The structural analysis of two PP/PE copolymer samples,1 and 2,was conducted by using^(13)C-NMR,GPC and crystallization segregation DSC(CSDSC)techniques.A pure polypropylene sample was also used for comparison.It was ...The structural analysis of two PP/PE copolymer samples,1 and 2,was conducted by using^(13)C-NMR,GPC and crystallization segregation DSC(CSDSC)techniques.A pure polypropylene sample was also used for comparison.It was found that the two copolymer samples are very close in composition(the ethylene mol content is 4.3%and 4.5%,respectively),stereoregularity(96%and 97%)and molecular weight(M_(w)=7.0 x 10^(4)and 7.3 x 10^(4);M-(w)/M_(n)=5.0 and 6.1,respectively).While the CSDSC thermograms of the two samples are quite different from each other.Sample 1 shows a higher average melting temperature and a broader distribution of its thermogram These phenomena were explained as an indication of a less uniform distribution of ethylene units along the PP chains for sample 1.It was noted that CSDSC is a very sensitive and convenient technique for structural studies of copolymers.展开更多
The melting behavior of polypropylene (PP) and low ethylene content polypropylenecopolymer with and without nucleating agent samples crystallized under both isothermal and non-isothermal conditions were studied by Dif...The melting behavior of polypropylene (PP) and low ethylene content polypropylenecopolymer with and without nucleating agent samples crystallized under both isothermal and non-isothermal conditions were studied by Differential Scanning Calorimeter (DSC) and X-raydiffraction. Multiple melting behavior were observed depending on the existence of nucleatingagent and crystallization conditions. The observed phenomena have been discussed by the effect ofnucleating agent on perfection of crystal and the melting and recrystallization of imperfect crystalto a more perfect crystal during the heating process of samples.展开更多
文摘The structural analysis of two PP/PE copolymer samples,1 and 2,was conducted by using^(13)C-NMR,GPC and crystallization segregation DSC(CSDSC)techniques.A pure polypropylene sample was also used for comparison.It was found that the two copolymer samples are very close in composition(the ethylene mol content is 4.3%and 4.5%,respectively),stereoregularity(96%and 97%)and molecular weight(M_(w)=7.0 x 10^(4)and 7.3 x 10^(4);M-(w)/M_(n)=5.0 and 6.1,respectively).While the CSDSC thermograms of the two samples are quite different from each other.Sample 1 shows a higher average melting temperature and a broader distribution of its thermogram These phenomena were explained as an indication of a less uniform distribution of ethylene units along the PP chains for sample 1.It was noted that CSDSC is a very sensitive and convenient technique for structural studies of copolymers.
文摘The melting behavior of polypropylene (PP) and low ethylene content polypropylenecopolymer with and without nucleating agent samples crystallized under both isothermal and non-isothermal conditions were studied by Differential Scanning Calorimeter (DSC) and X-raydiffraction. Multiple melting behavior were observed depending on the existence of nucleatingagent and crystallization conditions. The observed phenomena have been discussed by the effect ofnucleating agent on perfection of crystal and the melting and recrystallization of imperfect crystalto a more perfect crystal during the heating process of samples.
