Porous ceramics were prepared from kaolinite gangue and Al（OH）3 with double addition of MgCO3 and CaCO3 by the pore-forming in-situ technique.The characterizations of porous ceramics were investigated by X-ray diffr...Porous ceramics were prepared from kaolinite gangue and Al（OH）3 with double addition of MgCO3 and CaCO3 by the pore-forming in-situ technique.The characterizations of porous ceramics were investigated by X-ray diffractometry,scanning electron microscopy,and mercury porosimetry measurements,etc.It is found that although the decomposition of MgCO3 and CaCO3 has little contribution to the porosity,the double addition of MgCO3 and CaCO3 strongly affects the formation of liquid phase,and then changes the phase compositions,pore characterization,and strength.The appropriate mode is the sample containing 1.17wt% MgCO3 and 1.17wt% CaCO3,which has high apparent porosity（41.0%）,high crushing strength（53.5 MPa）,high mullite content（76wt%）,and small average pore size（3.24 μm）.展开更多
基金Puyang Re-fractories Co. Ltd. for financially supporting
文摘Porous ceramics were prepared from kaolinite gangue and Al（OH）3 with double addition of MgCO3 and CaCO3 by the pore-forming in-situ technique.The characterizations of porous ceramics were investigated by X-ray diffractometry,scanning electron microscopy,and mercury porosimetry measurements,etc.It is found that although the decomposition of MgCO3 and CaCO3 has little contribution to the porosity,the double addition of MgCO3 and CaCO3 strongly affects the formation of liquid phase,and then changes the phase compositions,pore characterization,and strength.The appropriate mode is the sample containing 1.17wt% MgCO3 and 1.17wt% CaCO3,which has high apparent porosity（41.0%）,high crushing strength（53.5 MPa）,high mullite content（76wt%）,and small average pore size（3.24 μm）.