The morphology,crystal structure,and electrochemical performance of spent LiFePO_(4)(S-LFP)are recovered by one-step low-temperature solid phase sintering.After sintering at 550℃ for 3 h,the secondary particle size d...The morphology,crystal structure,and electrochemical performance of spent LiFePO_(4)(S-LFP)are recovered by one-step low-temperature solid phase sintering.After sintering at 550℃ for 3 h,the secondary particle size distribution of regenerated LiFePO4(R-LFP)becomes narrower,and the D_(50) is reduced from 5.6 to 2.3μm.In addition,the content of Li-Fe antisite defect is reduced from 5.73%to 1.20%,and the F is doped to O(2)site in the structure of R-LFP.Moreover,a coating layer comprising carbon and LiF is formed on the surface of R-LFP because of the decomposition of PVDF.Therefore,the R-LFP demonstrates exceptional Li+diffusion dynamics and conductivity,which delivers a high discharge capacity of 157.3 mA·h/g at 0.1C.And it maintains 92%of its initial capacity after 500 cycles at 1C.展开更多
Porous ceramics were prepared with spodumene flotation talings(SFT),kaolin and low-melting point glass(LPG)powder,whose pores were formed by the chemical reaction of hydrogen peroxide(H_(2)O_(2)).LPG was used to reduc...Porous ceramics were prepared with spodumene flotation talings(SFT),kaolin and low-melting point glass(LPG)powder,whose pores were formed by the chemical reaction of hydrogen peroxide(H_(2)O_(2)).LPG was used to reduce the sintering temperature of porous ceramics and kaolin was used to realize the adsorption to methylene blue(MB)of porous ceramics.The average flexural strength,compressive strength,apparent porosity,water absorption and maximum MB adsorption capacity were 5.60 MPa,4.66 MPa,52.27%,44.32%and 0.7 mg/g,respectively.Moreover,the results of orthogonal experiments present that the sintering temperature and the dosage of H_(2)O_(2)had great influence on the mechanical properties and apparent porosity of porous ceramics,respectively.The main reason for the improvement of mechanical properties of porous ceramics was that LPG gradually became soft with increasing the sintering temperature,which made the mineral particles adhere to each other closely.Kaolinite was not completely converted into metakaolin at 550℃,which might be the main reason why porous ceramics had adsorption properties.展开更多
The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） con...The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） considerably facilitated the densification of Ba2Ti3Nb4O18 ceramics.Appropriate addition of H3BO3 （ 〈3.5 wt%） remarkably improved the microwave dielectric properties of ceramics.The addition of H3BO3 and CuO successfully reduced the sintering temperature of Ba2Ti3Nb4O18 ceramics from 1300 to 1050 ℃.Ba2Ti3Nb4O18 ceramics sintered at 1 050 ℃ for 4 h with the addition of 1.0 wt% CuO and 3.5 wt% H3BO3 exhibited good microwave dielectric properties：er=33.74,Q？f=13 812 GHz,and tf=-5.35 ppm/°C at about 5.0 GHz.展开更多
We studied the effects of sintering temperature on FeCuCo based pre-alloyed powder for diamond bits.The FeCuCo composite was fabricated by co-precipitation method.With the addition of tungsten carbide（WC）,sintering ...We studied the effects of sintering temperature on FeCuCo based pre-alloyed powder for diamond bits.The FeCuCo composite was fabricated by co-precipitation method.With the addition of tungsten carbide（WC）,sintering under different temperatures was investigated.Mechanical properties of the FeCuCo based matrix were systematically studied.The structure of the composite was evaluated by X-ray diffraction（XRD） and scanning electron microscope（SEM） was used to analyze the surface of the powder and matrix.The suitable sintering temperature was determined through differential scanning calorimeter（DSC）.Micro drilling experiments were performed,and 820 ℃ was identified to be the ideal sintering temperature,at which the matrix shows the best mechanical properties and drilling performance.展开更多
A spherical Fe matrix composite powder containing a high volume fraction （82vo1%） of fine TiC reinforcement was produced using a novel process combining in situ synthesis and plasma techniques. The composite powder ...A spherical Fe matrix composite powder containing a high volume fraction （82vo1%） of fine TiC reinforcement was produced using a novel process combining in situ synthesis and plasma techniques. The composite powder exhibited good sphericity and a dense structure, and the fine sub-micron TiC particles were homogeneously distributed in the α-Fe matrix. A TiC-Fe cermet was prepared from the as-prepared spherical composite powder using powder metallurgy at a low sintering temperature; the product exhibited a hardness of HRA 88.5 and a flexural strength of 1360 MPa. The grain size of the fine-grained TiC and special surface structure of the spherical powder played the key roles in the fabrication process.展开更多
The influences of BaCu(B2O5)(BCB)addition on sintering,microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry,scanning electron microscopy and microwave ...The influences of BaCu(B2O5)(BCB)addition on sintering,microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry,scanning electron microscopy and microwave dielectric measurements.The experimental results show that a small amount of BaCu(B2O5)addition can effectively reduce the sintering temperature to 900℃,and induce only a limited degradation of the microwave dielectric properties.Typically,the best microwave dielectric properties of er24.5,Q×f=24622 GHz,rf=4.2×10-6℃-1 are obtained for 1.0%BCB-doped Li2MgTi3O8 ceramics sintered at 900℃for 3 h.The BCB-doped Li2MgTi3O8 ceramics can be compatible with Ag electrode,which may be a strong candidate for low temperature co-fired ceramics applications.展开更多
In this study,a trifunctional strategy was developed to prepare a confined Ni-based catalyst(Ni-CeO_(2)@SiO_(2))for dry reforming of methane(DRM)of two main greenhouse gases-CO_(2)and CH_(4).The Ni-CeO_(2)@SiO_(2)cata...In this study,a trifunctional strategy was developed to prepare a confined Ni-based catalyst(Ni-CeO_(2)@SiO_(2))for dry reforming of methane(DRM)of two main greenhouse gases-CO_(2)and CH_(4).The Ni-CeO_(2)@SiO_(2)catalyst was fabricated by utilizing the confinement effect of the SiO_(2)shell and the synergistic interaction between Ni-Ce and the decoking effect of CeO_(2).The catalysts were systematically characterized via X-ray diffraction,N_(2 )adsorption/desorption,transmission electron microscopy,energy dispersive X-ray spectroscopy,hydrogen temperature reduction and desorption set by program,oxygen temperature program desorption,Raman spectroscopy,thermogravimetric analysis,and in situ diffuse reflectance infrared Fourier transform spectroscopy measurements to reveal their physicochemical properties and reaction mechanism.The Ni-CeO_(2)@SiO_(2)catalyst exhibited higher activity and stability than the catalyst synthesized via the traditional impregnation method.In addition,no carbon deposition was detected over Ni-CeO_(2)@SiO_(2)after a 100 h durability test at 800℃,and the average particle size of Ni nanoparticles(NPs)in the catalyst increased from 5.01 to 5.77 nm.Remarkably,Ni-CeO_(2)@SiO_(2)also exhibited superior low-temperature stability;no coke deposition was observed when the catalyst was reacted at 600℃ for 20 h.The high coking and sintering resistance of this confined Ni-based DRM catalyst can be attributed to its trifunctional effect.The trifunctional strategy developed in this study could be used as a guideline to design other high-performance catalysts for CO_(2)and CH4 dry forming and accelerate their industrialization.展开更多
Low-temperature sintering(LTS)experiments of UO2 pellets and their results were reported.Moreover,a routine process of LTS for UO2 pellets was primarily established.Being sintered at 1 400 ℃ for 3 h in a partially-ox...Low-temperature sintering(LTS)experiments of UO2 pellets and their results were reported.Moreover,a routine process of LTS for UO2 pellets was primarily established.Being sintered at 1 400 ℃ for 3 h in a partially-oxidative atmosphere,the relative density of the pellet can be up to around 94%.Pellets with such a high density are of benefit for following-up reduction-sintering processes.Orthogonal test indicates that the importance of factors affecting the density decreases in the sequence of partial-oxidative sintering temperature and time,reduction-sintering time and temperature,and sintering atmosphere.It is found that it is helpful to introducing a small amount of water vapor into the sintering atmosphere during the latter stage.It is believed that it is the key factor to raise the O/U ratio of original powder in order to improve the properties of the low-temperature sintered pellets.展开更多
In order to explore the effects of CaO,lignite dust and sawdust on the drying characteristics ofmunicipal sludge at different concentrations,a three-factor three-level regression experiment was carried out based on th...In order to explore the effects of CaO,lignite dust and sawdust on the drying characteristics ofmunicipal sludge at different concentrations,a three-factor three-level regression experiment was carried out based on the results of thermogravimetric experiment and single factor experiment.By fitting three common mathematical models,the Page model with the highest fitting degree was selected to determine the most suitable mathematical model to describe the municipal sludge drying process.In addition,the Box-Behnken design principle in the response surface method was used to analyze the interaction of three factors on the drying characteristics of municipal sludge.The results of the study show that below 100℃is the optimal drying temperature range for municipal sludge.The results of single factor experiments showed that the order of influence of the three factors on sludge drying time was CaO concentration>sawdust concentration>lignite dust concentration.In the single factor experiment,the optimal process parameterswere CaOconcentration 3%,lignite powder concentration 7%,and sawdust concentration 7%.In themulti-factor interaction analysis,the interaction between CaO and sawdust had the most significant effect on the reduction of drying time,and the order of influence was as follows:CaO interaction with sawdust>lignite dust interaction with sawdust>CaO interaction with lignite powder.Further analysis showed that the optimal process ratio was 3%CaO concentration and 3%sawdust concentration.展开更多
Lithium-ion batteries(LIBs),while dominant in energy storage due to high energy density and cycling stability,suffer from severe capacity decay,rate capability degradation,and lithium dendrite formation under low-temp...Lithium-ion batteries(LIBs),while dominant in energy storage due to high energy density and cycling stability,suffer from severe capacity decay,rate capability degradation,and lithium dendrite formation under low-temperature(LT)operation.Therefore,a more comprehensive and systematic understanding of LIB behavior at LT is urgently required.This review article comprehensively reviews recent advancements in electrolyte engineering strategies aimed at improving the low-temperature operational capabilities of LIBs.The study methodically examines critical performance-limiting mechanisms through fundamental analysis of four primary challenges:insufficient ionic conductivity under cryogenic conditions,kinetically hindered charge transfer processes,Li+transport limitations across the solidelectrolyte interphase(SEI),and uncontrolled lithium dendrite growth.The work elaborates on innovative optimization approaches encompassing lithium salt molecular design with tailored dissociation characteristics,solvent matrix optimization through dielectric constant and viscosity regulation,interfacial engineering additives for constructing low-impedance SEI layers,and gel-polymer composite electrolyte systems.Notably,particular emphasis is placed on emerging machine learning-guided electrolyte formulation strategies that enable high-throughput virtual screening of constituent combinations and prediction of structure-property relationships.These artificial intelligence-assisted rational design frameworks demonstrate significant potential for accelerating the development of next-generation LT electrolytes by establishing quantitative composition-performance correlations through advanced data-driven methodologies.展开更多
This study focused on improving the cathode performance of Ba_(0.6)Sr_(0.4)Co_(0.85)Nb_(0.15)O_(3-δ)(BSCN)-based perovskite materials through molybdenum(Mo)doping.Pure BSCN and Mo-modified-BSCN—Ea_(0.6)Sr_(0.4)Co_(0...This study focused on improving the cathode performance of Ba_(0.6)Sr_(0.4)Co_(0.85)Nb_(0.15)O_(3-δ)(BSCN)-based perovskite materials through molybdenum(Mo)doping.Pure BSCN and Mo-modified-BSCN—Ea_(0.6)Sr_(0.4)Co_(0.85)Nb_(0.1)Mo_(0.05)O_(3-δ)(B S CNM_(0.05)),Ba_(0.6)Sr_(0.4)Co_(0.85)Nb_(0.05)Mo_(0.1)O_(3-δ)(BSCNM_(0.1)),and Ba_(0.6)Sr_(0.4)Co_(0.85)Mo_(0.15)O_(3-δ)(BSCM)—with Mo doping contents of 5mol%,10mol%,and15mol%,respectively,were successfully prepared using the sol-gel method.The effects of Mo doping on the crystal structure,conductivity,thermal expansion coefficient,oxygen reduction reaction(ORR)activity,and electrochemical performance were systematically evaluated using X-ray diffraction analysis,thermally induced characterization,electrochemical impedance spectroscopy,and single-cell performance tests.The results revealed that Mo doping could improve the conductivity of the materials,suppress their thermal expansion effects,and significantly improve the electrochemical performance.Surface chemical state analysis using X-ray photoelectron spectroscopy revealed that 5mol%Mo doping could facilitate a high adsorbed oxygen concentration leading to enhanced ORR activity in the materials.Density functional theory calculations confirmed that Mo doping promoted the ORR activity in the materials.At an operating temperature of 600℃,the BSCNM_(0.05)cathode material exhibited significantly enhanced electrochemical impedance characteristics,with a reduced area specific resistance of 0.048Ω·cm~2,which was lower than that of the undoped BSCN matrix material by 32.39%.At the same operating temperature,an anode-supported single cell using a BSCNM_(0.05)cathode achieved a peak power density of 1477 mW·cm^(-2),which was 30.71%,56.30%,and 171.50%higher than those of BSCN,BSCNM_(0.1),and B SCM,respectively.The improved ORR activity and electrochemical performance of BSCNM_(0.05)indicate that it can be used as a cathode material in low-temperature solid oxide fuel cells.展开更多
Zirconia-toughened alumina(ZTA)ceramics have attracted much attention as electronic package substrate materials because of their excellent mechanical properties and chemical stability.The high sintering temperatures o...Zirconia-toughened alumina(ZTA)ceramics have attracted much attention as electronic package substrate materials because of their excellent mechanical properties and chemical stability.The high sintering temperatures of ZTA ceramics restrict their multilayer co-firing with copper electrodes for low-temperature co-fired ceramic(LTCC)applications.To achieve a balance between good properties and low sintering temperatures,this work proposes CuO-TiO_(2)-Nb_(2)O_(5)(CTN)composite oxide sintering aids for ZTA ceramics to obtain a novel glass-free LTCC material.A low-temperature densification mechanism based on multiphase synergy and interfacial reactions is revealed.The results show that the sintering temperature of ZTA ceramics doped with 5 wt% CTN can be significantly reduced to 1050℃,resulting in high thermal conductivity(18.7 W/(m·K)),high bending strength(405 MPa),and low dielectric loss(9.97×10^(−4)@11.97 GHz).The co-firing compatibility with a multilayer copper inner electrode is also demonstrated.This work overcomes the traditional trade-off between low-temperature sintering and high performance in glass-free LTCC materials and provides a new strategy for the design and development of multilayer ceramic substrates with copper inner electrodes.展开更多
With the enormous growth in the capacity of electrical equipment,power semi-conductor devices are developing rapidly towards larger size and higher capacity.To suppress the thermal resistance and achieve efficient hea...With the enormous growth in the capacity of electrical equipment,power semi-conductor devices are developing rapidly towards larger size and higher capacity.To suppress the thermal resistance and achieve efficient heat dissipation,the authors focus on developing a low-temperature sintering technique for wafer-level high-power semi-conductor de-vices.In detail,a 6-inch whole-wafer device was successfully fabricated by sintering the Si chip and Mo plate using a pulsed laser deposition(PLD)-based nano-Ag layer at a sin-tering temperature of 250℃,revealing edgewise delamination on the sintered layer.The formation mechanism of the destructive delamination was then unveiled,identifying excessive residual thermal stress due to an inappropriate sintering temperature as the ringleader.Furthermore,an optimisation methodology of the sintering temperature for the PLD-based nano-Ag layer was proposed,determining an optimal temperature range spanning from 190 to 211℃.Finally,a 6-inch sintered chip,the largest to date,was successfully fabricated with adequate integrity,robust reliability,and excellent thermal and electrical performance,evidentially verifying the feasibility of the nano-Ag-based sintering technique on large-sized whole-wafer semi-conductor devices.展开更多
In this study, low-temperature fired CaMg1−xLi2xSi2O6 microwave dielectric ceramics were prepared via the traditional solid-state reaction method. In this process, 0.4 wt% Li2CO3-B2O3-SiO2-CaCO3-Al2O3 (LBSCA) glass wa...In this study, low-temperature fired CaMg1−xLi2xSi2O6 microwave dielectric ceramics were prepared via the traditional solid-state reaction method. In this process, 0.4 wt% Li2CO3-B2O3-SiO2-CaCO3-Al2O3 (LBSCA) glass was added as a sintering aid. The results showed that ceramics consisted of CaMgSi2O6 as the main phase. The second phases were CaSiO3 always existing and Li2SiO3 occurring at substitution content x > 0.05. Li+ substitution effectively lowered sintering temperature due to 0.4 wt% LBSCA and contributed to grain densification, and the most homogeneous morphology could be observed at x = 0.05. The effects of relative density, the second phase, and ionic polarizability on dielectric constant (εr) were investigated. The quality factor (Q × f) varied with packing fraction that concerned the second phase. Moreover, the temperature coefficient of the resonant frequency (τf) was influenced by MgO6 octahedral distortion and bond valence. Excellent dielectric properties of the CaMg1−xLi2xSi2O6 ceramic was exhibited at x = 0.05 with εr = 7.44, Q × f = 41,017 GHz (f = 15.1638 GHz), and τf = −59.3 ppm/°C when sintered at 900 °C. It had a good application prospect in the field of low-temperature co-fired ceramic (LTCC) substrate and devices.展开更多
In this study,tri-rutile type Mg_(0.5)Ti_(0.5)TaO_(4) ceramics were synthesized,where the structure–property relationship,especially the structural configuration and intrinsic dielectric origin of Mg_(0.5)Ti_(0.5)TaO...In this study,tri-rutile type Mg_(0.5)Ti_(0.5)TaO_(4) ceramics were synthesized,where the structure–property relationship,especially the structural configuration and intrinsic dielectric origin of Mg_(0.5)Ti_(0.5)TaO_(4) ceramics,and the low-firing characteristics were studied.It is found that the tri-rutile structural type is unambiguously identified through the Rietveld refinement analysis,the selected area electron diffraction(SAED),and the high-resolution transmission electron microscopy(HRTEM)along the[110]zone axis.With the increase in sintering temperature,the densification and uniformity of crystal growth play important roles in regulating the microwave dielectric properties of Mg_(0.5)Ti_(0.5)TaO_(4) ceramics.Intrinsically,theoretical dielectric properties calculated by the far-infrared reflective spectra approached the experimental values,indicating the importance of structural features to dielectric properties.Furthermore,a glass additive with high matching relevance with ceramics has been developed to decrease the high sintering temperature of Mg_(0.5)Ti_(0.5)TaO_(4) ceramics,where 2–4 wt%Li_(2)O–MgO–ZnO–B_(2)O_(3)–SiO_(2)(LMZBS)glass frit was adopted to reduce the suitable temperature from 1275 to 1050℃ without significantly deteriorating the microwave dielectric characteristics.Specifically,Mg_(0.5)Ti_(0.5)TaO_(4) ceramics containing 2 wt% glass addition sintered at 1050℃for 4 h possess excellent microwave dielectric properties:dielectric constant(ε_(r))=44.3,quality factor multiplied by resonant frequency(Q×f)=23,820 GHz(f=6.2 GHz),and the temperature coefficient of resonant frequency(τ_(f))=123.2 ppm/℃.展开更多
Pb_(0.96)Sr_(0.04)(Zr,Ti)_(0.7)(Zn_(1/3)Nb_(2/3))_(0.3)O_(3)(PZN-PZT)piezoceramics with various Zr/Ti ratios and Li_(2)CO_(3)sintering aid were sintered at 900°C by the solid-state reaction route.The samples with...Pb_(0.96)Sr_(0.04)(Zr,Ti)_(0.7)(Zn_(1/3)Nb_(2/3))_(0.3)O_(3)(PZN-PZT)piezoceramics with various Zr/Ti ratios and Li_(2)CO_(3)sintering aid were sintered at 900°C by the solid-state reaction route.The samples with different Zr/Ti ratios were compared according to microstructure,phase structure,piezoelectricity,ferroelectricity,and dielectric relaxation.The Zr/Ti ratio in the PZN-PZT ceramics greatly affects the electrical properties.The Zr/Ti ratio affects the proportion between the rhombohedral and tetragonal phases and also affects the grain size.The PZN-PZT ceramics with the Zr/Ti ratio of 53:47 have the largest grain size and have optimized piezoelectric prop-erties(k_(p)=0.58,d_(33)=540 pC/N,and T_(C)=250°C).The larger the grain size,the lesser the grain boundary,the easier the domain wall motion,and the better the piezoelectric properties.The PZT ceramic with Zr/Ti ratio of 53:47 locates the morphotropic phase boundary(MPB)region which is one of the key factors for the high piezoelectric properties of the PZT.展开更多
Low-temperature sintered(Na_(1/2)Bi_(1/2))_(0.935)Ba_(0.065)Ti_(0.975)(Fe_(1/2)Nb_(1/2))_(0.025)O_(3)(NBT-BT-0.025FN)lead-free incipient piezoceramics were investigated using high-purity Li_(2)CO_(3) as sintering aids...Low-temperature sintered(Na_(1/2)Bi_(1/2))_(0.935)Ba_(0.065)Ti_(0.975)(Fe_(1/2)Nb_(1/2))_(0.025)O_(3)(NBT-BT-0.025FN)lead-free incipient piezoceramics were investigated using high-purity Li_(2)CO_(3) as sintering aids.With the ≤0.5 wt%Li_(2)CO_(3) addition,the introduced Li^(+) cations precede to enter the A-sites of the perovskite lattice to compensate for the A-site deficiencies.Once the addition exceeds 0.5 wt%,the excess Lit cations will occupy B-sites and give rise to the generation of oxygen vacancies,which accelerate the mass transport and thus lower the sintering temperature effectively from 1100℃ down to 925℃.It was also found that a small amount of Lit addition has little effect on the phase structure and electromechanical properties of the system,but overweight seriously disturbs these characteristics because of the large lattice distortion.The sintered NBT-BT-0.025FN incipient piezoceramics with 1.25 wt%Li_(2)CO_(3) addition at 925℃ provides a large strain of 0.33% and a corresponding large signal piezoelectric coefficient d_(33)^(*) of 550 pm/V at 60 kV/cm,indicating this system is a very promising candidate for lead-free co-fired multilayer actuator application.展开更多
Pb(Mg_(0.5)W_(0.5))O_(3)–Pb(Ni_(1/3)Nb_(2/3))O_(3)–Pb(Zr_(0.5)Ti_(0.5))O_(3)(PNN–PMW–PZT)piezoceramics were sintered at a low temperature of 900℃by the mixed metal oxide powder solid-state reaction route.CaCO_(3)...Pb(Mg_(0.5)W_(0.5))O_(3)–Pb(Ni_(1/3)Nb_(2/3))O_(3)–Pb(Zr_(0.5)Ti_(0.5))O_(3)(PNN–PMW–PZT)piezoceramics were sintered at a low temperature of 900℃by the mixed metal oxide powder solid-state reaction route.CaCO_(3) and Li_(2)CO_(3) as sintering aids and Yb_(2)O_(3) as a dopant were added into the PNN–PMW–PZT ceramic system for low-temperature sintering and enhancement of electrical properties,respectively.The effects of different Yb_(2)O_(3) doping amounts on the microstructure,dielectric,piezoelectric and ferroelectric properties of the samples were systematically investigated.The piezoceramics doped with 0.1 mol%Yb_(2)O_(3) have optimal electrical properties(d_(33)=563 pC/N,k_(p)=0.66,ε_(r)=2728(1 kHz),tanδ=0.0176(1 kHz),and T_(C)=301℃).While the piezoceramics doped with 0.3 mol% Yb_(2)O_(3) have optimal energy conversion properties:the piezoelectric voltage coefficient g_(33)=26.7×10^(-3)Vm/N and the effective piezoelectric energy conversion coefficient d_(33)×g_(33)=14366×10^(-15)m^(2)/N.展开更多
Electrochemical metallurgy at low temperature(<473 K)shows promise for the extraction and refinement of metals and alloys in a green and sustainable manner.However,the kinetics of the electrodeposition process is g...Electrochemical metallurgy at low temperature(<473 K)shows promise for the extraction and refinement of metals and alloys in a green and sustainable manner.However,the kinetics of the electrodeposition process is generally slow at low temperature,resulting in large overpotential and low current efficiency.Thus,the application of external physical fields has emerged as an effective strategy for improving the mass and charge transfer processes during electrochemical reactions.This review highlights the challenges associated with low-temperature electrochemical processes and briefly discusses recent achievements in optimizing electrodeposition processes through the use of external physical fields.The regulating effects on the optimization of the electrodeposition process and the strategies for select-ing various external physical fields,including magnetic,supergravity,and ultrasonic fields are summarized from the perspectives of equipment and mechanisms.Finally,advanced methods for in-situ characterization of external physical field-assisted electrodeposition processes are reviewed to gain a deeper understanding of metallic electrodeposition.An in-depth exploration of the mechanism by which external physical fields affect the electrode process is essential for enhancing the efficiency of metal extraction at low temperatures.展开更多
Dense CaAl2Si2O8 ceramics were prepared via a two-step sintering process at temperatures below 1000℃. First, pre-sintered CaAl2Si2O8 powders containing small amounts of other crystal phases were obtained by sintering...Dense CaAl2Si2O8 ceramics were prepared via a two-step sintering process at temperatures below 1000℃. First, pre-sintered CaAl2Si2O8 powders containing small amounts of other crystal phases were obtained by sintering a mixture of calcium hydroxide and kaolin powders at 950℃ for 6 h. Subsequently, the combination of the pre-sintered ceramic powders with MeO＇2B203 （Me = Ca, Sr, Ba） flux agents enabled the low-temperature densification sintering of the CaAl2Si2O8 ceramics at 950℃. The sintering behavior and phase formation of the CaAl2Si2O8 ceramics were investigated in terms of the addition of the three MeO·2B2O3 flux agents. Furthermore, alumina and quartz were introduced into the three flux agents to investigate the sintering behaviors, phase evolvements, microstructures, and physical properties of the resulting CaA12Si208 ceramics. The results showed that, because of their low-melting characteristics, the MeO·2B2O3 （Me = Ca, Sr, Ba） flux agents facilitated the formation of the CaAl2Si2O8 ceramics with a dense microstructure via liquid-phase sintering. The addition of alumina and quartz to the flux agents also strongly affected the microstructures, phase formation, and physical properties of the CaA12Si208 ceramics.展开更多
基金supported by the National Natural Science Foundation of China(Nos.51874360,51974370,52074360,52122407,52174285)the Innovation and Entrepreneurship Project of Hunan Province,China(No.2020GK4051)+1 种基金the Key R&D Program of Yunan Province,China(No.202103AA080019)the Natural Science Foundation for Distinguished Young Scholars of Hunan Province,China(No.2024JJ2077)。
文摘The morphology,crystal structure,and electrochemical performance of spent LiFePO_(4)(S-LFP)are recovered by one-step low-temperature solid phase sintering.After sintering at 550℃ for 3 h,the secondary particle size distribution of regenerated LiFePO4(R-LFP)becomes narrower,and the D_(50) is reduced from 5.6 to 2.3μm.In addition,the content of Li-Fe antisite defect is reduced from 5.73%to 1.20%,and the F is doped to O(2)site in the structure of R-LFP.Moreover,a coating layer comprising carbon and LiF is formed on the surface of R-LFP because of the decomposition of PVDF.Therefore,the R-LFP demonstrates exceptional Li+diffusion dynamics and conductivity,which delivers a high discharge capacity of 157.3 mA·h/g at 0.1C.And it maintains 92%of its initial capacity after 500 cycles at 1C.
基金the financial supports from the National Natural Science Foundation of China(Nos.51674207,51922091)the Young Elite Scientists Sponsorship Program by CAST,China(No.2018QNRC001)the Sichuan Science and Technology Program,China(Nos.2019YFS0453,2018JY0148).
文摘Porous ceramics were prepared with spodumene flotation talings(SFT),kaolin and low-melting point glass(LPG)powder,whose pores were formed by the chemical reaction of hydrogen peroxide(H_(2)O_(2)).LPG was used to reduce the sintering temperature of porous ceramics and kaolin was used to realize the adsorption to methylene blue(MB)of porous ceramics.The average flexural strength,compressive strength,apparent porosity,water absorption and maximum MB adsorption capacity were 5.60 MPa,4.66 MPa,52.27%,44.32%and 0.7 mg/g,respectively.Moreover,the results of orthogonal experiments present that the sintering temperature and the dosage of H_(2)O_(2)had great influence on the mechanical properties and apparent porosity of porous ceramics,respectively.The main reason for the improvement of mechanical properties of porous ceramics was that LPG gradually became soft with increasing the sintering temperature,which made the mineral particles adhere to each other closely.Kaolinite was not completely converted into metakaolin at 550℃,which might be the main reason why porous ceramics had adsorption properties.
文摘The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） considerably facilitated the densification of Ba2Ti3Nb4O18 ceramics.Appropriate addition of H3BO3 （ 〈3.5 wt%） remarkably improved the microwave dielectric properties of ceramics.The addition of H3BO3 and CuO successfully reduced the sintering temperature of Ba2Ti3Nb4O18 ceramics from 1300 to 1050 ℃.Ba2Ti3Nb4O18 ceramics sintered at 1 050 ℃ for 4 h with the addition of 1.0 wt% CuO and 3.5 wt% H3BO3 exhibited good microwave dielectric properties：er=33.74,Q？f=13 812 GHz,and tf=-5.35 ppm/°C at about 5.0 GHz.
基金Funded by the Special Fund for Research Institutes of the Ministry of Science and Technology of China(No.2013EG115007)the General Program of Natural Science Fund of Guangxi province in China(No.2013GXNSFAA019320)+2 种基金the Plan program of Scientific Research and Technical Development of Guangxi province in China(No.1348008-3)the Program of Scientific Development of China Nonferrous Metal Mining(group)Co,Ltd(No.2013KJJH11)the Plan program of Scientific Research and Technical Development of Guilin in China(Nos.20140104-4 and 20150105-1)
文摘We studied the effects of sintering temperature on FeCuCo based pre-alloyed powder for diamond bits.The FeCuCo composite was fabricated by co-precipitation method.With the addition of tungsten carbide（WC）,sintering under different temperatures was investigated.Mechanical properties of the FeCuCo based matrix were systematically studied.The structure of the composite was evaluated by X-ray diffraction（XRD） and scanning electron microscope（SEM） was used to analyze the surface of the powder and matrix.The suitable sintering temperature was determined through differential scanning calorimeter（DSC）.Micro drilling experiments were performed,and 820 ℃ was identified to be the ideal sintering temperature,at which the matrix shows the best mechanical properties and drilling performance.
基金financially supported by the National Natural Science Foundation of China (No. 51274039)the Research Fund for the Doctoral Program of Higher Education of China (No. 20120006110007)
文摘A spherical Fe matrix composite powder containing a high volume fraction （82vo1%） of fine TiC reinforcement was produced using a novel process combining in situ synthesis and plasma techniques. The composite powder exhibited good sphericity and a dense structure, and the fine sub-micron TiC particles were homogeneously distributed in the α-Fe matrix. A TiC-Fe cermet was prepared from the as-prepared spherical composite powder using powder metallurgy at a low sintering temperature; the product exhibited a hardness of HRA 88.5 and a flexural strength of 1360 MPa. The grain size of the fine-grained TiC and special surface structure of the spherical powder played the key roles in the fabrication process.
基金Project(2010GXNSFA013029)supported by the Natural Science Foundation of Guangxi Province,ChinaProject(101059529)supported by National Undergraduate Innovation Program of the Ministry of Education of China
文摘The influences of BaCu(B2O5)(BCB)addition on sintering,microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry,scanning electron microscopy and microwave dielectric measurements.The experimental results show that a small amount of BaCu(B2O5)addition can effectively reduce the sintering temperature to 900℃,and induce only a limited degradation of the microwave dielectric properties.Typically,the best microwave dielectric properties of er24.5,Q×f=24622 GHz,rf=4.2×10-6℃-1 are obtained for 1.0%BCB-doped Li2MgTi3O8 ceramics sintered at 900℃for 3 h.The BCB-doped Li2MgTi3O8 ceramics can be compatible with Ag electrode,which may be a strong candidate for low temperature co-fired ceramics applications.
文摘In this study,a trifunctional strategy was developed to prepare a confined Ni-based catalyst(Ni-CeO_(2)@SiO_(2))for dry reforming of methane(DRM)of two main greenhouse gases-CO_(2)and CH_(4).The Ni-CeO_(2)@SiO_(2)catalyst was fabricated by utilizing the confinement effect of the SiO_(2)shell and the synergistic interaction between Ni-Ce and the decoking effect of CeO_(2).The catalysts were systematically characterized via X-ray diffraction,N_(2 )adsorption/desorption,transmission electron microscopy,energy dispersive X-ray spectroscopy,hydrogen temperature reduction and desorption set by program,oxygen temperature program desorption,Raman spectroscopy,thermogravimetric analysis,and in situ diffuse reflectance infrared Fourier transform spectroscopy measurements to reveal their physicochemical properties and reaction mechanism.The Ni-CeO_(2)@SiO_(2)catalyst exhibited higher activity and stability than the catalyst synthesized via the traditional impregnation method.In addition,no carbon deposition was detected over Ni-CeO_(2)@SiO_(2)after a 100 h durability test at 800℃,and the average particle size of Ni nanoparticles(NPs)in the catalyst increased from 5.01 to 5.77 nm.Remarkably,Ni-CeO_(2)@SiO_(2)also exhibited superior low-temperature stability;no coke deposition was observed when the catalyst was reacted at 600℃ for 20 h.The high coking and sintering resistance of this confined Ni-based DRM catalyst can be attributed to its trifunctional effect.The trifunctional strategy developed in this study could be used as a guideline to design other high-performance catalysts for CO_(2)and CH4 dry forming and accelerate their industrialization.
文摘Low-temperature sintering(LTS)experiments of UO2 pellets and their results were reported.Moreover,a routine process of LTS for UO2 pellets was primarily established.Being sintered at 1 400 ℃ for 3 h in a partially-oxidative atmosphere,the relative density of the pellet can be up to around 94%.Pellets with such a high density are of benefit for following-up reduction-sintering processes.Orthogonal test indicates that the importance of factors affecting the density decreases in the sequence of partial-oxidative sintering temperature and time,reduction-sintering time and temperature,and sintering atmosphere.It is found that it is helpful to introducing a small amount of water vapor into the sintering atmosphere during the latter stage.It is believed that it is the key factor to raise the O/U ratio of original powder in order to improve the properties of the low-temperature sintered pellets.
基金the National Natural Science Foundation of China,grant number 52406074the China Postdoctoral Science Foundation under Grant Number 2025T180171+1 种基金the Natural Science Foundation of Guangdong Province(2025A1515011270)the China Southern Power Grid Technology Project(GDKJXM20231415/030100KC23120104).
文摘In order to explore the effects of CaO,lignite dust and sawdust on the drying characteristics ofmunicipal sludge at different concentrations,a three-factor three-level regression experiment was carried out based on the results of thermogravimetric experiment and single factor experiment.By fitting three common mathematical models,the Page model with the highest fitting degree was selected to determine the most suitable mathematical model to describe the municipal sludge drying process.In addition,the Box-Behnken design principle in the response surface method was used to analyze the interaction of three factors on the drying characteristics of municipal sludge.The results of the study show that below 100℃is the optimal drying temperature range for municipal sludge.The results of single factor experiments showed that the order of influence of the three factors on sludge drying time was CaO concentration>sawdust concentration>lignite dust concentration.In the single factor experiment,the optimal process parameterswere CaOconcentration 3%,lignite powder concentration 7%,and sawdust concentration 7%.In themulti-factor interaction analysis,the interaction between CaO and sawdust had the most significant effect on the reduction of drying time,and the order of influence was as follows:CaO interaction with sawdust>lignite dust interaction with sawdust>CaO interaction with lignite powder.Further analysis showed that the optimal process ratio was 3%CaO concentration and 3%sawdust concentration.
基金the financial support from the Key Project of Shaanxi Provincial Natural Science Foundation-Key Project of Laboratory(2025SYS-SYSZD-117)the Natural Science Basic Research Program of Shaanxi(2025JCYBQN-125)+8 种基金Young Talent Fund of Xi'an Association for Science and Technology(0959202513002)the Key Industrial Chain Technology Research Program of Xi'an(24ZDCYJSGG0048)the Key Research and Development Program of Xianyang(L2023-ZDYF-SF-077)Postdoctoral Fellowship Program of CPSF(GZC20241442)Shaanxi Postdoctoral Science Foundation(2024BSHSDZZ070)Research Funds for the Interdisciplinary Projects,CHU(300104240913)the Fundamental Research Funds for the Central Universities,CHU(300102385739,300102384201,300102384103)the Scientific Innovation Practice Project of Postgraduate of Chang'an University(300103725063)the financial support from the Australian Research Council。
文摘Lithium-ion batteries(LIBs),while dominant in energy storage due to high energy density and cycling stability,suffer from severe capacity decay,rate capability degradation,and lithium dendrite formation under low-temperature(LT)operation.Therefore,a more comprehensive and systematic understanding of LIB behavior at LT is urgently required.This review article comprehensively reviews recent advancements in electrolyte engineering strategies aimed at improving the low-temperature operational capabilities of LIBs.The study methodically examines critical performance-limiting mechanisms through fundamental analysis of four primary challenges:insufficient ionic conductivity under cryogenic conditions,kinetically hindered charge transfer processes,Li+transport limitations across the solidelectrolyte interphase(SEI),and uncontrolled lithium dendrite growth.The work elaborates on innovative optimization approaches encompassing lithium salt molecular design with tailored dissociation characteristics,solvent matrix optimization through dielectric constant and viscosity regulation,interfacial engineering additives for constructing low-impedance SEI layers,and gel-polymer composite electrolyte systems.Notably,particular emphasis is placed on emerging machine learning-guided electrolyte formulation strategies that enable high-throughput virtual screening of constituent combinations and prediction of structure-property relationships.These artificial intelligence-assisted rational design frameworks demonstrate significant potential for accelerating the development of next-generation LT electrolytes by establishing quantitative composition-performance correlations through advanced data-driven methodologies.
基金financially supported by the National Natural Science Foundation of China(No.22309067)the Open Project Program of the State Key Laboratory of Materials-Oriented Chemical Engineering,China(No.KL21-05)the Marine Equipment and Technology Institute,Jiangsu University of Science and Technology,China(No.XTCX202404)。
文摘This study focused on improving the cathode performance of Ba_(0.6)Sr_(0.4)Co_(0.85)Nb_(0.15)O_(3-δ)(BSCN)-based perovskite materials through molybdenum(Mo)doping.Pure BSCN and Mo-modified-BSCN—Ea_(0.6)Sr_(0.4)Co_(0.85)Nb_(0.1)Mo_(0.05)O_(3-δ)(B S CNM_(0.05)),Ba_(0.6)Sr_(0.4)Co_(0.85)Nb_(0.05)Mo_(0.1)O_(3-δ)(BSCNM_(0.1)),and Ba_(0.6)Sr_(0.4)Co_(0.85)Mo_(0.15)O_(3-δ)(BSCM)—with Mo doping contents of 5mol%,10mol%,and15mol%,respectively,were successfully prepared using the sol-gel method.The effects of Mo doping on the crystal structure,conductivity,thermal expansion coefficient,oxygen reduction reaction(ORR)activity,and electrochemical performance were systematically evaluated using X-ray diffraction analysis,thermally induced characterization,electrochemical impedance spectroscopy,and single-cell performance tests.The results revealed that Mo doping could improve the conductivity of the materials,suppress their thermal expansion effects,and significantly improve the electrochemical performance.Surface chemical state analysis using X-ray photoelectron spectroscopy revealed that 5mol%Mo doping could facilitate a high adsorbed oxygen concentration leading to enhanced ORR activity in the materials.Density functional theory calculations confirmed that Mo doping promoted the ORR activity in the materials.At an operating temperature of 600℃,the BSCNM_(0.05)cathode material exhibited significantly enhanced electrochemical impedance characteristics,with a reduced area specific resistance of 0.048Ω·cm~2,which was lower than that of the undoped BSCN matrix material by 32.39%.At the same operating temperature,an anode-supported single cell using a BSCNM_(0.05)cathode achieved a peak power density of 1477 mW·cm^(-2),which was 30.71%,56.30%,and 171.50%higher than those of BSCN,BSCNM_(0.1),and B SCM,respectively.The improved ORR activity and electrochemical performance of BSCNM_(0.05)indicate that it can be used as a cathode material in low-temperature solid oxide fuel cells.
基金supported by the Joint Funds of the National Natural Science Foundation of China(No.U24A2052)Mingsheng Ma acknowledges the Shanghai Eastern Talent Plan(No.QNKJ2024026).
文摘Zirconia-toughened alumina(ZTA)ceramics have attracted much attention as electronic package substrate materials because of their excellent mechanical properties and chemical stability.The high sintering temperatures of ZTA ceramics restrict their multilayer co-firing with copper electrodes for low-temperature co-fired ceramic(LTCC)applications.To achieve a balance between good properties and low sintering temperatures,this work proposes CuO-TiO_(2)-Nb_(2)O_(5)(CTN)composite oxide sintering aids for ZTA ceramics to obtain a novel glass-free LTCC material.A low-temperature densification mechanism based on multiphase synergy and interfacial reactions is revealed.The results show that the sintering temperature of ZTA ceramics doped with 5 wt% CTN can be significantly reduced to 1050℃,resulting in high thermal conductivity(18.7 W/(m·K)),high bending strength(405 MPa),and low dielectric loss(9.97×10^(−4)@11.97 GHz).The co-firing compatibility with a multilayer copper inner electrode is also demonstrated.This work overcomes the traditional trade-off between low-temperature sintering and high performance in glass-free LTCC materials and provides a new strategy for the design and development of multilayer ceramic substrates with copper inner electrodes.
基金National Natural Science Foundation of China,Grant/Award Numbers:52177153,52107004,52207164Integration Projects of National Natural Science Foundation of China,Grant/Award Number:U2166602。
文摘With the enormous growth in the capacity of electrical equipment,power semi-conductor devices are developing rapidly towards larger size and higher capacity.To suppress the thermal resistance and achieve efficient heat dissipation,the authors focus on developing a low-temperature sintering technique for wafer-level high-power semi-conductor de-vices.In detail,a 6-inch whole-wafer device was successfully fabricated by sintering the Si chip and Mo plate using a pulsed laser deposition(PLD)-based nano-Ag layer at a sin-tering temperature of 250℃,revealing edgewise delamination on the sintered layer.The formation mechanism of the destructive delamination was then unveiled,identifying excessive residual thermal stress due to an inappropriate sintering temperature as the ringleader.Furthermore,an optimisation methodology of the sintering temperature for the PLD-based nano-Ag layer was proposed,determining an optimal temperature range spanning from 190 to 211℃.Finally,a 6-inch sintered chip,the largest to date,was successfully fabricated with adequate integrity,robust reliability,and excellent thermal and electrical performance,evidentially verifying the feasibility of the nano-Ag-based sintering technique on large-sized whole-wafer semi-conductor devices.
基金This study was supported by the National Natural Science Foundation of China(Grant Nos.61771104 and U1809215).
文摘In this study, low-temperature fired CaMg1−xLi2xSi2O6 microwave dielectric ceramics were prepared via the traditional solid-state reaction method. In this process, 0.4 wt% Li2CO3-B2O3-SiO2-CaCO3-Al2O3 (LBSCA) glass was added as a sintering aid. The results showed that ceramics consisted of CaMgSi2O6 as the main phase. The second phases were CaSiO3 always existing and Li2SiO3 occurring at substitution content x > 0.05. Li+ substitution effectively lowered sintering temperature due to 0.4 wt% LBSCA and contributed to grain densification, and the most homogeneous morphology could be observed at x = 0.05. The effects of relative density, the second phase, and ionic polarizability on dielectric constant (εr) were investigated. The quality factor (Q × f) varied with packing fraction that concerned the second phase. Moreover, the temperature coefficient of the resonant frequency (τf) was influenced by MgO6 octahedral distortion and bond valence. Excellent dielectric properties of the CaMg1−xLi2xSi2O6 ceramic was exhibited at x = 0.05 with εr = 7.44, Q × f = 41,017 GHz (f = 15.1638 GHz), and τf = −59.3 ppm/°C when sintered at 900 °C. It had a good application prospect in the field of low-temperature co-fired ceramic (LTCC) substrate and devices.
基金support from the open research fund of Songshan Lake Materials Laboratory (No.2022SLABFN20)the Qinchuangyuan Citing Highlevel Innovation and Entrepreneurship Talent Projects (No.QCYRCXM-2022-40)+3 种基金the Natural Science Basic Research Program of Shaanxi (No.2022JQ-390)the National Natural Science Foundation of China (No.52102123)the National Key R&D Program of China (No.2022YFB2807405)the Natural Science Foundation of Sichuan Province (Nos.22NSFSC1973 and 2022NSFSC1959).
文摘In this study,tri-rutile type Mg_(0.5)Ti_(0.5)TaO_(4) ceramics were synthesized,where the structure–property relationship,especially the structural configuration and intrinsic dielectric origin of Mg_(0.5)Ti_(0.5)TaO_(4) ceramics,and the low-firing characteristics were studied.It is found that the tri-rutile structural type is unambiguously identified through the Rietveld refinement analysis,the selected area electron diffraction(SAED),and the high-resolution transmission electron microscopy(HRTEM)along the[110]zone axis.With the increase in sintering temperature,the densification and uniformity of crystal growth play important roles in regulating the microwave dielectric properties of Mg_(0.5)Ti_(0.5)TaO_(4) ceramics.Intrinsically,theoretical dielectric properties calculated by the far-infrared reflective spectra approached the experimental values,indicating the importance of structural features to dielectric properties.Furthermore,a glass additive with high matching relevance with ceramics has been developed to decrease the high sintering temperature of Mg_(0.5)Ti_(0.5)TaO_(4) ceramics,where 2–4 wt%Li_(2)O–MgO–ZnO–B_(2)O_(3)–SiO_(2)(LMZBS)glass frit was adopted to reduce the suitable temperature from 1275 to 1050℃ without significantly deteriorating the microwave dielectric characteristics.Specifically,Mg_(0.5)Ti_(0.5)TaO_(4) ceramics containing 2 wt% glass addition sintered at 1050℃for 4 h possess excellent microwave dielectric properties:dielectric constant(ε_(r))=44.3,quality factor multiplied by resonant frequency(Q×f)=23,820 GHz(f=6.2 GHz),and the temperature coefficient of resonant frequency(τ_(f))=123.2 ppm/℃.
基金This work was supported by Sichuan Science and Technology Program(2021YFG0234)the Fundamental Research Funds for the Central Universities(20826041E4280)the National Natural Science Foundation of China(52032007).
文摘Pb_(0.96)Sr_(0.04)(Zr,Ti)_(0.7)(Zn_(1/3)Nb_(2/3))_(0.3)O_(3)(PZN-PZT)piezoceramics with various Zr/Ti ratios and Li_(2)CO_(3)sintering aid were sintered at 900°C by the solid-state reaction route.The samples with different Zr/Ti ratios were compared according to microstructure,phase structure,piezoelectricity,ferroelectricity,and dielectric relaxation.The Zr/Ti ratio in the PZN-PZT ceramics greatly affects the electrical properties.The Zr/Ti ratio affects the proportion between the rhombohedral and tetragonal phases and also affects the grain size.The PZN-PZT ceramics with the Zr/Ti ratio of 53:47 have the largest grain size and have optimized piezoelectric prop-erties(k_(p)=0.58,d_(33)=540 pC/N,and T_(C)=250°C).The larger the grain size,the lesser the grain boundary,the easier the domain wall motion,and the better the piezoelectric properties.The PZT ceramic with Zr/Ti ratio of 53:47 locates the morphotropic phase boundary(MPB)region which is one of the key factors for the high piezoelectric properties of the PZT.
基金the generous support by the National Natural Science Foundation of China under grant no.51672092 and U1732117by the Project of Henan Province Science and Technology(Grant No.172102210380)+1 种基金China Postdoctoral Science Foundation funded project no.2018M632847the generous support by Wuhan Morning Light Plan of Youth Science and Technology(No.2017050304010299).
文摘Low-temperature sintered(Na_(1/2)Bi_(1/2))_(0.935)Ba_(0.065)Ti_(0.975)(Fe_(1/2)Nb_(1/2))_(0.025)O_(3)(NBT-BT-0.025FN)lead-free incipient piezoceramics were investigated using high-purity Li_(2)CO_(3) as sintering aids.With the ≤0.5 wt%Li_(2)CO_(3) addition,the introduced Li^(+) cations precede to enter the A-sites of the perovskite lattice to compensate for the A-site deficiencies.Once the addition exceeds 0.5 wt%,the excess Lit cations will occupy B-sites and give rise to the generation of oxygen vacancies,which accelerate the mass transport and thus lower the sintering temperature effectively from 1100℃ down to 925℃.It was also found that a small amount of Lit addition has little effect on the phase structure and electromechanical properties of the system,but overweight seriously disturbs these characteristics because of the large lattice distortion.The sintered NBT-BT-0.025FN incipient piezoceramics with 1.25 wt%Li_(2)CO_(3) addition at 925℃ provides a large strain of 0.33% and a corresponding large signal piezoelectric coefficient d_(33)^(*) of 550 pm/V at 60 kV/cm,indicating this system is a very promising candidate for lead-free co-fired multilayer actuator application.
基金financially supported by the Key Research and Development Program of the Sichuan Provincial Science and Technology Plan(No.2023DYF0173)the Fundamental Research Funds for the Central Universities(Nos.20826041E4280 and 20826041F4235).
文摘Pb(Mg_(0.5)W_(0.5))O_(3)–Pb(Ni_(1/3)Nb_(2/3))O_(3)–Pb(Zr_(0.5)Ti_(0.5))O_(3)(PNN–PMW–PZT)piezoceramics were sintered at a low temperature of 900℃by the mixed metal oxide powder solid-state reaction route.CaCO_(3) and Li_(2)CO_(3) as sintering aids and Yb_(2)O_(3) as a dopant were added into the PNN–PMW–PZT ceramic system for low-temperature sintering and enhancement of electrical properties,respectively.The effects of different Yb_(2)O_(3) doping amounts on the microstructure,dielectric,piezoelectric and ferroelectric properties of the samples were systematically investigated.The piezoceramics doped with 0.1 mol%Yb_(2)O_(3) have optimal electrical properties(d_(33)=563 pC/N,k_(p)=0.66,ε_(r)=2728(1 kHz),tanδ=0.0176(1 kHz),and T_(C)=301℃).While the piezoceramics doped with 0.3 mol% Yb_(2)O_(3) have optimal energy conversion properties:the piezoelectric voltage coefficient g_(33)=26.7×10^(-3)Vm/N and the effective piezoelectric energy conversion coefficient d_(33)×g_(33)=14366×10^(-15)m^(2)/N.
基金supported by Southern Marine Science and Engineering Guangdong Laboratory(Zhuhai)(No.SML2023SP243)the National Key Research and Development Program of China(No.2022YFC2906100)the National Natural Science Foundation of China(No.92475202)are acknowledged.
文摘Electrochemical metallurgy at low temperature(<473 K)shows promise for the extraction and refinement of metals and alloys in a green and sustainable manner.However,the kinetics of the electrodeposition process is generally slow at low temperature,resulting in large overpotential and low current efficiency.Thus,the application of external physical fields has emerged as an effective strategy for improving the mass and charge transfer processes during electrochemical reactions.This review highlights the challenges associated with low-temperature electrochemical processes and briefly discusses recent achievements in optimizing electrodeposition processes through the use of external physical fields.The regulating effects on the optimization of the electrodeposition process and the strategies for select-ing various external physical fields,including magnetic,supergravity,and ultrasonic fields are summarized from the perspectives of equipment and mechanisms.Finally,advanced methods for in-situ characterization of external physical field-assisted electrodeposition processes are reviewed to gain a deeper understanding of metallic electrodeposition.An in-depth exploration of the mechanism by which external physical fields affect the electrode process is essential for enhancing the efficiency of metal extraction at low temperatures.
基金supported by the Fundamental Research Funds for the Central Universities from China Government (Grant No. A0920502051513-5)
文摘Dense CaAl2Si2O8 ceramics were prepared via a two-step sintering process at temperatures below 1000℃. First, pre-sintered CaAl2Si2O8 powders containing small amounts of other crystal phases were obtained by sintering a mixture of calcium hydroxide and kaolin powders at 950℃ for 6 h. Subsequently, the combination of the pre-sintered ceramic powders with MeO＇2B203 （Me = Ca, Sr, Ba） flux agents enabled the low-temperature densification sintering of the CaAl2Si2O8 ceramics at 950℃. The sintering behavior and phase formation of the CaAl2Si2O8 ceramics were investigated in terms of the addition of the three MeO·2B2O3 flux agents. Furthermore, alumina and quartz were introduced into the three flux agents to investigate the sintering behaviors, phase evolvements, microstructures, and physical properties of the resulting CaA12Si208 ceramics. The results showed that, because of their low-melting characteristics, the MeO·2B2O3 （Me = Ca, Sr, Ba） flux agents facilitated the formation of the CaAl2Si2O8 ceramics with a dense microstructure via liquid-phase sintering. The addition of alumina and quartz to the flux agents also strongly affected the microstructures, phase formation, and physical properties of the CaA12Si208 ceramics.