The polymethyl-methacrylate (PMMA)-based composites were prepared using goose feather fibers at different diameters. The fibers, which were washed and dried, cut through the shaft, and their sizes were shrunk to short...The polymethyl-methacrylate (PMMA)-based composites were prepared using goose feather fibers at different diameters. The fibers, which were washed and dried, cut through the shaft, and their sizes were shrunk to short fiber form. Then the obtained short fibers were added into acryl matrix in portions of 2%, 4%, 6%, and 8% in volume. The mixture containing goose feather fiber was shaped via free casting method, and the goose feather fiber/PMMA composites were obtained. The samples, which were processed in accordance with the standards of test to be implemented after the thermal curing process, were characterized in terms of the mechanical properties after being evaluated by using three-point flexure test and impact test. For the goose feather-added composites, a significant increase was observed in rupture resistance, flexural strength, and flexure module. The flexure test curves of composites clearly revealed the slow and stable crack enlargement. Micro mechanisms of toughening and rupture processes were observed under the light of microstructure of rupture surfaces. The results of present study showed that the goose feather can be used as an important reinforcing material for bio-composites.展开更多
The present work is an attempt to develop bio-based hybrid composites by incorporating Betel nut Fiber(BF)and Chicken feather Fiber(CF)at different ratios in modified soybean oil matrix by compression molding techniqu...The present work is an attempt to develop bio-based hybrid composites by incorporating Betel nut Fiber(BF)and Chicken feather Fiber(CF)at different ratios in modified soybean oil matrix by compression molding technique.The ratio of the fiber and resin was taken as 30:70.Epoxidised soybean oil(ESO)was modified by using methacrylic acid and methacrylic anhydride.The ratio of CF and BF was varied from 2:1 to 1:2 respectively.The influence of hybrid fibers and fiber ratio on various properties of the composites was investigated.The obtained results showed that composites prepared with 1:1 ratio of CF and BF exhibited highest tensile strength compared to the other composites prepared by using different ratios of CF and BF.The surface morphology of the composites was studied by Scanning Electron Microscopy(SEM),where surface roughness was found to be decreased after incorporation of hybrid fibers.Thermogravimetric analysis was carried out to study the behaviour of the composites at high temperature,where thermal stability was found to enhance for hybrid composites compared to the composites prepared with single fibers.Also properties like water vapour uptake capacity and volumetric swelling were measured and found to be decreased for the hybrid composites.An overall improvement in properties was observed for composites having 1:1 ratio of CF:BF.Hence,it is concluded that 1:1 weight ratio of CF and BF is the optimum mixing ratio to enhance the various properties of the hybrid composites.展开更多
We studied the effect of wollastonite nanofibers on fluid flow in medium-density fiberboard （MDF）. Nanowollastonite （NW） was applied in MDF at 10 %, based on the dry weight of wood fibers. We also tested chicken f...We studied the effect of wollastonite nanofibers on fluid flow in medium-density fiberboard （MDF）. Nanowollastonite （NW） was applied in MDF at 10 %, based on the dry weight of wood fibers. We also tested chicken feathers as an additive to the matrix at 5 and 10 % by weight. The weight of feathers was reduced from the wood fibers to keep the density of the panels constant （0.66 g cm-3）. Wollastonite nanofibers acted as filler in the matrix and significantly decreased gas and liquid perme- ability. Higher thermal conductivity of the N-W-treated MDF-mats resulted in a better cure of resin, and conse- quently more integrity in the composite-matrix and lower permeability. The water-repellant property of wollastonite also contributed to the decrease in liquid permeability. Feathers reduced gas and liquid permeability due to the hydrophobic nature of keratin, as well as its formation as a physical barrier towards passing of fluids. Ten percent feather content proved too high and some checks and cracks occurred in the core of the panels after hot-pressing. Panels with 5 %-feather content resulted in both lower fluid flow and adequate physical integrity in the core sec- tion of the MDF-matrix.展开更多
文摘The polymethyl-methacrylate (PMMA)-based composites were prepared using goose feather fibers at different diameters. The fibers, which were washed and dried, cut through the shaft, and their sizes were shrunk to short fiber form. Then the obtained short fibers were added into acryl matrix in portions of 2%, 4%, 6%, and 8% in volume. The mixture containing goose feather fiber was shaped via free casting method, and the goose feather fiber/PMMA composites were obtained. The samples, which were processed in accordance with the standards of test to be implemented after the thermal curing process, were characterized in terms of the mechanical properties after being evaluated by using three-point flexure test and impact test. For the goose feather-added composites, a significant increase was observed in rupture resistance, flexural strength, and flexure module. The flexure test curves of composites clearly revealed the slow and stable crack enlargement. Micro mechanisms of toughening and rupture processes were observed under the light of microstructure of rupture surfaces. The results of present study showed that the goose feather can be used as an important reinforcing material for bio-composites.
基金The author,Gitashree Gogoi greatly acknowledged University Grants Commission(UGC),New Delhi,for providing the financial assistance(as fellowship).Grant number-NFO-2018-19-OBC-ASS-75119.
文摘The present work is an attempt to develop bio-based hybrid composites by incorporating Betel nut Fiber(BF)and Chicken feather Fiber(CF)at different ratios in modified soybean oil matrix by compression molding technique.The ratio of the fiber and resin was taken as 30:70.Epoxidised soybean oil(ESO)was modified by using methacrylic acid and methacrylic anhydride.The ratio of CF and BF was varied from 2:1 to 1:2 respectively.The influence of hybrid fibers and fiber ratio on various properties of the composites was investigated.The obtained results showed that composites prepared with 1:1 ratio of CF and BF exhibited highest tensile strength compared to the other composites prepared by using different ratios of CF and BF.The surface morphology of the composites was studied by Scanning Electron Microscopy(SEM),where surface roughness was found to be decreased after incorporation of hybrid fibers.Thermogravimetric analysis was carried out to study the behaviour of the composites at high temperature,where thermal stability was found to enhance for hybrid composites compared to the composites prepared with single fibers.Also properties like water vapour uptake capacity and volumetric swelling were measured and found to be decreased for the hybrid composites.An overall improvement in properties was observed for composites having 1:1 ratio of CF:BF.Hence,it is concluded that 1:1 weight ratio of CF and BF is the optimum mixing ratio to enhance the various properties of the hybrid composites.
基金supported by Shahid Rajaee Teacher Training University
文摘We studied the effect of wollastonite nanofibers on fluid flow in medium-density fiberboard （MDF）. Nanowollastonite （NW） was applied in MDF at 10 %, based on the dry weight of wood fibers. We also tested chicken feathers as an additive to the matrix at 5 and 10 % by weight. The weight of feathers was reduced from the wood fibers to keep the density of the panels constant （0.66 g cm-3）. Wollastonite nanofibers acted as filler in the matrix and significantly decreased gas and liquid perme- ability. Higher thermal conductivity of the N-W-treated MDF-mats resulted in a better cure of resin, and conse- quently more integrity in the composite-matrix and lower permeability. The water-repellant property of wollastonite also contributed to the decrease in liquid permeability. Feathers reduced gas and liquid permeability due to the hydrophobic nature of keratin, as well as its formation as a physical barrier towards passing of fluids. Ten percent feather content proved too high and some checks and cracks occurred in the core of the panels after hot-pressing. Panels with 5 %-feather content resulted in both lower fluid flow and adequate physical integrity in the core sec- tion of the MDF-matrix.