The 93 W and Mo1 refractory metals were bonded with different Cu_(1-x)Ni_(x) coating interlayers of various Ni content using plasma-activated sintering at 700℃.The effects of the Ni content in the Cu_(1-x)Ni_(x) coat...The 93 W and Mo1 refractory metals were bonded with different Cu_(1-x)Ni_(x) coating interlayers of various Ni content using plasma-activated sintering at 700℃.The effects of the Ni content in the Cu_(1-x)Ni_(x) coating interlayer on the interfacial microstructure evolution and mechanical properties of the W/Mo joints were studied.The maximum average shear strength of the W/Mo joint was 316.5 MPa when the Ni content of the Cu_(1-x)Ni_(x) coating interlayer was 25%.When the Ni content of the Cu_(1-x)Ni_(x) coating interlayer was below 50%,the atomic diffusion at the W/Mo joint interface was adequate without the formation of intermetallic compounds,as demonstrated by the High Resolution Transmission Electron Microscope analyses of the joints.The presence of Ni in Cu_(1-x)Ni_(x) promoted diffusion bonding at the interface,which contributed to the high mechanical properties of the W/Mo joint.With an increase in the Ni content of the Cu_(1-x)Ni_(x) coating interlayer,the Mo Ni intermetallic compound(IMC)nucleated and grew at the Cu1-xNix coating/Mo1 interface.When the Ni content of the Cu_(1-x)Ni_(x) coating interlayer was above 50%,the generation of a brittle Mo Ni IMC weakened the shear strength of the W/Mo joint dramatically.展开更多
Design and preparation of frequency doubling antireflection coating with different thicknesses of interlayer were investigated for LIB3O5 （LBO） substrate. The design was based on the vector method. The thickness of ...Design and preparation of frequency doubling antireflection coating with different thicknesses of interlayer were investigated for LIB3O5 （LBO） substrate. The design was based on the vector method. The thickness of the inserted SiO2 interlayer could be changed in a wide range for the four-layer design with two zeros at 1064 and 532 nm. The coatings without any interlayer and with 0.1 quarter-wave （λ/4）, 0.3 λ/4, 0.5 λ/4 SiO2 interlayer were deposited respectively on LBO by using electron beam evaporation technique. All the prepared coatings with SiO2 interlayer indicated satisfying optical behavior. This expanded our option for the thickness of an interlayer when coating on LBO substrate. The prepared films with SiO2 interlayer showed better adhesion than that without any interlayer. The thickness of the interlayer affected the adhesion, the adhesion for the coating with 0.5 λ/4 SiO2 interlayer was not as good as the other two.展开更多
基金the National Natural Science Foundation of China(Nos.51572208 and 51521001)the 111 Project(No.B13035)the Joint Fund(No.6141A02022255)。
文摘The 93 W and Mo1 refractory metals were bonded with different Cu_(1-x)Ni_(x) coating interlayers of various Ni content using plasma-activated sintering at 700℃.The effects of the Ni content in the Cu_(1-x)Ni_(x) coating interlayer on the interfacial microstructure evolution and mechanical properties of the W/Mo joints were studied.The maximum average shear strength of the W/Mo joint was 316.5 MPa when the Ni content of the Cu_(1-x)Ni_(x) coating interlayer was 25%.When the Ni content of the Cu_(1-x)Ni_(x) coating interlayer was below 50%,the atomic diffusion at the W/Mo joint interface was adequate without the formation of intermetallic compounds,as demonstrated by the High Resolution Transmission Electron Microscope analyses of the joints.The presence of Ni in Cu_(1-x)Ni_(x) promoted diffusion bonding at the interface,which contributed to the high mechanical properties of the W/Mo joint.With an increase in the Ni content of the Cu_(1-x)Ni_(x) coating interlayer,the Mo Ni intermetallic compound(IMC)nucleated and grew at the Cu1-xNix coating/Mo1 interface.When the Ni content of the Cu_(1-x)Ni_(x) coating interlayer was above 50%,the generation of a brittle Mo Ni IMC weakened the shear strength of the W/Mo joint dramatically.
文摘Design and preparation of frequency doubling antireflection coating with different thicknesses of interlayer were investigated for LIB3O5 （LBO） substrate. The design was based on the vector method. The thickness of the inserted SiO2 interlayer could be changed in a wide range for the four-layer design with two zeros at 1064 and 532 nm. The coatings without any interlayer and with 0.1 quarter-wave （λ/4）, 0.3 λ/4, 0.5 λ/4 SiO2 interlayer were deposited respectively on LBO by using electron beam evaporation technique. All the prepared coatings with SiO2 interlayer indicated satisfying optical behavior. This expanded our option for the thickness of an interlayer when coating on LBO substrate. The prepared films with SiO2 interlayer showed better adhesion than that without any interlayer. The thickness of the interlayer affected the adhesion, the adhesion for the coating with 0.5 λ/4 SiO2 interlayer was not as good as the other two.