise applications in a wide variety of technology areas. NiAl intermetallic compound is material that exhibits important characteristics such as high corrosion resistance and low density besides its ability to retain strength and stiffness at elevated temperatures. However NiAl intermetallic is too hard, brittle and exhibits very low ductility at room temperature being the reason because this material is not yet available for structural applications. In order to increase the ductility of the NiAl intermetallic compound, the addition of a third alloying element has been proved, nevertheless it is important to determine if such additions decrease or increase the hardness and the corrosion resistance of the alloy. So, the present investigation reports the corrosion performance of the NiAl intermetallic compound modified with Cu, emphasizing the EIS analysis and the relation between physical parameters and the modelling equations used in the Equivalent Electric Circuit. It was found that the addition of Cu promotes the formation of the γ’-Ni<sub>3</sub>Al phase in Cu contents greater than 15 at. %, in addition to a decrease in micro hardness and an increment in the I<sub>corr</sub> values. In this way, the electrochemical characterization evidenced a high corrosion resistance of these intermetallic alloys.
文摘Dissimilar AZ31B magnesium alloy and DC56D steel were welded via AA1060 aluminum alloy by magnetic pulse welding.The effects of primary and secondary welding processes on the welded interface were comparatively investigated.Macroscopic morphology,microstructure,and interfacial structure of the joints were analyzed using scanning electron microscope,energy dispersive spectrometer,and X-ray diffractometer(XRD).The results show that magnetic pulse welding of dissimilar Mg/Fe metals is achieved using an Al interlayer,which acts as a bridge for deformation and diffusion.Specifically,the AZ31B/AA1060 interface exhibits a typical wavy morphology,and a transition zone exists at the joint interface,which may result in an extremely complex microstructure.The microstructure of this transition zone differs from that of AZ31B magnesium and 1060 Al alloys,and it is identified as brittle intermetallic compounds(IMCs)Al_(3)Mg_(2) and Al_(12)Mg_(17).The transition zone is mainly distributed on the Al side,with the maximum thickness of Al-side transition layer reaching approximately 13.53μm.Incomplete melting layers with varying thicknesses are observed at the primary weld interface,while micron-sized hole defects appear in the transition zone of the secondary weld interface.The AA1060/DC56D interface is mainly straight,with only a small number of discontinuous transition zones distributed intermittently along the interface.These transition zones are characterized by the presence of the brittle IMC FeAl_(3),with a maximum thickness of about 4μm.
基金Funded by the National Key Research Program(No.2024-1129-954-112)National Natural Science Foundation of China(No.52372033)Guangxi Science and Technology Major Program(No.AA24263054)。
文摘In current research,Li_(2)O-Al_(2)O_(3)-SiO_(2)glass-ceramics were prepared by conventional meltquenching and subsequent heat treatment method.The effect of Al_(2)O_(3)content on microstructures,thermal properties,crystallization behaviours and mechanical properties were investigated.FTIR,Raman spectroscopy and nuclear magnetic resonance spectroscopy microstructure analysis showed that the silico-oxygen network was damaged,while the increase of[AlO_(4)]content repaired the glass network,and finally made the glass network have better connectivity,with the decrease of SiO_(2).The thermal analysis confirmed the increasing glass transition and crystallization temperatures from growing Al_(2)O_(3)content.In addition,different crystal phases can be precipitated in the glass matrix,such as LiAlSi_(4)O_(10),Li_(2)Si_(2)O_(5) in glass with low Al_(2)O_(3)content,the combination of Li_xAl_xSi_(1-x)O_(2),LiAlSi_(3)O_(8),Li_(2)SiO_(3)in glass with intermediate Al_(2)O_(3)content,and the combination of LiAlSi_(2)O_(6),SiO_(2)in glass with high Al_(2)O_(3)content.The hardness of as-prepared glass gradually increases with the increase of the Al_(2)O_(3)content.The Vickers hardness of the glass-ceramics is highly dependent on the Al_(2)O_(3)content in the glass and the heat treatment temperatures,reaching a maximum of 10.11 GPa.Scanning electron microscope images show that the crystals change from spherical to massive and finally to sheet.The change of glass structure,crystal phase and morphology is the main reason for the different mechanical properties.
基金the financial support by the Major Science and Technology Achievement Transformation Project in Heilongjiang Province(No.ZC2023SH0075)the National Natural Science Foundation of China(Nos.52425401,U2441255,52474377,and 52371015)+1 种基金the Young Elite Scientists Sponsorship·Program by CAST(No.2021QNRC001)the Henan Provincial Key Research and Development&Promotion Special Program(No.251111231400)。
文摘The microstructure of high Nb-TiAl alloys was optimized by the addition of a small amount of Ta elements to further improve their properties.A series of Ti46Al1.5Cr8Nb-xTa(x=0.2,0.4,0.6,0.8,1.0,at.%)alloys were prepared by vacuum arc melting.The microstructure,mechanical properties,and related influencing mechanisms were systematically investigated.The results indicate that the solidification microstructure of the Ti46Al1.5Cr8Nb-xTa alloys comprises theγ-TiAl phase,α_(2)-Ti_(3)Al phase,and B2 phase.As the Ta content increases from 0.2 at.%to 1.0 at.%,the content ofα_(2)phase and B2 phase increases,while theγphase content decreases.Among them,the B2 phase shows the most pronounced change,being significantly refined,with its content increasing from 12.49%to 21.91%.In addition,the average size of the lamellar colony decreases from 160.65 to 94.44μm.The addition of the Ta element shifts the solidification path toward lower aluminum concentrations,leading to changes in phase content.The tantalum-induced increase in the B2 phase and enhanced supercooling at the solidification front provide the basis for lamellar colony refinement.Compressive testing at room temperature reveals that the Ti46 Al1.5 Cr8 Nb0.4 Ta alloy exhibits optimal compressive properties,achieving a compressive strength of 2,434 MPa and a compressive strain of 33.1%.The improvement of its properties is attributed to a combination of lamellar colony refinement,solid solution strengthening resulting from the incorporation of Ta element,and a reduction in the c/a of theγphase.
基金financially supported by the National Science Fund for Distinguished Young Scholars,China(No.52025041)the National Natural Science Foundation of China(Nos.52450003,U2341267,and 52174294)+1 种基金the National Postdoctoral Program for Innovative Talents,China(No.BX20240437)the Fundamental Research Funds for the Central Universities,China(Nos.FRF-IDRY-23-037 and FRF-TP-20-02C2)。
文摘The rapid advancements in computer vision(CV)technology have transformed the traditional approaches to material microstructure analysis.This review outlines the history of CV and explores the applications of deep-learning(DL)-driven CV in four key areas of materials science:microstructure-based performance prediction,microstructure information generation,microstructure defect detection,and crystal structure-based property prediction.The CV has significantly reduced the cost of traditional experimental methods used in material performance prediction.Moreover,recent progress made in generating microstructure images and detecting microstructural defects using CV has led to increased efficiency and reliability in material performance assessments.The DL-driven CV models can accelerate the design of new materials with optimized performance by integrating predictions based on both crystal and microstructural data,thereby allowing for the discovery and innovation of next-generation materials.Finally,the review provides insights into the rapid interdisciplinary developments in the field of materials science and future prospects.
基金the support from the National Natural Science Foundation of China (Nos. U20A20274, 52061003)the Natural Science Foundation of Yunnan Province, China (No. 202301AT070209)the Science and Technology Major Project of Yunnan Province, China (No. 202102AG050017)。
文摘The age-hardening response,mechanical,and corrosion-resistant properties of AA7085 alloys with and without the addition of 0.3 wt.%scandium(Sc)were compared.Using advanced techniques such as aberration-corrected transmission electron microscopy and first-principles calculations,the underlying micromechanisms of Sc microalloying were revealed.Results show that the increase in strength of the AA7085-Sc alloy is mainly attributed to the decreased Al grain size and increased number density of both Al_(3)Sc@Al_(3)(Sc,Zr)core−shell nanoparticles and Sc-containingη_(p) and GP−η_(p) nanoprecipitates.Strong strain fields and evident electron transfer from Zr to the neighboring matrix Al atoms exist at the Al_(3)Sc@Al_(3)(Sc,Zr)/Al interface.The Sc doping in GP−η_(p) andη_(p) suppresses the GP−η_(p)→η_(p) transformation.Modified corrosion resistance of the AA7085-Sc alloy compared with AA7085 alloy is associated with the fine grain boundary precipitates ofη_(p)hases and narrow precipitation free zone.The reasons of property changes of AA7085 alloy after Sc microalloying are explored based on the multiscale microstructural characterization.
基金the financial support by the Project of Taihang Laboratory (No. A3023)Science Center for Gas Turbine Project (Grant No. P2022-CIV-002-001)。
文摘The unique crystallographic lamellar microstructure(CLM) Ni-based superalloys fabricated by laser powder bed fusion(LPBF) exhibits excellent tensile properties.This study aims to investigate CLM's high-temperature stress rupture behavior and use these findings to improve the additive manufacturing process.The result shows that the high temperature-induced intergranular fracture in <110> grain region is responsible for stress rupture failure under both conditions of 760 ℃/780 MPa and 980 ℃/260 MPa.Among them,the sub-grain boundary fracture occurs only under high temperature and low stress,980 ℃/260 MPa.Due to the severe intergranular fracture induced by stray grains,the stress rupture life is very low under both conditions.According to the finite element simulation,the formation of stray grains stems from the unstable heat flow within the melt pool during the process.In addition,the shorter stress rupture lifetime does not excite a more pronounced dislocation network around the γ′ phase.However,the deformation twins can still be activated inside the <110> grains,so it has excellent plasticity under both test conditions.Finally,this work indicates that the future optimization of CLM by LPBF should focus on eliminating of high-angle grain boundaries in <110> grains.
基金supported by Guangdong Major Project of Basic and Applied Basic Research, China (No. 2020B0301030006)Fundamental Research Funds for the Central Universities, China (No. SWU-XDJH202313)+1 种基金Chongqing Postdoctoral Science Foundation Funded Project, China (No. 2112012728014435)the Chongqing Postgraduate Research and Innovation Project, China (No. CYS23197)。
文摘A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.
基金Funded by Natural Science Foundation of Guangxi(No.2025GXNSFBA069565)Guangxi Science and Technology Program(No.AD25069101)Guangxi Bagui Scholars Fund。
文摘Crushing waste coral concrete into recycled aggregates to create recycled coral aggregate concrete(RCAC)contributes to sustainable construction development on offshore islands and reefs.To investigate the impact of recycled coral aggregate on concrete properties,this study performed a comprehensive analysis of the physical properties of recycled coral aggregate and the basic mechanical properties and microstructure of RCAC.The test results indicate that,compared to coral debris,the crushing index of recycled coral aggregate was reduced by 9.4%,while porosity decreased by 33.5%.Furthermore,RCAC retained the early strength characteristics of coral concrete,with compressive strength and flexural strength exhibiting a notable increase as the water-cement ratio decreased.Under identical conditions,the compressive strength and flexural strength of RCAC were 12.7% and 2.5% higher than coral concrete's,respectively,with porosity correspondingly reduced from 3.13% to 5.11%.This enhancement could be attributed to the new mortar filling the recycled coral aggregate.Scanning electron microscopy(SEM)analysis revealed three distinct interface transition zones within RCAC,with the‘new mortar-old mortar’interface identified as the weakest.The above findings provided a reference for the sustainable use of coral concrete in constructing offshore islands.
基金financially supported by the Natural Science Foundation of Liaoning Province of China(2022-MS-109)the Key Research and Development Program of Liaoning Province(2023JH2/101800045)the Ministry of Science and Technology of the Peoples Republic of China(ZZ2021006).
文摘The Cu-12Fe alloy has attracted significant attention due to its excellent electrical conductivity and electromagnetic shielding capability,high strength,cost-effectiveness,and recyclability.In the present work,the Cu-12Fe alloy strip with the thickness of 2.4 mm was successfully produced by twin-roll strip casting.The microstructure and properties of the Cu-12Fe alloy were tailored by cold rolling and aging treatment.The tensile strength of the as-cast strip is approximately 328 MPa and its elongation is 25%.The Fe phase randomly dispersed in the matrix,and the average size of Fe-rich phase is 2μm.Besides,enrichment of Fe phase is observed in the central layer of the strip,results in the formation of the“sandwich structure”.Moreover,the as-cast strip of Cu-12Fe was directly cold-rolled from 2.4 to 0.12 mm.The directly cold-rolled sample after aging at 450℃for 16 h(ProcessⅠ)shows excellent electrical conductivity of 69.5%IACS,the tensile strength and elongation are 513 MPa and 3.8%,the saturation magnetic flux density is 20.1 emu·g^(-1),and the coercive force is 25.2 Oe.In ProcessⅡ,the as-cast strip firstly cold-rolled to 1.2 mm,then aged at 500℃for 1.5 h,followed by cold rolling to 0.12 mm,finally aged at 450℃for 16 h.The sample after ProcessⅡshows the electrical conductivity of 66.3%IACS,the tensile strength of 533 MPa,an elongation of 3.5%,saturation magnetic flux density of 21.4 emu·g^(-1),and the coercive force of 22.3 Oe.
基金supported by National Natural Science Foundation of China(Grant No.52171032)Hebei Natural Science Foundation(Grant No.E2023501002)Fundamental Research Funds for the Central Universities(Grant No.2024GFYD003)。
文摘High entropy alloys(HEAs)have recently attracted significant attention due to their exceptional mechanical properties and potential applications across various fields.Friction stir welding and processing(FSW/P),as notable solid-state welding and processing techniques,have been proved effectiveness in enhancing microstructures and mechanical properties of HEAs.This review article summarizes the current status of FSW/P of HEAs.The welding materials and conditions used for FSW/P in HEAs are reviewed and discussed.The effects of FSW/P on the evolutions of grain structure,texture,dislocation,and secondary phase for different HEAs are highlighted.Furthermore,the influences of FSW/P on the mechanical properties of various HEAs are analyzed.Finally,potential applications,challenges,and future directions of FSW/P in HEAs are forecasted.Overall,FSW/P enable to refine grains of HEAs through dynamic recrystallization and to activate diverse deformation mechanisms of HEAs through tailoring phase structures,thereby significantly improving the strength,hardness,and ductility of both single-and dual-phase HEAs.Future progress in this field will rely on comprehensive optimization of processing parameters and alloy composition,integration of multi-scale modeling with advanced characterization for in-depth exploration of microstructural mechanisms,systematic evaluation of functional properties,and effective bridging of the gap between laboratory research and industrial application.The review aims to provide an overview of recent advancements in the FSW/P of HEAs and encourage further research in this area.
基金financially supported by the National Key Research and Development Program of China(No.2021YFB3701000)the National Natural Science Foundation of China(Nos.52471118,52101125,U2037601,and U21A2048)Young Elite Scientists Sponsorship Program by CAST,China(No.2022QNRC001)。
文摘The dependence of shrinkage porosities on microstructure characteristics of Mg−12Al alloy was investigated.The distribution,morphology,size,and number density of shrinkage porosities were analyzed under different cooling rates.The relationship between shrinkage porosities and microstructure characteristics was discussed in terms of temperature conditions,feeding channel characteristics,and feeding capacity.Further,the feeding behavior of the residual liquid phase in the solid skeleton was quantified by introducing permeability.Results show a strong correlation between the solid microstructure skeleton and shrinkage porosity characteristics.An increase in permeability corresponds to a declining number density of shrinkage porosities.This study aims to provide a more complete understanding how to reduce shrinkage porosities by controlling microstructure characteristics.
文摘This study investigated enhancing the wear resistance of Ti6Al4V alloys for medical applications by incorporating Ti C nanoreinforcements using advanced spark plasma sintering(SPS). The addition of up to 2.5wt% Ti C significantly improved the mechanical properties, including a notable 18.2% increase in hardness(HV 332). Fretting wear tests against 316L stainless steel(SS316L) balls demonstrated a 20wt%–22wt% reduction in wear volume in the Ti6Al4V/Ti C composites compared with the monolithic alloy. Microstructural analysis revealed that Ti C reinforcement controlled the grain orientation and reduced the β-phase content, which contributed to enhanced mechanical properties. The monolithic alloy exhibited a Widmanstätten lamellar microstructure, while increasing the Ti C content modified the wear mechanisms from ploughing and adhesion(0–0.5wt%) to pitting and abrasion(1wt%–2.5wt%). At higher reinforcement levels, the formation of a robust oxide layer through tribo-oxide treatment effectively reduced the wear volume by minimizing the abrasive effects and plastic deformation. This study highlights the potential of SPS-mediated Ti C reinforcement as a transformative approach for improving the performance of Ti6Al4V alloys, paving the way for advanced medical applications.
基金supported by the National Natural Science Foundation of China (Nos. 52075449, 51975480)。
文摘The dissimilar 2B06 and 7B04 Al alloy joints were prepared by refill friction stir spot welding(RFSSW),and the microstructural evolution and corrosion behavior of the joints were investigated.Based on microstructural analysis,the welded joints exhibit distinct microstructural zones,including the stir zone(SZ),thermomechanically affected zone(TMAZ),and heat-affected zone(HAZ).The grain size of each zone is in the order of HAZ>TMAZ>SZ.Notably,the TMAZ and HAZ contain significantly larger secondary-phase particles compared to the SZ,with particle size in the HAZ increasing at higher rotational speeds.Electrochemical tests indicate that corrosion susceptibility follows the sequence of HAZ>TMAZ>SZ>BM,with greater sensitivity observed at increased rotational speeds.Post-corrosion mechanical performance degradation primarily arises from crevice corrosion at joint overlaps,but not from the changes in the microstructure.
基金supported by the National Key Research and Development Program of China(No.2016YFB1100103)the Key Discipline and Major Project of Dalian Science and Technology Innovation Foundation(No.2020JJ25CY004).
文摘A novel Ti-6.38Al-3.87V-2.43Mo alloy was designed with a cluster formula of 12[Al-Ti12](V0.75Mo0.25Ti2)+4[Al-Ti12](Al3)by replacing Ti with Mo/V on the basis of the Ti-Al congruent alloy.The effects of laser power and scanning speed on the molten pool size,surface roughness,relative density,microstructure,and micro-hardness of single-track and bulk Ti-6.38Al-3.87V-2.43Mo samples prepared via laser additive manufacturing(LAM)were investigated.The results show that processing parameters significantly affect the formability,microstructure,and micro-hardness of the alloy.With decreasing laser power from 1,900 W to 1,000 W,the relative density is decreased from 99.86%to 90.91%due to the increase of lack-of-fusion;however,with increasing scanning speed,the relative density does not change significantly,but exceeds 99%.In particular,Ti-6.38Al-3.87V-2.43Mo samples of single-track and bulk exhibit a good formability under an input laser power of 1,900 W and a scanning speed of 8 mm·s_(-1),and display the lowest surface roughness(Ra=13.33μm)and the highest relative density(99.86%).Besides,the microstructure of LAM Ti-6.38Al-3.87V-2.43Mo alloy coarsens with increasing laser power or decreasing scanning speed due to the greater input energy reducing the cooling rate.The coarsening of the microstructure decreases the microhardness of the alloy.
基金Project(50235030) supported by the National Natural Science Foundation of China Project(G1999065009) supported by the National Basic Research Program of China Project(2003AA331130) supported by the Hi-tech Research and Development Program of China
文摘The n-SiO2/Ni composite electro-brush plating coating was prepared on the 1045 steel substrate. SEM and TEM were utilized to analyze the surface and cross-section morphologies or the microstructures of the composite coating before and after heat treatment, as well as a micro-hardness tester was used to measure the micro-hardness before and after heat treatment. The results show that the entrance of nano SiO2 particles into composite coating makes the micro-hardness higher. After heat treatment, due to the obstruction to growth of Ni crystals from nano particles, the composite coating still possesses a higher micro-hardness than that of common Ni-base coating.
基金Funded by the National Natural Science Foundation of China(Nos.U23A20672,52171270,51879168)the PI Project of Southern Marine Science and Engineering Guangdong Laboratory(Guangzhou)(GML20240001,GML2024009)。
文摘We have described in detail the effects of nano-SiO_(2),nano-CaCO_(3),carbon nanotubes,and nano-Al_(2)O_(3) on geopolymer concrete from the perspectives of macro mechanics and microstructure.The existing research results show that the mechanism of nano-materials on geopolymer concrete mainly includes the filling effect,nucleation effect,and bridging effect,the appropriate amount of nano-materials can be used as fillers to reduce the porosity of geopolymer concrete,and can also react with Ca(OH)2 to produce C-S-H gel,thereby improving the mechanical properties of geopolymer concrete.The optimum content of nano-SiO_(2) is between 1.0%and 2.0%.The optimum content of nano-CaCO_(3) is between 2.0%and 3.0%.The optimum content of carbon nanotubes is between 0.1%and 0.2%.The optimum content of nano-Al_(2)O_(3) is between 1.0%and 2.0%.The main problems existing in the research and application of nanomaterial-modified geopolymer concrete are summarized,which lays a foundation for the further application of nanomaterial in geopolymer concrete.
基金Natural Science Foundation of Shandong Province of China(ZR2023QE193)。
文摘The microstructures and mechanical properties of Al-8.3Zn-3.3Cu-2.2Mg alloys prepared via hot extrusion and liquid forging methods were investigated.Results show that based on DEFORM simulation analysis,the optimal hot extrusion parameters are determined as ingot initial temperature of 380°C and extrusion speed of 3 mm/s.The hot-extruded aluminum alloy after T6 heat treatment presents superior mechanical properties with yield strength of 519.6 MPa,ultimate tensile strength of 582.1 MPa,and elongation of 11.0%.Compared with the properties of gravity-cast and liquid-forged alloys,the yield strength of hot-extruded alloy increases by 30.8%and 4.9%,and the ultimate tensile strength improves by 43.5%and 10.2%,respectively.The significant improvement in tensile strength of the hot-extruded alloys is attributed to the elimination of casting defects and the refinement of matrix grain and eutectic phases.In addition,the hot-extruded alloy demonstrates superior plasticity compared with the liquid-forged alloy.This is because severe plastic deformation occurs during hot extrusion,which effectively breaks and disperses the eutectic phases,facilitating the dissolution and precipitation of the second phases and inhibiting the microcrack initiation.
文摘In-situ formed high Mn steel coating reinforced by carbides was formed by laser surface alloying(LSA).Laser alloyed layers on 1Cr18Ni9Ti steel with Mn+W_(2)C(specimen A),Mn+NiWC(specimen B)and Mn+SiC(specimen C)powders were fabricated to improve the wear and corrosion behavior of 1Cr18Ni9Ti steel blades in high speed mixers.Microstructure evolution,phases,element distribution,microhardness,wear and corrosion behavior of the laser alloyed layers were investigated.Results indicated that high Mn steel matrix composites with undissolved W_(2)C,WC and other in-situ formed carbides were formed by LSA with Mn+W_(2)C and Mn+NiWC while SiC totally dissolved into the high Mn matrix when adding Mn+SiC.Ni as the binding phase in Ni-WC powder decreased the crack sensitivity of the alloyed layer as compared with the addition of W_(2)C powder.An improvement in average microhardness was achieved in the matrix in specimen A,B and C,with the value of 615,602 and 277 HV_(0.5),while that of the substrate was 212 HV_(0.5).The increase of microhardness,wear and corrosion resistance is highly corelated to microstructure,formed phases,type and content of carbides,micro-hardness and toughness of the alloyed layers.