We investigated the effect of aligning crystal orientation in the microstructures containing sub micro-sized grains on the thermoelectric properties for polycrystalline Bi-Te materials.Bi-Te powder,prepared through th...We investigated the effect of aligning crystal orientation in the microstructures containing sub micro-sized grains on the thermoelectric properties for polycrystalline Bi-Te materials.Bi-Te powder,prepared through the conventional pulverization process,was sufficiently dispersed in an appropriate solvent,and then was formed into c-axis aligned green bodies under a designated high magnetic field.The green bodies were sintered with spark-plasma-sintering machine.The degree of crystal alignment of sintered bodies was examined with the electron-back-scatter-diffraction SEM and the X-ray diffraction patterns.It was observed that for both p and n type thermoelectric Bi-Te materials,aligning crystal orientation properly made electrical resistivity decreased with keeping Seebeck coefficient and thermal conductivity remained unchanged.As a typical result,the aligned Bi-Te material with the magnetic field of 10 tesla showed 30%enhancement of the thermoelectric performance.展开更多
基金Item Sponsored by Energy Efficiency&Resources of the Korea Institute of Energy Technology Evaluation and Planning (KETEP) grant funded by the Ministry of Knowledge Economy,Republic of Korea(2007EID11P050000)the DGIST Basic Research Program of the Ministry of Education,Science and Technology(MoEST),Republic of Korea(12-EN-01)
文摘We investigated the effect of aligning crystal orientation in the microstructures containing sub micro-sized grains on the thermoelectric properties for polycrystalline Bi-Te materials.Bi-Te powder,prepared through the conventional pulverization process,was sufficiently dispersed in an appropriate solvent,and then was formed into c-axis aligned green bodies under a designated high magnetic field.The green bodies were sintered with spark-plasma-sintering machine.The degree of crystal alignment of sintered bodies was examined with the electron-back-scatter-diffraction SEM and the X-ray diffraction patterns.It was observed that for both p and n type thermoelectric Bi-Te materials,aligning crystal orientation properly made electrical resistivity decreased with keeping Seebeck coefficient and thermal conductivity remained unchanged.As a typical result,the aligned Bi-Te material with the magnetic field of 10 tesla showed 30%enhancement of the thermoelectric performance.