Chitosan （CTS） coatings contained calcium （Ca） and phosphorus （P） on titanium （Ti） surface are prepared by the cathode liquid phase plasma technology （CLPT）, in a certain concentration electrolyte solution w...Chitosan （CTS） coatings contained calcium （Ca） and phosphorus （P） on titanium （Ti） surface are prepared by the cathode liquid phase plasma technology （CLPT）, in a certain concentration electrolyte solution with selective additions of ammonium dihydrogen phosphate and calcium nitrate. It is indicated that the parameters for a stable discharge are voltage of 400 V, frequency of 100 Hz, duty cycle of 30% based on a large amount of experiment data. The morphology, structure and composition of the coated samples are studied by SEM, FTIR, XRD, XPS. The results demonstrate that the composite coatings are uniform, and some solid particles of inorganic salt containing calcium and phosphorus dispersed on the coatings. CA tests show that the samples treated by the liquid plasma became less hydrophilic. The variation of hydrophilicity on the CLPT treated titanium is attributed to the change of the function groups on the sample surface. Meanwhile, a possible formation mechanism of the composite coatings is discussed.展开更多
Hybrid organic-inorganic halide perovskite material has been considered as a potential candidate for various optoelectronic applications. However, their high sensitivity to the environment hampers the actual applicati...Hybrid organic-inorganic halide perovskite material has been considered as a potential candidate for various optoelectronic applications. However, their high sensitivity to the environment hampers the actual application.Hence the technology replacing the organic part of the hybrid solar cells needs to be developed. Herein, we fabricated fullyinorganic carbon-based perovskite CsPbBr_3 solar cells via a sequential deposition method with a power conversion efficiency of 2.53% and long-time stability over 20 d under ambient air conditions without any encapsulation. An evolution process from tetragonal CsPb_2Br_5 to CsPb_2Br_5-CsPbBr_3 composites to quasi-cubic CsPbBr_3 was found, which was investigated by scanning electron microscopy, X-ray diffraction spectra, UV-vis absorption spectra and Fourier transform infrared spectroscopy. Detailed evolution process was studied to learn more information about the formation process before10 min. Our results are helpful to the development of inorganic perovskite solar cells and the CsPb_2Br_5 based optoelectronic devices.展开更多
基金supported by National Natural Science Foundation of China (No.10675078)
文摘Chitosan （CTS） coatings contained calcium （Ca） and phosphorus （P） on titanium （Ti） surface are prepared by the cathode liquid phase plasma technology （CLPT）, in a certain concentration electrolyte solution with selective additions of ammonium dihydrogen phosphate and calcium nitrate. It is indicated that the parameters for a stable discharge are voltage of 400 V, frequency of 100 Hz, duty cycle of 30% based on a large amount of experiment data. The morphology, structure and composition of the coated samples are studied by SEM, FTIR, XRD, XPS. The results demonstrate that the composite coatings are uniform, and some solid particles of inorganic salt containing calcium and phosphorus dispersed on the coatings. CA tests show that the samples treated by the liquid plasma became less hydrophilic. The variation of hydrophilicity on the CLPT treated titanium is attributed to the change of the function groups on the sample surface. Meanwhile, a possible formation mechanism of the composite coatings is discussed.
基金supported by the National Basic Research Program of China (2016YFA0202400 and 2015CB932200)the National Natural Science Foundation of China (21403247)+2 种基金Distinguished Youth Foundation of Anhui Province (1708085J09)the Fundamental Research Funds for the Central Universities (2017XS079)the Major/Innovative Program of Development Foundation of Hefei Center for Physical Science and Technology (2016FXZY003)
文摘Hybrid organic-inorganic halide perovskite material has been considered as a potential candidate for various optoelectronic applications. However, their high sensitivity to the environment hampers the actual application.Hence the technology replacing the organic part of the hybrid solar cells needs to be developed. Herein, we fabricated fullyinorganic carbon-based perovskite CsPbBr_3 solar cells via a sequential deposition method with a power conversion efficiency of 2.53% and long-time stability over 20 d under ambient air conditions without any encapsulation. An evolution process from tetragonal CsPb_2Br_5 to CsPb_2Br_5-CsPbBr_3 composites to quasi-cubic CsPbBr_3 was found, which was investigated by scanning electron microscopy, X-ray diffraction spectra, UV-vis absorption spectra and Fourier transform infrared spectroscopy. Detailed evolution process was studied to learn more information about the formation process before10 min. Our results are helpful to the development of inorganic perovskite solar cells and the CsPb_2Br_5 based optoelectronic devices.