Uniform crystalline TiO2 thin films were coated on silica glass fibers by liquid phase deposition from aqueous solution of ammonium hexafluorotitanate at low temperature. TiO2 thin films and nanopowders were prepared ...Uniform crystalline TiO2 thin films were coated on silica glass fibers by liquid phase deposition from aqueous solution of ammonium hexafluorotitanate at low temperature. TiO2 thin films and nanopowders were prepared by adding H3BO3 into （NH4）2TiF6 solution supersaturated with anatase nano-crystalline TiO2 at 40 ℃. The effects of the deposition conditions on the surface morphology, section morphology, thickness of the deposited TiO2 thin films were investigated. The results indicate that the growth rate and particle size of the thin films were controlled by both the deposition conditions and the amount of anatase nano-crystalline TiO2.展开更多
A novel method to fabricate composition- （IO） films using a positive sacrificial ZnO and topology-controlled ZnO/TiO2 inverse opals IO template has been developed. This method includes a two-step process, preparatio...A novel method to fabricate composition- （IO） films using a positive sacrificial ZnO and topology-controlled ZnO/TiO2 inverse opals IO template has been developed. This method includes a two-step process, preparation of ZnO IO by a simple electrochemical deposition using a self-assembly polystyrene colloidal crystal template and preparation of ZnO/TiO2 IO by a liquid phase deposition （LPD） process at room temperature. The composition and topology of ZnO/TiO2 IO can be easily controlled by changing the duration of the LPD. After 20 min LPD process, a ZnO/TiO2 composite IO with non-close-packed face-centered cubic air sphere array was obtained. Prolonging the duration to 60 min, a pure TiO2 IO （TIO-LPD60） with obviously thickened walls was formed. The formation mechanism for the compositional and topological variation was discussed. A preliminary study on UV photocatalytic property of the samples for degradation of methylene blue reveals that the composition and topology significantly influenced the photocatalytic activity of the IO film. The ZnO/TiO2 composite IO demonstrates a higher degree of activity than both pure ZnO and pure TiO2 IO, although they have a similar IO wall thickness. Moreover, with increasing IO wall thickness from -52 nm to -90 nm, TIO-LPD60 exhibits the highest level of photocatalytic performance.展开更多
文摘Uniform crystalline TiO2 thin films were coated on silica glass fibers by liquid phase deposition from aqueous solution of ammonium hexafluorotitanate at low temperature. TiO2 thin films and nanopowders were prepared by adding H3BO3 into （NH4）2TiF6 solution supersaturated with anatase nano-crystalline TiO2 at 40 ℃. The effects of the deposition conditions on the surface morphology, section morphology, thickness of the deposited TiO2 thin films were investigated. The results indicate that the growth rate and particle size of the thin films were controlled by both the deposition conditions and the amount of anatase nano-crystalline TiO2.
文摘A novel method to fabricate composition- （IO） films using a positive sacrificial ZnO and topology-controlled ZnO/TiO2 inverse opals IO template has been developed. This method includes a two-step process, preparation of ZnO IO by a simple electrochemical deposition using a self-assembly polystyrene colloidal crystal template and preparation of ZnO/TiO2 IO by a liquid phase deposition （LPD） process at room temperature. The composition and topology of ZnO/TiO2 IO can be easily controlled by changing the duration of the LPD. After 20 min LPD process, a ZnO/TiO2 composite IO with non-close-packed face-centered cubic air sphere array was obtained. Prolonging the duration to 60 min, a pure TiO2 IO （TIO-LPD60） with obviously thickened walls was formed. The formation mechanism for the compositional and topological variation was discussed. A preliminary study on UV photocatalytic property of the samples for degradation of methylene blue reveals that the composition and topology significantly influenced the photocatalytic activity of the IO film. The ZnO/TiO2 composite IO demonstrates a higher degree of activity than both pure ZnO and pure TiO2 IO, although they have a similar IO wall thickness. Moreover, with increasing IO wall thickness from -52 nm to -90 nm, TIO-LPD60 exhibits the highest level of photocatalytic performance.
