The corrosion resistance of aluminum(Al)cable-copper(Cu)terminal joints fabricated by magnetic pulse crimping(MPC)and hydraulic clamp crimping(HCC)was compared.Performance degradation was evaluated by mechanical and e...The corrosion resistance of aluminum(Al)cable-copper(Cu)terminal joints fabricated by magnetic pulse crimping(MPC)and hydraulic clamp crimping(HCC)was compared.Performance degradation was evaluated by mechanical and electrical properties.Additionally,corrosion behavior was analyzed by electrochemical testing.Microscopic characterization was performed by scanning electron microscopy(SEM)and energy dispersive spectroscopy(EDS).Results show that the tensile strength of the corroded joints is reduced.However,due to the advantages of high-speed forming and contact tightness unique to MPC,the contact resistance of the corroded joints still maintains excellent.Electrochemical tests demonstrate that the MPC joints have higher corrosion potentials and smaller corrosion currents,providing better corrosion resistance.The formation of a primary battery between Al and Cu at the lap joint leads to the formation of severer corrosion pits.展开更多
The paper studies the twin wire butt welding of 6mm-thick T2 copper and Q235 steel plate by using the twin wire consisting of one copper-plated welding wire and one steel welding wire.According to the appearance detec...The paper studies the twin wire butt welding of 6mm-thick T2 copper and Q235 steel plate by using the twin wire consisting of one copper-plated welding wire and one steel welding wire.According to the appearance detection,the weld joint gained is sound in shape without crackles,pores,incomplete fusion and other defects.As shown by the mechanical property,SEM and EDAX and in the metallographic analysis and test,the rupture position of copper-steel welded joint is located in the copper-part HAZ when the tensile strength reaches above 210MPa and Fe content of the welded joint involved in 1# test specimen reaches around 22.78%-26.75%,with the hardness achieving between 102～107HB and the weld structure being (α+ε) duplex solid solution.展开更多
基金supported by the National Natural Science Foundation of China (No.52175315)the Shenzhen Science and Technology Program,China (No.KQTD20200820113110016)the Hunan Provincial Postgraduate Research Innovation Program,China (No.CX20220404)。
文摘The corrosion resistance of aluminum(Al)cable-copper(Cu)terminal joints fabricated by magnetic pulse crimping(MPC)and hydraulic clamp crimping(HCC)was compared.Performance degradation was evaluated by mechanical and electrical properties.Additionally,corrosion behavior was analyzed by electrochemical testing.Microscopic characterization was performed by scanning electron microscopy(SEM)and energy dispersive spectroscopy(EDS).Results show that the tensile strength of the corroded joints is reduced.However,due to the advantages of high-speed forming and contact tightness unique to MPC,the contact resistance of the corroded joints still maintains excellent.Electrochemical tests demonstrate that the MPC joints have higher corrosion potentials and smaller corrosion currents,providing better corrosion resistance.The formation of a primary battery between Al and Cu at the lap joint leads to the formation of severer corrosion pits.
基金Foundation item:NUST Research Funding,No.2010XQTR01
文摘The paper studies the twin wire butt welding of 6mm-thick T2 copper and Q235 steel plate by using the twin wire consisting of one copper-plated welding wire and one steel welding wire.According to the appearance detection,the weld joint gained is sound in shape without crackles,pores,incomplete fusion and other defects.As shown by the mechanical property,SEM and EDAX and in the metallographic analysis and test,the rupture position of copper-steel welded joint is located in the copper-part HAZ when the tensile strength reaches above 210MPa and Fe content of the welded joint involved in 1# test specimen reaches around 22.78%-26.75%,with the hardness achieving between 102～107HB and the weld structure being (α+ε) duplex solid solution.