Continuous cooling transformation of a low carbon microalloyed steel was investigated after it was subjected to the simulation welding thermal cycle process and the interrupted cooling test. Microstructure observation...Continuous cooling transformation of a low carbon microalloyed steel was investigated after it was subjected to the simulation welding thermal cycle process and the interrupted cooling test. Microstructure observation was performed by optical microscopy and transmission electron microscopy. On the basis of the dilatometric data and microstructure observation, the continuous cooling transformation （CCT） diagram was determined, which showed that the main microstructure changes from a mixture of lath martensite and bainitic ferrite to full granular bainite with the increase in the cooling time t8/5 from 10 to 600 s, accompanied with a decrease in the microhardness. The interrupted cooling test confirmed that the bainitic ferrite can form attached to grain boundaries at the beginning of transformation even if the final microstructure contains a mixture of granular bainite and bainitic ferrite.展开更多
基金support of Shenyang Key Laboratory of Construction Project(Grant No. F12-256-1-00)Science Foundation for the Excellent Youth Scholars of Ministry of Education of China(Grant No. 90403006)
文摘Continuous cooling transformation of a low carbon microalloyed steel was investigated after it was subjected to the simulation welding thermal cycle process and the interrupted cooling test. Microstructure observation was performed by optical microscopy and transmission electron microscopy. On the basis of the dilatometric data and microstructure observation, the continuous cooling transformation （CCT） diagram was determined, which showed that the main microstructure changes from a mixture of lath martensite and bainitic ferrite to full granular bainite with the increase in the cooling time t8/5 from 10 to 600 s, accompanied with a decrease in the microhardness. The interrupted cooling test confirmed that the bainitic ferrite can form attached to grain boundaries at the beginning of transformation even if the final microstructure contains a mixture of granular bainite and bainitic ferrite.