In this study, a NiCrAIY ＋ AINiY composite coating was prepared by arc ion plating technique and sub- sequent annealing treatment. Cyclic hot corrosion tests of the composite coating and a reference NiCrAIY coating c...In this study, a NiCrAIY ＋ AINiY composite coating was prepared by arc ion plating technique and sub- sequent annealing treatment. Cyclic hot corrosion tests of the composite coating and a reference NiCrAIY coating coated with mixed salts of Na2SO4 ＋ K2SO4 and Na2SO4 ＋ NaC1 were carried out at 700 ℃. The results indicated that the composite coating performed better against the corrosion due to the gradient element distribution in Al-enriched outer layer and Cr-enriched inner layer. The corrosion mechanisms for the two coatings were also discussed.展开更多
MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage ...MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51001106)
文摘In this study, a NiCrAIY ＋ AINiY composite coating was prepared by arc ion plating technique and sub- sequent annealing treatment. Cyclic hot corrosion tests of the composite coating and a reference NiCrAIY coating coated with mixed salts of Na2SO4 ＋ K2SO4 and Na2SO4 ＋ NaC1 were carried out at 700 ℃. The results indicated that the composite coating performed better against the corrosion due to the gradient element distribution in Al-enriched outer layer and Cr-enriched inner layer. The corrosion mechanisms for the two coatings were also discussed.
基金Funded by the National Natural Science Foundation of China (No.51075237)the National Basic Research Program of China (No.2009CB724402)+3 种基金the Taishan Scholar Program of Shandong Provincethe Outstanding Young Scholar Science Foundation of Shandong (No.JQ200917)the National Natural Science Foundation of Shandong (No.ZR2010EZ002)National High Technology Research and Development Program (No.2009AA044303)
文摘MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.