This study shows the preparation of a TiO2 coated Pt/C（TiO2/Pt/C） by atomic layer deposition（ALD）,and the examination of the possibility for TiO2/Pt/C to be used as a durable cathode catalyst in polymer electrolyt...This study shows the preparation of a TiO2 coated Pt/C（TiO2/Pt/C） by atomic layer deposition（ALD）,and the examination of the possibility for TiO2/Pt/C to be used as a durable cathode catalyst in polymer electrolyte fuel cells（PEFCs）. Cyclic voltammetry results revealed that TiO2/Pt/C catalyst which has 2 nm protective layer showed similar activity for the oxygen reduction reaction compared to Pt/C catalysts and they also had good durability. TiO2/Pt/C prepared by 10 ALD cycles degraded 70% after 2000 Accelerated degradation test, while Pt/C corroded 92% in the same conditions. TiO2 ultrathin layer by ALD is able to achieve a good balance between the durability and activity, leading to TiO2/Pt/C as a promising cathode catalyst for PEFCs. The mechanism of the TiO2 protective layer used to prevent the degradation of Pt/C is discussed.展开更多
We have introduced a 5-parameter Morse function to simulate the pairwise poten-tial and studied the adsorption and diffusion of hydrogen atoms on the Ni low indexsurfaces by pairwise method and satistying results were...We have introduced a 5-parameter Morse function to simulate the pairwise poten-tial and studied the adsorption and diffusion of hydrogen atoms on the Ni low indexsurfaces by pairwise method and satistying results were obtained. In this letter,we further investigate the properties of the adsorption and diffusion of hydrogen at-oms on the Ni (115) stepped surface by the same method and the optimumparameters.展开更多
基金supported by the Ministry of Knowledge Economy (MKE, Korea) under the Global Collaborative R&D program supervised by the KIAT (N0000698)
文摘This study shows the preparation of a TiO2 coated Pt/C（TiO2/Pt/C） by atomic layer deposition（ALD）,and the examination of the possibility for TiO2/Pt/C to be used as a durable cathode catalyst in polymer electrolyte fuel cells（PEFCs）. Cyclic voltammetry results revealed that TiO2/Pt/C catalyst which has 2 nm protective layer showed similar activity for the oxygen reduction reaction compared to Pt/C catalysts and they also had good durability. TiO2/Pt/C prepared by 10 ALD cycles degraded 70% after 2000 Accelerated degradation test, while Pt/C corroded 92% in the same conditions. TiO2 ultrathin layer by ALD is able to achieve a good balance between the durability and activity, leading to TiO2/Pt/C as a promising cathode catalyst for PEFCs. The mechanism of the TiO2 protective layer used to prevent the degradation of Pt/C is discussed.
文摘We have introduced a 5-parameter Morse function to simulate the pairwise poten-tial and studied the adsorption and diffusion of hydrogen atoms on the Ni low indexsurfaces by pairwise method and satistying results were obtained. In this letter,we further investigate the properties of the adsorption and diffusion of hydrogen at-oms on the Ni (115) stepped surface by the same method and the optimumparameters.