To increase the adhesion strength between the coating and the substrate, sintered Ti（C,N）-based cermets were selected and deposited with monolayer TiN using a multiarc ion-plating technique; subsequently, hot isosta...To increase the adhesion strength between the coating and the substrate, sintered Ti（C,N）-based cermets were selected and deposited with monolayer TiN using a multiarc ion-plating technique; subsequently, hot isostatic pressing （HIPhag） treatment was performed at 1000℃ using nitrogen pressure up to 110 MPa. The mechanical properties of cermets after a coating process and subsequent HIPing treatment have been evaluated with respect to the hardness, the residual stress, and the coating adhesion. The results show that atter the HIPing process, there was a higher increase ha critical load ha the TiN-coated cermets with lower surface roughness compared with those with higher surface roughness. In all cases, the residual stress was found to be compressive. The effects of substrate surface roughness and posttreatment on the adhesion strength of the coatings were thus investigated. It was also fotmd that the HIPing posttreatment process is well suited for hacreasing the adhesion strength between the coating and the substrate.展开更多
The corrosion behavior of tantalum and its nitrides in stirring NaOHsolutions was researched by potentiostatic method, cyclic voltammetry and XPS. The results showedthat the corrosion products were composed of Ta_2O_5...The corrosion behavior of tantalum and its nitrides in stirring NaOHsolutions was researched by potentiostatic method, cyclic voltammetry and XPS. The results showedthat the corrosion products were composed of Ta_2O_5 and NaTaO_3. The corrosion reaction formula oftantalum and its nitrides was written according to cyclic volt-ampere curves. The electric chargetransfer coefficient and the electric charge transfer number were calculated展开更多
Based on the phase equilibrium calculation of the Ti-Al-N ternary system, the interfacial reactions and the phase formation sequences between different types of joints, （Ti matrix）/（AlN particles）, （Ti particles...Based on the phase equilibrium calculation of the Ti-Al-N ternary system, the interfacial reactions and the phase formation sequences between different types of joints, （Ti matrix）/（AlN particles）, （Ti particles）/（AlN plate）, and （Ti plate）/（AlN plate）, were analyzed theoretically under the reported experimental conditions, Different phase formation sequences for the three kinds of Ti/AlN joints were obtained, It proved that the different phase sequences of both the phase formation sequences and the apparent spatial phase sequences are dominated by the relative amounts and the distribution of the two pairs in the diffusion couples, The theoretical prediction can explain the experimental observations well.展开更多
Ta/NiFe/Ta ultrathin films with and without nano-oxide layers （NOLs） were prepared by magnetron sputtering followed by a vacuum annealing process. The influence of NOLs on the magnetoresistance （MR） ratio of ultra...Ta/NiFe/Ta ultrathin films with and without nano-oxide layers （NOLs） were prepared by magnetron sputtering followed by a vacuum annealing process. The influence of NOLs on the magnetoresistance （MR） ratio of ultrathin permalloy films was studied. The results show that the influence of grain size and textures on the MR ratio becomes weak when the thickness of the NiFe layer is below 15 nm. A higher MR ratio was observed for the thinner （〈 15 nm） NiFe film with NOLs. The MR ratio of a 10 nm NiFe film can be remarkably enhanced by NOLs. The enhanced MR ratio for these ultrathin films can be attributed to the enhanced specular reflection of conduction electrons.展开更多
The barrel lifes of three small caliber rifles were tested by using the propellant with nanomaterial and the standard propellant respectively. The test results show that the service life increases observably due to ad...The barrel lifes of three small caliber rifles were tested by using the propellant with nanomaterial and the standard propellant respectively. The test results show that the service life increases observably due to adding nanomaterial to the propellant. Then, the influence of the nanomaterial on the tube was researched by splitting the two barrels tested and detecting their inner surfaces. It was found that the erosion of the barrel bore is reduced observably by using the propellant with nanomaterial. And it makes the volume and the size of the gun chamber change less. Therefore, the barrel life can be prolonged by adding the nanomaterial in the propellant.展开更多
The combined quadratic orthogonal regression method of experiment design wasemployed to explore the effects of process parameters of plasma nitriding of tantalum such as totalpressure, temperature and original hydroge...The combined quadratic orthogonal regression method of experiment design wasemployed to explore the effects of process parameters of plasma nitriding of tantalum such as totalpressure, temperature and original hydrogen molar fraction on the hardness, roughness and structureof nitriding surfaces. The regression equations of hardness, roughness and structure were givenaccording to the results of regression and statistic analysis. And the diffusion activation energyof nitrogen in tantalum on plasma nitriding conditions was calculated according to the experimentaldata of hardness of plasma-nitriding of tantalum vs time and temperature. The diffusion activationenergy calculated belongs to (155.49 +- 10.51) kJ/mol (783-983 K).展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No. 50074017).
文摘To increase the adhesion strength between the coating and the substrate, sintered Ti（C,N）-based cermets were selected and deposited with monolayer TiN using a multiarc ion-plating technique; subsequently, hot isostatic pressing （HIPhag） treatment was performed at 1000℃ using nitrogen pressure up to 110 MPa. The mechanical properties of cermets after a coating process and subsequent HIPing treatment have been evaluated with respect to the hardness, the residual stress, and the coating adhesion. The results show that atter the HIPing process, there was a higher increase ha critical load ha the TiN-coated cermets with lower surface roughness compared with those with higher surface roughness. In all cases, the residual stress was found to be compressive. The effects of substrate surface roughness and posttreatment on the adhesion strength of the coatings were thus investigated. It was also fotmd that the HIPing posttreatment process is well suited for hacreasing the adhesion strength between the coating and the substrate.
文摘The corrosion behavior of tantalum and its nitrides in stirring NaOHsolutions was researched by potentiostatic method, cyclic voltammetry and XPS. The results showedthat the corrosion products were composed of Ta_2O_5 and NaTaO_3. The corrosion reaction formula oftantalum and its nitrides was written according to cyclic volt-ampere curves. The electric chargetransfer coefficient and the electric charge transfer number were calculated
基金The authors would like to express their appreciation to the Royal Institute of Technology Sweden for supplying the Thermo-Calc software.This work was financially supported by the National Natural Science Foundation of China (Nos.50731002 and 50671009)the Doctorate Program of the Ministry of Education of China (No.20060008015).
文摘Based on the phase equilibrium calculation of the Ti-Al-N ternary system, the interfacial reactions and the phase formation sequences between different types of joints, （Ti matrix）/（AlN particles）, （Ti particles）/（AlN plate）, and （Ti plate）/（AlN plate）, were analyzed theoretically under the reported experimental conditions, Different phase formation sequences for the three kinds of Ti/AlN joints were obtained, It proved that the different phase sequences of both the phase formation sequences and the apparent spatial phase sequences are dominated by the relative amounts and the distribution of the two pairs in the diffusion couples, The theoretical prediction can explain the experimental observations well.
基金supported by the National Science Foundation of China (Nos.50671008,50871014,and 50831002)
文摘Ta/NiFe/Ta ultrathin films with and without nano-oxide layers （NOLs） were prepared by magnetron sputtering followed by a vacuum annealing process. The influence of NOLs on the magnetoresistance （MR） ratio of ultrathin permalloy films was studied. The results show that the influence of grain size and textures on the MR ratio becomes weak when the thickness of the NiFe layer is below 15 nm. A higher MR ratio was observed for the thinner （〈 15 nm） NiFe film with NOLs. The MR ratio of a 10 nm NiFe film can be remarkably enhanced by NOLs. The enhanced MR ratio for these ultrathin films can be attributed to the enhanced specular reflection of conduction electrons.
文摘The barrel lifes of three small caliber rifles were tested by using the propellant with nanomaterial and the standard propellant respectively. The test results show that the service life increases observably due to adding nanomaterial to the propellant. Then, the influence of the nanomaterial on the tube was researched by splitting the two barrels tested and detecting their inner surfaces. It was found that the erosion of the barrel bore is reduced observably by using the propellant with nanomaterial. And it makes the volume and the size of the gun chamber change less. Therefore, the barrel life can be prolonged by adding the nanomaterial in the propellant.
文摘The combined quadratic orthogonal regression method of experiment design wasemployed to explore the effects of process parameters of plasma nitriding of tantalum such as totalpressure, temperature and original hydrogen molar fraction on the hardness, roughness and structureof nitriding surfaces. The regression equations of hardness, roughness and structure were givenaccording to the results of regression and statistic analysis. And the diffusion activation energyof nitrogen in tantalum on plasma nitriding conditions was calculated according to the experimentaldata of hardness of plasma-nitriding of tantalum vs time and temperature. The diffusion activationenergy calculated belongs to (155.49 +- 10.51) kJ/mol (783-983 K).