The disaccommodation of magnetic per- meability,specific magnetization and linear magnetostriction of amorphous(Fe_xNi_(1-x))_(76)- Si_8B_(16)alloys were measured.It was found that the disaccommodation obtained at low...The disaccommodation of magnetic per- meability,specific magnetization and linear magnetostriction of amorphous(Fe_xNi_(1-x))_(76)- Si_8B_(16)alloys were measured.It was found that the disaccommodation obtained at lower temperature is a monotonically decreasing function of Fe content, however,a peak is observed at higher temperature. The experimental results are discussed on the basis of magnetostrictive interaction and atomic directional ordering.展开更多
The disaccommodation(DA)measurements of initial susceptibility were performed in amorphous Fe_(90-x)Ni_xZr_(10)(x=10,20,30)alloys.The DA was measured for two different amorphous states:as-quenched and pretreated at 53...The disaccommodation(DA)measurements of initial susceptibility were performed in amorphous Fe_(90-x)Ni_xZr_(10)(x=10,20,30)alloys.The DA was measured for two different amorphous states:as-quenched and pretreated at 537 K for 45 min.For all the as- quenched samples,in the isochronal spectra of DA a well defined relaxation peak around 350 K is accompanied by a samll but distinct peak near the Curie temperature of Fe_(90)Zr_(10) phase(T_c=230 K).The reversibility and annealing effect on DA are analyzed within the framework of two-level model.The fits of the theory to the experimental data of reversible relaxation processes gave a spectrum,of activation energies and pre- exponential factor.展开更多
文摘The disaccommodation of magnetic per- meability,specific magnetization and linear magnetostriction of amorphous(Fe_xNi_(1-x))_(76)- Si_8B_(16)alloys were measured.It was found that the disaccommodation obtained at lower temperature is a monotonically decreasing function of Fe content, however,a peak is observed at higher temperature. The experimental results are discussed on the basis of magnetostrictive interaction and atomic directional ordering.
文摘The disaccommodation(DA)measurements of initial susceptibility were performed in amorphous Fe_(90-x)Ni_xZr_(10)(x=10,20,30)alloys.The DA was measured for two different amorphous states:as-quenched and pretreated at 537 K for 45 min.For all the as- quenched samples,in the isochronal spectra of DA a well defined relaxation peak around 350 K is accompanied by a samll but distinct peak near the Curie temperature of Fe_(90)Zr_(10) phase(T_c=230 K).The reversibility and annealing effect on DA are analyzed within the framework of two-level model.The fits of the theory to the experimental data of reversible relaxation processes gave a spectrum,of activation energies and pre- exponential factor.