A new concept of forming solid electrolyte interphases（SEI） in situ in an ionic conducting Li（1.5）Al（0.5）Ge（1.5）（PO4）3-polypropylene（LAGP-PP） based separator during charging and discharging is proposed and...A new concept of forming solid electrolyte interphases（SEI） in situ in an ionic conducting Li（1.5）Al（0.5）Ge（1.5）（PO4）3-polypropylene（LAGP-PP） based separator during charging and discharging is proposed and demonstrated. This unique structure shows a high ionic conductivity, low interface resistance with electrode, and can suppress the growth of lithium dendrite. The features of forming the SEI in situ are investigated by scanning electron microscopy（SEM） and x-ray photoelectron spectroscopy（XPS）. The results confirm that SEI films mainly consist of lithium fluoride and carbonates with various alkyl contents. The cell assembled by using the LAGP-coated separator demonstrates a good cycling performance even at high charging rates, and the lithium dendrites were not observed on the lithium metal electrode. Therefore, the SEI-LAGP-PP separator can be used as a promising flexible solid electrolyte for solid state lithium batteries.展开更多
Zr/ZrH2 particles with irregular morphologies and broad size distribution were uniformly coated with acicular α-FeOOH crystal grains via a facile route without using polymers or surfactants. The as-synthesized materi...Zr/ZrH2 particles with irregular morphologies and broad size distribution were uniformly coated with acicular α-FeOOH crystal grains via a facile route without using polymers or surfactants. The as-synthesized material was characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive X-ray （EDX）, UV-vis diffusion reflection （UV-vis） and Raman spectrometry. Based on these characterizations, the synthesis mechanism was explained in terms of combined heterogeneous nucleation and solid state transformation reaction. The presence of α-FeOOH coating greatly changed the combustion behavior of Zr/ZrH2 particles： the combustion lasting time decreased from 32 s for un-coated Zr/ZrH2 particles to 0.2 s for coated particles while the maximum temperature in the combustion process increased from 1510 ℃ to 2036℃.展开更多
基金Project supported by the Beijing Science and Technology ProjectChina(Grant No.Z13111000340000)+1 种基金the National Basic Research Program of China(Grant No.2012CB932900)the National Natural Science Foundation of China(Grant Nos.51325206 and 51421002)
文摘A new concept of forming solid electrolyte interphases（SEI） in situ in an ionic conducting Li（1.5）Al（0.5）Ge（1.5）（PO4）3-polypropylene（LAGP-PP） based separator during charging and discharging is proposed and demonstrated. This unique structure shows a high ionic conductivity, low interface resistance with electrode, and can suppress the growth of lithium dendrite. The features of forming the SEI in situ are investigated by scanning electron microscopy（SEM） and x-ray photoelectron spectroscopy（XPS）. The results confirm that SEI films mainly consist of lithium fluoride and carbonates with various alkyl contents. The cell assembled by using the LAGP-coated separator demonstrates a good cycling performance even at high charging rates, and the lithium dendrites were not observed on the lithium metal electrode. Therefore, the SEI-LAGP-PP separator can be used as a promising flexible solid electrolyte for solid state lithium batteries.
基金support from the National Natural Science Foun-dation (No. 20573128)National Basic Research Program of China(No. 2005CB221402)Shanxi Natural Science Foundation (Nos.20051025, 2006021031 and 2007021014)
文摘Zr/ZrH2 particles with irregular morphologies and broad size distribution were uniformly coated with acicular α-FeOOH crystal grains via a facile route without using polymers or surfactants. The as-synthesized material was characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive X-ray （EDX）, UV-vis diffusion reflection （UV-vis） and Raman spectrometry. Based on these characterizations, the synthesis mechanism was explained in terms of combined heterogeneous nucleation and solid state transformation reaction. The presence of α-FeOOH coating greatly changed the combustion behavior of Zr/ZrH2 particles： the combustion lasting time decreased from 32 s for un-coated Zr/ZrH2 particles to 0.2 s for coated particles while the maximum temperature in the combustion process increased from 1510 ℃ to 2036℃.