Aiming at the problems of insufficient activity and selectivity of Cu-based catalysts in CO_(2)hydrogenation to methanol,Al_(2)O_(3),ZrO_(2)and CeO_(2)modified Cu-ZnO catalysts by the co-precipitation method were prep...Aiming at the problems of insufficient activity and selectivity of Cu-based catalysts in CO_(2)hydrogenation to methanol,Al_(2)O_(3),ZrO_(2)and CeO_(2)modified Cu-ZnO catalysts by the co-precipitation method were prepared,and the influence mechanism of additives on the structure-performance relationship of the catalysts was systematically explored.Through a variety of characterization methods such as XRD,N2 physical adsorption-desorption,TEM,H_(2)-TPR,CO_(2)-TPD and XPS,combined with catalytic performance evaluation experiments,the correlation between the microstructure of catalysts and the reaction performance of CO_(2)hydrogenation to methanol was analyzed in depth.The results show that metal additives significantly improve the performance of catalysts.After the introduction of additives,the specific surface area and pore volume of the catalysts increase,the grain size of Cu decreases,and its dispersion improves.The Ce-modified CZC catalyst exhibited the best performance,with the grain size of CuO as small as 11.41 nm,and the surface oxygen vacancy concentration(OⅡ/OⅠ=3.15)was significantly higher than that of other samples.The reaction performance test shows that under the conditions of 2.8 MPa,8000 h−1 and 280℃,the CO_(2)conversion of the CZC catalyst reached 18.83%,the methanol selectivity was 68.40%,and the methanol yield was 12.88%,all of which are superior to other catalysts.Its excellent performance can be attributed to the fact that CeO_(2)enhances the metal-support interaction,increases the surface basicity,promotes the adsorption and activation of CO_(2),and simultaneously inhibits the reverse water-gas shift side reaction.This study clarifies the structure-activity regulation mechanism of additive modification on Cu-ZnO catalysts,providing a theoretical basis and technical reference for the development of efficient catalysts for CO_(2)hydrogenation to methanol.展开更多
Under the backdrop of“Carbon Peak and Carbon Neutrality”(dual carbon)goal in China,the methane-carbon dioxide reforming reaction has attracted considerable attention due to its environmental benefits of converting t...Under the backdrop of“Carbon Peak and Carbon Neutrality”(dual carbon)goal in China,the methane-carbon dioxide reforming reaction has attracted considerable attention due to its environmental benefits of converting two greenhouse gases(methane and carbon dioxide)into syngas and its promising industrial applications.Nickel(Ni)-based catalysts,with high catalytic activity,low cost,and abundant resources,are considered ideal candidates for industrial applications.In this article,three reaction kinetic models were briefly introduced,namely the Power-Law(PL)model,the Eley-Rideal(ER)model,and the Langmuir-Hinshelwood-Hougen-Watson(LHHW)model.Based on the LHHW model,the reaction kinetics and mechanisms of different catalytic systems were systematically discussed,including the properties of supports,the doping of noble metals and transition metals,the role of promoters,and the influence of the geometric and electronic structures of Ni on the reaction mechanism.Furthermore,the kinetics of carbon deposition and elimination on various catalysts were analyzed.Based on the reaction rate expressions for carbon elimination,the reasons for the high activity of transition metal iron(Fe)-doped catalysts and core-shell structured catalysts in carbon elimination were explained.Based on the detailed collation and comparative analysis of the reaction mechanisms and kinetic characteristics across diverse Ni-based catalytic systems,a theoretical guidance for the designing of high-performance catalysts was provided in this work.展开更多
Electrochemical water splitting represents a sustainable technology for hydrogen(H_(2))production.However,its large-scale implementation is hindered by the high overpotentials required for both the cathodic hydrogen e...Electrochemical water splitting represents a sustainable technology for hydrogen(H_(2))production.However,its large-scale implementation is hindered by the high overpotentials required for both the cathodic hydrogen evolution reaction(HER)and the anodic oxygen evolution reaction(OER).Transition metal-based catalysts have garnered significant research interest as promising alternatives to noble-metal catalysts,owing to their low cost,tunable composition,and noble-metal-like catalytic activity.Nevertheless,systematic reviews on their application as bifunctional catalysts for overall water splitting(OWS)are still limited.This review comprehensively outlines the principal categories of bifunctional transition metal electrocatalysts derived from electrospun nanofibers(NFs),including metals,oxides,phosphides,sulfides,and carbides.Key strategies for enhancing their catalytic performance are systematically summarized,such as heterointerface engineering,heteroatom doping,metal-nonmetal-metal bridging architectures,and single-atom site design.Finally,current challenges and future research directions are discussed,aiming to provide insightful perspectives for the rational design of high-performance electrocatalysts for OWS.展开更多
Against the backdrop of escalating global climate change and energy crises,the resource utilization of carbon dioxide(CO_(2)),a major greenhouse gas,has become a crucial pathway for achieving carbon peaking and carbon...Against the backdrop of escalating global climate change and energy crises,the resource utilization of carbon dioxide(CO_(2)),a major greenhouse gas,has become a crucial pathway for achieving carbon peaking and carbon neutrality goals.The hydrogenation of CO_(2)to methanol not only enables carbon sequestration and recycling,but also provides a route to produce high value-added fuels and basic chemical feedstocks,holding significant environmental and economic potential.However,this conversion process is thermodynamically and kinetically limited,and traditional catalyst systems(e.g.,Cu/ZnO/Al_(2)O_(3))exhibit inadequate activity,selectivity,and stability under mild conditions.Therefore,the development of novel high-performance catalysts with precisely tunable structures and functionalities is imperative.Metal-organic frameworks(MOFs),as crystalline porous materials with high surface area,tunable pore structures,and diverse metal-ligand compositions,have the great potential in CO_(2)hydrogenation catalysis.Their structural design flexibility allows for the construction of well-dispersed active sites,tailored electronic environments,and enhanced metal-support interactions.This review systematically summarizes the recent advances in MOF-based and MOF-derived catalysts for CO_(2)hydrogenation to methanol,focusing on four design strategies:(1)spatial confinement and in situ construction,(2)defect engineering and ion-exchange,(3)bimetallic synergy and hybrid structure design,and(4)MOF-derived nanomaterial synthesis.These approaches significantly improve CO_(2)conversion and methanol selectivity by optimizing metal dispersion,interfacial structures,and reaction pathways.The reaction mechanism is further explored by focusing on the three main reaction pathways:the formate pathway(HCOO*),the RWGS(Reverse Water Gas Shift reaction)+CO*hydrogenation pathway,and the trans-COOH pathway.In situ spectroscopic studies and density functional theory(DFT)calculations elucidate the formation and transformation of key intermediates,as well as the roles of active sites,metal-support interfaces,oxygen vacancies,and promoters.Additionally,representative catalytic performance data for MOFbased systems are compiled and compared,demonstrating their advantages over traditional catalysts in terms of CO_(2)conversion,methanol selectivity,and space-time yield.Future perspectives for MOF-based CO_(2)hydrogenation catalysts will prioritize two main directions:structural design and mechanistic understanding.The precise construction of active sites through multi-metallic synergy,defect engineering,and interfacial electronic modulation should be made to enhance catalyst selectivity and stability.In addition,advanced in situ characterization techniques combined with theoretical modeling are essential to unravel the detailed reaction mechanisms and intermediate behaviors,thereby guiding rational catalyst design.Moreover,to enable industrial application,challenges related to thermal/hydrothermal stability,catalyst recyclability,and cost-effective large-scale synthesis must be addressed.The development of green,scalable preparation methods and the integration of MOF catalysts into practical reaction systems(e.g.,flow reactors)will be crucial for bridging the gap between laboratory research and commercial deployment.Ultimately,multi-scale structure-performance optimization and catalytic system integration will be vital for accelerating the industrialization of MOF-based CO_(2)-to-methanol technologies.展开更多
To elucidate the effect of calcite-regulated activated carbon(AC)structure on low-temperature denitrification performance of SCR catalysts,this work prepared a series of Mn-Ce/De-AC-xCaCO_(3)(x is the calcite content ...To elucidate the effect of calcite-regulated activated carbon(AC)structure on low-temperature denitrification performance of SCR catalysts,this work prepared a series of Mn-Ce/De-AC-xCaCO_(3)(x is the calcite content in coal)catalysts were prepared by the incipient wetness impregnation method,followed by acid washing to remove calcium-containing minerals.Comprehensive characterization and low-temperature denitrification tests revealed that calcite-induced structural modulation of coal-derived AC significantly enhances catalytic activity.Specifically,NO conversion increased from 88.3%of Mn-Ce/De-AC to 91.7%of Mn-Ce/De-AC-1CaCO_(3)(210℃).The improved SCR denitrification activity results from the enhancement of physicochemical properties including higher Mn^(4+)content and Ce^(4+)/Ce^(3+)ratio,an abundance of chemisorbed oxygen and acidic sites,which could strengthen the SCR reaction pathways(richer NH_(3)activated species and bidentate nitrate active species).Therefore,NO removal is enhanced.展开更多
Catalysts are key for olefin polymerization reactions and are also ubiquitous in catalysis science.Multinuclear metal catalysts have witnessed enhanced performances in catalytic reactions relative to mononuclear catal...Catalysts are key for olefin polymerization reactions and are also ubiquitous in catalysis science.Multinuclear metal catalysts have witnessed enhanced performances in catalytic reactions relative to mononuclear catalysts,but which substantially involve multi-step,tedious,and difficult synthesis.Herein,this study reports an intriguing approach to construct multi-nuclear catalysts for the milestoneα-diimine nickel catalysts using an oligomeric strategy.A polymerizable norbornene unit is incorporated into theα-diimine ligand backbone,leading to the formation of the monomeric nickel catalyst Ni_(1)and its corresponding oligomeric nickel catalysts(Ni_(3)and Ni_(5))with varying degrees of polymerization(DP=3 and 5).Notably,the oligomeric catalyst Ni_(5)was facilely scaled up(50 g-level),showed enhanced thermal stability,exhibited 4.6 times higher activity,and yielded polyethylene elastomer with a 379%increased molecular weight in ethylene polymerization,compared to the monomeric catalyst Ni_(1).Catalytic performance enhancements of oligomeric catalysts were found to be DP-dependent.The kilogram-scale polyethylene,produced using Ni_(5)in a 20 L reactor,presented a highly branched all-hydrocarbon structure,which demonstrated typical elastic properties(tensile strength:4 MPa,elastic recovery:SR=72%)along with great processability(MFI=3.0 g/10 min),insulating characteristics(volume resistivity=2×10^(16)Ω/m),and hydrophobicity(water vapor permeability:0.03 g/m^(2)/day),suggesting potentially practical applications.展开更多
Seawater zinc-air batteries are promising energy storage devices due to their high energy density and utilization of seawater electrolytes.However,their efficiency is hindered by the sluggish oxygen reduction reaction...Seawater zinc-air batteries are promising energy storage devices due to their high energy density and utilization of seawater electrolytes.However,their efficiency is hindered by the sluggish oxygen reduction reaction(ORR)and chlorideinduced degradation over conventional catalysts.In this study,we proposed a universal synthetic strategy to construct heteroatom axially coordinated Fe–N_(4) single-atom seawater catalyst materials(Cl–Fe–N_(4) and S–Fe–N_(4)).X-ray absorption spectroscopy confirmed their five-coordinated square pyramidal structure.Systematic evaluation of catalytic activities revealed that compared with S–Fe–N_(4),Cl–Fe–N_(4) exhibits smaller electrochemical active surface area and specific surface area,yet demonstrates higher limiting current density(5.8 mA cm^(−2)).The assembled zinc-air batteries using Cl–Fe–N_(4) showed superior power density(187.7 mW cm^(−2) at 245.1 mA cm^(−2)),indicating that Cl axial coordination more effectively enhances the intrinsic ORR activity.Moreover,Cl–Fe–N_(4) demonstrates stronger Cl−poisoning resistance in seawater environments.Chronoamperometry tests and zinc-air battery cycling performance evaluations confirmed its enhanced stability.Density functional theory calculations revealed that the introduction of heteroatoms in the axial direction regulates the electron center of Fe single atom,leading to more active reaction intermediates and increased electron density of Fe single sites,thereby enhancing the reduction in adsorbed intermediates and hence the overall ORR catalytic activity.展开更多
Lithium-sulfur(Li-S)batteries boast a theoretical energy density as high as 2600 Wh·kg^(−1),positioning them as a highly attractive option for future advanced energy storage systems.Challenges such as slow transf...Lithium-sulfur(Li-S)batteries boast a theoretical energy density as high as 2600 Wh·kg^(−1),positioning them as a highly attractive option for future advanced energy storage systems.Challenges such as slow transformation kinetics and shuttle effects associated with lithium polysulfides(LiPSs)have seriously hindered their practical applications.In this paper,we present a new method for the synthesis of hollow carbon-sphere-supported Co monatomic catalysts(Co-N-C).This new synthesis method achieves pyrolytic coordination using a precursor rich in imide(-RC=N-)polymers.This synthesis method not only improves the adsorbability and catalytic activity of LiPS but also significantly weakens the shuttle effect and generates Co-N-C with superior conductivity,abundant hollow structures,and a high specific surface area,thus efficiently capturing and restricting the movement of LiPS intermediates.The dispersed Co monoatomic catalysts(Co SACs)were anchored to a highly conductive nitrogen-doped carbon framework and exhibited symmetric N-coordination active sites(Co-N_(4))to ensure fast redox kinetics of LiPS and Li_(2)S_(2)/Li_(2)S solid-state products.The lithium-sulfur battery with Co-N-C as the sulfur carrier showed excellent discharging capacity of 1146.6 mAh·g^(−1) at a discharge rate of 0.5 C and maintained excellent performance at a high discharge rate of 2 C.The capacity decay rate in 500 cycles was only 0.086%per cycle,reflecting excellent long-term cycle stability.This study highlights the key role of the synergistic effect between single-atom cobalt catalysts and hollow carbon spheres in enhancing the efficiency of lithium-sulfur(Li-S)batteries.It also provides valuable insights into the construction and fabrication of highly active monatomic catalysts.The catalytic conversion efficiency of lithium polysulfides is significantly enhanced when embedded in hollow carbon architectures,which serves as a critical strategy for optimizing the electrochemical behavior of next-generation Li-S batteries.展开更多
Methanol steam reforming(MSR)represents a promising route for hydrogen production,leveraging the high energy density and liquid-phase storage advantages of methanol.Copper-based catalysts have become indispensable for...Methanol steam reforming(MSR)represents a promising route for hydrogen production,leveraging the high energy density and liquid-phase storage advantages of methanol.Copper-based catalysts have become indispensable for MSR due to their cost-effectiveness,exceptional catalytic activity,and tunable selectivity.However,persistent challenges such as thermal sintering,undesirable CO byproduct formation,diminished low-temperature reactivity,and long-term catalyst deactivation limit their broad industrial deployment.This review comprehensively examines the mechanistic pathways of MSR over Cu-based catalysts,with particular focus on differentiating catalyst formulations optimized for high-temperature(>200°C)versus low-temperature(<200°C)operation.It highlights the decisive influence of Cu nanoparticle size,electronic structure,and crystal structure on catalytic performance.Cutting-edge design strategies,including multi-element engineering,innovative synthesis techniques,and deactivation mitigation,are critically evaluated to elucidate mechanistic connections between atomic-scale structure and catalytic performance enhancement.Finally,industrial applications of commercial Cu/ZnO/Al_(2)O_(3)variants and their scalability challenges are discussed,alongside prospective strategies for catalyst innovation and engineering to advance next-generation hydrogen production.展开更多
Endogenous hydrogen systems,consisting of metal–organic coordination catalysts and alcohols,have been widely applied for the transfer hydrogenation(TH)of biomass-derived carbonyl compounds in recent years.Metal-organ...Endogenous hydrogen systems,consisting of metal–organic coordination catalysts and alcohols,have been widely applied for the transfer hydrogenation(TH)of biomass-derived carbonyl compounds in recent years.Metal-organic coordination catalysts showed satisfactory ability of TH in the secondary alcohols,but most of them could not effectively employ the cheaper primary alcohols as hydrogen donors.Furthermore,they commonly contained high metal contents,which also led to low catalytic efficiency in significant measure.In this work,we constructed a novel magnesium single-atom catalyst(Mg-NC)with merely 0.37 wt%Mg by means of a combined self-assembly and pyrolysis strategy.The characterization results indicated that Mg was atomically dispersed and it was coordinated with four pyridinic-N in Mg-NC.Due to the obvious electron transfer from Mg to its coordinated pyridinic-N,Mg–N_(4)active centers displayed high Lewis acid-base strength with abundant content,which brought remarkable catalytic activity.When Mg-NC was used for the TH of 5-hydroxymethylfurfural(HMF)in ethanol(EtOH),2,5-bis(hydroxymethyl)furan(BHMF)yield was up to 96.3%with high productivity of 19.85 molBHMF mol_(Mg)^(−1)h^(−1)at 150°C for 5 h.More interestingly,the process of TH over Mg-NC in EtOH was proved to proceed via the hydrogen radical mechanism.Additionally,Mg-NC exhibited powerful catalytic universality;it could not only utilize other primary alcohols(such as n-propanol and n-butanol)as hydrogen donors,but also catalyze the TH of other carbonyl compounds(such as furfural,5-methylfurfural,benzaldehyde,cyclohexanone,and levulinic acid).Overall,this work offered some important clues and references to reinforce the hydrogen-supplying ability of primary alcohols in the TH of various biomass-derived carbonyl compounds to high-value fine chemicals.展开更多
High‐entropy amorphous catalysts(HEACs)integrate multielement synergy with structural disorder,making them promising candidates for water splitting.Their distinctive features—including flexible coordination environm...High‐entropy amorphous catalysts(HEACs)integrate multielement synergy with structural disorder,making them promising candidates for water splitting.Their distinctive features—including flexible coordination environments,tunable electronic structures,abundant unsaturated active sites,and dynamic structural reassembly—collectively enhance electrochemical activity and durability under operating conditions.This review summarizes recent advances in HEACs for hydrogen evolution,oxygen evolution,and overall water splitting,highlighting their disorder-driven advantages over crystalline counterparts.Catalytic performance benchmarks are presented,and mechanistic insights are discussed,focusing on how multimetallic synergy,amorphization effect,and in‐situ reconstruction cooperatively regulate reaction pathways.These insights provide guidance for the rational design of next‐generation amorphous high‐entropy electrocatalysts with improved efficiency and durability.展开更多
Using photoelectrocatalytic CO_(2) reduction reaction(CO_(2)RR)to produce valuable fuels is a fascinating way to alleviate environmental issues and energy crises.Bismuth-based(Bi-based)catalysts have attracted widespr...Using photoelectrocatalytic CO_(2) reduction reaction(CO_(2)RR)to produce valuable fuels is a fascinating way to alleviate environmental issues and energy crises.Bismuth-based(Bi-based)catalysts have attracted widespread attention for CO_(2)RR due to their high catalytic activity,selectivity,excellent stability,and low cost.However,they still need to be further improved to meet the needs of industrial applications.This review article comprehensively summarizes the recent advances in regulation strategies of Bi-based catalysts and can be divided into six categories:(1)defect engineering,(2)atomic doping engineering,(3)organic framework engineering,(4)inorganic heterojunction engineering,(5)crystal face engineering,and(6)alloying and polarization engineering.Meanwhile,the corresponding catalytic mechanisms of each regulation strategy will also be discussed in detail,aiming to enable researchers to understand the structure-property relationship of the improved Bibased catalysts fundamentally.Finally,the challenges and future opportunities of the Bi-based catalysts in the photoelectrocatalytic CO_(2)RR application field will also be featured from the perspectives of the(1)combination or synergy of multiple regulatory strategies,(2)revealing formation mechanism and realizing controllable synthesis,and(3)in situ multiscale investigation of activation pathways and uncovering the catalytic mechanisms.On the one hand,through the comparative analysis and mechanism explanation of the six major regulatory strategies,a multidimensional knowledge framework of the structure-activity relationship of Bi-based catalysts can be constructed for researchers,which not only deepens the atomic-level understanding of catalytic active sites,charge transport paths,and the adsorption behavior of intermediate products,but also provides theoretical guiding principles for the controllable design of new catalysts;on the other hand,the promising collaborative regulation strategies,controllable synthetic paths,and the in situ multiscale characterization techniques presented in this work provides a paradigm reference for shortening the research and development cycle of high-performance catalysts,conducive to facilitating the transition of photoelectrocatalytic CO_(2)RR technology from the laboratory routes to industrial application.展开更多
Large-scale CO_(2)emissions have exacerbated the greenhouse effect,reinforcing the critical need for efficient CO_(2)mitigation methods.Plasma-catalytic technology enables CO_(2)conversion under mild conditions,especi...Large-scale CO_(2)emissions have exacerbated the greenhouse effect,reinforcing the critical need for efficient CO_(2)mitigation methods.Plasma-catalytic technology enables CO_(2)conversion under mild conditions,especially for CO_(2)methanation(the Sabatier reaction),which has attracted significant attention due to its economic benefits and the potential for safe energy transportation via existing natural gas pipelines.The development of high-performance CO_(2)methanation catalysts remains an ongoing and long-term objective,and there is a lack of adequate in-situ characterization techniques to investigate the mechanisms.This study focuses on the Ni/La_(2)O_(3)(LN)catalyst and introduces two CO_(2)activation strategies through F and Na modifications:the Ni-Ov-Ni site activation with electron transfer from Ni0 under low-power conditions and basic site activation under high-power conditions.The LN-NaF catalysts enhance CO_(2)methanation activity across the entire power range compared to LN,achieving a CO_(2)conversion of 86.3%and CH4 selectivity of 99.4%.Additionally,LN-F(h)reaches a CH4 yield 4.15 times higher than that of LN at low power.Furthermore,in-situ diffuse reflectance infrared Fourier transform(DRIFT)spectroscopy with a self-made reactor are performed under plasma-catalytic conditions to reveal the CO_(2)adsorption and conversion mechanisms,indicating that different dopants(F,Na,and NaF)exhibit promoting effects on different intermediates,resulting in variations in CO_(2)methanation activity.This study provides valuable insights for improving catalyst performance and a thorough comprehension of mechanisms in CO_(2)methanation.展开更多
S and Co co-doped carbon catalysts were prepared via pyrolysis of MOF-71 and thiourea mixtures at 800℃at a mass ratio of MOF-71 to thiourea of 1:0.1 to effectively activate peroxymonosulfate(PMS)for methylene blue(MB...S and Co co-doped carbon catalysts were prepared via pyrolysis of MOF-71 and thiourea mixtures at 800℃at a mass ratio of MOF-71 to thiourea of 1:0.1 to effectively activate peroxymonosulfate(PMS)for methylene blue(MB)degradation.The effects of two different mixing routes were identified on the MB degradation performance.Particularly,the catalyst obtained by the alcohol solvent evaporation(MOF-AEP)mixing route could degrade 95.60%MB(50 mg/L)within 4 min(degradation rate:K=0.78 min^(-1)),which was faster than that derived from the direct grinding method(MOF-DGP,80.97%,K=0.39 min^(-1)).X-ray photoelectron spectroscopy revealed that the Co-S content of MOF-AEP(43.39at%)was less than that of MOF-DGP(54.73at%),and the proportion of C-S-C in MOF-AEP(13.56at%)was higher than that of MOF-DGP(10.67at%).Density functional theory calculations revealed that the adsorption energy of Co for PMS was -2.94 eV when sulfur was doped as C-S-C on the carbon skeleton,which was higher than that when sulfur was doped next to cobalt in the form of Co-S bond(-2.86 eV).Thus,the C-S-C sites might provide more contributions to activate PMS compared with Co-S.Furthermore,the degradation parameters,including pH and MOF-AEP dosage,were investigated.Finally,radical quenching experiments and electron paramagnetic resonance(EPR)measurements revealed that ^(1)O_(2)might be the primary catalytic species,whereas·O~(2-)might be the secondary one in degrading MB.展开更多
Green hydrogen from water splitting has emerged as a critical energy vector with the potential to spearhead the global transition to a fossil fuel-independent society.The field of catalysis has been revolutionized by ...Green hydrogen from water splitting has emerged as a critical energy vector with the potential to spearhead the global transition to a fossil fuel-independent society.The field of catalysis has been revolutionized by single-atom catalysts(SACs),which exhibit unique and intricate interactions between atomically dispersed metal atoms and their supports.Recently,bimetallic SACs(bimSACs)have garnered significant attention for leveraging the synergistic functions of two metal ions coordinated on appropriately designed supports.BimSACs offer an avenue for rich metal–metal and metal–support cooperativity,potentially addressing current limitations of SACs in effectively furnishing transformations which involve synchronous proton–electron exchanges,substrate activation with reversible redox cycles,simultaneous multi-electron transfer,regulation of spin states,tuning of electronic properties,and cyclic transition states with low activation energies.This review aims to encapsulate the growing advancements in bimSACs,with an emphasis on their pivotal role in hydrogen generation via water splitting.We subsequently delve into advanced experimental methodologies for the elaborate characterization of SACs,elucidate their electronic properties,and discuss their local coordination environment.Overall,we present comprehensive discussion on the deployment of bimSACs in both hydrogen evolution reaction and oxygen evolution reaction,the two half-reactions of the water electrolysis process.展开更多
With ongoing global warming and increasing energy demands,the CH_(4)-CO_(2)reforming reaction(dry reforming of methane,DRM)has garnered significant attention as a promising carbon capture and utilization technology.Ni...With ongoing global warming and increasing energy demands,the CH_(4)-CO_(2)reforming reaction(dry reforming of methane,DRM)has garnered significant attention as a promising carbon capture and utilization technology.Nickel-based catalysts are renowned for their outstanding activity and selectivity in this process.The impact of metal-support interaction(MSI),on Ni-based catalyst performance has been extensively researched and debated recently.This paper reviews the recent research progress of MSI on Ni-based catalysts and their characterization and modulation strategies in catalytic reactions.From the perspective of MSI,the effects of different carriers(metal oxides,carbon materials and molecular sieves,etc.)are introduced on the dispersion and surface structure of Ni active metal particles,and the effect of MSI on the activity and stability of DRM reactions on Ni-based catalysts is discussed in detail.Future research should focus on better understanding and controlling MSI to improve the performance and durability of nickel-based catalysts in CH_(4)-CO_(2)reforming,advancing cleaner energy technologies.展开更多
Exploiting non-precious metal catalysts with excellent oxygen reduction reaction(ORR)performance for energy devices is paramount essential for the green and sustainable society development.Herein,low-cost,high-perform...Exploiting non-precious metal catalysts with excellent oxygen reduction reaction(ORR)performance for energy devices is paramount essential for the green and sustainable society development.Herein,low-cost,high-performance biomass-derived ORR catalysts with an asymmetric Fe-N_(3)P configuration was prepared by a simple pyrolysis-etching technique,where carboxymethyl cellulose(CMC)was used as the carbon source,urea and 1,10-phenanthroline iron complex(FePhen)as additives,and Na_(3)PO_(4)as the phosphorus dopant and a pore-forming agent.The CMC-derived FeNPC catalyst displayed a large specific area(BET:1235 m^(2)g^(-1))with atomically dispersed Fe-N_(3)P active sites,which exhibited superior ORR activity and stability in alkaline solution(E_(1/2)=0.90 V vs.RHE)and Zn-air batteries(P_(max)=149 mW cm^(-2))to commercial Pt/C catalyst(E_(1/2)=0.87 V,P_(max)=118 mW cm^(-2))under similar experimental conditions.This work provides a feasible and costeffective route toward highly efficient ORR catalysts and their application to Zn-air batteries for energy conversion.展开更多
Converting CO_(2)with green hydrogen to methanol as a carbon-neutral liquid fuel is a promising route for the long-term storage and distribution of intermittent renewable energy.Nevertheless,attaining highly efficient...Converting CO_(2)with green hydrogen to methanol as a carbon-neutral liquid fuel is a promising route for the long-term storage and distribution of intermittent renewable energy.Nevertheless,attaining highly efficient methanol synthesis catalysts from the vast composition space remains a significant challenge.Here we present a machine learning framework for accelerating the development of high space-time yield(STY)methanol synthesis catalysts.A database of methanol synthesis catalysts has been compiled,consisting of catalyst composition,preparation parameters,structural characteristics,reaction conditions and their corresponding catalytic performance.A methodology for constructing catalyst features based on the intrinsic physicochemical properties of the catalyst components has been developed,which significantly reduced the data dimensionality and enhanced the efficiency of machine learning operations.Two high-precision machine learning prediction models for the activities and product selectivity of catalysts were trained and obtained.Using this machine learning framework,an efficient search was achieved within the catalyst composition space,leading to the successful identification of high STY multielement oxide methanol synthesis catalysts.Notably,the CuZnAlTi catalyst achieved high STYs of 0.49 and 0.65 g_(MeOH)/(g_(catalyst)h)for CO_(2)and CO hydrogenation to methanol at 250℃,respectively,and the STY was further increased to 2.63 g_(Me OH)/(g_(catalyst)h)in CO and CO_(2)co-hydrogenation.展开更多
The pursuit of alternative fuel generation technologies has gained momentum due to the diminishing reserves of fossil fuels and global warming from increased CO_(2)emission.Among the proposed methods,the hydrogenation...The pursuit of alternative fuel generation technologies has gained momentum due to the diminishing reserves of fossil fuels and global warming from increased CO_(2)emission.Among the proposed methods,the hydrogenation of CO_(2)to produce marketable carbon-based products like methanol and ethanol is a practical approach that offers great potential to reduce CO_(2)emissions.Although significant volumes of methanol are currently produced from CO_(2),developing highly efficient and stable catalysts is crucial for further enhancing conversion and selectivity,thereby reducing process costs.An in-depth examination of the differences and similarities in the reaction pathways for methanol and ethanol production highlights the key factors that drive C-C coupling.Identifying these factors guides us toward developing more effective catalysts for ethanol synthesis.In this paper,we explore how different catalysts,through the production of various intermediates,can initiate the synthesis of methanol or ethanol.The catalytic mechanisms proposed by spectroscopic techniques and theoretical calculations,including operando X-ray methods,FTIR analysis,and DFT calculations,are summarized and presented.The following discussion explores the structural properties and composition of catalysts that influence C-C coupling and optimize the conversion rate of CO_(2)into ethanol.Lastly,the review examines recent catalysts employed for selective methanol and ethanol production,focusing on single-atom catalysts.展开更多
Inactivation of carbon-based transition metal catalysts,which was caused by electron loss,limited their application in advanced oxidation processes.Therefore,Co and TiO_(2) double-loaded carbon nanofiber material(Co@C...Inactivation of carbon-based transition metal catalysts,which was caused by electron loss,limited their application in advanced oxidation processes.Therefore,Co and TiO_(2) double-loaded carbon nanofiber material(Co@CNFs-TiO_(2))was synthesized in this study.Photocatalytic and chemical catalytic systems were synergized efficiently.Tetracycline was eliminated within 15 min.The degradation rate remained above 90%after five cycles,and the 50%promotion proved the high stability of Co@CNFs-TiO_(2).The main reactive oxygen species in this system were sulfate radicals,whereas Co and TiO_(2) represented the active sites of the catalytic reaction.Electrons generated from TiO_(2) during the photocatalytic process were transferred to Co,which promoted the Co(Ⅲ)/Co(Ⅱ)cycle and maintained Co in a low-valence state,thereby stimulating the generation of sulfate radicals.In this study,the effective regulation of reactive oxygen species in the reaction system was realized.The results provided a guidance for in situ electron replenishment and regeneration of carbon-based transition metal catalysts,which will expand the practical application of advanced oxidation processes.展开更多
基金Supported by National Key R&D Program of China(2022YFA1503400)。
文摘Aiming at the problems of insufficient activity and selectivity of Cu-based catalysts in CO_(2)hydrogenation to methanol,Al_(2)O_(3),ZrO_(2)and CeO_(2)modified Cu-ZnO catalysts by the co-precipitation method were prepared,and the influence mechanism of additives on the structure-performance relationship of the catalysts was systematically explored.Through a variety of characterization methods such as XRD,N2 physical adsorption-desorption,TEM,H_(2)-TPR,CO_(2)-TPD and XPS,combined with catalytic performance evaluation experiments,the correlation between the microstructure of catalysts and the reaction performance of CO_(2)hydrogenation to methanol was analyzed in depth.The results show that metal additives significantly improve the performance of catalysts.After the introduction of additives,the specific surface area and pore volume of the catalysts increase,the grain size of Cu decreases,and its dispersion improves.The Ce-modified CZC catalyst exhibited the best performance,with the grain size of CuO as small as 11.41 nm,and the surface oxygen vacancy concentration(OⅡ/OⅠ=3.15)was significantly higher than that of other samples.The reaction performance test shows that under the conditions of 2.8 MPa,8000 h−1 and 280℃,the CO_(2)conversion of the CZC catalyst reached 18.83%,the methanol selectivity was 68.40%,and the methanol yield was 12.88%,all of which are superior to other catalysts.Its excellent performance can be attributed to the fact that CeO_(2)enhances the metal-support interaction,increases the surface basicity,promotes the adsorption and activation of CO_(2),and simultaneously inhibits the reverse water-gas shift side reaction.This study clarifies the structure-activity regulation mechanism of additive modification on Cu-ZnO catalysts,providing a theoretical basis and technical reference for the development of efficient catalysts for CO_(2)hydrogenation to methanol.
基金Supported by Innovation Capability Support Program of Shaanxi(2024RS-CXTD-53,2024ZC-KJXX-096)the Key R&D Program of Shaanxi Province(2022QCY-LL-69)Xi’an Science and Technology Project(24GXFW0089)。
文摘Under the backdrop of“Carbon Peak and Carbon Neutrality”(dual carbon)goal in China,the methane-carbon dioxide reforming reaction has attracted considerable attention due to its environmental benefits of converting two greenhouse gases(methane and carbon dioxide)into syngas and its promising industrial applications.Nickel(Ni)-based catalysts,with high catalytic activity,low cost,and abundant resources,are considered ideal candidates for industrial applications.In this article,three reaction kinetic models were briefly introduced,namely the Power-Law(PL)model,the Eley-Rideal(ER)model,and the Langmuir-Hinshelwood-Hougen-Watson(LHHW)model.Based on the LHHW model,the reaction kinetics and mechanisms of different catalytic systems were systematically discussed,including the properties of supports,the doping of noble metals and transition metals,the role of promoters,and the influence of the geometric and electronic structures of Ni on the reaction mechanism.Furthermore,the kinetics of carbon deposition and elimination on various catalysts were analyzed.Based on the reaction rate expressions for carbon elimination,the reasons for the high activity of transition metal iron(Fe)-doped catalysts and core-shell structured catalysts in carbon elimination were explained.Based on the detailed collation and comparative analysis of the reaction mechanisms and kinetic characteristics across diverse Ni-based catalytic systems,a theoretical guidance for the designing of high-performance catalysts was provided in this work.
基金Supported by the National Natural Science Foundation of China(No.52273056)the Science and Technology Development Program of Jilin Province,China(No.YDZJ202501ZYTS305)。
文摘Electrochemical water splitting represents a sustainable technology for hydrogen(H_(2))production.However,its large-scale implementation is hindered by the high overpotentials required for both the cathodic hydrogen evolution reaction(HER)and the anodic oxygen evolution reaction(OER).Transition metal-based catalysts have garnered significant research interest as promising alternatives to noble-metal catalysts,owing to their low cost,tunable composition,and noble-metal-like catalytic activity.Nevertheless,systematic reviews on their application as bifunctional catalysts for overall water splitting(OWS)are still limited.This review comprehensively outlines the principal categories of bifunctional transition metal electrocatalysts derived from electrospun nanofibers(NFs),including metals,oxides,phosphides,sulfides,and carbides.Key strategies for enhancing their catalytic performance are systematically summarized,such as heterointerface engineering,heteroatom doping,metal-nonmetal-metal bridging architectures,and single-atom site design.Finally,current challenges and future research directions are discussed,aiming to provide insightful perspectives for the rational design of high-performance electrocatalysts for OWS.
基金Supported by the National Key Research and Development Program of China(2023YFB4104500,2023YFB4104502)the National Natural Science Foundation of China(22138013)the Taishan Scholar Project(ts201712020).
文摘Against the backdrop of escalating global climate change and energy crises,the resource utilization of carbon dioxide(CO_(2)),a major greenhouse gas,has become a crucial pathway for achieving carbon peaking and carbon neutrality goals.The hydrogenation of CO_(2)to methanol not only enables carbon sequestration and recycling,but also provides a route to produce high value-added fuels and basic chemical feedstocks,holding significant environmental and economic potential.However,this conversion process is thermodynamically and kinetically limited,and traditional catalyst systems(e.g.,Cu/ZnO/Al_(2)O_(3))exhibit inadequate activity,selectivity,and stability under mild conditions.Therefore,the development of novel high-performance catalysts with precisely tunable structures and functionalities is imperative.Metal-organic frameworks(MOFs),as crystalline porous materials with high surface area,tunable pore structures,and diverse metal-ligand compositions,have the great potential in CO_(2)hydrogenation catalysis.Their structural design flexibility allows for the construction of well-dispersed active sites,tailored electronic environments,and enhanced metal-support interactions.This review systematically summarizes the recent advances in MOF-based and MOF-derived catalysts for CO_(2)hydrogenation to methanol,focusing on four design strategies:(1)spatial confinement and in situ construction,(2)defect engineering and ion-exchange,(3)bimetallic synergy and hybrid structure design,and(4)MOF-derived nanomaterial synthesis.These approaches significantly improve CO_(2)conversion and methanol selectivity by optimizing metal dispersion,interfacial structures,and reaction pathways.The reaction mechanism is further explored by focusing on the three main reaction pathways:the formate pathway(HCOO*),the RWGS(Reverse Water Gas Shift reaction)+CO*hydrogenation pathway,and the trans-COOH pathway.In situ spectroscopic studies and density functional theory(DFT)calculations elucidate the formation and transformation of key intermediates,as well as the roles of active sites,metal-support interfaces,oxygen vacancies,and promoters.Additionally,representative catalytic performance data for MOFbased systems are compiled and compared,demonstrating their advantages over traditional catalysts in terms of CO_(2)conversion,methanol selectivity,and space-time yield.Future perspectives for MOF-based CO_(2)hydrogenation catalysts will prioritize two main directions:structural design and mechanistic understanding.The precise construction of active sites through multi-metallic synergy,defect engineering,and interfacial electronic modulation should be made to enhance catalyst selectivity and stability.In addition,advanced in situ characterization techniques combined with theoretical modeling are essential to unravel the detailed reaction mechanisms and intermediate behaviors,thereby guiding rational catalyst design.Moreover,to enable industrial application,challenges related to thermal/hydrothermal stability,catalyst recyclability,and cost-effective large-scale synthesis must be addressed.The development of green,scalable preparation methods and the integration of MOF catalysts into practical reaction systems(e.g.,flow reactors)will be crucial for bridging the gap between laboratory research and commercial deployment.Ultimately,multi-scale structure-performance optimization and catalytic system integration will be vital for accelerating the industrialization of MOF-based CO_(2)-to-methanol technologies.
基金Supported by the Science and Technology Cooperation and Exchange special project of Cooperation of Shanxi Province(202404041101014)the Fundamental Research Program of Shanxi Province(202403021212333)+3 种基金the Joint Funds of the National Natural Science Foundation of China(U24A20555)the Lvliang Key R&D of University-Local Cooperation(2023XDHZ10)the Initiation Fund for Doctoral Research of Taiyuan University of Science and Technology(20242026)the Outstanding Doctor Funding Award of Shanxi Province(20242080).
文摘To elucidate the effect of calcite-regulated activated carbon(AC)structure on low-temperature denitrification performance of SCR catalysts,this work prepared a series of Mn-Ce/De-AC-xCaCO_(3)(x is the calcite content in coal)catalysts were prepared by the incipient wetness impregnation method,followed by acid washing to remove calcium-containing minerals.Comprehensive characterization and low-temperature denitrification tests revealed that calcite-induced structural modulation of coal-derived AC significantly enhances catalytic activity.Specifically,NO conversion increased from 88.3%of Mn-Ce/De-AC to 91.7%of Mn-Ce/De-AC-1CaCO_(3)(210℃).The improved SCR denitrification activity results from the enhancement of physicochemical properties including higher Mn^(4+)content and Ce^(4+)/Ce^(3+)ratio,an abundance of chemisorbed oxygen and acidic sites,which could strengthen the SCR reaction pathways(richer NH_(3)activated species and bidentate nitrate active species).Therefore,NO removal is enhanced.
基金financial support from the National Natural Science Foundation of China(Nos.22401274,U23B6011)the Jilin Provincial Science and Technology Department Program(No.20250102070JC)。
文摘Catalysts are key for olefin polymerization reactions and are also ubiquitous in catalysis science.Multinuclear metal catalysts have witnessed enhanced performances in catalytic reactions relative to mononuclear catalysts,but which substantially involve multi-step,tedious,and difficult synthesis.Herein,this study reports an intriguing approach to construct multi-nuclear catalysts for the milestoneα-diimine nickel catalysts using an oligomeric strategy.A polymerizable norbornene unit is incorporated into theα-diimine ligand backbone,leading to the formation of the monomeric nickel catalyst Ni_(1)and its corresponding oligomeric nickel catalysts(Ni_(3)and Ni_(5))with varying degrees of polymerization(DP=3 and 5).Notably,the oligomeric catalyst Ni_(5)was facilely scaled up(50 g-level),showed enhanced thermal stability,exhibited 4.6 times higher activity,and yielded polyethylene elastomer with a 379%increased molecular weight in ethylene polymerization,compared to the monomeric catalyst Ni_(1).Catalytic performance enhancements of oligomeric catalysts were found to be DP-dependent.The kilogram-scale polyethylene,produced using Ni_(5)in a 20 L reactor,presented a highly branched all-hydrocarbon structure,which demonstrated typical elastic properties(tensile strength:4 MPa,elastic recovery:SR=72%)along with great processability(MFI=3.0 g/10 min),insulating characteristics(volume resistivity=2×10^(16)Ω/m),and hydrophobicity(water vapor permeability:0.03 g/m^(2)/day),suggesting potentially practical applications.
基金funded by the Innovative Research Group Project of the National Natural Science Foundation of China(52121004)the Research Development Fund(No.RDF-21-02-060)by Xi’an Jiaotong-Liverpool University+1 种基金support received from the Suzhou Industrial Park High Quality Innovation Platform of Functional Molecular Materials and Devices(YZCXPT2023105)the XJTLU Advanced Materials Research Center(AMRC).
文摘Seawater zinc-air batteries are promising energy storage devices due to their high energy density and utilization of seawater electrolytes.However,their efficiency is hindered by the sluggish oxygen reduction reaction(ORR)and chlorideinduced degradation over conventional catalysts.In this study,we proposed a universal synthetic strategy to construct heteroatom axially coordinated Fe–N_(4) single-atom seawater catalyst materials(Cl–Fe–N_(4) and S–Fe–N_(4)).X-ray absorption spectroscopy confirmed their five-coordinated square pyramidal structure.Systematic evaluation of catalytic activities revealed that compared with S–Fe–N_(4),Cl–Fe–N_(4) exhibits smaller electrochemical active surface area and specific surface area,yet demonstrates higher limiting current density(5.8 mA cm^(−2)).The assembled zinc-air batteries using Cl–Fe–N_(4) showed superior power density(187.7 mW cm^(−2) at 245.1 mA cm^(−2)),indicating that Cl axial coordination more effectively enhances the intrinsic ORR activity.Moreover,Cl–Fe–N_(4) demonstrates stronger Cl−poisoning resistance in seawater environments.Chronoamperometry tests and zinc-air battery cycling performance evaluations confirmed its enhanced stability.Density functional theory calculations revealed that the introduction of heteroatoms in the axial direction regulates the electron center of Fe single atom,leading to more active reaction intermediates and increased electron density of Fe single sites,thereby enhancing the reduction in adsorbed intermediates and hence the overall ORR catalytic activity.
基金supported by the National Natural Science Foundation of China(No.52064035)the Key Research and Development Program of Gansu Province,China(No.25YFGA024)the Natural Science Foundation of Zhejiang Province,China(No.LGG22E020003).
文摘Lithium-sulfur(Li-S)batteries boast a theoretical energy density as high as 2600 Wh·kg^(−1),positioning them as a highly attractive option for future advanced energy storage systems.Challenges such as slow transformation kinetics and shuttle effects associated with lithium polysulfides(LiPSs)have seriously hindered their practical applications.In this paper,we present a new method for the synthesis of hollow carbon-sphere-supported Co monatomic catalysts(Co-N-C).This new synthesis method achieves pyrolytic coordination using a precursor rich in imide(-RC=N-)polymers.This synthesis method not only improves the adsorbability and catalytic activity of LiPS but also significantly weakens the shuttle effect and generates Co-N-C with superior conductivity,abundant hollow structures,and a high specific surface area,thus efficiently capturing and restricting the movement of LiPS intermediates.The dispersed Co monoatomic catalysts(Co SACs)were anchored to a highly conductive nitrogen-doped carbon framework and exhibited symmetric N-coordination active sites(Co-N_(4))to ensure fast redox kinetics of LiPS and Li_(2)S_(2)/Li_(2)S solid-state products.The lithium-sulfur battery with Co-N-C as the sulfur carrier showed excellent discharging capacity of 1146.6 mAh·g^(−1) at a discharge rate of 0.5 C and maintained excellent performance at a high discharge rate of 2 C.The capacity decay rate in 500 cycles was only 0.086%per cycle,reflecting excellent long-term cycle stability.This study highlights the key role of the synergistic effect between single-atom cobalt catalysts and hollow carbon spheres in enhancing the efficiency of lithium-sulfur(Li-S)batteries.It also provides valuable insights into the construction and fabrication of highly active monatomic catalysts.The catalytic conversion efficiency of lithium polysulfides is significantly enhanced when embedded in hollow carbon architectures,which serves as a critical strategy for optimizing the electrochemical behavior of next-generation Li-S batteries.
基金supported by the National Natural Science Foundation of China(No.22208374)the Excellent Youth Scientist Award Foundation of Shandong Province(No.ZR2024YQ009)+2 种基金the Distinguished Young Scholars of the National Natural Science Foundation of China(No.22322814)CNPC Innovation Found(2022DQ02-0607)the Fundamental Research Funds for the Central Universities(No.24CX07006A).
文摘Methanol steam reforming(MSR)represents a promising route for hydrogen production,leveraging the high energy density and liquid-phase storage advantages of methanol.Copper-based catalysts have become indispensable for MSR due to their cost-effectiveness,exceptional catalytic activity,and tunable selectivity.However,persistent challenges such as thermal sintering,undesirable CO byproduct formation,diminished low-temperature reactivity,and long-term catalyst deactivation limit their broad industrial deployment.This review comprehensively examines the mechanistic pathways of MSR over Cu-based catalysts,with particular focus on differentiating catalyst formulations optimized for high-temperature(>200°C)versus low-temperature(<200°C)operation.It highlights the decisive influence of Cu nanoparticle size,electronic structure,and crystal structure on catalytic performance.Cutting-edge design strategies,including multi-element engineering,innovative synthesis techniques,and deactivation mitigation,are critically evaluated to elucidate mechanistic connections between atomic-scale structure and catalytic performance enhancement.Finally,industrial applications of commercial Cu/ZnO/Al_(2)O_(3)variants and their scalability challenges are discussed,alongside prospective strategies for catalyst innovation and engineering to advance next-generation hydrogen production.
基金financially supported by the National Natural Science Foundation of China(U22A20421)the Qinglan Project of Jiangsu Province,the 533 Talent Program of Huaian City,and the College Students’Innovative Entrepreneurial Training Plan Program of Jiangsu Province(X202510323027).
文摘Endogenous hydrogen systems,consisting of metal–organic coordination catalysts and alcohols,have been widely applied for the transfer hydrogenation(TH)of biomass-derived carbonyl compounds in recent years.Metal-organic coordination catalysts showed satisfactory ability of TH in the secondary alcohols,but most of them could not effectively employ the cheaper primary alcohols as hydrogen donors.Furthermore,they commonly contained high metal contents,which also led to low catalytic efficiency in significant measure.In this work,we constructed a novel magnesium single-atom catalyst(Mg-NC)with merely 0.37 wt%Mg by means of a combined self-assembly and pyrolysis strategy.The characterization results indicated that Mg was atomically dispersed and it was coordinated with four pyridinic-N in Mg-NC.Due to the obvious electron transfer from Mg to its coordinated pyridinic-N,Mg–N_(4)active centers displayed high Lewis acid-base strength with abundant content,which brought remarkable catalytic activity.When Mg-NC was used for the TH of 5-hydroxymethylfurfural(HMF)in ethanol(EtOH),2,5-bis(hydroxymethyl)furan(BHMF)yield was up to 96.3%with high productivity of 19.85 molBHMF mol_(Mg)^(−1)h^(−1)at 150°C for 5 h.More interestingly,the process of TH over Mg-NC in EtOH was proved to proceed via the hydrogen radical mechanism.Additionally,Mg-NC exhibited powerful catalytic universality;it could not only utilize other primary alcohols(such as n-propanol and n-butanol)as hydrogen donors,but also catalyze the TH of other carbonyl compounds(such as furfural,5-methylfurfural,benzaldehyde,cyclohexanone,and levulinic acid).Overall,this work offered some important clues and references to reinforce the hydrogen-supplying ability of primary alcohols in the TH of various biomass-derived carbonyl compounds to high-value fine chemicals.
基金supported by the Australian Research Council(ARC)Projects(DP220101139,DP220101142,and LP240100542).
文摘High‐entropy amorphous catalysts(HEACs)integrate multielement synergy with structural disorder,making them promising candidates for water splitting.Their distinctive features—including flexible coordination environments,tunable electronic structures,abundant unsaturated active sites,and dynamic structural reassembly—collectively enhance electrochemical activity and durability under operating conditions.This review summarizes recent advances in HEACs for hydrogen evolution,oxygen evolution,and overall water splitting,highlighting their disorder-driven advantages over crystalline counterparts.Catalytic performance benchmarks are presented,and mechanistic insights are discussed,focusing on how multimetallic synergy,amorphization effect,and in‐situ reconstruction cooperatively regulate reaction pathways.These insights provide guidance for the rational design of next‐generation amorphous high‐entropy electrocatalysts with improved efficiency and durability.
基金supports from the National Natural Science Foundation of China(Grant Nos.12305372 and 22376217)the National Key Research&Development Program of China(Grant Nos.2022YFA1603802 and 2022YFB3504100)+1 种基金the projects of the key laboratory of advanced energy materials chemistry,ministry of education(Nankai University)key laboratory of Jiangxi Province for persistent pollutants prevention control and resource reuse(2023SSY02061)are gratefully acknowledged.
文摘Using photoelectrocatalytic CO_(2) reduction reaction(CO_(2)RR)to produce valuable fuels is a fascinating way to alleviate environmental issues and energy crises.Bismuth-based(Bi-based)catalysts have attracted widespread attention for CO_(2)RR due to their high catalytic activity,selectivity,excellent stability,and low cost.However,they still need to be further improved to meet the needs of industrial applications.This review article comprehensively summarizes the recent advances in regulation strategies of Bi-based catalysts and can be divided into six categories:(1)defect engineering,(2)atomic doping engineering,(3)organic framework engineering,(4)inorganic heterojunction engineering,(5)crystal face engineering,and(6)alloying and polarization engineering.Meanwhile,the corresponding catalytic mechanisms of each regulation strategy will also be discussed in detail,aiming to enable researchers to understand the structure-property relationship of the improved Bibased catalysts fundamentally.Finally,the challenges and future opportunities of the Bi-based catalysts in the photoelectrocatalytic CO_(2)RR application field will also be featured from the perspectives of the(1)combination or synergy of multiple regulatory strategies,(2)revealing formation mechanism and realizing controllable synthesis,and(3)in situ multiscale investigation of activation pathways and uncovering the catalytic mechanisms.On the one hand,through the comparative analysis and mechanism explanation of the six major regulatory strategies,a multidimensional knowledge framework of the structure-activity relationship of Bi-based catalysts can be constructed for researchers,which not only deepens the atomic-level understanding of catalytic active sites,charge transport paths,and the adsorption behavior of intermediate products,but also provides theoretical guiding principles for the controllable design of new catalysts;on the other hand,the promising collaborative regulation strategies,controllable synthetic paths,and the in situ multiscale characterization techniques presented in this work provides a paradigm reference for shortening the research and development cycle of high-performance catalysts,conducive to facilitating the transition of photoelectrocatalytic CO_(2)RR technology from the laboratory routes to industrial application.
基金supported by the National Natural Science Foundation of China(No.51878292).
文摘Large-scale CO_(2)emissions have exacerbated the greenhouse effect,reinforcing the critical need for efficient CO_(2)mitigation methods.Plasma-catalytic technology enables CO_(2)conversion under mild conditions,especially for CO_(2)methanation(the Sabatier reaction),which has attracted significant attention due to its economic benefits and the potential for safe energy transportation via existing natural gas pipelines.The development of high-performance CO_(2)methanation catalysts remains an ongoing and long-term objective,and there is a lack of adequate in-situ characterization techniques to investigate the mechanisms.This study focuses on the Ni/La_(2)O_(3)(LN)catalyst and introduces two CO_(2)activation strategies through F and Na modifications:the Ni-Ov-Ni site activation with electron transfer from Ni0 under low-power conditions and basic site activation under high-power conditions.The LN-NaF catalysts enhance CO_(2)methanation activity across the entire power range compared to LN,achieving a CO_(2)conversion of 86.3%and CH4 selectivity of 99.4%.Additionally,LN-F(h)reaches a CH4 yield 4.15 times higher than that of LN at low power.Furthermore,in-situ diffuse reflectance infrared Fourier transform(DRIFT)spectroscopy with a self-made reactor are performed under plasma-catalytic conditions to reveal the CO_(2)adsorption and conversion mechanisms,indicating that different dopants(F,Na,and NaF)exhibit promoting effects on different intermediates,resulting in variations in CO_(2)methanation activity.This study provides valuable insights for improving catalyst performance and a thorough comprehension of mechanisms in CO_(2)methanation.
基金financially supported by the National Natural Science Foundation of China(Nos.51602018 and 51902018)the Natural Science Foundation of Beijing Municipality(No.2154052)+3 种基金the China Postdoctoral Science Foundation(No.2014M560044)the Fundamental Research Funds for the Central Universities(No.FRF-MP-20-22)USTB Research Center for International People-to-people Exchange in Science,Technology and Civilization(No.2022KFYB007)Education and Teaching Reform Foundation at University of Science and Technology Beijing(Nos.2023JGC027,KC2022QYW06,and KC2022TS09)。
文摘S and Co co-doped carbon catalysts were prepared via pyrolysis of MOF-71 and thiourea mixtures at 800℃at a mass ratio of MOF-71 to thiourea of 1:0.1 to effectively activate peroxymonosulfate(PMS)for methylene blue(MB)degradation.The effects of two different mixing routes were identified on the MB degradation performance.Particularly,the catalyst obtained by the alcohol solvent evaporation(MOF-AEP)mixing route could degrade 95.60%MB(50 mg/L)within 4 min(degradation rate:K=0.78 min^(-1)),which was faster than that derived from the direct grinding method(MOF-DGP,80.97%,K=0.39 min^(-1)).X-ray photoelectron spectroscopy revealed that the Co-S content of MOF-AEP(43.39at%)was less than that of MOF-DGP(54.73at%),and the proportion of C-S-C in MOF-AEP(13.56at%)was higher than that of MOF-DGP(10.67at%).Density functional theory calculations revealed that the adsorption energy of Co for PMS was -2.94 eV when sulfur was doped as C-S-C on the carbon skeleton,which was higher than that when sulfur was doped next to cobalt in the form of Co-S bond(-2.86 eV).Thus,the C-S-C sites might provide more contributions to activate PMS compared with Co-S.Furthermore,the degradation parameters,including pH and MOF-AEP dosage,were investigated.Finally,radical quenching experiments and electron paramagnetic resonance(EPR)measurements revealed that ^(1)O_(2)might be the primary catalytic species,whereas·O~(2-)might be the secondary one in degrading MB.
基金support from the Czech Science Foundation,project EXPRO,No 19-27454Xsupport by the European Union under the REFRESH—Research Excellence For Region Sustainability and High-tech Industries project number CZ.10.03.01/00/22_003/0000048 via the Operational Programme Just Transition from the Ministry of the Environment of the Czech Republic+1 种基金Horizon Europe project EIC Pathfinder Open 2023,“GlaS-A-Fuels”(No.101130717)supported from ERDF/ESF,project TECHSCALE No.CZ.02.01.01/00/22_008/0004587).
文摘Green hydrogen from water splitting has emerged as a critical energy vector with the potential to spearhead the global transition to a fossil fuel-independent society.The field of catalysis has been revolutionized by single-atom catalysts(SACs),which exhibit unique and intricate interactions between atomically dispersed metal atoms and their supports.Recently,bimetallic SACs(bimSACs)have garnered significant attention for leveraging the synergistic functions of two metal ions coordinated on appropriately designed supports.BimSACs offer an avenue for rich metal–metal and metal–support cooperativity,potentially addressing current limitations of SACs in effectively furnishing transformations which involve synchronous proton–electron exchanges,substrate activation with reversible redox cycles,simultaneous multi-electron transfer,regulation of spin states,tuning of electronic properties,and cyclic transition states with low activation energies.This review aims to encapsulate the growing advancements in bimSACs,with an emphasis on their pivotal role in hydrogen generation via water splitting.We subsequently delve into advanced experimental methodologies for the elaborate characterization of SACs,elucidate their electronic properties,and discuss their local coordination environment.Overall,we present comprehensive discussion on the deployment of bimSACs in both hydrogen evolution reaction and oxygen evolution reaction,the two half-reactions of the water electrolysis process.
基金supported by the Natural Science Foundation of Shanxi Province(202203021221155)the Foundation of National Key Laboratory of High Efficiency and Low Carbon Utilization of Coal(J23-24-902)。
文摘With ongoing global warming and increasing energy demands,the CH_(4)-CO_(2)reforming reaction(dry reforming of methane,DRM)has garnered significant attention as a promising carbon capture and utilization technology.Nickel-based catalysts are renowned for their outstanding activity and selectivity in this process.The impact of metal-support interaction(MSI),on Ni-based catalyst performance has been extensively researched and debated recently.This paper reviews the recent research progress of MSI on Ni-based catalysts and their characterization and modulation strategies in catalytic reactions.From the perspective of MSI,the effects of different carriers(metal oxides,carbon materials and molecular sieves,etc.)are introduced on the dispersion and surface structure of Ni active metal particles,and the effect of MSI on the activity and stability of DRM reactions on Ni-based catalysts is discussed in detail.Future research should focus on better understanding and controlling MSI to improve the performance and durability of nickel-based catalysts in CH_(4)-CO_(2)reforming,advancing cleaner energy technologies.
基金supported by the National Natural Science Foundation of China(No.21571062)the Program for Professor of Special Appointment(Eastern Scholar)at the Shanghai Institutions of Higher Learning to JGL,and the Fundamental Research Funds for the Central Universities(No.222201717003)。
文摘Exploiting non-precious metal catalysts with excellent oxygen reduction reaction(ORR)performance for energy devices is paramount essential for the green and sustainable society development.Herein,low-cost,high-performance biomass-derived ORR catalysts with an asymmetric Fe-N_(3)P configuration was prepared by a simple pyrolysis-etching technique,where carboxymethyl cellulose(CMC)was used as the carbon source,urea and 1,10-phenanthroline iron complex(FePhen)as additives,and Na_(3)PO_(4)as the phosphorus dopant and a pore-forming agent.The CMC-derived FeNPC catalyst displayed a large specific area(BET:1235 m^(2)g^(-1))with atomically dispersed Fe-N_(3)P active sites,which exhibited superior ORR activity and stability in alkaline solution(E_(1/2)=0.90 V vs.RHE)and Zn-air batteries(P_(max)=149 mW cm^(-2))to commercial Pt/C catalyst(E_(1/2)=0.87 V,P_(max)=118 mW cm^(-2))under similar experimental conditions.This work provides a feasible and costeffective route toward highly efficient ORR catalysts and their application to Zn-air batteries for energy conversion.
基金supported by the Zhejiang Provincial Natural Science Foundation of China(LDT23E06012E06)National Key R&D Program of China(2023YFC3710800)+3 种基金the National EnergySaving and Low-Carbon Materials Production and Application Demonstration Platform Program(TC220H06N)Pioneer R&D Program of Zhejiang Province-China(2024SSYS0066,2023C03016)National Natural Science Foundation of China(42341208)Zhejiang Energy Group Research Fund(ZNKJ-2023-100)。
文摘Converting CO_(2)with green hydrogen to methanol as a carbon-neutral liquid fuel is a promising route for the long-term storage and distribution of intermittent renewable energy.Nevertheless,attaining highly efficient methanol synthesis catalysts from the vast composition space remains a significant challenge.Here we present a machine learning framework for accelerating the development of high space-time yield(STY)methanol synthesis catalysts.A database of methanol synthesis catalysts has been compiled,consisting of catalyst composition,preparation parameters,structural characteristics,reaction conditions and their corresponding catalytic performance.A methodology for constructing catalyst features based on the intrinsic physicochemical properties of the catalyst components has been developed,which significantly reduced the data dimensionality and enhanced the efficiency of machine learning operations.Two high-precision machine learning prediction models for the activities and product selectivity of catalysts were trained and obtained.Using this machine learning framework,an efficient search was achieved within the catalyst composition space,leading to the successful identification of high STY multielement oxide methanol synthesis catalysts.Notably,the CuZnAlTi catalyst achieved high STYs of 0.49 and 0.65 g_(MeOH)/(g_(catalyst)h)for CO_(2)and CO hydrogenation to methanol at 250℃,respectively,and the STY was further increased to 2.63 g_(Me OH)/(g_(catalyst)h)in CO and CO_(2)co-hydrogenation.
基金the Canadian NRCan OERD Energy Innovation Programthe Natural Sciences and Engineering Research Council of Canada,and the Carbon Solution Program for their financial support.
文摘The pursuit of alternative fuel generation technologies has gained momentum due to the diminishing reserves of fossil fuels and global warming from increased CO_(2)emission.Among the proposed methods,the hydrogenation of CO_(2)to produce marketable carbon-based products like methanol and ethanol is a practical approach that offers great potential to reduce CO_(2)emissions.Although significant volumes of methanol are currently produced from CO_(2),developing highly efficient and stable catalysts is crucial for further enhancing conversion and selectivity,thereby reducing process costs.An in-depth examination of the differences and similarities in the reaction pathways for methanol and ethanol production highlights the key factors that drive C-C coupling.Identifying these factors guides us toward developing more effective catalysts for ethanol synthesis.In this paper,we explore how different catalysts,through the production of various intermediates,can initiate the synthesis of methanol or ethanol.The catalytic mechanisms proposed by spectroscopic techniques and theoretical calculations,including operando X-ray methods,FTIR analysis,and DFT calculations,are summarized and presented.The following discussion explores the structural properties and composition of catalysts that influence C-C coupling and optimize the conversion rate of CO_(2)into ethanol.Lastly,the review examines recent catalysts employed for selective methanol and ethanol production,focusing on single-atom catalysts.
基金the financial support from the National Natural Science Foundation of China(Nos.52074176,52300165,52300056,52300099)Natural Science Foundation of Shandong Province Youth Project(No.ZR2022QB155)Open Project Program of Engineering Research Center of Groundwater Pollution Control and Remediation,Ministry of Education of China(No.GW202203)。
文摘Inactivation of carbon-based transition metal catalysts,which was caused by electron loss,limited their application in advanced oxidation processes.Therefore,Co and TiO_(2) double-loaded carbon nanofiber material(Co@CNFs-TiO_(2))was synthesized in this study.Photocatalytic and chemical catalytic systems were synergized efficiently.Tetracycline was eliminated within 15 min.The degradation rate remained above 90%after five cycles,and the 50%promotion proved the high stability of Co@CNFs-TiO_(2).The main reactive oxygen species in this system were sulfate radicals,whereas Co and TiO_(2) represented the active sites of the catalytic reaction.Electrons generated from TiO_(2) during the photocatalytic process were transferred to Co,which promoted the Co(Ⅲ)/Co(Ⅱ)cycle and maintained Co in a low-valence state,thereby stimulating the generation of sulfate radicals.In this study,the effective regulation of reactive oxygen species in the reaction system was realized.The results provided a guidance for in situ electron replenishment and regeneration of carbon-based transition metal catalysts,which will expand the practical application of advanced oxidation processes.