Adiabatic shear behavior and the corresponding mechanism of TiB2/Al composites were researched by split Hopkinson pressure bar （SHPB）.Results show that the flow stresses of the TiB2/Al composites exhibit softening t...Adiabatic shear behavior and the corresponding mechanism of TiB2/Al composites were researched by split Hopkinson pressure bar （SHPB）.Results show that the flow stresses of the TiB2/Al composites exhibit softening tendency with the increasing of strain rates. All the composites fail in splitting and cutting with a 45 degree, and the phase transformed bands of molten aluminum are found on the adiabatic shear layers. The deformation behavior and shear localization of the TiB2/Al composites specimens were simulated by finite element code MSC.Marc. The Johnson-Cook model was used to describe the thermo-viscoplastic response of the specimen material. There was unanimous between the numerical result and the experimental result on the location of the adiabatic shear band. From the numerical simulation and experiment, it was concluded that the instantaneous failure of the composite was ascribed due to the local low strength area where the formation of adiabatic shear band was, and the stress condition had significant effect on the initiation and propagation of adiabatic shear band （ASB）.展开更多
The metallic glass matrix composites（MGMCs）and bulk metallic glasses（BMGs）were studied by statistical analysis during plastic deformation at the strain rates of 2×10^-2,2×10^-3,and 2×10^-4 s^-1,resp...The metallic glass matrix composites（MGMCs）and bulk metallic glasses（BMGs）were studied by statistical analysis during plastic deformation at the strain rates of 2×10^-2,2×10^-3,and 2×10^-4 s^-1,respectively.No serration events occur in both MGMCs and BMGs during compression tests at the strain rate of 2×10^-2 s^-1.When deformed at the strain rate of 2×10^-3 s^-1,the BMG displays a larger plasticity,which is due to the larger serration events followed by a series of small serrations caused by the continuous movement of free volume.The amplitudes and elastic-energy densities increase with increasing the strain rates owing to many serrations in MGMCs.It is deduced that the Young′s modulus decreases from the normalized stress drop and fluctuations are observed on stressstrain curves,which is attributed to a lower coefficient according to the stick-slip model.展开更多
基金the National Engineering Research Center Open Fund(No.2011007B)Natural Science Foundation of GuangDong Province(No.10451064101004631)
文摘Adiabatic shear behavior and the corresponding mechanism of TiB2/Al composites were researched by split Hopkinson pressure bar （SHPB）.Results show that the flow stresses of the TiB2/Al composites exhibit softening tendency with the increasing of strain rates. All the composites fail in splitting and cutting with a 45 degree, and the phase transformed bands of molten aluminum are found on the adiabatic shear layers. The deformation behavior and shear localization of the TiB2/Al composites specimens were simulated by finite element code MSC.Marc. The Johnson-Cook model was used to describe the thermo-viscoplastic response of the specimen material. There was unanimous between the numerical result and the experimental result on the location of the adiabatic shear band. From the numerical simulation and experiment, it was concluded that the instantaneous failure of the composite was ascribed due to the local low strength area where the formation of adiabatic shear band was, and the stress condition had significant effect on the initiation and propagation of adiabatic shear band （ASB）.
基金Item Sponsored by National Natural Science Foundation of China(51371122,51471025,51210105006)Program for Innovative Talents of Higher Learning Institutions of Shanxi of China(2013)Youth Natural Science Foundation of Shanxi Province of China(2015021005)
文摘The metallic glass matrix composites（MGMCs）and bulk metallic glasses（BMGs）were studied by statistical analysis during plastic deformation at the strain rates of 2×10^-2,2×10^-3,and 2×10^-4 s^-1,respectively.No serration events occur in both MGMCs and BMGs during compression tests at the strain rate of 2×10^-2 s^-1.When deformed at the strain rate of 2×10^-3 s^-1,the BMG displays a larger plasticity,which is due to the larger serration events followed by a series of small serrations caused by the continuous movement of free volume.The amplitudes and elastic-energy densities increase with increasing the strain rates owing to many serrations in MGMCs.It is deduced that the Young′s modulus decreases from the normalized stress drop and fluctuations are observed on stressstrain curves,which is attributed to a lower coefficient according to the stick-slip model.