The polyoxometalate（POM）-imidazole ionic liquid（IL） [C8mim]2[Mo6O19]（C8mim=1-methyl-3-octylimi- dazolium） with a low melting point of 82.6 °C was successfully prepared and characterized by FTIR, XPS, NMR, T...The polyoxometalate（POM）-imidazole ionic liquid（IL） [C8mim]2[Mo6O19]（C8mim=1-methyl-3-octylimi- dazolium） with a low melting point of 82.6 °C was successfully prepared and characterized by FTIR, XPS, NMR, TG and so on. The polyoxomolybdate-based IL has high stability, and its decomposing temperature reaches 321 °C, which is higher than that of 1-alkyl-3-methylimidazolium halides IL. Further photocatalytic performances of the IL were measured via degrading dye rhodamine B（RB） in aqueous solution under the UV light irradiation. The experiments show that the conversion of RB reaches 80.5% after 90 min under UV-light and the degradation efficiency depends on the pH value of the solution, irradiation time and the dosage of the IL and so on.展开更多
NdF3-LiF melts are commonly used in the electrolysis process of metallic neodymium production. Research on the density and ionic structure of the electrolyte is important for its close connection with the electrolysis...NdF3-LiF melts are commonly used in the electrolysis process of metallic neodymium production. Research on the density and ionic structure of the electrolyte is important for its close connection with the electrolysis mechanism and process. In this paper, the density of LiF-NdF3 melts was studied by the Archimedes method. The results showed that the density decreased with increasing temperature and LiF contents. The changing law was discussed and explained in terms of the micro ionic structure of the melts....展开更多
Study of electrochemical behavior of chromium （molybdenum, tungsten） and silicon containing melts allowed defining conditions for synthesis of silicides of chromium, molybdenum and tungsten in the form of fine powde...Study of electrochemical behavior of chromium （molybdenum, tungsten） and silicon containing melts allowed defining conditions for synthesis of silicides of chromium, molybdenum and tungsten in the form of fine powders by electrolysis of halide-oxide melts. Sequence of stages of electrosynthesis of silicides of molybdenum and tungsten was found as follows： deposition of more electroposifve metal （molybdenum or tungsten）, deposition of the second component （silicon） on the surface of metal deposited previously, and reaction diffusion of silicon into the deep of the metal-salt ＂pear＂ with the formation of silicide phases of different compositions up to the higher silicides. In contrast, during the electrodeposition of chromium silicides, one of the components （chromium） is deposited not in elemental form, but in oxide form, and the other （silicon） acts as a reducing agent for this oxide to form binary compounds. Duration of the synthesis first stage （deposition of refractory metal or of its oxide） depends on the refractory metal compound content in the system and on the cathode current density. Synthesis of silicides is possible due to retention of powders of molybdenum （tungsten） or chromium oxide at the cathode without scaling. Optimal values of concentrations ratio, current density, temperature, and duration of electrosynthesis were found. Phase composition of products were obtained, as well as their chemical and thermal stability, were studied.展开更多
Influence of structural variations of N-vinylimidazolium tetrahalogenidoferrate(III) magnetic ionic liquids(MILs) on thermal properties was investigated. Using Gaussian09/B3 PW91/6-311 G(2d, p) density functional meth...Influence of structural variations of N-vinylimidazolium tetrahalogenidoferrate(III) magnetic ionic liquids(MILs) on thermal properties was investigated. Using Gaussian09/B3 PW91/6-311 G(2d, p) density functional methods, the microstructure of the MILs were analyzed. With differential scanning calorimeter(DSC) and thermogravimetric analysis(TGA), the thermal properties of the MILs were performed. The results showed that the interaction energies of ion pairs decreased, the crystallization temperature increased first and then decreased, and the surfusion first decreased and then increased with the elongation of the alkyl chain length on cation;with the increase of Br atom, the interaction energies of ion pairs increased;the interaction energies of ion pairs increased in the MILs with the same cation or anion, the nature of polarity of MILs increased and the melting point rose;as the cation or anion in MILs had a smaller size, it could have the solidsolid transition temperature. The results indicated that the decomposition temperature with the same type of MILs increased with the interaction energies of ion pairs. The interaction energy of ion pairs can be used to illuminate the correlation between the thermal properties and the structure of MILs. ILs possesses the properties of macromolecular.展开更多
基金Supported by the National Natural Science Foundation of China(Nos.2067101120731002+3 种基金20801004 10876002 20801005)the Specialized Research Fund for the Doctoral Program of Higher Education of China(No.200800070015).
文摘The polyoxometalate（POM）-imidazole ionic liquid（IL） [C8mim]2[Mo6O19]（C8mim=1-methyl-3-octylimi- dazolium） with a low melting point of 82.6 °C was successfully prepared and characterized by FTIR, XPS, NMR, TG and so on. The polyoxomolybdate-based IL has high stability, and its decomposing temperature reaches 321 °C, which is higher than that of 1-alkyl-3-methylimidazolium halides IL. Further photocatalytic performances of the IL were measured via degrading dye rhodamine B（RB） in aqueous solution under the UV light irradiation. The experiments show that the conversion of RB reaches 80.5% after 90 min under UV-light and the degradation efficiency depends on the pH value of the solution, irradiation time and the dosage of the IL and so on.
基金Project supported by the National Basic Research Program of China (2007CB210305) the Fundamental Research Funds for the Central Universities (N090302009)
文摘NdF3-LiF melts are commonly used in the electrolysis process of metallic neodymium production. Research on the density and ionic structure of the electrolyte is important for its close connection with the electrolysis mechanism and process. In this paper, the density of LiF-NdF3 melts was studied by the Archimedes method. The results showed that the density decreased with increasing temperature and LiF contents. The changing law was discussed and explained in terms of the micro ionic structure of the melts....
文摘Study of electrochemical behavior of chromium （molybdenum, tungsten） and silicon containing melts allowed defining conditions for synthesis of silicides of chromium, molybdenum and tungsten in the form of fine powders by electrolysis of halide-oxide melts. Sequence of stages of electrosynthesis of silicides of molybdenum and tungsten was found as follows： deposition of more electroposifve metal （molybdenum or tungsten）, deposition of the second component （silicon） on the surface of metal deposited previously, and reaction diffusion of silicon into the deep of the metal-salt ＂pear＂ with the formation of silicide phases of different compositions up to the higher silicides. In contrast, during the electrodeposition of chromium silicides, one of the components （chromium） is deposited not in elemental form, but in oxide form, and the other （silicon） acts as a reducing agent for this oxide to form binary compounds. Duration of the synthesis first stage （deposition of refractory metal or of its oxide） depends on the refractory metal compound content in the system and on the cathode current density. Synthesis of silicides is possible due to retention of powders of molybdenum （tungsten） or chromium oxide at the cathode without scaling. Optimal values of concentrations ratio, current density, temperature, and duration of electrosynthesis were found. Phase composition of products were obtained, as well as their chemical and thermal stability, were studied.
基金Funded by the Special Funds of the National Natural Science Foundation of China(No.81903579)the Natural Science Basis Research Plan in Shaanxi Province of China(No.2018JM7079)the Cultivating Special Funds of the National Natural Science Foundation of China from Xi’an Medical University(No.2017GJFY12).
文摘Influence of structural variations of N-vinylimidazolium tetrahalogenidoferrate(III) magnetic ionic liquids(MILs) on thermal properties was investigated. Using Gaussian09/B3 PW91/6-311 G(2d, p) density functional methods, the microstructure of the MILs were analyzed. With differential scanning calorimeter(DSC) and thermogravimetric analysis(TGA), the thermal properties of the MILs were performed. The results showed that the interaction energies of ion pairs decreased, the crystallization temperature increased first and then decreased, and the surfusion first decreased and then increased with the elongation of the alkyl chain length on cation;with the increase of Br atom, the interaction energies of ion pairs increased;the interaction energies of ion pairs increased in the MILs with the same cation or anion, the nature of polarity of MILs increased and the melting point rose;as the cation or anion in MILs had a smaller size, it could have the solidsolid transition temperature. The results indicated that the decomposition temperature with the same type of MILs increased with the interaction energies of ion pairs. The interaction energy of ion pairs can be used to illuminate the correlation between the thermal properties and the structure of MILs. ILs possesses the properties of macromolecular.