Polystyrene （PS） @SiO2 core-shell microbeads with large pore and large particle size were prepared via layer-by-layer（LBL）assembly technique for potential applications in nano-micro composites. Negative silica nan...Polystyrene （PS） @SiO2 core-shell microbeads with large pore and large particle size were prepared via layer-by-layer（LBL）assembly technique for potential applications in nano-micro composites. Negative silica nanoparticles synthesized via modified St6ber method and cationic poly （diallyldimethylammonium chloride） were alternately adsorbed on the surface of microbeads. Zeta potential, size, and morphology of the microbeads were monitored during LBL assembly process to ensure the successful deposition of silica nanoparticles. The porous shell was characterized using nitrogen adsorption and desorption analyses, and the surface area, volume and diame- ter of the pores were derived. It is found that the porous shell thickness and the pore size can be tuned by changing the coating times of silica nanoparticles. Finally, PS@SiO2 core-shell microbeads with 5 grn PS solid core and 350 nm mesoporous shell （mean BJH pore diameter is ~27 nm） were used to load CdSe/ZnS quantum dots （QDs）. The fluorescence microscopic image and the optical amplification of the QDs-embedded microbeads （QDBs） indicate that the as-prepared core-shell microbeads can provide adequate space for QDs and may be useful for further application of nano-micro composites.展开更多
基金Supported by the National Natural Science Foundation of China(No.51202160)
文摘Polystyrene （PS） @SiO2 core-shell microbeads with large pore and large particle size were prepared via layer-by-layer（LBL）assembly technique for potential applications in nano-micro composites. Negative silica nanoparticles synthesized via modified St6ber method and cationic poly （diallyldimethylammonium chloride） were alternately adsorbed on the surface of microbeads. Zeta potential, size, and morphology of the microbeads were monitored during LBL assembly process to ensure the successful deposition of silica nanoparticles. The porous shell was characterized using nitrogen adsorption and desorption analyses, and the surface area, volume and diame- ter of the pores were derived. It is found that the porous shell thickness and the pore size can be tuned by changing the coating times of silica nanoparticles. Finally, PS@SiO2 core-shell microbeads with 5 grn PS solid core and 350 nm mesoporous shell （mean BJH pore diameter is ~27 nm） were used to load CdSe/ZnS quantum dots （QDs）. The fluorescence microscopic image and the optical amplification of the QDs-embedded microbeads （QDBs） indicate that the as-prepared core-shell microbeads can provide adequate space for QDs and may be useful for further application of nano-micro composites.