Kevlar fiber （KF） is a synthesized product with strong mechanical properties. We used KF as a reinforcement to improve the mechanical properties of wood-flour/polypropylene （WF/PP） composites. KF was pretreated w...Kevlar fiber （KF） is a synthesized product with strong mechanical properties. We used KF as a reinforcement to improve the mechanical properties of wood-flour/polypropylene （WF/PP） composites. KF was pretreated with NaOH to improve its compatibility with the thermoplastic matrix. Maleated polypropylene （MAPP） was used as a coupling agent to improve the interfacial adhesion between KF, WF, and PP. Incorporation of KF improved the mechanical properties of WF/PP composites. Treatment of KF with NaOH resulted in further improvement in mechanical strength. Addition of 3% MAPP and 2% hydrolyzed KF （HKF） led to an increment of 93.8% in unnotched impact strength, 17.7% in notched impact strength, 86.8% in flexure strength, 50.8% in flexure modulus, and 94.1% in tensile strength compared to traditional WF/PP composites. Scanning electron microscopy of the cryo-fractured section of WF/PP showed that the HKF surface was rougher than the virgin KF, and the KF was randomly distributed in the composites, which might cause a mechanical interlocking between KF and polypropylene molecules in the composites.展开更多
Viscoelastic properties of maleated polypropylene （MAPP）-modified wood flour/polypropylene composites （WPC） were investigated by both a compression stress relaxation method and dynamic mechanical analyses （DMA）....Viscoelastic properties of maleated polypropylene （MAPP）-modified wood flour/polypropylene composites （WPC） were investigated by both a compression stress relaxation method and dynamic mechanical analyses （DMA）. Three wood to polymer ratios （40：60, 60：40, and 80：20） and five MAPP loading levels （0, 1, 2, 4 and 8%） were used to study their effects on the viscoelastic prop- erties of MAPP-WPC. The results show that： 1） higher wood to polymer ratio corresponds to higher stress relaxation levels for unmodified WPC. The modification with MAPP has an obvious effect on the stress relaxation of MAPP-WPC at higher wood to polymer ratios （60：40 and 80：20）, but almost no effect at the 40：60 wood to polymer ratio. The optimal MAPP loading level for the wood to polymer ratio of 60：40 appears at 1%; 2） the storage modulus reaches its maximum at a MAPP loading level of 1% for wood to polymer ratios of 40：60 and 60：40, while for the 80：20 wood to polymer ratio, a higher storage modulus is observed at higher MAPP loading levels, which is quite consistent with the stress relaxation results. The results suggested that a suitable loading level of MAPP has a positive effect on the viscoelastic properties of WPC at higher wood to polymer ratios. Excessive MAPP loading would have resulted in adverse effects.展开更多
Interfacial compatibility is a crucial factor to the performance of wood-plastic composites （WPCs）. Yet, so far, the coupling mechanisms of WPC have not been completely understood. In order to further clarify the in...Interfacial compatibility is a crucial factor to the performance of wood-plastic composites （WPCs）. Yet, so far, the coupling mechanisms of WPC have not been completely understood. In order to further clarify the interfacial coupling mechanism, the dielectric constant and dielectric loss factor of Simon poplar wood flour/polypropylene composites without additives at different wood contents were measured at oven-dry state, and parameters and thermodynamic quantities of the relaxation process were also analyzed and calculated. Consequently, an obvious relaxation process based on the reorientation of methanol groups in amorphous region of wood cell wall was observed exactly that its dielectric loss factor peak decreased with the decreasing wood content within the measured range of 50%-100%. With the trend of dielectric relaxation strength, the two changing trends both revealed that the existence of polypropylene could hinder reorientation of methanol groups. Following the decreasing wood contents, the effect of the hindrance on the dielectric properties turned obvious gradually. It elucidated that introduction of polypropylene caused the quantities of hydrogen bonds formed between each methanol group and the groups around it change. The same conclusion could be drawn from the analysis of thermodynamic quantities during the dielectric relaxation progress.展开更多
In order to improve the dimensional stability of wood-polymer composites, wood flour pre-treated by polyethylene glycol （PEG） at two different concentrations and then thermally treated at 140℃, was used as raw mate...In order to improve the dimensional stability of wood-polymer composites, wood flour pre-treated by polyethylene glycol （PEG） at two different concentrations and then thermally treated at 140℃, was used as raw material to produce wood flour/poly- propylene （PP） composites at a wood content of 40%. The structure of modified wood flour was analyzed with a scanning electron microscope （SEM） and its effect on the physical and mechanical properties of wood flour/PP composites was evaluated. The SEM results indicated the ＂bulking＂ effect of PEG on wood flour, which resulted in reduced water uptake. The combination of PEG and heat treatment further improved the moisture resistance of the composites. However, PEG modification had a negative effect on the flexural modulus of rupture （MOR） and the modulus of elasticity （MOE）; whereas heat treatment partly compensated for this reduc- tion. For dynamic mechanical properties, PEG treatment decreased the storage modulus （E＇）. However, the heat treatment resulted in an increase orE＇ of the wood flour/PP composites, with the temperature of loss factor peaks shifting to a higher temperature.展开更多
The influence of aryl amide compounds（TMB）as b-nucleating agents, on the non-isothermal crystallization of a wood-flour/polypropylene composite（WF/PP）prepared by compression molding was investigated by wide-angle ...The influence of aryl amide compounds（TMB）as b-nucleating agents, on the non-isothermal crystallization of a wood-flour/polypropylene composite（WF/PP）prepared by compression molding was investigated by wide-angle X-ray diffraction and differential scanning calorimetry. TMB was proved to be an effective b-crystalline nucleating agent for WF/PP. The DSC data showed that the crystallization peak temperature（Tp） increased and the half-time（t1/2） decreased with the addition of TMB.Three theoretical models were used to analyze the nonisothermal crystallization process. The modified Avrami method and Mo method successfully explained the nonisothermal crystallization behavior of PP and its composites. Their activation energies for non-isothermal crystallization were determined basing on the Kissinger method.展开更多
A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene （MA-PP） and maleic anhydride grafted ethylene-propylene-diene copolymer （MA-EPDM）, on wood-flou...A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene （MA-PP） and maleic anhydride grafted ethylene-propylene-diene copolymer （MA-EPDM）, on wood-flour/polypropylene （WF/PP） composites. WF/PP composites were prepared by direct extrusion profiles using a twin-screw/single-screw extruder system. DMA analysis showed that the loss factor of composites decreased and the storage modulus improved in the presence of MA-PP, which indicated much better interfacial adhesion between the PP matrix and wood flour filler than in the absence of compatibilizer. Morphological feature based on SEM observation showed that MA-PP and MA-EPDM improved the dispersion of the wood particles in the plastic matrix. MA-EPDM is a soft segment, although it improved the interfacial adhesion, storage modulus decreases with adding of MA-EPDM. As compatibilizer of wood-flour/polypropylene composites, both DMA analysis and SEM feature proved that MA-PP was superior to MA-EPDM.展开更多
This paper aims to investigate the water absorption of wood flour/polypropylene composites and its effects on dimensional stability and crystallization properties. Wood-plastic composites (WPCs) makes using polydopami...This paper aims to investigate the water absorption of wood flour/polypropylene composites and its effects on dimensional stability and crystallization properties. Wood-plastic composites (WPCs) makes using polydopamine modified wood flour (WF-D), virgin polypropylene, maleic anhydride-grafted polypropylene (MA) and antioxidant, by using hot-pressing moulding. Water absorption (WA), thickness swelling (TS) and failure of flexural properties of the composites have studied for a range of immersion times. It is found that the WA and TS have increased with WF content and immersion time. The water absorption and thickness swelling of WPCs are 0.85% and 0.99%, respectively, after 8 days immersion. With the prolonging of immersion time, the impact strength, flexural strength and flexural modulus of WPCs increase first and then decrease. The impact strength decreases from 3.32 kJ/m<sup>2</sup> to 2.94 kJ/m<sup>2</sup>, the retention rate is 88.55%;the flexural strength and flexural modulus by 68.58 Mpa and 3.92 Gpa, respectively. WPCs crystallization and thermal properties decrease slightly. Microstructures of the composites are examined to understand the mechanisms for the wood-plastic interaction which affects the water absorption and thickness swelling. Our work demonstrates that using polydopamine treatment wood flour for preparing WPCs can be an efficient way to improve the water resistance of WPCs.展开更多
This study assessed the life cycle of biocomposites with antioxidants by repeated processing.The effects of antioxidants on the life cycle of wood flour/polypropylene(PP)composites were determined by analyzing their m...This study assessed the life cycle of biocomposites with antioxidants by repeated processing.The effects of antioxidants on the life cycle of wood flour/polypropylene(PP)composites were determined by analyzing their mechanical and thermal properties.The composites were repeatedly processed for seven times with pelletizing and extruding.An antioxidant,pentaerythritoltetrakys 3-(3,5-ditert-butyl-4-hydroxyphenyl)propionate,was used.The mechanical strength of the biocomposites decreased after reprocessing.Fourier transformed infrared analysis showed that thermo-oxidative aging occurred during reprocessing.The thermal performance of the resulting composites decreased because of reprocessing.Wood flour/PP has a long lifetime and antioxidants can slow the thermo-oxidative and mechanical degradation during reprocessing.展开更多
Leachate sludge,a byproduct of municipal solid waste leachate treated through biochemical processes,is characterized by high water content(761.1%)and significant organic matter content(71.2%).Cement that is commonly u...Leachate sludge,a byproduct of municipal solid waste leachate treated through biochemical processes,is characterized by high water content(761.1%)and significant organic matter content(71.2%).Cement that is commonly used for solidifying leachate sludge has shown limited effectiveness.To address this issue,an alkali-activated ground-granulated blast-furnace slag(GGBS)geopolymer blended with polypropylene fibers was developed to solidify leachate sludge.Moreover,unconfined compressive strength(UCS),immersion,as well as X-ray diffraction(XRD),Fourier transform infrared spectroscopy(FTIR),and scanning electron microscope(SEM)tests were conducted to investigate the solidification effect and mechanism of the GGBS-based geopolymer and fibers on leachate sludge.The results showed that:the 28-d UCS of the solidified sludge with 20%and 30%GGBS is 0.35 MPa and 1.85 MPa,and decreases to 0.18 MPa and 1.13 MPa,respectively,after soaked in water for 28 d.Notably,the UCS of the solidified sludge with 30%GGBS satisfied the strength requirement of roadbed materials.Polypropylene fibers significantly enhanced the strength,ductility and water stability of the solidified sludge,with an optimal fiber content of 0.3%.Alkali-activated GGBS geopolymer generated three-dimensional,cross-linked geopolymeric gels within the solidified sludge,cementing sludge particles and filling intergranular pores to form a stable cementitious structure,thereby achieving effective solidification.Furthermore,incorporating polypropylene fibers improved the bonding and anchoring effect between fiber and solidified sludge,constrained lateral deformation of the solidified sludge,restricted crack propagation,and enhanced engineering performance of the solidified leachate sludge.展开更多
To compare the suitable working conditions of polypropylene(PP)and polycaprolactam(PA6)materials in actual use in automobiles,the effects of different temperature aging and different reagents on the mechanical propert...To compare the suitable working conditions of polypropylene(PP)and polycaprolactam(PA6)materials in actual use in automobiles,the effects of different temperature aging and different reagents on the mechanical properties of the two materials,such as tensile,bending,compression,and impact were studied.The results indicate that the short⁃term low⁃temperature environment had no much effect on the mechanical properties of PP and PA6.After long⁃term thermal aging at 80℃,the strength of PP and PA6 increased while their toughness decreased.After short⁃term thermal aging at 120℃,PP strength decreases and toughness increases,while PA6 strength increases and toughness decreases.The soaking of glass water and car shampoo had no much effect on the mechanical properties of PP,but had a significant impact on the mechanical properties of PA6.With the increase of soaking time,the strength of PA6 significantly decreases and the toughness significantly increases.The soaking of 95#gasoline had no much effect on the mechanical properties of PA6,but has a significant impact on the mechanical properties of PP.After 720 h of soaking,the retention rates of the tensile strength,bending strength,and compressive strength of PP were all less than 80%,while the retention rate of the impact strength of the cantilever beam was 160.4%.展开更多
The main objectives of this research were to study the effect of water absorption on mechanical properties of hybrid fiber reinforcement for polypropylene composites. The poor resistance towards water absorption is on...The main objectives of this research were to study the effect of water absorption on mechanical properties of hybrid fiber reinforcement for polypropylene composites. The poor resistance towards water absorption is one of the draw- backs of natural fibers. Hybrid filler-polypropylene composites are subjected to water immersion tests in order to study the effects of water absorption on the mechanical properties. Composites specimens containing 30 phr and 40 phr fiber weight were prepared by melt blending process. Water absorption tests were conducted by immersion specimens in distilled water at room temperature for different time durations (24, 48, 72, 96, 120, 144, 168, 192 hours). The tensile, flexural and impact properties were investigated before and after water absorption. The percentage of moisture uptake increased as the increasing order of the filler loading due to the high cellulose content. The phase morphology of wood flour/wheat husk polypropylene hybrid composites were investigated by SEM, the dynamic mechanical properties of the composite are analyzed by DMA & wheat, wood filler interaction are analyzed by FT-IR.展开更多
A novel eco-friendly charring agent(L-OH)was successfully synthesized by combining pentaerythritol(PER)with lignin through a simple two-step reaction.The structure of L-OH was characterized using Fourier transform inf...A novel eco-friendly charring agent(L-OH)was successfully synthesized by combining pentaerythritol(PER)with lignin through a simple two-step reaction.The structure of L-OH was characterized using Fourier transform infrared(FTIR),X-ray diffraction(XRD),scanning electron microscopy(SEM)and EDS.In addition,L-OH was introduced into polypropylene(PP)together with melamine(MEL)and ammonium polyphosphate(APP)as an intumescent flame retardant(IFRR).The flame retardancy of PP/IFRR composites were investigated using limited oxygen index(LOI),UL-94,thermogravimetric analysis(TGA)and cone calorimeter(CC)test.The experimental results indicate that the PP/IFRR composites pass the V-0 grade of the UL-94 test when the addition amount of IFRR is no less than 20%,and the LOI value of the composite reaches 32.2%at 30%IFRR addition.The peak heat release rate(PHRR)and peak smoke production rate(PSPR)of the composite decrease by 72.8%and 70.4%compared with pure PP,respectively.The flame retardancy mechanism was investigated by TGA,TG-FTIR and residual carbon analysis.These analyses indicate that L-OH can form a more continuous and dense carbon layer during the combustion process,which is the main factor contributing to the improved flame retardancy of PP.展开更多
A comparative study of products of thermal and thermocatalytic cracking of polypropylene(PP) in the presence of potassium polytitanate(PPT) synthesized by treatment of TiO_(2)(rutile) powder with molten mixture of KOH...A comparative study of products of thermal and thermocatalytic cracking of polypropylene(PP) in the presence of potassium polytitanate(PPT) synthesized by treatment of TiO_(2)(rutile) powder with molten mixture of KOH and KNO_(3) taken in a weight ratio of 30∶30∶40 has been carried out.It was shown that the studied type of PPT powder exhibits catalytic properties in the reaction of thermal decomposition of PP,compared to the effect of commercial zeolite catalyst CBV-780 traditionally used for this purpose.Based on the analysis performed,the differences in the mechanism of catalytic action of PPT and the zeolite were considered.The reasons for the observed differences in the composition of PP cracking products and in the rate of coke formation on the surface of studied catalysts were analyzed.Considering the obtained results,it has been proposed that the CBV-780 catalyst promoted more intensive production of the gaseous hydrocarbons compared to PPT,due to higher specific surface area(internal surface) accessible for relatively light and small-sized hydrocarbon products of cracking.However,intensive coke formation on the outer surface of the microporous zeolite contributes to the blocking of transport channels and the rapid loss of catalytic action.At the same time,PPT,which initially has a smaller specific surface area,retains its catalytic activity significantly longer due to slit-shaped flat pores and higher transport accessibility of the inner surface.展开更多
The present study presents an assessment of the interrelations between long-chain branching,specific nucleation,and end-use properties of polypropylene blends:blends of linear polypropylene(L-PP)and long-chain branche...The present study presents an assessment of the interrelations between long-chain branching,specific nucleation,and end-use properties of polypropylene blends:blends of linear polypropylene(L-PP)and long-chain branched polypropylene(LCB-PP)modified by a specificβ-nucleating agent(NA).Specimens with various LCB-PP compositions with and without NA were prepared under complex flow fields by injection molding.Wide-angle X-ray scattering was employed to capture the X-ray patterns of both the skin and core of the specimens,determining the overall crystallinity and amounts of individual polymorphs.The increasing content of LCB-PP andγ-phase,at the same time,in the blends is reflected in both increasing crystallinity and improved mechanical properties,namely,yield stress and Young’s modulus.On the other hand,the composition of the blends had no significant effect on the impact strength,except for nucleated L-PP.It has been demonstrated that adding a relatively small amount of LCB-PP is sufficient to modify the mechanical properties of linear polypropylene.Even a very small amount of LCB-PP in the L-PP suppressed the effectiveness of NA.展开更多
This study reports the fabrication of polypropylene(PP)-based microfiber webs(<1µm) using a hybrid melt electrospinning/blown process with the aim of establishing a scalable and solvent-free platform for advan...This study reports the fabrication of polypropylene(PP)-based microfiber webs(<1µm) using a hybrid melt electrospinning/blown process with the aim of establishing a scalable and solvent-free platform for advanced lithium-ion battery separators. The primary objective was to address the inherent limitations of conventional melt electrospinning particularly the difficulty of achieving fiber thinning due to the high viscosity of polymer melts by incorporating auxiliary hot air flow and reducing the nozzle diameter from 1.0mm to 0.3mm. This modified configuration enables enhanced jet elongation and fiber diameter control under processing conditions relevant to industrial applications. The effects of nozzle temperature, hot air temperature, and applied voltage on fiber formation and jet behavior were systematically examined using highspeed charge-coupled device(CCD) imaging techniques. The results demonstrated that increasing both the hot air temperature and applied voltage significantly improved fiber thinning and uniformity, yielding an average fiber diameter of approximately 0.86µm without evidence of thermal degradation. In contrast, elevated nozzle temperatures, while enhancing melt flowability, resulted in increased discharge rates and hindered fiber refinement when applied alone. These findings identify hot-air temperature as the most robust and controllable parameter for producing submicron fibers while maintaining the polymer integrity. Although the present study primarily focuses on morphological optimization and jet dynamics, future research will investigate the functional performance of fabricated microfiber webs as battery separators. Overall, the proposed hybrid process offers a technically feasible and environmentally sustainable route for the continuous production of fine PP-based fibers tailored for high-performance energy-storage applications.展开更多
Geological samples often contain significant amounts of iron,which,although not typically the target element,can substantially interfere with the analysis of other elements of interest.To mitigate these interferences,...Geological samples often contain significant amounts of iron,which,although not typically the target element,can substantially interfere with the analysis of other elements of interest.To mitigate these interferences,amidoximebased radiation grafted adsorbents have been identified as effective for iron removal.In this study,an amidoximefunctionalized,radiation-grafted adsorbent synthesized from polypropylene waste(PPw-g-AO-10)was employed to remove iron from leached geological samples.The adsorption process was systematically optimized by investigating the effects of pH,contact time,adsorbent dosage,and initial ferric ion concentration.Under optimal conditions-pH1.4,a contact time of 90 min,and an initial ferric ion concentration of 4500 mg/L-the adsorbent exhibited a maximum iron adsorption capacity of 269.02 mg/g.After optimizing the critical adsorption parameters,the adsorbent was applied to the leached geological samples,achieving a 91%removal of the iron content.The adsorbent was regenerated through two consecutive cycles using 0.2 N HNO_(3),achieving a regeneration efficiency of 65%.These findings confirm the efficacy of the synthesized PPw-g-AO-10 as a cost-effective and eco-friendly adsorbent for successfully removing iron from leached geological matrices while maintaining a reasonable degree of reusability.展开更多
Polypropylene(PP)has a relatively low melt strength due to its linear structure,which seriously limits its supercritical CO_(2)foaming performance.Introducing long-chain branches(LCBs)via grafting can significantly en...Polypropylene(PP)has a relatively low melt strength due to its linear structure,which seriously limits its supercritical CO_(2)foaming performance.Introducing long-chain branches(LCBs)via grafting can significantly enhance its melt strength.However,the relationship between the LCB level of high melt strength polypropylene(HMSPP)and its foaming behavior remains unclear.In this study,a series of HMSPP with different LCB levels was prepared using vinyl polydimethylsiloxane(VS)of varying viscosities as grafting monomers to investigate this relationship.Rheological analysis showed that the increase in viscosity of VS led to higher LCB levels in HMSPP.The melt strength of HMSPP increases with the increase of LCB levels,reaching up to 0.62 N,which is 13 times higher than that of the raw material.Supercritical CO_(2)foaming results revealed that the expansion ratio of HMSPP first increased and then decreased with the increase of melt strength,reaching a maximum of 39.4 times.Combining experiments with simulations,the influence of LCB levels on the dissolution and diffusion behavior of CO_(2)in HMSPP was clarified.This study deepens the understanding of the relationship between LCB and the foaming behavior of HMSPP,providing valuable insights for designing HMSPP with optimized foaming properties.展开更多
This study focuses on the electrical properties and microstructure of polypropylene(PP)-based blends used for cable insulation in nuclear power plants(NPPs).The PP-based blend,comprising isotactic PP and propylene-bas...This study focuses on the electrical properties and microstructure of polypropylene(PP)-based blends used for cable insulation in nuclear power plants(NPPs).The PP-based blend,comprising isotactic PP and propylene-based elastomer(PBE)at concentrations ranging from 0 to 50 wt%,underwent a melt blending process and subsequent cobalt-60 gamma-ray irradiation with doses ranging from 0 to 250 kGy.Electrical conductivity,trap distribution,and alternating(AC)breakdown strength were chosen to assess the insulation performance.These results indicate that the addition of PBE significantly improves the electrical properties of PP under irradiation.For PP,the electrical conductivity increased with irradiation,whereas the trap depth and breakdown strength decreased sharply.Conversely,for the blend,these changes initially exhibit opposite trends.When the irradiation was increased to 250 kGy,the AC breakdown strength of the blend improved by more than 21%compared to that of PP.The physical and chemical structures of the samples were investigated to explore the improvement mechanisms.The results offer insights into the design of new cable-insulation materials suitable for NPPs.展开更多
To examine the influences of waste polypropylene fiber(PPF)on the strength and internal pore structure of recycled aggregate concrete incorporating iron ore tailings,both the cubic compressive strength and axial compr...To examine the influences of waste polypropylene fiber(PPF)on the strength and internal pore structure of recycled aggregate concrete incorporating iron ore tailings,both the cubic compressive strength and axial compressive strength of the concrete were measured.Additionally,the microstructure was analyzed using scanning electron microscopy.The evolution of pore structure parameters,including pore size distribution,pore type distribution,and nuclear magnetic resonance spectral area in the concrete,was investigated through nuclear magnetic resonance(NMR)analysis.A model correlating the concrete's pore structure with its macroscopic performance was subsequently developed based on fractal theory.The results demonstrate that an appropriate amount of PPF created a bridging effect that decelerated the progression of macro cracks,enhanced the ductility of the concrete's failure mode,and increased both cubic compressive strength and axial compressive strength,with the most effective dosage being approximately 0.6%.An appropriate amount of PPF(ranging from 0.3%to 0.6%)facilitated the formation of harmless pores and shifted the pore size distribution towards medium and small sizes.Specifically,a fiber content of 0.6%resulted in the most significant reduction in the T2 spectral area.Furthermore,the pore structure of concrete exhibits distinct fractal characteristics.As the PPF content increased,the fractal dimension initially rose and then declined,demonstrating a strong correlation with the mechanical properties.展开更多
Polypropylene(PP) accounts for approximately 28.0% of the global polyolefin market,valued at $243.4 billion in 2022.Known for its lightweight,chemical resistance,costeffectiveness,high strength and melting point,PP is...Polypropylene(PP) accounts for approximately 28.0% of the global polyolefin market,valued at $243.4 billion in 2022.Known for its lightweight,chemical resistance,costeffectiveness,high strength and melting point,PP is widely used in various applications.Its properties and applications are closely tied to its tacticity.One-dimensional(1D) conventional 13C NMR has been extensively utilized to analyze PP tacticity,but its low sensitivity and longer relaxation time remain drawbacks.Typically,analyzing a single PP sample requires around 9 h of NMR time.Using of a cryogenically cooled 10 mm NMR probe can significantly reduce this measurement time;however,its high cost makes it inaccessible for most NMR laboratories.While the refocused insensitive nuclei enhanced by polarization transfer(RINEPT) technique is well-known for enhancing NMR sensitivity,there are no published studies using 1D 13C RINEPT to quantify PP tacticity.Relaxation agents like chromium(Ⅲ) acetylacetonate(Cr(acac)_(3)) have also been used to reduce relaxation times in polyolefin NMR analyses.Here we introduce a straightforward and easily implementable 1D 13C NMR method for rapid PP tacticity quantification.This method combines Cr(acac)_(3),Bruker's existing RINEPT pulse sequence(ineptrd),and our recently published ~1H decoupling sequence(bi_waltz65_256 pl) to eliminate ^(1)H decoupling artifacts.It is worth noting that decoupling artifacts are always present.When the signal-to-noise ratio(SNR) is low,these artifacts are obscured by noise.For example,in some two-dimensional(2D) or three-dimensional(3D) NMR spectra,decoupling artifacts are barely visible because of the low SNR.However,when attempting to observe weak signals in ^(1)D spectra,increasing the sample concentration or the number of scans enhances the SNR,revealing the decoupling artifacts.The decoupling artifacts appeared superimpose with some other weak signals,affecting the measurements of signal intensities.Therefore,improved ~1H-decoupling methods are crucial for such data acquisitio n.This synergy results in a 9.4-to 9.7-fold sensitivity enhancement,equating to an 88-to 94-fold reduction(9.4^(2)≈88,9.7^(2)≈94) in NMR acquisition time compared to conventional 1D ^(13)C NMR experiment with Cr(acac)_(3).The time savings are even more substantial compared to experiments without Cr(acac)_(3).The faster and quantitative approach is accessible to researchers with or without cryoprobes.Beyond PP,this method can be applied to tacticity measurements of other polyolefins,such as polybutene,polyhexene and polyoctene.展开更多
基金supported by the National Natural Science Foundation of China (Project Nos. 31010103905 and31070507)Program for New Century Excellent Talents in University of Ministry of Education of China (NCET-11-0608)the Fundamental Research Funds for the Central Universities (DL12DB02)
文摘Kevlar fiber （KF） is a synthesized product with strong mechanical properties. We used KF as a reinforcement to improve the mechanical properties of wood-flour/polypropylene （WF/PP） composites. KF was pretreated with NaOH to improve its compatibility with the thermoplastic matrix. Maleated polypropylene （MAPP） was used as a coupling agent to improve the interfacial adhesion between KF, WF, and PP. Incorporation of KF improved the mechanical properties of WF/PP composites. Treatment of KF with NaOH resulted in further improvement in mechanical strength. Addition of 3% MAPP and 2% hydrolyzed KF （HKF） led to an increment of 93.8% in unnotched impact strength, 17.7% in notched impact strength, 86.8% in flexure strength, 50.8% in flexure modulus, and 94.1% in tensile strength compared to traditional WF/PP composites. Scanning electron microscopy of the cryo-fractured section of WF/PP showed that the HKF surface was rougher than the virgin KF, and the KF was randomly distributed in the composites, which might cause a mechanical interlocking between KF and polypropylene molecules in the composites.
基金supported by the National Natural Science Foundation of China (Grant No. 30871966)
文摘Viscoelastic properties of maleated polypropylene （MAPP）-modified wood flour/polypropylene composites （WPC） were investigated by both a compression stress relaxation method and dynamic mechanical analyses （DMA）. Three wood to polymer ratios （40：60, 60：40, and 80：20） and five MAPP loading levels （0, 1, 2, 4 and 8%） were used to study their effects on the viscoelastic prop- erties of MAPP-WPC. The results show that： 1） higher wood to polymer ratio corresponds to higher stress relaxation levels for unmodified WPC. The modification with MAPP has an obvious effect on the stress relaxation of MAPP-WPC at higher wood to polymer ratios （60：40 and 80：20）, but almost no effect at the 40：60 wood to polymer ratio. The optimal MAPP loading level for the wood to polymer ratio of 60：40 appears at 1%; 2） the storage modulus reaches its maximum at a MAPP loading level of 1% for wood to polymer ratios of 40：60 and 60：40, while for the 80：20 wood to polymer ratio, a higher storage modulus is observed at higher MAPP loading levels, which is quite consistent with the stress relaxation results. The results suggested that a suitable loading level of MAPP has a positive effect on the viscoelastic properties of WPC at higher wood to polymer ratios. Excessive MAPP loading would have resulted in adverse effects.
基金funded by the National Natural Science Foundation of China (Grant No. 30871966).
文摘Interfacial compatibility is a crucial factor to the performance of wood-plastic composites （WPCs）. Yet, so far, the coupling mechanisms of WPC have not been completely understood. In order to further clarify the interfacial coupling mechanism, the dielectric constant and dielectric loss factor of Simon poplar wood flour/polypropylene composites without additives at different wood contents were measured at oven-dry state, and parameters and thermodynamic quantities of the relaxation process were also analyzed and calculated. Consequently, an obvious relaxation process based on the reorientation of methanol groups in amorphous region of wood cell wall was observed exactly that its dielectric loss factor peak decreased with the decreasing wood content within the measured range of 50%-100%. With the trend of dielectric relaxation strength, the two changing trends both revealed that the existence of polypropylene could hinder reorientation of methanol groups. Following the decreasing wood contents, the effect of the hindrance on the dielectric properties turned obvious gradually. It elucidated that introduction of polypropylene caused the quantities of hydrogen bonds formed between each methanol group and the groups around it change. The same conclusion could be drawn from the analysis of thermodynamic quantities during the dielectric relaxation progress.
基金supported by the National Natural Science Foundation of China (Grant No.30871966)
文摘In order to improve the dimensional stability of wood-polymer composites, wood flour pre-treated by polyethylene glycol （PEG） at two different concentrations and then thermally treated at 140℃, was used as raw material to produce wood flour/poly- propylene （PP） composites at a wood content of 40%. The structure of modified wood flour was analyzed with a scanning electron microscope （SEM） and its effect on the physical and mechanical properties of wood flour/PP composites was evaluated. The SEM results indicated the ＂bulking＂ effect of PEG on wood flour, which resulted in reduced water uptake. The combination of PEG and heat treatment further improved the moisture resistance of the composites. However, PEG modification had a negative effect on the flexural modulus of rupture （MOR） and the modulus of elasticity （MOE）; whereas heat treatment partly compensated for this reduc- tion. For dynamic mechanical properties, PEG treatment decreased the storage modulus （E＇）. However, the heat treatment resulted in an increase orE＇ of the wood flour/PP composites, with the temperature of loss factor peaks shifting to a higher temperature.
基金financially supported by‘‘the Fundamental Research Funds for the Central Universities’’(2572015AB07)the Forestry Industry Research of China(No.201204802)the National Natural Science Foundation of China(No.31100425)
文摘The influence of aryl amide compounds（TMB）as b-nucleating agents, on the non-isothermal crystallization of a wood-flour/polypropylene composite（WF/PP）prepared by compression molding was investigated by wide-angle X-ray diffraction and differential scanning calorimetry. TMB was proved to be an effective b-crystalline nucleating agent for WF/PP. The DSC data showed that the crystallization peak temperature（Tp） increased and the half-time（t1/2） decreased with the addition of TMB.Three theoretical models were used to analyze the nonisothermal crystallization process. The modified Avrami method and Mo method successfully explained the nonisothermal crystallization behavior of PP and its composites. Their activation energies for non-isothermal crystallization were determined basing on the Kissinger method.
基金This paper was supported by National Foundation of Application of Agricultural Scientific and Technological Achievements (2006GB23600450).
文摘A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene （MA-PP） and maleic anhydride grafted ethylene-propylene-diene copolymer （MA-EPDM）, on wood-flour/polypropylene （WF/PP） composites. WF/PP composites were prepared by direct extrusion profiles using a twin-screw/single-screw extruder system. DMA analysis showed that the loss factor of composites decreased and the storage modulus improved in the presence of MA-PP, which indicated much better interfacial adhesion between the PP matrix and wood flour filler than in the absence of compatibilizer. Morphological feature based on SEM observation showed that MA-PP and MA-EPDM improved the dispersion of the wood particles in the plastic matrix. MA-EPDM is a soft segment, although it improved the interfacial adhesion, storage modulus decreases with adding of MA-EPDM. As compatibilizer of wood-flour/polypropylene composites, both DMA analysis and SEM feature proved that MA-PP was superior to MA-EPDM.
文摘This paper aims to investigate the water absorption of wood flour/polypropylene composites and its effects on dimensional stability and crystallization properties. Wood-plastic composites (WPCs) makes using polydopamine modified wood flour (WF-D), virgin polypropylene, maleic anhydride-grafted polypropylene (MA) and antioxidant, by using hot-pressing moulding. Water absorption (WA), thickness swelling (TS) and failure of flexural properties of the composites have studied for a range of immersion times. It is found that the WA and TS have increased with WF content and immersion time. The water absorption and thickness swelling of WPCs are 0.85% and 0.99%, respectively, after 8 days immersion. With the prolonging of immersion time, the impact strength, flexural strength and flexural modulus of WPCs increase first and then decrease. The impact strength decreases from 3.32 kJ/m<sup>2</sup> to 2.94 kJ/m<sup>2</sup>, the retention rate is 88.55%;the flexural strength and flexural modulus by 68.58 Mpa and 3.92 Gpa, respectively. WPCs crystallization and thermal properties decrease slightly. Microstructures of the composites are examined to understand the mechanisms for the wood-plastic interaction which affects the water absorption and thickness swelling. Our work demonstrates that using polydopamine treatment wood flour for preparing WPCs can be an efficient way to improve the water resistance of WPCs.
基金This work was supported by the Fundamental Research Funds for the Central Universities(Grant No.2572018BB07)the National Natural Science Foundation of China(Grant No.31670570).
文摘This study assessed the life cycle of biocomposites with antioxidants by repeated processing.The effects of antioxidants on the life cycle of wood flour/polypropylene(PP)composites were determined by analyzing their mechanical and thermal properties.The composites were repeatedly processed for seven times with pelletizing and extruding.An antioxidant,pentaerythritoltetrakys 3-(3,5-ditert-butyl-4-hydroxyphenyl)propionate,was used.The mechanical strength of the biocomposites decreased after reprocessing.Fourier transformed infrared analysis showed that thermo-oxidative aging occurred during reprocessing.The thermal performance of the resulting composites decreased because of reprocessing.Wood flour/PP has a long lifetime and antioxidants can slow the thermo-oxidative and mechanical degradation during reprocessing.
基金financially supported by the National Natural Science Foundation of China(Grant No.52078142).
文摘Leachate sludge,a byproduct of municipal solid waste leachate treated through biochemical processes,is characterized by high water content(761.1%)and significant organic matter content(71.2%).Cement that is commonly used for solidifying leachate sludge has shown limited effectiveness.To address this issue,an alkali-activated ground-granulated blast-furnace slag(GGBS)geopolymer blended with polypropylene fibers was developed to solidify leachate sludge.Moreover,unconfined compressive strength(UCS),immersion,as well as X-ray diffraction(XRD),Fourier transform infrared spectroscopy(FTIR),and scanning electron microscope(SEM)tests were conducted to investigate the solidification effect and mechanism of the GGBS-based geopolymer and fibers on leachate sludge.The results showed that:the 28-d UCS of the solidified sludge with 20%and 30%GGBS is 0.35 MPa and 1.85 MPa,and decreases to 0.18 MPa and 1.13 MPa,respectively,after soaked in water for 28 d.Notably,the UCS of the solidified sludge with 30%GGBS satisfied the strength requirement of roadbed materials.Polypropylene fibers significantly enhanced the strength,ductility and water stability of the solidified sludge,with an optimal fiber content of 0.3%.Alkali-activated GGBS geopolymer generated three-dimensional,cross-linked geopolymeric gels within the solidified sludge,cementing sludge particles and filling intergranular pores to form a stable cementitious structure,thereby achieving effective solidification.Furthermore,incorporating polypropylene fibers improved the bonding and anchoring effect between fiber and solidified sludge,constrained lateral deformation of the solidified sludge,restricted crack propagation,and enhanced engineering performance of the solidified leachate sludge.
文摘To compare the suitable working conditions of polypropylene(PP)and polycaprolactam(PA6)materials in actual use in automobiles,the effects of different temperature aging and different reagents on the mechanical properties of the two materials,such as tensile,bending,compression,and impact were studied.The results indicate that the short⁃term low⁃temperature environment had no much effect on the mechanical properties of PP and PA6.After long⁃term thermal aging at 80℃,the strength of PP and PA6 increased while their toughness decreased.After short⁃term thermal aging at 120℃,PP strength decreases and toughness increases,while PA6 strength increases and toughness decreases.The soaking of glass water and car shampoo had no much effect on the mechanical properties of PP,but had a significant impact on the mechanical properties of PA6.With the increase of soaking time,the strength of PA6 significantly decreases and the toughness significantly increases.The soaking of 95#gasoline had no much effect on the mechanical properties of PA6,but has a significant impact on the mechanical properties of PP.After 720 h of soaking,the retention rates of the tensile strength,bending strength,and compressive strength of PP were all less than 80%,while the retention rate of the impact strength of the cantilever beam was 160.4%.
文摘The main objectives of this research were to study the effect of water absorption on mechanical properties of hybrid fiber reinforcement for polypropylene composites. The poor resistance towards water absorption is one of the draw- backs of natural fibers. Hybrid filler-polypropylene composites are subjected to water immersion tests in order to study the effects of water absorption on the mechanical properties. Composites specimens containing 30 phr and 40 phr fiber weight were prepared by melt blending process. Water absorption tests were conducted by immersion specimens in distilled water at room temperature for different time durations (24, 48, 72, 96, 120, 144, 168, 192 hours). The tensile, flexural and impact properties were investigated before and after water absorption. The percentage of moisture uptake increased as the increasing order of the filler loading due to the high cellulose content. The phase morphology of wood flour/wheat husk polypropylene hybrid composites were investigated by SEM, the dynamic mechanical properties of the composite are analyzed by DMA & wheat, wood filler interaction are analyzed by FT-IR.
基金the equipment support of Sharing Platform of Scientific Equipments,Ministry of Education's Research Center for Comprehensive Utilization and Clean Process Engineering of Phosphrous Resources,Sichuan University。
文摘A novel eco-friendly charring agent(L-OH)was successfully synthesized by combining pentaerythritol(PER)with lignin through a simple two-step reaction.The structure of L-OH was characterized using Fourier transform infrared(FTIR),X-ray diffraction(XRD),scanning electron microscopy(SEM)and EDS.In addition,L-OH was introduced into polypropylene(PP)together with melamine(MEL)and ammonium polyphosphate(APP)as an intumescent flame retardant(IFRR).The flame retardancy of PP/IFRR composites were investigated using limited oxygen index(LOI),UL-94,thermogravimetric analysis(TGA)and cone calorimeter(CC)test.The experimental results indicate that the PP/IFRR composites pass the V-0 grade of the UL-94 test when the addition amount of IFRR is no less than 20%,and the LOI value of the composite reaches 32.2%at 30%IFRR addition.The peak heat release rate(PHRR)and peak smoke production rate(PSPR)of the composite decrease by 72.8%and 70.4%compared with pure PP,respectively.The flame retardancy mechanism was investigated by TGA,TG-FTIR and residual carbon analysis.These analyses indicate that L-OH can form a more continuous and dense carbon layer during the combustion process,which is the main factor contributing to the improved flame retardancy of PP.
文摘A comparative study of products of thermal and thermocatalytic cracking of polypropylene(PP) in the presence of potassium polytitanate(PPT) synthesized by treatment of TiO_(2)(rutile) powder with molten mixture of KOH and KNO_(3) taken in a weight ratio of 30∶30∶40 has been carried out.It was shown that the studied type of PPT powder exhibits catalytic properties in the reaction of thermal decomposition of PP,compared to the effect of commercial zeolite catalyst CBV-780 traditionally used for this purpose.Based on the analysis performed,the differences in the mechanism of catalytic action of PPT and the zeolite were considered.The reasons for the observed differences in the composition of PP cracking products and in the rate of coke formation on the surface of studied catalysts were analyzed.Considering the obtained results,it has been proposed that the CBV-780 catalyst promoted more intensive production of the gaseous hydrocarbons compared to PPT,due to higher specific surface area(internal surface) accessible for relatively light and small-sized hydrocarbon products of cracking.However,intensive coke formation on the outer surface of the microporous zeolite contributes to the blocking of transport channels and the rapid loss of catalytic action.At the same time,PPT,which initially has a smaller specific surface area,retains its catalytic activity significantly longer due to slit-shaped flat pores and higher transport accessibility of the inner surface.
文摘The present study presents an assessment of the interrelations between long-chain branching,specific nucleation,and end-use properties of polypropylene blends:blends of linear polypropylene(L-PP)and long-chain branched polypropylene(LCB-PP)modified by a specificβ-nucleating agent(NA).Specimens with various LCB-PP compositions with and without NA were prepared under complex flow fields by injection molding.Wide-angle X-ray scattering was employed to capture the X-ray patterns of both the skin and core of the specimens,determining the overall crystallinity and amounts of individual polymorphs.The increasing content of LCB-PP andγ-phase,at the same time,in the blends is reflected in both increasing crystallinity and improved mechanical properties,namely,yield stress and Young’s modulus.On the other hand,the composition of the blends had no significant effect on the impact strength,except for nucleated L-PP.It has been demonstrated that adding a relatively small amount of LCB-PP is sufficient to modify the mechanical properties of linear polypropylene.Even a very small amount of LCB-PP in the L-PP suppressed the effectiveness of NA.
基金financially supported by the Technology Innovation Program(or Industrial Strategic Technology Development Program)(No.20017666)funded by the Ministry of Trade,Industry,and Energy(MOTIE,Korea)。
文摘This study reports the fabrication of polypropylene(PP)-based microfiber webs(<1µm) using a hybrid melt electrospinning/blown process with the aim of establishing a scalable and solvent-free platform for advanced lithium-ion battery separators. The primary objective was to address the inherent limitations of conventional melt electrospinning particularly the difficulty of achieving fiber thinning due to the high viscosity of polymer melts by incorporating auxiliary hot air flow and reducing the nozzle diameter from 1.0mm to 0.3mm. This modified configuration enables enhanced jet elongation and fiber diameter control under processing conditions relevant to industrial applications. The effects of nozzle temperature, hot air temperature, and applied voltage on fiber formation and jet behavior were systematically examined using highspeed charge-coupled device(CCD) imaging techniques. The results demonstrated that increasing both the hot air temperature and applied voltage significantly improved fiber thinning and uniformity, yielding an average fiber diameter of approximately 0.86µm without evidence of thermal degradation. In contrast, elevated nozzle temperatures, while enhancing melt flowability, resulted in increased discharge rates and hindered fiber refinement when applied alone. These findings identify hot-air temperature as the most robust and controllable parameter for producing submicron fibers while maintaining the polymer integrity. Although the present study primarily focuses on morphological optimization and jet dynamics, future research will investigate the functional performance of fabricated microfiber webs as battery separators. Overall, the proposed hybrid process offers a technically feasible and environmentally sustainable route for the continuous production of fine PP-based fibers tailored for high-performance energy-storage applications.
文摘Geological samples often contain significant amounts of iron,which,although not typically the target element,can substantially interfere with the analysis of other elements of interest.To mitigate these interferences,amidoximebased radiation grafted adsorbents have been identified as effective for iron removal.In this study,an amidoximefunctionalized,radiation-grafted adsorbent synthesized from polypropylene waste(PPw-g-AO-10)was employed to remove iron from leached geological samples.The adsorption process was systematically optimized by investigating the effects of pH,contact time,adsorbent dosage,and initial ferric ion concentration.Under optimal conditions-pH1.4,a contact time of 90 min,and an initial ferric ion concentration of 4500 mg/L-the adsorbent exhibited a maximum iron adsorption capacity of 269.02 mg/g.After optimizing the critical adsorption parameters,the adsorbent was applied to the leached geological samples,achieving a 91%removal of the iron content.The adsorbent was regenerated through two consecutive cycles using 0.2 N HNO_(3),achieving a regeneration efficiency of 65%.These findings confirm the efficacy of the synthesized PPw-g-AO-10 as a cost-effective and eco-friendly adsorbent for successfully removing iron from leached geological matrices while maintaining a reasonable degree of reusability.
基金the financial support of this work by the National Natural Science Foundation of China(Grant 21878089).
文摘Polypropylene(PP)has a relatively low melt strength due to its linear structure,which seriously limits its supercritical CO_(2)foaming performance.Introducing long-chain branches(LCBs)via grafting can significantly enhance its melt strength.However,the relationship between the LCB level of high melt strength polypropylene(HMSPP)and its foaming behavior remains unclear.In this study,a series of HMSPP with different LCB levels was prepared using vinyl polydimethylsiloxane(VS)of varying viscosities as grafting monomers to investigate this relationship.Rheological analysis showed that the increase in viscosity of VS led to higher LCB levels in HMSPP.The melt strength of HMSPP increases with the increase of LCB levels,reaching up to 0.62 N,which is 13 times higher than that of the raw material.Supercritical CO_(2)foaming results revealed that the expansion ratio of HMSPP first increased and then decreased with the increase of melt strength,reaching a maximum of 39.4 times.Combining experiments with simulations,the influence of LCB levels on the dissolution and diffusion behavior of CO_(2)in HMSPP was clarified.This study deepens the understanding of the relationship between LCB and the foaming behavior of HMSPP,providing valuable insights for designing HMSPP with optimized foaming properties.
基金supported by the National Natural Science Foundation of China(No.52077151)the State Key Laboratory of Electrical Insulation and Power Equipment(No.EIPE23208)the Key Laboratory of Engineering Dielectrics and Its Application,Ministry of Education(No.KFM202203).
文摘This study focuses on the electrical properties and microstructure of polypropylene(PP)-based blends used for cable insulation in nuclear power plants(NPPs).The PP-based blend,comprising isotactic PP and propylene-based elastomer(PBE)at concentrations ranging from 0 to 50 wt%,underwent a melt blending process and subsequent cobalt-60 gamma-ray irradiation with doses ranging from 0 to 250 kGy.Electrical conductivity,trap distribution,and alternating(AC)breakdown strength were chosen to assess the insulation performance.These results indicate that the addition of PBE significantly improves the electrical properties of PP under irradiation.For PP,the electrical conductivity increased with irradiation,whereas the trap depth and breakdown strength decreased sharply.Conversely,for the blend,these changes initially exhibit opposite trends.When the irradiation was increased to 250 kGy,the AC breakdown strength of the blend improved by more than 21%compared to that of PP.The physical and chemical structures of the samples were investigated to explore the improvement mechanisms.The results offer insights into the design of new cable-insulation materials suitable for NPPs.
基金Funded by the Natural Science Foundation of Shaanxi Province(No.2023-JC-QN-0553)。
文摘To examine the influences of waste polypropylene fiber(PPF)on the strength and internal pore structure of recycled aggregate concrete incorporating iron ore tailings,both the cubic compressive strength and axial compressive strength of the concrete were measured.Additionally,the microstructure was analyzed using scanning electron microscopy.The evolution of pore structure parameters,including pore size distribution,pore type distribution,and nuclear magnetic resonance spectral area in the concrete,was investigated through nuclear magnetic resonance(NMR)analysis.A model correlating the concrete's pore structure with its macroscopic performance was subsequently developed based on fractal theory.The results demonstrate that an appropriate amount of PPF created a bridging effect that decelerated the progression of macro cracks,enhanced the ductility of the concrete's failure mode,and increased both cubic compressive strength and axial compressive strength,with the most effective dosage being approximately 0.6%.An appropriate amount of PPF(ranging from 0.3%to 0.6%)facilitated the formation of harmless pores and shifted the pore size distribution towards medium and small sizes.Specifically,a fiber content of 0.6%resulted in the most significant reduction in the T2 spectral area.Furthermore,the pore structure of concrete exhibits distinct fractal characteristics.As the PPF content increased,the fractal dimension initially rose and then declined,demonstrating a strong correlation with the mechanical properties.
文摘Polypropylene(PP) accounts for approximately 28.0% of the global polyolefin market,valued at $243.4 billion in 2022.Known for its lightweight,chemical resistance,costeffectiveness,high strength and melting point,PP is widely used in various applications.Its properties and applications are closely tied to its tacticity.One-dimensional(1D) conventional 13C NMR has been extensively utilized to analyze PP tacticity,but its low sensitivity and longer relaxation time remain drawbacks.Typically,analyzing a single PP sample requires around 9 h of NMR time.Using of a cryogenically cooled 10 mm NMR probe can significantly reduce this measurement time;however,its high cost makes it inaccessible for most NMR laboratories.While the refocused insensitive nuclei enhanced by polarization transfer(RINEPT) technique is well-known for enhancing NMR sensitivity,there are no published studies using 1D 13C RINEPT to quantify PP tacticity.Relaxation agents like chromium(Ⅲ) acetylacetonate(Cr(acac)_(3)) have also been used to reduce relaxation times in polyolefin NMR analyses.Here we introduce a straightforward and easily implementable 1D 13C NMR method for rapid PP tacticity quantification.This method combines Cr(acac)_(3),Bruker's existing RINEPT pulse sequence(ineptrd),and our recently published ~1H decoupling sequence(bi_waltz65_256 pl) to eliminate ^(1)H decoupling artifacts.It is worth noting that decoupling artifacts are always present.When the signal-to-noise ratio(SNR) is low,these artifacts are obscured by noise.For example,in some two-dimensional(2D) or three-dimensional(3D) NMR spectra,decoupling artifacts are barely visible because of the low SNR.However,when attempting to observe weak signals in ^(1)D spectra,increasing the sample concentration or the number of scans enhances the SNR,revealing the decoupling artifacts.The decoupling artifacts appeared superimpose with some other weak signals,affecting the measurements of signal intensities.Therefore,improved ~1H-decoupling methods are crucial for such data acquisitio n.This synergy results in a 9.4-to 9.7-fold sensitivity enhancement,equating to an 88-to 94-fold reduction(9.4^(2)≈88,9.7^(2)≈94) in NMR acquisition time compared to conventional 1D ^(13)C NMR experiment with Cr(acac)_(3).The time savings are even more substantial compared to experiments without Cr(acac)_(3).The faster and quantitative approach is accessible to researchers with or without cryoprobes.Beyond PP,this method can be applied to tacticity measurements of other polyolefins,such as polybutene,polyhexene and polyoctene.