In-situ growing carbon nanotubes （CNTs） directly on carbon fibers （CFs） always lead to a degraded tensile strength of CFs and then a poor fiber-dominated mechanical property of carbon/carbon composites （C/ Cs）. ...In-situ growing carbon nanotubes （CNTs） directly on carbon fibers （CFs） always lead to a degraded tensile strength of CFs and then a poor fiber-dominated mechanical property of carbon/carbon composites （C/ Cs）. To solve this issue, here, a novel carbon fiber-based multiscale reinforcement is reported. To synthesize it, carbon fibers （CFs） have been first grafted by graphene oxide （GO）, and then carbon nanotubes （CNTs） have been in-situ grown on GO-grafted CFs by catalytic chemical vapor deposition. Characterizations on this novel reinforcement show that GO grafting cannot only nondestructively improve the surface chemical activity of CFs but also protect CFs against the high-temperature corrosion of metal catalyst during CNT growth, which maintains their tensile properties. Tensile property tests for unidirectional C/Cs with different preforms show that this novel reinforcement can endow C/C with improved tensile properties, 32% and 87% higher than that of pure C/C and C/C only doped with in-situ grown CNTs. This work would open up a possibility to fabricate multiscale C/Cs with excellent global performance.展开更多
The x wt%graphene-Ti composites（x = 0,0.2,0.3 and 0.4） were obtained using the powder metallurgy method.The X-ray diffraction results demonstrated that the peak intensity of graphene increased monotonically with inc...The x wt%graphene-Ti composites（x = 0,0.2,0.3 and 0.4） were obtained using the powder metallurgy method.The X-ray diffraction results demonstrated that the peak intensity of graphene increased monotonically with increasing graphene content.Furthermore,the number of grain boundary and interface between graphene and matrix increased as graphene increased,which led to a sharp rise of thermal resistances.The thermal conductivity and specific heat capacity of composites initially decreased drastically with addition of graphene,but then increased with increasing graphene content from 0.2 to 0.4 wt%.This phenomenon was connected with the graphene content and the characteristics of Ti matrix（pores,grain boundary and interface between graphene and matrix）.The variation of the compressive strength of composites was attributed to the interaction effects of the average grain size of the Ti matrix（d_m） and the volume fraction（V_f） and aspect ratio（A） of graphene.展开更多
This work studied the preparation of starting powder mixture influenced by milling time and its effect on the particle morphology （especially the shape） and, consequently, density and compression properties of in si...This work studied the preparation of starting powder mixture influenced by milling time and its effect on the particle morphology （especially the shape） and, consequently, density and compression properties of in situ Ti-TiB composite materials produced by selective laser melting （SLM） technology. Starting powder composite system was prepared by mixing 95 wt% commercially pure titanium （CP-Ti） and 5 wt% titanium diboride （TiB2） powders and subsequently milled for two different times （i.e. 2 h and 4 h）. The milled powder mixtures after 2 h and 4 h show nearly spherical and irregular shape, respectively. Subsequently, the resultant Ti-5 wt% TiB2 powder mixtures were used for SLM processing. Scanning electron microscopy image of the SLM-processed Ti-TiB composite samples show needle-shape TiB phase distributed across the Ti matrix, which is the product of an in-situ chemical reaction between Ti and TiB2 during SLM. The Ti-TiB composite samples prepared from 2 h and 4 h milled Ti-TiB2 powders show different relative densities of 99.5% and 95.1%, respectively. Also, the compression properties such as ultimate strength and compression strain for the 99.5% dense composite samples is 1421 MPa and 17.8%, respectively, which are superior to those （883 MPa and 5.5%, respectively） for the 95.1% dense sample. The results indicate that once Ti and TiB2 powders are connected firmly to each other and powder mixture of nearly spherical shape is obtained, there is no additional benefit in increasing the milling time and, instead, it has a negative effect on the density （i.e. increasing porosity level） of the Ti-TiB composite materials and their mechanical properties.展开更多
Microstructure and mechanical behavior of high volume content SiCp/7xxxAl composites have not been explored yet. Therefore, in the present work, 45 vol.% SiCp/7075Al composite has been prepared by pres- sure infiltrat...Microstructure and mechanical behavior of high volume content SiCp/7xxxAl composites have not been explored yet. Therefore, in the present work, 45 vol.% SiCp/7075Al composite has been prepared by pres- sure infiltration method. High density dislocations were found around SiC/Al interface in SiCp/7075Al composite after water-quenching and aging treatment. Fine dispersed nano-η＇ phases were observed after the aging treatment. Adverse to other SiCp/Al composites prepared by the pressure infiltration method, an interface layer was observed between SiC particles and AI matrix. Furthermore, high-resolution trans- mission electron microscopy （HRTEM） observation indicated that this interface layer was coherent/semi- coherent with that of the SiC particles. 45 vol.% SiCp/7075Al composite demonstrated high tensile strength （630 MPa） and micro-ductility. Compared to aged SiCp/2024Al composite, the aged SiCp/7075Al com- posite showed an increase of about 200% in the tensile strain and 90% in the tensile strength, respectively. It is speculated that nano-η＇ phases in the Al matrix significantly contributed to the strengthening effect while the interface layer between SiC and AI matrix might be beneficial to the strength and plasticity of SiCp/7075Al composite.展开更多
Relatively well crystallized and high aspect ratio Mg-Al layered double hydroxides（LDHs） were prepared by coprecipitation process in aqueous solution and further rehydrated to an organic modified LDH（OLDH） in the ...Relatively well crystallized and high aspect ratio Mg-Al layered double hydroxides（LDHs） were prepared by coprecipitation process in aqueous solution and further rehydrated to an organic modified LDH（OLDH） in the presence of surfactant. The intercalated structure and high aspect ratio of OLDH were verified by X-ray diffraction（XRD） and scanning electron microscopy（SEM）. A series of poly（propylene carbonate）（PPC）/OLDH composite films with different contents of OLDH were prepared via a melt-blending method. Their cross section morphologies, gas barrier properties and tensile strength were investigated as a function of OLDH contents. SEM results show that OLDH platelets are well dispersed within the composites and oriented parallel to the composite sheet plane. The gas barrier properties and tensile strength are obviously enhanced upon the incorporation of OLDH. Particularly, PPC/2%OLDH film exhibits the best barrier properties among all the composite films. Compared with pure PPC, the oxygen permeability coefficient（OP） and water vapor permeability coefficient（WVP） is reduced by 54% and 17% respectively with 2% OLDH addition. Furthermore, the tensile strength of PPC/2%OLDH is 83% higher than that of pure PPC with only small lose of elongation at break. Therefore, PPC/OLDH composite films show great potential application in packaging materials due to its biodegradable properties, superior oxygen and moisture barrier characteristics.展开更多
FeAl/TiC composites were fabricated by hot pressing blended elemental powders. The effects of Ni-doping on thedensification and mechanical properties of the composites were studied. Results show that the density of th...FeAl/TiC composites were fabricated by hot pressing blended elemental powders. The effects of Ni-doping on thedensification and mechanical properties of the composites were studied. Results show that the density of the composites decreases with the content of TiC increasing, and the addition of Ni significantly improves the densificationprocess by enhancing mass transfer in the bonding phase. The mechanical properties of the composites are closelyrelated with their porosity. Besides increasing the density of the composites, the addition of Ni improves the mechanical properties by other three effects: solution-strengthening the bonding phase, strengthening the FeAI-TiC interfaceand increasing ductile fracture in FeAl phase.展开更多
In spray atomization and codeposition, a molten stream of metal is disintegrated into a fine dispersion of droplets by high velocity gas jets. The resulting semi-solidified droplets are directed towards a substrate wh...In spray atomization and codeposition, a molten stream of metal is disintegrated into a fine dispersion of droplets by high velocity gas jets. The resulting semi-solidified droplets are directed towards a substrate where they impact and collect as rapidly solidified splats. Relatively high rates of solidification are achieved as a result of the thinness of the splats and the rapid heat extraction during flight and upon impacting with the substrate. The processing method uses codeposition of the metallic semi-solidified droplets (metallic matrix) with the injected reinforcement ceramic particles. In the present paper, the microstructures, mechanical properties, interfacial properties, thermal stability and aging behaviour of spray atomized and codeposited Al-Li-X MMC's (injected X=SiC, Al2O3) are reported and correlated to the processing conditions.展开更多
This paper proposes a new analytical solution to predict the shear modulus of a two-dimensional（2D） plain weave fabric（PWF） composite accounting for the interaction of orthogonal interlacing strands with coupled s...This paper proposes a new analytical solution to predict the shear modulus of a two-dimensional（2D） plain weave fabric（PWF） composite accounting for the interaction of orthogonal interlacing strands with coupled shear deformation modes including not only relative bending but also torsion,etc.The two orthogonal yarns in a micromechanical unit cell are idealized as curved beams with a path depicted by using sinusoidal shape functions.The internal forces and macroscopic deformations carried by the yarn families,together with macroscopic shear modulus of PWFs are derived by means of a strain energy approach founded on micromechanics.Three sets of experimental data pertinent to three kinds of 2D orthogonal PWF composites have been implemented to validate the new model.The calculations from the new model are also compared with those by using two models in the earlier literature.It is shown that the experimental results correlate well with predictions from the new model.展开更多
The phase compositions and properties of Ti3SiC2-based composites with SiC addition of 5%-30% in mass fraction fabricated by in-situ reaction and hot pressing sintering were studied. SiC addition effectively prevented...The phase compositions and properties of Ti3SiC2-based composites with SiC addition of 5%-30% in mass fraction fabricated by in-situ reaction and hot pressing sintering were studied. SiC addition effectively prevented TiC synthesis but facilitated SiC synthesis. The Ti3SiC2/Ti C-SiC composite had better oxidation resistance when SiC added quantity reached 20% but poorer oxidation resistance with SiC addition under 15% than Ti3SiC2/TiC composite at higher temperatures. There were more than half of the original SiC and a few Ti3SiC2 remaining in Ti3SiC2/Ti C-SiC with 20% SiC addition, but all constituents in Ti3Si2/TiC composite were oxidized after 12 h in air at 1500 °C. The oxidation scale thickness of TS30, 1505.78 μm, was near a half of that of T,2715 μm, at 1500 °C for 20 h. Ti3SiC2/Ti C composite had a flexural strength of 474 MPa, which was surpassed by Ti3SiC2/TiC-SiC composites when SiC added amount reached 15%. The strength reached the peak of 518 MPa at 20% SiC added amount.展开更多
Alumina-(0 similar to 20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed-alumina and iron powders at 1400 degreesC and 30 MPa for 30 min. Hot-pressed bodies with nearly theoretical density were...Alumina-(0 similar to 20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed-alumina and iron powders at 1400 degreesC and 30 MPa for 30 min. Hot-pressed bodies with nearly theoretical density were obtained for addition up to 10 vol. pct Fe, but relative density decreased gradually with further increase in Fe addition. The materials exhibit a homogeneous dispersion of Fe. Fracture strength of the composites exhibits a maximum value of 604 MPa at 15 vol. pct Fe, which is 1.5 times that of alumina alone. Fracture toughness increases with the increase in Fe content, reaching 7.5 MPa.m(1/2) at 20 vol. pct Fe. The theoretical values of fracture toughness was calculated and compared with the experimental one. Toughening mechanisms of the composites are also discussed.展开更多
The mechanical, electrical, and thermal expansion properties of carbon nanotube（CNT）-based silver and silver–palladium（10：1, w/w） alloy nanocomposites are reported. To tailor the properties of silver, CNTs were ...The mechanical, electrical, and thermal expansion properties of carbon nanotube（CNT）-based silver and silver–palladium（10：1, w/w） alloy nanocomposites are reported. To tailor the properties of silver, CNTs were incorporated into a silver matrix by a modified molecular level-mixing process. CNTs interact weakly with silver because of their non-reactive nature and lack of mutual solubility. Therefore, palladium was utilized as an alloying element to improve interfacial adhesion. Comparative microstructural characterizations and property evaluations of the nanocomposites were performed. The structural characterizations revealed that decorated type-CNTs were dispersed, embedded, and anchored into the silver matrix. The experimental results indicated that the modification of the silver and silver–palladium nanocomposite with CNT resulted in increases in the hardness and Young＇s modulus along with concomitant decreases in the electrical conductivity and the coefficient of thermal expansion（CTE）. The hardness and Young＇s modulus of the nanocomposites were increased by 30%？40% whereas the CTE was decreased to 50%-60% of the CTE of silver. The significantly improved CTE and the mechanical properties of the CNT-reinforced silver and silver–palladium nanocomposites are correlated with the intriguing properties of CNTs and with good interfacial adhesion between the CNTs and silver as a result of the fabrication process and the contact action of palladium as an alloying element.展开更多
An equivalent continuum method only considering the stretching deformation of struts was used to study the in-plane stiffness and strength of planar lattice grid com- posite materials. The initial yield equations of l...An equivalent continuum method only considering the stretching deformation of struts was used to study the in-plane stiffness and strength of planar lattice grid com- posite materials. The initial yield equations of lattices were deduced. Initial yield surfaces were depicted separately in different 3D and 2D stress spaces. The failure envelope is a polyhedron in 3D spaces and a polygon in 2D spaces. Each plane or line of the failure envelope is corresponding to the yield or buckling of a typical bar row. For lattices with more than three bar rows, subsequent yield of the other bar row after initial yield made the lattice achieve greater limit strength. The importance of the buckling strength of the grids was strengthened while the grids were relative sparse. The integration model of the method was used to study the nonlinear mechanical properties of strain hardening grids. It was shown that the integration equation could accurately model the complete stress-strain curves of the grids within small deformations.展开更多
Centrifugal casting was applied to produce cylindrical castings using SiCp/Al composite slurry,which contained 20%SiC particles.The castings comprised a particle free zone and a particle rich zone.The amount of SiC pa...Centrifugal casting was applied to produce cylindrical castings using SiCp/Al composite slurry,which contained 20%SiC particles.The castings comprised a particle free zone and a particle rich zone.The amount of SiC particles had a dramatic transformation from the particle rich zone to the particle free zone,and the maximum content of SiC particles in the particle rich zone reached up to 40 vol%.The ultimate tensile strength（UTS） of the as-cast SiCp / Al composites in the particle rich zone was 143 MPa,and the fracture was caused by the desorption of SiC particles from matrix alloy.The coefficient of thermal expansion（CTE） of the SiC_p / Al composites in the range of 20 and 100 ℃ was determined as 16.67×10^（-6） s^（-1）,and the experimental CTE was lower than the predicted data based on the Kerner＇s model.The results show that the decrease in CTE in the case of the composites at high temperature stage can be attributed to the solute concentration of Si in Al and the plastic deformation of the matrix alloy in the composites with void architecture.展开更多
Diamond particles reinforced aluminum–silicon matrix composites,abbreviated as Al（Si）/diamond composites,were fabricated by squeeze casting.The effect of Si content on the microstructure and mechanical properties o...Diamond particles reinforced aluminum–silicon matrix composites,abbreviated as Al（Si）/diamond composites,were fabricated by squeeze casting.The effect of Si content on the microstructure and mechanical properties of the composites were investigated.The mechanical properties are found to increase monotonically with Si content increasing up to 7.0 wt%.The Al-7.0 wt% Si/diamond composite exhibits tensile strength of 78 MPa,bending strength of 230 MPa,and compressive strength of426 MPa.Al–Si eutectic phases are shown to connect with Al matrix and diamond particles tightly,which is responsible for the enhancement of mechanical properties in the Al（Si）/diamond composites.展开更多
Hoppressed Si3N4/SiC platelet composites had been investigated with respect to their microstructure and mechanical properties. The results indicate that Vickers hardness, elastic modulus and fracture toughness of the ...Hoppressed Si3N4/SiC platelet composites had been investigated with respect to their microstructure and mechanical properties. The results indicate that Vickers hardness, elastic modulus and fracture toughness of the composites were increased by the addition of SiC platelet until the content up to 20 vol pct. A slight decrease in flexural Strength was measured at room temperature with increasing SiC platelet content. The high temperature flexural strength tests at 1150, 1250, and 1350℃ were conducted. It was found that the flexural strength at elevated temperature was degraded with the rising temperature, and the downward trend of flexural strength for the composite containing 10 vol. pct SiC platelet was less. The results indicate that SiC platelet had a positive influence on the high temperature strength. Effects of SiC platelet reinforcement were presented展开更多
A facile ammonium-dichromate solution immersion method was introduced to synthesize the copperwettable Cr3C2 coating on and inside the carbon-carbon （C/C） preform. The formation mechanism and the microstructures of ...A facile ammonium-dichromate solution immersion method was introduced to synthesize the copperwettable Cr3C2 coating on and inside the carbon-carbon （C/C） preform. The formation mechanism and the microstructures of the Cr3C2 coatings were studied. The contact angle between molten copper and the C/C decreased from 140°to 60°, demonstrating the significant improvement in the wettability. The Cr3C2- coated C/C-Cu composite with only 4.2% porosity and 3.69 gcm^-3 density was manufactured through copper infiltration. As a result, the thermal and electrical conductivity of the modified C/C-Cu increased significantly due to the infiltrated copper. Also the mechanical properties of the composites including both the flexural and compressive strengths were enhanced by over 100%. The modified C/C-Cu composite exhibited lower friction coefficients and wear rates for different load levels than those of the commercial C/Cu composite. These results demonstrate the potential of the modified C/C-Cu material for use in electrical contacts.展开更多
Calcium sulfate whiskers（CSWs） modified with glutaraldehyde-crosslinked poly（vinyl alcohol）（PVA） or traditional surface modifiers,including silane coupling agent,titanate coupling agent and stearic acid,were use...Calcium sulfate whiskers（CSWs） modified with glutaraldehyde-crosslinked poly（vinyl alcohol）（PVA） or traditional surface modifiers,including silane coupling agent,titanate coupling agent and stearic acid,were used to strengthen poly（vinyl chloride）（PVC）,and the morphologies,mechanical and heat resistant properties of the resulting composites were compared.The results clearly show that glutaraldehyde cross-linked PVA modified CSW/PVC composite（c PVA@CSW/PVC） has the strongest interfacial interaction,good and stable mechanical and heat resistant properties.Nielsen＇s modified Kerner＇s equation for Young＇s modulus is better than other models examined for the CSW/PVC composites.The half debonding angle θ of c PVA@CSW/PVC composite is lower than that of other composites except silane coupling agent modified CSW/PVC composites,indicating a very strong interfacial adhesion between c PVA@CSW and PVC.In general,cross-linked PVA is effective and environmentally friendly in modifying inorganic fillers.展开更多
In the present study,the chemical and mechanical properties and the thermal expansion of a carbon nanotube（CNT）-based crystalline nano-aluminum（nano Al） composite were reported.The properties of nanocomposites wer...In the present study,the chemical and mechanical properties and the thermal expansion of a carbon nanotube（CNT）-based crystalline nano-aluminum（nano Al） composite were reported.The properties of nanocomposites were tailored by incorporating CNTs into the nano Al matrix using a physical mixing method.The elastic moduli and the coefficient of thermal expansion（CTE） of the nanocomposites were also estimated to understand the effects of CNT reinforcement in the Al matrix.Microstructural characterization of the nanocomposite reveals that the CNTs are dispersed and embedded in the Al matrix.The experimental results indicate that the incorporation of CNTs into the nano Al matrix results in the increase in hardness and elastic modulus along with a concomitant decrease in the coefficient of thermal expansion The hardness and elastic modulus of the nanocomposite increase by 21%and 20%,respectively,upon CNT addition.The CTE of CNT/A1 nanocomposite decreases to 70%compared with that of nano Al.展开更多
Mg matrix composites with SiC particles ranging from 5vol%-25vol% were prepared using stirring casting method. Die casting, squeezing casting, and extrusion were applied for inhibiting or eliminating the defects such ...Mg matrix composites with SiC particles ranging from 5vol%-25vol% were prepared using stirring casting method. Die casting, squeezing casting, and extrusion were applied for inhibiting or eliminating the defects such as gas porosity and shrinkage void. Through die casting and squeezing casting, most of the defects in Mg matrix composites could be eliminated, but the mechanical properties were improved limitedly. On the other hand, after hot extrusion, not only most of the defects of as-cast composites ingots were eliminated, but also the mechanical properties were improved markedly. With the addition of SiC, the tensile strength, yield strength and elastic modulus of as extrusion SiCp/AZ61 composites increased remarkably, and the elongation decreased obviously.展开更多
Carbonaceous nanomaterials such as carbon nanotubes （CNTs）, magnetic metal nanomaterials and semicon- ductor nanomaterials are superior candidates for microwave absorbers. Taking full advantage of the features of CN...Carbonaceous nanomaterials such as carbon nanotubes （CNTs）, magnetic metal nanomaterials and semicon- ductor nanomaterials are superior candidates for microwave absorbers. Taking full advantage of the features of CNTs, nanophase cobalt and nanophase zinc oxide, whose main microwave absorption mechanisms are based on resistance loss, magnetic loss and dielectric loss, we fabricate CNT/Co and CNT/ZnO heterostructure nanocom- posites, respectively. By using the CNTs, CNT/Co nanocomposites and CNT/ZnO nanocomposites as nanofillers, composites with polyester as matrix are prepared by in situ polymerization, and their microwave absorption per- formance is studied. It is indicated that the synergetic effects of the physic properties of different components in nano-heterostructures result in greatly enhanced microwave absorption performance in a wide frequency range. The absorption peak is increased, the absorption bandwidth is broadened, and the maximum peak shifts to a lower frequency.展开更多
基金supported by the National Natural Science Foundation of China (Nos.51432008,51502242,U1435202,and 51202194)the Research Fund for the Doctoral Program of Higher Education of China (No.20126102110013)the Key Grant Project of Chinese Ministry of Education (No.313047)
文摘In-situ growing carbon nanotubes （CNTs） directly on carbon fibers （CFs） always lead to a degraded tensile strength of CFs and then a poor fiber-dominated mechanical property of carbon/carbon composites （C/ Cs）. To solve this issue, here, a novel carbon fiber-based multiscale reinforcement is reported. To synthesize it, carbon fibers （CFs） have been first grafted by graphene oxide （GO）, and then carbon nanotubes （CNTs） have been in-situ grown on GO-grafted CFs by catalytic chemical vapor deposition. Characterizations on this novel reinforcement show that GO grafting cannot only nondestructively improve the surface chemical activity of CFs but also protect CFs against the high-temperature corrosion of metal catalyst during CNT growth, which maintains their tensile properties. Tensile property tests for unidirectional C/Cs with different preforms show that this novel reinforcement can endow C/C with improved tensile properties, 32% and 87% higher than that of pure C/C and C/C only doped with in-situ grown CNTs. This work would open up a possibility to fabricate multiscale C/Cs with excellent global performance.
基金supported by the Chinese Postdoctoral Science Foundation(No.2014M561795)the Postdoctoral Scientific Research Project of Zhejiang Province,China(No.BSH1401037)
文摘The x wt%graphene-Ti composites（x = 0,0.2,0.3 and 0.4） were obtained using the powder metallurgy method.The X-ray diffraction results demonstrated that the peak intensity of graphene increased monotonically with increasing graphene content.Furthermore,the number of grain boundary and interface between graphene and matrix increased as graphene increased,which led to a sharp rise of thermal resistances.The thermal conductivity and specific heat capacity of composites initially decreased drastically with addition of graphene,but then increased with increasing graphene content from 0.2 to 0.4 wt%.This phenomenon was connected with the graphene content and the characteristics of Ti matrix（pores,grain boundary and interface between graphene and matrix）.The variation of the compressive strength of composites was attributed to the interaction effects of the average grain size of the Ti matrix（d_m） and the volume fraction（V_f） and aspect ratio（A） of graphene.
基金supported by the Australian Research Council’s Projects Funding Scheme (No. DP110101653)the European Commission (BioTiNet-ITN G.A. No.264635)the Deutsche Forschungsgemeinschaft (SFB/Transregio 79, Project M1)
文摘This work studied the preparation of starting powder mixture influenced by milling time and its effect on the particle morphology （especially the shape） and, consequently, density and compression properties of in situ Ti-TiB composite materials produced by selective laser melting （SLM） technology. Starting powder composite system was prepared by mixing 95 wt% commercially pure titanium （CP-Ti） and 5 wt% titanium diboride （TiB2） powders and subsequently milled for two different times （i.e. 2 h and 4 h）. The milled powder mixtures after 2 h and 4 h show nearly spherical and irregular shape, respectively. Subsequently, the resultant Ti-5 wt% TiB2 powder mixtures were used for SLM processing. Scanning electron microscopy image of the SLM-processed Ti-TiB composite samples show needle-shape TiB phase distributed across the Ti matrix, which is the product of an in-situ chemical reaction between Ti and TiB2 during SLM. The Ti-TiB composite samples prepared from 2 h and 4 h milled Ti-TiB2 powders show different relative densities of 99.5% and 95.1%, respectively. Also, the compression properties such as ultimate strength and compression strain for the 99.5% dense composite samples is 1421 MPa and 17.8%, respectively, which are superior to those （883 MPa and 5.5%, respectively） for the 95.1% dense sample. The results indicate that once Ti and TiB2 powders are connected firmly to each other and powder mixture of nearly spherical shape is obtained, there is no additional benefit in increasing the milling time and, instead, it has a negative effect on the density （i.e. increasing porosity level） of the Ti-TiB composite materials and their mechanical properties.
基金the financial support of the project from "Key Laboratory Fund (5780011513) of Harbin Institute of Technology""University Basic Fund (5710011113) of Harbin Institute of Technology""the Fundamental Research Funds for the Central Universities" (Grant No. HIT. NSRIF. 20161)
文摘Microstructure and mechanical behavior of high volume content SiCp/7xxxAl composites have not been explored yet. Therefore, in the present work, 45 vol.% SiCp/7075Al composite has been prepared by pres- sure infiltration method. High density dislocations were found around SiC/Al interface in SiCp/7075Al composite after water-quenching and aging treatment. Fine dispersed nano-η＇ phases were observed after the aging treatment. Adverse to other SiCp/Al composites prepared by the pressure infiltration method, an interface layer was observed between SiC particles and AI matrix. Furthermore, high-resolution trans- mission electron microscopy （HRTEM） observation indicated that this interface layer was coherent/semi- coherent with that of the SiC particles. 45 vol.% SiCp/7075Al composite demonstrated high tensile strength （630 MPa） and micro-ductility. Compared to aged SiCp/2024Al composite, the aged SiCp/7075Al com- posite showed an increase of about 200% in the tensile strain and 90% in the tensile strength, respectively. It is speculated that nano-η＇ phases in the Al matrix significantly contributed to the strengthening effect while the interface layer between SiC and AI matrix might be beneficial to the strength and plasticity of SiCp/7075Al composite.
基金financially supported by the National Natural Science Foundation of China(No.21376276)the Specialfunded Program on National Key Scientific Instruments and Equipment Development of China(No.2012YQ230043)+1 种基金Guangdong Province Sci&Tech Bureau(Key Strategic Project No.2008A080800024)the Fundamental Research Funds for the Central Universities
文摘Relatively well crystallized and high aspect ratio Mg-Al layered double hydroxides（LDHs） were prepared by coprecipitation process in aqueous solution and further rehydrated to an organic modified LDH（OLDH） in the presence of surfactant. The intercalated structure and high aspect ratio of OLDH were verified by X-ray diffraction（XRD） and scanning electron microscopy（SEM）. A series of poly（propylene carbonate）（PPC）/OLDH composite films with different contents of OLDH were prepared via a melt-blending method. Their cross section morphologies, gas barrier properties and tensile strength were investigated as a function of OLDH contents. SEM results show that OLDH platelets are well dispersed within the composites and oriented parallel to the composite sheet plane. The gas barrier properties and tensile strength are obviously enhanced upon the incorporation of OLDH. Particularly, PPC/2%OLDH film exhibits the best barrier properties among all the composite films. Compared with pure PPC, the oxygen permeability coefficient（OP） and water vapor permeability coefficient（WVP） is reduced by 54% and 17% respectively with 2% OLDH addition. Furthermore, the tensile strength of PPC/2%OLDH is 83% higher than that of pure PPC with only small lose of elongation at break. Therefore, PPC/OLDH composite films show great potential application in packaging materials due to its biodegradable properties, superior oxygen and moisture barrier characteristics.
基金This work was supported by Hunan Provincial Natural Science Foundation.
文摘FeAl/TiC composites were fabricated by hot pressing blended elemental powders. The effects of Ni-doping on thedensification and mechanical properties of the composites were studied. Results show that the density of the composites decreases with the content of TiC increasing, and the addition of Ni significantly improves the densificationprocess by enhancing mass transfer in the bonding phase. The mechanical properties of the composites are closelyrelated with their porosity. Besides increasing the density of the composites, the addition of Ni improves the mechanical properties by other three effects: solution-strengthening the bonding phase, strengthening the FeAI-TiC interfaceand increasing ductile fracture in FeAl phase.
文摘In spray atomization and codeposition, a molten stream of metal is disintegrated into a fine dispersion of droplets by high velocity gas jets. The resulting semi-solidified droplets are directed towards a substrate where they impact and collect as rapidly solidified splats. Relatively high rates of solidification are achieved as a result of the thinness of the splats and the rapid heat extraction during flight and upon impacting with the substrate. The processing method uses codeposition of the metallic semi-solidified droplets (metallic matrix) with the injected reinforcement ceramic particles. In the present paper, the microstructures, mechanical properties, interfacial properties, thermal stability and aging behaviour of spray atomized and codeposited Al-Li-X MMC's (injected X=SiC, Al2O3) are reported and correlated to the processing conditions.
基金National Natural Science Foundation of China(51075019)Aeronautical Science Foundation of China (20095251024)
文摘This paper proposes a new analytical solution to predict the shear modulus of a two-dimensional（2D） plain weave fabric（PWF） composite accounting for the interaction of orthogonal interlacing strands with coupled shear deformation modes including not only relative bending but also torsion,etc.The two orthogonal yarns in a micromechanical unit cell are idealized as curved beams with a path depicted by using sinusoidal shape functions.The internal forces and macroscopic deformations carried by the yarn families,together with macroscopic shear modulus of PWFs are derived by means of a strain energy approach founded on micromechanics.Three sets of experimental data pertinent to three kinds of 2D orthogonal PWF composites have been implemented to validate the new model.The calculations from the new model are also compared with those by using two models in the earlier literature.It is shown that the experimental results correlate well with predictions from the new model.
基金Project(51302206)supported by the National Natural Science Foundation of ChinaProject(2013JK0925)supported by Shaanxi Provincial Department of Education,China+1 种基金Project(SKLSP201308)supported by the State Key Laboratory of Solidification Processing in Northwestern Polytechnical University,ChinaProject supported by the State Scholarship Fund,China
文摘The phase compositions and properties of Ti3SiC2-based composites with SiC addition of 5%-30% in mass fraction fabricated by in-situ reaction and hot pressing sintering were studied. SiC addition effectively prevented TiC synthesis but facilitated SiC synthesis. The Ti3SiC2/Ti C-SiC composite had better oxidation resistance when SiC added quantity reached 20% but poorer oxidation resistance with SiC addition under 15% than Ti3SiC2/TiC composite at higher temperatures. There were more than half of the original SiC and a few Ti3SiC2 remaining in Ti3SiC2/Ti C-SiC with 20% SiC addition, but all constituents in Ti3Si2/TiC composite were oxidized after 12 h in air at 1500 °C. The oxidation scale thickness of TS30, 1505.78 μm, was near a half of that of T,2715 μm, at 1500 °C for 20 h. Ti3SiC2/Ti C composite had a flexural strength of 474 MPa, which was surpassed by Ti3SiC2/TiC-SiC composites when SiC added amount reached 15%. The strength reached the peak of 518 MPa at 20% SiC added amount.
文摘Alumina-(0 similar to 20 vol. pct) iron composites were fabricated by hot-pressing of well-mixed-alumina and iron powders at 1400 degreesC and 30 MPa for 30 min. Hot-pressed bodies with nearly theoretical density were obtained for addition up to 10 vol. pct Fe, but relative density decreased gradually with further increase in Fe addition. The materials exhibit a homogeneous dispersion of Fe. Fracture strength of the composites exhibits a maximum value of 604 MPa at 15 vol. pct Fe, which is 1.5 times that of alumina alone. Fracture toughness increases with the increase in Fe content, reaching 7.5 MPa.m(1/2) at 20 vol. pct Fe. The theoretical values of fracture toughness was calculated and compared with the experimental one. Toughening mechanisms of the composites are also discussed.
基金the financial assistance received from the Department of Science and Technology(Government of India)for conducting this investigation(Project-SR/FTP/PS-054/2011(G))
文摘The mechanical, electrical, and thermal expansion properties of carbon nanotube（CNT）-based silver and silver–palladium（10：1, w/w） alloy nanocomposites are reported. To tailor the properties of silver, CNTs were incorporated into a silver matrix by a modified molecular level-mixing process. CNTs interact weakly with silver because of their non-reactive nature and lack of mutual solubility. Therefore, palladium was utilized as an alloying element to improve interfacial adhesion. Comparative microstructural characterizations and property evaluations of the nanocomposites were performed. The structural characterizations revealed that decorated type-CNTs were dispersed, embedded, and anchored into the silver matrix. The experimental results indicated that the modification of the silver and silver–palladium nanocomposite with CNT resulted in increases in the hardness and Young＇s modulus along with concomitant decreases in the electrical conductivity and the coefficient of thermal expansion（CTE）. The hardness and Young＇s modulus of the nanocomposites were increased by 30%？40% whereas the CTE was decreased to 50%-60% of the CTE of silver. The significantly improved CTE and the mechanical properties of the CNT-reinforced silver and silver–palladium nanocomposites are correlated with the intriguing properties of CNTs and with good interfacial adhesion between the CNTs and silver as a result of the fabrication process and the contact action of palladium as an alloying element.
基金the China Postdoctoral Science Foundation (20060400465)the National Natural Science Foundation of China (10702033)
文摘An equivalent continuum method only considering the stretching deformation of struts was used to study the in-plane stiffness and strength of planar lattice grid com- posite materials. The initial yield equations of lattices were deduced. Initial yield surfaces were depicted separately in different 3D and 2D stress spaces. The failure envelope is a polyhedron in 3D spaces and a polygon in 2D spaces. Each plane or line of the failure envelope is corresponding to the yield or buckling of a typical bar row. For lattices with more than three bar rows, subsequent yield of the other bar row after initial yield made the lattice achieve greater limit strength. The importance of the buckling strength of the grids was strengthened while the grids were relative sparse. The integration model of the method was used to study the nonlinear mechanical properties of strain hardening grids. It was shown that the integration equation could accurately model the complete stress-strain curves of the grids within small deformations.
基金Funded by the National Natural Science Foundation of China(No.51174244)the Foundational and Cutting-edge Research Plan of Chongqing,China(No.csts2013jcyj A50014)the Fundamental Research Funds for Central University,China(No.CDJZR12240056)
文摘Centrifugal casting was applied to produce cylindrical castings using SiCp/Al composite slurry,which contained 20%SiC particles.The castings comprised a particle free zone and a particle rich zone.The amount of SiC particles had a dramatic transformation from the particle rich zone to the particle free zone,and the maximum content of SiC particles in the particle rich zone reached up to 40 vol%.The ultimate tensile strength（UTS） of the as-cast SiCp / Al composites in the particle rich zone was 143 MPa,and the fracture was caused by the desorption of SiC particles from matrix alloy.The coefficient of thermal expansion（CTE） of the SiC_p / Al composites in the range of 20 and 100 ℃ was determined as 16.67×10^（-6） s^（-1）,and the experimental CTE was lower than the predicted data based on the Kerner＇s model.The results show that the decrease in CTE in the case of the composites at high temperature stage can be attributed to the solute concentration of Si in Al and the plastic deformation of the matrix alloy in the composites with void architecture.
基金financially supported by the National Natural Science Foundation of China (No.51271017)the Fundamental Research Funds for the Central Universities (No.FRFTP-13-033A)the Program for New Century Excellent Talents in University (No.NCET-10-0227)
文摘Diamond particles reinforced aluminum–silicon matrix composites,abbreviated as Al（Si）/diamond composites,were fabricated by squeeze casting.The effect of Si content on the microstructure and mechanical properties of the composites were investigated.The mechanical properties are found to increase monotonically with Si content increasing up to 7.0 wt%.The Al-7.0 wt% Si/diamond composite exhibits tensile strength of 78 MPa,bending strength of 230 MPa,and compressive strength of426 MPa.Al–Si eutectic phases are shown to connect with Al matrix and diamond particles tightly,which is responsible for the enhancement of mechanical properties in the Al（Si）/diamond composites.
文摘Hoppressed Si3N4/SiC platelet composites had been investigated with respect to their microstructure and mechanical properties. The results indicate that Vickers hardness, elastic modulus and fracture toughness of the composites were increased by the addition of SiC platelet until the content up to 20 vol pct. A slight decrease in flexural Strength was measured at room temperature with increasing SiC platelet content. The high temperature flexural strength tests at 1150, 1250, and 1350℃ were conducted. It was found that the flexural strength at elevated temperature was degraded with the rising temperature, and the downward trend of flexural strength for the composite containing 10 vol. pct SiC platelet was less. The results indicate that SiC platelet had a positive influence on the high temperature strength. Effects of SiC platelet reinforcement were presented
基金the financial support from of the National Basic Research Program of China (Nos. 2012CB619600 and 2011CB012803)
文摘A facile ammonium-dichromate solution immersion method was introduced to synthesize the copperwettable Cr3C2 coating on and inside the carbon-carbon （C/C） preform. The formation mechanism and the microstructures of the Cr3C2 coatings were studied. The contact angle between molten copper and the C/C decreased from 140°to 60°, demonstrating the significant improvement in the wettability. The Cr3C2- coated C/C-Cu composite with only 4.2% porosity and 3.69 gcm^-3 density was manufactured through copper infiltration. As a result, the thermal and electrical conductivity of the modified C/C-Cu increased significantly due to the infiltrated copper. Also the mechanical properties of the composites including both the flexural and compressive strengths were enhanced by over 100%. The modified C/C-Cu composite exhibited lower friction coefficients and wear rates for different load levels than those of the commercial C/Cu composite. These results demonstrate the potential of the modified C/C-Cu material for use in electrical contacts.
基金financially supported by the National Natural Science Foundation of China(U 1507123)the Foundation from Qinghai Science and Technology Department(2014-HZ-817)Kunlun Scholar Award Program of Qinghai Province
文摘Calcium sulfate whiskers（CSWs） modified with glutaraldehyde-crosslinked poly（vinyl alcohol）（PVA） or traditional surface modifiers,including silane coupling agent,titanate coupling agent and stearic acid,were used to strengthen poly（vinyl chloride）（PVC）,and the morphologies,mechanical and heat resistant properties of the resulting composites were compared.The results clearly show that glutaraldehyde cross-linked PVA modified CSW/PVC composite（c PVA@CSW/PVC） has the strongest interfacial interaction,good and stable mechanical and heat resistant properties.Nielsen＇s modified Kerner＇s equation for Young＇s modulus is better than other models examined for the CSW/PVC composites.The half debonding angle θ of c PVA@CSW/PVC composite is lower than that of other composites except silane coupling agent modified CSW/PVC composites,indicating a very strong interfacial adhesion between c PVA@CSW and PVC.In general,cross-linked PVA is effective and environmentally friendly in modifying inorganic fillers.
基金supported by the Defence Research and Development Organization, New Delhi (No.ARMREB/CDSW/2011/135)
文摘In the present study,the chemical and mechanical properties and the thermal expansion of a carbon nanotube（CNT）-based crystalline nano-aluminum（nano Al） composite were reported.The properties of nanocomposites were tailored by incorporating CNTs into the nano Al matrix using a physical mixing method.The elastic moduli and the coefficient of thermal expansion（CTE） of the nanocomposites were also estimated to understand the effects of CNT reinforcement in the Al matrix.Microstructural characterization of the nanocomposite reveals that the CNTs are dispersed and embedded in the Al matrix.The experimental results indicate that the incorporation of CNTs into the nano Al matrix results in the increase in hardness and elastic modulus along with a concomitant decrease in the coefficient of thermal expansion The hardness and elastic modulus of the nanocomposite increase by 21%and 20%,respectively,upon CNT addition.The CTE of CNT/A1 nanocomposite decreases to 70%compared with that of nano Al.
基金Funded by the Program for New Century Excellent Talents in University(NCET-12-1040)the National Natural Science Foundation of China(Nos.50901048 and 51174143)+2 种基金the Key Project of Chinese Ministry of Education(No.2012017)the Program Foundation of Ministry of Education of China(No.20101402110008)Natural Science Foundation of Shanxi(No.2010021022-5)
文摘Mg matrix composites with SiC particles ranging from 5vol%-25vol% were prepared using stirring casting method. Die casting, squeezing casting, and extrusion were applied for inhibiting or eliminating the defects such as gas porosity and shrinkage void. Through die casting and squeezing casting, most of the defects in Mg matrix composites could be eliminated, but the mechanical properties were improved limitedly. On the other hand, after hot extrusion, not only most of the defects of as-cast composites ingots were eliminated, but also the mechanical properties were improved markedly. With the addition of SiC, the tensile strength, yield strength and elastic modulus of as extrusion SiCp/AZ61 composites increased remarkably, and the elongation decreased obviously.
基金Supported by the National Natural Science Foundation of China under Grant No 10332020
文摘Carbonaceous nanomaterials such as carbon nanotubes （CNTs）, magnetic metal nanomaterials and semicon- ductor nanomaterials are superior candidates for microwave absorbers. Taking full advantage of the features of CNTs, nanophase cobalt and nanophase zinc oxide, whose main microwave absorption mechanisms are based on resistance loss, magnetic loss and dielectric loss, we fabricate CNT/Co and CNT/ZnO heterostructure nanocom- posites, respectively. By using the CNTs, CNT/Co nanocomposites and CNT/ZnO nanocomposites as nanofillers, composites with polyester as matrix are prepared by in situ polymerization, and their microwave absorption per- formance is studied. It is indicated that the synergetic effects of the physic properties of different components in nano-heterostructures result in greatly enhanced microwave absorption performance in a wide frequency range. The absorption peak is increased, the absorption bandwidth is broadened, and the maximum peak shifts to a lower frequency.