AA 2219-0 Al-Cu alloy single bead welds were obtained by hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process with pulse frequency varying from 25 kHz to 70 kHz. Weld hardn...AA 2219-0 Al-Cu alloy single bead welds were obtained by hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process with pulse frequency varying from 25 kHz to 70 kHz. Weld hardness characteristics which mainly depicted by microhardness and its gradient were investigated systematically. The results show that pulse frequency has a great effect on the hardness characteristics. The weld zone microhardness and its gradient with different pulse frequency present an evident fluctuant trend. The fluctuation of gradient is slight, illustrating that the mierostructure is uniform with pulse frequcncy varied from 35 kHz to 60 kHz. The fusion zone microhardness and its gradient foUow the similar trends but fluetuate greatly. Maximum value of gradient appears around the fusion boundary due to the coarse and non- uniform microstrueture. The maximum gradient at 60 kHz is only 25.5 % of that at 45 kHz. According to the study, the best hardness characteristics are achieved at 60 kHz frequency.展开更多
Optimization of hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process was carried out to obtain the optimum weld characteristics of 5AO6-HX4 aluminum-magnesium alloy sheets ...Optimization of hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process was carried out to obtain the optimum weld characteristics of 5AO6-HX4 aluminum-magnesium alloy sheets of 3 mm thickness. The square butt joints were produced by HPVP-GTA W process, the microstructure and mechanical properties were systematically investigated. It is observed that the process parameters influence the weld microstructure and mechanical properties significantly. Weld microstructure is mainly composed of grid a （A1） solid solution, with a large number of intermetallic （ Mg2Al3 ） precipitates distributed in the matrix. The amount of ~ （ Mg2Al3 ） precipitates has an obvious difference with different parameters. Compared with that of the base material, tensile strength of 5AO6-HX4 alloy welded joints has a certain reduction, as well as the elongation and reduction of area. The optimized welding process parameters for 5A06-HX4 alloy sheets are presented.展开更多
基金The research is supported by the National Natural Science Foundation of China （No. 51005011 ） the Fundamental Research Funds for the Central Universities.
文摘AA 2219-0 Al-Cu alloy single bead welds were obtained by hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process with pulse frequency varying from 25 kHz to 70 kHz. Weld hardness characteristics which mainly depicted by microhardness and its gradient were investigated systematically. The results show that pulse frequency has a great effect on the hardness characteristics. The weld zone microhardness and its gradient with different pulse frequency present an evident fluctuant trend. The fluctuation of gradient is slight, illustrating that the mierostructure is uniform with pulse frequcncy varied from 35 kHz to 60 kHz. The fusion zone microhardness and its gradient foUow the similar trends but fluetuate greatly. Maximum value of gradient appears around the fusion boundary due to the coarse and non- uniform microstrueture. The maximum gradient at 60 kHz is only 25.5 % of that at 45 kHz. According to the study, the best hardness characteristics are achieved at 60 kHz frequency.
基金This work was supported by the National Natural Science Foundation of China under grant No. 51005011 and the Fundamental Research Funds for the Central Universities.
文摘Optimization of hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process was carried out to obtain the optimum weld characteristics of 5AO6-HX4 aluminum-magnesium alloy sheets of 3 mm thickness. The square butt joints were produced by HPVP-GTA W process, the microstructure and mechanical properties were systematically investigated. It is observed that the process parameters influence the weld microstructure and mechanical properties significantly. Weld microstructure is mainly composed of grid a （A1） solid solution, with a large number of intermetallic （ Mg2Al3 ） precipitates distributed in the matrix. The amount of ~ （ Mg2Al3 ） precipitates has an obvious difference with different parameters. Compared with that of the base material, tensile strength of 5AO6-HX4 alloy welded joints has a certain reduction, as well as the elongation and reduction of area. The optimized welding process parameters for 5A06-HX4 alloy sheets are presented.