To mitigate the impact of interdiffusion reactions between the silicide slurry and Ta12W alloy substrate during vacuum sintering process on the oxidation resistance of the silicide coating,a micro-arc oxidation pretre...To mitigate the impact of interdiffusion reactions between the silicide slurry and Ta12W alloy substrate during vacuum sintering process on the oxidation resistance of the silicide coating,a micro-arc oxidation pretreatment was employed to construct a Ta_(2)O_(5)ceramic layer on the Ta12W alloy surface.Subsequently,a slurry spraying-vacuum sintering method was used to prepare a Si-Cr-Ti-Zr coating on the pretreated substrate.Comparative studies were conducted on the microstructure,phase composition,and isothermal oxidation resistance(at 1600℃)of the as-prepared coatings with and without the micro-arc oxidation ceramic layer.The results show that the Ta_(2)O_(5)layer prepared at 400 V is more continuous and has smaller pores than that prepared at 350 V.After microarc oxidation pretreatment,the Si-Cr-Ti-Zr coating on Ta12W alloy consists of three distinct layers:an upper layer dominated by Ti_(5)Si_(3),Ta_(5)Si_(3),and ZrSi;a middle layer dominated by TaSi_(2);a coating/substrate interfacial reaction layer dominated by Ta_(5)Si_(3).Both the Si-Cr-Ti-Zr coatings with and without the Ta_(2)O_(5)ceramic layer do not fail after isothermal oxidation at 1600℃for 5 h.Notably,the addition of the Ta2O5 ceramic layer reduces the high-temperature oxidation rate of the coating.展开更多
A calcium zirconate crucible material with excellent performance was prepared by fixing the particle size proportion and exploring the addition of Y_(2)O_(3).The results show that Y^(3+)solid-dissolves into c-ZrO_(2)t...A calcium zirconate crucible material with excellent performance was prepared by fixing the particle size proportion and exploring the addition of Y_(2)O_(3).The results show that Y^(3+)solid-dissolves into c-ZrO_(2)to occupy the Zr^(4+)positions,leading to structural defects and promoting the sintering of calcium zirconate.Adding 0.5 wt.%Y_(2)O_(3)into calcium zirconate can enhance the modulus of rupture,reduce the thermal expansion coefficient,and improve the thermal shock resistance.Through high-temperature test,it is found that adding 0.5 wt.%Y_(2)O_(3)significantly improves the corrosion resistance of the sample.展开更多
The phase transformation and mechanical behavior of Ti-43Al-9V-0.2Y alloy under varied heat treatments were systematically investigated.The cooling phase sequence is identified as β→β+α→α→γ+α(α_(2))→β+γ+...The phase transformation and mechanical behavior of Ti-43Al-9V-0.2Y alloy under varied heat treatments were systematically investigated.The cooling phase sequence is identified as β→β+α→α→γ+α(α_(2))→β+γ+α(α_(2))→β(β_(0))+γ.Above 1240℃,slow cooling forms lamellar structures via α→γ+α(α_(2))→β+γ+α(α_(2)),while fast cooling follows α→γ+α→β(β_(0))+γ;below 1240℃,α→γ+α(α_(2))dominates.At 800℃ and 1.0×10^(−4)s^(−1),γphase in duplex microstructures restricts dislocation slip due to low stacking fault energy,promoting dynamic recrystallization.Mixed microstructure(γ/β_(0) lamellar and duplex microstructure)achieves a remarkable strength-ductility product of 4907 MPa%through synergistic effects:the duplex enhances plasticity,while the lamellar improves strength.In both microstructures,limited dislocation slip/climb in β_(0) phases creates dislocation density gradients at γ/β_(0) interfaces,inducing micro-void nucleation and microcracks in β_(0).γ phase impedes defect propagation,and micro-voids further suppress crack growth.The crack propagation in α_(2)/γ lamellar microstructure depends on stress direction:parallel stress hinders crack initiation and growth,while perpendicular stress promotes crack nucleation and expansion.展开更多
The limited high-temperature oxidation resistance of Mg alloys is a key factor restricting their development and application.The addition of some rare earth elements(REs),owing to their unique physical and chemical pr...The limited high-temperature oxidation resistance of Mg alloys is a key factor restricting their development and application.The addition of some rare earth elements(REs),owing to their unique physical and chemical properties,can significantly enhance the oxidation resistance of Mg alloys.Based on our previous study,we conclude that REs such as Gd,Y,and Ce enhance the oxidation resistance of Mg-RE alloys.This article comprehensively reviews recent research progress on high-temperature oxidation behavior and the potential mechanism in Mg-RE alloys.Based on the thermodynamic and kinetic analyses,the evolution of the complex oxide system formed during the high-temperature oxidation of Mg-RE alloys is first summarized.The diffusion behavior and concentration control mechanisms of REs during the oxidation process and how these mechanisms affect the sustained growth of the oxide film and antioxidant properties were elucidated.Moreover,the different structures of the oxide films were classified,and their properties were discussed.Finally,this paper introduces the applications of commonly used REs in Mg alloys and frontier research on their oxidation mechanisms.Based on the above review,we propose that future research perspectives can be explored in terms of expanding the experimental temperature range for oxidation tests,optimizing the chemical composition by adding trace REs to study their synergistic mechanism,revealing the underlying oxidation mechanism through advanced in situ microscopic characterization methods,and investigating the mechanical properties of oxide films using diverse approaches.展开更多
TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing Ti...TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing TiB_(2)coatings have disadvantages such as high equipment costs,complicated processes,and highly toxic gas emissions.This paper proposes an environmentally friendly method,which requires inexpensive equipment and simple processing,for preparing TiB_(2)coating on molybdenum via electrophoretic deposition within Na3AlF6-based molten salts.The produced TiB_(2)layer had an approximate thickness of 60μm and exhibited high density,outstanding hardness(38.2 GPa)and robust adhesion strength(51 N).Additionally,high-temperature oxidation experiments revealed that,at900℃,the TiB_(2)coating provided effective protection to the molybdenum substrate against oxidation for 3 h.This result indicates that the TiB_(2)coating prepared on molybdenum using molten salt electrophoretic deposition possesses good high-temperature oxidation resistance.展开更多
In this study,the design,analysis,manufacturing,and testing of a 3D-printed conformal microstrip array antenna for high-temperature environments is presented.3D printing technology is used to fabricate a curved cerami...In this study,the design,analysis,manufacturing,and testing of a 3D-printed conformal microstrip array antenna for high-temperature environments is presented.3D printing technology is used to fabricate a curved ceramic substrate,and laser sintering and microdroplet spraying processes are used to add the conductive metal on the curved substrate.The problems of gain loss,bandwidth reduction,and frequency shift caused by high temperatures are addressed by using a proper antenna design,with parasitic patches,slots,and metal resonant cavities.The antenna prototype is characterized by the curved substrates and the conductive metals for the power dividers,the patch,and the ground plane;its performance is examined up to a temperature of 600℃in a muffle furnace and compared with the results from the numerical analysis.The results show that the antenna can effectively function at 600℃and even higher temperatures.展开更多
The influence of Ti and Zr,Nb alloying on the microstructures and performance of laser-welded molybdenum socket joints was investigated.Following Nb alloying,the average microhardness of the fusion zone(FZ)increased f...The influence of Ti and Zr,Nb alloying on the microstructures and performance of laser-welded molybdenum socket joints was investigated.Following Nb alloying,the average microhardness of the fusion zone(FZ)increased from HV 194.7 to HV 283.3.Additionally,Nb can react with O to form dispersed Nb_(2)O_(5) along grain boundaries,impeding grain boundary migration and dislocation movement while reducing the content of volatile Mo oxide along these boundaries.The incorporation of Nb in FZ partially inhibits pore defects and enhances joint load-bearing capacity.In comparison to the laser-welded joints without adding Nb(LW),the tensile strength of the laser-welded joints with Nb alloying(LW-Nb)was significantly improved by approximately 69%from 327.5 to 551.7 MPa.Furthermore,the fracture mechanism of the joints transitioned from intergranular fracture to transgranular fracture.展开更多
Many high-temperature pressure pipelines in thermal power plants are prone to failure due to long-term service-induced creep damage,which significantly impacts the normal operation of the equipment.Repair welding is a...Many high-temperature pressure pipelines in thermal power plants are prone to failure due to long-term service-induced creep damage,which significantly impacts the normal operation of the equipment.Repair welding is a widely adopted method to mitigate damage,including creep voids and cracks,in high-temperature pressure pipelines.However,the mechanical property degradation of aging material and excessive residual stresses from repair welding can lead to the formation of new cracks.To support scientifically sound decisions regarding life extension or replacement,the feasibility of repair welding for an aged CrMo steel high-temperature pressure pipeline weldment is investigated in this study.Firstly,the modified Kachanov-Rabotonov creep damage constitutive model is employed to predict the creep damage distribution of the weldment that had been in service for 26 years,identifying the most severely damaged location for scarfing.Subsequently,a numerical simulation study is conducted to analyze the residual stress in repair welding,with a focus on the influence of material performance degradation and excavation methods.The results indicate that the maximum creep damage in the CrMo steel weldment is concentrated in the heat-affected zone(HAZ)and the adjacent base metal(BM).Overall,the repair welding stresses simulated with degraded mechanical properties are lower than those with the virgin mechanical properties.However,the stress discontinuity at the interface between the repair welding zone and the BM is more pronounced due to the high-level mismatch in mechanical properties,which poses a significant risk for inducing repair welding cracks.Based on the consideration of avoiding stress concentration within the weld and reducing stress discontinuity at the weld boundary,the step repair method is recommended for engineering applications.展开更多
A suitable model for high-temperature heat pipe startup is a prerequisite to realizing the numerical simula-tion for the heat pipe cooled reactor startup from the cold state.It is required that this model not only des...A suitable model for high-temperature heat pipe startup is a prerequisite to realizing the numerical simula-tion for the heat pipe cooled reactor startup from the cold state.It is required that this model not only describes the transient behavior during the startup period,but also reduces the computing resources of the heat pipe cooled reactor simulation in the simplest way.In this study,a simplified model that integrates the two-zone and network models is proposed.In this model,vapor flow in the vapor space,evaporation,and condensation in the vapor–liquid interface are decoupled with heat conduction to achieve a fast calculation of the transient characteristics of the heat pipe.An experimental system for a high-temperature heat pipe was developed to validate the proposed model.A potassium heat pipe was utilized as the experimental material.Startup experiments were performed with differ-ent heating powers.Compared with the experimental results,the accuracy of the proposed model was verified.Moreover,the proposed model can predict the vapor flow,pressure drop,and temperature drop in the vapor space.As indicated by the analysis results,the essential requirements for successful startup are also determined.The heat pipe cannot achieve a successful startup until the heating power satisfies these requirements.All the discussions indicate the capability of the proposed model for the simulation of a high-temperature heat pipe startup from the frozen state;hence,can act as a basic tool for the heat pipe cooled reactor simulation.展开更多
This study investigated the physicochemical properties,enzyme activities,volatile flavor components,microbial communities,and sensory evaluation of high-temperature Daqu(HTD)during the maturation process,and a standar...This study investigated the physicochemical properties,enzyme activities,volatile flavor components,microbial communities,and sensory evaluation of high-temperature Daqu(HTD)during the maturation process,and a standard system was established for comprehensive quality evaluation of HTD.There were obvious changes in the physicochemical properties,enzyme activities,and volatile flavor components at different storage periods,which affected the sensory evaluation of HTD to a certain extent.The results of high-throughput sequencing revealed significant microbial diversity,and showed that the bacterial community changed significantly more than did the fungal community.During the storage process,the dominant bacterial genera were Kroppenstedtia and Thermoascus.The correlation between dominant microorganisms and quality indicators highlighted their role in HTD quality.Lactococcus,Candida,Pichia,Paecilomyces,and protease activity played a crucial role in the formation of isovaleraldehyde.Acidic protease activity had the greatest impact on the microbial community.Moisture promoted isobutyric acid generation.Furthermore,the comprehensive quality evaluation standard system was established by the entropy weight method combined with multi-factor fuzzy mathematics.Consequently,this study provides innovative insights for comprehensive quality evaluation of HTD during storage and establishes a groundwork for scientific and rational storage of HTD and quality control of sauce-flavor Baijiu.展开更多
Co-based alloy coating was prepared on Zr alloy using laser melting and cladding technique to study the difference in the high-temperature oxidation behavior between pure metal Co coatings and Co-T800 alloy coatings,a...Co-based alloy coating was prepared on Zr alloy using laser melting and cladding technique to study the difference in the high-temperature oxidation behavior between pure metal Co coatings and Co-T800 alloy coatings,as well as the wear resistance of the coatings.Besides,the effect of changing the laser melting process on the coatings was also investigated.The oxidation mass gain at 800–1200℃and the high-temperature oxidation behavior during high-temperature treatment for 1 h of two coated Zr alloy samples were studied.Results show that the Co coating and the Co-T800 coating have better resistance against high-temperature oxidation.After oxidizing at 1000℃for 1 h,the thickness of the oxide layer of the uncoated sample was 241.0μm,whereas that of the sample with Co-based coating is only 11.8–35.5μm.The friction wear test shows that the depth of the abrasion mark of the coated sample is only 1/2 of that of the substrate,indicating that the hardness and wear resistance of the Zr substrate are greatly improved.The disadvantage of Co-based coatings is the inferior corrosion resistance in 3.5wt%NaCl solution.展开更多
High-nickel ternary cathodes hold a great application prospect in solid-state lithium metal batteries to achieve high-energy density,but they still suffer from structural instability and detrimental side reactions wit...High-nickel ternary cathodes hold a great application prospect in solid-state lithium metal batteries to achieve high-energy density,but they still suffer from structural instability and detrimental side reactions with the solid-state electrolytes.To circumvent these issues,a continuous uniform layer polyacrylonitrile(PAN)was introduced on the surface of LiNi_(0.8)Mn_(0.1)Co_(0.1)O_(2) via in situ polymerization of acrylonitrile(AN).Furthermore,the partial-cyclized treatment of PAN(cPAN)coating layer presents high ionic and electron conductivity,which can accelerate interfacial Li+and electron diffusion simultaneously.And the thermodynamically stabilized cPAN coating layer cannot only effectively inhibit detrimental side reactions between cathode and solid-state electrolytes but also provide a homogeneous stress to simultaneously address the problems of bulk structural degradation,which contributes to the exceptional mechanical and electrochemical stabilities of the modified electrode.Besides,the coordination bond interaction between the cPAN and NCM811 can suppress the migration of Ni to elevate the stability of the crystal structure.Benefited from these,the In-cPAN-260@NCM811 shows excellent cycling performance with a retention of 86.8%after 300 cycles and superior rate capability.And endow the solid-state battery with thermal safety stability even at hightemperature extreme environment.This facile and scalable surface engineering represents significant progress in developing high-performance solid-state lithium metal batteries.展开更多
High-temperature industries,as the primary consumers of energy,are greatly concerned with energy savings.Designing refractory linings with low thermal conductivity to reduce heat dissipation through high-temperature f...High-temperature industries,as the primary consumers of energy,are greatly concerned with energy savings.Designing refractory linings with low thermal conductivity to reduce heat dissipation through high-temperature furnace linings is a critical concern.In this study,a series of novel entropy-stabilized spinel materials are reported,and their potential applications in high-temperature industries are investigated.XRD and TEM results indicate that all materials possess a cubic spinel crystal structure with the■space group.Furthermore,these materials exhibit good phase stability at high temperatures.All entropy-stabilized spinel aggregates demonstrated high refractoriness(>1800℃)and a high load softening temperature(>1700℃).The impact of configurational entropy on the properties of entropy-stabilized spinel materials was also studied.As configurational entropy increased,the thermal conductivity of the entropy-stabilized spinel decreased,while slag corrosion resistance deteriorated.For the entropy-stabilized spinel with a configurational entropy value of 1.126R,it showed good high-temperature stability,reliable resistance to slag attack,and a low thermal conductivity of 2.776 W·m^(-1)·K^(-1)at 1000℃.展开更多
The austenite(γ)reversely transformed from lath martensite(LM),lath bainite(LB),granular bainite(GB)and pearlite+ferrite(P+F)in a high-strength steel was studied at high temperatures using in-situ electron backscatte...The austenite(γ)reversely transformed from lath martensite(LM),lath bainite(LB),granular bainite(GB)and pearlite+ferrite(P+F)in a high-strength steel was studied at high temperatures using in-situ electron backscatter diffraction(EBSD).The memory effect of initial γ significantly affects the nucleation of the reverted γ in LM and GB structures,while a weak influence on that of LB and P+F structures.This results in a significant difference in γ grain size after complete austenitization,with the first two obtaining larger γ grains while the latter two are relatively small.Crystallographic analysis revealed that the reverted γ with acicular morphology(γA),most of which maintained the same orientation with the prior γ,dominated the reaustenitization behavior of LM and GB structures through preferential nucleation within γ grains and coalesced growth modes.Although globular reverted γ(γ_(G))with random orientation or large deviation from the prior γ can nucleate at the grain boundaries or within the grains,it is difficult for it to grow and play a role in segmenting and refining the prior γ due to the inhibition of γ_(A) coalescing.For LB and P+F structures,the nucleation rate of intragranular γ_(G) increases with increasing temperature,and always shows a random orientation.These γ_(G) grains can coarsen simultaneously with the intergranular γ_(G),ultimately playing a role in jointly dividing and refining the finalγgrains.Research also found that the differences in the effects of four different microstructures on revertedγnucleation are closely related to the variant selection of the matrix structure,as well as the content and size of cementite(θ).High density of block boundaries induced by weakening of variant selection and many fineθformed in the lath are the key to promoting LB structure to obtain more intragranular γ_(G) formation,as well as the important role of the large-sized θ in P+F structure.展开更多
The high-temperature mechanical behaviors of Multi-Layer Composite Panels(MCP)and Corrugated Sandwich Panels(CSP)of Continuous Glass Fiber-Reinforced Polypropylene(CGFRPP)are critical for their application in aerospac...The high-temperature mechanical behaviors of Multi-Layer Composite Panels(MCP)and Corrugated Sandwich Panels(CSP)of Continuous Glass Fiber-Reinforced Polypropylene(CGFRPP)are critical for their application in aerospace fields,which have been rarely mentioned in previous studies.High-temperature quasi-static tensile and compression tests on CGFRPP MCP are conducted first.The results showed that the tensile and compression strength,stiffness,and tensile modulus of MCP decreased with increasing temperature.The Gibson model was found to be more suitable for predicting the high-temperature mechanical performance of MCP after comparing the calculated results of different theoretical models with experimental data.Secondly,hightemperature planar compression tests were conducted on the CGFRPP CSP,revealing that the main failure modes were corrugated core buckling and delamination between the face panel and core material,with delamination being intensified at higher temperatures.Therefore,we proposed a strength theoretical model that considers structural buckling failure and interface delamination failure,and introduced the influence factor to evaluate the effect of interface delamination on structural strength.展开更多
Commercial wrought high-strength Cu-Cr-Zr alloys face limited high-temperature properties due to the rapid coarsening or dissolution of Cr precipitates.Here,we report a laser powder bed fusion(LPBF)fabricated Cu-0.84C...Commercial wrought high-strength Cu-Cr-Zr alloys face limited high-temperature properties due to the rapid coarsening or dissolution of Cr precipitates.Here,we report a laser powder bed fusion(LPBF)fabricated Cu-0.84Cr-0.42Zr(wt.%)alloy with exceptional heat resistance after aging.Primary Cr@Cu_(5)Zr phase(∼39.8 nm)with core-shell structure and a high density of heat-stable dislocations were intro-duced from the rapid solidification of LPBF and enabled the alloy to gain significant improvement in high-temperature properties.After aging treatment,secondary Cr and Cu_(51)Zr_(14)phases(∼3.4 nm)were precipitated,in which Zr solute was segregated at one side of the Cr phase,enhancing the thermal sta-bility of Cr phase.The excellent combinations of strength and thermal conductivity were achieved at or above 400℃.Particularly at 600℃,the aged sample not only exhibited a high tensile strength of∼196 MPa,which significantly surpassed that of wrought Cu-Cr-Zr alloys,but also possessed a thermal conductivity of∼349 W/(m K)comparable to that of pure copper.展开更多
Burial dissolution is a critical diagenetic process influencing ultra-deep carbonate reservoir development and preservation.Artificial carbonate samples with different internal structures were prepared,and high-temper...Burial dissolution is a critical diagenetic process influencing ultra-deep carbonate reservoir development and preservation.Artificial carbonate samples with different internal structures were prepared,and high-temperature and highpressure dissolution kinetic simulations were conducted.The results demonstrate that the intensity of burial dissolution is controlled by temperature and pressure,while tectonic-fluid activity influences the development pattern of burial dissolution,ultimately determining the direction of its differential modification.Extensive burial dissolution is likely to occur primarily at relatively shallow depths,significantly influencing reservoir formation,preservation,modification,and adjustment.The development of faults facilitates the maintenance of the intensity of burial dissolution.The maximum intensity of burial dissolution occurs at the tips and overlap zones of faults and intersections of multiple faults.The larger the scale of the faults,the more conducive it is to the development of burial dissolution.Burial dissolution fosters the formation of fault networks characterized by enhanced reservoir capacity and permeability.Burial dissolution controlled by episodic tectonic-fluid activity is a plausible explanation for forming the Tarim Basin's ultra-deep fault-controlled“stringbead-like”reservoirs.展开更多
To study the heat and mass transfer characteristics of alkali metals in a combined porous wick in high-temperature heat pipes,a three-dimensional(3-D)numerical model is constructed by using the finite volume method,Da...To study the heat and mass transfer characteristics of alkali metals in a combined porous wick in high-temperature heat pipes,a three-dimensional(3-D)numerical model is constructed by using the finite volume method,Darcy’s theory,and the theory of local thermal equilibrium.The research finds that the pressure drop of fluids flowing through a combined porous wick exhibits an increasing trend with increasing flow velocity at the inlet and with decreasing permeability of the porous media;a combined porous wick of lower porosity and permeability and larger fluid velocity at the inlet is found to have a less uniformly distributed fluid velocity;the different temperatures of the fluid at the inlet mainly influence the inlet section of the computational model,while having negligible effect thereon in the axial direction(this embodies the thermal homogeneity of such heat pipes).The result reveals that the temperature change in fluids at the inlet does not significantly affect the overall temperature distribution in a combined wick.展开更多
The research on high-performance electromagnetic wave absorption materials with high-temperature and oxidative stability in extreme environments is gaining popularity.Herein,the lightweight silicon carbide nanowires(S...The research on high-performance electromagnetic wave absorption materials with high-temperature and oxidative stability in extreme environments is gaining popularity.Herein,the lightweight silicon carbide nanowires(SiC_(nws))/SiC composites are fabricated with in-situ SiC interface on one-dimensional oriented SiC_(nws)skeleton,which collaborative configuration by 3D printing and freeze casting assembly.The con-structed porous structure optimizes the impedance matching degree and scattering intensity,the maximum effective absorption bandwidth(EAB_(max))of 5.9 GHz and the minimum reflection loss(RL_(min))of−41.4 dB can be realized.Considering the inherent oxidation resistance of SiC,the composites present well-maintained absorption performance at 600℃.Even at 1100℃,the EAB_(max)of 4.9 GHz and RLmin of−30.4 dB also demonstrate the high-temperature absorption stability of the composites,indicating exceptional wave absorption properties and thermal stability.The slight attenuation can be attributed to the decrease in impedance matching capability accompanying the elevated dielectric constant.This work clarifies the impact of structure and component synergy on wave absorption behavior,and offers a novel approach to producing high-performance and high-temperature resistance ceramic-based electromagnetic wave absorption materials suitable for extreme environments.展开更多
With the laser remelting of cast alloys combined with non-equilibrium liquidus projection thermodynamic calculations,a high-strength and heat-resistant Al-3Fe-2Mn alloy was designed.Incorporating Mn atoms into the met...With the laser remelting of cast alloys combined with non-equilibrium liquidus projection thermodynamic calculations,a high-strength and heat-resistant Al-3Fe-2Mn alloy was designed.Incorporating Mn atoms into the metastable nanoscale Al_(6)Fe phase,occupying some lattice sites,enhances its thermal stability.Additionally,during rapid solidification of laser powder bed fusion(L-PBF),the solubility of Fe and Mn elements in the aluminum alloy increases significantly,forming a supersaturated solid solution with improved strength.This alloy demonstrates excellent processability,achieving a relative density of over 99%,and tensile strengths of 295 MPa at 200℃ and 230 MPa at 300℃.The Al-3Fe-2Mn alloy holds great potential for wide applications due to its high strength at high temperature.展开更多
基金National Natural Science Foundation of China(52071274)Key Research and Development Projects of Shaanxi Province(2023-YBGY-442)Science and Technology Nova Project-Innovative Talent Promotion Program of Shaanxi Province(2020KJXX-062)。
文摘To mitigate the impact of interdiffusion reactions between the silicide slurry and Ta12W alloy substrate during vacuum sintering process on the oxidation resistance of the silicide coating,a micro-arc oxidation pretreatment was employed to construct a Ta_(2)O_(5)ceramic layer on the Ta12W alloy surface.Subsequently,a slurry spraying-vacuum sintering method was used to prepare a Si-Cr-Ti-Zr coating on the pretreated substrate.Comparative studies were conducted on the microstructure,phase composition,and isothermal oxidation resistance(at 1600℃)of the as-prepared coatings with and without the micro-arc oxidation ceramic layer.The results show that the Ta_(2)O_(5)layer prepared at 400 V is more continuous and has smaller pores than that prepared at 350 V.After microarc oxidation pretreatment,the Si-Cr-Ti-Zr coating on Ta12W alloy consists of three distinct layers:an upper layer dominated by Ti_(5)Si_(3),Ta_(5)Si_(3),and ZrSi;a middle layer dominated by TaSi_(2);a coating/substrate interfacial reaction layer dominated by Ta_(5)Si_(3).Both the Si-Cr-Ti-Zr coatings with and without the Ta_(2)O_(5)ceramic layer do not fail after isothermal oxidation at 1600℃for 5 h.Notably,the addition of the Ta2O5 ceramic layer reduces the high-temperature oxidation rate of the coating.
基金provided by the National Natural Science Foundation of China(NSFC)through the Joint Fund Project(No.U24A202815)the Youth Science Fund Project(No.52302031).
文摘A calcium zirconate crucible material with excellent performance was prepared by fixing the particle size proportion and exploring the addition of Y_(2)O_(3).The results show that Y^(3+)solid-dissolves into c-ZrO_(2)to occupy the Zr^(4+)positions,leading to structural defects and promoting the sintering of calcium zirconate.Adding 0.5 wt.%Y_(2)O_(3)into calcium zirconate can enhance the modulus of rupture,reduce the thermal expansion coefficient,and improve the thermal shock resistance.Through high-temperature test,it is found that adding 0.5 wt.%Y_(2)O_(3)significantly improves the corrosion resistance of the sample.
基金supported by the National Natural Science Foundation of China(Nos.52201035 and FRF-TP-24-010A).
文摘The phase transformation and mechanical behavior of Ti-43Al-9V-0.2Y alloy under varied heat treatments were systematically investigated.The cooling phase sequence is identified as β→β+α→α→γ+α(α_(2))→β+γ+α(α_(2))→β(β_(0))+γ.Above 1240℃,slow cooling forms lamellar structures via α→γ+α(α_(2))→β+γ+α(α_(2)),while fast cooling follows α→γ+α→β(β_(0))+γ;below 1240℃,α→γ+α(α_(2))dominates.At 800℃ and 1.0×10^(−4)s^(−1),γphase in duplex microstructures restricts dislocation slip due to low stacking fault energy,promoting dynamic recrystallization.Mixed microstructure(γ/β_(0) lamellar and duplex microstructure)achieves a remarkable strength-ductility product of 4907 MPa%through synergistic effects:the duplex enhances plasticity,while the lamellar improves strength.In both microstructures,limited dislocation slip/climb in β_(0) phases creates dislocation density gradients at γ/β_(0) interfaces,inducing micro-void nucleation and microcracks in β_(0).γ phase impedes defect propagation,and micro-voids further suppress crack growth.The crack propagation in α_(2)/γ lamellar microstructure depends on stress direction:parallel stress hinders crack initiation and growth,while perpendicular stress promotes crack nucleation and expansion.
基金supported by the Key R&D Program of Shandong Province,China(No.2025CXGC 010412)the National Key Research and Development Program of China(No.2022YFB3709300)the National Natural Science Foundation of China(No.U21A2048).
文摘The limited high-temperature oxidation resistance of Mg alloys is a key factor restricting their development and application.The addition of some rare earth elements(REs),owing to their unique physical and chemical properties,can significantly enhance the oxidation resistance of Mg alloys.Based on our previous study,we conclude that REs such as Gd,Y,and Ce enhance the oxidation resistance of Mg-RE alloys.This article comprehensively reviews recent research progress on high-temperature oxidation behavior and the potential mechanism in Mg-RE alloys.Based on the thermodynamic and kinetic analyses,the evolution of the complex oxide system formed during the high-temperature oxidation of Mg-RE alloys is first summarized.The diffusion behavior and concentration control mechanisms of REs during the oxidation process and how these mechanisms affect the sustained growth of the oxide film and antioxidant properties were elucidated.Moreover,the different structures of the oxide films were classified,and their properties were discussed.Finally,this paper introduces the applications of commonly used REs in Mg alloys and frontier research on their oxidation mechanisms.Based on the above review,we propose that future research perspectives can be explored in terms of expanding the experimental temperature range for oxidation tests,optimizing the chemical composition by adding trace REs to study their synergistic mechanism,revealing the underlying oxidation mechanism through advanced in situ microscopic characterization methods,and investigating the mechanical properties of oxide films using diverse approaches.
基金supported by the Original Exploratory Program of the National Natural Science Foundation of China(No.52450012)。
文摘TiB_(2)coatings can significantly enhance the high-temperature oxidation resistance of molybdenum,which would broaden the application range of molybdenum and alloys thereof.However,traditional methods for preparing TiB_(2)coatings have disadvantages such as high equipment costs,complicated processes,and highly toxic gas emissions.This paper proposes an environmentally friendly method,which requires inexpensive equipment and simple processing,for preparing TiB_(2)coating on molybdenum via electrophoretic deposition within Na3AlF6-based molten salts.The produced TiB_(2)layer had an approximate thickness of 60μm and exhibited high density,outstanding hardness(38.2 GPa)and robust adhesion strength(51 N).Additionally,high-temperature oxidation experiments revealed that,at900℃,the TiB_(2)coating provided effective protection to the molybdenum substrate against oxidation for 3 h.This result indicates that the TiB_(2)coating prepared on molybdenum using molten salt electrophoretic deposition possesses good high-temperature oxidation resistance.
基金National Natural Science Foundation of China(No.U2241205)the Natural Science Basic Research Program of Shaanxi(Nos.2022JC-33,2023-GHZD-35,and 2024JC-ZDXM-25)+1 种基金the Fundamental Research Funds for the Central Universitiesthe National 111 Project to provide fund for conducting experiments。
文摘In this study,the design,analysis,manufacturing,and testing of a 3D-printed conformal microstrip array antenna for high-temperature environments is presented.3D printing technology is used to fabricate a curved ceramic substrate,and laser sintering and microdroplet spraying processes are used to add the conductive metal on the curved substrate.The problems of gain loss,bandwidth reduction,and frequency shift caused by high temperatures are addressed by using a proper antenna design,with parasitic patches,slots,and metal resonant cavities.The antenna prototype is characterized by the curved substrates and the conductive metals for the power dividers,the patch,and the ground plane;its performance is examined up to a temperature of 600℃in a muffle furnace and compared with the results from the numerical analysis.The results show that the antenna can effectively function at 600℃and even higher temperatures.
基金National Key Research and Development Project of China (No. 2022YFB3707602)National Natural Science Foundation of China (Nos. 52005393, 51775416)。
文摘The influence of Ti and Zr,Nb alloying on the microstructures and performance of laser-welded molybdenum socket joints was investigated.Following Nb alloying,the average microhardness of the fusion zone(FZ)increased from HV 194.7 to HV 283.3.Additionally,Nb can react with O to form dispersed Nb_(2)O_(5) along grain boundaries,impeding grain boundary migration and dislocation movement while reducing the content of volatile Mo oxide along these boundaries.The incorporation of Nb in FZ partially inhibits pore defects and enhances joint load-bearing capacity.In comparison to the laser-welded joints without adding Nb(LW),the tensile strength of the laser-welded joints with Nb alloying(LW-Nb)was significantly improved by approximately 69%from 327.5 to 551.7 MPa.Furthermore,the fracture mechanism of the joints transitioned from intergranular fracture to transgranular fracture.
基金Supported by National Natural Science Foundation of China(Grant Nos.52275168,51805546).
文摘Many high-temperature pressure pipelines in thermal power plants are prone to failure due to long-term service-induced creep damage,which significantly impacts the normal operation of the equipment.Repair welding is a widely adopted method to mitigate damage,including creep voids and cracks,in high-temperature pressure pipelines.However,the mechanical property degradation of aging material and excessive residual stresses from repair welding can lead to the formation of new cracks.To support scientifically sound decisions regarding life extension or replacement,the feasibility of repair welding for an aged CrMo steel high-temperature pressure pipeline weldment is investigated in this study.Firstly,the modified Kachanov-Rabotonov creep damage constitutive model is employed to predict the creep damage distribution of the weldment that had been in service for 26 years,identifying the most severely damaged location for scarfing.Subsequently,a numerical simulation study is conducted to analyze the residual stress in repair welding,with a focus on the influence of material performance degradation and excavation methods.The results indicate that the maximum creep damage in the CrMo steel weldment is concentrated in the heat-affected zone(HAZ)and the adjacent base metal(BM).Overall,the repair welding stresses simulated with degraded mechanical properties are lower than those with the virgin mechanical properties.However,the stress discontinuity at the interface between the repair welding zone and the BM is more pronounced due to the high-level mismatch in mechanical properties,which poses a significant risk for inducing repair welding cracks.Based on the consideration of avoiding stress concentration within the weld and reducing stress discontinuity at the weld boundary,the step repair method is recommended for engineering applications.
基金This work was supported by the National Key Research and Development Project of China(No.2020YFB1901700)Science Challenge Project(No.TZ2018001)+1 种基金the National Natural Science Foundation of China(Nos.11775126 and 11775127)the Tsinghua University Initiative Scientific Research Program.
文摘A suitable model for high-temperature heat pipe startup is a prerequisite to realizing the numerical simula-tion for the heat pipe cooled reactor startup from the cold state.It is required that this model not only describes the transient behavior during the startup period,but also reduces the computing resources of the heat pipe cooled reactor simulation in the simplest way.In this study,a simplified model that integrates the two-zone and network models is proposed.In this model,vapor flow in the vapor space,evaporation,and condensation in the vapor–liquid interface are decoupled with heat conduction to achieve a fast calculation of the transient characteristics of the heat pipe.An experimental system for a high-temperature heat pipe was developed to validate the proposed model.A potassium heat pipe was utilized as the experimental material.Startup experiments were performed with differ-ent heating powers.Compared with the experimental results,the accuracy of the proposed model was verified.Moreover,the proposed model can predict the vapor flow,pressure drop,and temperature drop in the vapor space.As indicated by the analysis results,the essential requirements for successful startup are also determined.The heat pipe cannot achieve a successful startup until the heating power satisfies these requirements.All the discussions indicate the capability of the proposed model for the simulation of a high-temperature heat pipe startup from the frozen state;hence,can act as a basic tool for the heat pipe cooled reactor simulation.
文摘This study investigated the physicochemical properties,enzyme activities,volatile flavor components,microbial communities,and sensory evaluation of high-temperature Daqu(HTD)during the maturation process,and a standard system was established for comprehensive quality evaluation of HTD.There were obvious changes in the physicochemical properties,enzyme activities,and volatile flavor components at different storage periods,which affected the sensory evaluation of HTD to a certain extent.The results of high-throughput sequencing revealed significant microbial diversity,and showed that the bacterial community changed significantly more than did the fungal community.During the storage process,the dominant bacterial genera were Kroppenstedtia and Thermoascus.The correlation between dominant microorganisms and quality indicators highlighted their role in HTD quality.Lactococcus,Candida,Pichia,Paecilomyces,and protease activity played a crucial role in the formation of isovaleraldehyde.Acidic protease activity had the greatest impact on the microbial community.Moisture promoted isobutyric acid generation.Furthermore,the comprehensive quality evaluation standard system was established by the entropy weight method combined with multi-factor fuzzy mathematics.Consequently,this study provides innovative insights for comprehensive quality evaluation of HTD during storage and establishes a groundwork for scientific and rational storage of HTD and quality control of sauce-flavor Baijiu.
基金National Natural Science Foundation of China(52071126)Natural Science Foundation of Tianjin City,China(22JCQNJC01240)+2 种基金Central Guidance on Local Science and Technology Development Fund of Hebei Province(226Z1009G)Special Funds for Science and Technology Innovation in Hebei(2022X19)Anhui Provincial Natural Science Foundation(2308085ME135)。
文摘Co-based alloy coating was prepared on Zr alloy using laser melting and cladding technique to study the difference in the high-temperature oxidation behavior between pure metal Co coatings and Co-T800 alloy coatings,as well as the wear resistance of the coatings.Besides,the effect of changing the laser melting process on the coatings was also investigated.The oxidation mass gain at 800–1200℃and the high-temperature oxidation behavior during high-temperature treatment for 1 h of two coated Zr alloy samples were studied.Results show that the Co coating and the Co-T800 coating have better resistance against high-temperature oxidation.After oxidizing at 1000℃for 1 h,the thickness of the oxide layer of the uncoated sample was 241.0μm,whereas that of the sample with Co-based coating is only 11.8–35.5μm.The friction wear test shows that the depth of the abrasion mark of the coated sample is only 1/2 of that of the substrate,indicating that the hardness and wear resistance of the Zr substrate are greatly improved.The disadvantage of Co-based coatings is the inferior corrosion resistance in 3.5wt%NaCl solution.
基金financially supported by the National Natural Science Foundation of China(Nos.22102212 and 22479067).
文摘High-nickel ternary cathodes hold a great application prospect in solid-state lithium metal batteries to achieve high-energy density,but they still suffer from structural instability and detrimental side reactions with the solid-state electrolytes.To circumvent these issues,a continuous uniform layer polyacrylonitrile(PAN)was introduced on the surface of LiNi_(0.8)Mn_(0.1)Co_(0.1)O_(2) via in situ polymerization of acrylonitrile(AN).Furthermore,the partial-cyclized treatment of PAN(cPAN)coating layer presents high ionic and electron conductivity,which can accelerate interfacial Li+and electron diffusion simultaneously.And the thermodynamically stabilized cPAN coating layer cannot only effectively inhibit detrimental side reactions between cathode and solid-state electrolytes but also provide a homogeneous stress to simultaneously address the problems of bulk structural degradation,which contributes to the exceptional mechanical and electrochemical stabilities of the modified electrode.Besides,the coordination bond interaction between the cPAN and NCM811 can suppress the migration of Ni to elevate the stability of the crystal structure.Benefited from these,the In-cPAN-260@NCM811 shows excellent cycling performance with a retention of 86.8%after 300 cycles and superior rate capability.And endow the solid-state battery with thermal safety stability even at hightemperature extreme environment.This facile and scalable surface engineering represents significant progress in developing high-performance solid-state lithium metal batteries.
基金financially supported by the National Natural Science Foundation of China(Nos.52472032 and 52172023)the Key Program of Natural Science Foundation of Hubei Province(No.2024AFA083)
文摘High-temperature industries,as the primary consumers of energy,are greatly concerned with energy savings.Designing refractory linings with low thermal conductivity to reduce heat dissipation through high-temperature furnace linings is a critical concern.In this study,a series of novel entropy-stabilized spinel materials are reported,and their potential applications in high-temperature industries are investigated.XRD and TEM results indicate that all materials possess a cubic spinel crystal structure with the■space group.Furthermore,these materials exhibit good phase stability at high temperatures.All entropy-stabilized spinel aggregates demonstrated high refractoriness(>1800℃)and a high load softening temperature(>1700℃).The impact of configurational entropy on the properties of entropy-stabilized spinel materials was also studied.As configurational entropy increased,the thermal conductivity of the entropy-stabilized spinel decreased,while slag corrosion resistance deteriorated.For the entropy-stabilized spinel with a configurational entropy value of 1.126R,it showed good high-temperature stability,reliable resistance to slag attack,and a low thermal conductivity of 2.776 W·m^(-1)·K^(-1)at 1000℃.
基金financially supported by the National Natural Science Foundation of China(Nos.52271089 and 52001023)the Basic Research and Application Basic Research Foundation of Guangdong Province(Nos.2022A1515240016 and 2023B1515250006)the Fundamental Research Funds for the Central Universities(No.FRF-BD-23-01).
文摘The austenite(γ)reversely transformed from lath martensite(LM),lath bainite(LB),granular bainite(GB)and pearlite+ferrite(P+F)in a high-strength steel was studied at high temperatures using in-situ electron backscatter diffraction(EBSD).The memory effect of initial γ significantly affects the nucleation of the reverted γ in LM and GB structures,while a weak influence on that of LB and P+F structures.This results in a significant difference in γ grain size after complete austenitization,with the first two obtaining larger γ grains while the latter two are relatively small.Crystallographic analysis revealed that the reverted γ with acicular morphology(γA),most of which maintained the same orientation with the prior γ,dominated the reaustenitization behavior of LM and GB structures through preferential nucleation within γ grains and coalesced growth modes.Although globular reverted γ(γ_(G))with random orientation or large deviation from the prior γ can nucleate at the grain boundaries or within the grains,it is difficult for it to grow and play a role in segmenting and refining the prior γ due to the inhibition of γ_(A) coalescing.For LB and P+F structures,the nucleation rate of intragranular γ_(G) increases with increasing temperature,and always shows a random orientation.These γ_(G) grains can coarsen simultaneously with the intergranular γ_(G),ultimately playing a role in jointly dividing and refining the finalγgrains.Research also found that the differences in the effects of four different microstructures on revertedγnucleation are closely related to the variant selection of the matrix structure,as well as the content and size of cementite(θ).High density of block boundaries induced by weakening of variant selection and many fineθformed in the lath are the key to promoting LB structure to obtain more intragranular γ_(G) formation,as well as the important role of the large-sized θ in P+F structure.
基金co-supported by the National Natural Science Foundation of China(Nos.12372127,12202085,12302464)the Fundamental Research Funds for the Central Universities,China(No.2024CDJXY009)+1 种基金the Chongqing Outstanding Youth Fund,China(No.CSTB2024NSCQ-JQX0028)the Chongqing Natural Science Foundation,China(Nos.cstc2021ycjh-bgzxm0117,CSTB2022NSCQ-MSX0608)。
文摘The high-temperature mechanical behaviors of Multi-Layer Composite Panels(MCP)and Corrugated Sandwich Panels(CSP)of Continuous Glass Fiber-Reinforced Polypropylene(CGFRPP)are critical for their application in aerospace fields,which have been rarely mentioned in previous studies.High-temperature quasi-static tensile and compression tests on CGFRPP MCP are conducted first.The results showed that the tensile and compression strength,stiffness,and tensile modulus of MCP decreased with increasing temperature.The Gibson model was found to be more suitable for predicting the high-temperature mechanical performance of MCP after comparing the calculated results of different theoretical models with experimental data.Secondly,hightemperature planar compression tests were conducted on the CGFRPP CSP,revealing that the main failure modes were corrugated core buckling and delamination between the face panel and core material,with delamination being intensified at higher temperatures.Therefore,we proposed a strength theoretical model that considers structural buckling failure and interface delamination failure,and introduced the influence factor to evaluate the effect of interface delamination on structural strength.
基金supported by the National Natural Science Foun-dation of China(Nos.52127802 and 52431008).
文摘Commercial wrought high-strength Cu-Cr-Zr alloys face limited high-temperature properties due to the rapid coarsening or dissolution of Cr precipitates.Here,we report a laser powder bed fusion(LPBF)fabricated Cu-0.84Cr-0.42Zr(wt.%)alloy with exceptional heat resistance after aging.Primary Cr@Cu_(5)Zr phase(∼39.8 nm)with core-shell structure and a high density of heat-stable dislocations were intro-duced from the rapid solidification of LPBF and enabled the alloy to gain significant improvement in high-temperature properties.After aging treatment,secondary Cr and Cu_(51)Zr_(14)phases(∼3.4 nm)were precipitated,in which Zr solute was segregated at one side of the Cr phase,enhancing the thermal sta-bility of Cr phase.The excellent combinations of strength and thermal conductivity were achieved at or above 400℃.Particularly at 600℃,the aged sample not only exhibited a high tensile strength of∼196 MPa,which significantly surpassed that of wrought Cu-Cr-Zr alloys,but also possessed a thermal conductivity of∼349 W/(m K)comparable to that of pure copper.
基金supported by the National Natural Science Foundation of China(Grant No.U21B2062)supported by the Key Laboratory for Carbonate Reservoirs of China National Petroleum Corporation。
文摘Burial dissolution is a critical diagenetic process influencing ultra-deep carbonate reservoir development and preservation.Artificial carbonate samples with different internal structures were prepared,and high-temperature and highpressure dissolution kinetic simulations were conducted.The results demonstrate that the intensity of burial dissolution is controlled by temperature and pressure,while tectonic-fluid activity influences the development pattern of burial dissolution,ultimately determining the direction of its differential modification.Extensive burial dissolution is likely to occur primarily at relatively shallow depths,significantly influencing reservoir formation,preservation,modification,and adjustment.The development of faults facilitates the maintenance of the intensity of burial dissolution.The maximum intensity of burial dissolution occurs at the tips and overlap zones of faults and intersections of multiple faults.The larger the scale of the faults,the more conducive it is to the development of burial dissolution.Burial dissolution fosters the formation of fault networks characterized by enhanced reservoir capacity and permeability.Burial dissolution controlled by episodic tectonic-fluid activity is a plausible explanation for forming the Tarim Basin's ultra-deep fault-controlled“stringbead-like”reservoirs.
基金supported by the Natural Science Foundation of Jiangsu Province,China(Grant No.BK20180177)the Science and Technology Foundation of Xuzhou,China(Grant No.KH17007)the Natural Science Foundation for Colleges and Universities of Jiangsu Province,China(Grant No.17KJB460015,No.18KJB460028).
文摘To study the heat and mass transfer characteristics of alkali metals in a combined porous wick in high-temperature heat pipes,a three-dimensional(3-D)numerical model is constructed by using the finite volume method,Darcy’s theory,and the theory of local thermal equilibrium.The research finds that the pressure drop of fluids flowing through a combined porous wick exhibits an increasing trend with increasing flow velocity at the inlet and with decreasing permeability of the porous media;a combined porous wick of lower porosity and permeability and larger fluid velocity at the inlet is found to have a less uniformly distributed fluid velocity;the different temperatures of the fluid at the inlet mainly influence the inlet section of the computational model,while having negligible effect thereon in the axial direction(this embodies the thermal homogeneity of such heat pipes).The result reveals that the temperature change in fluids at the inlet does not significantly affect the overall temperature distribution in a combined wick.
基金supported by the National Key R&D Program of China(No.2022YFB3707700)National Natural Science Foundation of China(No.52302121)+3 种基金Shanghai Sailing Program(No.23YF1454700)Shanghai Natural Science Foundation(No.23ZR1472700)Shanghai Post-doctoral Excellent Program(No.2022664)Shanghai Science and Technology Innovation Action Plan(No.21511104800).
文摘The research on high-performance electromagnetic wave absorption materials with high-temperature and oxidative stability in extreme environments is gaining popularity.Herein,the lightweight silicon carbide nanowires(SiC_(nws))/SiC composites are fabricated with in-situ SiC interface on one-dimensional oriented SiC_(nws)skeleton,which collaborative configuration by 3D printing and freeze casting assembly.The con-structed porous structure optimizes the impedance matching degree and scattering intensity,the maximum effective absorption bandwidth(EAB_(max))of 5.9 GHz and the minimum reflection loss(RL_(min))of−41.4 dB can be realized.Considering the inherent oxidation resistance of SiC,the composites present well-maintained absorption performance at 600℃.Even at 1100℃,the EAB_(max)of 4.9 GHz and RLmin of−30.4 dB also demonstrate the high-temperature absorption stability of the composites,indicating exceptional wave absorption properties and thermal stability.The slight attenuation can be attributed to the decrease in impedance matching capability accompanying the elevated dielectric constant.This work clarifies the impact of structure and component synergy on wave absorption behavior,and offers a novel approach to producing high-performance and high-temperature resistance ceramic-based electromagnetic wave absorption materials suitable for extreme environments.
基金supported by the National Natural Science Foundation of China(No.U21B2073)the Science and Technology Project of the Science and Technology Department of Hubei Province,China(No.2022EHB020)。
文摘With the laser remelting of cast alloys combined with non-equilibrium liquidus projection thermodynamic calculations,a high-strength and heat-resistant Al-3Fe-2Mn alloy was designed.Incorporating Mn atoms into the metastable nanoscale Al_(6)Fe phase,occupying some lattice sites,enhances its thermal stability.Additionally,during rapid solidification of laser powder bed fusion(L-PBF),the solubility of Fe and Mn elements in the aluminum alloy increases significantly,forming a supersaturated solid solution with improved strength.This alloy demonstrates excellent processability,achieving a relative density of over 99%,and tensile strengths of 295 MPa at 200℃ and 230 MPa at 300℃.The Al-3Fe-2Mn alloy holds great potential for wide applications due to its high strength at high temperature.