The total conductivity of Li-biphenyl-1,2-dimethoxyethane solution（Li_xBp（DME）_（9.65）, Bp = biphenyl, DME = 1,2-dimethoxyethane, x = 0.25, 0.50, 1.00, 1.50, 2.00） is measured by impedance spectroscopy at a tempe...The total conductivity of Li-biphenyl-1,2-dimethoxyethane solution（Li_xBp（DME）_（9.65）, Bp = biphenyl, DME = 1,2-dimethoxyethane, x = 0.25, 0.50, 1.00, 1.50, 2.00） is measured by impedance spectroscopy at a temperature range from 0℃ to 40℃. The Li_（1.50）Bp（DME）_（9.65） has the highest total conductivity 10.7 m S/cm. The conductivity obeys Arrhenius law with the activation energy（E_（a（x=0.50））= 0.014 eV, E_（a（x=1.00））= 0.046 eV）. The ionic conductivity and electronic conductivity of Li_xBp（DME）_（9.65） solutions are investigated at 20℃ using the isothermal transient ionic current（ITIC） technique with an ion-blocking stainless steal electrode. The ionic conductivity and electronic conductivity of Li_（1.00）Bp（DME）_（9.65） are measured as 4.5 mS/cm and 6.6 mS/cm, respectively. The Li_（1.00）Bp（DME）_（9.65） solution is tested as an anode material of half liquid lithium ion battery due to the coexistence of electronic conductivity and ionic conductivity. The lithium iron phosphate（LFP） and Li_（1.5）Al_（0.5）Ti_（1.5）（PO_4）_3（LATP） are chosen to be the counter electrode and electrolyte, respectively. The assembled cell is cycled in the voltage range of 2.2 V-3.75 V at a current density of 50 mA/g. The potential of Li_（1.00）Bp（DME）_（9.65） solution is about 0.3 V vs. Li~＋/Li, which indicates the solution has a strong reducibility. The Li_（1.00）Bp（DME）_（9.65） solution is also used to prelithiate the anode material with low first efficiency, such as hard carbon, soft carbon and silicon.展开更多
This paper presents a study on CO<sub>2</sub> atmospheric transformation which was reacted directly with lithium hydroxide solution and metallic lithium. This solution was obtained through the reaction bet...This paper presents a study on CO<sub>2</sub> atmospheric transformation which was reacted directly with lithium hydroxide solution and metallic lithium. This solution was obtained through the reaction between metallic lithium and deionized water where hydrogen is produced and by exposing the metal at ambient conditions. In the transformation process, atmospheric CO<sub>2</sub> gas reacts directly with LiOH solution, in both cases, the CO<sub>2</sub> transformation kinetics was different. For this purpose, reactions between CO<sub>2</sub> and LiOH solution were carried out under controlled temperature and the second process only with metallic lithium, which was exposed at room temperature, however, in these two processes lithium carbonate oxide was formed and identified. According to the results, the efficiency in CO<sub>2</sub> transformation is a function of temperature value which was variable until completely obtaining the by-product, its XRD characterization indicated the formation only of Li<sub>2</sub>CO<sub>3</sub> in both procedures. Under laboratory conditions lithium compounds selectively reacted with CO<sub>2</sub>. In the same way, there is an alternative procedure to obtain LiOH and Li<sub>2</sub>CO<sub>3</sub> for different applications in various areas.展开更多
Mg-8Li-3Al＋xCe alloys（x = 0.5wt%, 1.0wt%, and 1.5wt%） were prepared through a casting route in an electric resistance furnace under a controlled atmosphere. The cast alloys were characterized by X-ray diffraction, ...Mg-8Li-3Al＋xCe alloys（x = 0.5wt%, 1.0wt%, and 1.5wt%） were prepared through a casting route in an electric resistance furnace under a controlled atmosphere. The cast alloys were characterized by X-ray diffraction, optical microscopy, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The corrosion behavior of the as-cast Mg-8Li-3Al＋xCe alloys were studied under salt spray tests in 3.5wt% NaC l solution at 35°C, in accordance with standard ASTM B-117, in conjunction with potentiodynamic polarization（PDP） tests. The results show that the addition of Ce to Mg-8Li-3Al（LA83） alloy results in the formation of Al_2Ce intermetallic phase, refines both the α-Mg phase and the Mg_（17）Al_（12） intermetallic phase, and then increases the microhardness of the alloys. The results of PDP and salt spray tests reveal that an increase in Ce content to 1.5wt% decreases the corrosion rate. The best corrosion resistance is observed for the LA83 alloy sample with 1.0wt% Ce.展开更多
Falling film generation process in lithium bromide absorption refrigeration generation system is researched in thispaper. To describe the coupled heat and mass transfer of laminar falling film in vertical generation t...Falling film generation process in lithium bromide absorption refrigeration generation system is researched in thispaper. To describe the coupled heat and mass transfer of laminar falling film in vertical generation tube, a mathematicalmodel is developed, in which the effect of mass transfer on heat transfer is carefully evaluated. Moreover,an equation related Re number with solution volume flow was also obtained in given conditions. We carried outthe experiments with the mass fraction of the inlet solution LiBr being 49.5% and obtained an empirical correlationof heat transfer with the film Re number and heat flux in different volume flow. Specifically, when 5kW/m2<qw<25kW/m2 and Re<500 the heat transfer correlation is given as: h=14009.87qw0.0764Re-0.5391.展开更多
For utilization of the residual heat of flue gas to drive the absorption chillers,a lithium-bromide falling film in vertical tube type generator is presented.A mathematical model was developed to simulate the heat and...For utilization of the residual heat of flue gas to drive the absorption chillers,a lithium-bromide falling film in vertical tube type generator is presented.A mathematical model was developed to simulate the heat and mass coupled problem of laminar falling film evaporation in vertical tube.In the model,the factor of mass transfer was taken into account in heat transfer performance calculation.The temperature and concentration fields were calculated.Some tests were conducted for the factors such as Re number,heating flux,the inlet concentration and operating pressure which can affect the heat and mass transfer performance in laminar falling film evaporation.The heat transfer performance is enhanced with the increasing of heat flux.An increasing inlet concentration can weaken the heat transfer performance.The operating pressure hardly affects on heat and mass transfer.The bigger inlet Re number means weaker heat transfer effects and stronger mass transfer.The mass transfer obviously restrains the heat transfer in the falling film solution.The relation between dimensionless heat transfer coefficient and the inlet Re number is obtained.展开更多
Severe lithium intoxication requires intensive and prolonged hemodialysis as a definitive therapeutic measure. Such an aggressive stand is often needed to prevent the post-dialytic rebound in plasma lithium levels as ...Severe lithium intoxication requires intensive and prolonged hemodialysis as a definitive therapeutic measure. Such an aggressive stand is often needed to prevent the post-dialytic rebound in plasma lithium levels as a result of the drug＇s relatively slow equilibration across cellular membranes. Use of a conventional, phosphorus-free, bicarbonate-based dialysis solution in the course of a dialytic treatment may engender hypophosphatemia in these individuals.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant No.52315206)the Ministry of Science and Technology of China(Grant No.2016YFB0100100)the Beijing Municipal Science and Technology Commission,China(Grant No.D151100003115003)
文摘The total conductivity of Li-biphenyl-1,2-dimethoxyethane solution（Li_xBp（DME）_（9.65）, Bp = biphenyl, DME = 1,2-dimethoxyethane, x = 0.25, 0.50, 1.00, 1.50, 2.00） is measured by impedance spectroscopy at a temperature range from 0℃ to 40℃. The Li_（1.50）Bp（DME）_（9.65） has the highest total conductivity 10.7 m S/cm. The conductivity obeys Arrhenius law with the activation energy（E_（a（x=0.50））= 0.014 eV, E_（a（x=1.00））= 0.046 eV）. The ionic conductivity and electronic conductivity of Li_xBp（DME）_（9.65） solutions are investigated at 20℃ using the isothermal transient ionic current（ITIC） technique with an ion-blocking stainless steal electrode. The ionic conductivity and electronic conductivity of Li_（1.00）Bp（DME）_（9.65） are measured as 4.5 mS/cm and 6.6 mS/cm, respectively. The Li_（1.00）Bp（DME）_（9.65） solution is tested as an anode material of half liquid lithium ion battery due to the coexistence of electronic conductivity and ionic conductivity. The lithium iron phosphate（LFP） and Li_（1.5）Al_（0.5）Ti_（1.5）（PO_4）_3（LATP） are chosen to be the counter electrode and electrolyte, respectively. The assembled cell is cycled in the voltage range of 2.2 V-3.75 V at a current density of 50 mA/g. The potential of Li_（1.00）Bp（DME）_（9.65） solution is about 0.3 V vs. Li~＋/Li, which indicates the solution has a strong reducibility. The Li_（1.00）Bp（DME）_（9.65） solution is also used to prelithiate the anode material with low first efficiency, such as hard carbon, soft carbon and silicon.
文摘This paper presents a study on CO<sub>2</sub> atmospheric transformation which was reacted directly with lithium hydroxide solution and metallic lithium. This solution was obtained through the reaction between metallic lithium and deionized water where hydrogen is produced and by exposing the metal at ambient conditions. In the transformation process, atmospheric CO<sub>2</sub> gas reacts directly with LiOH solution, in both cases, the CO<sub>2</sub> transformation kinetics was different. For this purpose, reactions between CO<sub>2</sub> and LiOH solution were carried out under controlled temperature and the second process only with metallic lithium, which was exposed at room temperature, however, in these two processes lithium carbonate oxide was formed and identified. According to the results, the efficiency in CO<sub>2</sub> transformation is a function of temperature value which was variable until completely obtaining the by-product, its XRD characterization indicated the formation only of Li<sub>2</sub>CO<sub>3</sub> in both procedures. Under laboratory conditions lithium compounds selectively reacted with CO<sub>2</sub>. In the same way, there is an alternative procedure to obtain LiOH and Li<sub>2</sub>CO<sub>3</sub> for different applications in various areas.
文摘Mg-8Li-3Al＋xCe alloys（x = 0.5wt%, 1.0wt%, and 1.5wt%） were prepared through a casting route in an electric resistance furnace under a controlled atmosphere. The cast alloys were characterized by X-ray diffraction, optical microscopy, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The corrosion behavior of the as-cast Mg-8Li-3Al＋xCe alloys were studied under salt spray tests in 3.5wt% NaC l solution at 35°C, in accordance with standard ASTM B-117, in conjunction with potentiodynamic polarization（PDP） tests. The results show that the addition of Ce to Mg-8Li-3Al（LA83） alloy results in the formation of Al_2Ce intermetallic phase, refines both the α-Mg phase and the Mg_（17）Al_（12） intermetallic phase, and then increases the microhardness of the alloys. The results of PDP and salt spray tests reveal that an increase in Ce content to 1.5wt% decreases the corrosion rate. The best corrosion resistance is observed for the LA83 alloy sample with 1.0wt% Ce.
文摘Falling film generation process in lithium bromide absorption refrigeration generation system is researched in thispaper. To describe the coupled heat and mass transfer of laminar falling film in vertical generation tube, a mathematicalmodel is developed, in which the effect of mass transfer on heat transfer is carefully evaluated. Moreover,an equation related Re number with solution volume flow was also obtained in given conditions. We carried outthe experiments with the mass fraction of the inlet solution LiBr being 49.5% and obtained an empirical correlationof heat transfer with the film Re number and heat flux in different volume flow. Specifically, when 5kW/m2<qw<25kW/m2 and Re<500 the heat transfer correlation is given as: h=14009.87qw0.0764Re-0.5391.
文摘For utilization of the residual heat of flue gas to drive the absorption chillers,a lithium-bromide falling film in vertical tube type generator is presented.A mathematical model was developed to simulate the heat and mass coupled problem of laminar falling film evaporation in vertical tube.In the model,the factor of mass transfer was taken into account in heat transfer performance calculation.The temperature and concentration fields were calculated.Some tests were conducted for the factors such as Re number,heating flux,the inlet concentration and operating pressure which can affect the heat and mass transfer performance in laminar falling film evaporation.The heat transfer performance is enhanced with the increasing of heat flux.An increasing inlet concentration can weaken the heat transfer performance.The operating pressure hardly affects on heat and mass transfer.The bigger inlet Re number means weaker heat transfer effects and stronger mass transfer.The mass transfer obviously restrains the heat transfer in the falling film solution.The relation between dimensionless heat transfer coefficient and the inlet Re number is obtained.
文摘Severe lithium intoxication requires intensive and prolonged hemodialysis as a definitive therapeutic measure. Such an aggressive stand is often needed to prevent the post-dialytic rebound in plasma lithium levels as a result of the drug＇s relatively slow equilibration across cellular membranes. Use of a conventional, phosphorus-free, bicarbonate-based dialysis solution in the course of a dialytic treatment may engender hypophosphatemia in these individuals.