Modifed starch flms are gaining attention as biodegradable and sustainable materials in the food packaging industry.However,their inherent properties,including their brittleness and low antimicrobial and antioxidant c...Modifed starch flms are gaining attention as biodegradable and sustainable materials in the food packaging industry.However,their inherent properties,including their brittleness and low antimicrobial and antioxidant capacities,limit their extensive application.To address these shortcomings,in this study,a composite flm was developed using potato-modifed starch(PMS)as the base material,enhanced with konjac glucomannan(KGM),Pleurotus citrinopileatus polysaccharide(PCP),and nano titanium dioxide(nano TiO_(2)).Additionally,PCP and nano TiO_(2),which are bioactive components,were incorporated to improve the functional properties of the flms,promoting their application in food preservation.The optimal composition of the composite flms was determined through a fuzzy comprehensive evaluation,and the best performance was achieved with 10 g/L of PCP and 1.5 g/L of nano TiO_(2).These composite flms exhibited high mechanical strength,antimicrobial capacity,and antioxidant capacity while being noncytotoxic.The practical effcacy of the composite flms was verifed by applying them to preserve fresh-cut yams at room temperature,where they effectively delayed spoilage and maintained yam quality.This study demonstrates that PMS/KGM/PCP/nano TiO2 composite flms can signifcantly enhance the shelf life of fresh produce,providing a viable route for eco-friendly food preservation.展开更多
针对基于FROST阵列处理的最小均方算法(FROSR-least mean squares,FLMS)收敛速度较慢的缺点,将FLMS算法和变步长技术相结合,采用了一种基于Sigmoid函数的变步长快速自适应算法(variable step-size FROSR-least mean squares,VFLMS)。将...针对基于FROST阵列处理的最小均方算法(FROSR-least mean squares,FLMS)收敛速度较慢的缺点,将FLMS算法和变步长技术相结合,采用了一种基于Sigmoid函数的变步长快速自适应算法(variable step-size FROSR-least mean squares,VFLMS)。将该算法应用于GPS接收机空时自适应处理系统中,理论分析和计算机仿真表明,VFLMS算法能够抑制大于阵元个数的多个宽、窄带干扰,效果理想。展开更多
Polactide(PLA),poly(3-hydroxybutyrate-co-4-hydroxybutyrate)(P(3HB-CO-4HB)),and poly(butylene adipate co-terephthalate)(PBAT)ternary blends were prepared by extrusion blending.The biodegradable PLA/P(3HB-co 4HB)/PBAT f...Polactide(PLA),poly(3-hydroxybutyrate-co-4-hydroxybutyrate)(P(3HB-CO-4HB)),and poly(butylene adipate co-terephthalate)(PBAT)ternary blends were prepared by extrusion blending.The biodegradable PLA/P(3HB-co 4HB)/PBAT films were successfully obtained by using blown films technique.Excellnt siffness-toughness balance was achieved for 55/10/35 PLA/P(3HB-co 4HB)/PBAT film.The tensile strength reached 33.0 MPa(MD)and 23.5 MPa(TD).the elongation at break exceeded 1309%,and tear strength exceeded 110 kN/m.The Young's modulus as low as about 1800 MPa also met packaging applications.SEM observations revealed rough and long ligaments,indicating that the tear specimens were broken yieldingly.The addition of PBAT elastomers was the main reason for the improved toughness of the film.From DMA and SEM analysis,it was demonstrated that PLA P(3HB co 4HB),and PBAT were prilly compatible.With increasing P(3HB CO-4HB)content,the melt and cold crstallization of PLA was promoted.The enzymatic degradation experiments indicated that the films had good biodegradability.These findings gave important implications for designing and manufacturing biodegradation package of high biological carbon content.展开更多
基金supported by the Shenyang Medical College Scientifc Research Innovation Fund(Nos.20182033 and 20191038),China。
文摘Modifed starch flms are gaining attention as biodegradable and sustainable materials in the food packaging industry.However,their inherent properties,including their brittleness and low antimicrobial and antioxidant capacities,limit their extensive application.To address these shortcomings,in this study,a composite flm was developed using potato-modifed starch(PMS)as the base material,enhanced with konjac glucomannan(KGM),Pleurotus citrinopileatus polysaccharide(PCP),and nano titanium dioxide(nano TiO_(2)).Additionally,PCP and nano TiO_(2),which are bioactive components,were incorporated to improve the functional properties of the flms,promoting their application in food preservation.The optimal composition of the composite flms was determined through a fuzzy comprehensive evaluation,and the best performance was achieved with 10 g/L of PCP and 1.5 g/L of nano TiO_(2).These composite flms exhibited high mechanical strength,antimicrobial capacity,and antioxidant capacity while being noncytotoxic.The practical effcacy of the composite flms was verifed by applying them to preserve fresh-cut yams at room temperature,where they effectively delayed spoilage and maintained yam quality.This study demonstrates that PMS/KGM/PCP/nano TiO2 composite flms can signifcantly enhance the shelf life of fresh produce,providing a viable route for eco-friendly food preservation.
文摘针对基于FROST阵列处理的最小均方算法(FROSR-least mean squares,FLMS)收敛速度较慢的缺点,将FLMS算法和变步长技术相结合,采用了一种基于Sigmoid函数的变步长快速自适应算法(variable step-size FROSR-least mean squares,VFLMS)。将该算法应用于GPS接收机空时自适应处理系统中,理论分析和计算机仿真表明,VFLMS算法能够抑制大于阵元个数的多个宽、窄带干扰,效果理想。
基金This work was financially supported by the fund of Science and Technology Bureau of Jilin Province of China(No.201702040125F)Chinese Academy of Sciences(Changchun Branch)(No.2020SYHZ0002)+1 种基金Science and Technology Services Network Program of Chinese Academy of Sciences(STS Project)(No.KFJ-STS-ZDTP-082)the National Science Foundation of Zhejiang Province of China(No.LQY19B040001).
文摘Polactide(PLA),poly(3-hydroxybutyrate-co-4-hydroxybutyrate)(P(3HB-CO-4HB)),and poly(butylene adipate co-terephthalate)(PBAT)ternary blends were prepared by extrusion blending.The biodegradable PLA/P(3HB-co 4HB)/PBAT films were successfully obtained by using blown films technique.Excellnt siffness-toughness balance was achieved for 55/10/35 PLA/P(3HB-co 4HB)/PBAT film.The tensile strength reached 33.0 MPa(MD)and 23.5 MPa(TD).the elongation at break exceeded 1309%,and tear strength exceeded 110 kN/m.The Young's modulus as low as about 1800 MPa also met packaging applications.SEM observations revealed rough and long ligaments,indicating that the tear specimens were broken yieldingly.The addition of PBAT elastomers was the main reason for the improved toughness of the film.From DMA and SEM analysis,it was demonstrated that PLA P(3HB co 4HB),and PBAT were prilly compatible.With increasing P(3HB CO-4HB)content,the melt and cold crstallization of PLA was promoted.The enzymatic degradation experiments indicated that the films had good biodegradability.These findings gave important implications for designing and manufacturing biodegradation package of high biological carbon content.