The conventional melting methods were used to obtain in situ TiC particle-reinforced dual-phase steel,followed by hot rolling and heat treatment processes.The aim was to investigate the effect of TiC particles on the ...The conventional melting methods were used to obtain in situ TiC particle-reinforced dual-phase steel,followed by hot rolling and heat treatment processes.The aim was to investigate the effect of TiC particles on the fracture behavior of dual-phase steel at different annealing temperatures,by analyzing the microstructure and tensile behavior of the multiscale TiC particle-reinforced dual-phase steel.The results showed that TiC particles precipitated in the as-cast microstructure of dual-phase steel were distributed along the grain boundaries.During hot rolling,the grain boundary-like morphology of the micron-sized TiC particles was disrupted,and the particles became more refined and evenly distributed in the matrix.The tensile tests revealed that the strength of the TiC particle-reinforced dual-phase steel increased with increasing martensite content,while the elongation decreased.These results were similar to those of conventional steel.The addition of 1 vol.%multiscale TiC particles improved the strength of the dual-phase steel but did not affect elongation of the steel.Cracks and holes were primarily concentrated around the TiC particles rather than at the interface of martensite and ferrite.The main causes of crack sprouting were TiC particle interface cracking and TiC particle internal fragmentation.Overall,the study demonstrated the potential of multiscale TiC particle-reinforced dual-phase steel as a strong and tough material.The refined distribution of TiC particles in the matrix improved the strength of the material without compromising its elongation.The results also highlighted the importance of careful selection of reinforcement particles to avoid detrimental effects on the fracture behavior of the material.展开更多
Similar to other metallic materials,duplex stainless steel dramatically loses its advantage of high ductility as they are strengthened.Here,we produce a gradient nanograined dual-phase structure in the 2101 duplex sta...Similar to other metallic materials,duplex stainless steel dramatically loses its advantage of high ductility as they are strengthened.Here,we produce a gradient nanograined dual-phase structure in the 2101 duplex stainless steel,thus facilitating a superior strength-ductility synergy:a yield strength of 1009.5 MPa being two times higher than that of the as-received sample,a total elongation of 23.4%and a uniform elongation of 5.9%.This novel structure is produced through a processing route of ultrasonic severe surface rolling and annealing,which realizes a superposition of gradient nanostructure and lamellar dual-phase structure with austenite and ferrite.During the tension deformation of gradi-ent nanograined dual-phase structured duplex stainless steel,a significant accumulation of geometrically necessary dislocations occurs.These dislocations are formed to accommodate the deformation incompat-ibility caused by the layer-by-layer difference in strength and hardness of individual phase domains,as well as the inherent difference in properties between the austenite and ferrite domains.This results in a stronger hetero-deformation induced strengthening and hardening significantly contributing to superior mechanical properties.Our study provides a new avenue to develop advanced steels with high strength and ductility.展开更多
Continuous annealing simulation is used in studying the influence of continuous annealing process parameters on the microstructure and mechanical properties of a GPa-grade C-Si-Mn-Cr-Mo dual-phase steel.The experiment...Continuous annealing simulation is used in studying the influence of continuous annealing process parameters on the microstructure and mechanical properties of a GPa-grade C-Si-Mn-Cr-Mo dual-phase steel.The experimental results indicate that increasing soaking time increases the volume fraction of martensite and the size of martensite islands, as well as tensile strength(TS) and yield strength(YS),while decreasing plasticity.As the steel slowly cools to a lower temperature prior to final quenching, TS and YS decrease, whereas elongation increases.The decrease in martensite content is due to the partial decomposition of austenite into ferrite during long slow cooling before quenching.As overaging temperature increases because of the tempering of martensite and aging of ferrite, TS decreases and YS increases.Work hardening analysis shows that in the initial stage of deformation, low overaging temperatures enhance work hardening ability.展开更多
Different stress states have a significant influence on the magnitude of the microscopic plastic strain and result in the development of the microstructure evolution.As a result,a comprehensive understanding of the di...Different stress states have a significant influence on the magnitude of the microscopic plastic strain and result in the development of the microstructure evolution.As a result,a comprehensive understanding of the different scale variation on microstructure evolution during bending deformation is essential.The advanced high strength dual-phase(DP1180)steel was investigated using multiscale microstructure-based 3D representative volume element(RVE)modelling technology with emphasis on understanding the relationship between the microstructure,localised stress-strain evolution as well as the deformation characteristics in the bending process.It is demonstrated that the localised development in bending can be more accurately described by microscopic deformation when taking into account microstructural properties.Microstructure-based 3D RVEs from each chosen bending condition generally have comparable localisation properties,whilst the magnitudes and intensities differ.In addition,the most severe localised bands are predicted to occur close to the ferrite and martensite phase boundaries where the martensite grains are close together or have a somewhat sharp edge.The numerically predicted results for the microstructure evolution,shear bands development and stress and strain distribution after 3-point bending exhibit a good agreement with the relevant experimental observations.展开更多
Six new lanthanide complexes:[Ln(3,4-DEOBA)3(4,4'-DM-2,2'-bipy)]2·2C_(2)H_(5)OH,[Ln=Dy(1),Eu(2),Tb(3),Sm(4),Ho(5),Gd(6);3,4-DEOBA-=3,4-diethoxybenzoate,4,4'-DM-2,2'-bipy=4,4'-dimethyl-2,2'...Six new lanthanide complexes:[Ln(3,4-DEOBA)3(4,4'-DM-2,2'-bipy)]2·2C_(2)H_(5)OH,[Ln=Dy(1),Eu(2),Tb(3),Sm(4),Ho(5),Gd(6);3,4-DEOBA-=3,4-diethoxybenzoate,4,4'-DM-2,2'-bipy=4,4'-dimethyl-2,2'-bipyridine]were successfully synthesized by the volatilization of the solution at room temperature.The crystal structures of six complexes were determined by single-crystal X-ray diffraction technology.The results showed that the complexes all have a binuclear structure,and the structures contain free ethanol molecules.Moreover,the coordination number of the central metal of each structural unit is eight.Adjacent structural units interact with each other through hydrogen bonds and further expand to form 1D chain-like and 2D planar structures.After conducting a systematic study on the luminescence properties of complexes 1-4,their emission and excitation spectra were obtained.Experimental results indicated that the fluorescence lifetimes of complexes 2 and 3 were 0.807 and 0.845 ms,respectively.The emission spectral data of complexes 1-4 were imported into the CIE chromaticity coordinate system,and their corre sponding luminescent regions cover the yellow light,red light,green light,and orange-red light bands,respectively.Within the temperature range of 299.15-1300 K,the thermal decomposition processes of the six complexes were comprehensively analyzed by using TG-DSC/FTIR/MS technology.The hypothesis of the gradual loss of ligand groups during the decomposition process was verified by detecting the escaped gas,3D infrared spectroscopy,and ion fragment information detected by mass spectrometry.The specific decomposition path is as follows:firstly,free ethanol molecules and neutral ligands are removed,and finally,acidic ligands are released;the final product is the corresponding metal oxide.CCDC:2430420,1;2430422,2;2430419,3;2430424,4;2430421,5;2430423,6.展开更多
In this study,a novel polysaccharide GPA-G 2-H was derived from ginseng.Furthermore,the coherent study of its structural characteristics,fermented characteristics in vitro,as well as antioxidant mechanism of fermented...In this study,a novel polysaccharide GPA-G 2-H was derived from ginseng.Furthermore,the coherent study of its structural characteristics,fermented characteristics in vitro,as well as antioxidant mechanism of fermented product FGPA-G 2-H on Aβ25-35-induced PC 12 cells were explored.The structure of GPA-G 2-H was determined by means of zeta potential analysis,FTIR,HPLC,XRD,GC-MS and NMR.The backbone of GPA-G 2-H was mainly composed of→4)-α-D-Glcp-(1→with branches substituted at O-3.Notably,GPA-G 2-H was degraded by intestinal microbiota in vitro with total sugar content and pH value decreasing,and short-chain fatty acids(SCFAs)increasing.Moreover,GPA-G 2-H significantly promoted the proliferation of Lactobacillus,Muribaculaceae and Weissella,thereby making positive alterations in intestinal microbiota composition.Additionally,FGPA-G 2-H activated the Nrf 2/HO-1 signaling pathway,enhanced HO-1,NQO 1,SOD and GSH-Px,while inhabited Keap 1,MDA and LDH,which alleviated Aβ-induced oxidative stress in PC 12 cells.These provide a solid theoretical basis for the further development of ginseng polysaccharides as functional food and antioxidant drugs.展开更多
The accurate establishment of a ferrite transformation start temperature model is crucial to design a reasonable controlled rolling process and ensure uniform microstructure in aluminum bearing dual-phase steel.The me...The accurate establishment of a ferrite transformation start temperature model is crucial to design a reasonable controlled rolling process and ensure uniform microstructure in aluminum bearing dual-phase steel.The measurements of the expansion-temperature curves of aluminum bearing dual-phase steel under continuous cooling and isothermal conditions are presented,utilizing a dynamic transformation dilatometer experiment.Based on these expansion-temperature curves,the start temperature and incubation time of ferrite transformation were determined,elucidating the influence of process parameters on both the incubation time and the start temperature of ferrite transformation.By integrating metallurgical principles with measured incubation time of ferrite transformation,and considering the effects of temperature and strain,a fitting model for the variation in volume free energy during ferrite nucleation was derived.Building upon this foundation,a high-precision incubation time of ferrite transformation mathematical model for the experimental steel was established.To more accurately calculate the start temperature of ferrite transformation under continuous cooling conditions,the Scheil’s additivity rule was modified to account for the effects of deformation and cooling rate.The results indicate that the modification coefficient decreases with increasing the cooling rate and strain,thereby significantly improving the accuracy of calculating the starting temperature of ferrite transformation using the modified additivity rule.展开更多
Conformal truss-like lattice structures face significant manufacturability challenges in additive manufac-turing due to overhang angle limitations.To address this problem,we propose a novel angle-constrained optimizat...Conformal truss-like lattice structures face significant manufacturability challenges in additive manufac-turing due to overhang angle limitations.To address this problem,we propose a novel angle-constrained optimization method grounded in the global adjustment of nodal coordinates.First,a build direction is selected to minimize the number of violating struts.Then,an angular-constraint matrix is assembled from strut direction vectors,and analytical sensitivities with respect to nodal coordinates are derived to enable efficient constrained optimization under nonlinear angular inequality constraints.Numerical studies on two complex curved-surface lattices demonstrate that all overhang violations are eliminated while only minor changes are induced in global stiffness and strength.In particular,the maximum displacement of an ergonomic insole varies by only 2.87%after optimization.The results confirm the method’s versatility and engineering robustness,providing a practical approach for additive manufacturing-oriented lattice structure design.展开更多
Deployable Composite Thin-Walled Structures(DCTWS)are widely used in space applications due to their ability to compactly fold and self-deploy in orbit,enabled by cutouts.Cutout design is crucial for balancing structu...Deployable Composite Thin-Walled Structures(DCTWS)are widely used in space applications due to their ability to compactly fold and self-deploy in orbit,enabled by cutouts.Cutout design is crucial for balancing structural rigidity and flexibility,ensuring material integrity during large deformations,and providing adequate load-bearing capacity and stability once deployed.Most research has focused on optimizing cutout size and shape,while topology optimization offers a broader design space.However,the anisotropic properties of woven composite laminates,complex failure criteria,and multi-performance optimization needs have limited the exploration of topology optimization in this field.This work derives the sensitivities of bending stiffness,critical buckling load,and the failure index of woven composite materials with respect to element density,and formulates both single-objective and multi-objective topology optimization models using a linear weighted aggregation approach.The developed method was integrated with the commercial finite element software ABAQUS via a Python script,allowing efficient application to cutout design in various DCTWS configurations to maximize bending stiffness and critical buckling load under material failure constraints.Optimization of a classical tubular hinge resulted in improvements of 107.7%in bending stiffness and 420.5%in critical buckling load compared to level-set topology optimization results reported in the literature,validating the effectiveness of the approach.To facilitate future research and encourage the broader adoption of topology optimization techniques in DCTWS design,the source code for this work is made publicly available via a Git Hub link:https://github.com/jinhao-ok1/Topo-for-DCTWS.git.展开更多
Sandwich structures are widely favored for their lightweight,high strength and superior impact mitigation capabilities in blast mitigation and transportation safety applications.Their application in large-scale,high-e...Sandwich structures are widely favored for their lightweight,high strength and superior impact mitigation capabilities in blast mitigation and transportation safety applications.Their application in large-scale,high-energy rockfall protection remains limited due to their relatively low volumetric energy absorption efficiency and the complex fabrication processes of key energy-absorbing components.To address these limitations,this study proposes a novel sandwich structure incorporating mild steel tubes as core energy absorbers to efficiently mitigate highenergy rockfall impacts.A finite element model was developed in LS-DYNA to systematically investigate the deformation and energy absorption behaviors.Comprehensive parametric analyses were conducted to quantify the effects of key design variables,including tube wall thickness,tube spacing(number of tubes),and infill materials.The results demonstrate that increasing tube wall thickness significantly enhances ultimate energy absorption,with 12-mm-thick tubes absorbing 2.2 times more energy than 6-mm-thick tubes.Lateral constraints induced by adjacent tubes improve specific energy absorption per unit displacement by approximately 30%-45%.Furthermore,incorporating infill materials considerably enhances energy absorption,with aluminum foam infills achieving an 81%increase compared to empty tubes.Nevertheless,higher energy absorption capacity typically leads to greater peak impact forces,increasing the number of tubes offers a better balance between energy absorption and impact force,optimizing the structural performance.These findings provide valuable theoretical insights and practical guidelines for designing sandwich structures in civil and infrastructure engineering applications for effective rockfall protection.展开更多
Low-velocity impact tests are carried out to explore the energy absorption characteristics of bio-inspired lattices,mimicking the architecture of the marine sponge organism Euplectella aspergillum.These sea sponge-ins...Low-velocity impact tests are carried out to explore the energy absorption characteristics of bio-inspired lattices,mimicking the architecture of the marine sponge organism Euplectella aspergillum.These sea sponge-inspired lattice structures feature a square-grid 2D lattice with double diagonal bracings and are additively manufactured via digital light processing(DLP).The collapse strength and energy absorption capacity of sea sponge lattice structures are evaluated under various impact conditions and are compared to those of their constituent square-grid and double diagonal lattices.This study demonstrates that sea sponge lattices can achieve an 11-fold increase in energy absorption compared to the square-grid lattice,due to the stabilizing effect of the double diagonal bracings prompting the structure to collapse layer-bylayer under impact.By adjusting the thickness ratio in the sea sponge lattice,up to 76.7%increment in energy absorption is attained.It is also shown that sea-sponge lattices outperform well-established energy-absorbing materials of equal weight,such as hexagonal honeycombs,confirming their significant potential for impact mitigation.Additionally,this research highlights the enhancements in energy absorption achieved by adding a small amount(0.015 phr)of Multi-Walled Carbon Nanotubes(MWCNTs)to the photocurable resin,thus unlocking new possibilities for the design of innovative lightweight structures with multifunctional attributes.展开更多
To elucidate the effect of calcite-regulated activated carbon(AC)structure on low-temperature denitrification performance of SCR catalysts,this work prepared a series of Mn-Ce/De-AC-xCaCO_(3)(x is the calcite content ...To elucidate the effect of calcite-regulated activated carbon(AC)structure on low-temperature denitrification performance of SCR catalysts,this work prepared a series of Mn-Ce/De-AC-xCaCO_(3)(x is the calcite content in coal)catalysts were prepared by the incipient wetness impregnation method,followed by acid washing to remove calcium-containing minerals.Comprehensive characterization and low-temperature denitrification tests revealed that calcite-induced structural modulation of coal-derived AC significantly enhances catalytic activity.Specifically,NO conversion increased from 88.3%of Mn-Ce/De-AC to 91.7%of Mn-Ce/De-AC-1CaCO_(3)(210℃).The improved SCR denitrification activity results from the enhancement of physicochemical properties including higher Mn^(4+)content and Ce^(4+)/Ce^(3+)ratio,an abundance of chemisorbed oxygen and acidic sites,which could strengthen the SCR reaction pathways(richer NH_(3)activated species and bidentate nitrate active species).Therefore,NO removal is enhanced.展开更多
Anchovies are key forage species in coastal and pelagic food webs,playing crucial ecological and commercial roles in marine ecosystems.Encrasicholina punctifer is a commercially and ecologically important species,yet ...Anchovies are key forage species in coastal and pelagic food webs,playing crucial ecological and commercial roles in marine ecosystems.Encrasicholina punctifer is a commercially and ecologically important species,yet little is known about its osteological development characteristics.Understanding these ontogenetic patterns is essential for explaining phylogenetic relationships within Clupeiformes,informing larval identification in ichthyoplankton surveys,and enhancing aquaculture practices.This study describes the ontogenetic characteristics of the appendicular and median skeletons and fin supports in E.punctifer larvae and juveniles,providing quantitative ontogenetic timelines to address gaps in engraulid developmental biology and contribute to teleost ontogeny research.Larval and juvenile specimens of E.punctifer;size range:3.00-34.56 mm standard length(SL)and notochord length(NL)collected from the Philippine Sea were processed using the standard Alizarin red and Alcian blue clearing-and-staining technique to differentiate ossified and cartilaginous elements.Specimens were examined under a stereo microscope and imaged with an HTC1600ISP digital camera for detailed morphological analysis of skeletal structures.Caudal complex development was evident by 5.55 mm NL,with the initial appearance of cartilaginous hypurals 1–2 and parhypural,followed by Hy3–5 at 6.08 mm NL.Cartilaginous Hy6 was visible by 9.58 mm SL in postflexion larvae.Six hypural bones were present from the postflexion to juvenile stage.Principal fin rays formed via intramembranous ossification at 6.32 mm NL,and segmentation was evident by 10.24 mm SL.Neural arch 1 appeared at 7.38 mm NL,preceding full haemal arch development.Uroneurals 1–2 and ural centra ossified by 9.58 mm SL,with Hy5 detached from U1 at 10.24 mm SL.Preural centra ossified before the arches.Epurals 1 and 2 were evident by 10.24 mm SL.Dorsal fin proximal radials developed anteriorly and distal radials posteriorly.Pectoral fin development initiated with an ossified cleithrum and the coracoscapular cartilage at 5.25 mm NL.By 10.24 mm SL,cartilaginous neural and haemal arches and spines were distinct.Uroneural 1 initially develops as cartilage.The formation of a pleurostyle aligns with clupeoid fish skeletal ontogeny.Dorsal and anal fin development follows a distinctive pattern,with variability in fin support development.Our results reveal accelerated caudal complex formation in E.punctifer and contribute new knowledge on the osteological characteristics of the genus Encrasicholina,and aid in understanding larval and juvenile ontogeny of marine teleosts.展开更多
Abuse of chloramphenicol(CAP)could cause serious side effects to human health.Therefore,it is necessary to detect CAP residues in animal sourced food effectively.Here,the superiority(better stability,higher Apt-CAP lo...Abuse of chloramphenicol(CAP)could cause serious side effects to human health.Therefore,it is necessary to detect CAP residues in animal sourced food effectively.Here,the superiority(better stability,higher Apt-CAP loading efficiency,and higher CAP binding associated conformational change,etc.)of tetrahedral structure to double-chained structure for developing aptasensor was evaluated.Then,a self-assembled DNA tetrahedral structure-based electrochemical aptasensor targeting CAP was developed.Under the optimized conditions,the aptasensor exhibited high sensitivity toward CAP with a limit of detection(LOD)of 0.0676 ng/m L(linear range 0.19-387.76 ng/m L),and high selectivity against the structural analogs of CAP.Moreover,the recovery rate of CAP from spiked milk samples ranged from 100.57%to 101.69%,and only USD 1.34 is needed for detecting CAP in 1 sample.These results suggested the application potential of this aptasesor for detecting CAP in animal sourced foods.展开更多
Background:Chronic inflammation is closely associated with the most common and socially significant prostate conditions,including benign prostatic hyperplasia(BPH),prostate cancer(PCa),and prostatitis syndromes.NIHcat...Background:Chronic inflammation is closely associated with the most common and socially significant prostate conditions,including benign prostatic hyperplasia(BPH),prostate cancer(PCa),and prostatitis syndromes.NIHcategory IV prostatitis(histologic prostatitis,HP)is defined as asymptomatic chronic inflammation of the prostate.The presence of lymphoid follicles,referred to as tertiary lymphoid structures(TLSs),along with benign lympho-epithelial lesions(BLELs),is among the key histological indicators of immune inflammation and can be assessed relatively easily.This study aimed to quantitatively assess TLSs and BLELs,as well as their relationship with the severity of HP.Methods:We investigated TLSs and BLELs in 110 prostatic specimens,including inflammatory and normal tissues,within the context of common prostate pathologies such as BPH and PCa.HP was graded as low-grade(LG)or high-grade(HG)based on the severity of inflammation.Results:TLSs were observed in 51 out of 110 cases(46.4%),while BLELs were identified in 78 cases(70.44%).Both TLSs and BLELs co-occurred in 45 cases(40.9%).Statistical analysis revealed a significant correlation between the presence of TLSs,BLELs(individually or combined),and HG-HP(p<0.001).Conclusions:This study is the first to quantitatively evaluate the immunopathologic patterns in the inflamed human prostate by analyzing the presence and cooccurrence of TLSs and BLELs.Their formation,likely triggered by antigenic stimuli and external factors,indicates a chronic inflammatory microenvironment.The strong association between TLSs,BLELs,and HG-HP underscores their potential role in HP aggressiveness.These findings suggest that TLSs and BLELs may be crucial contributors to the pathophysiology and morphogenesis of NIH-category IV prostatitis.Furthermore,TLS/BLEL formation may represent a hallmark of tissue autoimmunity,reflecting the immune or autoimmune phase of this prostatitis subtype.展开更多
The testing of large structures is limited by high costs and long cycles, making scaling methods an attractive solution. However, the scaling process of elastic rings introduces complexities in multi-parameter geometr...The testing of large structures is limited by high costs and long cycles, making scaling methods an attractive solution. However, the scaling process of elastic rings introduces complexities in multi-parameter geometric distortions, leading to a diminution in the predictive accuracy of the distorted similitude. To address this challenge, this study formulates a novel set of scaling laws, tailored to account for the intricate geometric distortions associated with elastic rings. The proposed scaling laws are formulated based on the intrinsic deformation characteristics of elastic rings, rather than the traditional systemic governing equations. Numerical and experimental cases are conducted to assess the efficacy and precision of the proposed scaling laws, and the obtained results are compared with those achieved by traditional methods. The outcomes demonstrate that the scaling laws put forth by this study significantly enhance the predictive capabilities for deformations of elastic rings.展开更多
Fine-grained nuclear graphite is a key material in high-temperature gas-cooled reactors(HTGRs).During air ingress accidents,core graphite components undergo severe oxidation,threatening structural integrity.Therefore,...Fine-grained nuclear graphite is a key material in high-temperature gas-cooled reactors(HTGRs).During air ingress accidents,core graphite components undergo severe oxidation,threatening structural integrity.Therefore,understanding the oxidation behavior of nuclear graphite is essential for reactor safety.The influence of oxidation involves multiple factors,including temperature,sample size,oxidant,impurities,filler type and size,etc.The size of the filler particles plays a crucial role in this study.Five ultrafine-and superfine-grained nuclear graphite samples(5.9-34.4μm)are manufactured using identical raw materials and manufacturing processes.Isothermal oxidation tests conducted at 650℃-750℃ are used to study the oxidation behavior.Additionally,comprehensive characterization is performed to analyze the crystal structure,surface morphology,and nanoscale to microscale pore structure of the samples.Results indicate that oxidation behavior cannot be predicted solely based on filler grain size.Reactive site concentration,characterized by active surface area,dominates the chemical reaction kinetics,whereas pore tortuosity,quantified by the structural parameterΨ,plays a key role in regulating oxidant diffusion.These findings clarify the dual role of microstructure in oxidation mechanisms and establish a theoretical and experimental basis for the design of high-performance nuclear graphite capable of long-term service in high-temperature gas-cooled reactors.展开更多
The strong connection between braids and knots provides valuable insights into studying the topological state and phase classification of various physical systems.The phenomenon of non-Hermitian(NH)two-and three-band ...The strong connection between braids and knots provides valuable insights into studying the topological state and phase classification of various physical systems.The phenomenon of non-Hermitian(NH)two-and three-band braiding has received widespread attention.However,a systematic exploration and visualization of non-Abelian braiding and the associated knot transformations in four-band systems remains unexplored.Here,we propose a theoretical model of NH four-band braiding,provide its phase diagram,and establish its trivial,Abelian,and non-Abelian braiding rules.Additionally,we report on special knots,such as the Hopf and Solomon links in braided knots,and reveal that their transformations are accompanied by and mediated through exceptional points.Our work provides a detailed case for studying NH multiband braiding and knot structures in four-band systems,which could offer insights for topological photonics and analog information processing applications.展开更多
In this study,the shell structure of olives in nature was modeled,and a high-porosity bionic olive body-centered cubic structure(BCCO)with reinforcement structures of circular support(BCCR)and triangular support(BCCT)...In this study,the shell structure of olives in nature was modeled,and a high-porosity bionic olive body-centered cubic structure(BCCO)with reinforcement structures of circular support(BCCR)and triangular support(BCCT)with excellent mechanical properties was designed and prepared using selective laser melting technology.The surface morphology,deformation behavior,and energy absorption of BCCO were compared with those of the equivalent uniform body-centered cubic structure(BCC)and analyzed through quasi-static compression experiments and finite element analysis.The olive-shaped structure showed optimal load resistance when the radius of curvature was equal to the edge length of the lattice structure,and outperformed with a larger curvature than with a smaller curvature.With the added support structure,the energy absorption of the BCCR increased by 144.44%compared with that of the conventional BCC structure.The newly designed olive bionic structure has considerable potential for applications in various fields,such as aerospace and medical devices.展开更多
To realize the practical application of anion exchange membrane water electrolysis(AEMWE),it is essential to develop highly active,durable,and cost-effective electrocatalyst for oxygen evolution reaction(OER).Herein,w...To realize the practical application of anion exchange membrane water electrolysis(AEMWE),it is essential to develop highly active,durable,and cost-effective electrocatalyst for oxygen evolution reaction(OER).Herein,we report a hollow-structured Ni_(x)Co_(1−x)O/Ni_(3)S_(2)/Co_(9)S_(8)heterostructure synthesized via sequential template-assisted growth,thermal oxidation,and controlled sulfidation process.The abundant bimetallic heterointerfaces not only provide additional active sites but also promote electronic modulation via charge redistribution.Additionally,the porous and hollow architecture enhances active surface area and mass transfer ability,thereby increasing the number of accessible active sites for alkaline OER.As a result,the prepared electrocatalyst achieves low overpotential of 310 mV at 10 mA cm^(−2)and small Tafel slope of 55.94 mV dec^(−1),demonstrating the exceptional electrocatalytic performance for alkaline OER.When integrated as the anode in an AEMWE cell,it delivers outstanding performance with only 1.657 V at 1.0 A cm^(−2)and reaches high current density of 5.0 A cm^(−2)at 1.989 V,surpassing those of commercial RuO_(2).The cell also shows excellent long-term durability over 100 h with minimal degradation.This study highlights the strong potential of rationally engineered oxide/sulfide heterostructures for next-generation alkaline water electrolysis.展开更多
基金the National Basic Research Program,China(No.2022YFB3705300)National Natural Science Foundation of China(Nos.52274380,51874089,and U1960112)LiaoNing Revitalization Talents Program(XLYC2007030).
文摘The conventional melting methods were used to obtain in situ TiC particle-reinforced dual-phase steel,followed by hot rolling and heat treatment processes.The aim was to investigate the effect of TiC particles on the fracture behavior of dual-phase steel at different annealing temperatures,by analyzing the microstructure and tensile behavior of the multiscale TiC particle-reinforced dual-phase steel.The results showed that TiC particles precipitated in the as-cast microstructure of dual-phase steel were distributed along the grain boundaries.During hot rolling,the grain boundary-like morphology of the micron-sized TiC particles was disrupted,and the particles became more refined and evenly distributed in the matrix.The tensile tests revealed that the strength of the TiC particle-reinforced dual-phase steel increased with increasing martensite content,while the elongation decreased.These results were similar to those of conventional steel.The addition of 1 vol.%multiscale TiC particles improved the strength of the dual-phase steel but did not affect elongation of the steel.Cracks and holes were primarily concentrated around the TiC particles rather than at the interface of martensite and ferrite.The main causes of crack sprouting were TiC particle interface cracking and TiC particle internal fragmentation.Overall,the study demonstrated the potential of multiscale TiC particle-reinforced dual-phase steel as a strong and tough material.The refined distribution of TiC particles in the matrix improved the strength of the material without compromising its elongation.The results also highlighted the importance of careful selection of reinforcement particles to avoid detrimental effects on the fracture behavior of the material.
基金supported by the National Natural Science Foundation of China(Nos.51974032,52174355,51874043,and 51604034)the Jilin Scientific and Technological Develop-ment Program(Nos.20220201106GX and YDZJ202201ZYTS669).
文摘Similar to other metallic materials,duplex stainless steel dramatically loses its advantage of high ductility as they are strengthened.Here,we produce a gradient nanograined dual-phase structure in the 2101 duplex stainless steel,thus facilitating a superior strength-ductility synergy:a yield strength of 1009.5 MPa being two times higher than that of the as-received sample,a total elongation of 23.4%and a uniform elongation of 5.9%.This novel structure is produced through a processing route of ultrasonic severe surface rolling and annealing,which realizes a superposition of gradient nanostructure and lamellar dual-phase structure with austenite and ferrite.During the tension deformation of gradi-ent nanograined dual-phase structured duplex stainless steel,a significant accumulation of geometrically necessary dislocations occurs.These dislocations are formed to accommodate the deformation incompat-ibility caused by the layer-by-layer difference in strength and hardness of individual phase domains,as well as the inherent difference in properties between the austenite and ferrite domains.This results in a stronger hetero-deformation induced strengthening and hardening significantly contributing to superior mechanical properties.Our study provides a new avenue to develop advanced steels with high strength and ductility.
文摘Continuous annealing simulation is used in studying the influence of continuous annealing process parameters on the microstructure and mechanical properties of a GPa-grade C-Si-Mn-Cr-Mo dual-phase steel.The experimental results indicate that increasing soaking time increases the volume fraction of martensite and the size of martensite islands, as well as tensile strength(TS) and yield strength(YS),while decreasing plasticity.As the steel slowly cools to a lower temperature prior to final quenching, TS and YS decrease, whereas elongation increases.The decrease in martensite content is due to the partial decomposition of austenite into ferrite during long slow cooling before quenching.As overaging temperature increases because of the tempering of martensite and aging of ferrite, TS decreases and YS increases.Work hardening analysis shows that in the initial stage of deformation, low overaging temperatures enhance work hardening ability.
基金supported by HBIS Group under the Grant No.IRIS 200506003.
文摘Different stress states have a significant influence on the magnitude of the microscopic plastic strain and result in the development of the microstructure evolution.As a result,a comprehensive understanding of the different scale variation on microstructure evolution during bending deformation is essential.The advanced high strength dual-phase(DP1180)steel was investigated using multiscale microstructure-based 3D representative volume element(RVE)modelling technology with emphasis on understanding the relationship between the microstructure,localised stress-strain evolution as well as the deformation characteristics in the bending process.It is demonstrated that the localised development in bending can be more accurately described by microscopic deformation when taking into account microstructural properties.Microstructure-based 3D RVEs from each chosen bending condition generally have comparable localisation properties,whilst the magnitudes and intensities differ.In addition,the most severe localised bands are predicted to occur close to the ferrite and martensite phase boundaries where the martensite grains are close together or have a somewhat sharp edge.The numerically predicted results for the microstructure evolution,shear bands development and stress and strain distribution after 3-point bending exhibit a good agreement with the relevant experimental observations.
文摘Six new lanthanide complexes:[Ln(3,4-DEOBA)3(4,4'-DM-2,2'-bipy)]2·2C_(2)H_(5)OH,[Ln=Dy(1),Eu(2),Tb(3),Sm(4),Ho(5),Gd(6);3,4-DEOBA-=3,4-diethoxybenzoate,4,4'-DM-2,2'-bipy=4,4'-dimethyl-2,2'-bipyridine]were successfully synthesized by the volatilization of the solution at room temperature.The crystal structures of six complexes were determined by single-crystal X-ray diffraction technology.The results showed that the complexes all have a binuclear structure,and the structures contain free ethanol molecules.Moreover,the coordination number of the central metal of each structural unit is eight.Adjacent structural units interact with each other through hydrogen bonds and further expand to form 1D chain-like and 2D planar structures.After conducting a systematic study on the luminescence properties of complexes 1-4,their emission and excitation spectra were obtained.Experimental results indicated that the fluorescence lifetimes of complexes 2 and 3 were 0.807 and 0.845 ms,respectively.The emission spectral data of complexes 1-4 were imported into the CIE chromaticity coordinate system,and their corre sponding luminescent regions cover the yellow light,red light,green light,and orange-red light bands,respectively.Within the temperature range of 299.15-1300 K,the thermal decomposition processes of the six complexes were comprehensively analyzed by using TG-DSC/FTIR/MS technology.The hypothesis of the gradual loss of ligand groups during the decomposition process was verified by detecting the escaped gas,3D infrared spectroscopy,and ion fragment information detected by mass spectrometry.The specific decomposition path is as follows:firstly,free ethanol molecules and neutral ligands are removed,and finally,acidic ligands are released;the final product is the corresponding metal oxide.CCDC:2430420,1;2430422,2;2430419,3;2430424,4;2430421,5;2430423,6.
基金Supported by the National Key Research and Development Program of Traditional Chinese Medicine Modernization Project,China(No.2023YFC3504000)the Science and Technology Development Project of Jilin Province,China(No.20240404043ZP)the Science and Technology Innovation Cooperation Project of Changchun Science and Technology Bureau and Chinese Academy of Sciences,China(No.23SH14)。
文摘In this study,a novel polysaccharide GPA-G 2-H was derived from ginseng.Furthermore,the coherent study of its structural characteristics,fermented characteristics in vitro,as well as antioxidant mechanism of fermented product FGPA-G 2-H on Aβ25-35-induced PC 12 cells were explored.The structure of GPA-G 2-H was determined by means of zeta potential analysis,FTIR,HPLC,XRD,GC-MS and NMR.The backbone of GPA-G 2-H was mainly composed of→4)-α-D-Glcp-(1→with branches substituted at O-3.Notably,GPA-G 2-H was degraded by intestinal microbiota in vitro with total sugar content and pH value decreasing,and short-chain fatty acids(SCFAs)increasing.Moreover,GPA-G 2-H significantly promoted the proliferation of Lactobacillus,Muribaculaceae and Weissella,thereby making positive alterations in intestinal microbiota composition.Additionally,FGPA-G 2-H activated the Nrf 2/HO-1 signaling pathway,enhanced HO-1,NQO 1,SOD and GSH-Px,while inhabited Keap 1,MDA and LDH,which alleviated Aβ-induced oxidative stress in PC 12 cells.These provide a solid theoretical basis for the further development of ginseng polysaccharides as functional food and antioxidant drugs.
基金supported by the National Science and Technology Major Project-Intelligent Manufacturing Systems And Robots(2025ZD1602200)the National Key Research and Development Program of China(Grant No.2022YFB3304800).
文摘The accurate establishment of a ferrite transformation start temperature model is crucial to design a reasonable controlled rolling process and ensure uniform microstructure in aluminum bearing dual-phase steel.The measurements of the expansion-temperature curves of aluminum bearing dual-phase steel under continuous cooling and isothermal conditions are presented,utilizing a dynamic transformation dilatometer experiment.Based on these expansion-temperature curves,the start temperature and incubation time of ferrite transformation were determined,elucidating the influence of process parameters on both the incubation time and the start temperature of ferrite transformation.By integrating metallurgical principles with measured incubation time of ferrite transformation,and considering the effects of temperature and strain,a fitting model for the variation in volume free energy during ferrite nucleation was derived.Building upon this foundation,a high-precision incubation time of ferrite transformation mathematical model for the experimental steel was established.To more accurately calculate the start temperature of ferrite transformation under continuous cooling conditions,the Scheil’s additivity rule was modified to account for the effects of deformation and cooling rate.The results indicate that the modification coefficient decreases with increasing the cooling rate and strain,thereby significantly improving the accuracy of calculating the starting temperature of ferrite transformation using the modified additivity rule.
基金supported by the National Natural Science Foundation of China(Grant Nos.12432005 and 12472116)the Fundamental Research Funds for the Central Universities(DUTZD25240).
文摘Conformal truss-like lattice structures face significant manufacturability challenges in additive manufac-turing due to overhang angle limitations.To address this problem,we propose a novel angle-constrained optimization method grounded in the global adjustment of nodal coordinates.First,a build direction is selected to minimize the number of violating struts.Then,an angular-constraint matrix is assembled from strut direction vectors,and analytical sensitivities with respect to nodal coordinates are derived to enable efficient constrained optimization under nonlinear angular inequality constraints.Numerical studies on two complex curved-surface lattices demonstrate that all overhang violations are eliminated while only minor changes are induced in global stiffness and strength.In particular,the maximum displacement of an ergonomic insole varies by only 2.87%after optimization.The results confirm the method’s versatility and engineering robustness,providing a practical approach for additive manufacturing-oriented lattice structure design.
基金supported by the National Natural Science Foundation of China(No.12202295)the International(Regional)Cooperation and Exchange Projects of the National Natural Science Foundation of China(No.W2421002)+2 种基金the Sichuan Science and Technology Program(No.2025ZNSFSC0845)Zhejiang Provincial Natural Science Foundation of China(No.ZCLZ24A0201)the Fundamental Research Funds for the Provincial Universities of Zhejiang(No.GK249909299001-004)。
文摘Deployable Composite Thin-Walled Structures(DCTWS)are widely used in space applications due to their ability to compactly fold and self-deploy in orbit,enabled by cutouts.Cutout design is crucial for balancing structural rigidity and flexibility,ensuring material integrity during large deformations,and providing adequate load-bearing capacity and stability once deployed.Most research has focused on optimizing cutout size and shape,while topology optimization offers a broader design space.However,the anisotropic properties of woven composite laminates,complex failure criteria,and multi-performance optimization needs have limited the exploration of topology optimization in this field.This work derives the sensitivities of bending stiffness,critical buckling load,and the failure index of woven composite materials with respect to element density,and formulates both single-objective and multi-objective topology optimization models using a linear weighted aggregation approach.The developed method was integrated with the commercial finite element software ABAQUS via a Python script,allowing efficient application to cutout design in various DCTWS configurations to maximize bending stiffness and critical buckling load under material failure constraints.Optimization of a classical tubular hinge resulted in improvements of 107.7%in bending stiffness and 420.5%in critical buckling load compared to level-set topology optimization results reported in the literature,validating the effectiveness of the approach.To facilitate future research and encourage the broader adoption of topology optimization techniques in DCTWS design,the source code for this work is made publicly available via a Git Hub link:https://github.com/jinhao-ok1/Topo-for-DCTWS.git.
基金supported by the National Key R&D Program of China(Grant No.2019YFC1509703)the Tianjin Science and Technology Program Project(Grant No.23YFYSHZ00130)。
文摘Sandwich structures are widely favored for their lightweight,high strength and superior impact mitigation capabilities in blast mitigation and transportation safety applications.Their application in large-scale,high-energy rockfall protection remains limited due to their relatively low volumetric energy absorption efficiency and the complex fabrication processes of key energy-absorbing components.To address these limitations,this study proposes a novel sandwich structure incorporating mild steel tubes as core energy absorbers to efficiently mitigate highenergy rockfall impacts.A finite element model was developed in LS-DYNA to systematically investigate the deformation and energy absorption behaviors.Comprehensive parametric analyses were conducted to quantify the effects of key design variables,including tube wall thickness,tube spacing(number of tubes),and infill materials.The results demonstrate that increasing tube wall thickness significantly enhances ultimate energy absorption,with 12-mm-thick tubes absorbing 2.2 times more energy than 6-mm-thick tubes.Lateral constraints induced by adjacent tubes improve specific energy absorption per unit displacement by approximately 30%-45%.Furthermore,incorporating infill materials considerably enhances energy absorption,with aluminum foam infills achieving an 81%increase compared to empty tubes.Nevertheless,higher energy absorption capacity typically leads to greater peak impact forces,increasing the number of tubes offers a better balance between energy absorption and impact force,optimizing the structural performance.These findings provide valuable theoretical insights and practical guidelines for designing sandwich structures in civil and infrastructure engineering applications for effective rockfall protection.
基金supported by the Khalifa University of Science and Technology internal grants(Nos.2021-CIRA-109,2020-CIRA-007,and 2020-CIRA-024).
文摘Low-velocity impact tests are carried out to explore the energy absorption characteristics of bio-inspired lattices,mimicking the architecture of the marine sponge organism Euplectella aspergillum.These sea sponge-inspired lattice structures feature a square-grid 2D lattice with double diagonal bracings and are additively manufactured via digital light processing(DLP).The collapse strength and energy absorption capacity of sea sponge lattice structures are evaluated under various impact conditions and are compared to those of their constituent square-grid and double diagonal lattices.This study demonstrates that sea sponge lattices can achieve an 11-fold increase in energy absorption compared to the square-grid lattice,due to the stabilizing effect of the double diagonal bracings prompting the structure to collapse layer-bylayer under impact.By adjusting the thickness ratio in the sea sponge lattice,up to 76.7%increment in energy absorption is attained.It is also shown that sea-sponge lattices outperform well-established energy-absorbing materials of equal weight,such as hexagonal honeycombs,confirming their significant potential for impact mitigation.Additionally,this research highlights the enhancements in energy absorption achieved by adding a small amount(0.015 phr)of Multi-Walled Carbon Nanotubes(MWCNTs)to the photocurable resin,thus unlocking new possibilities for the design of innovative lightweight structures with multifunctional attributes.
基金Supported by the Science and Technology Cooperation and Exchange special project of Cooperation of Shanxi Province(202404041101014)the Fundamental Research Program of Shanxi Province(202403021212333)+3 种基金the Joint Funds of the National Natural Science Foundation of China(U24A20555)the Lvliang Key R&D of University-Local Cooperation(2023XDHZ10)the Initiation Fund for Doctoral Research of Taiyuan University of Science and Technology(20242026)the Outstanding Doctor Funding Award of Shanxi Province(20242080).
文摘To elucidate the effect of calcite-regulated activated carbon(AC)structure on low-temperature denitrification performance of SCR catalysts,this work prepared a series of Mn-Ce/De-AC-xCaCO_(3)(x is the calcite content in coal)catalysts were prepared by the incipient wetness impregnation method,followed by acid washing to remove calcium-containing minerals.Comprehensive characterization and low-temperature denitrification tests revealed that calcite-induced structural modulation of coal-derived AC significantly enhances catalytic activity.Specifically,NO conversion increased from 88.3%of Mn-Ce/De-AC to 91.7%of Mn-Ce/De-AC-1CaCO_(3)(210℃).The improved SCR denitrification activity results from the enhancement of physicochemical properties including higher Mn^(4+)content and Ce^(4+)/Ce^(3+)ratio,an abundance of chemisorbed oxygen and acidic sites,which could strengthen the SCR reaction pathways(richer NH_(3)activated species and bidentate nitrate active species).Therefore,NO removal is enhanced.
文摘Anchovies are key forage species in coastal and pelagic food webs,playing crucial ecological and commercial roles in marine ecosystems.Encrasicholina punctifer is a commercially and ecologically important species,yet little is known about its osteological development characteristics.Understanding these ontogenetic patterns is essential for explaining phylogenetic relationships within Clupeiformes,informing larval identification in ichthyoplankton surveys,and enhancing aquaculture practices.This study describes the ontogenetic characteristics of the appendicular and median skeletons and fin supports in E.punctifer larvae and juveniles,providing quantitative ontogenetic timelines to address gaps in engraulid developmental biology and contribute to teleost ontogeny research.Larval and juvenile specimens of E.punctifer;size range:3.00-34.56 mm standard length(SL)and notochord length(NL)collected from the Philippine Sea were processed using the standard Alizarin red and Alcian blue clearing-and-staining technique to differentiate ossified and cartilaginous elements.Specimens were examined under a stereo microscope and imaged with an HTC1600ISP digital camera for detailed morphological analysis of skeletal structures.Caudal complex development was evident by 5.55 mm NL,with the initial appearance of cartilaginous hypurals 1–2 and parhypural,followed by Hy3–5 at 6.08 mm NL.Cartilaginous Hy6 was visible by 9.58 mm SL in postflexion larvae.Six hypural bones were present from the postflexion to juvenile stage.Principal fin rays formed via intramembranous ossification at 6.32 mm NL,and segmentation was evident by 10.24 mm SL.Neural arch 1 appeared at 7.38 mm NL,preceding full haemal arch development.Uroneurals 1–2 and ural centra ossified by 9.58 mm SL,with Hy5 detached from U1 at 10.24 mm SL.Preural centra ossified before the arches.Epurals 1 and 2 were evident by 10.24 mm SL.Dorsal fin proximal radials developed anteriorly and distal radials posteriorly.Pectoral fin development initiated with an ossified cleithrum and the coracoscapular cartilage at 5.25 mm NL.By 10.24 mm SL,cartilaginous neural and haemal arches and spines were distinct.Uroneural 1 initially develops as cartilage.The formation of a pleurostyle aligns with clupeoid fish skeletal ontogeny.Dorsal and anal fin development follows a distinctive pattern,with variability in fin support development.Our results reveal accelerated caudal complex formation in E.punctifer and contribute new knowledge on the osteological characteristics of the genus Encrasicholina,and aid in understanding larval and juvenile ontogeny of marine teleosts.
基金supported by the National Nature Science Foundation of China(82174531)the Medicine and Health Science Technology Development Project of Shandong Province,China(202212060626).
文摘Abuse of chloramphenicol(CAP)could cause serious side effects to human health.Therefore,it is necessary to detect CAP residues in animal sourced food effectively.Here,the superiority(better stability,higher Apt-CAP loading efficiency,and higher CAP binding associated conformational change,etc.)of tetrahedral structure to double-chained structure for developing aptasensor was evaluated.Then,a self-assembled DNA tetrahedral structure-based electrochemical aptasensor targeting CAP was developed.Under the optimized conditions,the aptasensor exhibited high sensitivity toward CAP with a limit of detection(LOD)of 0.0676 ng/m L(linear range 0.19-387.76 ng/m L),and high selectivity against the structural analogs of CAP.Moreover,the recovery rate of CAP from spiked milk samples ranged from 100.57%to 101.69%,and only USD 1.34 is needed for detecting CAP in 1 sample.These results suggested the application potential of this aptasesor for detecting CAP in animal sourced foods.
文摘Background:Chronic inflammation is closely associated with the most common and socially significant prostate conditions,including benign prostatic hyperplasia(BPH),prostate cancer(PCa),and prostatitis syndromes.NIHcategory IV prostatitis(histologic prostatitis,HP)is defined as asymptomatic chronic inflammation of the prostate.The presence of lymphoid follicles,referred to as tertiary lymphoid structures(TLSs),along with benign lympho-epithelial lesions(BLELs),is among the key histological indicators of immune inflammation and can be assessed relatively easily.This study aimed to quantitatively assess TLSs and BLELs,as well as their relationship with the severity of HP.Methods:We investigated TLSs and BLELs in 110 prostatic specimens,including inflammatory and normal tissues,within the context of common prostate pathologies such as BPH and PCa.HP was graded as low-grade(LG)or high-grade(HG)based on the severity of inflammation.Results:TLSs were observed in 51 out of 110 cases(46.4%),while BLELs were identified in 78 cases(70.44%).Both TLSs and BLELs co-occurred in 45 cases(40.9%).Statistical analysis revealed a significant correlation between the presence of TLSs,BLELs(individually or combined),and HG-HP(p<0.001).Conclusions:This study is the first to quantitatively evaluate the immunopathologic patterns in the inflamed human prostate by analyzing the presence and cooccurrence of TLSs and BLELs.Their formation,likely triggered by antigenic stimuli and external factors,indicates a chronic inflammatory microenvironment.The strong association between TLSs,BLELs,and HG-HP underscores their potential role in HP aggressiveness.These findings suggest that TLSs and BLELs may be crucial contributors to the pathophysiology and morphogenesis of NIH-category IV prostatitis.Furthermore,TLS/BLEL formation may represent a hallmark of tissue autoimmunity,reflecting the immune or autoimmune phase of this prostatitis subtype.
基金Project supported by the National Natural Science Foundation of China(Nos.52405095,12272089,and 92360305)the Guangdong Basic and Applied Basic Research Foundation of China(No.2023A1515110557)+4 种基金the Natural Science Foundation of Liaoning Province of China(No.2023-BSBA-102)the Open Fund of National Key Laboratory of Particle Transport and Separation Technology of China(No.WZKF-2024-6)the Open Project of Guangxi Key Laboratory of Automobile Components and Vehicle Technology of China(Nos.2024GKLACVTKF07 and 2024GKLACVTKF06)the Basic Research Projects of Liaoning Provincial Department of Education of China(No.JYTQN2023162)the Fundamental Research Funds for the Central Universities of China(No.N2403022)。
文摘The testing of large structures is limited by high costs and long cycles, making scaling methods an attractive solution. However, the scaling process of elastic rings introduces complexities in multi-parameter geometric distortions, leading to a diminution in the predictive accuracy of the distorted similitude. To address this challenge, this study formulates a novel set of scaling laws, tailored to account for the intricate geometric distortions associated with elastic rings. The proposed scaling laws are formulated based on the intrinsic deformation characteristics of elastic rings, rather than the traditional systemic governing equations. Numerical and experimental cases are conducted to assess the efficacy and precision of the proposed scaling laws, and the obtained results are compared with those achieved by traditional methods. The outcomes demonstrate that the scaling laws put forth by this study significantly enhance the predictive capabilities for deformations of elastic rings.
基金supported by the National Key Research and Development Program of China(2024YFA1612900)the National Natural Science Foundation of China(Grant No.52103365 and No.12375270)the Guangdong Innovative and Entrepreneurial Research Team Program,China(Grant No.2021ZT09L227).
文摘Fine-grained nuclear graphite is a key material in high-temperature gas-cooled reactors(HTGRs).During air ingress accidents,core graphite components undergo severe oxidation,threatening structural integrity.Therefore,understanding the oxidation behavior of nuclear graphite is essential for reactor safety.The influence of oxidation involves multiple factors,including temperature,sample size,oxidant,impurities,filler type and size,etc.The size of the filler particles plays a crucial role in this study.Five ultrafine-and superfine-grained nuclear graphite samples(5.9-34.4μm)are manufactured using identical raw materials and manufacturing processes.Isothermal oxidation tests conducted at 650℃-750℃ are used to study the oxidation behavior.Additionally,comprehensive characterization is performed to analyze the crystal structure,surface morphology,and nanoscale to microscale pore structure of the samples.Results indicate that oxidation behavior cannot be predicted solely based on filler grain size.Reactive site concentration,characterized by active surface area,dominates the chemical reaction kinetics,whereas pore tortuosity,quantified by the structural parameterΨ,plays a key role in regulating oxidant diffusion.These findings clarify the dual role of microstructure in oxidation mechanisms and establish a theoretical and experimental basis for the design of high-performance nuclear graphite capable of long-term service in high-temperature gas-cooled reactors.
基金supported by the National Natural Science Foundation of China(Grant Nos.62575099,62075059,61405058)Guangdong Basic and Applied Basic Research Foundation(Grant No.2024A1515011353)+2 种基金Open Project of the State Key Laboratory of Advanced Optical Communication Systems and Networks of China(Grant No.2024GZKF20)the Natural Science Foundation of Hunan Province(Grant Nos.2020JJ4161 and 2017JJ2048)Scientific Research Foundation of Hunan Provincial Education Department(Grant No.21A0013)。
文摘The strong connection between braids and knots provides valuable insights into studying the topological state and phase classification of various physical systems.The phenomenon of non-Hermitian(NH)two-and three-band braiding has received widespread attention.However,a systematic exploration and visualization of non-Abelian braiding and the associated knot transformations in four-band systems remains unexplored.Here,we propose a theoretical model of NH four-band braiding,provide its phase diagram,and establish its trivial,Abelian,and non-Abelian braiding rules.Additionally,we report on special knots,such as the Hopf and Solomon links in braided knots,and reveal that their transformations are accompanied by and mediated through exceptional points.Our work provides a detailed case for studying NH multiband braiding and knot structures in four-band systems,which could offer insights for topological photonics and analog information processing applications.
基金Supported by Key Technologies Research and Development Program of China(Grant No.2022YFC2406004).
文摘In this study,the shell structure of olives in nature was modeled,and a high-porosity bionic olive body-centered cubic structure(BCCO)with reinforcement structures of circular support(BCCR)and triangular support(BCCT)with excellent mechanical properties was designed and prepared using selective laser melting technology.The surface morphology,deformation behavior,and energy absorption of BCCO were compared with those of the equivalent uniform body-centered cubic structure(BCC)and analyzed through quasi-static compression experiments and finite element analysis.The olive-shaped structure showed optimal load resistance when the radius of curvature was equal to the edge length of the lattice structure,and outperformed with a larger curvature than with a smaller curvature.With the added support structure,the energy absorption of the BCCR increased by 144.44%compared with that of the conventional BCC structure.The newly designed olive bionic structure has considerable potential for applications in various fields,such as aerospace and medical devices.
基金supported by the Korea Institute for Advancement of Technology (KIAT)the Ministry of Trade,Industry&Energy (MOTIE) of the Republic of Korea (No. P0022130)by the Institute of Information&Communications Technology Planning&Evaluation(IITP)-Innovative Human Resource Development for Local Intellectualization program grant funded by the Korea government (MSIT)(IITP-2025-RS-2023-00259678)
文摘To realize the practical application of anion exchange membrane water electrolysis(AEMWE),it is essential to develop highly active,durable,and cost-effective electrocatalyst for oxygen evolution reaction(OER).Herein,we report a hollow-structured Ni_(x)Co_(1−x)O/Ni_(3)S_(2)/Co_(9)S_(8)heterostructure synthesized via sequential template-assisted growth,thermal oxidation,and controlled sulfidation process.The abundant bimetallic heterointerfaces not only provide additional active sites but also promote electronic modulation via charge redistribution.Additionally,the porous and hollow architecture enhances active surface area and mass transfer ability,thereby increasing the number of accessible active sites for alkaline OER.As a result,the prepared electrocatalyst achieves low overpotential of 310 mV at 10 mA cm^(−2)and small Tafel slope of 55.94 mV dec^(−1),demonstrating the exceptional electrocatalytic performance for alkaline OER.When integrated as the anode in an AEMWE cell,it delivers outstanding performance with only 1.657 V at 1.0 A cm^(−2)and reaches high current density of 5.0 A cm^(−2)at 1.989 V,surpassing those of commercial RuO_(2).The cell also shows excellent long-term durability over 100 h with minimal degradation.This study highlights the strong potential of rationally engineered oxide/sulfide heterostructures for next-generation alkaline water electrolysis.